By L. J. Boucher

The beneficiation process at Northampton is described and reasons are given for installing a flotation plant. The economics of running the plant, the difficulties of operation, and subsequent remedial action are discussed.

Jan 3, 1953

By Lawrence Addicks

THrough the courtesy of Dr. James Douglas I am permitted to give a summary of some of the results obtained in leaching slimes tailings in a series of experiments conducted under my direction at Douglas, Ariz., during the past year. While the test run for which the data are given deals with a particular case, much of the work is general in its application and may therefore be of interest. This work was done upon the ores of the Burro Mountain Copper CO. A description of the geology of the district will be found in the paper by R. E. Somers published in this volume, p. 604. The mineral is pyrite and chalcocite very finely disseminated throughout the gangue and a characteristic of all the ores is the large amount of alumina present. A representative analysis of the particular ore under consideration would be about as follows: Cu, per cent..................... 2.35 S, per cent...................... 3.0 Ag, ounces per ton.............. 0.05 CaO, per cent.................. 0.5 Au............................ None K2O, per cent.................... 4.0 Fe, per cent..................... 1.50 SiO², per cent.................... 70.0 Alz²O³, per cent....................13.OO The leaching of the ore direct was early dismissed from consideration for the following reasons: 1. The ore would have to be quite finely crushed to liberate the mineral for leaching; concentrating after crushing would cost but a few cents a ton; and a higher total reeovery would result from leaching tailings rather than ore. 2. Rough concentration would yield a suitable material for roasting to make sulphur dioxide or sulphuric acid in connection with the leaching scheme. 3. Such a program put the question of cost vs. recovery on a basis where flotation and discarding of tailings were directly comparable. Concentrating experiments already available indicated that the tail-

Jan 1, 1916

(Members are urged 'to, send in for this column any notes of interest concerning themselves or, their fellow-members.) Members and guests who registered at Institute headquarters during the period Sept. 10 to Oct. 10, 1915: George H. Blakemore, Sydney, N. S. W. W. B. A. Dingwall, San Antonio, Tex.. H. Haege, Sydney, N. S. W. R. H. Jeffrey, London, England. C. A. Filteau, New York, N. Y. H. S. Emlaw, Spring Lake, Mich. Myron R. Walker, Cerro de Pasco, Peru. Y. T. Woo,' Tientsin, China. William R. Grunow, Morenci, Ariz. A. L. DeDeken, LouVain, Belgium. E. DeGolyer, Norman, Okla. K. P. Swensen, Tokyo, Japan. William W. Elmer, Tuttletown, Cal. Charles Enzian, Wilkes-Barre, Pa. Huntington Adams, Iquique, Chile. C. F. Schnepp, Cobalt, Ont., Canada. W. Ray Cox, for several years Mineral Inspector of the General Land Office at Portland, Ore., has been appointed Professor of Mining and Metallurgy in the School of Mines, Oregon Agricultural College, Corvallis, Ore.

Jan 11, 1915

Through the generosity of Sir Robert Hadfield, Honorary Member, the Directors of the American Institute of Mining Engineers are enabled to announce the Hadfield Research Prize of $1,000 for the best contribution to the publications of the Institute upon the general subject of The Different Forms and Combinations of Carbon with Iron, including those in Iron Alloys. The prize will be awarded at the Annual Meeting of the Institute in February, 1916, to the best paper upon this subject which is presented to the Institute before Nov. 1, 1915, provided such paper is deemed worthy by the Institute's Iron and Steel Committee. The following suggestions are also added for the guidance of those who may take part in this research. While' it is not desired to define closely the exact lines or scope of the proposed research, as it is advisable to make these as broad as possible, the object in mind maybe said to be generally as follows: To elaborate and find out the best methods of determining the forms of carbon in steel or iron, including those in iron alloys. A portion of the work would probably be a continuation of the researches which have in the past been carried out by Jullien, Abel, Muller, Ledebur, T. Sterry Hunt, Akerman, Arnold, Stead, E. D. Campbell, Hogg, Parry, Upton, and others. In a generic way, metallurgists now speak of carbides, sub-carbides, double carbides, special carbides, and other combinations. It is very desirable that these should be accurately defined and understood. It is also desirable to know whether there are other or new forms; if so, can these be separated and their characteristics obtained. It may be interesting to point out that the carbon compounds now definitely known are stated to number over 80,000. It is very probable, therefore, that there is room for much valuable and useful research to be carried out with the object of increasing our knowledge of the various combinations of carbon with iron, as probably some of these are still unknown

Jan 5, 1914

By Foster Fraas

That variations in the humidity of the air and in the moisture content of a mixture of broken solids being separated electrostatically cause trouble is not new.' Much of the reputation for unreliability commonly ascribed to the electrostatic separation processes is probably due to this one factor alone. Some operators dry thoroughly before separating; and while this is good in many instances, there are others in which it is not the remedy for trouble. Some mixtures behave best in very dry air and with the mixtures fed to the separator while hot to reduce the adsorbed water content. On the other hand, an overdried mixture on coming to equilibrium with more humid air, has been known to take up moisture selectively on one family of particles, as of coal in the presence of slate and clay, and give sharper electrostatic separation. From these observations it is concluded that there is a permissible moisture content for a particle and also for the atmosphere surrounding it, if in equilibrium, at which the particle will have a conductivity or cntact potential2-4 that is ideal for electrostatic separation. This permissible moisture content varies between a wide range of limits for the different materials that are are and with the kind of electrostatic separating process used. Water can be present as a result of adsorption and condensation from the atmosphere, as an accumulation before or during mining, or as a residue from a previous process step. The water may exist as a liquid film or as an adsorbed layer of vapor. If the water exceeds permissible limits it must be removed. Its state determines the method. Drying by evaporation is necessary for adsorbed water, for part of the liquid-film water (that is, up to several percent of the dry weight), and for free water in the internal structure. Large water contents may be removed by drainage Or filtration. At just what point mechanical removal should cease and drying by evaporation begin depends upon the method of mechanical removal and its cost. Particles can also be separated according to their differences in dielectric constant when suspended in a liquid of intermediate dielectric constant. Recovery of this liquid presents a a problem' Permissible Moisture The adsorbed moisture on the outer surface of minerals can be quickly removed or replaced. Accordingly, in speaking of adsorbed moisture contents, either that of the solid or that of the surrounding air may be considered, the two values being connected by a distribution coefficient which varies with the temperature. However, such a condition does not necessarily exist in processes where an initially dry material is suddenly introduced into an atmosphere having a partial pressure of water vapor or where a moist material is suddenly introduced into a dry atmosphere. Here the resultant differences in the

Jan 1, 1949

By Reuel A. Cochrane, Harry H. Angst

The successful exploitation by opencut methods of the low-grade porphyry copper deposits is due to the economical handling of large tonnages. Large tonnages are possible only if the rock material is broken so that the large power shovels can operate with minimum delays. This is particularly true at the New Cornelia mine, where the dense, hard, tough rock material creates problems not encountered in most of the porphyry copper mines. The introduction of churn drills at the New Cornelia for primary drilling, in 1936, necessitated a complete change in the methods of breaking ground as formerly air drills had been used. The blasting operations are of particular interest because of the handling of great quantities of high explosives in safely and efficiently fragmenting the hard rock material. Rock Formations At the New Cornelia mine the rocks are quartz monzonite with a diorite border facies intruding a rhyolitic series. Overlying these formations is a fanglomerate formation composed of boulders of monzonite, diorite, rhyolite, and other types of rock of unknown derivation. (The word "fanglomerate" is used in this paper in referring to the local conglomerate type of rock formations.) The ore body is approximately 4800 ft. long and 2800 ft. wide, and is of the disseminated type. Mineralization occurs principally in the quartz monzonite and to some extent in the adjacent diorite and rhyolite. The principal ore minerals are chalcopyrite, bornite, and a small amount of chalcocite. Over a considerable area the quartz monzonite is extremely hard and siliceous in character, owing to pegmatitic zones of alteration. The hardness of the ground depends on the intensity of the silicification. In a small area in the pit, the monzonite contains an abundance of pyrite accompanied by sericitization and is soft and easily fragmented. This is true also in the remaining oxidized portion of the ore body. The diorite and rhyolite formations, like the monzonite, vary from extremely hard to very soft material, but on the whole are easier to fragment than the monzonite. Jointing is prevalent in all the rock formations and plays an important role in the blasting efficiencies. In the fanglomerate formation, numerous well-defined joints, widely spaced, tend to make the ground blocky when blasted. This is a deterrent to good fragmentation. In the other rocks the joints are more numerous and are closely spaced, except in localized areas where the formations are extremely hard. These descriptions indicate that the lowest blasting efficiency will be obtained in the harder formations, from which the major portion of the mine production is obtained; namely, the monzonite and rhyolite. All rock formations mined at the New Cornelia pit are so hard that excavation

Jan 1, 1943

By Harry H. Angst, Reuel A. Cochrane

The successful exploitation by opencut methods of the low-grade porphyry copper deposits is due to the economical handling of large tonnages. Large tonnages are possible only if the rock material is broken so that the large power shovels can operate with minimum delays. This is particularly true at the New Cornelia mine, where the dense, hard, tough rock material creates problems not encountered in most of the porphyry copper mines. The introduction of churn drills at the New Cornelia for primary drilling, in 1936, necessitated a complete change in the methods of breaking ground as formerly air drills had been used. The blasting operations are of particular interest because of the handling of great quantities of high explosives in safely and efficiently fragmenting the hard rock material. Rock Formations At the New Cornelia mine the rocks are quartz monzonite with a diorite border facies intruding a rhyolitic series. Overlying these formations is a fanglomerate formation composed of boulders of monzonite, diorite, rhyolite, and other types of rock of unknown derivation. (The word "fanglomerate" is used in this paper in referring to the local conglomerate type of rock formations.) The ore body is approximately 4800 ft. long and 2800 ft. wide, and is of the disseminated type. Mineralization occurs principally in the quartz monzonite and to some extent in the adjacent diorite and rhyolite. The principal ore minerals are chalcopyrite, bornite, and a small amount of chalcocite. Over a considerable area the quartz monzonite is extremely hard and siliceous in character, owing to pegmatitic zones of alteration. The hardness of the ground depends on the intensity of the silicification. In a small area in the pit, the monzonite contains an abundance of pyrite accompanied by sericitization and is soft and easily fragmented. This is true also in the remaining oxidized portion of the ore body. The diorite and rhyolite formations, like the monzonite, vary from extremely hard to very soft material, but on the whole are easier to fragment than the monzonite. Jointing is prevalent in all the rock formations and plays an important role in the blasting efficiencies. In the fanglomerate formation, numerous well-defined joints, widely spaced, tend to make the ground blocky when blasted. This is a deterrent to good fragmentation. In the other rocks the joints are more numerous and are closely spaced, except in localized areas where the formations are extremely hard. These descriptions indicate that the lowest blasting efficiency will be obtained in the harder formations, from which the major portion of the mine production is obtained; namely, the monzonite and rhyolite. All rock formations mined at the New Cornelia pit are so hard that excavation

Jan 1, 1943

By Foster Fraas

INTRODUCTION THAT variations in the humidity of the air and in the moisture content of a mixture of broken solids being separated electrostatically cause trouble is not new.1 Much of the reputation for unreliability commonly ascribed to the electrostatic separation processes is probably due to this one factor alone. Some operators dry thoroughly before separating; and while this is good in many instances, there are others in which it is not the remedy for trouble. Some mixtures behave best in very dry air and with the mixtures fed to the separator while hot to reduce the adsorbed water content. On the other hand, an overdried mixture on coming to equilibrium with more humid air, has been known to take up moisture selectively on one family of particles, as of coal in the presence of slate and clay, and give sharper electrostatic separation. From these observations it is concluded that there is a permissible moisture content for a particle and also for the atmosphere surrounding it, if in equilibrium, at which the particle will have a conductivity or contact potential2-4 that is ideal for electrostatic separation. This permissible moisture content varies between a wide range of limits for the different materials that are separated and with the kind of electrostatic separating process used. Water can be present as a result of adsorption and condensation from the atmosphere, as an accumulation before or during mining, or as a residue from a previous process step. The water may exist as a liquid film or as an adsorbed layer of vapor. If the water exceeds permissible limits it must be removed. Its state determines the method. Drying by evaporation is necessary for adsorbed water, for part of the liquid-film water (that is, up to several percent of the dry weight), and for free water in the internal structure. Large water contents may be removed by drainage or filtration. At just what point mechanical removal should cease and drying by evaporation begin depends upon the method of mechanical removal and its cost. Particles can also be separated according to their differences in dielectric constant when suspended in a liquid of intermediate dielectric constant. Recovery of this liquid presents a similar problem. PERMISSIBLE MOISTURE The adsorbed moisture on the outer surface of minerals can be quickly removed or replaced. Accordingly, in speaking of adsorbed moisture contents, either that of the solid or that of the surrounding air may be considered, the two values being connected by a distribution coefficient which varies with the temperature. However, such a condition does not necessarily exist in processes where an initially dry material is suddenly introduced into an atmosphere having a partial pressure of water vapor or where a moist material is suddenly introduced into a dry atmosphere. Here the resultant differences in the

Jan 1, 1947

By A. W. Schlechten, W. J. Kroll

As this paper is written, the only method for the commercial production of lithium metal is by the fusion electrolysis of LiCl-KCl mixtures, as first proposed by Guntz.2 The details of the industrial process have not been made public but Osborg8 stated that an efficiency of more than go pct is obtained with a lithium metal recovery above 95 pct and that the metal is 99.5 pct pure. Pletenev9 gave a power consumption of 66 kw-hr per kilogram of lithium metal produced with a salt consumption of 9 kg of LiCl and 0.4 kg of KCI. Pletenev's figures indicate a somewhat lower recovery than that given by Osborg. In a recent report on German lithium plants, Motock7 gives figures that are also less favorable than those reported by Osborg. At the German plants the lithium recovery in electrolysis was only 83.4 pct, with a power consumption of too kw-hr per kilogram of lithium. The metal averaged only 97 pct pure, with sodium and potassium as the chief impurities. The presence of SO2, SO3, Si02, Ba, Ca, and appreciable amounts of Na and Fe2O3 were especially disturbing in the electrolysis, and it was necessary to run the cell for some time to eliminate most of these impurities and condition the bath. It may be noted here that most of these impurities do not interfere with a thermal reduction process. These facts show that the present method of producing lithium is fairly efficient and would suggest that other methods could not compete. However, fusion electrolysis has certain drawbacks, such as the necessity of supplying costly, low-voltage direct current and of collecting and processing the anodic chlorine if it is not to be wasted. An even greater disadvantage is that lithium chloride must be used for an electrolyte. It is one of the most expensive salts of lithium, since it cannot be produced in anhydrous form by precipitation from aqueous solution, as is done with LiF or Li2CO3. The reduction of lithium by a vacuum process similar to the ferrosilicon method for the production of magnesium would have certain advantages. Small units, such as Pidgeon retorts, would give flexibility of production to meet demand, and a small plant would require moderate capital outlay. There is a possibility of using idle Government-owned magnesium plants for such purposes. The raw materials needed for vacuum thermal reduction would not have to be extremely pure, especially with respect to the iron and calcium content. This paper describes a series of experiments to determine the effectiveness of various agents for the reduction of lithium compounds. The investigation is part of a program of vacuum metallurgy con-

Jan 1, 1947

Jan 1, 1895

By Lee Morris, Charles E. Lawall

This paper represents the results of a study to determine the source, mode of occurrence and conditions influencing the flow and liberation of large volumes of inflammable gas in the Pocahontas No. 4 coal bed in southern West Virginia. A study of this kind is of interest in connection with mine ventilation, because in the removal of gases from coal mines it is very important to know the origin, the occurrence and laws of gas flow. The study was started in April, 1931, and the data and observations were obtained throughout a period of 15 months of field work. Geology The country where this study was made is mountainous and rugged; great cliffs, precipitous slopes and deep narrow gorges are found throughout the area. The outcropping rocks consist of stratified layers of sandstone, shale, limestone and deposits of coal of Carboniferous age. The Pottsville series of the Pennsylvanian, lying at the base of this period, cover the greater portion of the area. A stratigraphic section of the Pocahontas group of the Pottsville series is shown in Fig. 3. The older rocks outcrop in the extreme southeastern part of the area, but are under drainage in the central and northern parts due to the gradual northwest dip of the strata. The structure has a general northeast-southwest trend (Fig. 1). North of Dry Fork anticline the strata have been only slightly disturbed by movements of the earth's crust; it is now a long monocline. Southeast1 of Dry Fork anticline the strata are warped into great arches and deep troughs and are broken by overthrust faults. All of this folding is probably the result of the intense folding associated with the formation of the Appalachian Mountains. Pocahontas No. 4 Coal Bed The Pocahontas No. 4 bed, lying approximately 550 ft. above the base of the Pottsville series, is one of the thickest and most gassy coal beds in

Jan 1, 1934

By Gilbert Soler

Producers of alloy steels recognize the importance of chemical composition in relation to the hot-working properties and the typical surface defects found in their product. Each analysis of steel has its own peculiar characteristics. Under conditions of standard mill practice each analysis is susceptible to certain types of defects. Mill practice must be varied to obtain the best combination of surface and internal quality in the product. Chemical composition influences the cast structure and crystallization characteristics of the ingot. It also determines the rate of heating and cooling, the plastic hot-working range, and the phase structure of the steel at various temperatures. as well as the tendency toward scale formation and decarburization. This paper endeavors to emphasize the manner in which chemical composition affects the various properties of steel, and to indicate the relative importance of these factors in relation to the hot-working properties and surface characteristics of killed steel. The influence of chemical composition may be outlined as follows: I. Effect on the cast structure of steel, including: A. State of deoxidation, and type of inclusions. B. Gas content of steel. C. Freezing point and melting point of steel. D. Crystallization characteristics and segregation. 11. Effect on the hot-working properties and surface characteristics of steel, including: A. Plastic hot-working range. B. Phase structures at hot-working temperatures. C. Rate of heating. D. Cooling characteristics. E. Scale formation. F. Surface decarburization. EFferect of Chemical Composition on Cast Structure of Steel State of Deoxidation and Type of Inclu-sions.—The state of deoxidation is limited by the final chemical analysis desired in the finished product, and is controlled primarily by carbon, manganese, silicon, and aluminum, and to a lesser degree by chromium, titanium, vanadium, or other deoxidizing elements. The degree of deoxidation affects the density of the cast structure and broadly classifies the steel as killed, semikilled, or rimming. This in turn manifests itself in surface characteristics. The manner and extent of deoxidation also controls the amount, type, and distribution of nonmetallic inclusions formed. The equilibrium of manganese, silicon and aluminum with the slags and pouring refractories with which the metal comes in contact is important, especially in regard to inclusions of fire-clay origin. Some surface Seams and hot-working difficulties can be traced to nonmetallic inclusions.

Jan 1, 1941

By Gilbert Soler

Producers of alloy steels recognize the importance of chemical composition in relation to the hot-working properties and the typical surface defects found in their product. Each analysis of steel has its own peculiar characteristics. Under conditions of standard mill practice each analysis is susceptible to certain types of defects. Mill practice must be varied to obtain the best combination of surface and internal quality in the product. Chemical composition influences the cast structure and crystallization characteristics of the ingot. It also determines the rate of heating and cooling, the plastic hot-working range, and the phase structure of the steel at various temperatures. as well as the tendency toward scale formation and decarburization. This paper endeavors to emphasize the manner in which chemical composition affects the various properties of steel, and to indicate the relative importance of these factors in relation to the hot-working properties and surface characteristics of killed steel. The influence of chemical composition may be outlined as follows: I. Effect on the cast structure of steel, including: A. State of deoxidation, and type of inclusions. B. Gas content of steel. C. Freezing point and melting point of steel. D. Crystallization characteristics and segregation. 11. Effect on the hot-working properties and surface characteristics of steel, including: A. Plastic hot-working range. B. Phase structures at hot-working temperatures. C. Rate of heating. D. Cooling characteristics. E. Scale formation. F. Surface decarburization. EFferect of Chemical Composition on Cast Structure of Steel State of Deoxidation and Type of Inclu-sions.—The state of deoxidation is limited by the final chemical analysis desired in the finished product, and is controlled primarily by carbon, manganese, silicon, and aluminum, and to a lesser degree by chromium, titanium, vanadium, or other deoxidizing elements. The degree of deoxidation affects the density of the cast structure and broadly classifies the steel as killed, semikilled, or rimming. This in turn manifests itself in surface characteristics. The manner and extent of deoxidation also controls the amount, type, and distribution of nonmetallic inclusions formed. The equilibrium of manganese, silicon and aluminum with the slags and pouring refractories with which the metal comes in contact is important, especially in regard to inclusions of fire-clay origin. Some surface Seams and hot-working difficulties can be traced to nonmetallic inclusions.

Jan 1, 1941

By Stanley D. Michaelson, Norman Weisis

The purpose of beneficiation is to increase the economic value of an ore by elimination of waste rock or by separation of minerals that require separate reduction, without destroying the physical and chemical identity of the minerals. Flotation has replaced older methods of beneficiation to a very great ex- tent, nearly entirely in the case of the copper, lead, and zinc minerals and less completely in the case of such other minerals as iron, coal, and titanium. Flotation is also used to recover barite, fluorspar, feldspar, cement rock, spodumene, vermiculite, silica, beryl, and potash in the nonmetallic field, and cobalt, vanadium, germanium, antimony, mercury, molybdenum, manganese, nickel, gold and silver, cadmium, and bismuth for metals. The rapid growth of flotation to pre-eminence cannot be attributed to its low cost, because gravity, magnetic, and electrical methods may in some cases cost only half as much. But for ores containing finely disseminated minerals, these other methods are successful only in exceptional cases, for example the magnetic taconites or titanium-bearing sands. For low grade ores with coarse texture or spotty mineralization the advantages of low-cost gravity methods and highly efficient flotation are often combined, as in the beneficiation of coal and some ores of lead and zinc, phosphate, tungsten, and manganese. When an ore is responsive to either flotation or non-flotation concentration, or to combinations of the two, the choice depends upon cost of the process only when dealing with ores of low value; in other cases it is dictated by either the process efficiency or the product specification. Generally speaking, flotatio.1 is so efficient as compared with other methods of concentration that process cost is rarely an important factor in its selection. It is said, "The metal in the mill tailing has already been mined." Once the mining cost has been paid it doesn't increase total costs very much to do a thorough job of milling. With the exception of the few types of ores that are not amenable to flotation, the chief reason for preferring electrical and gravity methods to flotation may lie in the specification of the product. Flotation demands fine grinding, and specifications may not permit this with many nonmetallic ores or coal. Another reason is the size of investment-where capital is hard to obtain or the life of the property is short, the justification for a flotation plant may not exist, and one must be content to skim off the cream. y not exist, and one must be content to skim off the cream. Gravity processes often cost less than flotation because a large part of the waste rockcan be rejected without costly grinding, no chemicals are required,

Jan 1, 1962

By G. W. Form, W. A. Spitzig

The effects of hydrogen and vacuum shtering treatments on the physical and mechanical properties of arc plasma-sprayed tungsten were inuestigated. Temperatures examined ranged from 3000" to 4000°F in vacuum and 2000" to 3000°F in hydrogen for both single and duplex sintering cycles. Densities of 92 pct of theoretical density were obtained when a long-time hydrogen treatment at 2000°Fpreceded sintering in vacuum at 4000°F for 4 hr. This cycle also produced the highest ualues for modulus of rupture and bend angle. The results of this investigation point out the desirability of using a low-temperature long-time hydrogen treatment prior to a high-temperature vacuum sinter for arc plasma-sprayed tungsten. ADVANCES in the development of arc plasma-generating equipment have provided a high-temperature heat source that makes the fabrication of tungsten shapes possible by a metallizing process. Tungsten in the as-sprayed condition is very brittle. It has a density between 80 and 85 pct of theoretical density, a lamellar structure with elongated pores, and a high interstitial impurity content. To improve these properties, sintering treatments can be applied to the as-sprayed material, similar to those used for the densification of compacted tungsten powder. However, in view of the differences in the density and microstructure of as-sprayed tungsten as compared with compacted tungsten, responses to sintering were expected to be different. EXPERIMENTAL PROCEDURES The tungsten powder used in this investigation had a particle size varying from 3 to 13 p with an average diameter of 8p. The impurity level was less than 0.1 pct. The arc plasma spraying was done with an F-40 Thermal Dynamics Corp. plasma jet. Spraying was performed in air and thus required cooling of the substrate by an air blast in order to minimize oxidation. The spraying parameters employed in the fabrication of all specimens are listed below: Power input, kw 12 Arc-gas flow, cfh 95N2 + 5H2 Powder feed rate, g per min 33 Powder carrier gas flow, cfh ION, Spray distance, in. 3 Traverse rate, in. per min 30 Mandrel speed, rpm 100 Nozzle orifice, in. 7/32 These values of the spraying parameters correspond to optimum conditions ascertained in a previous study. Sintering was conducted at 3000°, 3500, and 4000°F in vacuum (< 0.1 Hg), and at 2000 and 3000°F in hydrogen. Duplex sintering treatments investigated are listed in Table I together with the designations that will be used for reference throughout this paper. The samples were fabricated by spraying onto a copper mandrel which was removed prior to sintering. The specimens used for the sintering analyses had the shape of small hollow truncated cones 1 in. high with an inside diameter varying from 0.500 to 0.125 in. and a wall thickness of 1/8 in. Specimens for bend testing were taken from hollow hexagonal prisms 1-1/2 in. high with a 1-in. diam across the flats and a wall thickness of 1/8 in. The bend-test specimens were ground to the dimensions 0.085 by 0.350 by 1-1/2 in. Prior to bend testing 0.0025 in. of stock was removed from each surface by electro-polishing. Density measurements were made by the water-displacement method. In addition, a porosimeter was used to determine the amount of interconnected porosity for representative samples. Strength and ductility were determined from recorded values in transverse bending using a cross head speed of 0.020 in. per min. The load was applied at the midpoint of a 1-in. span. The deflection data reported herein refer only to the plastic portion of the total deflection. RESULTS AND DISCUSSION The as-sprayed samples had a density corresponding to 83 pct (l pct) of the theoretical density of tungsten. Fig. 1 shows a representative as-sprayed tungsten structure.

Jan 1, 1964

By D. Harker, M. J. Murphy

The mechanism by which age-hardening takes .place is still not completely understood. The principal theories range from the extreme of "precipitaiion-hardening" to that of "order-hardening," with many intermediate gradations. In the hope of obtaining new data on which to base a choice among the many theories, the authors have made electron micrographs of formvar replicas taken from metallic specimens at various stages of age-hardening. The results so obtained on an alloy of 2 per cent beryllium in copper and one of 20 per cent molybdenum in iron will be described in the following pages, as well as the technique used in preparing the replicas. Preparation of Formvae. Replicas of Metallic Specimens This section is concerned with the techniques that have roved successful in preparing formvar replicas for studying the microstructure of metals with the electron microscope. Because of its simplicity and accuracy, the formvar replica1 method developed in the General Electric Research Laboratory has been used exclusively, since it is much simpler than the silica replica method of Heidenreich and Peck2 and produces as good results. The formvar method to be described requires a technique acquired only by practice, and no foolproof set of rules can be given. it is a rapid method and a replica can be obtained in less than five minutes under favorable conditions. This does not mean that perfect replicas can be produced every five minutes, but rather that one can well afford to take several strippings* in order to produce a replica of high quality. The metallographic technique required for replica work—very fine polishing and etching with very dilute solutions—is described here. It can be said, in general, that almost any surface that has been carefully prepared for a photomicrograph at 1000 or more diameters can be used to obtain a replica for the electron microscope. Preparation of Metallographic Specimens The preparation of the metallographic specimens is somewhat more exacting than that usually given to samples to be used for inspection under the light microscope. After much experimentation, it was concluded that the best method consists in polishing the metal through to the coarse cloth, then etching and repolishing on final cloth until the layer of distorted metal is removed. After this procedure has been completed, a dilute etch—to approximately the depth necessary for a micrograph at 1000 diameters—usually produces a sur-

Jan 1, 1945

By Prof. B. Hopkinson

Introduction.-A short time ago Professor Stoughton asked the writer if he would present a paper for the February meeting of our Institute. In reply to this suggestion, some notes have been prepared relating to the subject mentioned in the title. It is to be hoped they may be of interest to our members. The research now described is the joint work of Prof. B. Hopkinson, F. R. S., and the writer. Those interested in the subject will find further data in a paper entitled The Magnetic and Mechanical Properties of Manganese Steel, which will probably be read at this year&apos;s May Meeting of the Iron and Steel Institute in London. This paper was submitted to the Institute in October last, and advance copies will shortly be available. The present paper has been drawn up by the writer on this side the water, and he has not had time to communicate with Professor Hopkinson with regard to the statements or opinions expressed herein. While the writer believes that Professor Hopkinson would in the main agree with the statements herein set forth, it should be understood that apart from the actual work described he is not otherwise responsible. The experiments described have been carried out on the material known as manganese steel, which one of the writers of these notes discovered in 1883. A paper by him describing this material was read before this Institute in 1893, entitled Iron Alloys, with Special Reference to Manganese Steel. It is not necessary to describe manganese steel nowa-days; its qualities are so well known, and its use throughout the world is on a very extensive scale.

Jan 3, 1914

By E. E. Malouf

For centuries small amounts of copper have been recovered from acid mine-drainage waters. In recent years, the expansion of copper-bearing waste dump leaching for copper recovery has established a technological basis that is rapidly converting the art of copper leaching into a science. Copper leaching and recovery from solution has become an important adjunct of nearly all copper mining operations. Leaching of copper, whether from copper- bearing ore or waste, follows well established chemical reactions commonly in an acid circuit, but where leaching of copper is to be made in rock that is a high acid consumer, ammonia and ammonia carbonate, as well as cyanide leach solutions, can be used effectively. Current hydrometallurgical processes are being applied at an ever increasing rate to recover the trace amounts of copper in copper mine waste by in-place leaching. Currently approximately 300,000 tons of copper are produced annually in this manner while as recently as ten years ago, only one-eighth of this amount of precipitate copper was produced. Where copper occurs as an oxide in higher concentrations as to be classified as an ore rather than waste, then the hydrometallurgical processes are applied as percolation or agitation leaching in vats, pachuca tanks or prepared heaps. This approach gives better control over the recovery of the leach solutions, particularly in the processes where ammonia or cyanide leaching agents are to be used.

Jan 8, 1972

By P. G. Shewmon

A novel technique for determining the surface energy (?) and its derivative with respect to orientation, (?&apos;) is described. Essentially it involves the &apos;floating" of a wedge on the substrate, said wedge being made of a material which is not wet or only slightly wet by the substrate, i. e., as a greased needle "floats" on water. A thermodynamic analysis of a system in which the wedge is supported entirely by surface energy is given. If the original suyface is not at a cusp orientation, the surface tension is directly measurable from the groove angle formed. If the original surface is at a cusp orientation, there may or may not be a groove depending on the relative value of ?&apos; and the weight of the wedge. Experiments primarily on copper and silver showed that sapphire, quartz and refractory metal wedges were wet while graphite wedges were not. The technique was demonstrated to work using graphite wedges, but the results obtained were not as eccurate as those obtained by other workers using the wire-creep experiments. It is concluded that the technique might prove most useful with non-metals where ?&apos; is large and filament creep experiments would be quite difficult. If an absolute value of the surface free energy (?) of a metal is to be determined, the most reliable methods used to date measure an average over the various orientations exposed on a polycrystalline sample. For example, ? for silver, gold, and copper have been measured by determining the force required to just keep a thin wire,&apos; or foil,&apos; specimen from contracting under the influence of ?. Herring 3 has predicted and experiment confirms, that the sensitivity of this method is inversely proportional to the grain size.&apos; Thus it cannot be used to measure ? for a particular orientation by using a foil single crystal or a very coarse-grained specimen. An accurate value if ? for tungsten averaged over a range of orientations has been determined using a field emission technique. The same techniques cannot or have not been used to measure ? for non-metallic solids, and as a result the values available are much less accurate.4 This Paper resents a means of making an absolute determination of ? for a particular surface orientation on any solid, as long as the given surface orientation does not break up into other orientations during an anneal. Experimentally ? is found to vary with orientation and at a few low index orientations it is found to have a cusped minimum, i.e., the derivative of ? with respect to the orientation of the surface changes discontinuously at the low index orientation, see Fig. 1. The slope of a plot of ? vs orientation (herein designated ?&apos;) is called the torque on the surface, since it tends to rotate the exposed surface toward the low index orientation, or if the surface is at the cusp orientation it opposes any force tending to rotate the surface out of the low index orientation. The ratio ?&apos;/? has been determined for a few metals, but in cases where this ratio is high there is presently no means of determining either ?&apos;/? or the absolute value of ?&apos; for the orientations present on an annealed surface. The technique discussed herein also provides a means of determining an absolute value of ?&apos; for those orientations which deviate only infinitesimally from a cusp orientation. It should work best on surfaces where ?&apos;/? is large; that is, for cases where no other technique is available for measuring ?&apos;. Aside from trying to learn more about surfaces through measuring ? and ?&apos;, the primary reason for wanting values of ? or ?&apos; is to study adsorption. From measurements of the variation of ? for a particular orientation with the concentration of an impurity, one can obtain the number of impurity atoms adsorbed per unit area (Ti) on that orientation using the Gibbs adsorption equation.&apos; where µi is the chemical potential of the adsorbed impurity. Thus, if absolute values of ? could be obtained for the free surface of a given surface orientation as a function of µi, ri could be determined for the given orientation. Furthermore, by equilibrating a grain boundary with the given surface at various values of ki, one could also determine ri for the grain boundary. Similarly Robertson 6 has pointed out that if y is taken to be a continuous function of and µi, then a2 ?/a @a µ2 = a2 ?/a pi a +. Thus, at all orientations away from cusps the following equation holds From a measurement of ?&apos; vs ki, it is thus possible

Jan 1, 1963

THE problem of reaction rates in the open-hearth process is essentially that of trying to form a fairly clear picture of the "chemical mechanisms" in the bath. Quantitative data on reaction rates would not be very useful even if they were available; however, what few , approximate data there are, can be used in combination with data given in Chapters XVI and XVII to sketch a picture of the "chemical mechanics" of the open-hearth process that is consistent with essentially all the present available evidence. The result may later be found incorrect in many details but even so it will illustrate certain useful methods for obtaining a clearer understanding of the process. As discussed in the last portion of Chapter XIII chemical reactions in general involve the following factors: 1. The reacting molecules are mixed together in space in such fashion as to favor collisions among them. 2. A certain number of collisions occur per unit time among the reagent molecules, depending on their concentration and on temperature. 3. A certain percentage of these collisions result in reaction, these being the collisions between those molecules possessing at the moment energy levels above certain minimum values. The temperature factor enters mainly through (3), and its effect is very marked. (What is called temperature is really the mean energy content of all the molecules of the substance involved; at any one temperature a certain proportion of the molecules will have much higher energy content than the mean value.) Various reaction rates measured at around room temperatures have been found to be speeded from 1.6 to 4.0 times by an increase of only 15 to 20°F., simply because increasing temperature produces a rapidly increasing percentage of molecules with energy levels above the minimum needed to produce chemical reaction in a collision.

Jan 1, 1944