By J. W. Downey, A. E. Dwight, R. A. Conner

In a previous paper' we have reported the existence of a number of AB2 Laves phases in which A is a member of the scandium group (including the 1an-

Jan 1, 1967

By J. F. Shultz

The Bureau of Mines investigated the hydrogenation of carbon monoxide and carbon dioxide over Raney nickel catalyst and nitrided fused-iron catalyst using both a single-pass and a recycle system. Activation energy over Raney nickel catalyst is 29 to 32 kcal/mole for synthesis from either CO or CO2, Pressure dependence of the gas conversion is to the 0.3 power for synthesis from CO and to the 0.5 power for synthesis from CO2. Nitrided fused-iron catalysts were tested using high recycle rates and 3H2+lCO, 2H2+lCO, and 1H2+lCO feed gas at 21.4 atmospheres absolute pressure. The relative usage of hydrogen (moles H2 consumed per moles Ha+CO consumed) was larger than in corresponding single-pass tests, and the relative usage of hydrogen approached the feed gas ratio monotonically as conversion increased. Activation energy was found to be 12 or 13 kcal/mole fresh feed gases of 3H2+lCO or 2H2+lCO. For single-pass operation the activation energy under the same conditions was 19 to 21 kcal/mole.

Jan 1, 1967

"Far from being eclipsed by petroleum and natural gas, Canadian coal continues to command wide (and apparently growing) interest.Major R & D investigations are currently heavily oriented toward coal beneficiation (e.g., cleaning and utilization of fines) and toward a broad range of studies on metallurgical coals and cokes. However, active work is also being carried out in the areas of coal geology, mining, transportation and combustion; and, in some laboratories, increasing stress has been laid on developing a number of new, essentially non-fuel uses for coal and coal products.This review summarizes the work of Canadian coal research agencies during 1966 and indicates some of the more important advances made by them."

Jan 1, 1967

By N. G. W. Cook

When an excavation is made underground the original rock stresses are removed from the surfaces of the excavation. These surfaces converge to partially close the excavation and the superincumbent rock mass moves down towards the excavation. If the convergence of the surfaces of the excavation were controlled, energy generated by their motion against the controlling forces could be extracted. Since the total forces in the rock mass are not significantly affected by the excavation, stress concentrations arise around the excavation, which compensate exactly for those stresses no longer transmitted through the excavation. These phenomena give rise to two general principles which provide the basis for analyzing the effects of making any underground excavation. The first of these is that the total force resulting from the stresses across any plane in the rock, including any plane through the excavation, must be the same before and after the excavation is made. The second of these is that energy must necessarily be released as a result of making an underground excavation. It is instructive to consider the implications of these two principles for two extreme cases of material behavior between which the actual behavior of rock must lie, namely, the behavior of a fluid and the behavior of an elastic solid. For the purpose of analysis in this paper, an underground excavation is defined as an excavation in which the smaller horizontal dimension of any open void at a particular horizon is less than the depth of that horizon below surface. In the case of a fluid, any unsupported excavation would fill immediately, as a fluid cannot sustain shear stresses. For the same reason, stress concentrations could not arise and the forces across any plane would necessarily be the same before and after excavation. If the filling of the excavation were controlled by forces applied to the surfaces of the excavation, an amount of energy equal to the product of the fluid pressure

Jan 1, 1967

By William C. Hagel

Oxygen-18 exchange between gaseous oxygen, held at a pressure of 125 mm Hg in a PL-IORh chamber, and splzeres of a Fe2O3 containing three or less grains was determined from 9000 to 1250°C. Isotope equilibrum on crystal surfaces appears to be quickly established, and the rate-determining factor is self-difiusion confbvrning to the relation D = 2.04 esp(- 77,900/RT) sq cin sec-'. Changing sphere diameters caused no detectable variation in diffusion coefficients. Oxygen ions diffuse faster than cations at low temperatures, but a crossover may occur at about 1150°C. INVESTIGATIONS by Davies et al.' and Himmel et al2 have suggested that the mechanism of iron oxidation above 600°C involves a predominance of cation migration in the wüstite (FeO) and magnetite (Fe301) layers and oxygen-ion migration in the hematite (a Fe2O3) layer. Evidence for little cation migration during hematite growth consists of: 1) the disappearance of radioactive-silver markers, presumed to vaporize from the oxide-gas interface, and 2) a large discrepancy between parabolic rate constants for magnetite oxidation and those calculated from Lindner's3 data for cation self-diffusion, D:, using Wagner's theory.4 Reversing the calculations gave anticipated self-diffusion coefficients, D:, for oxygen ions of 3.6 x 10-9 sq cm sec-1 at 1100°C and 5.9 x 10-10 sq cm sec-1 at 1000°C. Since then Kingery et a1.5 reported three values for oxygen-ion diffusion in polycrystalline, sintered hematite. These were obtained near 1200°C, at an oxygen pressure of approximately 150 mm Hg, and could be represented by the Arrhenius expression, Dg = 1 x 10 11 exp(-146,000/RT) sq cm sec-1. Extrapolation to temperatures below 1100°C infers that oxygen ions are less mobile than cations. This contradicts the aforementioned oxidation evidence and also coble7s study of the initial sintering of hematite. From the latter, apparent diffusion coefficients for the slowest rate-controlling species could be calculated, and fair agreement was found with an extension of Lindner's data for cation diffusion. Fig. 1 depicts such comparisons graphically. Three points have been included for the determinations of Himmel et al. on cation diffusion in large, natural hematite crystals surrounded by pure oxygen at atmospheric pressure. No dependence on crystal log raphic direction was noted. Since the value of 10-l4 sq cm sec-' at 1000°C actually represents an upper limit, one might interpret that there is a small decrease in D: when single crystals are employed. On the whole, however, cation diffusion appears relatively well-defined,* while the few results tension to lower temperatures. After having gained experience measuring oxygen-ion diffusion in certain glasses7 and in the corundum oxide, a Cr2O3, the purpose of this work was to determine D; values for hematite and thus possibly assist a mechanistic understanding of the kinetics of the oxidation and reduction of solid iron oxides. I) EXPERIMENTAL PROCEDURE A) Material. Hematite powder of moderately high purity was received from the Columbian Carbon Co. An accompanying lot analysis listed 0.03 H2O, 0.008 weight percents, with the remainder Fe2O3. Subsequent treatments were ball milling, drying, prepressing, and hot-pressing for 60 min at 1350°C under 5000 psi. Since graphite dies coated with a slurry of alumina were used for hot-pressing, the surrounding atmosphere at temperature was sufficiently reducing to form some magnetite on the outer surface of each cylinder. After removing any attached alumina, a stabilizing anneal of 50 hr at 1300°C in oxygen was added. The final product was nonmagnetic and exceeded 97 pct of the density (5.24 g cm-3) usually given for FezO3. On polishing cylindrical ends, counts were made of the number of grain boundary intercepts per

Jan 1, 1967

By C. G. Dunn

This note describes a method for revealing micro-structures in tantalum through an {hkl} effect which was found during a study involving amorphous and crystalline tantalum oxides. Three steps are involved. First, an amorphous film of Ta2O5 is formed anodically1 on the surfaces of the tantalum. The amount needed depents on the thickness of the substrate tantalum; 1600Å of oxide, however, is generally satisfactory in the 1/2 -mil (12 µ) to 3-mil thickness range. The film at this point is uniform in color. Second, the anodized specimen is heated to 800°C in. vacuo during a period of a few minutes and held at temperature for 5 min. During such a treatment some oxygen leaves the oxide through dissolution into the substrate tantalum (e.g., at 10-8 Torr oxide films thinner than about 800 completely disappear on 5-mil strip). Considerable crystallization of the amorphous oxide also occurs adjacent to the metal/oxide interface but not throughout the oxide thickness. The thickness of oxide needed as a residue is not too critical; values between 500 and 1000Å (optical estimate') may be most useful. (The presence of a residual oxide layer after the heat treatment usually is not apparent; in fact, in most instances the surfaces have a metallic appearance. This can be the case also for thicker residual films needed in the detection of a crystalline oxide phase by surface X-ray diffraction—e.g., if the initial oxide film is 3000Å thick, enough crystalline oxide is formed for X-ray detection.) The third step eliminates the metallic appearance at the surface and reveals (or produces) a varied colored film of tantalum oxide. Two methods can be used and both will be illustrated. If the specimen is dipped in 48 pct HF for a few seconds, the tantalum is found to be covered with a multicolored oxide. Moreover the colors correlate with the grain structure of the substrate tantalum through an orientation dependence of the type illustrated in Fig. 1, where results of an orientation analysis by the Laue X-ray method have been plotted. Other film conditions would have provided a different set of colors for the same orientations. Any such correlation, however, provides a basis for a qualitative assessment of the distribution of orientations in a large sample. The cold-rolled structure of tantalum foil produced by a recrystallization anneal and a cold-rolling reduction of 95 pct is not easily obtained by usual metal-lographic methods.' The structure, however, is easily revealed by the present technique, Fig. 2. The alternative third step is to reanodize the specimen. The optical nature of the final anodic film depends on the presence of the crystalline oxide phase; color variations indicate optical thickness variations in the film. As the reanodization voltage is increased from zero, straw and light brown colors appear (as usual), followed now by variations in color from grain to grain depending on {hkl} orientation. Suitable end points, which are determined by voltage and time, are easily established. Fig. 3, for example, shows the grain structure developed in 5-mil tantalum strip during a 30-min re-crystallization and grap-growth anneal at 1800°C. An anodic film of 1600Å thickness was added prior to the special 800°C anneal. Reanodization was done at constant current density (near 0.2 ma per sq cm) in an aqueous solution of H3PO4 (0.01 pct) and was terminated after the initial brown colors were replaced by a deep blue at approximately 30 v. Although good grain contrast can be obtained with bright field illumination, even greater contrast for black and white micrographs may be obtained with polarized light, as in Fig. 3.

Jan 1, 1967

By Robert M. Doerr

The purpose of the investigation was to determine the oxidation behavior of selected tungsten-cobalt alloys. Specimens of Wand W-Co containing 0.7, 1.7, 3.4, and 9.7 weight-percent Co were subjected to pure 02 at 1,000° and 1,100° K, and specimens of W-Co containing 29.8 weight-percent Co, at 1,100° K. Reaction kinetics were determined volumetrically. For specimens other than those containing 29.8 percent Co, the reactions proceeded at about a constant rate at either temperature, indicating the formation of a scale of constant protectivity; the reaction rates were essentially independent of the Co concentration. The scales on these alloy specimens consisted principally of WO3 and CoWO4. Specimens of a 29.8 weight-percent Co alloy, consisting primarily of the W6CO7 phase, oxidized with only slight deviations from the parabolic rate law at 1,100° K. The protective scale on these specimens consisted chiefly of Co3O4, CoW04, and W1 8°49; Co3O4 was outermost, and the W18O49 was adjacent to the alloy. The results suggest that the Co-rich outer scale inhibited the inward transport of 0 to an extent sufficient to greatly limit the amount of the nonprotective WO3 formed, so that protective W18O49 formed instead.

Jan 1, 1967

By S. J. Aresco

The Bureau of Mines has been active in promoting the purchase of coal for Government use under specifications that define the requirements in terms of heating value of the coal, expressed in British thermal units, and the composition as shown by proximate analyses. To these, when required, are added the ash-softening temperature, the free-swelling index, and the Hardgrove grindablity index. Under most of these specification contracts the bidders guarantee the quality of the coal, and that guaranteed by the successful bidder becomes the standard of his contract. The deliveries are sampled in accordance with instructions3 issued by the Bureau of Mines; the samples are analyzed in the Bureau laboratory to determine whether the coal is of the quality guaranteed by the contractor; if it is not, a price adjustment is made. Analyses of the delivered coal and tipple samples (samples collected at mine tipples as coal is being loaded into railroad cars or trucks) provide valuable data for use in evaluating future bids. In addition, the continuous of coal as delivered is a check on the practical results obtained in the coal.

Jan 1, 1967

By D. A. Elkins

This report is the second of a series of three that will evaluate, in order, the metallothermic, carbothermic, and electrolytic methods of magnesium production. The historical development of the carbothermic process is outlined. Production costs varying from 38.9 to 21.8 cents per pound of magnesium are estimated for different versions of the process. Additional suggested process modifications are listed. The technical and economic potential of the different versions are compared. Areas deemed most promising for future research on the process are delineated.

Jan 1, 1967

By H. G. Iverson

Solid state reactions of manganese with silica were investigated in high-temperature tests. Reactions of 0.5 to 4.0 moles manganese (Mn) with 1 mole silica (SiO2) at 1,100° C and of 2.0 Mn:SiO2 mole-ratio mixtures at 1,000° to 1,150° C yielded products consisting of a slag phase and a metallic phase. At 1,100° C, the slag phase from reactions of the low Mn:SiO2 mole-ratio mixtures was composed of SiO2 and rhodonite (MnSiO3), and the slag phase from the high Mn:SiO2 mixtures was composed of MnSiOs and tephroite (Mn2SiO4). The metallic phase from the corresponding low Mn:SiO2 mole-ratio reactants consisted of two manganese silicides, Mn5Si3 and Mn3Si; from the high Mn:SiOg mixtures, it was Mn and the manganese silicide (Mn5Si). For the higher mole ratios of MnSiO2 the manganese content in the metallic phase increased, while the manganese and silica contents of the slag phase remained nearly constant. The slags did not contain free or uncombined manganese oxide (MuO). For the 2.5 to 4.0 Mn:SiO2 mole-ratio mixtures reacted at 1,100° C, the maximum quantities of silica reduced and of the manganese in the slag appeared to become asymptotical at about 41 and 48 percent, respectively. A brominating procedure was developed that was highly selective in removing the metallic constituents from the reaction product, leaving the slag phase as residue. X-ray diffraction patterns were obtained on prepared silicides Mn5Si, Mn3Si, and MnSi.

Jan 1, 1967

By R. N. Orava, L. A. Rice

One of the difficulties encountered in the preparation of titanium specimens for transmission electron microscopy is the formation of a surface hydride phase during the thinning operation at ambient temperatures. This necessarily destroys contrast, obscures features of interest, and often leads to misleading results. By cooling the polishing solution to temperatures below 0°C this problem has been overcome in the past.' However, since the cooling procedure is somewhat inconvenient, a technique was developed at this laboratory for thinning titanium at room temperature. The material examined was A-70 grade commercial-purity titanium purchased from the Crucible Steel Co. of America. The mechanical and thermal treatments, described elsewhere,* yielded a recrystallized grain size of 4 to 5 p. A slice, 0.5 mm thick and 1.5 mm wide, was cut from a bulk specimen2 using a diamond cut-off wheel. The sample was then coated with paraffin wax. Two concentric holes, about 0.03 in. in diam, one at each broad face, were scribed through the wax to the surface of the metal. Subsequent polishing for several minutes resulted in a preferentially thinned or "dimpled" region. Thereafter, the wax was removed and the entire specimen polished to the point of breakthrough at the base of the dimple. Polishing was effected chemically in a solution comprised of 30 pct HF and 70 pct HN03 by volume, kept at room temperature (20" to 25OC). The specimens were mounted in a stereo holder and examined at 100 kv in a Philips l00 B Electron Microscope. A micrograph from a foil prepared in this way is shown in Fig. 1. Several points are noteworthy. This electron micrograph shows neither evidence for the formation of a hydride phase due to specimen preparation nor, moreover, any obvious surface contamination in electron-transparent areas of a freshly prepared foil. Localized variations in foil thickness observed in some specimens seem to be a characteristic of this chemical polish but do not seriously detract from foil quality. With care, the lifetime of a good specimen exceeded 2 hr in the beam. On the other hand, the exposure of a sample to air at atmospheric pressure, when still warm from the beam, clearly resulted in the deterioration of a formerly clean area just previously in the field of view. An example in Fig. 2 of a contaminated region reveals features, and "spots", not unlike those observed in much purer material by Yamane and Ueda. Consequently, one can conclude that: 1) titanium can be thinned satisfactorily in a solution at room temperature for transmission electron microscopy; 2) large-scale precipitates, >50A in diam, are absent in commercial-purity, recrystallized, furnace-cooled, A-70 titanium containing about 3800 wt ppm interstitials and the same amount of iron; 3) care must be taken not to attribute surface contaminants to precipitates. The authors are grateful to the Franklin Institute for financial support and permission to publish.

Jan 1, 1967

By E. R. Dean

A wire-feed mechanism has been employed to fabricute metal alloy film resistors to various sheet resistivities on oxidized silicon substrates. The effect of several thousand hours storage in air at elevated temperatures on the resistance and temperature coefficient of resistance is presented. Unprotected films of- sheet resistivity between 100 and 500 ohms per sq fabricated at 300°C substrate tenzperatures were unstable when stored at 150°Cfor extended periods. The higher sheet resistivity films exhibited the greatest instability; however, even the 100 ohms per sq films drijted excessively for device application. When stored at still higher temperatures, the normalized resistance increases to maximum, then decreases until a minimum value is obtained, then finally increases in resistance until open. The use of a protective overcoating of SiO has had considerable benejicial effects on the film stability, so that 250 ohms per sq films deposited on 300°C substrates are now stable after 1000 hr storage at 250°C and possess a temperature coefficient of resistance less than 200 ppm per C. The use of a low substrate temperature during depositon (100°C) enables the preparation oj resistors with very low tenperature coefficients of resistance (10 to 20 ppnl per 'C). However, these films are less stable than their higher substrate temperatuve counterparts. During extended storage, the resistance of the protected films always decreases with lower substrate films exhibiting larger normalized resistance decreases. This resistance decrease is accompanied by a linearly related increase in the temperature coefficient of resistance. The electrical behavior of these films may be explained by postulating That the structure of the films is in the transition region between thick continuous films and ultrathin island structure films so that the conductivity is the restlt of both electron scattering and tunneling-activated charge carrier creation between neighboring grains. The annealing behavior when thermally aged is the result of defect anneal, grain growth, and selective oxidation. TheRE is a considerable interest in thin metallic films for use as resistor elements in microelectronic circuits.1,2 These resistor films must be stable when exposed to elevated-temperature storage or operating ambient, possess low temperature coefficients of resistance (hereafter referred to as T.C.R.), and be of a high enough sheet resistivity to be useful. The resistivity and T.C.R. of a thin metallic film are determined by the structure and thickness of the film. Hence the stability of the film when exposed to stress would depend on the stability of the structure. The resistivity of a thin film is the result of the electrons' interaction with the lattice vibrations (electron-phonon scattering), scattering of electrons due to impurities, defects, and grain boundaries and specula reflection from the film surfaces.3' All of these effects serve to reduce the electron mean free path and result in a resistivity higher than the ideal bulk. In ultrathin films possessing essentially an island structure consisting of a planar array of aggregates separated by a few to a few tens of angstroms, conduction is dominated by a combination of tunneling and activated charge carrier reation. Thin films would be characterized by relatively low resistivity, positive T.C.R., and reasonable structure stability whereas ultrathin films possess unstable structures, negative T.C.R., and exhibit high resistivity. Feldman6 has investigated films intermediate between the two regions and postulates that the resistivity of a film in the transition region is composed of two linearly additive parts: that due to the resistance of the grains and that due to the gaps. The grain resistivity would represent the scattering of the conduction electrons by defects, surfaces, and phonon interaction while the gap term represents the tunneling contribution. For gold and platinum films, he found as the film structure becomes progressively less continuous, corresponding to thinner films, the absolute value of the T.C.R. becomes progressively smaller until negative values are observed with respective zero T.C.R.'s at about 35 and 150 ohm per sq, respectively. Recently the author7 investigated the behavior of a multicomponent alloy of nickel, chromium, and iron and found the T.C.R.'s of these films decrease with decreasing substrate temperature during deposition. The lower T.C.A. associated with lower substrate temperatures was attributed to an increased contribution to the total resistivity from the negatively temperature-dependent gap tunneling since it is well-known that thin films deposited on low-temperature substrates consist of a higher density of smaller grains than the same sheet resistivity films deposited on higher-temperature substrates. Under conditions of thermal anneal, the author found that, when various sheet resistivity films fabricated at 300°C substrate temperature are exposed to extended storage in air at 300°C, the thinner films increase in resistance until open, while the thicker films

Jan 1, 1967

By Olav Mellgren

Part I. The interaction between potassium ethyl xanthate and lead salts has been studied thermo-chemically. It is shown that ethyl xanthate reacts with lead carbonate, basic carbonate, thiosulfate and sulfate according to principles of simple chemistry, whereas reactions with lead sulfite, metasulfite, basic thiosulfate and hydroxide at high pH are associated with secondary reactions. A new compound "xanthogen thiosulfate" is postulated. Part 11. Adsorption of ethyl xanthate on galena has been studied quantitatively and thennochemi-cally. It is shown that an ion-exchange mechanism governs the adsorption process and that the heat of adsorption of xanthate on galena is equivalent to the heat of reaction of ethyl xanthate with bulk lead salts. It is concluded that the entropy content of the surface "compound" on galena is different from that of a corresponding bulk lead salt. Alkali depression is in part shown to be due to the instability of the xanthate-galena system at high pH and to the formation of basic lead salts. Sulfate and carbonate ions are shown to have a stabilizing effect on the xanthate-galena system. PARTI. THERMOCHEMISTRY OF ETHYL XANTHATE AND OF ITS REACTION WITH LEAD SALTS In the past little attention has been paid to the chemistry of lead xanthate. It is known that xan-thates form slightly soluble compounds with lead and that suspensions of lead xanthates in alkaline solution decompose rather readily.' The solubility of lead ethyl xanthate is of the order of 2.6 x 10-6 moles per 1. At increasing pH the xanthate concentration of a saturated solution contains more xanthate. Thus at pH 11 this xanthate content is about 100-fold larger than at pH 7.1 Xanthates are known to be consumed when added to a suspension of slightly soluble lead salts such as lead sulfate and lead carbonate. It is unknown to what extent this xanthate consumption is due to a simple chemical reaction because, frequently, observations are made which reveal secondary reaction products in such reactions. Thermochemical study of the reaction between xanthate and lead salts offers a means to clarify the significance of these reactions as the enthalpy changes can be accurately predicted from heat of formation of lead salts in pure solution reactions. In the present work the heats of formation of lead ethyl xanthate from potassium ethyl xanthate and lead salts are determined and some thermochemical aspects of xanthate in solution are studied. The results of these investigations are presented in Part I. In Part II the heat of adsorption of ethyl xanthate on galena surfaces is presented. All enthalpy changes were measured directly in a microcalorimeter. Calorimeter: The calorimeter used for measuring enthalpy changes was similar to that used by Redinha and Kitchener2 which was based on a description by Derbyshire and Marshall.3 Other useful references4,5 are listed. A sketch of the calorimeter

Jan 1, 1967

By J. M. Tobin, L. H. Cadoff, L. M. Adelsberg

The reaction between liquid zirconium and graphite at temperatures above 2000 °C has been investigated. The reaction products were found to be carbon-saturated zirconium metal and ZrC which formed between the graphite and the metal. Parabolic growth behavior was observed for the ZrC Phase at all temperatures of this investigation. The parabolic growth constant at temperatures between 2000° and 2860°C was measured to be 1.83 exp 84,300/RT) sq cm per sec. The reaclion mechanism was proposed to be the rapid carbon saturation of the liquid metal and the formation of ZrC at the metal-carbide interface with diffusion of carbon through the ZrC, the "rate - determining step" of the reaction. The concentration-independent diffusion coefficient of carbon in ZrC, (DZrC), was expressed as 0.95 exp? 78,700/RT) sq cm per sec. This value mas calculated using the temperature-invariant ZrC phase fields proposed in the literature. The [ZrQiq)] — [ZYQiq) + ZrC] phase boundary over the temperature range 2000° to 2800°C was determined and the ZrC + C eutectic temperature was found to be 2890° ± 50°C. ThE Group IV and VB transition-metal refractory carbides are of interest because of their high melting points, high temperature strength properties, and relative inertness in certain corrosive environments. The present-day understanding of these materials, however, is limited by the general unavailability of accurate and reliable physical and chemical property data. This is due primarily to the difficulties associated with the preparation of suitable, high-density, high-purity carbide samples, and the achievement and control of uniform high-temperature environments. Accurate measurement of temperature is also an important factor limiting the reliability of reported data. The Zr-C reaction was selected for investigation because of the high melting point (>34000C) and favorable nuclear properties of the reaction product, ZrC. The direct reaction method afforded an opportunity to obtain kinetic data on the fully dense carbide. In this paper, layer-growth techniques were used to estimate the diffusivity of carbon in ZrC and to investigate the phase equilibria in the Zr-C system at temperatures above 2000°C. EXPERIMENTAL PROCEDURES AND DATA Crystal bar zirconium (99.9 pct Zr), purchased from the Nuclear Materials and Engineering Corp., and ZTA graphite (99.9+ pct) were used in this study. The analyses of the materials are listed in Table I. A schematic of the high-temperature carburization apparatus is shown in Fig. 1. The sample was a zirconium metal charge in a 1/2 -in.-ID graphite crucible which was capped with a tightly fitting graphite stern. The crucible and stem were designed to closely approximate black-body conditions. The graphite crucible was packed in lampblack (outgassed 1 hr at 2100°C) which provided insulation and thermal stability to the system. The inert atmosphere was maintained by a constant flow of high-purity argon or helium gas. The nozzle-diffuser section on the top flange was sufficient to prevent back-diffusion of air into the system. Chemical analysis of the carburized samples revealed oxygen and nitrogen concentrations of less than 44 and 20 ppm, respectively. The sample was heated by induction with a Westing-house 5 kw-450 kc power source. Temperature was measured with a Milletron two-color pyrometer which was sighted into the crucible by reflection from an overhead front surface mirror. Optical losses due to glass absorption and light reflection at air-glass interfaces were minimized by the employment of the dynamic-gas seal. It was found that no correction was required for the front surface reflector. The pyrometer was calibrated periodically against a U.S. Bureau of Standards tungsten ribbon secondary standard. Temperatures inside the crucible were also calibrated against the Zr-ZrC eutectic (1850°C)1 and the Nb-Nb2C eutectic (2335°C)2,3 temperatures and agreed to within ±10°C of these values. The temperature was controlled by manually adjusting the power input; variations of

Jan 1, 1967

By K. H. Kilgren

At high formation pressures the distillate produced from a gas-condensate reservoir may be black in color. In this event the dense gas phase existing above the dew point is correspondingly dark. Volumetric phase data and an analysis of a reservoir fluid exhibiting these characteristics, together with a description of the visual equilibrium cell in which these observations were made, are presented in this paper. INTRODUCTION Previously the author, like many others in the oil and gas industry perhaps, tacitly assumed that the expressions black or dark oil system, crude oil system and bubble-point system were synonymous. Crude oil reservoir fluids are bubble-point systems and yield a black or dark stock-tank oil of relatively low API gravity. Conversely, a clear or amber colored trap distillate of high API gravity is assumed indicative of a dew point system or a gas-condensate reservoir fluid. This broad classification appears satisfactory for shallow reservoirs, but as the following study demonstrates, may be misleading when applied to deep reservoirs. Theoretically, there is no reason to exclude the possibility of producing a dark, low-gravity distillate from a gas-condensate reservoir. At sufficiently high values of pressure and temperature, heavy, dark-colored hydrocarbons may exist in the vapor state of a multi-component system. If enough dark-colored components are present in the reservoir vapor phase, the resulting condensate will be dark. The reservoir fluid investigated in the present study supports this contention. Stock-tank production was black in color and measured 29" APT gravity. From outward appearances, the liquid closely resembled a medium gravity crude oil. Experimental measurements proved the reservoir fluid was in reality a gas-condensate system. Volumetric phase data for this high-pressure system and a description of the visual cell in which the study was conducted successfully are presented in this paper. THEORY Phase behavior of a reservoir fluid can be predicted accurately with reference to a pressure-temperature phase diagram. If the reservoir temperature is lower than the critical temperature of the hydrocarbon fluid in place, bubble-point behavior will be observed. If the reservoir temperature lies between the critical and cricondentherm temperature, dew point behavior and retrograde condensation will occur. For reservoir temperatures above the cri- condentherm, only a single gas phase can exist in the reservoir regardless of pressure. Providing the composition of the reservoir fluid were known, it would be possible to predict the critical temperature and estimate the phase behavior from equilibrium relationships. However, the usual practice is to obtain a sample of reservoir fluid, subject it to varying pressures at the reservoir temperature and observe the phase behavior experimentally. The latter method was used to obtain the data reported here. WELL AND TRAPPING INFORMATION A summary of pertinent data for the well from which the reservoir fluid was sampled is presented in Table 1. This well is located offshore Louisiana. Except for the pressure which substantially exceeds hydrostatic pressure, the information does not appear unusual. Prior to the sampling program, the well was produced for 22 hours at a stock tank oil rate of 139 B/D. Average trapping conditions and gauging data for the six-hour test period that followed are summarized in Table 2. Samples of the first-stage trap gas and liquid were obtained during the latter portion of the test period. Ambient temperature remained 5 to 10F below trap temperature and presented no problem for sampling. Surface wind and moderate foaming of stock-tank oil presented some difficulty in obtaining accurate stock-tank gauges. SAMPLE ANALYSIS Compositions of the gas and liquid samples are shown in Table 3. The trap gas was analyzed by isothermal chromatography which revealed only a trace of heptane in the stream. The trap liquid was initially analyzed by low-temperature fractional distillation, yielding a bottom product of heptane and heavier components. Specific gravity of this fraction was measured and the mol weight was determined by freezing point depression. The hexane and lighter overhead gas collected during distillation was

Jan 1, 1967

By Robert E. Barieau

General expressions for evaluating practically all the thermodynamic properties of a fluid from a single equation of state are derived. Most of the formulas are expressed in terms of the compressibility factor, with this factor being an explicit function of the temperature and the molal density. Similar expressions are given using reduced variables.

Jan 1, 1967

By Manuel Gomez

This, report presents correlative data on ash and sulfur forms for Pittsburgh seam coal from Greene County, Pa. Prediction equations were developed for sulfur form distributions and washability characteristics. The equations developed were evaluated with an independent set of exploration core samples. It was demonstrated-that both sulfur distributions and washability characteristic's can be predicted from exploration core data ahead of mining. This information can improve the efficiency of selective mining techniques for the production of a uniform metallurgical coal product.

Jan 1, 1967

By D. R. Corson

The Bureau of Mines instrumented an operating stope in a deep vein mine to determine the amount of wall closure and the magnitude of loads imposed on a backfilled stope. Hydraulic pressure cells used to monitor pressures in the fill) with bolt closure points to measure vein-wall movement and the procedure for their installation) are described) and the results of the laboratory calibration analysis of the reliability of these cells are given. An attempt to monitor density and moisture changes in the backfill with a nuclear density-moisture device was only partly successful) owing to either deformation of access tubing or relative displacements of the vertical vein walls relative to the emplaced tubes. Data from the instrumentation indicate vein-wall closure in excess of 20 inches and pressures within the fill approaching 600 psi. Analysis) incorporating field data with results of laboratory tests of the compressibility of timber and tests defining the constrained moduli of the fill) points out the limited restraint to vein closure offered by timber sets. Ground movement induced by mining activity could be more effectively con-trolled by the use of densely compacted backfill.

Jan 1, 1967

By S. H. Gelles

Samples of poly crystalline zinc of 99.999+ pct purity were observed metallographically after having been exposed to hydrostatic pressures of up to 27 kbars. The deforrnation produced by this treatment was analyzed using X-ray and metallogaphic techniques. Basal-plane slip occurred universally in all grains exumined at the lowest pressure used (8 kbars). At pressures of >23 kbars, {1012} twin nucleation and growth were noted as well as slip. Formation of bend planes, complex kink bands, and recrystallization at the gain boundaries were also observed in this pressure range. These observations are discussed in reference to the expected deformation behavior of zinc under high hydrostatic pressure. It has been shown over the past few years1'3 that anisotropic, poly crystalline metals can be made to deform plastically by the application of a hydrostatic pressure. The effect is greater 1) the larger the anisotropy of linear compressibility and 2) the smaller the stress level needed to produce plastic deformation. Zinc having both very anisotropic linear compressibilities and a very low critical resolved shear stress (CRSS) for basal-plane slip has been shown to exhibit large amounts of plastic deformation when subjected to a hydrostatic pressure.2,3 At pressures up to 15 kbars, grain boundary migration and slip on one set of glide planes have been reported.' After exposing samples to 20 kbars pressure, grain boundary migration, single slip, multiple slip, and twinning have been noted.' The identification of the deformation modes operative under these conditions has not been reported. It was the purpose of this research to identify the deformation modes induced in poly crystal line zinc by the action of a hydrostatic stress and to study the strain accommodation at grain boundaries. Hydrostatic pressure could affect the operational modes of deformation by altering the Peierls-Nabarro stress. This may be roughly approximated by the relationship4

Jan 1, 1967

By L. C. George

The Bureau of Mines measured vapor pressures of selected mixtures in the binary system SnCla-ZnC12 by the static pressure method. Equations expressing the vapor pressure) and the heat and free energy of vaporization) as functions of temperature were developed by numerical analysis based on the sigma-plot method. It was found that the vapor pressure of any SnCl2-ZnCl2 mixture) at any temperature within the range of this investigation) could be accurately calculated from the derived values for the heat and free energy of vaporization for the mixture, with a probable error of 0.01 cm Hg or less.

Jan 1, 1967