By Helmut Antrekowitsch

Nowadays nearly the half of the world zinc production is used for galvanizing. After their life span most of the galvanized products return as scrap to the steel mill During the steel process the zinc is collected in the flue dust It is astonishing to notice that between 40 and 50 % of the zinc produced is brought into the steel processing cycle by the coated scrap while only 3 to 5 % of the zinc production can be covered by the recycling of the zinc-bearing steel mill dusts. Responsible for this worse ratio is the fact that the established recycling technologies suffer from high energy consumption, low zinc yields, halogen problems and hardly any iron recovery. A development of new or an optimization of current recycling procedures for the dusts is unalterable because of increasing zinc amounts in these residues and the rising costs for the disposal. Different pyrometallurgical recycling technologies are tested in rotary kilns and vertical retorts at the Department of Nonferrous Metallurgy, University of Leoben, Austria. Various reducing agents from carbon monoxide to hydrogen and combinations are used. The results should make it possible to draw conclusions that allow an economical and ecological judgement of the different varieties. The goal is to support the affected industry to increase the low recycling rate and prevent a loss of high zinc values in the steel industry filter dusts.

Jan 1, 2003

By Helmut Antrekowitsch

Nowadays nearly the half of the world zinc production is used for galvanizing. After their life span most of the galvanized products return as scrap to the steel mill. During the steel process the zinc is collected in the flue dust It is astonishing to notice that between 40 and 50 % of the zinc produced is brought into the steel processing cycle by the coated scrap while only 3 to 5 % of the zinc production can be covered by the recycling of the zinc-bearing steel mill dusts. Responsible for this worse ratio is the fact that the established recycling technologies suffer from high energy consumption, low zinc yields, halogen problems and hardly any iron recovery. A development of new or an optimization of current recycling procedures for the dusts is unalterable because of increasing zinc amounts in these residues and the rising costs for the disposal. Different pyrometallurgical recycling technologies are tested in rotary kilns and vertical retorts at the Department of Nonferrous Metallurgy, University of Leoben, Austria. Various reducing agents from carbon monoxide to hydrogen and combinations are used. The results should make it possible to draw conclusions that allow an economical and ecological judgement of the different varieties. The goal is to support the affected industry to increase the low recycling rate and prevent a loss of high zinc values in the steel industry filter dusts.

Jan 1, 2003

By R. W. Harnmack

Hydrogen sulfide generated by the anaerobic respiration of sulfate-reducing bacteria was used to treat pH 2.2 water from the abandoned Rio Tinto copper mine in Nevada. The untreated water contained 550 mg/L Fe, 140 mg/L Al, 90 mg/L Cu, 80 mg/L Mn, 60 mg/L Zn, 4 mg/L Co, and 2 mg/L Ni. The bench-scale treatment system examined consisted of a bioreactor for H2S generation and three precipitator/clarifier units for metal sulfide precipitation and recovery. The treatment system reduced the concentrations of all metals except Mn to less than 0.1 mg/L. Manganese concentrations were reduced by 96 percent to 3.3 mg/L. A CUS/SO concentrate (33 pct Cu) and a ZnS/5° concentrate (28 pct Zn) were produced that may be suitable for metal recovery at existing smelters

Jan 1, 1994

By Anne Kvithydl

Printed circuited boards contain considerable quantities of valuable metal, while also containing many environmental pollutants making them unsuitable for landfill. In this study the decomposition of common plastics used in printed circuit boards were studied. Polytetrafluoroethylene (PTFE), polyvinyl chloride (PVC) and polyethylene (PE) were heated in both CO, and argon atmospheres using a thermo-gravimetric furnace (TG) coupled to a mass spectrometer (MS). Soda ash Na,C03 and baking soda NaHC03 were used as reactants. The degradation temperatures and evolved gases are presented for single plastics and mixtures. Mixed plastics are shown to behave as a sum of the individual plastics. The mass loss temperature is the same in CO, and argon. However, less residue is formed when heated in CO,.

Jan 1, 2008

The paper describes the propensity of tin to form intermetallic compounds with microalloying elements such as Nb, Ti and aluminium, which are commonly used as additions to achieve particular combination of strength and toughness. Two series of alloys were prepared by arc melting under an argon atmosphere. Each series was based on Fe, Sn and A1 with either Nb or Ti additions. The microstructures were studied using scanning electron microscopy, transmission electron microscopy, energy dispersive X-ray spectroscopy and microprobe analysis. It was found that the level of Nb addition has an effect on the formation of Sn-rich compounds. For small Nb additions, no Sn containing compounds were found, whereas in higher Nb alloy, a Laves phase (FezNb, hexagonal, a = 0.4830 nm and c = 0.7879 nm) containing about 1 at % Sn was found. A FezNb3 phase (cubic, a = 1.1261 nm) associated with the formation of alumina was also found but did not contain tin. No Sn containing compounds were found with Ti additions. The experimental observations have been compared with thermodynamic calculations performed using MTDATA.

Jan 1, 1999

By Garg. D.

Premixed bronze powders are widely used to produce a wide variety of P/M components including bearings and bushings by the powder metal industry. The physical and mechanical properties of sintered bronze components such as dimensions, strength, microstructural characteristics, and sintered density are well known to change with sinlering furnace design, particle size distribution in powders, green density, preheating and sinlering time" and temperature, and protective atmosphere flow rate. " However, not much is known about the effect of protective atmosphere composition on physical and mechanical properties of sintered bronze components; This paper describes effects of protective atmosphere composition and sintering temperature on physical and mechanical properties of sintered bronze components

Jan 1, 1996

By Edmundo Manilla, Merete Tangstad, Daniel Davila, Eli Ringdalen

FeMn alloys are typically produced with lumpy ore or sinters. Minara Autlan, the Mexican FeMn producer, is however making Mn-nodules as a raw material for Mn-alloy production. The Mn nodules have been characterized by XRF, XRD, by wet chemical methods and by EPMA. The Mn/Fe ratio is somewhat lower compared to commercial Mn ore on the marked. The basicity of the ore is however close to 1, and additional fluxes may not be used. The Mn-nodules will be in a state of manganosite (MnO), tephroite ((Mn, Ca)2SiO4) and galaxite ((Mn,Mg)Al2O4). This leads to a low melting temperature area. A low porosity and low amount of higher Mn-oxides gives a high thermal strength to the nodules.

Jan 1, 2016

By J. W. Matousek

Cobalt behavior in pyrometallurgical processes is traditionally analyzed using slaglmatte distribution coefficients as functions of matte grades or matte iron contents. L(s/m) = (%Co) I [%Co] = f [%CuNi] or f [%Fe] The method is inconvenient to use in predictive mass balance work because of the interdependence of assays and mass quantities. An alternative procedure is proposed based on cobaltliron ratios for slags and mattes: Js = (%Co) / (%Fe), Jm = [%Co] / [%Fe], and J, = b + m [Jm]

Jan 1, 1993

By Valery Kaplan

Sulfur emission in the form of SO2 in flue gases is one of the most serious atmospheric pollutants associated with coal combustion and non-ferrous metals production. The carbonate eutectic method for removing SO2 from flue gases at 723–923 K was initially proposed in the 1970s but despite its great efficiency (SO2 concentration in the flue gas after purification reached 0.003 volume %), it could not be implemented by industry due to the complexity of the carbonate melt regeneration stage. Earlier we proposed a method suited to coal-firing power stations where the melt was regenerated using CO as a reducing agent. However, most metallurgical plants do not use coal and therefore lack a large source of CO. Here we propose a method for removing sulfur from the carbonate eutectic melt by purging it with natural gas or a natural gas/air mixture, which are available in the vast majority of metallurgical plants. This reaction leads to the reduction of sulfate to H2S gas that leaves the melt. The experiments we conducted show that nearly complete sulfur removal from the melt is possible at 823 K and that the reaction rate is sufficiently high for a large scale process. One can foresee that this carbonate melt-based SO2 removal technique may become a practical and economically attractive method for limiting sulfur emission to the atmosphere from non-ferrous metallurgical processing plants.

By Steven R. Izatt

IBC Advanced Technologies, Inc. (IBC) has developed a mercury selective product, which can be used by sulfuric acid producers as either a polisher, or as the primary technology for mercury removal from sulfuric acid. The Molecular Recognition Technology (MRT) separations material selectively binds Hg2+, and to a lesser extent Hg+, out of concentrated sulfuric acid. Mercury output levels of less than 0.1 ppm can be attained by the MRT system. Pilot plant tests have been successfully conducted at base metal smelting operations. A large-scale commercial plant is due for commissioning in 2003. Results from these projects will be discussed.

Jan 1, 2003

By Elliot Schwartz, Julian Szekely

"In this paper we describe an experiment that was recently performed on the IML-2 Space Shuttle mission in which the thermophysical properties of molten metals were measured using electromagnetic levitation. In the planning of these experiments calculations had to be performed to predict the levitation and stirring forces, heating rates, sample deformation, and internal flows within the sample. These predictive calculations were essential for both the planning of the experiments and for the re-planning of experimental runs during the actual Space Shuttle mission.Introduction""Materials Processing in the Computer Age"" involves the use of mathematical modeling to obtain a quantitative understanding of the phenomena that govern materials processing operations. Microgravity, or space shuttle experimentation represents a specific case in point here; the very high cost of the space shuttle flights, the very limited flight opportunities that are available, and the tight resources aboard a shuttle clearly mandate that these experiments be very precisely planned and that all possible opportunities for mathematical modeling be fully exploited.The purpose of this paper is to present the results of calculations performed for the planning of a space shuttle experiment involving electromagnetic levitation and wherever possible present a comparison of the computational predictions with both experimental measurements and asymptotic analyses. Finally we shall seek to discuss the practical implications of both the computational methodologies and the potential experimental findings."

Jan 1, 1994

By lonkion M. Font

Due to the known disadvantages of the use of iron silicate slag in the nickel converting stage, i.e., high metal losses, high magnetite content, and low fixation of impurities in the slag, the development of the new proposed "ferrous calcium silicate slag" for smelting and converting processes of nickel is very promising. Hence, considering the successful experimental results of using CaO base slag for the nickel smelting process, a study based on a detailed comparison for the phase equilibrium, and the minor elements distribution between the NilS2-FeS matte with either FeOx-CaO or FeOx-Si02 base slag was investigated. The main results are summarized as: no difference in the nickel losses between both slags was found at high nickel content in the matte, and the fractional distribution analysis for arsenic and antimony pointed out their preferential fixation in the calcium ferrite slag rather than in the iron silicate slag. Considering the energy and pollution issues, the technical feasibility of using calcium ferrite slag in a converting process of the Bessemer matte will have a prominent future for the nickel industry.

Jan 1, 2003

By Jacques Magnaudet, Julie Cranga, Didier Huin, Pascal Gardin

"With the aim of controlling steel grade in steelmaking reactors, IRSID and IMFT are developing a numerical description of the evolution of bubbles in the vicinity of a liquid steel/ slag interface. The objective is to identify the main parameters affecting the hydrodynamics of the various phases. The goals of the present paper are:• To describe the numerical technique developed to predict the multi phase flow including bubbles, liquid metal and slag layer.• To analyze the influence of the absolute pressure on the bursting of bubbles in a RH degasser. Validation is given by comparison with results available in the literature. The major point concerns the distinct behaviors observed whether the pressure is low or high.• To study the influence of the properties of the slag layer (thickness, viscosity and interfacial tension) on the entrainment of liquid metal in the wake of the bubble and on the nature of the projections from the bath surface.IntroductionMost of secondary steelmaking processes use gas stirring for homogenization, removal of nonmetallic inclusions or decarburization under reduced pressure. The bursting of gas bubbles at the metal or slag layer surface produces a beneficial ejection of metal droplets in the low pressure atmosphere, provided that there is no violent projection, which may have detrimental effects on the process.Our objective is to develop a numerical tool to study the phenomena occurring in the vicinity of the bath surface, in particular bubble bursting under reduced pressure and entrainment of metal in the slag layer. In this paper we report the first conclusions of our study. In the first section we describe the numerical model used to describe the three-phase flow and the expansion of the gas bubbles under the effect of the ferrostatic pressure. The second section is devoted to the study of pressure effects on bubble rise and bursting. The third section reports some computational results about the rise of a gas bubble through the interface between the two liquids."

Jan 1, 2001

By Bradford H. Miller

Separation and Recovery Systems, Inc. (SRS) provides on-site waste minimization and resource recovery using its state-of-the-art MX-1500 centrifuge and MX-2000 thermal desorber. The MX-1500 can process over 450 feed tons of material per day, resulting in centrifuged cake containing 20% to 60% by weight. The MX-2000 is a hollow-flite thermal processor indirectly heated by either steam or hot oil. SRS has dewatered and/or deoiled over 1,000,000 feed tons of material in the refining, chemical, and energy industries using the MX-1500. SRS estimates that over 300,000 barrels of reusable oil have been recovered from that material. Additionally, SRS has dried and/or detoxified over 150,000 wet tons of solids or soil to regulatory or customer-specified limits using the MX-2000.

Jan 1, 1994

By M. Drozd

Multi-use pad operators require an efficient and economic method to destroy cyanide in their process residues so new material can be stored on the pad and leached. Operators of the dedicated or single-use pads require an effective cyanide destruction method for pad closure. Cyanide destruction can be accomplished by utilizing oxidants such as hydrogen peroxide or calcium hypochlorite, or by utilizing ferrous sulfate which sequesters the cyanide in strong acid dissociable complex. Ferrous sulfate can be the preferred method of cyanide destruction because it is a less costly chemical, reaction rates are almost immediate and unlike oxidants, it can penetrate the total depth of a pile without being destroyed by side reactions. Literature indicates that the (Fe(CN)6)-4 com~lex is produced slowly but it appears that complexes such as Fe(CN)4(H20)2-or Fe(CN)4(OH)2)-4, are formed quickly and should have no U.V. sensitifity, unlike (Fe(CN)6)-4. Stoichiometry of the testwork indicates that Fe«CN)4(OH)2)-4 complex may be the species formed. The usage of ferrous sulfate has the advantage of being able to bring ~ level down that divalent metal ions such as Cu++, Cd++, Hg++, Pb++ and Zn will form insoluble complexes and precipitate from solutions does not destroy weak acid dissolvable complexes and can leave a heavy metal problem behind after cyanide destruction.

Jan 1, 1990

By T. C. Goel, A. Venna, R. G. Mendiratta

"Processing of ferrites has gained tremendous importance in recent times to meet the high performance demands on ferrites in keeping with the fast emerging· technologies. The quality of ferrite powders has strong influence on ·the performance of final device. Fabrication· of high performing ferrite components requires starting ferrite powders of precise stoichiometry, purity and microstructure. It is difficult to obtain these attributes by the conventional ceramic method. The key to obtaining quality powders lies in the· solution techniques. With this in view soft ferrites have been prepared by a wet chemical process, known as the citrate precursor method, which involves the formation of citrate complexes of the constituent cations. The advantages of this process are the ease of preparation and close control of composition, homogeneity, purity and particle size. Electrical and magnetic measurements on lithium ferrites have shown resistivity higher by more than two orders of magnitude compared to that observed for samples prepared by the conventional ceramic method, and low magnetic losses, making the ferrites specially suitable for high frequency applications.IntroductionProperties of ferrites are known to be sensitive to .their processing technique. A small deviation in the compositional stoichiometry of the ferrite affects its properties greatly. Soft ferrites such as Ni-Zn, Mn-Zn and Mg-Mn. are well known ferrites covering wide-ranging applications [1,2]. Lithiiim ferrites have also assumed technological importance for microwave applications and are potential substitutes for the expensive garnets [3]. Lithium ferrites are often doped with zinc to tailor the saturation magnetization required at high frequencies. Lithium and lithium-zinc ferrites, however, present difficulty to processing due to the volatile nature of both the cation components, namely Li and Zn. These ions are volatile at temperatures > 1000°C which makes their processing difficult. One of the main considerations of high frequency performance of ferrites is the high eddy current losses which prevent the interaction of the magnetic field with the ferrite component and hence impair device performance. These losses can be reduced by having a material of high resistivity. Electrical conductivity in lithium ferrite has been attributed to electron hopping [4] between the two vaience states of iron, Fe2+ <=> Fe3+, on octahedral sites. Maintaining the + 3 valence state of otahedral- Fe ions is thus a prerequisite for achieving high resistivity. The resistivity of ferrites is normally found to be low when processed by the conventional solid-state or the ceramic method [5]. This is attributed to (a) extensive ball-milling employed in the method to mix the component oxides results in non-stoichiometric compositions due to introduction of additional Fe ions on abrasion of steel balls during milling, (b) high processing temperatures involved which result in significant volatilization of Li and Zn ions creating thereby oxygen non-stoichiometry which results in reduction of Fe3 + to Fe2 +, (c) large and non-uniform grain sizes. In the present work, preparation of Li and Li-Zn ferrites by a non-conventional method known as a citrate precursor method [6, 7] which requires lower processing temperatures and duration is reported. The method gives stoichiometric compositions on account of homogeneous atomic-scale mixing of the constituent cations via the formation of metal-citrate complexes mixed in solution state. The method is also capable of giving small grain size which aids the oxidation ofFe2+ ions."

Jan 1, 2000

By Xin-liang Gao, Qing Li, Gui-qin Fu, Duo Jin, Miao-yong Zhu

"Optical microscope together with alternative wet-dry cyclic accelerated corrosion tests and XRD, SEM were employed on bridge weathering steel samples with different Mn and Ni contents which were vacuum induction melted and rolled to study their effects on the microstructure and rust layer evolution in er' containing condition. The results show that the microstructure is mainly ferrite and pearlite when Mn and Ni contents are 0.75 %, 0.42 %, respectively. Both the increase of Mn and Ni contents will make pearlite disappear while granular bainite appear, meanwhile the grain size decreases. With the increase of Mn content, the corrosion rate decreases in the initial stage, but the effect becomes little in the later stage. The increase of Ni not only improves the corrosion resistance of steel base at the initial stage but also hinders the tendency of further corrosion. As Mn content increases, a-FeOOH contents in rust layer decreases. With increase of Ni content, the content of a-FeOOH in the rust increases while that ofy-FeOOH decreases.IntroductionWeathering steels had been ~radually applied in manufacture of bridges owing to reducing the corrosion rate remarkably [I- l .Good weldability was needed for high performance bridge weathering steels. Since carbon was thought to be bad for weldability, low carbon content steel was adopted and Mn was added to amend the mechanical strength loss. Some scholars[6, 7l believed that Mn was beneficial for increasing corrosion resistance performance of the steel in marine atmospheric environment. Some scholars [S, 9l thought that Mn had little effect on corrosion resistance in marine atmospheric environment. Presently, the effect of Mn on bridge weathering steel in marine atmospheric environment still remained poorly understood. Ni was considered to be beneficial for increasing corrosion resistance performance in marine atmospheric environment [JO-l4l However, the high cost limited its application range. What would bring to the rust and corrosion by decreasing Ni content needed further research.Most researchers assumed that microstructures only affected the corrosion behavior of bare steel. But the study of Guo et al. P5l showed that the homogenous microstructures were beneficial for the corrosion resistance of steels. The effect of Mn, Ni content change on microstructure and microstructure on corrosion still remained poorly understood. In the present work, the effect of Mn and Ni on the microstructures of steel matrix, as well as the microstructures on the rust and corrosion was investigated."

Jan 1, 2014

By S. N. Ojha, Gouthama, R. K. Mandal

"Spray deposition processing of liquid immiscible alloys, based on AI-Pb and Cu-Pb systems have been investigated. Process variables have been optimized to generate uniform dispersion of ultrafine second phase particles in· the matrix of the primary phase. Mechanisms governing the microstructural evolution in this synthesis methodology are discussed. Results of the present investigation are used to demonstrate that rapid solidification of atomized droplets initially provides a high nucleation rate of the second phase during the liquid phase separation. The solid matrix phase nucleates at a later stage and grows with a high velocity enabling trapping of the dispersed phase. Subsequent alteration in the size and size distribution of the second phase is suggested to arise further during deposition of high velocity droplets. Possible reasons for this effect are brought out. Microstructural features of atomized powders and spray-deposits of these alloys are presented to support the present approach of synthesizing composites. IntroductionIn recent years, synthesis of advanced materials with metastable microstructures and ultra fine dispersion of second phase particles has led to the development of novel techniques of materials processing. The other requirement of such a processing methodology is to achieve near-net shape geometries in less number of processing steps. The solidification processing method via spray deposition route qualifies these criteria. This process primarily involves atomization of a melt by high energy gas jets into spray of droplets which are subsequently propelled by the kinetic energy of the gas towards a deposition substrate to build-up a thick high density preform. Although the concept of spray deposition was pioneered by Singer [1] in the early seventies, the fundamentals of the deposition process has been understood only recently [2-4]. Several benefits of spray deposition processing are by now well established [5,6]. Rapid solidification effects are inherent in spray deposition processing due to high heat exchange rate at the droplet-gas interface and also on the deposition surface by force convection. Since considerable heat extraction occurs from the atomized spray prior to droplet consolidation, a relatively low processing temperature is ensured in this process. As a result deleterious coarsening phenomenon can be minimized. In addition, controlled maneuvering of the substrate provides the capability of the process in producing disc, sheet or tube shape preforms of difficult to work materials in a single operation. A significant improvement in properties, resulting from microstructural homogeneity and refinement in grain size induced by spray deposition has been reported for several alloy systems [7,8]."

Jan 1, 1994

By M. M. Kim

As-electrogalvanized coatings of pure Zn, Zn-11% Fe, and Zn-18% Fe coatings were characterized in terms of initial crystal structure and surface morphology. Samples were then subjected to heat treatments simulating the paint bake cycle of automobile manufacturers. Surface morphology changes were correlated with the process variables, and crystallo.graphic changes were interpreted by mapping heat treatment routes on the Fe-Zn phase diagram. The morphology of pure zinc electrogalvanized coatings with heat treatment from platelets to smeared platelets. The zn-11% Fe coating changes with heat treatment from tetrahedral nodules to a mixture of round and tetrahedral nodules, with the Zn-:18% Fe coating always having round nodules. Regarding crystal structure, a critical transformation time can be defined at any selected temperature, below which the crystal structure does not change. This temperature is related to iron content.

Jan 1, 1990

By K. Tozwa

The electrical conductivity of electrolytes for copper electrorefining and electrowinning processes has been reported by many researchers since 1911. The experimental results show that the conductivity increases with an increase in sulfuric acid concentration and decreascs with an increase in copper concentration. In pure copper sulfate solution, however, the conductivity increases with an increase in the copper concentration. After confirming the conductivity of pure and acidified copper sulfate solutions experimentally, the concentrations of hydrogen ion and free (not hydrated) water in the electrolytes were estimated and it was found that the relation between the conductivity of acidified copper sulfate electrolytes and the products of concentration of hydrogen ion and free water is linear. Accordingly, the conductivity of acidified copper sulfate electrolytes increases with an increase in sulfuric acid concentration and decreases with an increase in copper concentration.

Jan 1, 2003