ALTHOUGH the refining period of the heat is generally defined as A starting after the charge has been completely melted, it may more properly be considered as beginning with the first efforts to facilitate the shaping up of the slag and the making of corrective additions for the control of slag or metal composition. Such actions may be initiated during the latter half of the lime boil. The early part of the refining period may, then, in essence overlap the latter part of the melting period. The primary aims of the refining period are to reduce phosphorus and sulphur from the steel bath to levels safely below the maximum contents specified, to eliminate carbon as rapidly as possible and still allow time for proper conditioning of the slag and attainment of the necessary bath temperature, and to deliver the heat ready for tapping or furnace deoxidation, with slag in the proper physical and chemical condition, and with carbon and oxygen contents and the temperature of the steer bath at the proper levels for the composition and grade of steel being produced. The particular conditions that fulfil these aims are distinctly different, depending upon whether the steel is to be finished according to fully-killed, semikilled, or rimming practice and also depending upon the carbon range specified. Regard- less of the type of charging practice employed, the object of the refining period is to produce repeatedly the desired finishing and tapping conditions for the grade of steel being produced. The variations and proportions of raw materials used in the charge may cause some variations in the degree of control required during refining, but not in the method of control. The refining period can therefore be discussed from a viewpoint largely independent of charging and melting practice. SHAPING UP THE SLAG In the first helper's vocabulary, refining practice consists in "shaping up" his heat. This includes elimination of sulphur, phosphorus, and carbon, putting the slag in proper condition, and adjusting bath temperature. Shaping up the slag is a major consideration because

Jan 1, 1944

By J. H. Fletcher

AIR has been cooled, heated, washed; humidified and dehumidified for many purposes and in many industries. At a number of metal mines air is conditioned to reduce the high humidity and unbearable heat found in deep workings, and at some mines air is washed to allay siliceous dust. Steam is introduced into the intake air at many coal mines, particularly in winter, for the purpose of keeping loose coal dust so moistened that the hazard of an explosion is lessened. This paper will describe a further successful application of air conditioning in a coal mine, where, for over three years, all intake air has been cooled to a constant temperature for the sole purpose of preventing roof falls.

Jan 1, 1931

By E. Miller, J. M. Eldridge, K. L. Komarek

The thermodynamic properties of- liquid Mg-Pb allojs have been determined by an isopiestic method from 18 to 42 at. pct Pb and by a thevmodynumic analysis of the phase diagram frofiz 0 to 100 at. pct Pb. In the overlapping composition range the magneszupn activity values derived by the two methods are in excellent agreement, thus mutually supporting the correctness of the Mg-Pb phase diagram previously determined by the authors and of the acticitzes deriz~ed isopiestically. SEVERAL studies have been made of the thermody-namic properties of liquid Mg-Pb alloys. Wagner and Engelhardt,1 Lantratov,2 Knappwost,3 Sryvalin et al.* and Wilson5 used the electromotive-force method, Scheil and Wolf8 and Schmahl and Sieben" applied the transpiration technique, and the present authors8 utilized the phase diagram to determine the activity of magnesium in the Mg-Pb system. The results of these studies are not in very good agreement and could not be incorporated into a general systematic analysis of the thermodynamic properties of the homologous series of the Mg-Group IV B systems Mg-Pb,8 Mg-Sn,° Mg-Ge,10and Mg-Si.11 The thermodynamic properties of the Mg-Pb system were therefore re investigated by an isopiestic technique which has been developed for similar studies in the Mg-SnB and Mg-Ge10 systems- Lead specimens, contained in iron or graphite crucibles, were heated in a temperature gradient in an evacuated and sealed titanium reaction tube and equilibrated with magnesium vapor of known vapor pressure to form alloys of compositions which depended on their temperatures, the temperature of the magnesium vapor source, and the thermodynamic properties of the system. EXPERIMENTAL PROCEDURE Magnesium (Dominion Magnesium Ltd., Toronto, Canada) of 99.99+ pct purity and lead (American Smelting and Refining Co.) of 99.999 pct purity were used. In the early experiments, Runs 2 and 3, the alloys were contained in uncovered high-purity iron crucibles. Alloys formed in the uncovered iron crucibles had to be chemically analyzed owing to the slight volatility of lead under the imposed experimental equilibration conditions. The compositions of these alloys were determined by a gravimetric analysis of lead as lead chromate. To avoid this problem, the remaining runs were made in covered graphite crucibles machined from high-density (1.92 g per cu cm) graphite rods (Basic Carbon Corp., Sanborn, N.Y.) which had a maximum ash content of less than 0.04 pct. The non- i reactivity of graphite with lead and magnesium has been previously established,' and the experimental procedure has been described in full detail.' In the runs using covered graphite crucibles it was found that the weight increases of the crucibles and their contents after equilibration equaled the magnesium contents of the alloys within the accuracy of the chemical analysis (i0.3 at. pct Pb). Clearly, the small lid openings of the graphite crucibles prevented significant lead losses during a run, and the weight increase was therefore taken as the magnesium content of the alloys. EXPERIMENTAL RESULTS At thermodynamic equilibrium the magnesium partial pressure of the specimens equaled that of the reservoir. Since the magnesium reservoir was always maintained at the temperature minimum of the system, the activity of magnesium of any specimen was given by the ratio of the magnesium reservoir pressure to the vapor pressure of pure magnesium at the specimen temperature. The standard state was chosen as liquid magnesium and the vapor pressure of liquid magnesium

Jan 1, 1968

IN NOVEMBER 1933 I had the pleasure of receiving an autographed copy of a small brochure entitled "Birth of the Porphyry Coppers." The author, James Colquhoun, a distinguished British mining engineer, had been the dominant figure in the Arizona Copper Company, Limited, which, until its acquisition by the Phelps Dodge Corporation in 1921, had been the principal producer of copper in the Morenci district. In addition to the highly productive Humboldt and Longfellow mines it owned the Clay property, which, of course, has now become Arizona's No. 1 copper mine. Except for Utah Copper it is the premier Porphyry copper enterprise in the United States. Mr. Colquhoun's little volume was inspired by THE PORPHYRY COPPERS which had appeared early that year. In a most courteous and friendly way he adduces data to show that "we (Arizona Copper Company Limited) were successfully treating low-grade porphyry ores in quantity for at least four years (1901 to 19W) before the Utah Copper Company did anything at all." This last remark is based on the figures in THE PORPHYRY COPPERS showing that Utah's first production came from the Copperton pilot plant in 1905. Mr. Colquhoun traces the story of Morenci beginning in 1883 when he first arrived there. He tells how the rich self-fluxing ores (containing lime- stone, silica, and iron in proportion to permit direct smelting to produce black copper) were gradually exhausted. High-grade siliceous ore could be mixed in limited quantity with the self-fluxing ores; and oxidized ores were leached to contribute substantially to the production of the district. But

Jan 1, 1957

By James Paul

BEGINNING in December, 1933, and continuing to the close of April, 1934, large sums of money were expended in the states of Pennsylvania, Ohio and West Virginia through the conduct of Federal and State Civil Works Administration, financed by the Government as a part of the President's recovery program to furnish employment to mine employees idle as a result of the economic depression. PURPOSE OF THE PROJECT The protection of the public health against the pollution of public water supply by acid mine drainage was the incentive that prompted the request that the sealing of abandoned bituminous coal mines be made a Federal project. A paper before the Central Section of the American Water Works Association, Wheeling, W. Va., on Aug. 24, by E. S. Tisdale, Chief Engineer of the West Virginia Department of Health, tersely says: In October, 1933, the combined experience of the U. S. Bureau of Mines and the U. S. Public Health Service and the States of Pennsylvania, Ohio, West Virginia and Kentucky resulted in a report being filed in Washington, first with the Public Works Administration and later with the Civil Works Administration, where it was favorably acted upon, calling for these governmental agencies under the direction of the U. S. Public Health Service to expend $1,500,000 in a unified effort to seal abandoned coal mines in Pennsylvania, Ohio, West Virginia, Kentucky and six other states farther down along the Ohio river. The report referred to was embodied in a petition that was signed by the chief engineers of the State Departments of Health of the several states contiguous to the drainage area of the Ohio River. The project as established under Federal supervision became interstate with respect to the several states involved, and upon the termination of the Federal project on Feb. 15, it was authorized as a State C.W.A. project, effective Feb. 20, under the supervision of the State Departments of Health and the State C.W.A. Administration, which continued to March 29, and was succeeded by the S.E.R.B. of the R.W.D. from April 2 to April

Jan 1, 1935

By Evans B. Mayo

This study examines the structural framework of the Southwest for evidence of the four principal trends of lineament tectonics. It attempts to classify their intersections and compares the positions of those trends that appear most favorable with the positions of the presently known mining districts. This is a controversial topic. The author, in presenting his analysis, is aware that the study of lineament tectonics and relation of ore districts to regional structure is complicated by insufficient data and, unavoidably, by personal bias. The development of lineament tectonics has been summarized by Umbgrove.' Early attempts to fit ore districts into the Cordilleran framework were made by Billingsley and Locke, who do not refer to lineament tectonics, although their appoach is similar; they observe that heat and fluids, including the ore-depositing fluids, are most likely to rise at or near intersections of major structures where the crust is fractured, or weakened, to great depth. As a result of studies distributed over the earth-including ocean basins as well as continents— some tectonists recognize four dominant structural trends: 1) northwest; 2) northeast; 3) nearly east-west, or equatorial; and 4) nearly north-south, or meridional. Baker' proposed a theory to account for these trends and Sonder" called their world-wide arrangement the regmatic shear pattern. Moody and Hill proposed a much more complicated shear network which, although fascinating and perhaps ultimately useful, will not be followed here. In a recent review of deformation within the Cordillera, Wisser mentioned the four fundamental directions. The fact that many geologists deny the existence of the regmatic shear pattern implies that the fundamental structures are far from obvious. It may mean, also, that some geologists are not accustomed to examine regional and world maps analytically. The maps require much study, and certain features should be isolated on overlays. Even so, with the present limited knowledge, uncertainties remain. The following analysis is a qualitative experiment, subject to change as information accumulates, and should be supplemented by the western sheet of the Tectonic Map of the United States.' Many have probably gained the impression that the Cordillera of the West is oriented northwest-southeast and from this, unless experience rules otherwise, it is natural to assume that the structure likewise trends northwest-southeast. To an important extent this is true, yet anyone tracing off the western sheet of the Tectonic Map all the recorded north west-southeast structures may be surprised to see what a small part of the entire area they occupy. In southwestern U. S. (Fig. 1) the northwest-southeast structures are mostly restricted to the eastern, southern, and western parts. The eastern margin of the Cordillera from northern Colorado to the International Boundary near El Paso, Tex., is obviously determined by some structure other than northwesterly ones. In eastern Nevada and far southward toward the Gulf of California many mountain ranges, valleys, and faults are meridional. In the Rocky Mts. of Colorado, and at many places in southern Arizona, the crystalline Pre-Cambrian is foliated northeast-southwest. The Uinta Mts. of Utah trend approximately east-west, in much the same way as a broad belt of transverse, west-northwest structures—the Texas lineament of Hill",' and Ransome10 in southern Arizona, southwestern New Mexico, and southern California. It seems, then that there are four regmatic shear directions in the Southwest, but at many places they are discontinuous, and their projections must be inferred. To clarify these trends the four sets have been isolated into two systems: 1) northwest-northeast and 2) east-west-north-south (Figs. 2 and 3). Northwest-Northeast System: A number of prominent northwest-trending zones of structure are easily recognized. They are designated by circled Roman numerals, the northeast-trending structures by circled capital letters. Perhaps no two geologists would agree completely on the positions of all these belts. Names given below are for convenience only, and may be discarded where other names have priority. (I) The Sierra Nevada-Lower California belt contains the Jurassic-Cretaceous granitic massifs of the Sierra Nevada and Lower California. These

Jan 1, 1959

By F. H. Rhines, A. H. Grobe

The constitution of the indium-zinc alloy series has been investigated by Wilson and Peretti,1 who determined the liquidus and eutectic temperatures by the conven-tional method of cooling curves and the eutectic composition by analyzing eutectic exudations. Recent developments affecting the availability of indium and consequent increased interest in its applications make a more complete knowledge of the constitu- tion of its alloys desirable. As a part of a program far the reexamination of the constitution of indium alloys by precision methods, the indium-zinc phase diagram (Figs. I and 2) has been redetermined in its entirety. The eutectic temperature (I43. 5°C.) reported by Wilson and Peretti has been confirmed exactly, but their value of the zinc concentration at the eutectic, 4 per cent, was found to be high; the new value is 2.8 per cent of zinc. There is also a rather large difference between the forms of the liquidus curves of Wilson and Peretti and those found in the present studies. The solidus curves herein have been located for the first time and the limits of solid solubility have been tenta-

Jan 1, 1944

By A. H. Grobe, F. H. Rhines

The constitution of the indium-zinc alloy series has been investigated by Wilson and Peretti,1 who determined the liquidus and eutectic temperatures by the conven-tional method of cooling curves and the eutectic composition by analyzing eutectic exudations. Recent developments affecting the availability of indium and consequent increased interest in its applications make a more complete knowledge of the constitu- tion of its alloys desirable. As a part of a program far the reexamination of the constitution of indium alloys by precision methods, the indium-zinc phase diagram (Figs. I and 2) has been redetermined in its entirety. The eutectic temperature (I43. 5°C.) reported by Wilson and Peretti has been confirmed exactly, but their value of the zinc concentration at the eutectic, 4 per cent, was found to be high; the new value is 2.8 per cent of zinc. There is also a rather large difference between the forms of the liquidus curves of Wilson and Peretti and those found in the present studies. The solidus curves herein have been located for the first time and the limits of solid solubility have been tenta-

Jan 1, 1944

By Richard McCaffery

WHEN we began the study of blast furnace slags we limited our work at first to a study of those slags containing only lime, alumina and silica. In our paper1 on some of the results of this first work, the solubility of. sulfur in slags containing no magnesia was reported and the question of sulfur solubility and slag viscosity discussed. There has been, for a long time, a very great difference of opinion among metallurgists as to .the effect of magnesia in blast furnace slags, and the literature is full of expressions of the most contrary opinions on the subject. As a result, our next publication2 developed the constitution of slags considered as a four-component system, silica-alumina-lime-magnesia, and advanced an explanation of slag structure which accorded with the facts and with scientific theory. The present paper continues our study of the general subject of slags. As blast furnace slags are included in the silica-alumina-lime-magnesia system, which is a particular case of four-component solutions, we have determined that there are 22 components (Table 1), which may enter into the silica-alumina-lime-magnesia system and that 10 or 12 of these components may be present in blast furnace slags which are within the ordinary ranges of composition. To have a very definite conception of the behavior of these components in a slag, we have developed the theory of the cooling of a four-component solution from the liquid state to the solid and the conclusions that we obtained have been made use of in this paper. On account of the importance of the four oxides and 18 compounds which enter into the silica-alumina-lime-magnesia system, some method of calculating the percentages of the various compounds that are present in the slag when the percentages of the oxides are given, seemed very desirable and we develop a method later herein for doing this, and finally we give illustrations of

Jan 10, 1926

Jan 1, 1910

By A. S. Nowick, E. S. Machlin

One of the main criteria used to rate the heat-resisting properties of alloys is stress rupture.' During a stress-rupture test a tensile specimen is held under a constant load at a constant temperature until it fractures. The chief measurement made during this test is the time requird for rupture at the specific test stress and temperature. It was found empirically from a series of stress-rupture tests at a constant temperature that when the logarithm of the time for rupture is plotted against the logarithm of stress a straight line is obtained within experimental error This method of showing stress-rupture data has been adopted by many investigators and the NACA.' By interpolation and extrapolation from these plots, values of the stresses required to rupture the specimens (the rupture strengths) in 10, roo, and 1000 hr are obtained for specific temperatures. Alloys are then rated for a particular application on the basis of their rupture strengths at the rupture life that most nearly represents the application. Inasmuch as stress rupture is an important criterion in rating heat-resisting alloys, it would be advantageous to know the quantitative dependence of the time lor rupture on stress, temperature, composition, and structure. In order to obtain this information, an investigation was made at the NACA Cleveland laboratory during the spring of 1945. The theory of rate processes was used because it has been found to apply to certain processes such as chemical reactions, viscous flow, and creep that occur at a definite rate for given conditions. It was thought that stress rupture was such a process. An equation was derived that gives, for a given composition and structure, the dependence of the time for rupture on stress and temperature. The investigation is part of a general program to provide information that will lead ultimately to the development of better alloys in order that the efliciency and power output of gas turbines used in aircraft propulsion can be increased. Theory The theory of rate processes will first be discussed as a general theory. It will then be shown that if stress rupture of heat-resisting alloys can be treated as a rate process, certain equations must be satisfied. Later sections will then show that these equations are satisfied. General Theory of Rate Processes The theory of rate processes5 developed by Eyring and others has been applied to chemical reactions as well as to other processes such as viscosity of liquids and diffusion. In every case in which rate-process theory can be applied, there is a small subdivision, so that the macroscopic process is the net effect of all the small processes. This smallest subdivision is called the "unit process." For example, in a chemical reaction the unit process is

Jan 1, 1948

By A. S. Nowick, E. S. Machlin

One of the main criteria used to rate the heat-resisting properties of alloys is stress rupture.' During a stress-rupture test a tensile specimen is held under a constant load at a constant temperature until it fractures. The chief measurement made during this test is the time requird for rupture at the specific test stress and temperature. It was found empirically from a series of stress-rupture tests at a constant temperature that when the logarithm of the time for rupture is plotted against the logarithm of stress a straight line is obtained within experimental error This method of showing stress-rupture data has been adopted by many investigators and the NACA.' By interpolation and extrapolation from these plots, values of the stresses required to rupture the specimens (the rupture strengths) in 10, roo, and 1000 hr are obtained for specific temperatures. Alloys are then rated for a particular application on the basis of their rupture strengths at the rupture life that most nearly represents the application. Inasmuch as stress rupture is an important criterion in rating heat-resisting alloys, it would be advantageous to know the quantitative dependence of the time lor rupture on stress, temperature, composition, and structure. In order to obtain this information, an investigation was made at the NACA Cleveland laboratory during the spring of 1945. The theory of rate processes was used because it has been found to apply to certain processes such as chemical reactions, viscous flow, and creep that occur at a definite rate for given conditions. It was thought that stress rupture was such a process. An equation was derived that gives, for a given composition and structure, the dependence of the time for rupture on stress and temperature. The investigation is part of a general program to provide information that will lead ultimately to the development of better alloys in order that the efliciency and power output of gas turbines used in aircraft propulsion can be increased. Theory The theory of rate processes will first be discussed as a general theory. It will then be shown that if stress rupture of heat-resisting alloys can be treated as a rate process, certain equations must be satisfied. Later sections will then show that these equations are satisfied. General Theory of Rate Processes The theory of rate processes5 developed by Eyring and others has been applied to chemical reactions as well as to other processes such as viscosity of liquids and diffusion. In every case in which rate-process theory can be applied, there is a small subdivision, so that the macroscopic process is the net effect of all the small processes. This smallest subdivision is called the "unit process." For example, in a chemical reaction the unit process is

Jan 1, 1948

By Doll. H. G.

THIS paper discusses a method and apparatus for determining the dip of formations traversed by a drill hole, by means of electrical measurements in the hole. The process consists in recording the Spontaneous Potentials present along three oriented generatrices in the hole, By comparison of the three curves thus obtained, after application of a correction factor to compensate for any deviations of the hole, the dip angle and the dip direction are determined. Excellent accuracy is obtained for dip angles over 10°. Because the method is simple and the apparatus rugged, the measurements are rapid and reliable; consequently, they can be made at all the levels that are of interest at any time after the well has been drilled. Mechanical cores are not needed to evaluate the dips. A convenient, time-saving procedure is to perform the dipmeter survey at the time the electrical log is taken, using for both operations the same cable and truck. Actual examples of results obtained in wells of the Gulf Coast area are given.

Jan 1, 1942

By Roland Blanchard

ABSTRACT RECENT discovery at Mount Isa of copper mineralization in commercial amount at a depth of 1000 ft., coinciding with downward termination of ore at about the same depth within the larger silver-lead-zinc lenses that have been the standby of Mount Isa's production to date, has been cited as an example in support of mineral zoning. A previous paper by the author and Graham Hall1 furnished a detailed description of the geology of the ore at Mount Isa as exposed up to that time, but necessarily dealt mainly with the silver-lead-zinc mineralization. Most of the geologic facts that constitute the first half of the present paper were set forth in the previous one in much greater detail, with full supporting evidence for the facts cited. The large amount of underground development (approximately 20 miles) and the extensive exploration carried out by diamond drilling (100,000 ft.) at Mount Isa, added to extensive microscope work conducted over a period of years, both by the company's staff and by others, had made possible the calculation within fairly close limits of mineralogical composition of the principal mineralized block of ground down to 1000-ft. depth, and had established closely the mineral succession, with reasons for deposition of the various minerals in the patterns now occupied by them. The geologic facts as outlined in the previous paper remain as stated; but because substantial development within the new copper ore body and further exploratory diamond drilling within the new silver-lead-zinc area (Race-course) have taken place since that paper was written, statements and figures relating to those two areas in the present paper supersede those furnished in the previous one. The recent work likewise has established more clearly the paragenetic relationship between the chalcopyrite and galena. Evidence confirming the relationship is furnished in the present paper. The facts of ore occurrence at Mount Isa show [ACCEPTED ZONAL SUCCESSION Silver sulphantimonides Galena Sphalerite Tetrahedrite Arsenical sulphides Chalcopyrite Pyrrhotite MOUNT ISA SUCCESSION Chalcopyrite In the main but Silver sulphantimonides wholly Tetrahedriteably not Galenacontemporaneous Pyrrhotite Sphalerite Arsenical sulphides They show further: (I) that instead of the silver-lead minerals yielding to increased zinc in depth, the zinc yields to increased silverlead; (2) no dovetailing of the silver-lead-zinc sulphides into chalcopyrite takes place; (3) despite the large amount of pyrrhotite deposited in the district (estimated at upward of 100,000,000 tons), its deposition took place under moderately low temperature conditions; (4) no evidence has been found for increase in temperature of deposition, with depth, to deepest exploration in ore (1495 ft.). The anomalous condition at Mount Isa, both as to the unorthodox mineral succession and the largely unorthodox pattern of mineral distribution, is explained in the present paper,

Jan 1, 1943

By J. B. Warriner

Stripping is the name given to the process of removing clay, rock, or other cover from deposits of coal or ore. In this paper it is intended to cover the methods used in carrying on this operation in the anthracite coal regions of Pennsylvania. In doing this, attention will be chiefly devoted to those methods wherein practice in different sections of the region differs, or is susceptible to change or improvement, though it is intended to give as complete data as possible concerning all stages of the operation. The data from which this paper has been prepared have been collected and submitted by a committee† representing the larger users of stripping methods, of which committee the writer has acted as chairman. Data and assistance have also been obtained from various mining men, engineers, contractors and manufacturers of stripping equipment, to all of whom our appreciation is due. Early History and Statistics The earliest mining operation on a commercial scale in the anthracite region was a stripping operation. This was the famous Quarry mine at Summit Hill, where this method was used only because no other method of mining a deposit of the nature found there seemed feasible to the early operators. A description of this stripping from a report published in 1821 is as follows: "The coal mine at present worked by the company lies on the top of a mountain, and appears to extend over some hundred acres of land covered by about 12 ft,. of loose black dirt resembling moist gunpowder, which can be removed by cattle with scrapers, and thrown into the valley below so as never to impede the work. The thickness of the coal is not known, but a shaft has been sunk in it 35 ft. without penetrating through. More than an acre of mine has been uncovered and presents a huge rock of coal, which is easily quarried without blasting."

Jan 1, 1918

By T. E. Leontis, R. S. Busk

WORK was initiated several years ago at The Dow Chemical Company to determine the applicability of powder metallurgy processes to magnesium and its alloys. Although it was found possible to apply the normal techniques of compacting and sintering, it was discovered early that the technique of extrusion offered special promise. This technique and the alloys produced were therefore studied extensively, and the present paper is a partial report of those studies. It is expected that a second paper will discuss more extensively some of the alloy systems simply mentioned here. Although the literature on powder metallurgy is very extensive, there are only two articles dealing with magnesium13,14 and there is no reference to the direct extrusion of the powder of any metal without the preliminary step of compacting. Furthermore, no mention has been made of the possibility of designing alloys by the technique of powder extrusion, particularly alloys that cannot be made in any other way. Sauerwaldl3 discusses the extrusion of magnesium and aluminum powder to produce alloys containing nonequilibrium phases, but again he emphasizes the importance of pre-compacting before extrusion. There seems to be general agreement that some form of hot-pressing is essential to obtain in a compact the full theoretical density of the metal used.'-" The nearest approach to the technique of direct powder extrusion is that of extrusion of pre-sintered compacts,'-" for which the best review through 1944 is that by Kieffer and Hotop.11 Ensign* discussed a specialized technique of "extruding" already compacted and sintered gears for the purpose of sizing. Sauerwa1d13 discussed the compacting and extrusion of magnesium and magnesium-aluminum alloy band-saw chips. The properties of the extruded compacts were found to be comparable with those of extrusions prepared from solid billets. He also extruded a compacted mixture of magnesium and aluminum powder and found the properties to be somewhat different from those obtained on an extrusion made from a cast billet of the same composition. The second reference dealing specifically with the powder metallurgy of magnesium is Stern's patent," in which is described the extrusion of scrap chips and turnings following a hot-pressing and sintering step. Considerable emphasis in most of these articles is placed on the necessity of atmospheric protection to minimize the danger of oxidation. Experimental Procedure The first experiments were made with the small extrusion press shown in fig. 1. With this press, billets of about 1/2 in. diam are used to produce wire

Jan 1, 1951

By C. R. McEwen

The displacement equations of Buckley and Lever-ett' have been successfully applied to the prediction of oil recovery in frontal drives for a number of years. Commonly, the capillary pressure term is omitted from Leverett's fractional flow formula. The resulting satura-tion-vs-distance curves become multi-valued, however. Buckley and Leverett, recognizing that the neglect of capillarity was most likely the cause, proposed that this part of the solution he ignored. An ingenious method of propagating a discontinuity in place of the multi-valued portlon of the curve was devised by Cardwell using "non-capillary displacement theory". However, it would seem that a completc description of the displacement pracess would require the inclusion of capillary forces. Three publications on displacement theory have appeared in which capillary pressure was included. Ter-williger. et al', calculated saturation profiles which matched those which they observed when gas displaced water vertically downward. Based on their study, Jones-Parra and Calhoun5 roposed a method of computing saturation distributions sufficiently removed in time from the initial conditions so that all saturations in the flood front region were assumed to move with the same velocity. This latter assumption corresponds to the tangent construction on the flowing fraction-vs-satura-tion curve proposed by Welge." A numerical solution to the problem of water displacing oil from a water-wet porous medium was recently presented by Blair, ef at'. The initial conditions included a uniform saturation slightly above interstitial water saturation. that is, the permeability to water ahead of the front was not zero. This appeared to result in a region of slowly rising water saturation ahead of the front, at least for the particular set of relative permeability and capillary pressure data used to illustrate the computation. The authors also postulated an "end-effect" at the outflow face of the system, whereby no water could pass out of the system until the water saturation had built up to a high value. The saturation profiles computed under these assumptions show water accumulating at the downstream end of the system while the flood front proper is still traveling toward the outlet. The purpose of this paper is to present the results of a numerical solution to the one-dimensional water-flooding equation in which no outlet end-effect is considered and where there is no flow of water ahead of the flood front. It should be noted that the contemporary paper of Fayers and Sheldon8 deals with the problem under discussion. For a thorough treatment including both capillarity and gravity the reader is referred to their paper.

By J. B. Berkowitz-Mattuck, R. Hopper, L. Kaufman, E. V. Clougherty

MARNOCH has reported on the attractive high-temperature oxidation resistance of Hf-Ta alloys.' In view of current interest in these alloys, three Hf-Ta alloys were tested in the present study. These included a Hf-27Ta alloy and a Hf-20Ta-2Mo alloy which were supplied by Marquardt Corp. and a Hf-20Ta-Zr alloy provided by Illinois Institute of Technology Research Institute.' The microstructure of these alloys was heated inductively in a glass vacuum system; the oxidizing gas, helium carrier plus a known partial pressure of oxygen (35-102 Torr), was continually passed over the sample at temperature for a given time period. The concentration of oxygen in the gas stream was continuously measured by a differential thermal conductivity technique2 so that the rate of oxygen picked up by the sample could be obtained. The flow rates were 0.1 to 0.2 ft per sec in the vicinity of the specimen. The concentration of oxygen did not fall below 50 pct of the input level in any of the experiments. In several cases a single sample was exposed consecutively at a series of increasing temperature levels. In a second system at ManLabs, cylindrical specimens were exposed to flowing air in a z irconia tube which was heated by radiation from a carbon tube resistance furnace. The specimen was heated from room temperature to the test temperature in flowing argon, then oxidized in air flowing at 0.1 to 0.2 ft per sec. Following exposure, the air was displaced by argon and the specimen was cooled. Postoxidation metallography was performed on every sample. The depth of conversion of the metal matrix to oxide was measured as shown in Fig. 1. The conversion depth was obtained by measuring the oxygen-contaminated metallic zone (which is bounded by a dense outer oxide and a subscale oxide region), subtracting its dimensions from the original dimensions, and dividing by two. Preferential oxidation of

Jan 1, 1968

Since production curtailment for other than engineering reasons is gradually disappearing, and more and more wells are now producing at capacity and showing declining production rates, it was considered timely to present a brief review of the development of decline-curve analysis during the past three or four decades. Several of the commoner types of decline curves were discussed in detail and the mathematical relationships between production rate, time, cumulative production and decline percentage for each case were studied. The well-known loss-ratio method was found to be an extremely valuable tool for statistical analysis and extrapolation of various types of curves. A tentative classification of decline curves, based on their loss ratios, was suggested. Some new graphical methods were introduced to facilitate estimation of the future life and the future production of producing properties where curves are plotted on semilogarithmic paper. To facilitate graphical extrapolation of hyperbolic-type decline curves, a series of decline charts was proposed, which will make straight-line extrapolation of both rate-time and rate-cumulative curves possible. Introduction During the period of severe production curtailment, which is now behind us, production-decline curves lost most of their usefulness and popularity in prorated areas because the production rates of all wells, except those in the stripper class, were constant or almost constant. While production-decline curves were thus losing in importance for estimating reserves, an increasing reservoir consciousness and a better understanding of reservoir performance developed among petroleum engineers. This fact, together with intelligent interpretation and use of electric logs, core-analysis data, bottom-hole pressure behavior and physical characteristics of reservoir fluids, eliminated a considerable part of the guesswork in previous volumetric methods and put reserve estimates, based on this method, on a sound scientific basis' At the same time, a number of ingenious substitutes were developed for the regular production-decline curve, which made it possible to obtain an independent check on volumetric estimates in appraisal work, even though the production rates were constant. with the now steadily increasing demand for oil to supply the huge requirements of this global war, proration for reasons of than prevention of underground waste is gradually disappearing. More and more wells are, or will be, producing at capacity or at their optimum rates, as determined by sound engineering practice. With this trend, the character of producing wells seems to regain, more or less, its "individuality," and the old and familiar decline curve appears to have had a comeback as a valuable tool in the hands of the petroleum engineer. It may be timely, therefore, to retrace the development of decline-curve analysis in the past by presenting a brief chronological review of bulletins and papers published during the past three or four decades, which have

Jan 1, 1945

By Y. Okahara, I. Iwasaki

Chlorination behaviors of pure iron and manganese oxides were investigated by combining a thermogravimetric analysis (TGA) technique with batch-boat roasting followed by leaching. Ferrous and manganous oxides could be chlorinated readily, but, in the absence of a reductant, the higher oxides of both iron and manganese were dificult to chlorinate. Thermogravimetric analysis curves were drawn to illustrate the complexities of the reactions, and the possible mechanisms were discussed. Then three manganif-erous materials from the Cuyuna Range of Minnesota were treated by a process involving the selective chlorination of manganese followed by leaching. The results were interpreted in the light of the chlorination mechanisms observed on the pure iron and manganese oxides. One of the unsolved problems challenging Minnesota's mining industry is the development of an economic process to utilize the manganiferous iron ores of the Cuyuna Range. Although these ores constitute one of the major domestic reserves of manganese (estimated at 432 million tons'), their grade is too low for them to be mined solely for manganese. The nearly exclusive dependence of the U.S. steelmaking industry on foreign manganese ores has stimulated research over the years in treating the low-grade Cuyuna ores. As a result, a number of processes have been proposed.'-' Among these processes is chlorination. Chlorination is the high-temperature conversion of metallic oxides to chlorides by either chlorine or hydrogen chloride gas, or by solid chlorides of sodium, calcium, or magnesium. The metallic chlorides are then recovered by either vaporization or leaching. Although chlorination is an old art, it has become popular in recent years for the recovery of such new metals as titanium, zirconium, and niobium; for the removal of impurities like copper, lead, and zinc from pyrite cinder for ironmaking raw materials;' and for the segregation roasting of coppera and nickel' ores. The chlorination processes proposed for manganifer-ous iron ores have been relatively few (hydrogen chloride chloridization-leaching, hydrogen chloride and calcium chloride chloridization-volatilization,' and chlo-rination-selective condensation6), due presumably to the economics and to the corrosion problems involved. However, the successful application of chlorination processes to other ores will undoubtedly contribute to technological advancements in the chlorination of man-

Jan 1, 1971