By Zhang Yongzhu

Developments on bioleaching of low grade ores and refractory gold ores by T. Ferrooxidans in China are summarized. Effect of the ions on bacterial growth, bioelectrochemical reaction mechanism of sulfide minerals and bacterial reaction mechanism are also discussed.

Jan 1, 1992

By Jing Zhan

The fibrous precursor can be obtained by coordination precipitation process, using oxalate, cobalt chloride and ammonia. The composition and morphology of fibrous precursor were characterized by XRD, IR, DTA/TGA and SEM analysis. The results show that XRD pattern and composition of the precursor with fibrous morphology precipitated at pH=9.0 were different from that of ß-CoC2O4?2H2O precipitated at pH=1.0. The mechanism on the thermal decomposition of fibrous precursor was addressed. The influences of various conditions in pyrolysis, including the temperature, time, atmosphere, and the morphology of the precursor, on the morphology, average size and specific surface area of the Co powders were investigated in detailed. At last, the final product, fibrous cobalt powders with diameter about 0.3~0.5µm in size and 40~60 in aspect ratio, were produced by thermal decomposition at 400~500? in the weak reducing atmosphere. The structure of pores in cobalt powders was capillary tube with open ports and the majority was mesoporous.

Jan 1, 2009

By Srinath Viswanathan, Zhijing Zhang, Ramana G. Reddy

"The viscosity measurements were carried out on melts of 380 aluminum alloy containing 20 volume % SiC particulates under various shear rates at different temperatures using a Brookfield viscometer. Results showed that viscosities of the melts increased with decreasing temperature and decreased with increasing shear rate. These results were compared with those of 356 alloy and it was found that the temperature had a more significant effect on viscosity of 356 alloy than that of 380 alloy containing SiC particulates. Based on the present experimental data an empirical viscosity model, which considers the effects of both solid fractions in the melt and shear rate, is proposed.IntroductionDiscontinuously reinforced metal matrix composites materials (MMCs) such as aluminum alloy containing SiC particulates have considerable potential for applications in the automotive industry because of their superior stiffness, higher specific mechanical properties, better dimensional stability and strength retention at elevated temperatures when compared to their monolithic counterparts. They have a great advantage in the specificity of their properties, meaning that specific materials can be engineered for specific applications. With such freedom of design, materials engineers have to accumulate a very large database of mechanical properties. Among these properties, the viscosity of alloy slurries is very important for producing, casting and forming process of metal matrix composites materials because viscosity has a decisive influence on fluid flow. The understanding of the rheological behavior of alloy slurries is necessary for these materials to become economic reality. Therefore, a study was carried out to measure the viscosities of 380 aluminum alloy containing 20 volume % SiC particulates under various shear rates and temperatures. In addition, a viscosity model representing the primary features of the alloy slurries was developed."

Jan 1, 1999

By Ramana. G. Reddy, Haoxing Yang

The electrodeposition of zinc from zinc oxide using urea and choline chloride mixture in a molar ratio 2:1 is investigated in different experimental variables, namely, the concentration of added [BMIM]HSO4, temperature, and applied cell voltage. The additive, [BMIM]HSO4, was determined to have beneficial effect on the current efficiency, energy consumed in the process and surface morphology of the deposits. The highest current efficiency (92.6%) and lowest energy consumption (2.92kWh/kg) was obtained for solution with 20mg/mL [BMIM]HSO4. The morphology showed the formation of absorbed additive layer on the cathode at higher concentration of additives. Experiments were conducted at different temperatures between 343K and 388K and at various applied cell voltages between 2.7V to 3.6V to determine the best experimental conditions. By varying temperature, highest current efficiency (91.3%) and lowest energy consumption (2.69 kWh/kg) was obtained at 373K. The electrodeposition process is enhanced between the applied voltage 3.0-3.3V by achieving lower energy consumption (2.75~3.06kWh/kg) and higher current efficiency (88.4~89.7%). SEM images showed grain size is significantly increased in higher applied voltages. While at higher temperatures, it seemed to generate particle growth as clusters at the outer deposit layer.

Jan 1, 2014

By Xin Li, Hai-Xing Fang, Bing Xie, Hong-Yi Li

Chromium-containing vanadium slag (V-Cr slag) was obtained by an industrial smelting process of Hongge Ore, which is valuable vanadium-titanium magnetite to extract V and Cr in China. Sodium roasting thermodynamics of V-Cr slag in presence of oxygen were calculated to evaluate the reactivity of chemical compounds. Results showed that the oxidation of FeV2O4 was intensified in presence of Na2CO3 while the oxidation tendency of FeCr2O4 was far lower than that of FeV2O4. It was probably that reactions of impurities including Al2O3, SiO2 and Fe2O3 with Na2CO3 happened and the products can promote the oxidation of vanadium or chromium compounds in lower valence. Based on thermodynamic analysis, a two-step selective extraction process of vanadium and chromium was proposed. Extraction rate of vanadium was 88.6% while 7.0% for chromium in the first extraction step; extraction rate of 90.7% and 95.4% for vanadium and chromium, respectively, were obtained in the second step.

Jan 1, 2014

By Randy Martin

"Greenstone Resources Ltd. constructed and operates the Santa Rosa open pit, heap-leach gold mine in Veraguas, Panama. The project was commissioned in 1995 at a designed capacity of 1.8 million tons per year. The ore exhibits a long leach up to three years, and requires three stage crushing to minus 3/8 inch to achieve on average a 74% gold recovery. The crushing plant is required to handle high volumes of clay and the circuit includes a Barmac Crusher. Panama receives over 3 meters of rain annually and Greenstone is using innovative means to control the project's water balance. Greenstone has developed a successful approach to operating a low grade (1.5 gm Au/T) deposit under difficult operation conditions.ABSTRACT ONLY"

Jan 1, 1997

By I. U. Onyenanu, C. E. Ilochonwu, E. I. Nwonye, C. O. Nwajagu

This work shows how pure silica was derived directly from rice husks ash (RHA) in different temperatures for reduction to Silicon (Si). The processes to form Si materials are usually complex, costly and energy-intensive. The silica in the ash undergoes structural transformations depending on the conditions of combustion. A high purity silica was produced at 650oC after burning the rice husk (RH) for up to 7 hours. The purity of the silica was determined by dissolving the RHA with alkali solution to form sodium silicate solution of pH 11.0. This was added to hydrochloric acid of pH 1.5 which lowered the pH of the solution to 4.0 to form silica gels. The silica gels produced were washed and dried to powder and then characterized using XRD and EDX techniques. This study was done to reduce energy waste and environmental pollution in Nigeria as silica is used to develop many materials.

Jan 1, 2015

By H. Kaffash

Ferromanganese is a ferroalloy with high manganese content which finds many uses for example as deoxidizer in steelmaking industry. However, there is very little data on the dissolution rate of carbonaceous materials in Mn containing metals. In this paper, the kinetic analysis of carburization reactions is investigated for Mn–Fe alloys. Dissolution rate of graphite in pure iron and four different alloys with 10 wt%, 40 wt%, 60 wt% and 85 wt% manganese at 1823 K was studied. Results showed that the dissolution rate of carbon from graphite increased with increasing time for all alloys. The dissolution rate constant increased with the increasing manganese content from 6.5 × 10−3 cm/s for 0%Mn to 23.6 × 10−3 cm/s for 85%Mn.

By Takayuki Watanabe, Yoshiki Shimizu, Yusuke Moriyoshi

"B-C-N nanotubes prepared by a flush evaporation method using a de arc plasma were mainly characterized by transmission electron microscopy (TEM) and electron energy· loss spectroscopy (EELS). The nanotubes obtained· were divided into three types such as carbon boron nitride and carbon or carbon nanotubes surrounded with boron nitride nanotubes. These types of nanotubes were obtained at higher temperatures than about 3000 K, however, these were not formed at lower temperatures than about 3000K. On the other hand, 11anocapsules were· formed at all the experimental temperatures and nanocapsules with a homogeneous phase were obtained at lower temperatures than about 3000 K. The effect of additives on the formation of B-C-N nanotubes was not clear. Based on these experimental data depending on temperatures and corresponding microstructures, the formation mechanisms of both nanotubes and nanocapsules were briefly .discussed 1 Introduction As reported previously, nano tubes have unique electrical properties1, 3) The preparations of nallotupes have been usually carried out by flush evaporation methods using either a de arc plasma or a laser4 -5) By these methods the reaction rate is so rarid that we have no data of intermediate products between initial raw materials and. final products of nanotubes 6-9). So, the formation mechanisms of nanotubes have been mainly speculated only from the microstructures of resultant nanoiubes. In order to have more reliable formation mechanisms, it is particularly important to have the information of intermediate products at the corresponding temperatures. From the viewpoints, we have studied about the effects of temperatures on the preparation of nanolubes. Here we report mi firstly some problems on the preparation of B-C-N nanotubes 10), secondly the effects of temperatures on the preparation of B-C-N nanotubes, and finally the formation mechanisms of nanotubes."

Jan 1, 2000

By C. A. Summers

The U.S. Bureau of Mines applied process mineralogy to investigate a lead and zinc deposit located near Story Creek, Colville Mining District, Alaska. Mineralization is hosted by the Kayak Shale in veins, veinlets, and breccia. Sphalerite and galena, with supergene anglesite, occur in symmetrical quartz veins and between breccia clasts. The study sample analyzed 2.11 percent Pb, 5.37 percent Zn, 0.014 percent Cu, and 1.2 oz/ton Ag. Analyses of crushed products showed that 33 percent of the sample weight, and more than 50 percent of the Pb and 65 percent of the Zn, are in the minus 850 um fraction. Liberated grains of sphalerite and galena were found in crushed products finer than 300 um. Beneficiation tests indicate the material is amenable to processing by traditional gravity and flotation techniques.

Jan 1, 1991

By Jack S. McPartland

The recent developments on the concentration and recovery of gold from leached gold thiosulfate solutions by solvent extraction, reduction-precipitation, and electrochemical deposition are reviewed in this paper. Alkyl phosphorus esters have been found to extract gold only in alkaline thiosulfate solutions, The recovery of gold increases with thiosulfate concentration in the aqueous phase and with alkyl phosphorus esters concentration in the organic phase with aliphatic hydrocarbon diluents. The addition of ammonia improves the extraction. The extraction of gold with amines in either aliphatic or aromatic diluent decreased in the following order: primary>secondary>tertiary amines. Increase in the extractant concentration at high pH increased the extraction of gold. At pH < 9, the primary amine, RR&apos;CHNH2 with 1&apos;9-23 carbon atoms is the main extractant with TBP as the synergistic reagent and at pH >9, the primary amine shows a synergistic effect on the extraction of gold&apos; with TBP. TheAu(I) ions in thiosulfate solution are reduced by sodium borohydride (SBH) to metallic gold, with particles in the sub micron range, At an SBH/ Au ratio of 6.25, pH = 6, and at room temperature, the I e ppm Au(I) in a solution of ] 0 gil thiosulfate was completely reduced to metallic gold in about 60 minutes.

Jan 1, 1999

By Maija-Leena Metsiirinta

The behaviour of copper and lead in zinc roasting has been studied in laboratory scale roasting experiments as well as in large scale trials in an industrial fluidized bed, with the background of Outokumpu Kokkola Zinc smelter. Commercial zinc concentrates with a low and high ( up to 3 wt % ) copper content and with a low and high ( up to 3.5 wt % ) lead content were oxidized to various desulphurisation degrees in the fluidized bed to establish the reaction mechanisms and the paths for copper and lead oxidation in the roasting. Influences of the agglomerate size on the roasting kinetics and micro- scale phenomena were also determined. Optical microscopy was used on the calcine and the findings are presented as numerous photographs of the polished cross sections. SEM/EDS techniques were used for analyzing chemically the phases and particle morphologies present in the samples. Computational thermodynamics was applied to the complex phase equilibria occurring during roasting in the agglomerating calcine. A complete oxidation of zinc concentrate with a high copper and lead content requires a careful control of oxygen coefficient in the roasting in order to maintain a stable operation of the fluidized bed. Oxygen coefficient thus seems to have a significant impact on the hydrodynamic stability of the fluidized bed with fine raw materials.

Jan 1, 2003

By Maija-Leena Metsärinta

The behaviour of copper and lead in zinc roasting has been studied in laboratory scale roasting experiments as well as in large scale trials in an industrial fluidized bed, with the background of Outokumpu Kokkola Zinc smelter. Commercial zinc concentrates with a low and high ( up to 3 wt % ) copper content and with a low and high (up to 3.5 wt % ) lead content were oxidized to various desulphurisation degrees in the fluidized bed to establish the reaction mechanisms and the paths for copper and lead oxidation in the roasting. Influences of the agglomerate size on the roasting kinetics and micro-scale phenomena were also determined. Optical microscopy was used on the calcine and the findings are presented as numerous photographs of the polished cross sections. SEMIEDS techniques were used for analyzing chemically the phases and particle morphologies present in the samples. Computational thermodynamics was applied to the complex phase equilibria occurring during roasting in the agglomerating calcine. A complete oxidation of zinc concentrate with a high copper and lead content requires a careful control of oxygen coefficient in the roasting in order to maintain a stable operation of the fluidized bed. Oxygen coefficient thus seems to have a significant impact on the hydrodynamic stability of the fluidized bed with fine raw materials.

Jan 1, 2003

By Chuan-fu Zhang

Li(Nil/3Col/3- xMnl/3)MxO2(M=Ti, Mg) cathode materials were prepared from LiOH?H2O and oxalate precursor. The physical and electrochemical properties were studied by XRD, SEM, cyclic volt-ampere (CV), AC impedance and constant current charge-discharge. The results show that crystal volume of Ti4+ or Mg2+ doped sample is increasing and the electrochemical reaction resistant Rct is decreased at high rate, improving the cyclic performance and rate capability. The effect of Ti4+ doped is better than Mg2+. The sample is well crystallized and simple pure phase with a-NaFeO2 layered structure when doping quantity x=0.025. The second specific discharge capacity of Li(Nil/3Col/3- 0.025Mnl/3)Ti0.025O2 is 143.2mAh/g at 1C,128.0mAh/g at 2C in the voltage of 2.75-4.3V,and still has 140.7mAh/g and 121.7mAh/g after 20 cycles, respectively, keeping 98.25%, 95.07% capacity.

Jan 1, 2009

By Yunhua Gan, Xiaowen Chen, Yang Tong

Experimental studies of electro-spraying were carried out using ethanol as fuel in a microcombustor under combined electric field. And the effects of different electro-spraying modes on the combustion efficiency were analyzed. Results showed that when ring electrode potential was invariant, there were four different electro-spraying modes with the variations of nozzle potentials, which were varying with the flow of ethanol. The cone-jet mode was the stablest one during the whole experimental process. The atomized ethanol was ignited and combusted stably near the steel mesh, the combustion efficiency increased firstly and then decreased along with the increasing of the equivalent ratios, reached the maximum values when the equivalent ratio equal to 1.0. And the maximum values were the highest at the cone-jet mode, and the lowest at the pulsed-jet mode.

Jan 1, 2016

By D. D. Harbuck

The U.S. Bureau of Mines recently identified a significant new source of scandium in an Oklahoma tantalum waste residue (approximately 0.24 pct Sc). Because scandium is a strategic and critical metal which the Department of Defense has classified for special consideration, the Bureau is researching methods of recovering scandium and associated metals from this and other process residues. A variety of operating parameters were evaluated to determine the best technique for recovering scandium. Testing showed that by sulfating the residue at temperatures as low as 150&apos; C for reaction times as short as 0.5 hr, over 94 pct of the scandium converted to a water soluble form. Solvent extraction using DEHPA selectively recovered 100 pct of the scandium from the water leach solution.

Jan 1, 1992

By Takashi Ikeda, Masafumi Maeda

"Demand for solar cells is increasing linearly throughout the world. Last year production totaled 3000 tons worldwide. The market size of solar silicon is expected to increase further because of international ""political"" demand to reduce carbonaceous emission from energy consumed. Most elemental silicon is produced by the carbon reduction of Silica in an electric arc furnace. Purity of silicon at this stage is 90-99%. Major impurities are Fe, Ti, Ca· and Al, and minor ones are P, B and carbon. The oxidizing metallurgical process is no longer effective to remove transitfon metals because those are less noble to silicon. Nonmetallic impurities such as phosphorus and boron must be reduced to 0.001ppm for semiconductor use. The most common process for high purity silicon is the Siemens C process, which is basically distillation of hydro-chlorinated silicon followed by CVD of SiHCl3. The cost of such silicon is expensive to allow its popular use in solar cells. Currently scrap silicon -of semiconductors is used for this; however, the supply-of that scrap is limited to just a portion of semiconductor production.In this paper world demand for silicon will be reviewed and some of the processes proposed summarized.IntroductionSilicon is element 14 in atomic number and has an atomic weight of 28.0855. Little elemental silicon is found in the earth, and it is mostly found as oxides or silicate. The Clark number of silicon is very large and the second in its number. If we were discussing the volatility of silicon element on the globe, we would never worry about it. However, it is very difficult to obtain pure elemental silicon because a high purity silicon compound is very rare. In most cases these are silica (silicon oxide SiO2). As shown in Table 1, there are many grades of silica ore classified mainly by their content of iron and alumina."

Jan 1, 2000

By Hirofumi Tai, Masafumi Morishita, Toshiya Miyake

"In order to prevent corner cracks on cast steel slab and bloom, solidification delay at the corners should be controlled at the proper level. For this purpose, controlling the heat flux from the molten steel to the solidified shell at corners is essential. In this paper, optimization of the submerged nozzle was studied based on flow and solidification analysis.First, for the slab caster, the submerged nozzle shape was optimized. The improved nozzle was tested in actual casting and completely succeeded in preventing corner cracks. It was clearly demonstrated that the solidification delay and the corner cracks were strongly affected by the spouting stream from the submerged nozzle.For the bloom caster, on the other hand, the setting angle of the nozzle was optimized. Numerical simulations demonstrated that the spouting stream from the nozzle causes solidification delay, impinging at the corners under electromagnetic stirring conditions. Optimization of the setting angle of the nozzle is a possible means to reduce the solidification delay at the corners for the bloom caster.Related to the numerical analysis of flow and solidification, the effect of the critical solid fraction at the tip of the dendrite structure on the solidification under electromagnetic stirring conditions was studied."

Jan 1, 1999

By Fumitaka Tsukihashi

Increasing amounts of steel scrap are being used as resources for steelmaking. Therefore, there has been a growing interest in the removal of harmful tramp elements such as antimony, zinc, tin, arsenic, bismuth, lead and copper from the molten steel. The problem that should be solved is the economic removal treatment of residual tramp elements in the steelmaking processes and the production of high quality steel by reducing the effect of the contaminated tramp elements and satisfying the environmental regulations. In this paper, the available thermodynamic data of the residual tramp elements in the molten steel arc summarized and the possibility of the removal of residual tramp elements from the molten steel is thermodynamically estimated.

Jan 1, 2003

By Michael S. Moats, Daniel Kim, Shijie Wang

"The behavior and deportment of lead, arsenic, antimony and bismuth are critical in producing high quality cathode by copper electrorefining. A critical review of research related to these elements is presented along with a comparison to industrial data, where appropriate. These elements exist predominantly in the anode as complex oxides along die grain boundaries. Upon dissolution, Group 15 elements report both to the electrolyte and slimes while lead essentially enters the slimes. The deportment of the Group 15 elements appears to be influenced by several chemical interactions which are discussed. The effect of these elements on floating slimes and anode passivation is reviewed. Under normal electrorefining conditions, lead, antimony and bismuth are thought to enter the cathode through the encapsulation of slime particles. The literature indicates that arsenic enters the cathode predominately by electrolyte entrainment. Finally, areas for future research regarding these elements are presented.IntroductionControlling lead, arsenic, antimony and bismuth is critically important for the production of high quality cathode in copper electrorefining. The reasons for this are twofold. First, ASTM Grade 1 Cathode specifications [1] for these elements are low, as listed in Table 1. Second, they can affect the efficiency of the electrorefining process (e.g., through passivation, current efficiency, slime processing)."

Jan 1, 2012