By San-chuan Tang, Wen Chen, Shun-ming Ning, Kan-ping Yu, Qiang Zhao, Xue-yong Xing

"A new type of desilication agent (PA-2) was selected by experiment based on the analysis of the characters of silica gel, and the influence of desilication type, desilication dosage, pH value, temperature and aging time on the desilicating effect was studied. The test results showed that on the conditions that pH was 2.0, temperature was 20""C, aging time was12 hours and the dosage of desilication agent was 0.23%, the desilication rate was higher than 93% in solution.IntroductionVanadium is an important strategic resources, which applies to steel industry and petrochemical industry. The main materials for vanadium product are steelmaking vanadium slag, stone coal and containing vanadium waste catalyst, etc. And stone coal is a low-grade carbonaceous silicified vanadium resource, which is unique material for vanadium extraction in China. Meanwhile, our stone coal reserves is No.l throughout the world.The silica acid solution containing vanadium is produced by acid leaching of raw stone coal or its roasted ore. The silica content of this solution is mostly high, besides, when pH is higher than 2 , the solution is unstable. Furthermore, it is very easy to generate gel substance with the increasing of pH value and standing time. 'Ibis silica gel is composed of colloidal particles with the size in 0.001 - 0.1 um. As a result, it is very hard even impossible for the following operation of solution."

Jan 1, 2013

By Jian Li, Guo Chen, Bingguo Liu, Hongying Xia, Jinhui Peng, Libo Zhang

"Decomposition of ammonium tetramolybdate to prepare Mo03 using silicon carbide crucible in microwave fields was investigated. The results were analyzed Using TG-DTG and X-ray diffraction. Meanwhile, the effects of heating rat, material thickness, socking time, socking temperature on the structure of preparing Mo03 were studied. TG-DTG curves show that the decomposition process of ammonium tetramolybdate is only one stage, in the temperature range 300-350°C, whose begin to decompose when temperature increases beyond 300°C. The molybdenum trioxide was prepared by thermal decomposition. The quality ofMo03 was not affected under the heating rat is 12°C/min. It was beneficial for decomposition ratio with the lower material thickness, longer soaking time, and higher soaking temperature. XRD curves showed that it is viable method for preparation of Mo03 by decomposition from ammonium tetramolybdate in microwave fields.IntroductionMolybdenum is widely used in national defense, aviation, industrial and agricultural production as rare refractory metal. Molybdenum trioxide is vital raw materials for the process of preparation of molybdenum. The traditional production technology of molybdenum oxide is that ammonium tetramolybdate is calcined in rotary kiln or 4-tube furnace [J,2J. But the longer production time, the higher production cost, the lower furnace thermal efficiency, and bigger the energy consumption, especially the powder is easy to leak, the working environment is poor by using rotary kiln [ 3 l _ The particle of molybdenum oxide is non-uniform by using 4-tube furnace because of the uneven temperature of every tube and the poor exhaust of boat bottom [4l _ However microwave heating is quick and uniformity, it is a meaningful research that the microwave is used in the process of calcining ammonium tetramolybdate."

Jan 1, 2013

By Bing Gao, Zhe Wang, Xiangdong Xing, Xueqi Zhang, Shan Ren, Jianliang Zhang

"In sintering, the flame front speed (bed permeability) and sinter qualities are greatly depended on the feed size, especially coke breeze and limestone particle size. It is well known that coke breeze provides sinter bed with heat to meet the demand of partial fusion and diffusion bonding while limestone reacts with iron ore to generate bonding phase in the sintering process. Accordingly, it is necessary to find the optimum combination of different particle size of coke breeze and limestone to yield sinter associated with better qualities. In this study, sinter was produced in the sinter pot with varying coke breeze and limestone particle size together in sintering of a coarse hematite iron ore. The sintering productivity was measured and all of the result sinters were examined by microstructure analysis and reduction degradation test (RDI test). For the sintering of a coarse hematite iron ore, it was found that the optimum mean particle size combination of coke breeze and limestone was 1. 71mm and 1.55mm in the sinter mix. On such a circumstance, sintering productivity was higher and the properties of sinter were better.IntroductionNowadays, as the main iron bearing burden material of modem blast furnaces, sinter has a great influence on the blast furnace operation. Sintering is a greatly complex process involving various chemical reactions to form kinds of mineral phases [1, 2]. In the sintering process, coke breeze is used for fuel and it generates heat to raise the green bed temperature. Limestone serves as flux and it reacts with iron ore to produce various mineral phases. On one hand, during the sintering process, the particle size of coke breeze can have an effect on temperature, atmosphere, the flame front speed and all of them act on the microstructure and mineral constitutions of sinter [3, 4]."

Jan 1, 2013

By Bohumir Jelinek, Sergio Felicelli, Mohsen Eshraghi

"We present a parallel lattice Boltzmann - cellular automaton model of the two-dimensional dendritic growth during solidification of binary alloys. The model incorporates effects of solute and energy transport under melt convection. The parallel performance of the algorithm is assessed. A loss in the parallel efficiency is observed when multiple computational cores per processor are utilized. Excellent strong scaling up to thousands of computing cores is obtained across the nodes of a computer cluster, along with the near-perfect weak scaling up to forty thousand cores. The presented solidification model shows a good scalability up to centimeter size domains, including millions of dendrites.IntroductionLattice Boltzmann method (LBM) is an attractive numerical technique for solving fluid dynamics problems. Its advantages are simple formulation and locality, with locality facilitating parallel implementation. In the present model, interface kinetic is driven by the difference between local actual and local equilibrium liquid composition [1]. The cellular automaton (CA) technique is deployed to track the solid-liquid interface [2]. A serial version of the present LBM-CA model with a small number of dendrites was validated against theoretical and experimental results in the previous publications [3, 4]. In this work, it is the first time that simulations with millions of dendrites were performed, something not possible with the computationally much more costly phasefield method [5].This research effort examines a technique for simulations of millions of dendrites in centimeter size domains, including thermal, convection, and solute redistribution effects. Nearly ideal scaling properties of the model are demonstrated. This extensively large landmark was achieved because of• the CA technique being two orders of magnitude faster than alternative, phase-field methods [5]• highly parallelizable LBM method, convenient for simulations of flow within complex and time dependent boundaries• availability of the powerful NSF Extreme Science and Engineering Discovery Environment (XSEDE) supercomputing resources"

Jan 1, 2013

By Cheng Gong-jin, Chu Man-sheng, Liu Zheng-gen, Zhang Yong, Liu Jian-xing, Xue Xiang-xin

"High chromium vanadium-titanium magnetite is one kind of Fe-V-Ti-Cr composite ore resources, which owes high utilization value. Owing to lacking systematic study on the sintering of this ore home and abroad, effects of carbon addition and basicity on sintering process and sinter metallurgical properties, such as sinter yield, vertical sintering speed, tumbler strength, sinter machine utilization coefficient, and low temperature reduction degradation were investigated systematically under laboratory conditions in the paper. The results shows that, when high chromium vanadium-titanium magnetite proportion is kept unchanged as 13% in sintering feeds, sintering process index and metallurgical properties are the optimum under carbon addition 5.0% and basicity 2.70, which meets the requirements of blast furnace burdens. This research provides technical parameters for practical sintering production of high chromium vanadium-titanium magnetite.IntroductionHigh chromium vanadium-titanium magnetite (hereinafter abbreviated as hi§h-Cr V-Ti magnetite), in which Fe is closely symbiotic with Ti and isomorphous with V and Cr1'- l, is one kind of typical vanadium-titanium magnetite resources with high comprehensive utilization value but the difficulties are extremely high due to complex chemical composition and mineral structure. At present, the feasible and mainstream utilization process of high-Cr V-Ti magnetite should be the route of agglomeration-blast furnace smelting. Thus, sintering production is the foundation for high-Cr V-Ti magnetite utilization. However, till now there are few research documentations on high-Cr V-Ti magnetite sintering home and abroad. Under the above background, this study focused on detailed researches of high-Cr V-Ti magnetite sintering. Sintering process uses the powders or fine iron ores to produce artificial rich ore with good metallurgical properties 4l Solid fuel provides 90% heat requirement during sintering15J. The appropriate amount of fuel and flux should be added during sintering in order to provide necessary heat and maintain the desired basicity16l. That is to say, carbon addition and basicity are two key factors affecting metallurgical properties of sintering products17J. Therefore, the effects of carbon addition and basicity on sintering process and metallurgical properties, including sinter yield, vertical sintering speed, tumbler strength, sinter machine utilization coefficient, and low temperature reduction degradation, are systemically investigated under laboratory conditions in the study, on purpose to achieve the optimization of sintering process for high-Cr V-Ti magnetite."

Jan 1, 2013

By Hadi Fanisalek

"Most industries attempted to conduct their energy consumptions in an optimized way for a few decades. This is because policymakers and top managements in industries have felt the critical situation of a possible energy shortage that could happen for them in the near future, even in countries with significant fossil fuel resources. Decisions related to energy consumption in any industry will have a long-term effect on different parts of the industry structure. In this way, energy decisions should be categorized as part of any industry's main strategic and long-term decisions, which should be made by top strategists. On the other hand, strategic management has many powerful tools to help the policymakers in industries to establish a long-term strategy for energy consumption and reducing or preferably eliminating the energy loss. This will be more important for industries in the Middle East, where they have just started to make an applicable strategy for their energy consumption and to design a long-term procedure for their energy management. Based on strategic management and by comparison we designed and offered a new model for establishing the main structure of energy management strategy in primary aluminum industry, which is a high consuming energy industry. This strategy, which we will call ESM (Energy Strategic Model) and has been applied for a typical primary aluminum industry in this paper, is similar to the practical models in the field of strategic management, which were developed for designing the overall company strategy.IntroductionThe elementary goal for introducing strategic management in any organization was to establish a successful plan helping the company to survive and to gain competitive advantage over its competitors in a rough business environment. Strategic management is an ongoing process that evaluates and controls the business and industries in which the company is involved; assesses its competitors and sets goals and strategies to meet all existing and potential competitors; and then reassesses each strategy annually to determine how it has been implemented and whether it has succeeded or needs replacement by a new strategy to meet changed circumstances, new technology, new competitors, and a new economic environment[!]."

Jan 1, 2013

By Saad Elias Kaskah

"The Box-Behnken Design (BBD) is used to model the sacrificial Cathodic Protection System (SCPS) to find the factors effectiveness behaviour. For protection potential assessment the BBD receives (resistivity of environment, sacrificial anode alloy, distance between anode and cathode and surface area for the structure to be protected) as input and gives the protection potential as output. By applying BBD with their analysis tools we get many results. The important results which are the factors individual effectiveness on the sacrificial cathodic protection (SCP) process are the resistivity which has the greatest effect on the potential protection (rank=l) followed by sacrificial anode alloy type (rank=2), surface area for structure protected required (rank=3) and distance between anode and cathode (rank=4). The interaction of sacrificial anode alloy and cathode area {X2X4 ) has significant effect on CP process with the limits which are used in this work while the other factors interaction (X1X2, X1X3, X1X4,X2X3, X3X4 ) has insignificant effect on the limits which used in this work.IntroductionFor carbon steel in seawater the normal corrosion potential E '°""_is in the range -550 to -600 mV vs. Ag/AgCI [1]. The most effective method to overcome the corrosion is cathodic protection {CP) which represents a control method in the steel wall corrosion. Cathodic protection has been used in several areas including marine and underground structures, storage tanks, and pipelines [2]. Sacrificial anodes system generates protective current which depends upon the inherent potential difference between the anodes and the structure to be protected. If the structure is made of iron or steel, any metal that is more active in the electromotive force series can theoretically be used as anode material [3]. There are many factors influencing on cathodic protection like resistivity (NaCl content), chemical composition of sacrificial anode alloy, distance between anode and cathode, surface area of cathode, temperature, humidity, velocity of solution, dust, impurities, bacteria and etc .. The present work studied four factors: NaCl content, resistivity), chemical composition of sacrificial anode alloy, distance between anode and cathode, surface area of cathode) with different three levels of values for each one. Then this work will find the optimum value from the factors levels that tacked to investigated there influencing on sacrificial cathodic protection system."

Jan 1, 2013

By Hiroaki Kawamura, Takeshi Yoshikawa, Kazuki Morita, Yutaka Yanaba

"To develop an alternative metallurgical process for phosphorus removal in the production of solar-grade silicon (SOG-Si), slag treatment of metallurgical-grade silicon (MG-Si) was conducted, followed by acid leaching. Phosphorus-doped silicon alloy or MG-Si containing certain amounts of phosphorus and calcium was reacted at 1723 K and 1773 K with CaO--CaF2 of several compositions. Phosphorus removal from the molten silicon into the slag phase was confirmed by reduction to phosphide ions, P3-, and phosphate ions, P3-. These ions were separately determined using a wet chemical analysis method developed by ourselves. The highest phosphorus distribution ratio obtained was 2. 7 after reaction for 18 h with 17.5 mass% CaO--CaF2 slag. We then conducted acid leaching of the silicon and achieved removal of a large fraction (over 90 % ) of the phosphorus, which was much higher than that obtained by ordinary oxidizing slag treatment.IntroductionIn recent years, the production of solar cells has been increasing rapidly. Because of this, the demand for solar-grade silicon (SOG-Si) has also been growing rapidly. The development of lower-cost mass production processes is therefore needed to provide silicon feedstock. Phosphorus is one of the impurities in metallurgical-grade silicon (MG-Si). Because of its large segregation coefficient (kp = 0.35) [l ], it is difficult to remove phosphorus using a solidification refining process. Vacuum melting is considered to be a promising method for removing phosphorous from MG-Si [2], but the issues of high cost and large energy consumption have still to be resolved.Slag treatment is often used to remove impurity elements by oxidizing reactions during general oxidation refining processes. For example, phosphorus in molten steel is removed into a slag phase as phosphate ions, PO4 3-l-, by the following reaction:"

Jan 1, 2013

By Monteirom Sergio N., Romulo L. Loiola, Giulio R. Altoe, Noan Simonassi, Frederico M. Margem

"The environmental concern is creating pressure for the substitution of high energy consumption materials for natural and sustainable ones. Compared to synthetic fibers, natural fibers have shown advantages in technical aspects such as flexibility and toughness. So there is a growing worldwide interest in the use of these fibers. Buriti fiber extracted from buriti palm tree (Mauritia flexuosa), presents some significant characteristic, but until now only few studies on buriti fiber were performed. This work aims to make the analysis of the tensile strength of epoxy composites reinforced with buriti fibers. This analysis was performed in fibers with diameters between 0.1 and 0.4 mm. Those fibers were incorporated into the epoxy matrix with volume fraction from 0 to 30%. The fiber diameters were measured by a profile projector. After fracture the specimens were analyzed by a SEM (scanning electron microscope).IntroductionNatural fibers with high amount of cellulose, also known as lignocellulosic fibers, have been used from primeval times of our civilization. In the last century, synthetic fibers such as nylon, carbon, aramid and glass fibers gained interest owing to superior strength and precise dimensional control. Natural fibers were then replaced by synthetics in many fields such as textiles, sports goods and appliances. In the past decades, however, environmental issues drawn, once again, the attention to lignocellulosic fibers as possible substitute for intensive energy-consuming and long term polluting synthetics, specially the glass fiber(1). In particular, research works have disclosed the potential advantages associated with the use of lignocellulosic fibers as the reinforcing phase in polymer composites(2-3). Among the advantages it is worth mentioning the renewability, recyclability, biodegradability and the fact that natural fibers are neutral with respect to CO2 emissions responsible for global warming. In addition to environmental benefits(l,10) the lignocellulosic fibers present economical advantages, such as worldwide abundance and comparatively low costs as well as some technical properties associated with flexibility and toughness( 4), which contribute to the performance of automobile components fabricated with natural fibers composites(l 1-13)."

Jan 1, 2013

By Gaifeng Xue, Jingxuan Zhou, Shangchao Liu

"Both COD and TOC can characterize organic pollution of coking wastewater. In theory, there is a linear correlation between these two indicators. After continuous monitoring TOC and COD of coking waste water, linear regression relationship between of these to indicators was studied with the use of mathematical statistics. And conversion equation between these two indicators was established, and using t-test method for significance testing. The results showed that the linear relationship of COD and TOC was significant. Also interval estimation of equation slope and intercept were given in the condition of 95% confidence level. A linear regression equation established can be used to indirectly convert TOC to COD with high precision and accuracy.IntroductionBoth chemical oxygen demand (COD) and total organic carbon (TOC) are measure of the degree of characterization for organic pollution of water bodies. The current COD standard analytical methods is Potassium dichromate titration method [1] . there are some disadvantages in this method, such as only part of organic matter in the water bodies being oxidated, the refluxed steps, a long time needed for each measurement, high cost. It is the most important that sulfuric acid silver and mercury sulfate reagents used in the measurement may easily lead to secondary pollution. In contrast, the measurement of TOC is by the method of combustion or Photocatalytic Oxidation. The result could be easily got from the instrument. There are some advantages in this way, such as easy operation, short time and little expenses for each measurement and no secondary pollution 121• In addition, the measurement of TOC has higher degree of precision and accuracy than the measurement of COD both in the determination of calibration standards and actual samples. The meaning and contrast of TOC and COD are listed in the table 1."

Jan 1, 2013

By James C. Sever

"With the advent of high energy costs and increasing concern for the environment leading to the incorporation the C02 life cycle as a criteria for the material used in a finished product, it is beneficial to analyze the plant and the process used in producing a raw material in order to identify practical, economic energy recovery opportunities. To this end a study was made of the proposed Nevada Clean Magnesium, Inc. Tami-Mosi reduction facility. Each source of waste heat is listed together with the assessment for potential co generation or direct recovery. The overall impact on energy requirement and C02 generation is provided.IntroductionHistorically metal reduction plants, large consumers of energy, do not recover waste heat. This occurred for many reasons:• Energy costs were low and the capital for a co-generation system could not be justified;• Waste heat sources contained entrained solids or liquids which would inhibit efficient energy recovery;• The exit temperature for the heat source was too low for efficient use by aaqueous Rankine cycle system.The business environment has now changed adding impetus to the recovery of energy previously discarded. Power costs have greatly increased. Global warming and the impact of carbon dioxide on the environment has become an issue which could impact the permitting of a plant. Technology improvements especially the development of a scaling environment waste heat boiler [l] and the development of the organic cycle Rankine cycle recovery system enable up to 70% energy recovery from ""low grade"" heat sources [2].With the inception of Nevada Clean Magnesium, Inc. 's (formerly Molycor Gold Corporation, Inc.)Northern Nevada Tami-Mosi project [3], an opportunity was presented to incorporate energy optimization from the initial design phase."

Jan 1, 2013

By E. V. Redin, B. A. Dubrovsky, E. V. Knyazev, A. I. Starikov

"Ti-V magnetite is one of the most abundant composite ore resources in the world. This ore cannot be fully processed via blast furnace technology because of high content of Ti02. According to the investigations carried out in the USA and Japan ITmk3 RHF (Rotary Hearth Furnace) technology is a breakthrough in Ironmaking. Reduction, melting and slag removal can be achieved in just 10 min. The main objective of the investigation is to establish optimum operation conditions for the production of iron nuggets from Ti-V magnetite ore via the ITmk3 by means of the lab scale testing. Samples of ore from the Maly Kuybas deposit (Southern Ural), carbon reductant and fluxes were chemically analyzed. Green pellets were processed via a lab chamber furnace to simulate RHF conditions. The nuggets and slag were chemically analyzed. This preliminary test work provides valuable information which may be used for large-scale testing in a commercially sized RHF.IntroductionThe ITmk3 process upon which this paper focuses was developed by Kobe Steel in its research facilities [l]. After pilot testing at Kobe Steel's Kakogava Works in 1999-2004 the pilot demonstration plant was built and operations were successfully carried out by Mesabi Nugget joint venture in 2002-2004. Steel Dynamics put into operation the commercial plant at the Mesabi Nugget site in Hoyt Lakes (Minnesota) in 2010. Results were consistent with nugget characteristics confirming ITmk3' s flexibility with respect to raw material inputs. At the same time, no research in the field of nugget from the Ti-V magnetite bearing ore with high content of Ti02 and Alz03 has been done. It is well known, if a lot of Ti02 and Alz03 enter the blast furnace, slag becomes viscous. The viscous slag is obstacle for stable operation of the blast furnace. Besides, high content of Alz03 raises the melting temperature of gangue minerals disturbing the coalescence of reduced iron to the nuggets."

Jan 1, 2013

By Shuo Wang, Yu Wang, Bing Xie, Rui Tang, Hong-Yi Li, Kun Wen

"During present converter vanadium extraction process, phosphorus could not be removed from hot metal due to absence of CaO in slag though it is an efficient way for vanadium extraction. In order to improve the phosphorus remove and produce CaO-containing vanadium slag, which could be directly used in subsequent roasting process, during the converter vanadium extraction process, lime dissolution in FeOx-Si02-V203-Ti02 slag was investigated by using a rotating cylinder technique and the slag-lime interface was characterized by SEM/EDS. Results showed that changes in the slag chemistry and phase compositions during the lime dissolution process were similar to that in CaO-Si02-FeOx based slag during the BOF process. The V and Ti in the slag were expected to diffuse into the lattice of2CaO·Si02 solid solution, which formed a rather thinner layer in thickness at the slag-lime interface than that in BOF process, leading to improvement of lime dissolution in the slag.IntroductionVanadium is important material that widely applied in industries. The traditional technique to extract vanadium was to leach vanadium after sodium salt roasting. However, the sodium salt roasting process has several problems including lower yielding rate[!] and environmental pollution[2]. Therefore, the more environment-friendly technique of calcium roasting[3-4] was proposed. In order to increase roasting efficiency of vanadium slag, it is essential to study the dissolution/reaction mechanism between lime and vanadium slag. Many investigations about the dissolution reaction of lime in molten slag have been carried out from the standpoints of rapid slagging to De-Pin steelmaking process[5-6]. However, their studies were focused on BOF slag and the reaction mechanism between solid lime and slag containing vanadium has not been reported yet. In present work, the dissolution process was studied with rotating cylinder technique and the reaction interfaces were observed and analyzed by SEM/EDS to elucidate the dissolution mechanism of lime in vanadium slag. This work was supported by National Natural Science Foundation of China No. 51090382."

Jan 1, 2013

By Gerald Onyedika, Tochi Onwumere, Martin Ogwuegbu

"The kinetic study for the leaching of iron from cassiterite ore in KOH solution was studied. The effects of KOH concentration, particle size and reaction temperature on the leaching rate of iron were also examined. The results of leaching studies showed that the leaching of iron from cassiterite ore in KOH solution is significantly influenced by the reaction temperature, KOH concentration, and decrease in particle size. The study showed that 90.62% of iron ore was leached in 8M KOH solution at 80°C within 120 minutes. The experimental data were well evaluated using the shrinking model for surface chemical reaction and diffusion control through the product layer. The activation energies for the iron ore dissolution using the two models were calculated to be 32.06KJmor1 and 97.97 KJmor' respectively.IntroductionIn recent times, there has been increasing attention on the kinetic study of mineral dissolution. In most of these studies, the experimental results were analyzed with a suitable shrinking core model under the assumption that the ore is a homogeneous spherical solid phase [1-4]. A study of the dissolution kinetics of a Nigerian cassiterite ore by hydrochloric acid showed that increase in the hydrochloric acid concentration is accompanied with increase in the amount of cassiterite ore dissolved at various times [4]. The optimal concentration was found to be 4.0M HCl, after which there was a decline in the amount of the ore dissolved, which showed that the concentration of the reagent has a significant effect on the leaching rate of the ore. Also in studying the effect of stirring speed on the rate of cassiterite ore dissolution while keeping other conditions constant for 120 minutes, the result showed that the rate of cassiterite ore dissolution was dependent on the stirring speed over a range of 0 to 630 rpm. Above 360 rpm, the stirring speed no longer had any effect on the solid dissolution. The dissolution rates of cassiterite were analyzed using a suitable shrinking model. The results showed that the reaction was controlled by the diffusion of tin through the porous product layer, a reaction order with respect to hydrogen ion concentration of 0.92 M and activation energy of 50.05KJmor'. In another kinetic study on the leaching of a low grade niobium-tantalum ore with concentrated KOH solution the effect ofreaction temperature, KOH concentration, agitation speed, particle size and alkali-to-ore mass ratio on the dissolution rate of niobium were examined [5]. The result of niobium leaching from low grade niobium-tantalum ore with concentrated KOH, solution at different agitation speeds showed that the dissolution rate increased with increase in agitation rate. In the case of particle size effect, the results show that small particles require much shorter time for complete dissolution than the large ones."

Jan 1, 2013

By Esperidiana A. B. Moura, Michelle Gomes, Cordelia M. F. Escanhoela, Francisco R. V. Diaz, Angel Ortiz, Rene R. Oliveira

"This work evaluates changes in morphological, mechanical and thermo-mechanical properties of electron-beam irradiated HDPE/nanoclay and HDPE/Piassava fiber/nanoclay. Material samples irradiated with 100 and 200 kGy using a 1.5 Me V electron beam accelerator (room temperature, presence of air) were submitted to tensile, flexural, and HDT tests. MFI, SEM and XRD analyses were carried out. Correlation between properties was discussed. Results showed that incorporation of piassava (Attalea funifera Mart) fiber and nanoclay, followed by irradiation represented significant gain in thermo-mechanical properties. Changes in surface morphology and reduction in MFI were observed. In conclusion, it may be claimed that the incorporation of piassava fiber in small size particles and nanoclay in the HDPE followed by electron-beam irradiation effectively improved the polymer properties and led to materials with superior properties suitable for several industrial applications.1. IntroductionIn recent years, the preference for using natural fibers instead of synthetic ones in polymer composites has been growing significantly. In Brazil, due to the great diversity of woody and fibrous plants of our forests, a vast potential of natural fibers is found, presenting good mechanical strength properties, chemical and biological stability, fire resistance, abrasion resistance, shear strength and lightness, among other which may contribute to the development of new materials for different applications such as automotive, aerospace, construction, food segment, cosmetics and others [ 1]."

Jan 1, 2013

By Duan Xin-hui, Wang Xin, Peng Jin-hui, C. Srinivasakannan, Zhang Li-bo

The work attempts to optimize the process of preparation of modified semi-coke from semi-coke using phosphoric acid (H3P04) as the activating agent using the response surface methodology (RSM). The influences of three major dependent variables, the impregnation ratio, activation time, and activation temperature were assessed on the independent variables yield and the iodine number. The empirical relationship between the dependent and the independent variables were established using the quadratic response surface models, which were utilized to optimize the process parameters. The significance of each of the parameters and interaction among the parameters on the independent variable was assessed based on analysis of variance (ANOVA). The process variables were varied within the range of impregnation ratio (IR) from 1.5 to 4, activation time from 30 to 90 min and activation temperature from 550 'C to 650 'C. The optimized process conditions were estimated to be an IR of 2.29, activation time of 32 min, and an activation temperature of 605°C respectively using the process optimization tool. The BET surface area of modified semi-coke of the optimized sample was estimated to be 915m2/g, with the pore volume of0.71cm3/g, with an average pore diameter of 3.09 nm, with micropore volume fraction being 52.36%. The scanning electron microscope (SEM) images were utilized to visualize the surface pore structure.

Jan 1, 2013

By Gaifeng Xue, Lei Zhang, Xia Liu, Lina Wang, Pu Liu, Benquan Fu

"Experiments were conducted to investigate the behavior of the integrated process with a three-dimensional electrode reactor combined with Fenton process for coking wastewater treatment. Effects of initial pH value, reaction time, H20 2 dosage, Fe2+ dosage on Total organic carbon (f OC) removal rate were investigated. The kinetics of degradation of TOC from coking wastewater by three-dimensional fluid bed electrode reactor combined with Fenton process was also studied. Experimental results shows that three-dimensional fluid bed electrode reactor combined with Fenton process had better synergic effect, average 17.4% TOC removal rate was improved within an hour. It was found that TOC degradation in coking wastewater followed a pseudo-first-order reaction kinetic model. The optimum degradation efficiencies of TOC were up to 60% as pH3.4, 3.5 mM ofFe2+ andl.2-1.8ml/L H20 2 in 90min reaction period. Furthermore, the integrated process showed a rapid reaction performance at a low temperature within a short reaction time and remained high efficiencies for TOC removal. Overall, the integrated process was proved feasible for coking wastewater treatment in practical applications.IntroductionCoking wastewater is generated from coal coking, coal gas purification, and by-product recovery processes of coking, which is composed of phenolic compounds, heterocyclic compounds, polycyclic aromatic hydrocarbons, ammonia, cyanide, polycyclic nitrogen-containing aromatics, acyclic compounds, etc. Most of these constituents are refractory, poor biodegradability, toxic and carcinogenic['-31. Currently, coking wastewater is usually treated by different forms of A/O biological nitrogen removal process as the primary treatment process, but the aforementioned processes are not efficient enough to meet the requirements from the National Discharge Standard in China (GB13456-1992). According to the continuous requirement on improving environmental protection for coking industry (revised 2008), increasing wastewater utilization ratio and reducing discharge of effluent in the coke industry has to be implemented for cleaner production and sustainable development. Therefore, advanced technologies need to be developed to treat coking wastewater and reutilize the product as industrial cooling water, which would be one of the best choices to achieve zero discharge of wastewater and reduce water consumption per ton of steel [4-51 . In this study, three-dimensional fluidized bed electrode reactor combined with Fenton process was adopted to advanced treatment of coking wastewater, and the effects of operating conditions, including H2O 2 dosage, Fe2+ dosage, initial pH, and reaction time on TOC removal rate, were investigated. Meantime, study of kinetics of reaction was estimated."

Jan 1, 2013

By Jean Igor Margem., Lucas Barbosa de Souza Martins, Frederico Muylaert Margem, Sergio Neves Monteiro, Artur Camposo Pereira, Rômulo Leite Loiola

"The fibers extracted from the stem of the bamboo plant have been investigated as possible reinforcement composites due to their relatively high tensile strength. Although previous works have already been conducted about the mechanical properties, up to now a dimensional characterization of the distribution and the effect of diameter on the elastic modulus of bamboo fiber of the specimen dendrocalmus giganteus has not been performed. The aim of the present work was to statistically characterize the distribution of the diameter of a lot of bamboo fibers of that specimen. Based on this characterization, diameter intervals were set and the dependence of the Elastic Modulus (E) of theses fibers with a corresponding diameter was analyzed by the Weibull Method. The results indicated an inverse dependence, in which the highest Elastic Modulus were obtained for the thinnest fibers. Moreover, it was found that a mathematical hyperbolic relationship fit well this inverse correlation between the Elastic Modulus and the bamboo fibers diameters.IntroductionBamboo is a well known grass-type plant with a hard and stiff stem or culm that can reach, in some species, more than 10 cm in cross section diameter and stand several meters height. Owing to its low density, approximately 0.9 g/cm3, bamboo culms have been used in house construction from scaffoldings to panels. As an abundant natural resource in tropical and temperate regions, specially in Asia and South America, bamboo is also a substitute for wood and plastics in furniture and lightweight parts of automobile [1,2]. The cylindrical shape of the culm is, however, a limitation for its direct use in engineering systems. Consequently, research works have been conducted on bamboo fibers stripped off from the culm as reinforcement of polymer composites. [1-12]. According to Shin et al [3] bamboo fiber-epoxy laminates can be made into specific sizes and shapes, preserving the natural microstructural properties. These fiber composites overcome the limitation of the culm's cylindrical macrostructure. As a further advantage, Shin et al [3] indicated that cracking and bioerosion caused by insect pests is prevented."

Jan 1, 2013

By Hongli Wen, Guangkun Shen, Qiong Deng, Shoujian Huang, Min Gan, Xiaohui Fan

"Due to the low iron grade and high sulfur content, pyrite cinder is difficult to be directly used for iron-making. In this paper, technology of magnetic roasting -grinding and magnetic separation -acid leaching was put forward for reclamation of pyrite cinder. For pyrite cinder of TFe53.51%, S2.20 %, studies showed that good magnetic effect can be achieved at roasting temperature 650~7000, reducing atmosphere CO/(CO + C02) 10~20% and roasting time 10~30 minutes. In separation conditions of grinding size -0.045mm accounting for 96.09% and magnetic field intensity of 1240 GS, iron concentrate of TFe64.81 %, S0.18% and iron recovery rate 91.44% was achieved. Acid leaching was studied to strengthen desulfurization. Results showed that high-quality iron ore concentrate of TFe66.3 l %, S0.10% was obtained under the conditions of hydrochloric acid mass fraction of 5%, pulp density of30%, leaching temperature of70? and leaching time of2 hours.IntroductionPyrite cinder is produced as a by-product of sulfuric acid industry [1] Domestic production is more than 12 million tons every year and occupied area is over 10 million square meters [2,3]. The pyrite cinder outdoor not only pollutes air but also damages surrounding surface [4] It after treatment used for iron-making is an ideal reclamation approach for its rich iron which is commonly 40-60% [5]. But pyrite cinder gets low utilization for its low iron grade and high sulfur content in China [6]. Therefore, comprehensive utilization of pyrite cinder has profound significance to environmental protection and the development of domestic iron and steel industry."

Jan 1, 2013

By Takeshi Yoshikawa, Kazuki Morita, Kunitoshi Matsunaga

"In metallurgical grade silicon (MG-Si), most impurities mainly exist at the grain boundaries and distribute in silicon grains at extremely small contents. Grain boundary phases in MG-Si transform into liquid above the eutectic temperature, and migrate towards high temperature regions when heated under a temperature gradient. With the migration of all liquid phases in MG-Si to the surface, the impurity contents will be decreased less than their solubilities in principle.In the present work, the fundamental research was conducted to discuss the possibility for purification using the liquid phase migration technique. The purification limit was estimated by thermodynamic calculations, and metallic impurities were estimated to be effectively removed except for Fe and Al. The migration behavior of the liquid phase in the synthesized silicon substrate was investigated by unidirectional heating under infrared radiation at 1523-1548 K, and the proceeding of migration was confirmed. The migration velocity was 1.4--2.0xl0-7 mis, and found to be controlled by the liquid phase diffusion.IntroductionPhotovoltaic energy is one of promising energy resources in a sustainable society because of its inexhaustibility and cleanliness. Although the production and installation of solar cells have increased significantly during the last decade, the cost of solar cell installation is still high. To enable the widespread use of photovoltaics and for the photovoltaic electricity price to reach grid parity, a low-cost and abundant feedstock of solar grade silicon (SOG-Si) is essential. Recently, a modified Siemens process and a fluidized bed reactor process were developed to address the cost and energy issues associated with the conventional Siemens process. However, their cost reduction potential is limited because of the large energy consumption needed to convert silicon into gaseous compounds. Purification of silicon through metallurgical routes offers a promising way for producing SOG-Si from metallurgical grade silicon (MG-Si), because it enhances productivity and can also lower the process costs. Although several metallurgical processes such as directional solidification [l ], vacuum refining [2-4] and plasma oxidation [5-7], have been developed, processing times and refining efficiencies still have to be optimized."

Jan 1, 2013