Search Documents

By S. H. Amini

The effects of CaF2 and ilmenite on dissolution rate and diffusivity of CaO in calcium alumino-silicate based slag in a temperature range of 1500 ? 1600 ºC were studied by using the rotating disk/cylinder technique. The effect of rotation speed on the rate of dissolution in the base slag indicated that mass transfer in liquid slag played a significant role in controlling the dissolution. At a constant rotation speed, the effect of 5 wt% addition of fluxes tothe slag on the dissolution rate was investigated at various temperatures. While CaF2 had the highest effect, addition of ilmenite increased the rate of dissolution significantly. The diffusivity of lime in these slags was quantified using the dimensionless mass transfer correlations for rotating disk/cylinder in the melt. The diffusivity values were deduced using the data on dissolution rate and solubility of lime in the slags. The measured diffusivity in base slag at 1500 C was found to be about 1.32 10-5 cm2/s and increased to 3.07 10-5 cm2/s at 1600 °C. Addition of 5wt% CaF2 increased the diffusivity by a factor of 3 to 5, while 5wt% ilmenite increased the diffusivity by a factor of 2 to 3 in the temperature range of 1500 to 1600 ºC. The two examined fluxes reduced the activation energy of diffusion.

Jan 1, 2006

By Edgar Vidal

Beryllium metal and alloys have been crucial in the advancement of technologies in space exploration, transportation, national defense, communications, energy, safety and medicine, to name a few. Beryllium is one-third lighter than aluminum and six times stiffer than steel, with unique thermal properties. Demand for this metal is expected to continue to increase as new technologies emerge, hence its efficient and safe extraction needs to be addressed. Current extraction technologies are very complex and energy intensive, but at the same time yield excellent quality metal. In order to develop new or improve current extraction methods, a detailed analysis of current and past extraction technologies must be made. This work intends to compile and interpret most of the research, development and industrial practices used in the production of beryllium, and open the field for innovative extraction methods.

Jan 1, 2006

By Patrick R. Atkins

Energy issues will have increasing impacts on decision making in all facets of society over the next few decades. Industrial users of energy and producers of products that affect energy use must be fully aware of the implications of their processes and products on the energy situation. This paper describes a model that has been developed for the aluminum industry that allows scenarios to be evaluated to gain improved understanding of possible implications for our businesses. A brief overview of the model is provided.

Jan 1, 2006

By Hirokazu Narita

The extractability for Pd(II) using MOTDA and DHS and their durability against a mixed solution of HNO3 and HCl was investigated by solvent extraction and FT-IR measurements. Both MOTDA and DHS selectively extracted Pd(II) over Pt(IV) from 0.75 M HNO32.25 M HCl solutions. The extraction rate of Pd(II) with MOTDA was much greater than that with DHS. In the durability test, the extraction percentage of Pd(II) and the FT-IR spectra were measured using MOTDA and DHS after stirring with 0.75 M HNO32.25 M HCl solutions. The extraction percentage of Pd(II) with MOTDA hardly changed during the two-month stirring; however, that with DHS decreased with an increase in the stirring time. The FT-IR spectra showed the sulfoxide formation by the oxidation of the sulfide in DHS, but not in MOTDA. Consequently, it was found that MOTDA is more durable than DHS.

Jan 1, 2006

By Laila A. Guirguis

Impurities are removed from crude phosphoric acid (57.75% P2O5) with a mixture of low and high molecular weight alcohols, one of which is hydrophilic and the other is hydrophobic i.e. methanol and hexanol. In a single stage, the phosphate values segregate to the high molecular weight alcohol fraction and the impurities segregate to the low molecular weight alcohol fraction. The optimum ratio for the extraction is found to be 0.5 part methanol, one part impure acid and four parts hexanol where an extraction percent of more than 95% is achieved. Re-extraction of the phosphate value from the solvent is obtained by 6% phosphoric acid and the different factors affecting the re-extraction process have been studied. Finally, the purified acid is concentrated under reduced pressure and passed through activated carbon column, whereas the alcohols are re-circulated. The produced phosphoric acid was found to be in good match with the international specifications of food grade quality acid. A technological flow sheet is elucidated.

Jan 1, 2006

By Takayuki Ichikawa

Hydrogen storage properties of ballmilled mixtures composed of the hydrogenated nano-structured carbon (CnanoHx) and lithium hydride (LiH) were examined by thermal and optical spectroscopic analyses. LiH needs higher temperature than 600°C for hydrogen desorption even under vacuum condition, while CnanoHx, which was mechanochemically synthesized from graphite powder by ballmilling under hydrogen atmosphere, reveals hydrogen and hydrocarbons desorption in wide temperature range from 300 to 800°C. Nevertheless, the composite of CnanoHxand LiH prepared by ballmilling desorbs hydrogen in relatively lower temperature range from 150 to 450°C. These phenomena indicate that the thermally liberated hydrocarbon radicals immediately react with LiH and release hydrogen instead of hydrocarbons emission, because CnanoHx contains hydrocarbon groups at the edge of nano-meter sized graphenes, which are recognized as IR active C-H stretching mode, and LiH is well-known as an ionic crystal. Furthermore, it is of interest that a nanostructural feature persists in this composite even after annealing at 350°C, which shows excellent cycle properties as hydrogen storage media.

Jan 1, 2006

By V. A. Bryukvin

A hydroelectrochemical technology has been proposed and experimentally proven for processing metallic gold- and silver-containing concentrates on the basis of copper and copper alloys obtained as a result of preliminary physico-mechanical upgrading of electronic scrap. The proposed technology is based on hydroelectrochemical leaching of scrap using reversible electric current and diluted nitric acid solutions, containing complexing agents, permitting complete separation of gold from the nonferrous matrix without involving gold in the process, and dissolving copper, zinc, lead and tin virtually without any emission of nitrose gases.

Jan 1, 2006

By Yonggang Liu

Microstructure and precipitates in hot rolled low carbon steel sheet by CSP were investigated in this paper. It is pointed out the precipitates in low carbon steel sheet by CSP are different with that by traditional hot rolling. The bainites were found in CSP hot rolled steel sheet by TEM testing and these bainites could maintain in the sheets even after batch annealing. The selected area electron diffraction analyzing indicated that there were many CrB2BN and FeB4BN phases precipitated in hot rolled steel sheet and no AlN grains precipitated. The nitrides forming can limit AlN grains precipitating during the batch annealing processing, and this could do harm to the texture pipeline along orientation line forming with formed properties.

Jan 1, 2006

By Fumiatsu Sato

In recent years, an increasing number of urban soil contamination cases have been found during redevelopment of former factory sites. Hydroclassification technique, separating heavily contaminated fine soil particles from contaminated sites, is one of the economical remediation techniques for contaminated soil by heavy metals, but the separated fine soil particles are generally landfilled because of the difficulty in removing strongly adsorbed heavy metals on them. In the previous study, the authors have investigated the mechanism and the optimum condition of chlorination-volatilization technique to eliminate heavy metals from inorganic waste and found it was needed to heat up around 1273K. In this paper, a new remediation technique for lead contaminated fine soil particles is proposed. This technique is composed of chlorination and subsequent warm water extraction. In the chlorination step, water-insoluble lead complex is chlorinated to be water-soluble lead chloride without volatilization, by heating the soils with MgCl2-CaCl2-KCl salt mixture at relatively low temperature. By subsequent warm water extraction, lead chloride is leached out. Effects of chlorination conditions, such as time, temperature, composition of the salt and added salt ratio, on lead behavior were investigated. It was proved that lead concentration could be reduced below Japanese environmental standard.

Jan 1, 2006

By M. Kawakami

In the blast furnace, the reduction of iron oxide and gasification of coke occur simultaneously. It is well accepted that the gasification reaction controls the simultaneous reaction. Therefore, it is important to develop highly reactive carbonaceous materials. It is also known that the reaction is accelerated catalytically with the addition of some materials. In the present work, the catalytic effect of iron, nickel and CaO on the gasification of graphite and coke was examined. The catalytic effect of iron, nickel and CaO on the reaction rate of graphite was noticed The effect was larger at lower temperature. At 1373 K, the effect almost vanished. The effect was larger in the order of CaO, iron and nickel. The reaction rate of de-ashed coke increased by the addition of iron and nickel. The effect of iron was larger than that of nickel. The effect was larger at higher temperature, which was contrary to the case of graphite. The reactive surface area increased also by the addition. Therefore, the catalytic effect on reaction rate might be attributable to the increase in the reactive surface area.

Jan 1, 2006

By K. A. Lewandowski

Agglomeration of ore can be used to immobilize fine particles during heap leaching by agglomerating them into granules. Without agglomeration, the fine ore particles can migrate within the heap, clogging flow channels and producing large areas where access of solution to the ore is very poor. The benefits of agglomeration are well-known in gold heap leaching operations, which can be effectively agglomerated using binders such as Portland cement due to the alkaline leaching solutions used. However, agglomeration has not been very effective in the heap leaching of copper ores, because these ores require an acidic leaching solution. Acid destroys the effectiveness of most binders, causing the agglomerates to disintegrate as soon as the leaching solution is applied. In order to gain the benefits of agglomeration in copper heap leaching, an economical, acid-resistant binder is needed. The two issues that needed to be addressed were: 1) Lack of effective methods for evaluating binder acid resistance before performing expensive, time-consuming, full-scale heap leaching tests, and 2) The vast majority of known binders react poorly to acid conditions, and so a basis was needed for determining which binders are most likely to be acid-resistant. In this paper, the development of two new tests for evaluating binder acid resistance in the laboratory are described. The ?soak test? determines the degree to which agglomerates disintegrate and release fines on contact with acidic solution, measuring the relative quantities of fines released by agglomerates made with different binders under controlled conditions, and serves as a rapid means for comparing large numbers of binders. The ?percolation test? measures several different parameters to determine how a binder is likely to perform in heap leaching: 1) the degree of ?slump? and compaction of agglomerates as they are wetted by acidic solutions; 2) the hydraulic conductivity of the agglomerate bed; 3) the migration of fines through the bed as the solution flows through it; and 4) the quantity of liquid retained in the agglomerates after they are drained. Using these tests, a broad spectrum of binders were examined. Soak testing determined that the most acid-resistant binders were nonionic polymers. Five of these binders were further evaluated using percolation testing.

Jan 1, 2006

By Guy Deschênes

In spite of the wide use of lead compounds to enhance cyanidation of free milling sulphide-bearing gold ores, an industrial control method was only implemented four years ago. This study presents the results of the investigation that led to the development of the on-line control technology. Two free milling sulphide-bearing gold ores and high purity minerals were used to develop and test the concept. The first ore contains 2.8 g/t Au, 6.2% pyrrhotite, 2.1% pyrite 0.6 % arsenopyrite, 0.1% chalcopyrite and 0.1% organic carbon. The second ore contains 10.4 g/t Au, 3.2% pyrite, 0.8% pyrrhotite and 0.38% chalcopyrite. The first ore showed a much higher oxidation rate in the pre-leach than the second one and consumed seven times more cyanide. A relation between the formation of thiosulphate and thiocyanate and the additions of lead nitrate were quantified. The ?reducing power?, a titration with permanganate, predominantly determines the concentration of thiosulphate and thiocyanate in cyanide solution. The relation between the reducing power and the addition of lead nitrate at various concentrations of pyrrhotite and chalcopyrite in the ores was established, providing a monitor/control strategy for lead nitrate addition.

Jan 1, 2006

By P. N. Anyalebechi

The effects of solidification rate on the cast microstructures of aluminum alloys 6009 and 6016 have been investigated with directionally cooled laboratory-size ingots, at 0.2-10.1 K/s and 0.4- 23.1 K/s, respectively. These ranges of solidification rate are within those observed in commercial-size ingots. In both alloys, the average dendrite cell size and second phase particle size decreased with increase in average solidification rate and with a decrease in average local solidification time. However, at comparable solidification rates, the dendrite cells and second phase particles are finer in the shorter freezing range alloy 6009 than in the longer freezing range alloy 6016. This is provisionally attributed to the earlier formation of second phase intermetallics at higher temperatures during solidification and to the formation of greater amount of the relatively coarse plate-like ß -phase (Al9Fe2Si4) phases in alloy 6016. In general, in both alloys, the types and relative amounts of the second phase particles in both alloys are independent of solidification rate.

Jan 1, 2006

By Karel Verscheure

Hydrometallurgical zinc leach residue, EAF dust and other Zn-bearing by-products pose potentially serious environmental problems that threaten the sustainability of the operations. A pyrometallurgical process designed for treatment of such residues is the high-temperature submerged plasma Zn-fuming process. The successful operation of this process requires high Zn fuming rates whilst retaining vessel integrity through stable freeze-lining. A Zn-fuming model has been developed and used to systematically investigate a range of operating scenarios and to identify potential fluxing parameters such as CaO/SiO2, Fe/SiO2, MgO/feed-ratios in the input and fluxing additions of dolomite for maximum fuming rates and stable freeze-lining.

Jan 1, 2006

By Tapio Ahokainen

Commercial modeling software and increasingly efficient computers enable today computational fluid dynamics (CFD) to be used as a tool for a more comprehensive understanding of the flash smelting and flash converting processes. CFD modeling can be used for design purposes in many technological areas, but some relevant physical and chemical phenomena are still missing in the commercial CFD solver packages. Therefore, Outokumpu has developed several subroutines for solvers to describe analytically the phenomena in the flash smelting environment. CFD sub-models of the copper concentrate and matte combustion, the particle-particle-wall interactions and for more accurate radiation properties of the gas-particle suspension are needed to ensure reliability of numerical simulations on the flash smelting and converting vessels. Several basic combustion phenomena can be modeled with a number of commercial solver packages, but own models for combustion must be included in the case of sulfides as the feed. Mathematical models for copper concentrate and solid matte combustion have been developed during the last decade. They calculate compositions of the particles and temperature, based on extensive experimental research work in laboratory scale furnaces with validated kinetic parameters and temperature measurements of reacting particles. Inside and near the concentrate burner, the standard particle tracking methods do not include the particle-particle interactions and the particle-wall interaction is too much simplified to describe properly the particle collisions with the distribution cone. Therefore, additional models for the particle-particle as well as particle-wall interactions have been written and implemented. For thermal radiation, models for the emissivity of a gas mixture and for calculating the particle absorption and scattering coefficients have been developed and tested. In addition, the advanced radiation model can be used i.e. in the enhanced simulation of off-gas cooling in the heat recovery boiler area of the flash smelter.

Jan 1, 2006

By L. Béjar-Gómez

The aim of this research work is to study and characterize precipitates in structural microalloyed steel by transmission electron microscopy and analysis by high resolution (HRTEM). Microalloyed steel with titanium was produced by casting in an electrical induction oven of 25 Kg. capacity. Carbon content in steel was less than 0.1 % and titanium content of 0.04%. Steel was processed thermomechanically; reheated to 1250ºC and hot rolled on a laboratory mill to a 13.0 mm thick plate with a finish rolling temperature of 900ºC and thickness reduction of 80%. Analysis by High Resolution Transmission Electron Microscopy (HRTEM) identified precipitates in the steel; type and morphology. Energy Dispersive Spectroscopy (EDS) analysis was applied to obtain the chemical composition of precipitates and the matrix. STEM-EDS analysis was also applied to obtain the element profile of precipitates. The results showed the presence of carbonitride precipitates of titanium, Ti (CN), with a circular morphology and size of 10 nm and less.

Jan 1, 2006

By Vinod K. Namilakonda

In situ synthesis of discontinuously reinforced aluminum alloy metal matrix composites was investigated. Aluminum alloy (A356: Al-7 wt% Si) was reinforced with dispersed AlN particles. Thermodynamic calculations were made for the composition determination of various phases formed during bubbling of NH3 gas into the Al alloy melts in the temperature range 1173-1473 K. Experiments were carried out for in situ production of AlN particles with the reaction between Al melt and NH3 gas in high temperature resistance furnace at 1473 K. The products were characterized using SEM, EDS and XRD. Effect of bubbling time of NH3 gas on the AlN formed in the composites was studied. The amount of AlN reinforcement in the Al alloy composites was observed to be in the range of 5 to 35 wt%. Good agreement was observed between the experimental and thermodynamic calculated data on the composition of AlN in Al alloy composites.

Jan 1, 2006

By N. Solak

CrN, TiN and Ti-B-N coatings were deposited onto H13 hot-working tool steel and alumina substrates by arc-PVD. The coatings were characterized with respect to their mechanical and structural properties. Oxidation behavior of the coatings on alumina substrates was investigated by TG/DTA. Samples coated on H13 substrates were oxidized in a tube furnace under atmospheric conditions at specific temperatures determined from TG/DTA tests of the same coatings deposited on alumina substrates. The oxide scale morphology was characterized by scanning electron microscopy and X-ray diffraction. Oxide scale thickness change and TG data were used to calculate oxidation reaction activation energies. It was determined that boron addition into TiN coating improves not only mechanical properties but also oxidation resistance. Depending on the substrate material different oxidation activation energy values for the TiN and Ti-B-N coatings were determined revealing the importance of film morphology on oxidation resistance.

Jan 1, 2006

By Renaud Metz

The DOPA process (Direct Oxidation of a Precursor Alloy) was used to prepare ceramic powders based on doped SnO2 and ZnO. The DOPA process consists essentially in the direct oxidation of a homogeneous precursor alloy. A unique advantage of this process is its rather benign environmental impact since no dangerous reactants are used and no harmful by-products are generated. Only oxygen and the alloy metals participate on the chemical reaction to produce the multi-component oxide. Homogeneous alloys of niobium, cobalt and chromium doped tin have been prepared. The molten metal alloy is atomised in air using a double fluid nozzle to produce metallic powders. A subsequent thermal treatment is carried out to fully oxidise the sprayed metal alloy powders. These raw powders are used to prepare a ceramic powder through a mill homogenisation and atomisation process. The ceramic powder is then uniaxially compacted in disc shape and sintered in an oxidising atmosphere. The resulting sintered bodies are metallised on their flat faces and the cylindrical surface is passivated using lead free glass enamel. These ceramics present excellent semiconducting properties with non-linear (non-ohmic) characteristics. The DOPA process is found to be an attractive procedure to obtain ceramic powders for the preparation of SnO2 varistors.

Jan 1, 2006

By F. A. Myzenkov

The technology developed by the authors uses new methods for raw material smelting in electric furnaces, a new autogenous method and apparatus for subliming smelting for antimony trioxide production and separation of antimony and gold. Concentrate produced from the ore deposits in Yakutia has the following average contents of main constituents, % by weight: 29.4 Sb, 1.2 Fe, 13.1 S, 40.0 SiO2, 0.2 As, 2.6 CaO and 45 g/t of Au. Unlike the technology used abroad a new autogenous method makes it possible to increase considerably specific capacity and reduce gold losses with antimony trioxide by several times. At the same time mineralogical composition of trioxide has improved considerably ? it has mainly a cubic base with prevalence of senarmontite. The content of a main component (Sb2O3) in the final product has increased from 99.0% up to 99.6% which means better quality and makes it suitable for use in special technologies. Despite a lower antimony content of the concentrate (29.4% as compared with over 33% as common in the world practice), an antimony recovery of 85.3% into a commercial-grade product has been achieved, as well as a gold recovery of 96.65% into a gold-antimony alloy. The technology for processing gold-antimony materials developed and introduced at the Ryaztsvetmet plant is unique in the world with respect to gold recoveries.