By J. E. Gosline

In any theory of a hydrodynamic nature dealing with the vertical flow of gas-liquid mixtures in pipes, the two factors that present the greatest difficulty are the relative motion between the phases and the energy loss resulting from turbulence work. The former has generally been referred to in the literature as "slippage" and the latter as "friction." A third factor of importance is the nature of admixture between liquid and gas for both the relative motion between the phases as well as the turbulence work are functions of the type of mixture. Although much work of a general nature has been performed on the vertical flow problem, there have been very few attempts made to study experimentally the factors involved in the phenomenon individually. Of these, perhaps the most notable is the work of Moore and Wilde1 on slippage. Some writers on the subject have assumed that over a wide range of operating conditions the controlling type of mixture is one in which gas bubbles of uniform size are distributed throughout the liquid, and that the data obtained from experiments on the motion of single bubbles through various liquids may be used in evaluating the slippage. Ver-sluys2 has further assumed another controlling type of mixture in which the liquid occurs as a dispersed phase within the gas and applies data on the fall of drops of water in air to calculating the relative velocity. It was for the purpose of studying the applicability of data on single bubble motion to the slippage factor and to further observe the nature of mixtures that a research program was conducted at the University of California during 1932 and 1933. These experiments formed a basis for

Jan 1, 1936

By E. Stansfield, J. W. Sutherland

It is well known that the ash left when coal is burned is not the same either in chemical composition or in weight as the mineral matter originally present in the coal. This mineral matter has been referred to as "mineral impurity," "ash-forming constituents" and "corrected ash." The authors prefer the simple name used in the title and throughout this paper. The mineral matter in a sample of coal cannot be isolated unchanged and then weighed; but if the relation between the weight of mineral matter in the coal and the weight of ash remaining when the coal is burned can be ascertained, the weight of mineral matter in the sample can be calculated from the determined weight of ash. When the weight of mineral matter in the sample is known, the weight of pure coal can be found by subtraction. This pure coal must be the basis of accurate coal classification. W. F. Wheeler,l,3 W. Brinsmaid,2 S. W. Parr, and many subsequent workers have studied the relation between mineral matter and ash. Wheeler and Parr and others have deduced formulas for calculating this ratio, and used heavy-solution separations for checking the accuracy of their formulas. Brinsmaid hand-picked and analyzed two separate samples (and mixtures of these) and based thereon a graphical method of deducing the ratio. In the Fuel Testing Laboratories of the Scientific and Industrial Research Council of Alberta, a graphical method, based on heavy-solution fractionation of coal samples, has been used with marked success for the past 7¼ years for determining the mineral matter-ash ratio. This method resembles that employed by Brinsmaid in 1907.

Jan 1, 1930

By Robert L. Davidoff

INTRODUCTION The impact of taxation differs substantially from state to state in a complex fashion that depends on both the physical characteristics of a mineral deposit and on the price of the mineral commodity relative to its costs of production. A comparative analysis of the tax structures of eight states (Arizona, Colorado, Idaho, Montana, Nevada, New Mexico, Utah and Wisconsin) showed wide variations in rates of return for any given type of mineral property, with no state having either the most burdensome or least burdensome tax structure under all circumstances. Three hypothetical mineral operations were analyzed: a producing open-pit copper property, a non-producing underground platinum operation, and a non-producing underground gold operation. None of them corresponds exactly to an existing property. Each of these property types is further defined to have ore feed grades at three different levels, leading to three potential profitability levels, referred to in this paper as "economic", "marginal" and "subeconomic". Thus the differential impact of state tax structures is measured for mineral properties of different types, as well as for different profitability levels. Montana is used as the base case. This study does not address the topic of corporate structures or tax consolidation. There are no costs assumed external to the operation of the deposit (e.g. exploration to locate additional deposits). Two types of analyses were performed for this study. The first calculates the total cumulative tax payments in each state using all applicable taxes (including U.S. federal income taxes and examines the resultant differences in discounted cash-flows rate of returns DCFROR's amoung the eight states. The second is a sensitivity analysis that examines each type of state tax separately (i.e. state income, property, and severance taxes) in order to isolate and examine the differences in tax payments that are due to the difference in rates and methods of computing specific types of taxes in each state. The results of this study serve to illustrate the complex nature of interactions among various taxes. For example, property tax is a deduction in calculating severance tax in some state. Changes in property-tax and severance-tax payments both enter into the calculation of state and federal income-tax liability. This, in turn, could change the timing and usage of tax-loss carry forward amounts and investment tax credits. Additionally, the physical characteristics of a property, the method and costs at which the mineral will be extracted, and the profitability level at which each property operates will affect tax treatment. Each mineral operation was evaluated at three different predetermined profitability levels, referred to using the terms economic, marginal and sub-economic. These three profitability levels are defined by the ore feed grades of the primary commodity that yield in constant terms, approximately an "economic" 18% DCFROR, "a marginal." 10% DCFROR, and a "sub-economic" 5% DCFROR, respectively, under the Montana tax structure. In the analyses, the mining and processing parameters for each of the three types of properties were assumed to be identical for each of the eight states. It was assumed that each operation produces at full operating capacity throughout its life. This implies the level of mineral commodity demand will support the inferred commodity price, such that each operation will be able to sell all its output. The analyses performed for this study were done using a comprehensive economic evaluation simulator that is used in the Bureau of Mines, Division of Minerals Availability MAS program to perform DCFROR analyses. All economic evaluations performed upon these data (see appendix 2) were in constant January 1981 dollars. By-product prices used for the analyses were: [Gold $425.00/troy ounce Palladium$200.00/troy ounce Silver $ 10.00/troy ounce] Typical cash-flow calculation layout is given in Appendix 3. The initial step for each evaluation is to define an "economic" profitability level scenario. An 18% DCFROR rate in Montana was considered the

Jan 1, 1985

By R. E. Cech, J. H. Hollomon

KURDJUMOV and Maksimova reported experiments with manganese steels and high carbon steels' and with an Fe-Ni-Mn alloy' in which mar-tensite was formed isothermally over a range of temperatures. They found in some cases that mar-tensite formation could be suppressed by rapid quenching to liquid nitrogen temperature. From their microstructural observations of martensite formed isothermally, they concluded that the rate controlling step is nucleation rather than growth. Kulin and Cohen,3 in an attempt to reproduce these experiments, found that with a steel having the same composition as that reported by Kurd-jumov and Maksimova, the transformation to martensite was essentially complete above the temperature range of Kurdjumov and Maksimova's isotherms. The possible reasons for this disagreement were not considered. Recent papers by Das Gupta and Lement4 and Kulin and Speich5 report the formation of isothermal martensite in a high chromium steel and in an Fe-Cr-Ni alloy, but neither paper can be considered a verification of the original Kurdjumov and Maksimova results. Further, in neither case were the authors able to suppress the formation of martensite entirely. Because of the important bearing the Kurdjumov and Maksimova results have to an understanding of the mechanism of martensite reactions it was felt that an experimental investigation directly concerned with checking the validity of their results was in order. This paper describes the results obtained on the isothermal transformation over the temperature range from —79" to —196°C of an alloy of iron, nickel, and manganese. Experimental Apparatus A 15 lb heat of an alloy containing 73.3 pct Fe, 23.0 pct Ni, and 3.7 pct Mn was melted by induction and cast under argon. The ingot was forged to 1-in. bar and a portion rolled to 1/16x1 1/2-in. strip. This strip was pack-homogenized 300 hr at 1100" in a helium-filled sealed iron tube. The composition after homogenization was 73.2 pct Fe, 22.94 pct Ni, 3.73 pct Mn, 0.05 pct C, and 0.015 pct N. The strips were cut to 1/2-in. width for dilatometer and metal-lographic specimens. Only the center portion of the 11/2-in. strip was used in the present investigation. The dilatometer employed was similar in design to one described by Flinn, Cook, and Fellows." A concentric fused auartz rod and tube assembly with hooks for holding the specimen was mounted so as to transmit the specimen dilation to a 1/10,000 in., 1/10 in. travel dial gage. The dilatometer proper was mounted by means of extension arms to a counterweighted sliding member on a vertical standard. This method of mounting permitted rapid transfer of the dilatometer from the austenitizing furnace to the quenching bath and low temperature chamber. A small electrical vibrator on the dilatometer kept frictional effects of the quartz members at a minimum. The austenitizing unit was a vertical, molybdenum-wound, hydrogen atmosphere furnace maintained at a constant temperature ±3°C by means of constant power input. A 12-in. stainless steel jacketed copper liner having 1/2-in wall thickness acted to equalize the temperature in the hot zone of the furnace. This liner, closed at the bottom end and open at the top to permit entrance of the dilatometer and specimen, was kept filled with dry nitrogen gas. A chromel-alumel thermocouple was placed inside the tube to determine the temperature. The 4-in. dilatometer specimens in the chamber varied less than 1/2° across the specimen length except for a 1 1/20 drop at the end nearest the open end of the furnace. The low temperature isothermal holding bath was a double Dewar arrangement similar to one described by Turnbull7. The outer bath was filled with a refrigerant at a temperature lower than the desired holding temperature. The inner bath was filled with Freon "11" or "12" or a mixture of both, depending upon the holding temperature. This inner bath which tended to be cooled by the outer bath was kept at a constant temperature by introducing a small amount of heat with a manually controlled electric heater. Stirring was accomplished by bubbling dry air through the bath. A Leeds and North-rup type K potentiometer was used to measure the inner bath temperature as indicated by a five element copper-constantan thermopile. The bath temperature was maintained within ±0.2°C of the desired temperature by occasionally adjusting the heater current so as to keep the Leeds and Northrup galvanometer at zero deflection with a constant setting of the potentiometer. Isothermal tests were usually continued for 300 to 400 min and another reading made at approximately 1000 min if the bath, unattended overnight, had not deviated in temperature more than 5°C. Transformation curves are drawn dashed (Fig. 1) through the time region where temperature was not controlled precisely. Experimental Procedure Dilatometer specimens of 1/2x1/16-in. strip were cut to 41/2-in. length and holes were drilled for the quartz hooks with proper spacing to give a 4-in. measured length. A thermocouple consisting of 0.012-in. diameter chrome1 and alumel wires was spot welded to the specimen and threaded between the dilatometer rods to binding posts near the dial

Jan 1, 1954

By F. E. Streigert, J. H. Mallery, A. H. Geisler

The existing data on precipitation in Cu-Be alloys have been reconciled with some new data to present a more complete and rational analysis of the atomic rearrangements involved in the process. Two different coherent precipitates were proposed. Each is responsible for a type of diffuse X-ray diffraction effect. THE nature of the atomic rearrangement involved in the precipitation of the compound y-Cu-Be from supersaturated solid solutions of the copper-base alloys has been the subject of two extensive investigations.'-" he precipitate in this alloy system has a rather simple structure; at equilibrium it has a body-centered cubic unit cell with copper atoms on the corner sites and beryllium atoms on the center site. While a simple mechanism would be expected to obtain for the precipitation process, those which have been proposed do not adequately explain all of the reported data. The purpose of the present report is to rationalize some of the previous observations and to contribute new data on the subject obtained by the usual techniques of structure analyses. The Cu-Be system of alloys represents one of the most extensively investigated precipitation systems, so a detailed review of the pertinent literature on structure is in order. Striations: Since one of the important features of the mechanism—the habit plane—is determined by microscopic examination, microstructural features that have been observed should be considered at this time in order to assess their role in the precipitation process in Cu-Be alloys. One of the most prominent features appears as regularly oriented markings or stripings (ripples or striations) across the crystals on a suitably polished and etched sample of the aged alloy. These have been observed and interpreted by many workers. Masing and Dah14 observed striations in both the a and /3 phases of a 2.5 pct Be alloy, and attributed them to the beginning of the precipitation of very fine y crystals along favored planes of the a matrix and to the local decomposition of the £ crystals into a plus y. These markings were apparent in both the a and /3 phases of the micrographs given by Smith5 for a 2.75 pct Be alloy, while Moore" detected them in the a matrix phase using polarized light. Desch7 attributed the markings to fine precipitate particles lined up on a family of matrix planes like Masing and Dahl had done, and he identified the planes as those of the (111) family, the slip planes of the matrix. The striations were presumably the structure which Northcott- eferred to as "martensitic." He found that this structure was present in samples that had been aged under widely different conditions with hardness values ranging from 160 to 400 VHN. Later Guinier and Jacquet' also found striations in both the a matrix and secondary /3 phase. Their analyses showed that the striations were along (110) planes of the matrix phase, apparently in contradiction of the results of Desch. They found that the striations were developed during aging on the surface of a specimen that had been polished prior to aging.' On this basis they concluded that the striations represented mechanical deformation by slip along (110) planes of the matrix resulting from precipitation stresses.'" Similar but fainter striations were observed in the same manner on an A1-Cu alloy sample, in which the change in volume was much less than for Cu-Be alloys and

Jan 1, 1953

By J. C. Scully, G. Sanderson

The electrolytic formation of y hydride in thin foils of Ti-5Al-Z.5Sn alloy and four Ti-A1 binary alloys has been studied by electron microscopy and electron diffraction. Two orientation relationships have been found: THE adsorption of hydrogen by titanium alloys from aqueous solutions has been widely reported. This can occur, for example, in both alkaline' and acidic2 pickling baths, in chemical polishing374 and electro-polishing Solutions,3,4 during cathodic polarization5" and under certain corrosion conditions,7,8 Etching reagents may also produce visible precipitates, sometimes after an aging period.9 During an investigation into the stress corrosion susceptibility of a titanium alloys by thin foil electron microscopy many observations have been made of hydride precipitation which has been deliberately promoted by techniques that are described below. The characteristics of hydride precipitation are reported and the observed crystallographic orientation relationships are discussed with reference to distortion in the titanium lattice created by the presence of the hydride. EXPERIMENTAL TECHNIQUE One grade of commercial titanium and five alloys were examined. Their composition and hardness values are shown in Table I. All the materials were in the form of thin sheet, 0.05 to 0.065 cm thick, which had been annealed after cold rolling. Foils suitable for transmission electron microscopy were made in two ways: a) by chemical polishing; and b) by elec-tropolishing. The solution used for chemical polishing was a mixture of 44 pct HF and 73 pct HNO3 in the volumetric ratio 2:3. During this polishing specimens were manually moved up and down in the solution. The reaction was veFy rapid, specimens thinning to foil thickness (2000A) in 5 min. Since chemical polishing solutions tend not to cause hydride contamination if they are kept cool3 no attempt was made to prevent the solution from becoming hot during the thinning operation. Electropolishing was performed at -30° C with a mixture3 composed of 295 cu cm methyl alcohol, 175 cu cm n-butyl alcohol, and 30 cu cm perchloric acid with an applied voltage of 40 v after chemically thinning specimens to approximately 0.017 cm thickness in a cool solution of 44 pct HF, 40 vol H2O2, and water in the volumetric ratio 1:6:3. EXPERIMENTAL RESULTS 1) Ti-5A1-2.5Sn Alloy. The Ti-5A1-2.5Sn alloy was severely contaminated by hydrogen during the chemical polishing. Foils obtained in this way contained large amounts of the y hydride phase. A typical micrograph is shown in Fig. l. The laths were identified as the hydride phase by selected-area diffraction of a large number of foils examined in a tilting stage that could be turned through 40 deg. Using the lattice spac-ings of the alloy obtained by X-ray diffraction as a standard the a value of the hydride was determined fromo the electron diffraction patterns to be 4.38 to 4.40A. The accuracy of this figure is only about ±2 pct. Further evidence of the identification was obtained by vacuum annealing chemically polished foils of the alloy at 500°C. This resulted in the dissociation of the hydride with the production of dislocations and possibly vacancy loops as shown in Fig. 2. The hydride

Jan 1, 1968

By J. C. Yannopoulos, N. J. Themelis

Ah electronic thermogravirnetric balance was used to measure the veductioiz rule o single cirpric oxide particles suspended in a stream of hydrogen. Very jzne thermocouples embedded in lie center and at the surface of the sphere recorded the variation of terw perature during reduction. In contrast to iron oxide reduction, where in most instances the rate of interface reactiokl is controlling, the heat- and mass-transfer phenotnena play a predolrinant role in the reduction of cupric oxide. The correlation of experitnental data or tnass lransfev lhrough the boundary layer at Reynolds nunlber 0-4 50 was as jollocs: ThE reduction of cupric oxide by hydrogen is represented by the equation: It is a highly exothermic reaction and the amount of heat released varies only slightly with temperature (-21,430 cal per g-mole at 400°C). Most of the published studies on this system have been conducted at temperatures in the range of 34 to 280c.l-&apos; The concensus of opinion has been that at temperatures below 200°C the reaction is preceded by an induction period during which there is very little or no reduction. The length of this period diminishes as the temperature of the reaction is increased1l5 and aseawa found that at 280°C reduction starts practically immediately when the oxide is exposed to hydrogen gas. The existence of an induction, or incubation, period has led experimenters to believe that the reduction of CuO by hydrogen is catalyzed by metallic copper.&apos; Boldurev and rmolaev found that mechanical additions of powdered copper to oxide did not affect its reduction, although metallic copper produced during the reduction seemed to have a catalytic effect. At least three other authors2&apos;5&apos;7 have reported that addition of copper had no effect on the rate of reduction. Pease and alor&apos; observed that water vapor had a strong inhibiting effect on the reduction at 1503C, but its effect was greatly diminished at 200 C. Pavlychenko and Rubinchik5 studied this reaction at 159 to 235 C and found that, once the reaction had been initiated, there was no inhibiting effect due to the introduction of water in the hydrogen stream; at temperatures above 183°C there was no inhibiting effect due to water vapor, either before or during reaction. The same authors noted that the rate of reduction was independent of pressure in the range of 200 to 700 mm Hg. aseawa investigated the kinetics of the CuO-Hz system at 160 to 280°C and estimated the apparent activation energy at 14,000 cal per g-mole. A similar value (13,500 1200 cal per g-mole) was reported by ond&apos; in the temperature range 148 to 216°C. Bond also reported that there was no incubation period and that water vapor had no inhibiting effect on reduction at temperatures above 190 C. The above studies have been conducted at temperatures below 280°C and the physical configuration of the system under investigation has not been defined adequately. However, it is well-known that the mechanism of gas-solid reactions depends on a number of in series physical and chemical rate prcesses.&apos;&apos; It is, therefore, essential to include among the experimental factors the geometry of the solid system and the mass-transport characteristics of the reducing gas. Scott studied the reduction of packed beds of cupric oxide cylinders by Hz-He streams of very low hydrogen concentrations at temperatures 400 to 600 C, pressure of 10 to 30 atm, and gas velocity from 0.18 to 5.8 ft per sec (3 < Rep < 30). The reduction rate was found to be mainly controlled by diffusion through the boundary layer and through the pores of the reduced copper phase. The following correlation was proposed: Scott in an earlier work studied the reduction of fixed beds of cupric oxide wire and found that the rate of flow of the gas stream through the bed had a controlling effect on the rate of reduction. The same mass-transfer phenomenon was observed by Bond and clark13 on a similar reduction system. The analogy between mass and heat transfer through the boundary layer which exists between a solid surface and the bulk stream stems from the similarity of the differential equations representing these phenomena

Jan 1, 1967

By Tibor Stefansky, John E. Dorn

MOTT and Nabarro1-5 were first to illustrate the importance of the flexibility of dislocations in accounting for the strengthening that metals undergo due to the presence of internal-strain centers. Such strain-centers might arise from a number of causes such as radiation damage, the presence of semicoherent and coherent precipitates and clusters, as well as individually dispersed interstitial and misfit substitutional solute atoms. Each strain-center induces positive and negative shear stress fields on the slip planes of the surrounding alloy matrix. In order to effect plastic deformation, therefore, the alloy must be subjected to sufficiently high applied shear stresses to push dislocations past all such internal stress fields. If dislocations were inflexible and moved as rigid lines, they would be equally pushed and pulled by internal stress fields. At this extreme the strengthening would be vanishingly small. Dislocations, however, are not rigid; they are flexible and extensible. They wiggle between positive and negative strain-centers, thus increasing their line energy at the expense of their interaction energy with strain-centers. cottrel16 and Friedel7,8 have independently presented lucid reviews of the significance of the Mott-Nabarro dislocation-flexibility concept to the strain-center strengthening of alloys. Their analyses however were only semi-quantitative. There is evidence in the recent literature of renewed interest in a more rigorous analysis of flexibility. Thus, Gleiter9 and Gerald" have shown that the calculated strain-energy interaction between a dislocation and the stress fields of coherent precipitates can be seriously in error if the flexibility of the dislocation is not taken into account. This report will be concerned with a more detailed analysis of the problem based on the following approximations: 1) Although many types of strain-centers exist, the following analysis will be limited to the case of solute-atom strain-centers in fcc substitutional alloys. 2) To facilitate the analysis by avoiding statistical considerations, the strain-Centers are assumed to be in regular arrays on the slip plane. Although the quantitative results are somewhat dependent on the type of array that is assumed, the qualitative trends are similar for various arrays that were studied. 3) An adjustment of the results from those for square arrays to those for the more realistic case of a random distribution of strain-centers is accomplished by adopting the interesting statistical theory first introduced by Kochs,11,12 elaborated on by Dorn, Guyot, and stefansky,13 and analyzed by Foreman and Makin14 in their computerized experiments. 4) For simplicity the dislocation lines are taken to wiggle about their edge orientation and no correction is applied to their line energy for deviations from edge configurations or for the elastic interaction between segments of the now curved dislocation. It will be shown that for extremely low concentrations of atomic strain-centers the strengthening increases with the square root of their concentration. For slightly higher concentrations the strengthening rate becomes less rapid. At a critical concentration a maximum strength is obtained and a decrease in the strengthening takes place as the concentration of solute atoms is further increased. These trends are a direct consequence of dislocation flexibility. They arise from changes in the amplitude of the waviness of the dislocation line at the yield stress with solute atom concentration. Despite the simplifying assumptions that were made, the results agree qualitatively with appropriate experimental data. I) STRESS FIELDS ON SLIP PLANES Internal stresses are introduced in a lattice whenever a host atom of radius ro is replaced by another that has a different atomic radius. According to the classical theory of linear elasticity,15 the stress field about a solute atom at the origin of a spherical coordinate system is given by arr=-4G€(?_0)3 ffflfl ="W =2G€{t) f°rr^ro(l+e) UJ where G is the shear modulus of elasticity and Y, = ro(l + E) is the radius in situ, of the substituted atom. As shown by ~shelb~,&apos;~ this approximation assumes that the bulk modulus of elasticity of the substituted atom is identical with that of the host species. ~abarro&apos;~ suggested that the strain E can be deduced

Jan 1, 1970

By R. M. Waterstrat, E. C. van Reuth

BINARY- alloy phases having the A15-type crystal structure have been described as occurring at a simple and more or less invariant stoichiometric composition (A3B) which corresponds to the relative number of atoms occupying each of the two crystallographi lattice sites in this structure.1,2 It is frequently assumed, therefore, that each crystallographic site is occupied exclusively by one kind of atom. In most cases, however, there have been insufficient experimental data to establish whether atomic ordering is, in fact, complete. Recent studies have shown that binary A15-type phases are sometimes stable over an appreciable composition range3&apos;&apos;* and, occasionally, the composition range of stability does not even include the "ideal" A3B stoichiometric composition.5-7 We have observed the existence of nonstoichiometric A15-type phases in the binary systems Cr-Pt and Cr-Os. This has not been reported in previous work on these alloy systems.1,8-11 A series of alloys, each weighing approximately 30 g, was prepared by are-melting in an Ar-He atmosphere using 99.999 pct Cr, 99.999 pct Os, and 99.99 pct Pt as starting materials. Each alloy was melted four times with a total weight loss of less than 1 pct. The stoichiometric (A3B) alloys were sealed in evacuated quartz tubes and annealed at 1200°C for periods of time ranging from 3 days to 2 months. Examination of the alloy microstructures revealed that little change had occurred over this time interval and it was therefore assumed that the microstructures were fairly representative of equilibrium conditions. No evidence of contamination was observed although there was apparently some loss of chromium which was confined to a thin layer at the surface of the specimens. The quartz tubes were quenched from the annealing temperature into cold water. X-ray diffraction and metallographic examination of the stoichiometric alloys revealed an estimated 10 to 30 pct of second phases which were tentatively identified as phases previously reported in these binary-alloy systems.8-11 A second series of alloys was prepared by mixing -325 mesh metal powders having a nominal purity of 99.9 pct and compressing these mixed powders in a cylindrical die at a pressure of 43,000 psi. These alloys, each weighing 15 g, and some of the arc-melted alloys were annealed in a high-temperature vacuum furnace heated by tantalum strips at a pressure of 10-8 Torr and were rapidly cooled by turning off the furnace power. X-ray and metallographic examination of both series of alloys served to establish the composition ranges of the A15-type phases. Although some chromium losses occurred during the vacuum annealing, they were largely confined to a thin layer on the outer surfaces of the samples. It was established that the A15 phases occur in the Cr-Pt system at 21 ± 1 at. pct Pt after 1 week at 1200°C and in the Cr-Os system at 28 ± 1 at. pctOs after 1 day at 1400°C (see Table I). We also observed that an arc-melted stoichiometric (A3B) alloy in the Cr-Ir system was single-phase (A15-type) in the "as-cast" condition in agreement with previous work.8,13 In addition we obtained a sample of the Cr-Os A15-type phase from Argonne National Laboratory. This alloy contained less than 1 pct second phase12 and was submitted to a density measurement. The density measurement yielded a value of 11.14 g per cu cm in comparison to a theoretical value of 11.25 g per cu cm calculated using the observed lattice constant (4.6806Å) of this alloy. The uncertainty in measurement was 0.1 pct but the sample may have contained some cracks or minor imperfections which could account for the low experimental value. We have also studied the atomic ordering in these phases by means of integrated line intensity measurements using thick, flat, rotating powder samples and CuK a radiation in an X-ray diffractometer. We have obtained order parameters of 0.90 for the Cr-Pt phase, 0.89 for the Cr-Ir phase, and 0.64 for the Cr-Os phase using the formula: where s is the usual Bragg and Williams order parameter, ra is the fraction of chromium atoms in A sites, and FA is the fraction of chromium atoms in the alloy. The values obtained are estimated to be accurate within ±4 pct. If the unusually small value for the order parameter of the Cr-Os A15 phase were due to the existence of lattice vacancies on the "B-atom" sites, then a density of 10.04 g per cu cm would be expected in contrast to the observed value of 11.14 g per cu cm. We, therefore. conclude that the fraction of lattice vacan-

Jan 1, 1967

By Milton Ohring, Stephen M. Edelglass

THE recently determined coefficients for diffusion of very dilute impurities in aluminum are shown in Table I. Of these data the activation energies for Ag110, cu54, Mn54 and zn85 are clustered about the value of self-diffusion in aluminum; for the remaining

Jan 1, 1970

By Paul Weir

During the past decade, methods of producing bituminous coal in the state of Illinois, which ranks third in production among the states in which bituminous coal is mined, have undergone great changes. From less than one million tons in 1923, the strip-mine production has gradually increased to a high of 11,725,870 tons in 1937. From a negligible amount prior to 1927, the amount of coal mechanically loaded underground had increased to a high of 28,374,362 tons in 1937. The amount manually loaded in 1937 reached a low of 12,332,023 tons. In this same year, this state ranked first in strip-mine production, also in mechanically loaded production. For this reason a study of the influence of mechanization on location of production in Illinois may be helpful in anticipating what may happen in other producing states. The reason for the changes in methods lies in the differences in costs of production. The Bureau of Research and Statistics of the National Bituminous Coal Commission has made public the following costs of production by various methods in the state of Illinois (district 10) for the last nine months of 1937: all mines, $1.7602 per ton; strip mines, $1.4319; mechanical loading mines, $1.7457; hand loading mines, $2.1793; all underground mines, $1.8703. These are weighted averages for the entire district. Inasmuch as production in 1937 was reported from 58 counties scattered over two-thirds of the area of the state and from five different seams varying in thickness from less than 3 ft. to as much as 12 ft., it is apparent that the location of production must be influenced by the extent of mechanization possible in the various producing counties. SHIFT in Production The term "mechanization" is commonly used to designate the coal-loading operation. However, in a broader sense it embraces the use of any and all mechanical and electrical equipment on the surface and underground. Strip mining is an intensive form of mechanization. The mechanical cleaning of coal is a form of mechanization. Cutting machines and motor haulage likewise are forms of mechanization, hence

Jan 1, 1940

By Paul Weir

During the past decade, methods of producing bituminous coal in the state of Illinois, which ranks third in production among the states in which bituminous coal is mined, have undergone great changes. From less than one million tons in 1923, the strip-mine production has gradually increased to a high of 11,725,870 tons in 1937. From a negligible amount prior to 1927, the amount of coal mechanically loaded underground had increased to a high of 28,374,362 tons in 1937. The amount manually loaded in 1937 reached a low of 12,332,023 tons. In this same year, this state ranked first in strip-mine production, also in mechanically loaded production. For this reason a study of the influence of mechanization on location of production in Illinois may be helpful in anticipating what may happen in other producing states. The reason for the changes in methods lies in the differences in costs of production. The Bureau of Research and Statistics of the National Bituminous Coal Commission has made public the following costs of production by various methods in the state of Illinois (district 10) for the last nine months of 1937: all mines, $1.7602 per ton; strip mines, $1.4319; mechanical loading mines, $1.7457; hand loading mines, $2.1793; all underground mines, $1.8703. These are weighted averages for the entire district. Inasmuch as production in 1937 was reported from 58 counties scattered over two-thirds of the area of the state and from five different seams varying in thickness from less than 3 ft. to as much as 12 ft., it is apparent that the location of production must be influenced by the extent of mechanization possible in the various producing counties. SHIFT in Production The term "mechanization" is commonly used to designate the coal-loading operation. However, in a broader sense it embraces the use of any and all mechanical and electrical equipment on the surface and underground. Strip mining is an intensive form of mechanization. The mechanical cleaning of coal is a form of mechanization. Cutting machines and motor haulage likewise are forms of mechanization, hence

Jan 1, 1940

By Cyril Smith

SEVERAL investigators, mainly concerned with the mechanical proper-ties of the alloys, have studied the so-called aluminum bronzes after various quenching and reheating treatments. Of these works, perhaps the most complete is that of Bouldoires,1 who studied changes of length, electrical conductivity, thermoelectric force, hardness and micro-structure oh tempering quenched alloys containing 5 to 20 per cent of aluminum, although the work of Carpenter and Edwards,2 Curry,3 Greenwood,4 Braesco,5 Matsuda;6,7 Grard8 and others has added much to our knowledge of the changes occurring during tempering. The so-called acicular ß decomposes on tempering at temperatures between 350° C. and the eutectoid, giving rise to a Widmanstätten structure of a needles in a matrix of d or fine a + d, associated with an increase in hardness and almost complete loss of ductility. Matsuda, studied the&apos; eutectoid transformation by means of dilatation and electrical "conductivity measurements during cooling at different rates. He found that on cooling at the rate of 10° C. per minute there was a decrease in electrical resistance and in length instead of the usual increase which occurred with slow rates of cooling. On tempering the rapidly cooled samples, the increase commenced at about 400° C. and at 520° C. the resistance and length had reached the equilibrium values. These peculiarities he accounted for as being due to a transitional phase ß&apos; being formed, ß having an electrical resistance and volume less than either ß or a + d.

Jan 1, 1933

By R. B. Gilmore

The North Texas district, as herein defined, includes the counties of Archer, Baylor, Clay, Cooke, Foard, Hardeman, Jack, Kiiox, Montague, Wichita, Wil-barger, and Young. Jack and Young Counties are included for the first time so that this district will correspond with District No. 9 of the Texas Railroad Commission. This area covers generally the crest and south flank of a system of buried mountains known as the Red River uplift. The oil and gas accumulations along this feature are in traps, which, although localized by structures incident to the regional uplift, usually are modified by stratigraphic changes in the sediments. The structural deformation caused by the Red River uplift is modified by the Rend arch, which is a broad anticline plunging northward from the Llano uplift in central Texas through Young and into Archer Counties. The fields in southern Archer, southeastern Baylor, southwestern Clay, and western Jack Counties arc on the extreme north end and along the flanks of the Bend arch and have generally the same type of oil and gas accumulation as the other fields in this district. Recent exploration has been along the flanks of the Fort Worth syncline, which is east of the Bend arch and south of the Red River uplift and extends into southeastern Clay and southwestern Montague Counties and along the eastern part of Jack County. The larger part of past oil and gas produc- tion has come from Pennsylvanian strata, with less important amounts lrom the Permian, and minor quantities from the Mississippian and Ordovician. Developments during 1943 About 1100 wells were drilled in the district during 1943 and more than 500 oil wells were completed, an increase from 1942. of approximately 12 per cent in the number of successful drilling operations of the total wells drilled. The addition of Jack and Young Counties to this district accounts for part of this increase, almost 150 wells being completed in the two counties. Production increased slightly over the previous year as a result of an increase in the number of producing wells and a greater demand for this high-gravity, sweet crude oil. The average depth of discovery wells was about 400 ft. deeper than in 1942. Although more discoveries produced from horizons below the base of the Strawn series than from those above the Straw, the deeper horizons, including the Bend series of the Pennsylvanian, the Mississippian limestone and Ellenburger of the Ordo-vician, largely were dissappointing from the viewpoint of major additions to oil reserves. The largest single addition to the reserves was in the basal Strawn sand in the Walnut Bend field, Cooke County. During the year, 31 wells were completed, both in the field and as cxtensions. The most active arca Was Jack County, in which five fields or potential fields were discovered, although only 44 oil wells were completed.

Jan 1, 1944

By R. B. Gilmore

The North Texas district, as herein defined, includes the counties of Archer, Baylor, Clay, Cooke, Foard, Hardeman, Jack, Kiiox, Montague, Wichita, Wil-barger, and Young. Jack and Young Counties are included for the first time so that this district will correspond with District No. 9 of the Texas Railroad Commission. This area covers generally the crest and south flank of a system of buried mountains known as the Red River uplift. The oil and gas accumulations along this feature are in traps, which, although localized by structures incident to the regional uplift, usually are modified by stratigraphic changes in the sediments. The structural deformation caused by the Red River uplift is modified by the Rend arch, which is a broad anticline plunging northward from the Llano uplift in central Texas through Young and into Archer Counties. The fields in southern Archer, southeastern Baylor, southwestern Clay, and western Jack Counties arc on the extreme north end and along the flanks of the Bend arch and have generally the same type of oil and gas accumulation as the other fields in this district. Recent exploration has been along the flanks of the Fort Worth syncline, which is east of the Bend arch and south of the Red River uplift and extends into southeastern Clay and southwestern Montague Counties and along the eastern part of Jack County. The larger part of past oil and gas produc- tion has come from Pennsylvanian strata, with less important amounts lrom the Permian, and minor quantities from the Mississippian and Ordovician. Developments during 1943 About 1100 wells were drilled in the district during 1943 and more than 500 oil wells were completed, an increase from 1942. of approximately 12 per cent in the number of successful drilling operations of the total wells drilled. The addition of Jack and Young Counties to this district accounts for part of this increase, almost 150 wells being completed in the two counties. Production increased slightly over the previous year as a result of an increase in the number of producing wells and a greater demand for this high-gravity, sweet crude oil. The average depth of discovery wells was about 400 ft. deeper than in 1942. Although more discoveries produced from horizons below the base of the Strawn series than from those above the Straw, the deeper horizons, including the Bend series of the Pennsylvanian, the Mississippian limestone and Ellenburger of the Ordo-vician, largely were dissappointing from the viewpoint of major additions to oil reserves. The largest single addition to the reserves was in the basal Strawn sand in the Walnut Bend field, Cooke County. During the year, 31 wells were completed, both in the field and as cxtensions. The most active arca Was Jack County, in which five fields or potential fields were discovered, although only 44 oil wells were completed.

Jan 1, 1944

By W. A. Anderson, R. F. Mehl

RECRYSTALLIZATION of cold-worked metals has long been known to proceed by a process of nucleation and growth.1 When a cold-worked metal is heated to a temperature at which recrystallization will ensue, nuclei of new grains, essentially strain-free, appear and grow. As the process proceeds, nuclei continue to appear and to grow, until the cold-worked matrix has been entirely consumed and recrystallization has been completed (Fig. I). Conducted isothermally, a measurement of the fraction of the matrix recrystallized plotted against time, yields an isothermal recrystallization curve, showing the time course of the recrystallization process (Fig. 2).2 Evidently, then, the rate of recrystallization is determined by the rate at which nuclei form and the rate at which they grow. The rate of nucleation N is the number of nuclei that form in unit time in unit volume of the unrecrystallized matrix, and the rate of growth G is the increase in radius of the recrystallized grain per unit time. In recent years attempts have been made to determine N and G as these vary with the well-recognized variables affecting recrystallization: time, temperature, degree of deformation, etc.&apos; Such studies yield information that is more fundamental than that conveyed by the conventional recrystallization diagram,&apos; since the rate of recrystallization is thus analyzed into its two component rates.2 Methods are now available by which N and G can be measured, and analytical expressions have been developed for the interrelationships among N, G, the isothermal recrystallization curve, and the final grain size, which greatly facilitate analysis.2-4 The application of these methods has been demonstrated recently for the recrystallization of silicon ferrite.2 Data on N and G in dependence upon the recognized recrystallization variables are, however, very fragmentary;* values of N and G have been determined for some metals, but the effect of temperature, which would yield the fundamentally important activation energies, has been too little studied. Thus far there has been no detailed study of the recrystallization of any one metal in terms of N and G over appreciable ranges of the variables time, temperature, degree of deformation, and original grain size. It is the purpose of the present paper to provide such a study, employing aluminum.

Jan 1, 1945

By E.G. Lewis, l.M. Barker

The literature of milling is replete with papers devoted to the subject of ball milling, all of which no doubt have contributed in one way or another to progress in that art. In this paper reference will be made to only a few of the many authors, but the value of the contributions of all who have written on that subject is hereby acknowledged. With a few exceptions the efforts of most students of the subject have been devoted to laboratory investigations of principles. Davis1 was one of the first to report on plant-scale investigations and to present to mill men certain criteria for the guidance of ball-milling practices. His conclusions with respect to the significance of sizing analyses of classifier sands in their relation to the factors of mill speed and ball sizing are particularly referred to. Those conclusions were: 1. If the balls are large or the speed of the mill is high, crowding will appear at the finer sizes in the classifier sands. 2. If the balls are small or the speed is low, crowding will appear at the coarser sizes in the classifier sands. 3. The indications are that best efficiency is obtained when the screen analysis of the sands show a minimum crowding at any size. The last conclusion was qualified by the statement that it had not been proved conclusively. It is surprising, however, that the litera- ture of later years reveals little evidence that millmen have made any serious attempt to apply those criteria. This may, perhaps, be explained by the fact that the average plant-scale ball-milling problem presents so many variables that an investigation of any one of them encounters the problem of control of the others—a problem that often is unsurmountable in a small plant. In a large plant, in which there is a duplication of grinding units in parallel operation, opportunity may be afforded for determining the value of such criteria. Nevertheless, a study of published data from grinding circuits of both large and small plants suggests that either Davis&apos; criteria have been tried and found inapplicable or have never been given consideration. For the purpose of testing Davis&apos; conclusions and with improvement of ball-milling efficiency as the final objective, a test program was initiated in the concentrator of the New Cornelia branch of the Phelps Dodge Corporation early in 1938. The practices of that plant have already been described.2 The fine-grinding units are arranged so that any one of eight units may be operated as a test unit and its results compared with those of the remaining units. All units receive similar feed from a common storage bin, in which the product of the fine-crushing plant is bedded by traveling tripper. The ball mills are all similar in size and operated at the same speeds, and are individually metered. The feeder conveyors of each unit are equipped with Merrick weightometers. The test program as initially outlined proposed investigation of the following:

Jan 1, 1943

By L. M. Barker, E. G. Lewis

The literature of milling is replete with papers devoted to the subject of ball milling, all of which no doubt have contributed in one way or another to progress in that art. In this paper reference will be made to only a few of the many authors, but the value of the contributions of all who have written on that subject is hereby acknowledged. With a few exceptions the efforts of most students of the subject have been devoted to laboratory investigations of principles. Davis1 was one of the first to report on plant-scale investigations and to present to mill men certain criteria for the guidance of ball-milling practices. His conclusions with respect to the significance of sizing analyses of classifier sands in their relation to the factors of mill speed and ball sizing are particularly referred to. Those conclusions were: 1. If the balls are large or the speed of the mill is high, crowding will appear at the finer sizes in the classifier sands. 2. If the balls are small or the speed is low, crowding will appear at the coarser sizes in the classifier sands. 3. The indications are that best efficiency is obtained when the screen analysis of the sands show a minimum crowding at any size. The last conclusion was qualified by the statement that it had not been proved conclusively. It is surprising, however, that the litera- ture of later years reveals little evidence that millmen have made any serious attempt to apply those criteria. This may, perhaps, be explained by the fact that the average plant-scale ball-milling problem presents so many variables that an investigation of any one of them encounters the problem of control of the others—a problem that often is unsurmountable in a small plant. In a large plant, in which there is a duplication of grinding units in parallel operation, opportunity may be afforded for determining the value of such criteria. Nevertheless, a study of published data from grinding circuits of both large and small plants suggests that either Davis&apos; criteria have been tried and found inapplicable or have never been given consideration. For the purpose of testing Davis&apos; conclusions and with improvement of ball-milling efficiency as the final objective, a test program was initiated in the concentrator of the New Cornelia branch of the Phelps Dodge Corporation early in 1938. The practices of that plant have already been described.2 The fine-grinding units are arranged so that any one of eight units may be operated as a test unit and its results compared with those of the remaining units. All units receive similar feed from a common storage bin, in which the product of the fine-crushing plant is bedded by traveling tripper. The ball mills are all similar in size and operated at the same speeds, and are individually metered. The feeder conveyors of each unit are equipped with Merrick weightometers. The test program as initially outlined proposed investigation of the following:

Jan 1, 1943

By Charles H. Eldridge, Robert J. Anderson

When a metal or alloy is poured into a mold, internal stresses are set up by the cont,raction in volume on passing from the liquid state at the temperature of pouring to the solid state at the ordinary temperature. It is assumed by the writers that all castings are internally stressed. That any casting is internally stressed is shown by its warping or distortion on maturing at the ordinary temperature, by warping or cracking on heating, or by cracking or distortion on machining. In the investigation made by the writers, the internal stresses in cast non-ferrous alloys were studied with a view to examining the effects of heat treatment (i.e., simple anneal) on the release of such stresses. Data have been obtained that show quantitatively that internal stresses can be removed by appropriate heat treatment. The investigation was limited to a study of the effect of heat treatment on stress release in cast rings of the 87:7:5:1 copper-tin-zinc-lead alloy. The writers are indebted to E. G. Fahlman for the method used for inducing stress in cast rings; to M. E. Boyd for microscopic examination and for other aid; and to G. B. Dalrymple for the chemical analyses. General Information While casting stresses have been discussed considerably, they have usually been treated in a general way, and so far as the writers know no measurements of the magnitude of internal stresses in castings have been reported. It has been suggested by many investigators, particularly in the case of steel castings, that castings are internally stressed, and that these stresses can be removed by annealing. In a casting, the internal

Jan 1, 1923

By Robert J. Anderson, Charles H. Eldridge

When a metal or alloy is poured into a mold, internal stresses are set up by the cont,raction in volume on passing from the liquid state at the temperature of pouring to the solid state at the ordinary temperature. It is assumed by the writers that all castings are internally stressed. That any casting is internally stressed is shown by its warping or distortion on maturing at the ordinary temperature, by warping or cracking on heating, or by cracking or distortion on machining. In the investigation made by the writers, the internal stresses in cast non-ferrous alloys were studied with a view to examining the effects of heat treatment (i.e., simple anneal) on the release of such stresses. Data have been obtained that show quantitatively that internal stresses can be removed by appropriate heat treatment. The investigation was limited to a study of the effect of heat treatment on stress release in cast rings of the 87:7:5:1 copper-tin-zinc-lead alloy. The writers are indebted to E. G. Fahlman for the method used for inducing stress in cast rings; to M. E. Boyd for microscopic examination and for other aid; and to G. B. Dalrymple for the chemical analyses. General Information While casting stresses have been discussed considerably, they have usually been treated in a general way, and so far as the writers know no measurements of the magnitude of internal stresses in castings have been reported. It has been suggested by many investigators, particularly in the case of steel castings, that castings are internally stressed, and that these stresses can be removed by annealing. In a casting, the internal

Jan 1, 1923