By D. D. Pollock, D. I. Finch

Relationships between the compositions of specially prepared manganin-type alloys and some of their electrical properties have been established. Empirical equations, based upon the electronic configurations of the alloying elements, are given which describe the resistivity, temperature coefficient, peak temperature, and thermoelectric power of Cu-Mn-Ni-Fe alloys at approximately room temperature. Calculations based upon these relationships are correlated with experimental data. SECURING suitable alloys for the construction of stable resistors, for use in precise electrical measuring devices, has been important ever since the art of electrical measurement was begun. German silver, Pt-Ag, and Platinoid are examples of some of the alloys in early use. These early alloys were un- satisfactory for one or more of the following reasons: l—insufficient stability of electrical properties with time, 2—poor reproducibility of electrical characteristics from melt to melt, 3—excessive temperature coefficients of resistance, and 4—excessive cost. Weston introduced the Cu-Mn-Fe and Cu-Mn-Ni-Fe alloys of the type now generally known as manganins. His patents are believed to represent the first disclosure of any alloy with a negative temperature coefficient of resistance. After this work, the German company, Isabellenhutte, in conjunction with Feussner and St. Lindeck, produced alloys of

Jan 1, 1957

By Henry P. Ehrlinger, James C. Bradbury

Tripoli is a naturally occurring, very finely divided form of silica found chiefly in some midwestern and southeastern states and used commercially as fillers and abrasives. Definitions Tripoli is a microcrystalline, finely particulate, more or less friable form of silica that appears to be the product of leaching of siliceous limestone or calcareous chert. The term was originally applied to a deposit near Seneca, MO, that resembled material of that name found near Tripoli In North Africa (Hovey, 1894). The two deposits were subsequently found to have different physical characteristics -the North African tripoli, now called tripolite, is a diatomite, composed of the siliceous skeletons of microscopic marine plants called diatoms; the Missouri tripoli contains no diatom remains. The term tripoli, however, continued to be used for the Missouri material and is now applied in a general way to most silica deposits similar to it in characteristics and geologic origin. In commercial trade tripoli is commonly understood to designate material from the Missouri-Oklahoma field; silica from southern Illinois, the other major producing area, is referred to commercially as amorphous silica. Each term, however, may be used commercially for material, regardless of place of origin, that has the characteristics or uses commonly ascribed to the material from one or the other major producing area. For example, in the commodity price listings, Engineering & Mining Journal routinely lists under Tripoli, prices "f.o.b. Elco, IL" and "f.o.b. Seneca, MO, and Rogers, AR," and under Silica, amorphous, prices "f.o.b. IL," and "f.o.b. bierks, AR." Amorphous silica, the commercial designation given to southern Illinois tripoli, is, like the term tripoli, a misnomer. Mineralogically, the southern Illinois deposits are composed of microcrystalline quartz, and no amorphous material has been detected during X-ray and scanning electron microscope investigations (Leamnson, Thomas, and Ehrlinger, 1969; Thomas et al., 1970; Keller, 1978). Soft silica is another term that has been applied to Illinois and Tennessee tripoli, presumably to distinguish it from the more compact Missouri material. It has also been used in the ceramic trade to distinguish tripoli from "hard" silica, or silica flour, produced by pulverizing silica sand (Heinz, 1937). Rottenstone, produced commercially in Pennsylvania, is similar to tripoli in that a major constituent is finely particulate silica, and its uses are much the same as those of Tripoli-as abrasives and fillers. The origin of rottenstone also is similar to that of tripoli-decomposition of a siliceous sedimentary rock. The parent rock is defined as a siliceous limestone (Gary, McAfee,, and Wolf, 1972; Thrush, 1968) or as shale. Heinz (1937) quotes a brief statement describing the Pennsylvania deposits -"a black impure shaly limestone grading into black shale"-but does not identify the source of the statement. For convenience, rottenstone is included with tripoli in the reporting of production statistics in US Bureau of Mines (USBM) Minerals Yearbooks. Other materials that have been called tripoli include siliceous deposits in San Bernardino County, California (USBM Minerals Yearbooks, 1934-1941) and in Nevada (Chandler, 1960). These, however, differ in composition and/or origin from tripoli and, therefore, should not be identified by the name tripoli.

Jan 1, 1983

By Armando M. Lago

Secular and cyclical patterns of postwar sources and uses of funds of the mineral sector are analyzed. A simultaneous equation behavior model of sources and uses of funds is developed for both mining firms and integrated producers, and these models were put through the task of predicting the financial and expenditure be-havior of mineral corporations in response to mergers and changes in investment tax credits and depletion allowances. Finally, the quantitative analysis methodology is applied to the analysis of optimum capital structure of mining corporations. The postwar changes that have occurred in the expenditure and financial behavior of mineral corporations are reviewed, particularly the relative importance of factors that affect the industry's supply and demand for funds. This quantitative statistical investigation of factors affecting sources and uses of funds of mineral corporations is achieved through the formulation of a simultaneous equation model of sources and uses of funds. After a description of the study sample, the postwar cyclical and secular financial behavior of mineral corporations is analyzed in detail. An econometric model of mineral corporate financial behavior is formulated. This model is then estimated and reviewed. Policy issues regarding depletion allowances, investment tax credits, and industrial organization of the mineral sector are discussed. Finally, the optimum financial structure of mining firms is discussed and the effect of corporate financial structure on the mining corporations' average cost of capital is analyzed.

Jan 1, 1971

Nationalization of the coal mining industry in Great Britain was one of the first pieces of major legislation enacted by the post-war Labor Government in 1964. It followed a long period of economic depression with high unemployment and bad industrial relations in the coal mining industry during the 1930's, and shortages of coal during the last war. Upon nationalization, the National Coal Board took over control of the industry in 1947 and so became the biggest single employer of labor in the western world. As well as the coal mines themselves, it assumed responsibility for a great variety of other assets including coke ovens, byproduct plants, land, houses, railways and shipping wharves.

Jan 6, 1964

By Paul Foote

MOST of the treatises on metallurgy intimate that simultaneously with the development by the atomic physicist of a really satisfactory theory of the atom will be inaugurated a new epoch in the science of metals. Metallurgically and metaphorically, we shall dwell in the Utopia of Sir Thomas More. It is my privilege this afternoon to demonstrate that this state has not arrived. An atom is a miniature planetary system consisting of a positively charged nuclear sun about which revolve electrons each carrying the negative charge e. The charge on the nucleus is + Ze where Z is the atomic number and the number of planetary electrons in a neutral atom is equal to Z. These electrons are arranged in several groups having different binding energies. Ordinary x-ray phenomena relate to processes occurring deep within the atom, usually with electrons in the so-called K or L shells. Such electrons in the heavier atoms are so closely bound to the nucleus that the forces exerted by neighboring atoms in a solid are relatively inappreciable. For most practical x-ray investigation, the atom may, be considered as in the gaseous phase completely isolated from its neighbors. The K radiation from an element in the gaseous state, in the solid or liquid phase, or even in combination with other elements in all its possible valences, is almost identical. ? Visual and ultraviolet spectroscopy is concerned with disturbances of the most loosely, bound outer or valence electrons of the atom, always in the vapor state. The remarkable progress of the last year in both theo-

Jan 2, 1926

By L. L. Wyman

SINCE the observations of Heyn,1 relative to the embrittlement of copper after having been heated in hydrogen, this subject has received considerable attention from later investigators. The published works of Archbutt2 and of Bengough and Hill3 give the reasons for this embrittlement-the formation of steam by the reaction between cuprous oxide and hydrogen. From Ruder,4 Pilling,5 Moore and Beckinsdale,6 Bassett and Bradley,7 and from Smith8 can be obtained quantitative data concerning the action of hydrogen and other reducing gases on copper samples having various oxygen contents. This problem has been discussed from a practical standpoint by Fuller9 who calls attention to some of the instances of this embrittlement encountered in the manufacturing field. The examples he cites may be considered typical cases of copper embrittlement which were incident to the process of manufacture. In many cases, such difficulties are overcome by changes in the manufacturing process.

Jan 1, 1931

By Frank Tolonen

IRON-ORE beneficiation is becoming of vital importance to the Lake Superior region, since only a few decades will be needed to exhaust the direct shipping ores even if generous allowances are made for discoveries of new orebodies. If the region is to continue as the chief source of ore to the steel industry of the United States, it must concentrate or otherwise beneficiate the enormous tonnages of available iron formations. A beginning along this line has already been made. About one-fifth of the total shipment, even now, is the product of some sort of concentrating process, while another fifth is improved in physical structure by crushing, screening, drying, sintering, or some other similar method. The amount of material amenable to these processes is limited, however; and, in order to be able to utilize the billions of tons of iron formations that cannot be so beneficiated, an intensive study of their nature and concentration possi-bilities is necessary. As long as high-grade ores are available in ample quantities, ore dressing is economically impossible, but as soon as the supply nears exhaustion it becomes necessary. At first the products of ore dressing must meet as nearly as possible the same specifications as the rich ores in order to be adapted to the reduction processes already established. The future requirements as to quality will depend on the one hand upon the ability of the ore dresser to eliminate undesired constituents and charac-teristics in the material, and on the other upon the adaptation of the reduction processes to the product that can be economically supplied. A better understanding of the blast furnace and other reduction reactions, and improvements in the preparation of raw materials, should enable the Michigan districts to continue to supply ore for a long time to come. The study and testing of the iron formations necessary to bring a utilization of the low-grade ores, though requiring time and effort on the part of all concerned, should not be postponed, especially since the economic situation forces the use of the highest grade ore in preference to the leaner material.

Jan 1, 1933

By J. R. Wylie, L. C. Huntley

Drilling for oil in the eastern producing states was fairly active during the first part of 1931, although less so than in 1930. With low prices development declined during the year, until the low prices of the summer resulted in an almost complete shut-down of drilling. This coincided with the action of the Conservation Board of the Pennsylvania Crude Oil Producers Assn, in limiting pipe line runs to 50 per cent of the 1930 normal for the Bradford district and upper country, and to 70 per cent for the balance of the region. Not only was new drilling halted but in many cases oil-producing properties were shut in. In November crude prices were partly restored, and all oil offered was being taken except in the Bradford district which was restricted to 80 per cent of the 1930 normal. During the latter part of the year drilling was being resumed on a moderate scale, and new production indicated a resumption of the proration order. The interest in gas development which has been under way for several years, maintained its supremacy over the search for oil in 1931. New reserves of importance were developed during the year in the Western Kentucky Coal Basin, in the Eastern Kentucky shale gas territory, in Stark County, Ohio, as well as the Oriskany sand development in northern Pennsylvania and central New York. A gas line was completed to the Eastern Seaboard serving Washington and Baltimore, and other lines were under construction designed to serve portions of the territory not hitherto supplied with natural gas. The low price of fuel oil at seaboard is understood to be the deterrent factor against further extension of natural gas lines to these markets at present. The development of these new reserves, as well as those developed by intensive drilling in old areas, resulted in the building up of large potential gas production and a lowering of rates paid to the producer. This, coupled with the country-wide tendency to lower the consumer rates of all public utilities, resulted in a general threat to reopen rate cases before various state commissions. Oil Development The past year was marked only by the almost complete shut-down of new development, reaching its low point during the summer, with its

Jan 1, 1932

By B. G. Klugh

(New York Meeting, February, 1913.) THE present paper represents a preliminary investigation of the ultimate structure of iron-bearing materials which have been subjected to heat treatment for the purpose of agglormer-ating the fines, or for chemical changes, or for both. Primarily, the object of this inquiry was to determine the relation of the microstructure of each of these materials-to its specific susceptibility to the action in the blast-furnace. It is hoped that this small contribution will serve as a nucleus to a line of research that will throw some light upon the debated questions involved in blast-roasting. Thus far the investigation has been conducted along lines of analogy of known principles, rather than through the applica-tion of any well-defined system of microscopic petrography. This is obviously due to the fact that we are dealing with materials which are the artificial products of a new art, rather than with the natural materials from which the essence of the pure science has been evolved. In the limited tune allowed for this research, it has been conducted upon those materials the chemical content of which allows of their use commercially in the blast-furnace.

Jan 5, 1913

By John J. Egan, A. B. Kinzel, Walter Crafts

The demands of the petroleum and chemical industries for steels to be used in pressure vessels and similar structures at artificially low temperatures are continually increasing, and the writing of proper specifications with suitable tests becomes increasingly important. Likewise, the selection of suitable steels for such applications is of increasing concern to the metallurgist. It is generally recognized that highly alloyed steels of the austenitic stainless type retain their properties even at very low temperatures and represent the best technological solution of the low-temperature steel problem. However, in many instances less expensive carbon or low-alloy steels suitable for service within limited temperature ranges are available. The problem thus becomes one of defining the various factors involved in the production and fabrication of these less expensive steels and determining the temperature ranges in which their properties justify engineering application. Most of the applications involve welded structures, and the heat effect of welding as well as the nature of the weld metal are matters of prime concern. The first problem that the metallurgist faces is the determination of the type of test to be used as a criterion of the performance of the steel in low-temperature service. It has been generally recognized that the static properties of steel as determined in the ordinary tensile test undergo a gradual and relatively slight change as the temperature of test is lowered in the range of current interest; i.e., from room temperature to minus 120' C. It is further generally recognized that the behavior of steel under impact involving notch sensitivity is definitely affected at the lower temperatures. While the major subject of this paper is the effect of grain-refining deoxidizers, of low-alloy additions and of welding on the low-temperature notched-bar impact properties, an inquiry into the general behavior of steel under low-temperature impact testing is included. This is a pertinent portion of the investigation and the results thereof are

Jan 1, 1937

By C. B. Alcock, M. G. Hocking

The kinetics of the growth of sulfate layers on blocks of Cu20 has been studied between 688" and 800°C. At 788c the over-all weight increases followed the parabolic rate law, with k = 216 30 sq mg per cm4 min, using a 1:1 entering gas mixture of SO2:02. At 757 after an initial linear period the parabolic rate law was followed, with k = 57.8 10 sq mg per cm4 min. The gas mixture required a platinum catalyst to produce the maximum SOs pressure. The sulfation rate at 757' and 788c was high until all the CUZO had changed into a core of CuO, when it became very much lower. At 757°C marker experiments showed that the sulfates (CuO. CuS04 and CuSO4) grow outwards from the oxide surface, but CuO. CuS04 mixed with CuO was found beneath the markers. At 688 markers were found at the CuO. CuS04/CuS04 interface. Visual observations at 757 showed a liquid eutectic moving beneath the sulfate surface. causing very rapid sulfation and extruding to solidify as thick 'needles" up to 8 mm long. Marker experiments have shown conclusi.cely that CuO grows on Cu20 in air by the outward migration of copper. ThermODYNAMIC measurements on the sulfate and basic sulfate of copper, reported recently,' are followed here by measurements of the rates of formation of these sulfates on cuprous oxide, in order to provide a background for the understanding of roasting processes. peretti2 and McCabe and Morgan3 have shown that the phase Cu20 lies next to Cu2S when the sulfide is roasted under conditions where sulfates will be formed. Since this would present too complex a system for kinetic study, the present work4 has been based on the kinetics of sulfation of the oxide phase. The results of a study of the kinetics and mechanism of the sulfation of cobaltous oxide have recently been reported.4,5 Results on the sulfation of cuprous oxide have also appeared,6 but are at variance with those to be reported here. This seems to be because the previous workers6 did not obtain constant SO3 pressures from the SO2/O2 sulfating gas mixtures used, as will be discussed later. Wadsworth, Leiter, Porter, and Lewis found that the sulfates produced when SO2/O2 mixtures are passed over Cu20 at red heats are CuS04 and the basic sulfate CuO.CuSO4. When the decomposition of CuS04 was followed' by differential thermal analysis, a stage corresponding to CuO .CuS04 was reached before decomposition into the oxide occurred. APPARATUS The vertical furnace used for quantitative studies was a conventional resistance-heated and propor- tionately controlled furnace with an even zone (1 deg) which was 4 cm long. The gas mixtures of SO2 and 02 were made by mixing measured flows from capillary flowmeters and drying over phosphorous pentoxide before passing them into the Pyrex top-piece of the furnace assembly. A mullite tube of bore 2% cm was used as reaction vessel and at the bottom of this tube was a trap for SO3, which condensed as a colorless liquid. The residual gas was led into a fume cupboard for ventilation to the atmosphere. The furnace used for visual observations of needle growth and other phenomena consisted of a transparent silica reaction tube of bore 3 cm, having an optically flat silica window sealed into its wall. The reaction tube was clamped vertically, inside a mullite tube of bore 4 cm and length 42 cm which was heated by Kanthal windings. The window in the silica reaction tube was arranged opposite a hole 3 cm wide and 2 cm tall which had been cut in the wall of the mullite winding tube 19 cm from its top end. A binocular microscope was used to look through the window, illumination being provided by a focusing microscope-lamp offset sideways and downwards. The oxide block to be sulfated was suspended from the removable Pyrex top-piece to the reaction tube, by means of which it was inserted at the start of the experiment, and through which entered the S02/02 gas mixture. The variation of the temperature inside the reaction tube with horizontal and vertical displacement from the window was investigated, and, while it can be said that the temperature was constant 1 deg, its value at a given position was known only to 12 deg. In both furnaces, the oxide block to be sulfated was suspended from a small silica hook immediately downstream from a platinum thimble used as catalyst, which was held on a long silica rod from a Pyrex spring attached to the removable Pyrex top-piece of the furnace. The spring was only included in the quantitative sulfating furnace; its sensitivity was 1.4 cm per g and it was found to be free from creep in a 16-hr test when carrying the working load. The extensions were followed by a cathetometer which could be read to 0.001 cm, corresponding to i0.7 mg. Extensions of the spring were measured on adding weights between 5 and 500 mg to the working load (thimble + oxide block), and Hooke's law was closely obeyed. SAMPLES Cuprous oxide blocks were prepared by oxidizing Johnson Matthey "Specpure" copper sheet of 1 mm thickness (impurities: iron at 3 ppm, silver at 2 ppm, lead, nickel, sodium, and silicon each at 1 ppm, calcium, chromium, magnesium, and manganese each at less than 1 ppm) for 6 days in air at 1000°C in a re-crystallized alumina boat. It has been reported7 that when Cu20 is prepared by heating copper sheet for 1 day the central plane of the blocks produced consists

Jan 1, 1967

By Robert McKay

THE practical study of corrosion requires consideration off its economic aspects. It must be based on sound scientific principles, but it should be borne in mind that probably the most important object of a corrosion test is to determine what metal in corrosion-resisting construction will produce the greatest operating profit. Thus the corrosion test must be directly connected with money values or it is not a practical corrosion test. This, perhaps unusual, connection between corrosion and economics is partially due to the fact that corrosion deals only with the time factor or duration of equipment, and it is almost the only test which deals with this feature. In these statements a departure is made from the academic definition of the word corrosion and it is done deliberately. The use of the term corrosion is unusual. It is as though we spoke of a tensile test as. a "breaking" test. We are not interested primarily in the break but in the strength of the metal. There is no English word which expresses our main interest in corrosion-testing, but let us have clearly in mind that we make corrosion tests to prevent corrosion. Our real interest is in this corrosion-prevention, not in the corrosion. Previous to 1922, it was common comment that "it is impossible to determine the course of corrosion by laboratory testing." This statement was true at that time in that the technique of laboratory testing for corrosion resistance was so vague that tests in the laboratory gave untrue results almost as often as true ones. This was so, even in the simple case of determining which one of two metals better resists a given solution. While this is no longer true the number of misleading "corrosion tests" still being ground out by laboratories is too large in the light of our present knowledge. There are two important features of corrosion testing whose neglect is a large contributing factor to misleading results: (1) The economic relations of the corrosion tests to other tests; (2) testing technique.

Jan 1, 1929

By J. Nutting, J. W. Cahn

WITH the development of thin film techniques for the direct examination of metals in the electron microscope some new problems in quantitative metallography have become apparent. In order to obtain certain contrast effects in the electron optical image when examining thin films from alloys containing dispersed phases, it is essential to use films of a thickness at least two or three times greater than that of the mean particle diameter of the dispersed phase. From micrographs of such specimens it may be desired to obtain the volume fraction of the dispersed phase and the number of particles of the phase in a unit volume of the matrix. Under these conditions the particles sectioned by

Jan 1, 1960

By M. R. Geer, H. F. Yancey

With the exception of pneumatic processes and a few special beneficiation methods of comparatively limited application, all mechanical coal-cleaning and mineral-dressing processes involve the admixture of solid particles with a liquid, generally water. Upon completion of the beneficia-tion process the solids must be reclaimed from the water. With coarse particles separation of solids from water is accomplished readily by the simple expedient of screening, but recovery of fine solids presents a much more difficult problem. Thickening and dewatering are practiced so generally, both within the mineral industry and elsewhere, that they have been the subject of study through the years and a number of processes for making the solid-liquid separation have been developed. Dorr-type thickeners have been standard equipment lor many years, and more recently driers employing centrifugal force have gained in popularity.' A cyclone device employed to thicken the loess suspension is a novel feature of the loess heavy-medium coal-cleaning process developed by the Netherlands State Mines in the thirties. The cyclone thickener was first mentioned by Driessen2 in 1939 in a paper describing the loess process and has been the subject of two more recent reports by the same author.3 The cyclone does not differ greatly from cyclone dust collectors used in this country for years, except that it is operated wet rather than dry. Advantages of the cyclone over other thickening devices are its simplicity of construction, high capacity, and the fact that, having no moving parts, it is simple and inexpensive to operate. The Bureau of Mines became interested in the cyclone after one of the present authors observed it in operation in the Netherlands in 1945. The first experimental work with the cyclone conducted by the Bureau of Mines was an investigation of the unit functioning as a heavy-medium cleaner for fine coal—a use for the cyclone that was conceived long after it had been perfected as a thickener. The results of this investigation were published last year.4 The present investigation deals exclusively with operation of the cyclone as a thickener. Object and Scope of Investigation Although the cyclone thickener has been dealt with in three reports by Driessen, its use as a thickener was not the principal subject of any of these reports and therefore neither the cyclone itself nor its operation was described completely. The design of the cyclone was described only in a very general way, only limited operating results were given, and virtually nothing was disclosed about the influence of the various possible operating variables. Moreover, the Netherlanders apparently had employed the cyclone exclusively for thickening loess and had not employed it On coal 'lurries. One English colliery has used a cyclone to thicken coal slurry,5 and as it appeared that

Jan 1, 1949

By L. L. Melton, W. T. Malone

Fluid mechanics research conducted with non-Newtonian fluid systems now permits prediction of the behavior of these fluid systems in both laminar and turbulent modes of flow through circular pipes. Present work concerns non-Newtonian fluid systems currently used in the hydraulic fracturing process. During fracturing treatments, an unsteady-state condition may frequently be encountered arising from. the reaction rate of a chemical additive. This condition must be evaluated in order to predict the actual behavior of a particular fluid during field application. Design and operation of the apparatus used to determine fluid-flow behavior permit obtaining data under such non-equilibrium conditions. This paper shows methods used to obtain rheology measurements, develop hydraulic relationships and evaluate chemical reactions producing unsteady-state conditions. Engineering application of this research is illustrated by employing measured rheological values and developed hydraulic retationships to produce frictional pressure loss (psi/100 ft) us flow rate (bbl/min) charts of common tubing and casing sizes for an example fracturing fluid. How these charts and chemical reaction rate information are then combined to predict actual turbulent hydraulic behavior during unsteady-state field conditions is also discussed INTRODUCTION Many fluids used in hydraulic fracturing contain chemical additives which impart non-Newtonian fluid properties that may drastically alter their hydraulic behavior. Equally drastic alteration in wellhead pressure, injection rate and hydraulic horsepower requirement may result from these fluid properties. Prior research conducted to relate non-Newtonian fluid properties with hydraulic behavior has not as yet produced a universal relationship, particularly for the turbulent flow region. which of the many Possible non-Newtonian fluid properties is responsible has not been conclusively established. A systematic description, suggested by Metzner, of the many possible non-Newtonian fluid properties exhibited by real-fluid behavior, and a current discussion of theoretical and applied aspects of non-Newtonian fluid technoloy can be found in Handbook of Fluid Dynamics. f Little or no research has previously been attempted with fluids exhibiting time - dependent properties. Addition of chemicals during a fracturing treatment is often accomplished by continuously mixing and displacing the fluid. This produces a time-dependent effect or unsteady-state condition while the fluid is progressing through surface and wellbore conductors. This condition is due to solution or chemical reaction of the additive. Considerable departure from conventional methods of obtaining and interpreting data was found necessary to consider these conditions. Therefore methods were developed to obtain hydraulic behavior information under these complex, unsteady-state conditions. Relationships presented in this paper to predict hydraulic behavior of non-Newtonian fluids in circular pipes were obtained by constructing and operating a small pipeline apparatus in the manner of a pilot-plant study. These relationships are suggested as scaleup equations and are not proposed as fundamental rheological parameters. While perhaps deficient from a fundamental research viewpoint, a pilot-plant study does permit the determination and convenient evaluation of variables pertinent to a process. A pilot-plant study can result in a valid engineering application procedure even when fundamental relationships are still undefined. An excellent series of articles by Bowen has appeared in the chemical engineering literature.2-8 These give a thorough review of proposed hydraulic relationships and their limitations for non-Newtonian fluid behavior in circular pipes. A graphical method is presented to scale up data for a fluid exhibiting an anomalous hydrau1ic behavior in the turbulent flow region. Considerable assistance has been obtained from these articles to interpret the anomalous behavior noted during this investigation. These articles also provided assurance that a pilot plant is a practical approach to evaluate the hydraulic behavior of non-Newtonian fracturing fluids. _____________

Jan 1, 1965

By G. S. Cole, G. F. Bolling

A series of Al-Cu alloys has been cast from constant superheat to solidify either with a hot top or with a free liquid/air interface. All the other variables which affect relative fluid motions were kept constant except the imposition of slow rotations m oscillations of the mold. Depending upon the exact circumstances, evi-dence could be found for the nucleation of equiaxed grains from dendrite bits detached from the columnar zone, or from the free surface, or from solid bits induced at pouring; a special experiment showed the solute buildup during ingot solidification and by inference the reality of constitutional supercooling. All methods of grain nucleation are thus supported. When solidification is arranged in a static mold the columnar- to-equiaxed transition occurs by one of these nucleation paths, subject to the natural decay of temperature gradients which promotes nucleation or the survival of nuclei. But when solidification is forced under special fluid flows it may display odd transitions. In one of these the equiaxed zone is synihesized from. dendrite bits detached from the solid/liquid interface. These survive under the concurrent lowering of temperature gradients and eventually cause transition by impeding columnar growth. GRAIN structure control is desired because real experience shows that specific properties are associated with specific cast grain structures. But since control is thus a matter of need and does not require understanding, much of casting remains art. For example, the manipulation of relative fluid motions in simple ingots provides a control of grain structure development,1-4 but theoretical insight is not required in order to broaden its potential applicability. Fortunately, however, once a variable like fluid flow is recognized it can also provide paths toward new insight. New observations using this variable have provided an insight which is curious. All the theories or descriptions of the columnar-to-equiaxed transition (CET) seem to be supported as long as the appropriate experiment is carried out. In order to develop this idea, let us ignore segregation, the chill zone (until a later section of this paper), and the origin and development of the columnar zone.= The details of questioning how equiaxed material forms in a casting may be divided in two. The first part is simply a questioning of the origin for equi-axed grains: are there fresh nuclei from heterogeneous nucleation, or dendrite bits broken off or melted from the columnar zone or elsewhere,6 or other solid bits surviving from the outset of freezing? The second is more complex, a questioning of the CET: does columnar growth slow down and allow the dominance of equiaxed grains, however they are formed, or do equi-axed grains take over and force columnar growth to stop? This "chicken-or-the-egg" second question can be quite useful, especially because it allows us to delineate the ordinary or NATURAL EQUIAXED ZONE and the induced or SYNTHETIC EQUIAXED ZONE. A natural equiaxed zone occurs if solidification proceeds in the absence of disturbances or extraneous forces such as ultrasonics, stirrings, and so forth. Both the CET theory proposed by Winegard and Chal-mers, 7requiring constitutional supercooling, and the CET theory suggested by Chalmers,8 requiring nuclea-tion only on pouring, pertain to the natural equiaxed zone. The best collating evidence to date for both these theories is contained in the work by Biloni and Chal-mers;9,10 the former theory7 is supported by special versions of the unidirectional growth experiment performed by Plaskett and winegardl1 and the latter theory' is supported in detail for the solidification of small ingots. An equiaxed zone can be synthesized when disturbances caused by forced fluid flows2-4 or other artificial means9,10 break off or melt off dendrite tips from an advancing solid/liquid interface,* if (and only if) temperature gradients in the melt are (forcibly) reduced enough to ensure the survival of these bits of dendrites, 2'3 Willful disturbances even so trivial as those produced by rapping a mold might be included here; as will be shown for example, this follows Southin's suggestion that the free liquid/air interface

Jan 1, 1970

By E. A. Gulbransen, J. W. Hickman

IN a previous paper1 the authors have investigated the structure of the oxide films formed on most of the metals that make up the alloys of this study. The metals were studied in order to provide basic information on the structures, both physical and chemical, of the oxide films and to determine how these structures are effected by the temperature, time of oxidation, and surface preparation. It was felt that an understanding of the physical and chemical structure as well as the stability of the oxide film might furnish clues as to the nature of the reaction process and the protective quality of the film. The oxidation of the metals was studied over the temperature range 300° to 700°C. except for copper, where the range selected was 100° to 500°C. The results of these studies were presented in graphical form as existence diagram, of the oxides on a time-temperature scale. For some of the metals the existence diagrams were simple and showed few chemical transitions, but there were numerous cases where the physical state of the oxide surface was a function of time and temperature. In general the physical state of the oxide surface changed with increasing temperature so as to increase the sharpness of the diffraction patterns and to cause orientation effects to be more pronounced. Deviations in lattice parameters from X-ray values were noted. In general these deviations were of positive nature and may be due to solid solution of the metal in the oxide lattice. This effect might be expected in thin oxide films. In a study of the oxidation of alloys containing two or more metals, there may arise the complicating factor of identification of the oxides formed. A thorough understanding of the oxides formed on the pure metals, therefore, was, essential before investigation of the oxidation of alloys. In this paper it is our purpose to present a study of the following problems: I The existence diagrams of various alloys. [2.] The effect of the structure of the [ying] metal on the existence diagram of Iron. 3. The effect of the percentage of chromium on the oxides formed on Fe-Cr alloys. 4. The relationships, if any, between the oxides formed and the protective quality of the oxides. The following alloys are included in this study: alloys of iron with body- centered cubic, face-centered cubic and other metals, 13 Cr-Fe, 18-8 stainless steel, K42B1 Nichrome V, Hipernik, Inconel, Stellite " 21," Refractaloy, Kovar, mild steel, a series of Cr-Fe alloys and a series of Co-Fe alloys. Since many of the commercial alloys in this list contain more than two metals, various complicating factors in the identification of the oxides formed may arise.

Jan 1, 1946

By Erland Johnson

BRINE was discovered at Avery Island, La., in 1790, but it was not until 1862 that rock salt was found about 13 ft below surface-the first discovery of rock salt on the continent. Maximum elevation of the island is 152 ft and elevation at the shaft 31 ft. The mining level is 530 ft below elevation at the shaft and the shallowest salt about 12 ft below surface. A shaft was sunk in 1869 when the mining operation started. In 1898 the present shaft was sunk, and the mine has been operated by International Salt Co. ever since.

Jan 6, 1957

By Chandler Morse

RENEWABLE VS. NONRENEWABLE NATURAL RESOURCES Nonrenewable resources, such as minerals, are the inevitable center of attention in discussions of depletion and exhaustion. Nevertheless, it may well be proper to regard some nonrenewable resources as not subject to exhaustion, and renewable resources may sometimes be treated as if they were finite stocks. Thus, the availability of nonrenewable resources is not and probably never will be known completely Chap. 2.5A, and therefore is not subject to firm predictions concerning exhaustibility. Moreover, because exploration and discovery are more or less continuous processes it is often appropriate to regard mineral supplies as flows, and to treat the estimated reserves as working capital, an inventory, continually depleted by use and augmented by discoveries.23 The aggregate economically exploitable stocks of a given mineral are seldom estimated (or estimatable) with precision, as Chap. 2.5A shows, and even when they are, forecasts concerning years of remaining life can be and often are falsified by changes in one or more of the multidimensional conditions of supply and demand; or the productive services formerly derived from an exhausted stock may continue to provided without material impairment by one or more substitutes b Conversely, the renewable resources are all subject to depletion when the rate of use exceeds the natural or induced rate of replenishment, and cases of exhaustion or near exhaustion, as through soil erosion, overcuttmg of forest lands, and overfishing, are rather common c Where exhaustion is a clear possibility the resource may either be exploited on a consciously adopted "sustainable yield" basis or be treated as an exhausting asset." In some cases, conscious treatment

Jan 1, 1976

By E. T. Turkdogan, L. S. Darken, R. J. Fruehan

Further consideration is given to the application of the quadratic formalism to evaluate the thermodynamics of binary metallic solutions from experimental data. The use of the thermodynamic relation, in(r1/r2) dN2= 0, in the evaluation of activity data is discussed. The empirical correlations derived previously for enthalpies and entropies of solutions in Part II are shown to be predicted theoretically for a special case. The applicability of the quadratic formalism to the activity coefficients for binary organic solutions is demonstrated. DARKEN&apos; introduced a quadratic formalism describing the composition dependence of the activity coefficient in the terminal regions of binary metallic solutions. In a subsequent paper (Part II) Turkdogan and Darkeen2 extended this formalism to the enthalpy and excess entropy of binary metallic solutions, and showed that the available data for the activity coefficients and heats of mixing of many solid and liquid binary metallic solutions confirm reasonable applicability of the quadratic formalism. Much variation was noted, however, in the extent of the terminal regions from one system to another, commonly from about 10 to 70 at. pct. For the present purpose, equations derived previously need be given only for one of the terminal regions, e.g. region (I), 0 < N2 < N&apos;2: where subscripts 1 and 2 indicate quantities for components 1 and 2 and superscript ° the values at infinite dilution; other terms are: N = atom fraction, y = activity coefficient, = partial molar enthalpy of solution, ?HM = molar heat of solution, ?Sx = excess partial molar entropy, ?Sx = excess molar entropy. The heat and entropy like terms (constants) el, and S12 are defined in the following expression for the temperature dependence of a12, thus a12 £12 — s12 rnl 2.303RT 2.303 R l J Using this formalism, the thermodynamics of binary systems in the terminal regions may be described over a temperature range of experisental interest in terms of eight quantities: Lº1—Lº2, ?Sx1,?Sxº2 , £12 ,£21,fiai, S12, and S21. In the previous paper, these quantities were evaluated for many solid and liquid binary solutions, and two significant correlations were observed between these thermodynamic quantities pertaining to the terminal regions, thus [10] and [11] Combining Eqs. [9], [l0], and [ll] and rearranging gives a12 -a21 = 1.382R log rº2- 0.08(?S2xº- ?S1xº) [12] Since the second term involving entropies is small and Eqs. 1101 and [ll] are empirical relations, the above equation may be simplified to a12 = 2.74 log rº2 [13] Using the values of a&apos;s and y°&apos;s compiled in Parts I and 11, a12 - a21 is plotted against log(rº2/rº1) in Fig. 1; the line drawn has a slope of 2.74. For Hg-K at 300°C, log(yº2 /yº1)= —5.10, not shown in Fig. 1, and from correlation [13], a12 - a21 = -13.97; this is to be compared with -10.76 derived from the activity data (Part II).

Jan 1, 1970