By A. Totani, S. Nakajima, H. Okazaki

The phase diagram for the SnTe-SnSe system has been studied in the temperature range from 300° to 900°C by differential thermal and quenching techniques. The X-ray measurements were made on quenched specimens. High-temperature diffraction was also made to study the phase transition in SnSe. The system is proved to be of a eutectic type in which no intermetallic compound exists. The eutectic point is at the composition SnTeo.55 Seo.45. the eutectic temperature being 755°C. Solid solubility limits are SnTeo.6Seo.r and SnT eo. 3s Seo.6s at the eutectic temperature, and change almost linearly to SnTeo.aaSeo.lz and SnTeo.18 Seo.az as temperature decreases to 300°C. It was shown that the SnSe phase has a phase transition of the second order at about 540°C and that the transition temperature decreases with increase of the SnTe content. THERMOELECTRIC properties of tin telluride (SnTe) and tin selenide (SnSe) have been studied extensively in recent years. The variation of physical properties with composition could be of interest if these compounds form an appreciable crystalline solution. The purpose of present investigation is to confirm the formation of crystalline solution or intermetallic compound, if any, and to establish the phase diagram for this system. The crystal structure of SnTe is NaCl type with a cubic unit cell1 (a = 6.313A). The crystal of SnSe having an orthorh2mbic unit cellz (a = 11.496, b = 4.1510, and c = 4.4437A) is isomorphous with tin sulfide (SnS) which has a distorted sodium chloride structure. It has been known that SnSe has a phase at at 540°C; the transition has been assumed to be of the second order. As far as we know, only two studies on the SnTe-SnSe pseudobinary system have been reported. The conclusion obtained in these papers is that, in the composition regions near SnTe and SnSe, the system forms a crystalline solution of the SnTe structure and the SnSe structure, respectively, and that, in the intermediate region, both phases coexist. However, neither the variation of the solid solubility vs the temperature nor the liquidus and solidus were investigated. Hence present writers have attempted to determine the phase diagram of the system by differential thermal analysis (D.T.A.) and X-ray diffraction. EXPERIMENTAL Sample Preparation. Starting materials, SnTe and SnSe, were prepared by the direct fusion of commercially available high-purity (99.999 pct) elements. Stoichiometric amounts of each couple Sn-Te or Sn-Se were weighed into a clear fused silica ampule. After evacuation to a pressure below 10-3 mm Hg, the am- pule was sealed, and annealed at 900°C for 5 hr. The melt was quenched in water. X-ray analysis confirmed the formation of a single phase of SnTe or SnSe. The other samples, SnTel-,Sex were synthesized from these SnTe and SnSe by mixing them in the required ratio, followed by annealing at 900°C and quenching. These samples were used directly for D.T.A. For X-ray measurements, samples were annealed at 700°, 600°, or 500°C for 100 hr or at 300°C for 150 hr, and then quenched in water. It was found that the lattice constants of the SnTe phase annealed for 150 hr at temperatures above 500°C did not differ from those annealed for 100 hr at the same temperatures. However the X-ray phase analysis showed that at 300°C the annealing for 150 hr was necessary to attain a true equilibrium state. D.T.A. The solid-liquid equilibrium temperature was determined from D.T.A. measurements. The sample was sealed in an evacuated silica tube and molybdenum powders sealed in an another tube were used as a reference material. The sample and the reference tube were placed in a nickel block and were heated from room temperature to 900°C at a rate of 3°C per min and then cooled down at the same rate to 600°C. Thermocouples for these measurements were Pt-Pt. Rh (10 pct) and the error of temperature measurements was within + l0C. D.T.A. curves were obtained on a two-pen recorder and an automatic controller (PID type) was used for the program of heating and cooling. When temperature reaches the solidus from the low-temperature side, there appears an endothermic peak. The solidus temperature was determined by extrapolation of the straight portion of the starting flank of this peak to the base line. In a similar way, the liquidus temperature was determined from an exothermic peak on D.T.A. cooling curve. In the case of supercooling, if any, its degree can be estimated from the magnitude of the abrupt temperature rise. X-Ray . X-ray powder patterns were taken by a diffractometer using CuK, radiation. Since the SnSe crystal is cleaved easily, the powders become flaky when SnSe-rich samples are ground in an agate

Jan 1, 1969

By M. T. Hepworth, A. K. Stewart

Iron containing 0.1 pct A1 and -0.9 pct P by weight was internally oxidized in the temperature range 900° to 1300° C, where the bcc structure is stabilized by phosphorous. By measuring the depth of penetration of oxygen with time in an internally oxidized zone for an imposed surface oxygen potential, oxygen permeability was determined. The dgfusion coefficient of oxygen in iron was then calculated using known solubility data, yielding the expression: where Do is the diffusion coefficient of oxygen in bcc iron in sq cm per sec and T is temperature in OK. RECENTLY Hepworth, Smith, and Turkdoganl measured the diffusivity of oxygen in bcc iron and reported the temperature dependence of diffusivity from data determined in the a, and 6 temperature ranges. Subsequently Swisher and Turkdogan' have measured the diffusivity of oxygen in fcc iron. Internal oxidation techniques were employed by these investigators and in this current study. The analysis of this technique is developed by wagner3 (presented in English by Hauffe4 and Rapp 5). In this present study bcc iron stabilized by phosphorous was used to determine oxygen diffusivity in the temperature range 900° to 1300°C. Meijerin 6 has studied oxygen permeability in this temperature range using bcc iron stabilized with 5 pct Sn. Other inves- tigators who have studied oxygen permeability in bcc iron at other temperatures are Schenck et al., 7 Bohen-kamp and Engell, 8 and Bradford. EXPERIMENTAL Electrolytic iron of 99.99 pct purity was alloyed to contain 0.897 pct P and 0.093 pct Al. The maximum weight percent phosphorous required to stabilize bcc iron between 910" and 1392°C is 0.51 pct as determined by Haughton,10 0.42 pct by Roquet and jegaden," and 0.58 pct by vogel,12 with the latter value preferred by Hansen.13 Microprobe analysis indicated that there was no segregation of the phosphorous either before or after permeability studies; therefore, the quantity of phosphorous added was assumed to be sufficient to stabilize the bcc structure. Furthermore, the permeability results of studies on this alloy agreed substantially with interpolated values from previous data on bcc iron.' An ingot of the Fe-P-A1 alloy was hot-rolled to a l-in.-thick slab. Specimens were machined to dimensions: 13/8 by $ by 1/4 in. The experimental apparatus and procedure used have been described before.' A constant oxygen potential was established by passing argon and hydrogen through a column of oxalic acid dihydrate, which has a water vapor pressure which is well-known as a function of temperature. Slab specimens were exposed to a gas mixture sufficiently lean in oxygen to prevent the formation of a surface oxide for predetermined temperature for selected times. The specimens were then quenched, sectioned, and examined metallo-graphically. All quenched specimens were iron-plated to provide protection from the outside sample edge during polishing. Fig. 1 shows a typical microstruc-ture for a specimen oxidized at 953°C for 48.00 hr at a water vapor-to-hydrogen pressure ratio of 0.20. DISCUSSION AND RESULTS The following equation was derived by Hepworth et al.' from Wagner's kinetic expressions for internal oxidation:

Jan 1, 1969

By K. E. Manchester, A. H. Clark

Hall measurements have been made on three groups of silicon samples, which were implanted with boron, aluininunz, and phosphorus ions. Boron and phosphorus implants show essentially bulk properties when annealed under previously determined conditions, i.e., 15 min at 80O°C for boron and 10 mirz at 600°C for phosphorus. Bulk properties were also observed in alu?rrilzum-implanted samples when ion concentrations were below 1015 cm-'; however, strange low- terrzperalure behavior and a falloff in cavrier concenlralion was observed for sarnples with ion concenlration abozle loL5 ern-'. This can be attributed to solid-solubility effects since the average bulk concentration f0.r the sample exhibiting bulk properties was below the reported solubility limit for aluminum, while the other samples were above the limit. A detailed study of the annealirzg process indicates that mobilities reach bulk c~alues in phosphorus implants at 250DC, in alutninurn ivnplanls a1 500°C, and in boron implants at 700°C. A simple rnodel has been proposed to fit the annealing data. THE technique of semiconductor doping by direct injection of energetic ions is being actively investigated at this Center. Previously published results from this laboratory have been concerned with the investigation of implanted profiles in silicon and the electrical properties of the resultant p-n structures.1'2 Diode properties have been reported for junctions produced by implantation of boron ions and aluminum ions in n-type silicon and phosphorus ions in p-type silicon. Reverse current characteristics, as well as electron diffraction data, have indicated that the damage to the structure produced by the energetic ions during the stopping process can be minimized by a gentle anneal. The time-temperature conditions for this process have been determined by sheet resistivity studies.3 Electrical profiles of implanted phosphorus ions which have been determined by a differential sheet conductivity technique are based on the assumption that the carrier mobilities and activation energies for ionization are the same as in bulk silicon. These assumptions have been substantiated experimentally by measurement of Hall constants and resistivities of these implanted structures and the results are presented herein. After establishing the bulk property equivalence of the annealed layers, a more detailed examination of the annealing process was undertaken. The sheet resistivity technique initially used to determine anneal conditions has been broadened to include Hall constants and mobility behavior with anneal conditions. PROCEDURE The three groups of samples prepared for Hall measurements were implanted with mass-separated beams of boron, aluminum, and phosphorus ions. Ion concentrations are equivalent surface concentration and they have been determined from beam current measurements during implantation. Implant conditions for the samples are shown in Table I. In all cases, the samples had previously been angle-lapped on one edge and the junction delineated with an HF-copper sulfate solution. The surfaces of the implanted regions of the samples were exposed to the delineating solution and in the case of the "n"-type phosphorus-implanted areas it was later discovered that a finite amount of surface could be etched by this solution. This is discussed in the section on results. The implanted samples were ultrasonically cut into the conventional six-probe configuration shown in Fig. l.* In the annealing studies, for which the meas- urements were taken at room temperature, the sample holder was a Bakelite jig incorporating tungsten mechanical probes. The other measurements were taken using a conventional liquid-nitrogen cryostat, in which the temperature could be varied from 77" to about 400°K. For these measurements, 10-mil aluminum dots were evaporated onto the samples and alloyed with the silicon at 530°C for 15 min. The samples were then mounted in flat-packs, and gold wires were bonded to the aluminum dots. The electrical measurements were made with either a Leeds & Northrup K-5 Potentiometer, a Keithley 147 Nanovolt Null Detector, or a Keithley 601 Electrometer. No external bias was applied to the substrate. There is an inherent self-biasing arrangement at one or the other of the current contacts (depending upon the polarity), and this suffices to limit the current flow to the implanted layer. The magnetic field was generated by an A. D. Little electromagnet. Except for occasional checks of linearity of the Hall voltage with

Jan 1, 1969

By Mary A. Barrett

The Bureau of Mines conducted a laboratory-scale investigation of grouting mixtures containing iron or aluminum to determine the existence of health or explosion hazards, due respectively to oxygen depletion or hydrogen emission. Mixtures containing iron created an oxygen deficiency in less than 24 hours and released small amounts of hydrogen; a health hazard could occur but only under extremely unfavorable conditions. Mixtures containing aluminum released little hydrogen and consumed little oxygen; however, if improper on-site mixing yielded high local metallic aluminum concentrations, enough hydrogen might be released to produce an explosive atmosphere in a confined space.

Jan 1, 1969

By David J. T. Carson

"The metalliferous deposits of Vancouver Island have generally been assigned to the Mesozoic ""Coast Range Orogeny."" However, a metallogenic study by the writer has revealed that several important classes are early or middle Tertiary. Included are porphyry coppers, and gold-quartz, arsenic and copper-arsenic veins.The porphyry coppers and many gold-quartz veins are within and adjacent to Oligocene-Eocene quartz diorite intrusive complexes. Arsenic and copper-arsenic veins have a close spatial relationship to sills and laccoliths of Oligocene dacite porphyry which intrude the late Cretaceous Nanaimo Group.Other deposits of demonstrable Tertiary age include a molybdenum stockwork related to a relatively potassic Eocene plug and a few small copper-skarn occurrences. Some copper stockworks and a mercury deposit are probably also Tertiary.The copper deposits of previously recognized Tertiary age are those of the Sooke area that occur in Eocene basalts and Oligocene gabbros."

Jan 1, 1969

By H. I. Aaronson, C. Laird

Cold rolling by 50 pct a A1-4 pct Cu alloy containing many 0' plates has been found to accelerate markedly the transformation of 8' to 0 upon further aging. Although the basic mechanism of this transformation remains unchanged by plastic deformation, the nuclea-tion kinetics of 8 become appreciably more rapid and also less dependent upon temperature. Particularly at lower aging temperatures, rounded idiomorphs replace several faceted rnorphologfes. The rates of growth of 9 idiomorphs in deformed specimens aged at 300°C are appreciably more rapid than simple volume diffusion control allows. This observation is shown to be explained by an excess vacancy, rather than by a dislocation Piping mechanism of growth. ThE rather complex phenomenology of the 8' —8 transformation in Al-Cu alloys has been recently elucidated in considerable detail by means of transmission electron microscopy.'-4 This technique was also employed in the present investigation in order to examine the effects of plastic deformation upon the transformation of 8' to 8. The mechanism of the transformation in undeformed Al-Cu alloys has been established as the following sequence of events.1"4 The first step is the nucleation of 9 at (Y:8' boundaries. Nucleation of a 0 crystal takes place, however, at only a very small proportion of the 8' plates present. Each 0 crystal simultaneously consumes the host 8' plate and the a! in the immediate vicinity, with growth into a being the rate-controlling process. The remaining 8' plates are then dissolved as they fall under the concentration shadow of the growing 8 crystals. The evidence on the effects of plastic deformation upon these processes is intriguing, but much less detailed. The careful X-ray studies of Graf and Guinier have shown that the aging times required to form detectable amounts of 8' and 8 are reduced by prior cold working. Thomas and Nutting confirmed these results by replication electron microscopy. Nile-shwar,* on the other hand, reported that creep deformation decreases the rate of formation of 0. While this difference may have been caused by the use of concurrent rather than successive deformation and ag- ing, the X-ray technique which he used was able to monitor only the 0 phase. It is thus possible that the times needed to form 8' were increased moreg than the kinetics of 8' — 8 transformation were accelerated. At 90 pct deformation by cold rolling, Graf and Guinier found that the usual 0' —0 8 sequence is reversed: 0 forms first. von Heimendahl 10 confirmed this result with transmission electron microscopy. Pollard and Nutting, 11 and more recently Driver and Barrand, 9 having used the same technique, report that 9 also forms first during creep deformation. In the present study, the maximum amount of deformation was limited to 50 pct reduction by cold rolling in order to insure that 8 formed principally by the decomposition of . I) EXPERIMENTAL PROCEDURES This investigation was conducted on an Al- 3.93 pct Cu alloy, prepared as previously described. 4 Morphological and crystallographic effects of plastic deformation were studied in specimens annealed 6 hr at 548°C, quenched, and then aged for either 3 or 8 hr at 250°C to form large numbers of 0' plates. After cold rolling to a 50 pct reduction in thickness, the

Jan 1, 1969

Jan 1, 1969

By Paul Soros

The Conneaut, Ohio, terminal of the Bessemer & Lake Erie Railroad was the first rail-to-ground-to-water coal terminal on the Great Lakes. Compared to the traditional method of holding coal in railroad cars at the ports for dumping their contents into vessels, it provided for: a. Immediate train turn-around independently of vessel arrivals. b. Winter storage of coal at the port, permitting year round shipment by the mines and year round operation of the railroad.

Jan 1, 1969

By Klaus Schonert

The elements of a mill matrix and the classifier matrix de- scribing the grinding process depend on operating conditions, especially on the feed rate. Relationships between the matrix elements and the feed rate have a great influence on the stability of a closed circuit and its optimum point. These problems have been studied by means of computer simulation and different kinds of classifier characteristics have been considered. A circuit with a cross stream classifier has only a limited range where stable operation condition can be attained. Beyond the stable limit, the recirculation ratio increases rapidly and there is no correlation between feed rate of the circuit and feed rate of the mill. In comparison, a spiral stream classifier gives a wide range of stable operation. The recirculation ratio can be greater than in the case of the cross stream classifier if the feed rate is small. The results of the simulation provide a better understanding of the real behavior of closed circuit grinding.

Jan 1, 1969

Radioisotope X-ray and neutron techniques of analysis can be used for the determination of a wide range of elements in minerals. The most important applications of these techniques to the mineral industry are for on-stream analysis of slurries and solids, and for geological assay. The radioisotope X-ray techniques are the more developed ones and two installations for on-stream analysis are in routine use in mineral processing plants in Australia. Neutron techniques are being developed, and should prove valuable for geological assay of large numbers of mineral samples, for borehole logging, and for specific on-stream analysis when the cost of the equipment is warranted.

Jan 1, 1969

Jan 1, 1969

By John T. Dickman, Ralph E. O’Dette

Chemical Abstracts Service (CAS) is in the process of evolving a computer-based information system which will process all of the material selected for abstracting in the area of chemistry and chemical engineering and its related fields such as the earth sciences and technologies. This system is already operational to some extent and is expected to be fully utilized by 1971. The objective of CAS is to make chemical and related information more readily available, more usable and more used. Chemical Abstracts handle some 5000 abstracts weekly from 13, 000 journals and patents from 25 nations. These cover all of the 80 CA subject sections which relate to chemistry and also extend into areas of interest to geologists, mineralogists, and mining engineers. In this way, CAS fulfills its objective of complete coverage of its major fields, informative abstracting, and indexing to maximum specificity. The concept of a computer-based information system is that of a single machine-language data base into which the results of intellectual analysis of the literature are entered and from which computer programs produce a variety of publications and services applicable to the needs of a wide range of users.

Jan 1, 1969

By Neil H. Bostick

This research, sponsored at Stanford Research Institute by the Grand Junction Operations Office of the U.S, Atomic Energy Commission, was an outgrowth of the concern that presently-known ore reserves may be inadequate to meet the projected demands of nuclear power reactors. The original program at SRI was to design a comprehensive geological information system and use it to store and analyze the very great quantity of data needed to estimate uranium ore reserves. Study of the problem showed that it could be solved only by use of modern electronic data processing techniques, so such a comprehensive system was designed and tested. The system test was satisfactory, but input lead time and total expense were shown to be too great for the system to be practicable for the AEC under present circumstances. Thus, based on results of the earlier research, a specialized and simplified procedure for predicting approximate uranium ore reserves was devised. The prediction is based on general geology of specific area cells of the earth, in order to provide complete volume coverage; the strata in these ores are evaluated for uranium ore favorability on the basis of a few selected criteria in order to allow rapid data input. Since the bulk of U.S. reserves are in clastic host rocks only such strata are considered in this work. This paper describes the structure and some details of the resource system and how it was tested in rn area of the western United States.

Jan 1, 1969

By E. L. Burwell

Preliminary results of an in situ oil shale retorting experiment conducted by the Bureau of Mines in a shallow bed of Green River oil shale at Rock Springs, Sweetwater County, Wyo., are described. Eleven wells were drilled into a 20-ft-thick section of the shale lying between 68 and 88 It deep, and attempts were made to connect the wells through the shale with a fracture system created by application of high-voltage electricity (electro-linking), hydraulic fracturing, and explosive fracturing. Ignition of the shale through the central well was easily achieved with a propane burner, and shale oil began to collect in three wells within 3 hours. Propane injection was discontinued after 7 days, and combustion continues, although attempts to control the direction of the combustion front have been unsuccessful. Production rates as high as 4 ½ barrels of nil per day have been recorded, but too little is known about underground conditions to permit an estimate of recovery efficiency at this time.

Jan 1, 1969

By M. J. Young, C. A. Aird

"The Gem molybdenum prospect is situated at the head-waters of Clear creek, between the Fraser river and Harrison lake, about 30 miles north of• Harrison Hot Springs, B.C. Clear creek follows a deeply eroded fault zone southwesterly through the center of the claim group. Elevations range from 2,000 feet in the creek bed up the steep slopes flanking the creek to a height of 5,500 feet. The property lies within an area underlain by schists and gneisses which strike from north to west in a broad fold plunging steeply to the northeast. This metamorphic complex has been invaded by numerous bodies of grano-diorite, much of which is gneissic. A granite plug, roughly 2,400 by 4,000 feet in size, has intruded this broad fold just west of Clear creek and encloses a circular breccia pipe 1,500 feet in diameter. In the breccia pipe, fragments of metamorphic rocks, granite and quartz monzonite porphyry are firmly cemented in a matrix of quartz monzonite porphyry. All the above rocks are cut by numerous fractures filled by vuggy quartz veins, many of which contain molybdenite. Attentien was first drawn to the area by a quartz vein, 18 inches in width, known as the Gem vein, which consists of several laminated bands of quartz and molybdenite. Since 1964, exploration efforts have been directed toward attempting to outline a large, low-grade type of molybdenum deposit."

Jan 1, 1969

By B. V. P. Rao, H. L. Lovell, G. Simkovich

In the study described here, flotation tests were conducted on pure CaF2, on CaF2 doped at several concentration levels with either NaF or YF3, and on natural fluorite samples containing various amounts of impurities in an effort to extend previous knowledge of the influence of crystalline point imperfections on the flotation properties of solids. The results of these tests showed that although recoveries generally decreased as impurities increased, the differences in recovery were not nearly as striking as those detected in earlier experiments. A number of experimentalists have shown an interest in the way in which crystalline point imperfections affect the flotation properties of solids. As long ago as 1953, Welch hypothesized that it might be possible to control surface imperfections and thereby also control the flotation of solids.' A few years later, in some rather extensive work, Plaksin and his coworkers varied the surface imperfections of a number of compounds by oxidation or reduction processes and found that significant variations in flotation properties resulted.2-4 More recently, Simkovich showed that the recovery of both AgCl and PbS could be markedly varied by adding solid-solution impurities, which acted as doping agents, to these compounds.5 Then Mular studied the flotation of ZnO as a function of the doping agents Al2O3 and Li2O.6 Once again, it was found that these impurities, even in very low concentrations, had profound effects upon flotation recoveries. From an imperfection point of view, the defect structures of the compounds tested previously are as follows:7 PbS — amphoteric semiconductor with a Frenkel-type defect structure in the cation sub-lattice.8 AgCl - ionic conductor-Frenkel type defect structure? ZnO — n-type semiconductor, zinc ion interstitials and quasi-free electrons.10 All of these works undoubtedly bear some relation to the findings that the flotation properties of seemingly identical minerals from different ore deposits often exhibit extreme variation in flotation behavior, i.e., that small amounts of analytically undetectable impurities often have a great influence upon flotation

Jan 1, 1969

By Phillip E. Deering, Robert M. Cox

A model pillar study was conducted in which the engineering principles of dimensional analysis were applied to the problem of coal mine pillar design. The paper reviews the theory of similitude as applied to the model pillar study conducted in the investigation. An example solution of a design problem is included to indicate how the results of the study may be used as a first approximation in the design of coal mine pillars. The design of mine pillars for adequate support with minimum loss of valuable raw materials has always presented a problem to the mining engineer. Most often, for lack of a better method, past practice has influenced the design of new mine pillars. This process has always left doubt as to the safety factor of the pillars. The work presented in this paper is an initial attempt toward adapting the engineering principles of dimensional analysis to the problem of pillar design in underground mines. The use of the dimensional analysis technique is advantageous because all the variables associated with the problem are considered, and by systematic analysis the relative influence of each variable is determined. The model material utilized in this study was taken from the Helena seam of the Cahaba coal field located in central Alabama. The research study was sponsored by The Southern Electric Generating Co. as part of an over-all rock mechanics investigation of the Helena seam area. THEORY OF SIMILITUDE Model analysis is used extensively in engineering today, particularly in the solution of design problems that defy the classical methods of analysis. Such problems arise when materials with a nonlinear stress-strain relationship are involved, when geo- metric boundaries are difficult to define in simple form, when strains become large, or when partial failure occurs. All of these difficulties usually exist in pillar design problems. Those principles which underlie proper design and construction of models, and the interpretation of test results, comprise the theory of similitude. That is, the theory of similitude includes a consideration of the conditions under which the behavior of two separate entities or systems will be similar, and the techniques of accurately predicting behavior of one from observation of the other. The theory of similitude may be developed by dimensional analysis. Dimensional analysis, as a powerful analytical tool, is developed from a consideration of the dimensions in which each of the important quantities involved in a phenomenon is expressed. It is based on two axioms: 1) Absolute numerical equality of quantities may exist only when the quantities are similar qualitatively. 2) The ratio of the magnitudes of two like quantities are dependent on the units used in their measurement, provided that the same units are used for evaluating each. Dimensional analysis, developed from these two axioms, differs from other types of analysis in that it is based solely on the relationships that must exist among the pertinent variables because of their dimensions, rather than on the relationship of natural laws. In itself, dimensional analysis ~rovides qualitative, rather than quantitative relationships, but when it is combined with experimental procedures, it may be made to supply quantitative results and accurate prediction equations. APPLICATION OF THEORY The design of an adequate mine pillar requires the determination of a design equation and the selection of a dimensional system with which to work. Since force plays an important part in the design of mine support, the FLT (force, length, time) system has been used. The factors involved in the dimensional analysis of mine pillars and their dimensions are: A = cross-sectional area L Cp = design strength FL- E, = tangent modulus of elasticity FL

Jan 1, 1969

Very little has been written about the discovery and early history of prospecting of ironstone deposits in the Iron Knob-Middleback Range area of South Australia, the main source of supply of ironstone (hematite) for the Australian steel industry, and scanty though the record is, much of it is wrong or misleading.With the help of several people, to whom acknowledgement is made at the end of the paper, the writer has unravelled some of the story, but not the whole story. It is hoped that publication of this paper will stimulate interest in others, who may be able to supplement this account from family records, from the files of newspapers, or from archives.

Jan 1, 1969

By John W. King

reserves are exploring to increase them.. Uranium exploration projects are known to be active or planned also in Guayana, Colombia, Ecuador, Peru, Chile, Bolivia, and Uruguay in South America; in the UAR, Nigeria, Angola, Mozambique, Malawi, Kenya, and Somali in Africa; and in Greece, Iran, Pakistan., Indonesia, and New Zealand. The above list, to which several might be added makes a total of at least 43 nations actively interested in exploration for nuclear raw materials. As we consider the distribution of the world's uranium resources, it is interesting to note that roughly one third of the total occurs in deposits that are economically dependant upon another product. The very large reserves of South Africa could not be produced for uranium alone, but gold has carried a sufficient part of the total cost that uranium can be recovered profitably. Approximately 40 percent of the US reserves, or 120,000 tons, are estimated as by-product recovery from porphyry copper and phosphate operations, but these reserves are not presently in production. The remaining two thirds of the world's uranium reserves have been sought, developed, and produced primarily for their uranium content. Those deposits are estimated to contain 613,000 tons of uranium oxide recoverable at less than $10 per pound. Nearly half of that uranium occurs in unmetamorphosed sandstone hosts, mostly of late Phanerozoic age--the Colorado Plateau type. About 30 percent is contained in the quartz pebble conglomerates of southern Ontario, Canada, and 20 percent is in magmatic-related deposits--veins, contact deposits, mineralized breccias, etc.

Jan 1, 1969

By Goodman, Richard E.

A complete rational analysis for design of excavation slopes and loaded rock masses is a desirable but perhaps unattainable goal. Irregular external and internal boundary conditions, poor understanding of failure criteria for large masses of rock, capricious material properties, and the importance of indeterminate forces and inaccessible and virtually un- sampleable rock defects emphasize the importance of experience in this aspect of rock engineering. The experience must be correlated with geological factors. In certain regions the accumulation of such experience through the observation of existing rock slopes in various formations constitutes an important aspect of studies for design of rock excavations.

Jan 1, 1969