By W. T. Hicks

The oxidation of CbO was studied by a gravimetric technique from 400° to 1200°C in oxygen. In this temperature range the oxidatiotz is characterized by an irlductive period of low oxidation rate, which becomes shorter as the temperature increases, followed by a rapid parabolic oxidation. The oxidation of CbO cannot be rate controlling in the oxidation of Cb metal in the temperature range, 800° to 1200°C. A thin optically inactive layer has been observed between the metal and Cb2O5 layer of Cb oxidized at 700°C or higher temperatures. Figs. 1(a) and 1(b) show the edge of a sample of Cb reacted to 50 pct of complete oxidation at 800°C. Fig. l(a) taken under bright field illumination shows a layer of oxide adhering to the unoxidized metal core. Fig l(b) taken under polarized light shows that this oxide layer is

Jan 1, 1962

Discussion of the paper of John H. Hall, presented at the New York. Meeting, October, 1913, and printed in Bulletin No. 79, July, 1913, pp. 1247 to 1256. WILLIAM 'R. WEBSTER, Philadelphia, Pa.:-I would like to call ,attention to the fact that the results of the ordinary tension and bend tests do not always give us the information we want even if we figure out the amount of work done. You want a bending test of sufficient width and full thickness. In the case of eyebars, for instance, I have had experience with a 10- by 1-in. eyebar which gave perfectly good results in a full-size test of the finished bar. The 10- by 1.5-in. and 10- by 1.75-in. eyebars from the same heats-of steel were absolutely worthless in full-size tests. The narrow bending tests from all these bars gave good results. Bat after going into the matter fully, we found that if pieces about 3 in. wide and full thickness were used for the. cold bending tests, the heavier material would not stand this test, but failed. That is, in order to check the quality of the rolled bar you should have a wide piece of full thickness for cold bending, as the narrow pieces give misleading results. J. E. JOHNSON, JR., New York, N. Y. :-I would like to ask if there have been any tests made to compare the results of Charpy tests with the true dynamic test similar .to the Wohler test, except that the piece is subjected to a tensile or compressive stress and to alternating stresses in addition, at the same time. This seems to me to approach more nearly than any other test to the conditions of actual service. where the piece is under a fixed initial stress plus a highly variable and often alternating stress. Some tests were made on this plan in England within a year or two. The test piece was Subjected to either a tensile or compressive stress of known amount and simultaneously to alternating stresses in addition. Such a. test as this gives information which we cannot get by a tensile test or even from the tensile strength multiplied by an. elongation. Such tests, however, are exceedingly tedious and require long periods of time in order to obtain valuable results. If material could be subjected to these dynamic tests and the same material to the. Charpy shock test, and if some reasonable qualitative relation could be established between the results of the two tests, then we could assume that the shock test, which is so simple and easy to make, was a measurably accurate test of the dynamic qualities of the material. At present it does not seem

Jan 12, 1913

By E. L. Larison

DURING the early years of the present century a notable interest appeared in American industry in the matter of recovering and render-ing profitable byproducts of manufacturing operations. Among the byproducts of reduction of sulfide ores in many plants large amounts of sulfur dioxide gas were available. In certain instances the concentration of SO2 in the gases evolved was, or could be made, sufficient to make them suitable for manufacturing sulfuric acid. At the Anaconda Reduction works such a condition existed. Large tonnages of copper concentrate were being roasted and the roaster gases were available and suitable as a source of sulfuric acid. Earlier work on a large scale at Martinez, Calif., and in the Ducktown region, Tennessee, had shown the feasibility of manufacturing sulfuric acid from the SO2 contained in gases arising from the reduction of copper sulfide ores. In California and Tennessee the acid found a ready market in manufacture of fertilizers, while the situation regarding disposal of the sulfuric acid was quite different at Anaconda. No local use for acid existed, and a commodity of such low value could not stand freight charges to consuming centers. There was a very large accumulation of sand tailings from the gravity concentration mill below the plant at Anaconda. This material, made by the comparatively crude methods in use up to about 1915, contained about 13 lb. of copper per ton, largely as sulfide minerals. In 1912 serious research work toward recovery of this copper was instituted and after about two years of laboratory and pilot-plant development, a process for accomplishing it was perfected. This process involved roast-ing the sand tailings, leaching the roasted tailings with sulfuric acid, and throwing out the copper by passing the solutions over scrap iron. Under this plan each ton of sand required the introduction of about 70 lb. of 60° Be. sulfuric acid.

Jan 1, 1934

By Benjamin C. Greene, H. Beecher Charmbury

Water is a most remarkable substance, essential for life of all kinds. As well as needing water to survive, man has always used it for agriculture, transportation, recreation, and many other things. When our country was young and inhabited by few people, the streams, rivers, and lakes were able to provide all the clean water needed by man and take away all the wastes created. However, with our growing population and an ever-increasing demand for goods and services, the public, industry, and government at all levels have become acutely aware of the need to manage the nation's water resources more efficiently. Abundant energy from many sources has helped this nation to become the greatest industrial nation in the world. Coal has contributed a major portion of this energy, generating electricity, running railroads, and maintaining national security during wartime. The result has been the highest standard of living in the world and a time of widespread economic prosperity. The use of water in coal mining is somewhat different from its use in most industries. With the exception of water used in cleaning plants, for underground dust control, and for fire protection, most of the water en- countered in coal mining operations serves no useful purpose. In other words, it is an undesirable element and must be removed, otherwise it will interfere with operations, cause potential water quality problems, and may even stop operations by flooding. In the past, removing water from working areas of most mines was usually a fairly simple matter. Pumps with piping were installed at sumps or low spots in the mine and the water was pumped to the surface or to drainage control facilities constructed for the operation. Ditches were often used to collect and drain the water by gravity to the outside or to main sumps for pump discharge. In either case, the water was allowed to flow into the nearest stream or river. The concept of "water is water" was generally accepted without too much concern for what was in

Jan 1, 1981

By J. L. Huitt, IM. L. Slusser, E. E. Glenn, M. L. Slusser

This paper is concerned with: (1) an analysis and interpretation of the filtration characteristics of drilling muds on filter paper, and (2) an interpretation of early stage "filtration" on consolidated synthetic porous media, herein referred to as the "surge loss" period. It is shown that water-loss data can be plotted so as to disclose the existence of a surge period, a non-uni-form cake thickness period, and a constant pressure filtration period. The same periods occur during exposure of consolidated porous media to muds. The data on consolidated porous media indicate that: (1) mud particles bridge pores inside porous media during the surge period, and (2) "filter cake" build-up inside porous media occurs during subsequent filtration. The data also show that the surge loss increases with sample permeability and with pressure differential. INTRODUCTION The phenomenon of mud filtrate invasion into porous sands of a drilling well has been recognized for many years.1,2,3,4 Part of API Code 29 is concerned with the filtration testing of a drilling mud to yield data on this subject. In a number of investigations "plastering properties" of muds were studied,5,6,7,8 "plastering" apparently meaning cake forming properties. In such studies the characteristics (thickness, permeability, and toughness) of the cake and the rate at which the liquid phase of the mud was separated from the solids (filtration rate through the cake, commonly referred to as water loss) were measured or at least considered. From the standpoint of its effect on well productivity, filtrate invasion into "clean" water-wet pay sands (i.e., those containing no clay minerals) may not necessarily be a serious problem. An increase in water saturation in the zone immediately around the wellbore would cause loss of oil permeability. However, in such a system, much of this water may be removed by oil production. If filtration occurs into "dirty" sands (i.e., those containing appreciable clay minerals), clay swelling or other mechanisms may cause losses in oil permeability which cannot be overcome by oil production.'.' The phenomenon of mud particle invasion into the pay sand of a drilling well was considered to be a possible serious factor in the early days of rotary drilling. Opinions varied as to whether drilling fluids "mudded up" and "sealed" oil sands. In 1932 Rubel,9 Gill,10 and Parsons," in separate papers, presented differences of opinion together with some laboratory and field data concerning loss of oil production caused by drilling fluid invasion into pay zones. These papers, and the discussions, furnish a large background on this subject and indicate the very clear thinking of many men at a time when petroleum production technology was in its infancy. Jones and Babson,6 and Silent,' experimentally found that the depth to which mud particles invaded water-saturated sand packs was small (no greater than 1/16 in). Arn-quist12 in 1937 observed loss of water permeability due to invasion of mud particles into water-saturated, consolidated, sandstone samples. Williams and Cannon5 studied the filtra-tion properties of drilling muds and mentioned "sludge" which penetrated a short distance into the water-saturated filtering medium (sand pack). Byck5 concluded that formation permeability had no effect on the plas-

Jan 1, 1958

By J. P. Heller, H. B. Bradley, A. S. Odeh

A potentiometric model technique is presented for determining the areal sweep efficiency of a five-spot well pattern, at and beyond breakthrough. A sharp interface between displaced and displacing fluids is assumed. Although the prototype svstem is referred to as a waterflood operation, obvious changes in the notation and computations will adapt the results to other displacement processes. The results of the study include the following. 1. Areal sweep efficiencies for a five-spot well pattern, at and beyond breakthrough, for mobility ratios (displacing to displaced fluid) of 4:1, 2:1, 1:1 and 1:4. 2. Extension of potentiometric analysis to the investigation of the areal sweep efficiency beyond breakthrough in a five-spot pattern by the application of conformal mapping and conductive-solid models. 3. The use of layers of conductive fabric in representing mobility ratio changes in potentiometric models. 4. The development of a probe mechanism for probing conductive solids. The results obtained by conductive-cloth models agree with earlier areal sweep efficiencies at breakthrough obtained by Aronofsky and Ramey 1 on the potentiometric analyzer using electrolytic-tank models. Results beyond breakthrough differ from those obtained by the X-Ray Shadowgraph technique. Data from this study show that, for mobility ratios greater than one, water cut rises rapidly as fluid is produced after breakthrough. However, for mobility ratios smaller than one, a large increase in area swept resulted with only a small increase in water cut. INTRODUCTION In calculating reservoir performance of waterflood-ing operations and other fluid-injection programs, it is necesssary to estimate the areal sweep efficiency * before and after injected-fluid breakthrough into production wells. Influence of mobility ratio on oil-production history, before and after breakthrough for a five-spot well pattern, has been studied by X-Ray Shadowgraph techniques 2-5 and by gelatin models.6 In none of these investigations was the transition zone controlled experimentally. Steady-state anaiog techniques assume that a vertical and discrete interface exists between the displacing and displaced phase. Thus, when using a potentiometric analysis, it is assumed that no transition zone exists. To determine the areal sweep efficiency beyond breakthrough for a five-spot well pattern using the potentiometric analyzer, four principal problems had to be resolved. These were the following. 1. The laborious method of representing changes in mobility ratio in electrolytic tanks by means of contoured wooden blocks. 2. Vapcrization of the electrolyte solution during the study causing concentration changes and, thereby, variable conductivity. 3. The scale-limitation problem 7 that is accentuated by abrupt eiectrolyte depth changes. 4. A wellbore geometry problem. EXPERIhlENTAL EQUIPMENT AND PROCEDURES CONDUCTIVE-SOLID MODEL The theory, equipment and procedural techniques of the electrolytic-tank potentiometric model have been treaced excellently by Lee8 and by Muskat.9 By the use of a conductive solid to represent the fluid conductivity of the porous media, the need for contouring wooden blocks to represent mobility ratio was eliminated. It was found that a carbon-black coated fabric, Uskon D-16,** could be employed as a fairly uniform conductive media. This material, when stacked in appropriate layers and pressed together, can be used to represent changes in mo-

By R. J. Teitel

The Pb-U system has been investigated by X-ray, thermal, and microscopic analyses. Two pyrophoric intermetallic compounds were found; UPb3 and UPb. The crystallographic structure of UPb3 is reported. A phase diagram was drawn for the system showing three eutectic and one syntectic reaction. AS a result of the interest in uranium metallurgy, the Pb-U system has been investigated. Practically no quantitative data appears in the literature concerning this system. Chips were machined from bars of high-purity uranium obtained from Ames Laboratory and the lead was 99.9 pct high-purity grade from Bel-mont Smelting & Refining Co. The chips were pickled in a dilute solution of nitric acid, washed in water and then alcohol, and dried prior to use for alloy preparation. The lead was simply sheared from the pig with no chemical treatment. Lead and uranium were placed in graphite crucibles and loaded into an induction furnace. In order to insure good alloy formation, the lead was loaded above the uranium to wash the uranium chips into the melt. After the charge was held at the desired preparation temperature for 15 to 30 min, it was allowed to cool in the crucible. The entire melting operation was accomplished in an atmosphere of helium (double charcoal refined grade with no further treatment). The procedure was to outgas the furnace by first evacuating it to 10-% m Hg, admitting helium to 8 psi gage and sealing the furnace off. An optical pyrometer focused on the charge through a hole in the crucible cover was employed for thermal measurements. Usually a 50° to 70°C correction had to be added to the instrument value. The most suitable alloy preparation temperature range was found between 1220° and 1280°C. The reason for this is explained by the phase diagram, Fig. 7. Above this temperature range two liquids separate preventing alloy formation upon cooling at a reasonable rate. On the other hand, below this range the uranium was coated with a layer of both compounds and the rate of reaction was diminished by diffusion processes. The fastest reaction rate occurred in this narrow range of temperature because only UPb coats the uranium and it evidently does not protect the uranium as well as UPb,. Apparatus and Procedures The development of apparatus and techniques was determined by the peculiar properties of the alloys. All the alloys were pyrophoric, and, consequently, the alloys had to be protected from oxidation by handling them in a dry box or inert atmosphere furnaces. Other operations performed outside of this equipment had to be done as quickly as possible. Thermal analyses were conducted in a furnace and arrangement similar to that described by the author.' Graphite crucibles having a thermocouple well in the bottom were used to contain the prepared alloy, while a helium atmosphere protected the melt from oxidation. The furnace was outgassed by pumping a 10-3 mm Hg vacuum until the furnace had been heated to 400°C. Then helium was admitted and the furnace sealed under 8 psi gage pressure. Chromel-alumel thermocouples were used for thermal analysis and the accuracy of thermal measurements was judged to be k 5°C. At first, an attempt was made to use platinum-platinum-rhodium thermocouples, but evidently lead vapors attack it at high temperatures forming low melting alloys. These lead vapors had direct access to the thermocouple because the graphite crucible was porous. A differential temperature control was used to regulate thermal analyses. The thermal gradient across an alundum tube placed between the windings and the crucible was maintained constant by a controller.

Jan 1, 1953

By M. Kaufman, A. E. Palty

The phase structure and aging characteristics of two nickel-base alloys, Inconel 718 and 702, were investigated. Wrought and cast Inconel 718 showed ArisCb as the major hardening phase, as well as ture was positively identified. Inconel 702 had Ni3Al as the major hardening phase, as well as Cr7C3-of the phase amounts with temperature was determined. 1 HE value of phase structure and aging rate information in the utilization of alloys has been well established. As part of a continuing program, the results obtained on two nickel-base alloys, hconel 718 and Inconel 702, are presented here. Inconel 718 is a relatively new alloy considered for application in both sheet and cast form. Its novelty lies in the use of high columbium tantalum levels in a Ni-Cr-Fe base. No previous work on this type of alloy has been reported in the literature. Inconel 702 is being used now as an oxidation-resistant sheet alloy. Occasional fabrication problems spurred work on its basic structural behavior. The composition of 702 is essentially nichrome plus aluminum and titanium for strengthening and added oxidation resistance. This puts it in the basic class of other nickel-base alloys which have already been studied. The two alloys will be treated separately. INCONEL 718 Phase Study Methods. The phases present after the various conditions investigated were determined by X-ray diffraction analysis of two different elec-trolytically extracted residues and microscopic examination. The extraction methods, using 10 pct HC1 in alcohol and 10 pct H3PO, in water and the X-ray technique have been described previously.' The effect of temperature on the phase behavior was studied on sheet material using the following heat treatments: 2250°F, 2 hr, ice brine quench 1300 100 hr, water quench 2250°F, 2 hr, ice brine quench 1400°, 100 hr, water quench 2250°F, 2 hr, ice brine quench 1500°F, 100 hr, water quench 2250o 2 hr, ice brine quench 1700°F, 48 hr, water quench 2250°F, 2 hr, ice brine quench 1850°, 24 hr, water quench 2250°, 2 hr, ice brine quench 2000°F, 6 hr, water quench The high solution temperature was an attempt to dissolve as many phases as possible without causing melting. Aging exposures were made longer than normal heat treating times in order to approach equilibrium conditions more closely. Cast material was examined only in the as-cast condition and with the normal heat treatment (1700°F, 1 hr, air cool 1325oF, 16 hr,air cool). Materials. The full phase study was performed on sheet specimens approximately 1/2 in. by 2 in. by 1/16 in. The cast pieces were cut from the gating system of a vacuum-cast test piece. An all weld-metal specimen was made by running many weld beads on the sheet using filler made from the sheared edges of the sheet. All external contamination was removed by belt-sanding followed by an electro-polishing treatment. The typical composition of wrought Inco 718 is as follows: The alloy is air-melted. Cast hco 718 may have higher molybdenum. Due to the expectation of finding a Ni-Cb phase (Ni, Cb) for which no X-ray diffraction pattern was available in the ASTM Index, a special 5 Ib heat to the stoichiometric composition of this intermetallic

Jan 1, 1962

By Vincent T. Ricca, Kurtis Chow

When dealing with acid mine drainage as to treatment levels, costs, and evaluation of abatement schemes, predictions of the quantity and quality of the discharges are needed. An acid mine-drainage model is presented in this paper. In essence, the model is a hybrid of computer programs for stream flow simulation and acid mine drainage. Two major aspects of the model are discussed: mine-water generation and acid-load production. The former is based on hydrologic concepts and the latter on pyrite oxidation kinetics and oxidation product removal. The total model is programmed for the high-speed digital computer. The major inputs are: climatological, basin characteristics, and mine characteristics data. By the use o f the hydrologic model the amount of water that flows through the pyritic system is determined. From this information, acid loads removed by leaching, inundation, and gravity diffusion are then predicted. The outputs from the total model are: average daily mine-water discharge, the associated acid concentration or load, plus the average daily flow in the receiving streams or at basin outlets. The capabilities of the separate models have been tested individually and the joint model has been applied to a small drift mine in southeastern Ohio.

Jan 1, 1975

By Fred C. Bond

The process of comminution by grinding is properly classified as an art, rather than as a science. Like most other operations concerned in ore dressing, or in the treatment of nonmetallic minerals, the mathematical relationships of rock breaking are still obscure, and much disputed. If some basic formula exists, comparable for instance to E = RI in electricity, it has not yet been placed in common use. The absence of such a comprehensive mathematical background undoubtedly is the cause of many inefficient designs and installations, as well as of much poorly oriented experimental work. On the other hand, the mathematical immaturity of the process constitutes an opportunity for a real contribution on the part of those who enjoy mental pioneering. Some of the statements made in any such exploratory work may be little more than opinions, and it is to be expected that some will later be proved untrue; but such an evolutionary development is necessary if we are ever to arrive at the fundamental laws, the discovery of which can change the empirical art into a mathematically exact science. The most significant principle of comminution that we possess is probably Rittinger's law, which states that the work done in crushing or grinding is proportional to the area of the new surface produced. There is an alternative theory, known as Kick's law, which formerly was preferred to Rittinger's but which now is rather discredited. According to Kick, the work done in comminution is proportional to the volume, or weight, of the pieces broken, or to the cube of their diameters, while according to Rittinger it is proportional to the square of the diameters. Careful determinations of size distribution below the limit of sieve sizes1 indicate strongly that under ordinary grinding conditions the amount of new surface area produced is directly proportional to the net power input. Changes in the size ratio between the balls and the particles cause important differences in the proportion of the product that passes a given mesh size, but do not affect the total amount of new surface area; they merely change the distribution of the surface among mesh sizes. The principle of constant surface area is the logical result of Rittinger's law, and it may well have an important bearing on the comminution theories of the future. Formula for Ball Wear Grinding tests have been made in the Allis-Chalmers laboratory for more than 9 years, using a standard charge of mixed balls of different sizes; and a continuous record has been kept of the rates of wear of each size. These results have been combined and plotted in various ways in order to discover the relationship that exists

Jan 1, 1943

By J. W. Hickman, E. A Gulbransen

The physical and chemical structure of the oxide films formed on metals and alloys is of interest in our understanding of their protective properties. According to Pilling and Bedworth,¹ if the specific volume of the oxide is equal to or greater than that of the metal, a compact or continuous structure results; if the volume of the oxide is less, a cellular or porous structure forms. With the cellular type of coating the surface layer of oxide offers no impedance to oxidation; at a given temperature the rate of oxidation is quite constant. On the other hand, the compact type of coating acts as an effective barrier to oxygen and the rate of oxidation will follow a parabolic law. The recent work of Gulbransen2 and of Leontis and Rhines3 on the oxidation of magnesium indicates that it is not necessary for the volume of the oxide to be greater than that of the metal in order that the oxidation may follow a parabolic rate law. One exception to the rule of Pilling and Bedworth¹ is noted by Scheil;4 namely, tungsten. At 500° and 700°C long-time oxidations indicate a linear rate law with time. However, Dunn's6 0xidation measurements from 700°to 1000°C indicate that a parabolic rate law is followed. The oxide is mainly yellow WO a with a thin layer of the blue oxide. Preliminary results on the oxidation of tungsten6 in the temperature range 400° to 500°C indicate that the oxidation does proceed according to a parabolic rate law. Irrespective of the actual rate law that tungsten may obey, it is of interest to compare the results obtained on the oxidation of tungsten in the thin film region with those found when the metal is scaling. A time-temperature study of the oxides formed on both molybdenum and tungsten may indicate whether there exist any peculiarities in the oxide structures of the thin film region compared with those of the scaling region of oxidation. In a recent paper the authors7 presented an investigation of the structures of the oxide films formed on the metals iron, cobalt, nickel, chromium and copper. The results of these studies are presented in graphical form as existence diagrams of the oxides on a time-temperature scale. The existence diagrams of the oxides occurring on some of the metals are simple and show few chemical transitions, but there are many cases in which the physical state of the oxide surface changes as a function of time and temperature, as evidenced by the appearance or disappearance of orientation effects and sharpness of patterns. In general an increase in temperature results in an increase in

Jan 1, 1947

By Fred C. Bond

The process of comminution by grinding is properly classified as an art, rather than as a science. Like most other operations concerned in ore dressing, or in the treatment of nonmetallic minerals, the mathematical relationships of rock breaking are still obscure, and much disputed. If some basic formula exists, comparable for instance to E = RI in electricity, it has not yet been placed in common use. The absence of such a comprehensive mathematical background undoubtedly is the cause of many inefficient designs and installations, as well as of much poorly oriented experimental work. On the other hand, the mathematical immaturity of the process constitutes an opportunity for a real contribution on the part of those who enjoy mental pioneering. Some of the statements made in any such exploratory work may be little more than opinions, and it is to be expected that some will later be proved untrue; but such an evolutionary development is necessary if we are ever to arrive at the fundamental laws, the discovery of which can change the empirical art into a mathematically exact science. The most significant principle of comminution that we possess is probably Rittinger's law, which states that the work done in crushing or grinding is proportional to the area of the new surface produced. There is an alternative theory, known as Kick's law, which formerly was preferred to Rittinger's but which now is rather discredited. According to Kick, the work done in comminution is proportional to the volume, or weight, of the pieces broken, or to the cube of their diameters, while according to Rittinger it is proportional to the square of the diameters. Careful determinations of size distribution below the limit of sieve sizes1 indicate strongly that under ordinary grinding conditions the amount of new surface area produced is directly proportional to the net power input. Changes in the size ratio between the balls and the particles cause important differences in the proportion of the product that passes a given mesh size, but do not affect the total amount of new surface area; they merely change the distribution of the surface among mesh sizes. The principle of constant surface area is the logical result of Rittinger's law, and it may well have an important bearing on the comminution theories of the future. Formula for Ball Wear Grinding tests have been made in the Allis-Chalmers laboratory for more than 9 years, using a standard charge of mixed balls of different sizes; and a continuous record has been kept of the rates of wear of each size. These results have been combined and plotted in various ways in order to discover the relationship that exists

Jan 1, 1943

By E. A. Gulbransen, J. W. Hickman

THE physical and chemical structure of the oxide films formed on metals and alloys is of interest in our understanding of their protective properties. According to Pilling and Bedworth,1 if the specific volume of the oxide is equal to or greater than that of the metal, a compact or continuous structure results; if the volume of the oxide is less, a cellular or porous structure forms. With the cellular type of coating the surface layer of oxide offers no impedance to oxidation; at a given temperature the rate of oxidation is quite constant. On the other hand, the compact type of coating acts as an effective barrier to oxygen and the rate of oxidation will follow a parabolic law. The recent work of Gulbransen2 and of Leontis and Rhines3 on the oxidation of magnesium indicates that it is not necessary for the volume of the oxide to be greater than that of the metal in order that the oxidation may follow a parabolic rate law. One exception to the rule of Pilling and Bedworth' is noted by Scheil;4 namely, tungsten. At 500° and 700°C long-time oxidations indicate a linear rate law with time. However, Dunn's5 oxidation measurements from 700° to 1000°C indicate that a parabolic rate law is followed. The oxide is mainly yellow W03 with a thin layer of the blue oxide. Preliminary results on the oxidation of tungsten6 in the temperature range 400° to 500°C indicate that the oxidation does proceed according to a parabolic rate law. Irrespective of the actual rate law that tungsten may obey, it is of interest to compare the results obtained on the oxidation of tungsten in the thin film region with those found when the metal is scaling. A time-temperature study of the oxides formed on both molybdenum and tungsten may indicate whether there exist any peculiarities in the oxide structures of the thin film region compared with those of the scaling region of oxidation. In a recent paper the authors' presented an investigation of the structures of the oxide films formed on the metals iron, cobalt, nickel, chromium and copper. The results of these studies are presented in graphical form as existence diagrams of the oxides on a time-temperature scale. The existence diagrams of the oxides occurring on some of the metals are simple and show few chemical transitions, but there are many cases in which the physical state of the oxide surface changes as a function of time and temperature, as evidenced by the appearance or disappearance of orientation effects and sharpness of patterns. In general an increase in temperature results in an increase in

Jan 1, 1947

By E. A. Gulbransen, J. W. Hickman

The physical and chemical structure of the oxide films formed on metals and alloys is of interest in our understanding of their protective properties. According to Pilling and Bedworth,¹ if the specific volume of the oxide is equal to or greater than that of the metal, a compact or continuous structure results; if the volume of the oxide is less, a cellular or porous structure forms. With the cellular type of coating the surface layer of oxide offers no impedance to oxidation; at a given temperature the rate of oxidation is quite constant. On the other hand, the compact type of coating acts as an effective barrier to oxygen and the rate of oxidation will follow a parabolic law. The recent work of Gulbransen2 and of Leontis and Rhines3 on the oxidation of magnesium indicates that it is not necessary for the volume of the oxide to be greater than that of the metal in order that the oxidation may follow a parabolic rate law. One exception to the rule of Pilling and Bedworth¹ is noted by Scheil;4 namely, tungsten. At 500° and 700°C long-time oxidations indicate a linear rate law with time. However, Dunn's6 0xidation measurements from 700°to 1000°C indicate that a parabolic rate law is followed. The oxide is mainly yellow WO a with a thin layer of the blue oxide. Preliminary results on the oxidation of tungsten6 in the temperature range 400° to 500°C indicate that the oxidation does proceed according to a parabolic rate law. Irrespective of the actual rate law that tungsten may obey, it is of interest to compare the results obtained on the oxidation of tungsten in the thin film region with those found when the metal is scaling. A time-temperature study of the oxides formed on both molybdenum and tungsten may indicate whether there exist any peculiarities in the oxide structures of the thin film region compared with those of the scaling region of oxidation. In a recent paper the authors7 presented an investigation of the structures of the oxide films formed on the metals iron, cobalt, nickel, chromium and copper. The results of these studies are presented in graphical form as existence diagrams of the oxides on a time-temperature scale. The existence diagrams of the oxides occurring on some of the metals are simple and show few chemical transitions, but there are many cases in which the physical state of the oxide surface changes as a function of time and temperature, as evidenced by the appearance or disappearance of orientation effects and sharpness of patterns. In general an increase in temperature results in an increase in

Jan 1, 1947

By Ernest Stütz

The problem of increasing blast-furnace efficiency through diminution of flue-dust production while operating with burdens consisting largely of fine ores has of recent years attracted the attention of metallurgists, whether directly or indirectly interested in the economies of iron smelting, and the various methods evolved from theory or practice have been submitted to wide discussion. After the very thorough and, at that time, exhaustive view of the whole subject, which was afforded to the industry by the meeting of this Institute in February, 1912, the subject was again taken up at the meeting of the Verein deutscher Eisenh?ttenleute at D?sseldorf in December, 1912. While American and German conditions are not entirely identical, it may be of interest to give here the words of the gentleman summing up the discussion at the Diisseldorf meeting: " The chief advantage offered by the use of briquettes lies in the fact that disturbances in the furnace, caused mostly by the presence of fine ores in the burden, are avoided, and that blast pressure can be considerably reduced. The resulting economies cannot be overrated, as, with lower blast consumption per ton of product, the installation will be able to take care of increased production. In consequence of lower pressure and speed of blast, heat is more efficiently utilized, flue gas temperature is lowered, and coke particles are less liable to be carried along with the flue dust, of which considerably less is produced. Finally, by increased regularity of operation and higher temperature in the lower parts of the furnace, the quality of the product is improved. The question of briquetting iron ores has grown to be one of the most important in the iron industry, and it is not any more a question of what is the cost of briquetting a ton of ore, but what, in using ore briquettes, is the cost of production of a ton of iron." Dr. A. Weiskopf, of Hannover, admirably condenses in these words

Jan 1, 1914

By H. M. Roche

MAGNETITE is the important iron ore of New Jersey although bog ore, limonite and red hematite were mined in sizable quantity early in the state's min-ing history. The deposits of mag-netite are found in the Highland area in the northern part of the state. These ores outcrop a broad belt 20 miles wide, extending in a northeasterly direction from Phil-lipsburg, on the Delaware River, to Greenwood Lake, at the southern boundary of the state of New York, a distance of 60 miles. The area in which the magnetite is found (see map, Fig. 1) contains 1200 square miles and the center of the area is at Dover, 40 miles west of New York City. In the general area are found 18 parallel ranges or lines of ore deposits. These ranges may be re-garded as mineralized zones in which occur orebodies that are rich enough in magnetite to war-rant mining. Usually a number of the orebodies lie one above the other in the same plane, all dipping and pitching in the same direction. Within the ranges, there may be several parallel orebodies of work-able size. The average strike of the orebodies is N.41° 30' E., with an average dip of 55° southeast and an average pitch of 15 ° to the northeast. Orebodies suitable for mining range from 6 to 100 ft. wide, as measured from foot wall to hanging wall. Their heights, as measured on the dip and normal to the long axis of the orebody, vary from 200 to 3,000 ft. The length along the pitch has never been determined by mining, al-though several of the orebodies have been worked to lengths of 10,000 ft. The grade of the ore as mined today varies from 30 to 60 per cent iron, and the gangue min-erals are chiefly silica, alumina, magnesia, lime and phosphorus.

Jan 1, 1937

By O. W. Ellis

RECENTLY there has been a considerable revival of interest in the effects of the various elements commonly added to brass for the purpose of increasing its strength. For many years the work of Guillet2? alone gave reliable information in this regard. Even today his determination's of the coefficients of equivalence of the various elements relative to zinc in brass are those universally employed in industry. This is so because these coefficients have stood the test of time-their substantial correctness has been proved in almost universal practice. It is not our intention to discuss here these coefficients or their use. Rather do we wish to emphasize the need for further systematic studies of the mechanical properties of the ternary systems of copper, zinc, and other individual elements. Since Guillet published the results of his first investigations Millington,16 Smalley33 and Thibaud45 have added somewhat to our information. In general they have confirmed the findings of Guillet, which may be stated in the following rather general terms: 1. The addition of aluminum to the 70:30 and 60:40 brasses progressively increases their hardness and strength and reduces their ductility and resistance to shock. 2. The addition of small amounts of iron to a 60:40 brass improves its strength without affecting its ductility. 3. The addition of small amounts of manganese to a 60:40 brass causes a progressive increase in its strength and reduction in its ductility. A considerable amount of information has been amassed in regard to the effect of nickel on brass (9, 22, 41) which it is unnecessary to refer to here, in view of the scope of this paper.

Jan 1, 1929

By Albert Roberts

Summary In response to a growing intolerance towards ground vibrations and noise as environmental pollutants the engineer must consider the effects of his operations as they are likely to be judged subjectively by the public at large. Much work has been done on the study of vibration damage to structures, but the damage criteria normally applied do not take into account any resonance effects, nor do they embody any subjective criterion. Mu1tiple criterion techniques of subjective appraisal have proven to be of value .in the assessment of environmental comfort in relation to ventilation, air conditioning, and lighting. One such scale, the Reiher-Meister Scale, has also been applied to ground vibrations and noise, and an attempt has been made to correlate this scale with objective criteria, using the parameters of frequency and displacement. This paper quotes examples and compares ground vibrations resulting from blasting, the operation of, vibrating and impact-hamner pi1e drivers, forge hammers, and railway and road traffic. The Reiher- Meister Scale was applied to a subjective-objective correlation in relation to vibrations from railway traffic and gave results which did not conflict with experience.

Jan 1, 1971

By David R. Mitchell, R. B. Hewes

MANY processes for cleaning coal that are in use depend primarily on physical properties of coal and refuse other than specific gravity and surface conditions relating to froth flotation. These properties are' shape, coefficient of sliding friction, resilience, friability, magnetic susceptibility, and electrical conductivity. In many of these processes specific gravity does have some effect and many separators are designed to utilize more than one of the physical properties cited. Although the processes described herein do not have a widespread application, yet for specific coals and specific conditions, they are economically important. A problem confronting many coal-mining districts is the marketing of the slacks or screenings and dust passing the final sizing screens. Proc¬esses in commercial use installed primarily to increase the form value, and hence the market value, of these slacks and dusts include briquetting, packaging, and low-temperature carborization. MECHANICAL PICKERS Machines utilizing shape, frictional resistance, and differences in resilience of coal and impurities are usually called mechanical pickers. They require a closely sized feed, therefore their use is confined to the pea, nut, and egg sizes. Various types of these devices are described by Berrisford, 1. 2 Taggart, and Yeele.

Jan 1, 1943

By George B. Clark, Edward E. Hornsey

Pulses from large underground explosions which traverse the rock beyond the "fracture" and "plastic" zones do not behave as a spherical elastic model. Observed attenuation is greater than that predicted by the elastic wave equation, and the pulse form changes in a different manner, i.e., it usually lengthens with the first power of the distance. To more clearly define a mathematical real earth-wave model, detailed analyses of the spherical elastic and the Voigt viscoelastic models have been made, and results compared with observed wave forms from large confined chemical and nuclear explosions. TRANSIENT SPHERICAL ELASTIC WAVES Scope of Investigation Transient elastic spherical waves were investigated in detail. However, an elastic model is not, in general, an exact representation of wave propagation in rock. An understanding of transient elastic waves is desirable for gaining insight into explosive-generated wave phenomena because it can be employed for comparison of more complex and realistic models, such as the Voigt model, or others which may simulate real earth waves. The study was concentrated primarily on the peak values of the radial wave parameters : displacement, particle velocity, acceleration, stress, and strain.

Jan 1, 1972