By Toshiyuki Kawai

Copper concentrate smelting directly in P-S converters was started at Onahama Smelter in 1983. Thereafter, the tonnage of concentrate smelted through the P-S converters increased, such that by 2002, it equaled the tonnage smelted through the reverberatory furnaces. In 2003, 56% of the total copper concentrates treated at Onahama Smelter were processed directly through the P-S converters. Technical improvements are reviewed and advantages of direct smelting in P-S converters are reported.

Jan 1, 2005

A sinter plant baghouse dust has been treated as a hazardous solid waste, and disposed at a very high price. A series of leaching tests were conducted to examine the possibility to produce high grade potassium chloride from the solid waste. It is found that around 40% of the solid wastes can dissolve into water, and a deposit with more than 90% KCl can be produced after simply drying the solution.

Jan 1, 2009

By Fanke Meng

Electrolyzing oxides of titanium, aluminum and niobium could prepare high-Nb bearing TiAl alloy (Ti-45Al-9Nb) at 1500°C. The chosen electrolysis voltage is 3.5V, which is lower than reducing voltage (~4.7V) of electrolyte CaF2, but higher than that of titanium, aluminum and niobium oxides. The investigation shows that compared with traditional methods, this method for preparing high-Nb bearing TiAl alloy is of many advantages such as few steps, friendly environment, low energy consumption, low cost and high current efficiency.

Jan 1, 2009

By K. Sarveswara Rao

"Any innovative approach made in non-ferrous metallurgical industry centers upon developing new processes, saving materials, improving production quality, and bornagain materials. Aqueous processing is commonly used to treat lean grade or more complex ore bodies. Its sustenance largely depends on energy and environmental compliance including water and wastewater management. The present paper focuses the importance of using particle size distribution and surface area measurements during ammoniacal dissolution of a Cu-Pb-Zn sulphide bulk concentrate and with an overview of the effect of water salinity on the process chemistry and residue mineralogy. Accordingly, an effort is made here to discuss the emerging perspective and highlight the recent successes and trends in terms of energy savings in non-ferrous hydrometallurgy.IntroductionThe nature and structure of the global energy industry is likely to change significantly in the 21st Century. Rabago et al [1] have comprehensively discussed how the mining and minerals industries can adapt to the challenges and opportunities posed by trends and drivers in global energy use. According to the authors, the drivers of sustainability include water, efficient energy use, climate modification, transportation technologies and energy security. Sustainability and competitiveness for the minerals industry will depend on natural capitalism, resource efficiency, new processes, saving materials, improving production quality, born-again materials and the solutions economy. Based on this motivation, the theme of the present paper is centered upon applications as relevant to energy and sustainable development in non-ferrous hydrometallurgy."

Jan 1, 2009

The mineralogy of the platinum group metals is fairly complex, and it is therefore not surprising that the different minerals have variable responses to metallurgical processes, in particular, flotation and leaching. The PLATSOL® leach process was developed to extract simultaneously base metals, gold and platinum group metals from various materials. Extensive research has indicated that most PGM?s were amenable to the PLATSOL process, with the notable exception of cooperite PtS. Further work showed that a thermal pretreatment at 500-700ºC transformed the structure of the cooperite and similar refractory minerals (Pt,Pd)S into Pt metal and Pt-Pd alloys that responded well to the PLATSOL® process. Examples are presented of the mineralogy of PGM concentrates as produced, in the residue from the PLATSOL® leach and after thermal pretreatment.

Jan 1, 2006

By Scott A. Shuey

Keywords: E-Waste, Pyrometallurgy Many might think addressing the issue of e-waste is a new area of study. Electronics disposal has been discussed in some circles for at least the past 25 years. The recycling of electronic waste (e-waste) tends to be a rather complex undertaking when considering the intimate bonding of materials in the average printed circuit board. The development of a recycling process is further complicated when considering the wide variety of products being generated under the heading of ?electronics.? Focusing only on the primary constituents (polymers, Cu, Al, Fe, etc.) tends to lead one to fairly simple flowsheets. Ignoring trace elements, and the various halide species generated, will lead process engineers down a development path that is sure to cause material handling issues. Researchers at Colorado School of Mines are modeling the complex chemistry that exists within the body of e-waste?comprising 39 of the known elements. An understanding of the systems thermodynamic behavior will result in the development of a more robust, long-term process for the recovery of valuable materials from the e-waste stream.

Jan 1, 2005

By J. S. Becker

Technology developed and first implemented in the United Kingdom enables very low grade aluminum scraps containing oils, organics, plastics and ferrous metals to be directly charged, without pretreatment, into a unique melting furnace. The system has been in full scale production for four years. The oxy-fuel-based furnace design incorporates internal afterburning in the furnace's hot zone, producing excellent thermal efficiency and very low emissions. The furnace is inherently low in NOx. This paper will provide both theoretical background and extensive operating results for this new melting concept. Applications describing both purpose built new furnaces and retrofits of existing reverberatory furnaces will be presented. Extensive operating emissions data will be presented.

Jan 1, 1997

By Kwong. Kyei-Sing

Gasification is a process that converts a carbon feedstock into synthesis gas (CO+H2). Slagging gasifiers operate at high temperature and pressure and in a corrosive-wear environment from the slag. Cr2O3-based refractory linings are used to protect the steel vessel that comprises the gasifier from the aggressive gasification environment. Increasing service life of the gasifier is one of the keys for wide spread development of this technology. In support of the goals, research on the gasifier atmosphere, the slag chemistry, the interaction of Cr2O3 refractory with different feedstock mixtures (e.g., coal and petcoke) were characterized by post mortem analysis of bricks from service in gasifiers and thermodynamics simulation of the environment. Examples demonstrating how thermodynamic calculations can explain the post mortem results and make predictions of material interactions will be given. Attention is placed on the possibility of Cr+6 in different feedstock mixtures and operating conditions.

Jan 1, 2010

By M. E. Huckman

In this paper, we review the equations needed to construct an ion exchange column model. These models contain three major components: 1) a differential material balance around the colunm, 2) a differential material balance around an ion exchange particle, and 3) a constitutive equation for diffusive flux We then examine the ability of a fairly simple mathematical model to predict ion exchange column experimental data. This model contains the traditional absorption theory equations and is used to predict the behavior of a column filled with a hydrous crystalline silico-titanate and which is removing trace amounts of Cs+ from a high pH, complex electrolyte solution. Finally, we propose replacing Fick's law with the Nernst-Planck equation as the constitutive equation for diffusive flux We use a Nernst-Planck type model to predict batch experimental data, then evaluate it by comparing it's ability to predict experimental data to that of a more traditional Fick's law type model? The data from this comparison suggests that the Nemst-Planck type model yields better results.

Jan 1, 1996

By P. Rooney

In due course, new smelters will have to be installed in order to meet the increasing worldwide demand for copper. This paper presents the results of a study made for the purpose of identifying the most desirable countries in the world in which to locate a new smelter. Both sociopolitical and economic factors were taken into account. Criteria developed and methods used to assess each possible location are described. The study indicated that the most interesting potential locations are Canada, -Chile, Portugal and the USA for new copper smelting complexes.

Jan 1, 1983

By Omid Lashkari

Keywords: SEED, SSM materials, Microstructural evolution, Rheology, Swirling Speed SEED (Swirled Enthalpy Equilibration Device) is established itself as a new technology amongst the many Semi-Solid Metal (SSM) processes, where swirling of the mush plays an important role in modifying the dendritic structure of as-cast parts. A range of semi solid metal structures, dendritic, rosette and/or globular morphology of primary phase, can be prepared using SEED. The current article reports on the application of rheological tests in characterizing microstructural evolution during SSM processing of 356 Al-Si foundry alloy. A simple parallel plate test machine, designed and constructed at our labs, was used to determine viscosity values for each structure and identify the optimum structure with superior die filling characteristics. Such findings have important technological and economical implications during high pressure die casting of semi- solid metals. The strain-time graphs for 356 Al-Si foundry alloy indicated lower viscosity values for globular microstructure, i.e. improved die filling.

Jan 1, 2005

By Clara María Lamus Molina

The following minerals found in the residual black sands from gold mining in El Bagre Antioquia (Colombia) were identified as having major economic interest: Ilmenite (FeTiO3), with an average of 49% of TiO2, frequently altered presenting crowns; lamellaes of rutile and alteration textures; titanomagnetite with up to 25% of TiO2; magnetite (Fe3O4) in individual grains or associated with others minerals as hematite and ferromagnesian silicates rutile (TiO2) with considerable quantities of Nb2O5(0.1-3.7%Wt); zircon (ZrSiO4) with 66%Wt of ZrO2 and monazite with an average of 63.43%Wt of REE, this frequently associated to xenotime and thorite forming textures as little drops. Analysis in EPMA and SEM/EDS showed percentages of minor elements and traces, thereby clearly establishing the applications of these minerals in diverse industries. Furthermore, a detailed granumetric study of the different minerals and textural relationships among them also allowed for establishing the basis for possible processing and exploitation.

Jan 1, 2006

By Regina Maria Pinheiro

This work has for objectives to characterize a waste generated in the form of sludge during the treatment of the effluent of a paper making industry and to evaluate the effect of its incorporation in the amount of 10 wt.% on the properties and microstructure of a clayey body used for brick production. For the characterization of the waste the following techniques were used: X-ray diffraction, X-ray fluorescence, differential thermal analysis and termogravimetric analysis. Incorporated bricks were produced in industrial scale before firing at 750°C in a Modified Caieira type furnace. The physical and mechanical properties evaluated were water absorption and compression strength. The microstructure of the fired ceramic was evaluated by optical microscopy. The environmental evaluation was made by solution test and atmospheric emission by monitoring the release of SO2, NOx and particulate material. The results showed that, in agreement with the characteristics of the waste, its recycling into red ceramic can contribute to decrease the consumption of fuel during the firing stage. The properties of the fired ceramic attend the norms. With respect to the environmental aspect, the incorporation of the waste did not impact the environment.

Jan 1, 2009

By Akihide Hosokawa

The void growth and coalescence in model materials involving a pre-existing three dimensional void array (i.e. multiple layers of a void array) was studied by X-ray computed tomography (XCT) coupled with in situ tensile deformation. To reduce the recording time, a new technique called fast tomography was employed. The model materials used in this paper were fabricated by the combination of an ultra-short pulsed laser machining system and a diffusion bonding technique, and two different types of arrays were prepared namely, FCC 1 and FCC 2 type array. This methodology allowed the authors to capture the entire process of growth and coalescence events of a void array embedded in the metal matrix. The failures in the both materials involved internal necking and shear localization. One of the highlights of this paper is that the plastic strain at the onset of void coalescence was measured for each model material. These values are in fact the adequate values to be compared with the coalescence strain predicted by existing void coalescence models such as the Brown and Embury model, the Thomason model and the Pardoen and Hutchinson model. The comparison suggested that the Brown and Embury model underestimated the coalescence in neither of the current model materials, while the Thomason model and the Pardoen and Hutchinson model showed a quite good agreement with the result for FCC 1 material. On the other hand the result from FCC 2 material agreed with none of the models probably due to the geometry of the void array that is not compatible with the existing models.

Jan 1, 2010

By Sebastiaan Peelman

NdFeB permanent magnets are the best available magnets used in many technology applications. However, at their end-of-life (EoL) most of magnets and the contained REEs are lost during the recycling of the bulk metals. The REEs are classified as the most critical raw materials in the European Union, and recycling of REEs from EoL products will reduce their criticality and contribute to the sustainability of REE. Various technological routes have been reported, but most of the methods are effective for highly concentrated magnets or magnet scrap, which is greatly dependent on expensive pre-dismantling processes. This paper presents various innovative metallurgical solutions to the effective REE recovery from current industrial practice for WEEE recycling, including the ferrous scrap from WEEE shredder products and shredder residues from computer hard disk drives. Both hydrometallurgical and combined hydro- and pyrometallurgical REE recovery routes are developed after demagnetization and physical upgrading.

By Pinai Mungsantisuk

Keywords: Pd-Ni alloys, Pd-Fe alloys, Pd-Co alloys, Magnetostriction, Magnetic Properties The presence of congruent melting minima, the occurrence of ferromagnetic transition over a large composition range, and FCC type crystal structure make Pd-Ni, Pd-Co, and Pd-Fe based systems attractive candidates in our search for materials with no rare-earths, large low-field magnetostriction, and good mechanical properties. The presence of paramagnetic-ferromagnetic transition over a broad range of composition also provides opportunity for fundamental studies. In this work, we have examined the magnetic and magnetostrictive behavior of Pd-Ni, Pd-Co, and Pd-Fe alloys over the entire composition range. Alloy sample rods were prepared by arc melting and casting. X-ray diffractometer was used to obtain lattice parameter data. Magnetostriction was measured along the rod axis using strain gages. Magnetic properties were measured using a vibrating sample magnetometer.

Jan 1, 2005

By Art Cooper

Granulation systems are customarily viewed as problem areas in metallurgical operations. The inherent risk of explosion when combining a high temperature melt with water creates a safety hazard. Separation of the granulated material from the quenching medium generally involves equipment that can have significant maintenance and operating costs. Granulation systems' reliability and availability can negatively affect the plant production. Against this background, granulation systems have been treated by design firms and producers as an add-on and a necessary evil. The technology is becoming better understood and solutions to common problems are being found. This paper will discuss typical problems in common systems, and some of the improvements that have been made, with particular reference to non-ferrous applications.

Jan 1, 2006

By Hui Lu

The structural changes in solutionized AA2618 during natural aging and their effects on subsequent artificial aging were investigated by hardness measurements, X-ray diffraction, differential scanning calorimetry and transmission electron microscopy. The changes in lattice parameter and hardness during natural aging indicate that copper-enriched clusters form in the earliest stage, followed by the formation of magnesium-enriched clusters and coppermagnesium co-clusters. Prior natural aging consistently weakened the hardening during subsequent artificial aging at 180, 200 and 230 °C but had no effects on artificial aging at 150 °C. The decreased age hardening was attributed to the reversion of small clusters/zones that formed during prior natural aging. The lattice parameter exhibited erratic changes with increasing artificial aging time, reflecting the complex sequence of the reversion and precipitation.

Jan 1, 2006

By SM Rao

Nuclear Fuel Complex (NFC ) , Hyderabad (IN DIA ) , is engaged in the manufacture of nuclear fuel assemblies and zircaloy structural components required for the Indian nuclear power reactors. The production of zirconium oxide, sponge and zircaloy materials through chemical and hydro - metallurgical processes generates many effluents containing valuable zirconium and hafnium . This paper deals with the various processes such as multiple crystalization, phosphate precipitation, ion-exchanges amine solvent extraction etc, for the treatment of these effluents and subsequent recovery of valuable zirconium and hafnium .

Jan 1, 1992

By Henry Hu

In high pressure die casting processes, proper control of temperature die yields a high casting production rate and superior quality components, Die temperature is usually influenced by various die design and process parameters such as size and location of intemal water cooling lines, flow rates of cooling lines, and pouring temperature of molten metal. Among them, the cooling water flow rate plays a major role in controlling thermal pattern of the die_ In order to develop an effective control strategy, data of local die temperature must be collected and analyzed, In this study, a PC-based data acquisition and control system (DACS) for die temperature control has been designed, and established, The developed DACS has three input channels for temperature signals and one input channel for water flow rate signals, as well as one output channel for a water pump, and is capable of displaying data in both curve format and value format. Implementation of the DACS in a laboratory setup has also been attempted, It should be pointed out that more advanced control mechanisms can be potentially integrated into this system in future,

Jan 1, 2003