All ferrous alloys can be made brittle by straining at sufficiently low temperatures. However, the changes in mechanical properties for different ferrous materials with decreasing testing temperature do not appear to follow any universal law. In particular, complex effects of testing temperature have been observed if cold worked steels were subjected to tensile tests at low temperatures. EFFECTS OF PRESTRAINING AT A TEMPERATURE ABOVE THE TESTING TEMPERATURE ON THE FRACTURE CHARACTERISTICS‡ A considerable amount of data has been presented by a number of investigators on the fracture characteristics of various cold worked steels.' These data usually relate to a two-step procedure first used by Davidenkov,² consisting of stretching by tension to a certain strain or " prestraining" at room temperature and then completing the tensile test, or "testing" at the temperature of liquid air. On the basis of data of this type made available to date, ferrous alloys can be classified into two groups with respect to their fracture characteristics observed on testing at a low temperature after prestraining at room temperature. Very complex phenomena have been observed for all annealed steels. On the other hand, some observations indicate that steels in certain other conditions represent a fundamentally simpler relation. In considering the effect of prestraining at one temperature on the properties obtained at some lower temperature, it should be expected that any cold work reduces the ductility retained in proportion to the magnitude of the cold work. However, the test data presented to date indicate that only heat treated (quenched and tempered) steels appear to conform to this expectation, according to the very limited test data in Fig 1, presented by McAdam, Geil and Mebs. This series of tests, Fig 1, shows that the retained ductility became smaller the larger the prestrain. However, this decrease is less than the amount of prestrain or, in other words, less than the decrease in ductility at the prestraining temperature. These effects of prestraining are fundamentally identical with those observed by Bridgman3 when a steel was prestrained (in tension) under hydrostatic pressure and then subjected to a regular tension test. It appears, therefore, that the basic effect of prestraining under conditions which yield a higher ductility than the (subsequent) testing procedure, consists of gradually increasing the total ductility of the metal from the initial low value of testing to the higher value of prestraining. On the other hand, all annealed steels, if cold worked by tension at room temperature and then tested at a lower temperature, provided that some ductility is retained, showed a far more complex behavior than that discussed above. This relationship is exemplified by Fig 2, for three pearlitic steels.4,5 These particular steels were selected because of the various shapes of their ductility-prestrain curves. All three steels, and any other investigated so far, suffered a rapid decrease in retained (and consequently also in total) ductility when subjected to small pre-strains. Then, after exceeding a certain prestrain it was generally observed that the ductility recovered.* This rather complex behavior of annealed steels may be tentatively correlated with the presence of stretcher strains at small restrains. Heat treated steels do not exhibit stretcher strains. This fact might possibly explain their simpler prestrain-retained ductility relationship. The destructive effect of these stretcher strains may possibly be associated with the presence of triaxiality, which may occur in any highly non-uniform stress and strain state (and which is retained as residual stress after unloading). Even a small degree of triaxiality may then cause a reduction in ductility, or even embrittlement at a sufficiently low testing temperature. The discussion presented above deals with the effects of cold working at a high temperature on the fracturing

Jan 1, 1950

By George W. Small

The ore, as it is raised from the mine, has all average assay-value of $11 per ton, chiefly in the form of free gold. All the ore goes directly to the stamp-mills, of which there are two. The older and larger mill contains sixteen batteries of five stamps each, with one Frue vanner to each battery. The new mill has eight batteries of five stamps and two Frues to each battery. The large mill is driven by Leffel turbine wheels, with a pressure of eighty feet, and a consumption of 600 miners' inches of water. The smaller mill is driven by "hurdy-gurdy" wheels with a pressure of about 550 feet and a consumption of 150 inches of water. At both mills the tailings from the stamps pass over about 20 feet of plates on their way to the Frues. In each set of plates the first or upper one is copper, the rest are so-called silver plates. The bullion from the stamps is about 800 fine in gold and 200 in silver. The concentrates from the Frues average from 11/4 to 1 ; per cent. of the ore stamped. They very rarely exceed 2 per cent. I was unable to get the exact assay-value of the concentrates, but it is said to vary between $100 and $200 per ton. The concentrates are treated at the chlorination works at the rate of one hundred tons per month. The capacity of the works is somewhat greater than this, but as the supply of concentrates is limited it is not deemed advisable to work them up any faster. Care is taken to keep the concentrates always damp until they are put into the roasting furnace. If this is not done, a decomposition of the pyrites begins, forming lumps which do not roast, and which consequently cause a loss of gold in the residues from leaching. A Fortschaufelungsofen is used for roasting. Its dimensions, incloding fire-box, are 12' X 80'. The hearth is one continuous plane, but the charges, of which there are three in the furnace at one time, are kept entirely separate. The furnace-men call the three compartments, the "drying," the " burning," and the " cooking" compartments. In the middle, or "burning" compartment, the ore is spread

Jan 1, 1887

By D. Ott

Results of a research project on investment or lost wax casting will be presented. The project was concerned with various aspects of the process as they are typical for the production of jewellery from gold alloys. During these investigations testing methods for investment quality as well as for casting quality and the various process parameters were developed and charateristic defects as they occur in practice were traced back to their origin in the process. Investigated were various static casting and centrifugal casting methods in different atmospheres as well as vacuum casting in devices of different design. It was shown that independent of the method a close control of the many process parameters interfering with each other is essential for a quality casting.

Jan 1, 1984

By M. Metzger, J. Intrater

IN the large number of important studies on high-purity aluminum (e.g., recrystallization and grain growth, creep, internal friction), it does not seem to have been generally recognized that the iron content, despite its very low figure, has a strong influence on a number of properties. In part, its influence is due to the very low solubility of the Fe-A1 6 phase. For aluminum of about 99.99 pct purity, the iron content may be 0.001 to 0.004 pct. For values in this range, a second phase will be present below 410" to 480 °C. This was determined by extrapolation of a log solubility vs inverse temperature plot of the solid solubility data of Edgar.' One consequence is the inhibition of grain coarsening below the solubility limit. This is shown in Table I, which gives, for three iron contents, the annealing temperature required for the absence of grains smaller than 1/2 mm average diameter together with the minimum temperature for the presence of some grains larger than 2 mm diameter. The specimens were 1/4x 1 1/2-in. strips cut from hard-rolled 1/16-in. sheet supplied by the Aluminum Co. of America.

Jan 1, 1954

By N. Standish

Heat transfer coefficients have been measured in beds of various packings irrigated with mercury and molten fusible alloy countercurrent to hot gases. The measured coefficients for both systems were found to increase with gas velocities and liquid rates. Correlations were determined which show this dependence and also indicate that heat transfer in these systems is influenced by the liquid flow characteristics and the thermal conductivity of the gas and the solid packings. A heat transfer model has beer2 proposed which explains the various features of the experimental results. On the basis of this study, which gives an insight into the heat exchange in the melting zone of the blast furnace, it was concluded that by comparison with the furnace stack heat transfer coefficients are about 1.5 times higher in the melting zone. EACH year large tonnages of metal are produced in operations which, in part, involve liquid metal irrigation of "packings" countercurrent to hot gases. The melting zone in blast furnaces and in cupolas is a good example of packings irrigated with a liquid melt countercurrent to gases. In all instances of this kind large amounts of heat are exchanged and it is desirable to have some knowledge of heat transfer phenomena involved in these systems. So far the most common method of analyzing furnace efficiencies, fuel requirements, and the general thermal state of the furnace has been through the use of heat balances. As heat balances are essentially statements of the first law of thermodynamics they give no real indication of the factors which govern heat transfer between phases in the various zones of blast furnaces. Hence, rational improvement in production efficiency and the development of theoretical models is only possible if the heat transfer characteristics are known at every stage of the process and related to the important variables involved. This has been generally recognized for some time but it was only recently that Kitaev et al.' have produced a comprehensive treatment of heat transfer in solid-gas countercurrent systems such as the blast furnace stack and the packed bed regenerator. Using their treatment it is now possible to predict the effect of particle size, thermal conductivity, bed porosity, and the flow rates of both the gas and the solid material on the heat transfer in the blast furnace stack. However, the stack of a blast furnace is only one part of an integral unit for which the heat transfer analysis cannot be complete without also considering the heat exchange in the melting zone. The complexity of heat transfer processes in this region of the furnace has so far escaped quantitative description. Yet, the melting zone accounts for a greater amount of heat exchange than all the other zones of the furnace put together. Moreover, if the reduction of oxides in the melting zone proceeds in part in the liquid state the importance of heat transfer on furnace productivity and on the metal and slag temperatures is obvious. THEORY Heat transfer for two-phase flow in packed beds is a complex problem involving a number of heat exchange paths for which interphase areas are not known with any degree of certainty. Analytical solution is, therefore, difficult. This difficulty is emphasized by noting that Rabinovich~ and Luck have only recently solved the steady-state heat transfer for simplified two-phase heat exchangers of known area. However, useful progress can be made for the system considered by making a not unreasonable assumption that the usual heat transfer considerations apply and restricting treatment to the steady state. For these conditions the rate of heat transfer dq in a height dz of a packed bed of unit area is: dq = UaATdz [I.] Integration of Eq. [I] then gives the total heat transferred: assuming both U, the overall heat transfer coefficient, and a, the interphase area, to be independent of bed height. Since a, in these systems, is unknown it is convenient to combine this term with U. The group U, then represents the overall heat transfer coefficient on a volumetric basis. If AT is linear with q, then for a bed of unit volume Eq. [Z] can be integrated to give: is the log mean of terminal temperature differences. From Eq. [3] U, can be readily calculated as q and {AT)im are experimentally obtained quantities, but a difficulty arises in interpreting its meaning. Two approaches are possible depending on whether the effect of packing in the transfer of heat is neglected or not. If the packing is thermally decoupled then the resistance concept gives the relationship: which states that the overall resistance is the sum of the gas phase and the liquid phase resistances (assuming areas are equal throughout). Because the resistance to heat transfer in liquid metals is negligible by comparison with that of the gas,4 Eq. [4] can be simplified, i.e.:

Jan 1, 1969

By J. W. Harden

THE observations here following are the result of an examination made as to the feasibility of extending the South Mountain Railroad from Pine Grove to Waynesborough, and of the commercial value of the ore through which such extension would be made to pass. The road at present built and in operation has a junction with the Cumberland Valley Railroad, half a mile east of Carlisle, and extends southward to Pine Grove, a distance of 176 miles. The extension proposed will add to it near 27 miles, making its total length 44$, more than 23 of which will run through, or in close proximity to, beds of ore. Along the route taken there are a number of openings at which the ore is gotten, of which the Craighead bank, Huntzinger's bank, Lowrey's bank, Wenkoop's bank, the Henry Clay bank, the Fuller

By E. C. van Reuth

FIFTY-three alloys have been examined in the Fe-W and Co-W alloy systems in an attempt to verify the finding of o phases in these systems as reported by Goldschmidt.' The alloys were examined metallographically and by X-ray diffraction. The 10-g specimens were made by powder metallurgy techniques. Very fine, high-purity powders were compressed in a double-acting die at 120,000 psi after hydrogen reduction. All compacts were then sintered for 200 hr at 950°C in a helium atmosphere. Metallographic investigation and X-ray diffraction proved this time to be sufficient to allow complete homogenization before the subsequent high-temperature anneal. Each specimen was then sealed into an evacuated silica capsule and annealed at 1400"or 1500 C (except two) for 25 hr. (The 60 pct Fe and 55 pct Co alloys taken to 1610"and 1680°C respectively were held at these temperatures for 1hr. However, since these structures were at equilibrium before the anneal, and in view of their resultant structures, it is assumed that they reached equilib-

Jan 1, 1960

By B. J. Bayles, J. A. Ford, M. J. Salkind

Unidirecltonally sulidijied AL-A13Ni was found to exliibit excellent microstructural stability to 508°C. Above this temperature the transverse micvostructure coarsened in a manner analogous to "Ostwald Ripening", but the A13Ni whiskers did not spheroidize or foreshorlen. The coarsened whiskers reinforced the matrix as effectirely as the finer whiskevs and no reduction in room-temperature tensile strength mas noled after exposure for 90 hr at 96 pel 0-1 the absollite melling temperature of the eulectic. The slability was auribucted to the presence of low-index (and presurrlably lor-energy) cvystallographic interjaces between phases. The driving force for microstructural coursening was presumed to be the reduction of interfacial energy between the phases. Finer micvoslructures were found to coarsen more rapidly than those which weve imitally coarser. FIBER-reinforced metals have been shown to exhibit good short-time tensile properties at elevated temperatures.1-4 However, many elevated-temperature applications require long-time property retention which dictates the necessity for microstructural stability. Two types of instability are common to fiber composities. The first, chemical instability, is due to chemical reaction between the matrix and the relnforcing phase. Petrasek and weeton5 have shown that chemical reaction between tungsten wire and several copper alloy matrices resulted in degradation of the reinforcing phase and reduction in strength of the composite materials. Kreider and Leverant4 have noted similar behavior for boron-reinforced aluminum above 400°C. The second type of instability arises in systems in which the phases are essentially chemically stable with respect to each other and is characterized by spheroidization and/or agglomeration of the reinforcing phase. parratt6 has reported this type of degradation to occur relatively rapidly at moderate temperatures for nickel and cobalt alloys containing whiskers of silicon nitride, aluminum oxide, and silicon carbide and has identified it as "physicochemical" instability. Although both types of instability are the result of the differences in the chemical potential between the fibrous phase and the matrix, they may be differentiated by the fact that the second type, "physicochemi-call' instability, results in little or no net change in the composition or amount of each phase present. It does, however, result in a morphological change which profoundly affects the strengthening mechanism. Chemical interaction. on the other hand, results in a change in the composition and amount of one or more of the phases present, or the appearance of a new phase. In the latter case, the appearance of the mi-crostructure, that of a fibrous phase aligned in a matrix, may remain essentially unchanged, but the chemical degradation of the fiber results in markedly reduced composite strength. This investigation was initiated in an attempt to evaluate the microstructural and related mechanical property changes of a whisker-reinforced eutectic composite after elevated-temperature exposure. The composite system chosen for this study was the uni-directionally solidified A1-A13Ni eutectic which Lemkey. Hertzberg, and Ford7,8 demonstrated to behave as a whisker-reinforced composite. The microstructure of the unidirectionally solidified material consists of aligned needles of A13Ni in a matrix of aluminum. EXPERIMENTAL PROCEDURE Eutectic ingots having a nominal composition of 6.2 wt pct Ni were produced by melting 99.99+ pct A1 and 99.99 pct Ni in recrystallized alumina crucibles in an argon atmosphere. The analyses of the starting materials are listed in Table I. These master heats were cut up? melted by induction heating, and unidirectionally solidified vertically in 1/2 -in.-ID. 6-in.-long graphite crucibles, in a dynamic argon atmosphere. Therma1 gradients in the liquid were determined by measuring the temperature in the melt as a function of apparatus travel distance, as discussed by Kraft and Albright.9 The rate of solidification was assumed to be equal to the uniform rate at which the crucible assembly was withdrawn from the furnace. Ingots representative of nominal growth rates of 2, 5, and 11 cm per hr were produced and the solidification parameters are summarized in Table 11. Ingots used for met allographic analysis were pre-

Jan 1, 1968

By Beverley S. Randolph

The coal-measures of George's Creek coal-region, in Maryland, lie in a comparatively flat synclinal basin, about 4 miles wide. The dip of the measures is, in places near the edge of the basin, as much as 20 feet in 100. The Pittsburgh seam, known locally as the " Big Vein," is the only seam worked at the present time. Ocean No. 3, one of the large mines of the Consolidation Coal Company, has its opening on the outcrop of the Pittsburgh seam, in a ravine which cuts into this seam to such an extent as to bring this opening to within a mile of the axis of the basin. After working all the coal to the rise of this point, the mine was further developed by extending a slope down the dip of the seam, making such an angle with the line of greatest dip as to give a grade varying from 1 to 10 per cent., down which the empty cars carry a rope from a single-drum winding-engine. The coal was worked from each side of this slope in successive Iifts during its progress. From the top of the slope, for a distance of 4000 feet to the fourth lift, the " make " of water is drained by gravity through a heading into the adjoining mine. Below this point the water was pumped into this same heading, at the fourth lift, from which point, as before mentioned, it flowed by gravity.

Jan 1, 1895

Ware B. Gay, Richmond, Va.: Having followed the remarks of Prof. Woodworth with great interest, especially his suggestions for drilling in the part of the coal-field on the south side of the James river, I would like to inquire of him if he reached his conclusions after fully considering the situation as existing upon the north side of the James ? My reason for this inquiry is, that upon the north side the eastern and western outcrops are much nearer each other than appears to me to be the case upon the south side, and also that the western outcrop on the north side is much more clearly defined than upon the south side. It is now about twelve years since I first became interested in the Richmond coal-field—and until about six years ago I passed much time in investigation and spent thousands of dollars in developments. About six years ago the properties in which I was more especially interested were leased to other parties, and since that time I have had little or nothing to do with the mining operations. I regret to say the price of coals has ruled so low during most of the time since the lease was made that the developments have not been as extensive as the lessees had originally intended. The result of my investigations after considering all the theories, expert reports, legends and other information I could obtain bearing upon the subject, was the opinion, which I still hold, that the most practicable and most economical way for proving the extent and value of the field is by sinking slopes from the eastern outcrop, and by prosecuting such slopes in the vein and following the coal to the western outcrop, thus obtaining an actual cross-section in fact and not in theory. Proceeding upon this hypothesis, I sought for the positions where this could probably be accomplished most quickly and develop a marketable coal-area as the work thus progressed. The outcrops on the north side being nearer each other, and

Jan 1, 1902

By A. F. Melcher

THE present paper is a progress report. on an investigation of the physical factors of oil and gas and especially of their sands, I such as-pore space, size of pores or permeability, retentivity, viscosity of the oil, temperature, pressure, thickness and area of the pay sand, water relations, and capillarity. The purpose is to determine as many of these physical factors as possible, and to ascertain the relations existing, directly or indirectly, between these physical factors and the production of oil and gas. As yet only pore space2 and size of grains of pay sands have, been investigated, although an apparatus has been designed to determine the permeability of a sand to oil, water, or gas under definite drops of pressure between the entrance face and exit face of the sample. Messrs. E. W. Shaw, R. Van A. Mills, D. Dale Condit, G. B. Richardson, G. C. Matson, and C. H. Wegemann collected the samples upon which the physical determinations were made. Acknowledgment is made to my colleagues of the United States Geological Survey for many suggestions and criticisms; to Mr. Mills for the production data given of the oil wells from which some of the samples were collected; to Mr. A. W. McCoy of the Empire Gas and Fuel Co., Bartlesville, Okla., for many ideas.

Jan 4, 1920

By A. M. Crawford

INTRODUCTION Grouting is an engineering operation which has been practiced for many years and a considerable amount of experience and skill has been developed in this field. However, a review of the current literature (Houlsby, 1982) reveals that the theoretical background and experimental observations that are necessary to adequately predict or describe the performance of a particulate grout (e.g. cement based) in a jointed geologic media are somewhat inadequate. In the near future it is envisaged that the use of grout and grouting techiques will be used to tackle even more difficult problems than have been considered in the past. One problem that is currently being faced by the rock mechanics engineer is the development of geologic repositories for the disposal and containment of high level radioactive waste. In such structures there will be only one opportunity to ensure the success of the containment system. This success will depend to a large extent on the adequate and successful performance of the grout curtains to be utilized around the shafts and shaft liners. Regrouting will not be possible. There are other problems in rock mechanics in which it is frequently necessary to inject particulate media into passages of small dimensions, and where typically the size of fracture being injected is of the same order of magnitude as the particle dimension. For example, in the oil industry in hydraulic fracturing the enhancement of fracture conductivity is maintained by means of proppants introduced into the fracture.

Jan 1, 1984

By D. G. Hartley, P. C. Hayward, K. R. Weller, U. J. Sterns

The major copper loss at Mount Lyell is in the coarsest particles presented to flotation. An analysis of data collected from the five Primary and six secondary ball mill circuits showed that grinding was limited by low breakage rates in secondary mills, possibly due to oversize balk. For five months, the make-up ball size for one secondary mill was reduced from 50 to 30 mm (2 to 1.1 in.). Frequent steady-state tests indicated that overall average breakage rates could be increased by about 70% using smaller balk. A mathematical simulation of the whole circuit with increased breakage rates showed that the resultant finer grind was likely to improve copper recoveries by about 2%.

Jan 1, 1984

By P. H. Dudley

When we see the magnificent passenger-trains of from 8 to 12 coaches, drawn by locomotives weighing from 100 to 110 tons, at speeds of from 50 to 60 miles per hour between terminals, to make a schedule of 45 miles per hour, and freighttrains of from 50 to 75 cars of 60,000 pounds capacity, drawn by one locomotive, it is hard to realize that it lacks a few months of fifteen years since my pioneer 5-inch 80-pound rail for the United States was laid by the New York Central aid Hudson River Railroad Co., in July, 1884, on the Harlem line. Shorter passenger-trains, of from 4 to 5 coaches, are run much faster, notably the Empire State Express, the schedule of which for the 440 miles between New York and Buffalo requires 53.3 miles per hour, calling for a running-speed, for much of the time, of from 65 to 75 miles per hour, while higher speeds are very common. On other railroads laid with my 5 1/8-inch 80-pound rail, speeds of from 60 to 75 miles per hour obtain in daily practice. On many of the important railroads east of the Mississippi high speeds of from 60 to 70 miles per hour are part of the daily service. So many instances of speeds of 90, and even 100, miles per hour have been recorded that they must be considered as likely to occur on important lines, and provision must be made for them in the track. Solid mail-trains of from 6 to 8 cars are run from New York to Chicago, 1000 miles, in twenty-four hours; and, commeneing with the present year, shorter trains are running from Chicago to San Francisco, 2000 miles, in three and one-half days. In the freight-service equally important progress has been

Jan 1, 1900

By Arnulf Muan

PHASE relations in three isothermal sections (l000°, 1100°, 1200°C) of the system Ag-Fe-Pd have been determined as part of a program to develop improved crucible materials for containing low-melting iron silicates at low oxygen potentials. The following experimental method was used: Two- to 3- g samples of each of forty different alloys within the system Ag-Fe-Pd were made up from metals of 99.9 pct purity. The mixed metal powders were contained in a 1-cc crucible of dense recrystal-lized alumina and heated in a protective atmosphere (90 vol pct A, 10 vol pct H2), first to complete melting for approximately 30 min and subsequently at the desired equilibration temperature (1000°, 1100°, or 1200°C) for approximately 24 hr. The samples were then quenched rapidly to room temperature and examined metallographically as well as by X-ray techniques. Unit cell dimensions were compared with standards obtained by study of one-phase alloys of known compositions. The results are summarized in diagrams (a), (b), and (c) shown in Fig. 1. Heavy solid curves outline areas comprising compositions of mixtures consisting of the phases labeled for each area. Mixtures in which liquid is the only condensed phase present are confined to very narrow areas adjacent to the Ag-Pd join at high silver contents. An enlarged, distorted picture of the phase relations prevailing in these areas is shown in the upper-left circular insert. Particular attention is directed toward the misci-bility gap which occupies major parts of the composi-

Jan 1, 1962

By James P. Kimball

THE object of the present memoir is to put on record some practical experiments by the writer in smelting a silicious native magnetite with no other flux than the silicates of its own gangue: This work was undertaken in the spring of 1878 for Messrs. Naylor & Co., of Boston, to whom I am indebted for the privilege of here communicating its results, these having hitherto only been simply announced.* So far as I am aware these are the first instances of the kind in this country that non-calcareous; or rather non-carbonated, magnetites have successfully been used strictly alone as self-fluxing ores in the blast furnace; that is, without the addition of calcareous flux in the form either of limestone, quicklime, calcareous ore, or basic (calcareous). slag. Previous to the spring of 1878, when the Chateaugay magnetic ore was first brought to my notice, its use had been limited to Catalan forges, after "separation" at the ore bed. The blooms and billets made from it in the several forges of Messrs. Weed & Williams, and of Mr. Williams, were well known in the trade as among the best in the market. The Chateaugay ore beds proving of great magnitude, and the ore exceptionally low in phosphoric acid, it commended itself for blast-furnace purposes to Messrs. Naylor & Co., who employed nee to blow-in the charcoal furnace at Pittsford, Vt., on this ore in the spring of 1878., a previous trial of this ore in the same furnace in the fall of 1877 having proved abortive. This was therefore the first time that Chateaugay ore was successfully smelted in a blast furnace, although since well known as a blast-furnace ore possessing superior and exceptional qualities. The Pittsford furnace, although rebuilt in 1844, and subsequently improved by the former owner, the late J. Prichard, is one of the few furnaces of the old type with open breast (Sumpfofen) still active in this country. Its improvements on furnaces of the period, * Bulletin American Iron and Steel Association, XII, 1878, 132, 156.

Jan 1, 1881

By L. S. Richardson, N. J. Grant

Iodide-grade titanium, two oxygen alloys, and two aluminum alloys were studied by means of creep-rupture tests from 1000° to 2000°F. From the test information an evaluation was made of, 1) the relative creep-rupture strengths of the u (hexagonal-close-packed) and 0 (body-centered-cubic) forms of titanium and some of its alloys; 2) the effects of solid-solution strengthening by oxygen and aluminum on the u and 0 structures; and 3) the extent and effect of atmospheric oxygen alloying on rupture life in tests above about 1000°F. THE use of titanium alloys at temperatures above 1000° F has been considered unlikely by most investigators because of low creep strength (based on a requirement for room-temperature ductility, formability, and weldability) and low oxidation resistance. The results of this testing program do not entirely uphold this pessimism in terms of strength and oxidation resistance. The observations described below are based entirely on stress-rupture results, although some creep tests were also carried out on these alloys. Three items of primary importance are covered: 1) Stress-rupture data in the form of the Larson-Miller parameter curves for several titanium alloys at temperatures up to 2000°F; 2) The relative strengths of the hexagonal-close-packed a structure and the body-centered-cubic 0 structure; 3) The effects of solid-solution alloying on the creep-rupture properties of titaniu'm at elevated temperatures. Only two investigatons have reported the creep- rupture properties of titanium at temperatures above 1000° F. Lunsford and rant' tested iodide titanium; their values are also utilized in the paper. EXPERIMENTAL PROCEDURE After a few tests had been made in a conventional creep-rupture test machine, it became clear that some sort of atmospheric protection would be necessary for short-time tests conducted at temperatures above 1600°F, or for times greater than 100 hr at 1200°F or above. Several furnace units and test machines were constructed, the most successful of which is shown in Fig. 1. Certain experimental difficulties peculiar to titanium were encountered; for example, the use of molybdenum holders was dictated because titanium forms low melting-point eutectics with conventional high-temperature alloys containing appreciable amounts of iron, nickel, or cobalt. This same difficulty made the use of chrome l-alumel thermocouples in direct contact with a test specimen impossible, above about 1500" F. The high-temperature high-vacuum furnace shown in Fig. 1 was capable of maintaining a vacuum of better than 10"5 mm of mercury at 2000°F (pressure measured in cold part of system) and 5 X lo-' mm at room temperature. Most of the tests eonducted in vacuum were at temperatures

Jan 1, 1960

By C. C. CONCANNON

POTASH is an essential. It is necessary as an ingredient in fertilizers or as a plant food, and certainly one of the great problems, and one of increasing gravity, is the maintenance of agricultural fertility that we may have adequate food supplies. When one thinks of potash one thinks of Germany. The first and most important deposits of soluble potash salts were found in Germany, and it was through Ger- man research and the application of a highly developed knowledge of chemistry that the value of these deposits was recognized and appreciated in the field of agricultural fertilization. The Germans knew that they had something of great value in their potash resources, not only because of the advantage derived from the extensive use of it in their own intensive farming operations at home, but also because of the pressing need for it on the part of other countries. Appreciating the economic value of this in international trade, they fostered the industry to the fullest extent and devoted much attention to well organized propaganda designed to bring out the essential need for potash of German origin throughout the world. Thus every one came to believe that potash was an essential commodity of only German origin and as such it held an extraordinary position in world trade prior to 1914.

Jan 1, 1926

By W. L. Falke, A. A. Cochran

Vast deposits of low-grade manganese ore exist in the United States, yet domestic production is insignificant compared to the more than 2 million tons of ore imported yearly into this country.1 A basic problem in connection with manganese is to find economical ways to utilize domestic resources.2 As a part of its program to conserve domestic mineral resources and to reduce dependence on foreign sources, the U.S. Bureau of Mines has conducted extensive research to broaden manganese technology and to find economical processes for recovering manganese from these low-grade resources. Although a great many processes have been proposed for treating domestic manganese resources, a failing of many of them is that too many steps are involved for economical operation.2 Some of the major processes that have been proposed were reviewed by Norman and Kirby.3,4

Jan 3, 1967

EUGENE COSTE, ? Calgary, Alta.-Evidently in Argentine they have a petroliferous province just east of the Andes where very much the same conditions exist as are found on the east side of the Rocky Mountains and in the plains adjacent. It strikes me, though, that the same mistake is being made in Argentine in the exploration for oil as was made in Alberta, Canada; viz., drilling the wells too .near the seepages in the belt in the eastern part of the petroliferous province, too near the mountains. This same mistake was made in Alberta, with disastrous results; viz., only fissure production was found. The strata so near the mountains are tilted at a very strong angle, such as is described in this paper, and the dislocations are intense. On the other hand, we have found that when we get 100 or 200 mi. away from the mountains we get into oil and gas belts which are very prolific. So far our fields in Alberta have been gas, but in Wyoming, as you know, they get many thousands of barrels a day. I have no doubt that conditions in Argentine are exactly similar but that they have so far kept too near the mountains and that they want to explore the belts farther east to obtain better results.

Jan 4, 1919