By E. T. Turkdogan, M. T. Hepworth, R. P. Smith

The permeability of oxygen in 0 iron in the tempera-ture range 700" to 900 C and in 6 iron at 1450°C was determined by the rate of internal oxidation of iron, containing -0.1 pct Al. The solubility of oxygen in zone-refined iron was determined by equilibration with hydrogen-water vapor gas mixtures at 1450" and 1510°C; oxygen solubilities , for iron in equi1ibriu.rn with molten oxide, are found to be 66 and 83 ppm for these two temperatures, respectively. The diffusivity of oxygen in iron at 14500C3 as calculated from the permeability and solubility data, is (4.1 * 0.6) x 10 "B sq cm per sec. OXYGEN is one of the most common impurities present in iron or steel, mainly in the form of oxide inclusions. In the study of many metallurgical problems concerning solid iron, it is often desirable to know with a reasonable accuracy the solubility and diffusivity of oxygen over a wide temperature range. The solubility of oxygen in solid iron has been the subject of numerous studies yielding highly discordant results as seen for example from the literature surveys made by Meijering &apos; and Schenck et a1.&apos; As shown by Kitchener et aL3 and by Sifferlen, the high oxygen solubilities reported by many investigators are the result of oxidizable impurities which are often present in iron. In addition, there have been experimental problems associated with icaccuracy of oxygen analysis of iron containing less than 100 ppm 0. A number of studies have been made on the permeability of oxygen in a and y iron using Fe-Si, Fe-Mn, and Fe-A1 alloys in the internal-oxidation experiments.1&apos;2&apos;5&apos;6 However, no direct measurements have been made of the diffusivity of oxygen in iron. In the present work two sets of experimental measurements were made: permeability and solubility studies at 1450" and 1510°C and permeability studies only in the range 700 to 900°C. In both sets of permeability measurements slab-shaped specimens containing small predetermined amounts of aluminum in solution were exposed at constant temperature to gas mixtures of hydrogen, water vapor, and argon for varying times. These specimens were quenched, sectioned, and examined for oxygen penetration by metallographic observation of aluminum oxide particles which formed. From these data, it is possible to calculate the ratio of the diffusivity of oxygen in iron, D, to the equilibrium constant K for the reaction Hz(g) * O (dissolved in iron) = H,O(g). EXPERIMENTAL Permeability Measurements at 1450°C. An ingot of vacuum-carbon deoxidized iron containing 0.086 pct A1 was prepared, using commercial "Type lO4A Plas-tiron"; after hot rolling, specimens were machined into slabs a by 2 by 2 in. The impurity contents were: S, P < 0.002 pct; C, Mn < 0.01 pct; each of all other Usual impurities < 0.004 pet. The amount of oxide inclusions in this material, determined by a bromine-methyl acetate extraction, corresponded to about 20 ppm 0 in the iron which agreed well with the results of vacuum-fusion analysis. Each specimen was annealed at 1450°C for 1 hr in purified hydrogen, polished to a smooth surface, and then introduced into a controlled oxidizing atmosphere in a recrystallized alumina tube at 1450°C. The constant temperature zone (*3"C) was about 3 in. in length. The gas composition was controlled by mixing argon with hydrogen (using calibrated constant-head flow meters) and passing the mixture through a column of a mixture of oxalic acid dihydrate and 10 pct anhydrous oxalic acid, to establish a required water-vapor content in the gas mixture. The temperature of the oxalic acid dihydrate column was controlled by a thermostat. The total gas flow was in the range 800 to 1000 cu cm per min. The exit gas from the reaction tube was passed through a weighing bottle containing a desiccant, to cross-check the degree of water-vapor saturation, which for all experiments was about 97 pct of those derived from the data of Baxter and Lansing.1 For a typical experiment, a specimen was introduced into the furnace in a stream of dry argon and hydrogen. The specimen was then rapidly raised by a Pt-Rh alloy wire into the hot zone and allowed to reach the reaction temperature, at which time the oxidizing gas mixture was introduced. The oxygen potentials employed were sufficient to oxidize aluminum but not to cause liquid iron oxide to form. After a specified time, the experiment was ended by dropping the specimen onto a water-cooled copper block at the bottom of the reaction tube. The depth of the internally oxidized zone, hereafter called the "case", was determined by sectioning the specimen at right angles to the long direction. The section was then examined under a microscope equipped with a micrometer stage. In general, the oxide particles were fairly uniform in size and distribution, forming a reasonably well-defined interface between the oxidized and unoxidized region. A typical cross section as observed at X30 is shown in Fig. 1. A thermal macroetch was used in one selected specimen to delineate the case. A cross section of a previously oxidized slab was polished and reheated at 1450°C in a hydrogen atmosphere for about 10 min. Upon quenching, the surface relief shown in Fig. 2 was produced; causes of this effect are unknown. Permeability Measurements Below 900°C. A slightly

Jan 1, 1967

By S. Leber, R. F. Hehemann

This investigation describes the kinetics of alloying in a (Cb-15 wt pct W. 5 wt pct Mo, 1 wt pct Zr) powder-metallurgy alloy. The degree of homogeneity obtained in hydrostatic ally pressed and vacuum-sintered samples is described by composition distributions resulting from analysis of X-ray dvfraction line profiles. Sintering variables and degvee of powder dispersion were evaluated. The utility of single-value parameters obtained from composition distributions is disaissed. The spatial distribution of composition, as revealed by anodically tinted metallographic sarrzples, was used to provide diffision models based on a concentric-sphere geometry. Diffusion equations developed from these models were found to be in general agreement with experimental results. The powder-metallurgy method for the production of refractory metal alloys has the ability to produce an inherently fine-grained, fabricable structure. The more general use of this method is inhibited, in part, by the presumed difficulty in obtaining homogeneity on a microscale. The degree of homogeneity therefore is an important, but usually neglected, variable in specifying the quality of a powder-metallurgy alloy. Convenient techniques for measuring the degree of homogeneity are now available,&apos; and have been used to develop a model describing the process of alloying in a simple binary mixture.&apos; In this investigation, the process of alloy formation has been studied in a more complex system. PROCEDURE The columbium-based F-48 mixture was prepared from the constituent powders shown in Table I. The particle sizes tabulated were provided by the vendors of the individual powders. Standard laboratory techniques utilizing a jar mill were employed for blending. The blended powders were hydro-pressed into 1-in. diam rods which were then sliced into thin discs for vacuum sintering. All samples were given a preliminary treatment at 1700°C for 2 hr. Varying degrees of homogeneity were obtained using additional treatments at higher temperatures. The degree of homogeneity obtained by a specific sintering treatment was evaluated metallographi-cally using the anodic-tinting technique described by olff,&apos; and quantitatively by the analysis of X-ray diffraction line profiles using the X-ray diffraction technique developed by udman.&apos; The diffraction technique is strictly valid only for binary systems. However, the relatively small difference between the lattice parameters of tungsten and molvbdenum when compared with columbium permitted the treatment of the complex composition of F-48 as a (W, Mo)-Cb pseudobinary. Calculations were weighted in accord with the W-Mo ratio in the F-48 composition. The contribution of the 1 pct Zr was ignored since it could not even be detected in the blended powder. Two factors are required to convert an X-ray line profile into a composition distribution. The variation of these factors with composition is shown in Fig. 1. Curve A was used to convert angular posi-

Jan 1, 1964

By H. G. Moulton

THE INCREASING scale of mining operations over the past decade, particularly in connection with the exploitation of large bodies of comparatively low-grade copper ores, has made necessary the study of the behavior of rock under failure. When extractions of as high as 40,000 tons a day are reached in steam-shovel operations and as high as 20,000 tons per day in underground mining operations, it is evident that excavations soon become of such size that the behavior of the rock will often be dependent on fundamental principles applicable to more or less homogeneous materials under stress, rather than on weathering or local planes of weakness. In the ordinary rock excavations encountered in civil-engineering practice, such as excavations for subways, highways, railroads, etc., rock faces are not carried to depths sufficient to develop any pressures, or consequently any failures, except those due to loose masses resulting from local planes of weakness. When, however, orebodies whose tonnage is measured by hundreds of thousands are to be extracted by steam-shovel operations in open pits, it is necessary to determine if possible in advance the slopes that the sides of the pits will assume, for these slopes influence the shape of the excavations and thereby the amount of ore that may be extracted by the open-pit method. When large orebodies are mined underground at depths of 300 to 500 ft. (91 to 152 m.) by caving methods, the surface subsiding as the ore is withdrawn, it is necessary to determine in advance the outermost limits of fracture in the subsiding surface, for on the delineation of these limits depends the location of surface improvements, mills, smelters, etc. and also the location of development work, such as hoisting shafts, main haulage levels, and all other underground openings that must remain undisturbed during the period of ore extraction. Heretofore, in civil-engineering practice, it has been assumed that earth and rock behave differently in failure. For the calculation of earth

Jan 2, 1920

By J. E. Steiner, J. M. Hodge, M. A. Orehoski

Ingots of four steels (1045, 1080, Ni-Mo-V, and Ni-Cr-Mo-V) were cast at pressures varying from about 1 to 760 mm of mercury, so as to obtain a range of hydrogen contents in each steel. The susceptibility of these steels to flaking was evaluated by cooling hot-rolled blooms at a range of cooling rates, varying from water quenching to slag cooling, and studying the occurrence of flaking as a function of cooling rate. The steels exhibited differences in susceptibility to flaking, and a tlzreshold value for hydrogen content for each steel was found, below which the susceptibility was very low and above which the susceptibility increased markedly with increasing hydrogen content. Mechanical property evaluations, metallogvaplzic exantinations, and X-my diffraction determinations o,t retained austenite were made on samples from the blooms. A mechanism of flaking which is consistent with the observed behaviors, the effects of hvdrogen content, and the differences in susceptibility among the steels investigated is postulated, based on the results of mechanical property evaluations and metallographic and X-ray diffraction studies. ThE important role of hydrogen as a factor in the occurrence of "flakes" or "hair-line cracks" in steel has now been established by many investigations. These have included investigations by steel producers and forging manufacturers, to whom the prevention of flaking is a very real and serious problem, and many research studies aimed primarily at establishing the mechanism of this behavior Several investigators3 have reported that steels cast at reduced pressures (absolute pressures of about 1 mm) not only are low in hydrogen content but are essentially insensitive to the formation of flakes. These investigations have shown that a general relationship exists between hydrogen content and susceptibility to flaking. The difficulty of obtaining suitable samples of steels of a given composition with the desired range of hydrogen contents, particularly in the relatively large sections in which flaking most commonly occurs, has been the principal obstacle to quantitative evaluations of these relationships. Steels with intermediate hydrogen contents between 1 ppm, and the 4ppm or higher of air-cast steels are generally not available in commercially produced steels. Laboratory procedures, in which the hydrogen is introduced into solid steel samples by heating in a hydrogen atmosphere under pressure, generally involve a limitation in the size of the sample which can be treated, and thus are not representative of the behaviors in large sections. The availability of a facility at the South Chicago Works of U.S. Steel, in which several ingots could be cast from a single heat of steel at total air pressures ranging from 0.25 to 760 mm of Hg, has made it possible to overcome this obstacle and to obtain ingots of a given steel covering the intermediate range of hydrogen contents desired. These ingots, furthermore, are of a size suitable for the production of product with section sizes large enough to be representative of the products in which flaking most commonly occurs in commercial production. In these experiments, this facility was used to study the relationships between hydrogen content and the susceptibility to flaking of four steels, two plain carbon steels at 0.45 and 0.80 pct C and two low-carbon alloy steels representing a medium and a rather high hardenability level. These flaking studies were supplemented by evaluations of mechanical properties and by metallographic studies on samples from the blooms, in order to obtain pertinent information on the factors other than hydrogen content which influence the susceptibilities of these steels to flaking. Based on the results of these tests, a mechanism for the initiation and propagation of the flaking cracks, which is consistent with the observed behaviors, is postulated. MATERIALS AND EXPERIMENTAL WORK Steelmaking and Conversion. To provide material for the investigation, five 29- by 35-in., hot-topped, big-end-up ingots were cast from each of four 80-ton, basic electric-furnace heats of four different steels (a 1045 steel, a 1080 steel, a Ni-Mo-V steel, and a Ni-Cr-Mo-V steel). A double-slag practice was used on all steels and the two plain carbon steels were Si-A1 deoxidized with an addition of 2 lb of A1 per ton, while the Ni-Mo-V and Ni-Cr-Mo-V steels were deoxidized only with silicon and

Jan 1, 1964

By W. P. Sykes

SEVEN years ago, Dr. S. L. Hoyt1 presented a masterful discussion of the hard metal carbides and cemented tungsten carbide. His lecture summarized most of the data then available in the field; many of the details relating to the production, properties and structure of cemented tungsten carbide had never been previously published, for, in fact, this information was only then being acquired. During the intervening years, the cemented carbides have assumed a place of real importance in the commercial field, with an ever widening variety of applications due to constant improvement in the control of production technique and the unremitting search for new compositions that might better the performance of the alloys in one or another type of service. The most recent summary of production methods, properties and guides for the successful application of the cemented carbides appears in the 1936 edition of the Metals Handbook. Of necessity, much detailed information relating to structures and physical properties is not included in such a summary, and it is with such details that the present discussion is concerned.

Jan 1, 1938

By C. F. Smart

The heat treatment of the bronze composed of 88 per cent. copper, 10 per cent. tin, and 2 per cent. zinc, has been investigated by H. S. and J. G. S. Primrose,&apos; and also by the U. S. Bureau of Standards.2 The results obtained by H. S. and J. G. S. Primrose on dry-sand castings subjected to reheating followed by air cooling, or by quenching in water, are shown in Figs. 1 and 2. The values for tensile strength have been converted from tons per square inch to pounds per square inch. Figs. 3 and 4, have been plotted from values obtained by the Bureau of Standards on material of the same composition and treatment. Both investigations show that the ductility of the cast bronze is improved by heating to 700&apos; C. and cooling in air, the strength not being impaired by this treatment. They are not in agreement, howevcr, as to the effect of quenching, Messrs. Primrose reporting a decrease, and the Bureau of Standards an increase, in both strength and ductility when the cast bronze is heated to 600&apos; or 700&apos; C. and quenched. The present investigation was undertaken to study the effect of annealing followed by different rates of cooling, and, in particular, the

Jan 1, 1921

By A. C. Halferdahl

DURING a study of reactions involving iron sulfides, it became desirable to know approxi-mately the heat of decomposition of pyrite. The values given for the heats of formation of pyrite and ferrous sulfide are 35,500 calories and 23,070 calories respectively. For the reaction 2FeS2= 2FeS+S:, the heat effect would be-24,860 calories. But pyrite gives sulfur and pyrrhotite upon heating and the latter is a solid solution of sulfur in ferrous sulfide. The only meas-urements of this decomposition are those of Allen and Lombard1 of the Geophysical Laboratory who have measured dissociation pressures of both covellite and pyrite and have carefully reviewed the literature. They give a table of values for covellite as determined by Preuner and Brockmoller2 and by Wasjuchnowa3 and compare these values with their own measurements. The conclusion is that the measurements of Preuner and Brockmoller are seriously in error, while Was-juchnowa&apos;s values fit in well with those of Allen and Lombard. Wasjuchnowa&apos;s measurements were made by a dynamic method, while Allen and Lombard em-plowed a static method on both covellite and pyrite. Tables I and II reproduce the measurements of Wasjuchnowa and of Lombard and Allen on covellite and pyrite.

Jan 11, 1927

By R. B. Snow

THIS paper describes a technique of polishing and etching specimens of open-hearth furnace slags or hearth aggregates for identification of the crystalline constituents-lime (CaO), tricalcium silicate (3CaO•SiO2), dicalcium silicate (2CaO-SiO2), monticellite (CaO•MgO-SiO2), or forsterite (2MgO•SiO2), with especial emphasis on the mineral merwinite (3CaO-MgO.2SiO2). With proper standardization, this identification does not require the use of the petrographic microscope. The composition of basic open-hearth slags and furnace bottoms falls, almost without exception, within systems containing CaO, MgO, "FeO," MnO and SiO2, in which the number of basic molecules so greatly exceeds the orthosilicate ratio (two molecules of base to one of silica) that free basic oxides, and combinations between them such as aluminates or ferrites, are present in cooled specimens. Orthosilicates of (CaO + MgO) are the most common in such specimens, since in nearly all cases, except premelt slags, the molecular ratio of (CaO + MgO) to SiO2 is more than 2 to r. When sufficient lime is available it combines with the silica to form dicalcium silicate (2CaO•SiO2), which contains little, if any, MgO, FeO or MnO in solid solution whereas the latter oxides combine to form the oxide solid solution known as periclase. If the lime present is insufficient to form dicalcium silicate (2CaO•SiO2) it combines with MgO to form either merwinite (3CaO•MgO.2SiO2) or monticellite (CaO-MgO•SiO2); these minerals take little if any FeO or MnO into solid solution and the remaining MgO, FeO and MnO combine as periclase. This generalization seems to be valid for basic slags and furnace bottoms, since minerals such as CaO-MnO•SiO2 and CaO-FeO-SiO2 are found only in slags in which the lime-silica ratio is less than 2 and are not observed in specimens from furnace bottoms. The identification of crystalline constituents in such materials, especially of fine crystals in the groundmass, is difficult under the petrographic microscope. They are often masked by their neighbors because of their small size in relation to the thickness of the thin section and because of the presence of opaque or colored constituents. The indices of retraction and the optical sign of the mineral are sometimes difficult to determine because of the small size or because of twinning or of inclusions within the crystal. Moreover, the positive identification of merwinite (3CaO•MgO.2SiO2) from its optical properties is usually difficult in the presence of dicalcium silicate (2CaO•SiO2). CaO, MgO, 3CaO•SiO2 and 2CaO•SiO2 in open-hearth slags have been identified for a number of years in the U.S. Steel Corporation Laboratory by the usual

Jan 1, 1947

By R. V. Smith

The theoretical background for calculating friction factors for flow in gas wells by two methods is presented. The first method, requiring pressures, temperatures and specific volumes of the flowing fluids at various depths in the well bore, shows how the mechanical-energy-balance equation for vertical flow may be graphically integrated over the actual path of the expansion of the fluid in the well. Thus, assumptions regarding the effective temperature and effective compressibility of the fluid in the well are avoided. The second method presents an equation derived on a basis of the assumptions that both the temperature and the compressibility are fixed at constant effective values throughout the flowing column of gas. The second method provides a convenient and practical means of calculating friction factors for gas wells and lends itself readily to the problem of calculating subsurface pressures in a flowing gas well. The application of both methods to actual test data taken on a flowing gas well is illustrated in the paper. INTRODUCTION As friction factors for the producing strings of flowing gas wells cannot be measured directly and must be calculated from flow-test data, study of the methods of arriving at friction factors is a necessary adjunct to understanding the characteristics of flow in gas wells. There are two methods of calculating friction factors for gas wells; they differ from one another mainly in the treatment of the path of expansion of the fluid in the well. In the flowing well, the energy consumed in lifting the fluid from the bottom to the top of the well, overcoming the friction between the moving fluid and the pipe walls, and increasing the velocity of the fluid as it flows up the producing string is supplied by expansion of the flowing fluid. The available energy is determined by the expansion of the fluid that follows a path determined by conditions of temperature, compressibility and phase changes of the fluid during the expansion. A means of evaluating the available energy in a flowing gas well and determining the proportion of the available energy used in lifting the gas, overcoming friction, and increasing the velocity of flow is developed in this report. Knowing how much energy is consumed in overcoming friction makes it possible to calculate friction factors for given flow rates in given sizes of pipes in wells. Friction coefficients, as used in this report, are dimension- less proportionality multipliers used in the flow equations to satisfy the equality between the terms of the equation. The square root of the reciprocal of the friction coefficient is termed the friction factor. It has been known for many years that friction factors may be computed directly from mathematical formulas based on certain assumptions regarding the temperature and compressibility of the moving fluid in a well. A general equation is presented in this report without assumptions for vertical flow of fluids and a conventional-type equation is derived on the basis of assumptions that fix the temperature and compressibility at constant values. Accurate pressures at the sand faces in wells are required in the method of determining the productivity of gas wells, as outlined by Rawlins and Schellhardt1 in Bureau of Mines Monograph 7. Where measurements are not made with subsurface-pressure gauge; or static gas columns are unavailable, flowing pressures customarily are calculated at the sand face in the well by the use of the well-known Weymouth formula1. Natural gas engineers have realized that errors introduced by the use of friction factors as given by the Weymouth formula are relatively unimportant in testing low-capacity gas wells; they also know that such factors are important considerations in testing large-capacity gas wells. Accordingly. present research on the productivity of gas wells at the Petroleum Experiment Station of the Bureau of Mines, Bartlesville, Okla., is being directed toward measurement of the pressure loss due to friction in flowing gas wells. It is beyond the scope of this report to show how friction factors vary with rate of flow and in pipes of different diameters, as it is intended only to develop and illustrate the use of mathematical expressions for calculating friction factors from flow-test data. The equations presented apply only to turbulent flow in circular pipes. ENERGY RELATIONS FOR FLOW OF FLUIDS2 The concept of conservation of energy is usually the basis of any study of fluid flow through vertical pipes as in gas wells, horizontal pipe lines, or orifices. In deriving equations, the following symbols are used:

Jan 1, 1950

By A. R. Troiano, E. A. Steigerwald, F. W. Schaller

The kinetics of crack propagation in a hydrogenated high-strength steel at subzero temperatures indicated that cracking progressed in a discontinuous fashion. The delayed failure process thus involves a series of crack initiations rather than the continuous growth of a single crack. The incubation time required for the initiation of delayed failure was controlled by the diffusion of hydrogen. The activation energy for the process was 9120 cal per g-alom. As the test temperature was lowered the incubation time constituted a greater percentage of the total tinze to fracture, and al -50°F the incubation and fracture times were essentially coincident resulting in instantaneous, catastroplzic fracture. A unique feature of hydrogen embrittlement is the delayed failure process in which the material fails under the action of a sustained load even though it is capable of supporting a higher load for a finite period of time.&apos;)&apos; Delayed failure of steel and titanium is characterized by an incubation time, preceding the initiation of a crack in a highly localized region, and the subsequent growth of the crack to ultimate failure.3-5 The kinetics of crack growth in hydro-genated high-strength steels have been studied through the use of resistance measurements and have an important bearing on the mechanism of delayed failure. Delayed failure is believed to be merely a facet of hydrogen embrittlement in which sufficient time is allowed during a test for hydrogen diffusion. The current theories employed to explain hydrogen em-brittlement can be grouped into two types. one6-8 explains the embrittlement on the basis of the pressure exerted by molecular hdrogen in lattice voids or defects while the other9-10 attributes the embrittlement to the influence of hydrogen in the lattice. The mechanism used to explain the nature of the crack kinetics in delayed failure is based on the stress-induced diffusion of hydrogen to the area of maximum triaxiality.3 When the hydrogen concentration in this region reaches a critical value, a crack is nucleated. This initial crack propagates instantaneously until stopped by the higher fracture stress of the adjacent material of lower hydrogen content. The continuation of cracking must then await the further diffusion of hydrogen to the new region of triaxiality near the base of the crack where another initiation will occur. From this mechanism it follows that crack propagation is nothing more or less than a series of initiations with limited fracture. The purpose of this investigation was to examine the kinetics of crack growth in an effort to determine whether or not the process was discontinuous. Studies of crack propagation were conducted at low temperatures to retard the diffusion of hydrogen which is presumed to be the rate controlling process in delayed failure. MATERIALS AND PROCEDURE Specimen Preparation—A commercial heat of air-craft quality SAE-AISI 4340 steel, designated as Heat G, was furnished by the Republic Steel Co. in the form of %-in. hot-rolled bars. The material had the following chemical analysis: Composition of 4340 Steel—G Heat C Mn Si Ni Cr Mo 0,395pct 0.82pct 0.29pct 1.76pct 0.85pct 0.25pct Notched tensile specimens with less than a 0.001 in. radius, Fig. 1, were used throughout the investigation. The specimens were heat treated to a 230,000 psi strength level according to the following sequence: a) Normalize bar stock at 1650°F for 1 hr, b) Stress relieve at 1200°F for 4 hr and furnace cool,

Jan 1, 1960

By Arthur Taggart

THE major portion of the work described in this paper was performed by R. W. Young,+ a graduate student in the department of Mining and Metallurgy, Sheffield Scientific School, Yale University, working under a cooperative agreement between the Hardinge Conical Mill Co., the Sheffield Scientific School, and himself. Since this cooperative scheme is at present in effect in the case of a considerable number of other students in the department and since it is the hope of the school that the privilege thus extended may be utilized even more freely in the future by mining and manufacturing companies, it may not be amiss at this point to give a summary of the general plan. Briefly it is as follows: A graduate student, whose undergraduate work in this or other universities shows promise of ability to handle research work, is chosen by conference between the company and instructor involved. The aim of the company in the agreement then entered into is to obtain the solution of one or more of the technical problems with which it may be confronted, or, at the end of 1 or 2 years, to obtain as an employee a man especially trained in its work. As. a means to accomplish one or both of these ends, the company furnishes the machine, apparatus, or material to be tested and pays the student during his graduate work a small salary, usually just sufficient to cover his living expenses, tuition and fees. The aim of the student is special training along a line in which he is particularly interested, the attainment of his advanced degree, and the chance to show to his future employer ability to handle such problems as may be presented to him. In return for the financial aid which he receives he agrees to devote at least half of his working time to the special problem submitted by his company. The other half is devoted to study of the collateral subjects required by the department for the granting of the degree which the student seeks. The student further agrees to enter the employ of the company in question at a wage not greater than that paid in like positions to recent graduates not specially trained and to remain with his employer at such wage for at least 1 year. If the student is to obtain a degree, the special work forming the basis of his investigation must be such as will involve real research and not mere routine manipulation. The subject is chosen by conference between the three parties to the agreement. The work is carried on under the direct supervision of the instructor involved. The school furnishes the general laboratory and library equipment essential to the pursuit of any extended investigation, In

Jan 4, 1917

By M. C. Dow

INTRODUCTION BELT conveyors generally are conceded to be the most economical method yet devised for the transportation of large quantities of bulk materials within plants. Belts are coming into greater use for transportation over long distances and are replacing other forms of long-haul conveyance. It is not the intent of the writer to comment on the design of belt conveyors, but to offer some suggestions for improvement in the operation of conveying belts, based on many years experience with belts in several stonecrushing plants. It is the contention of this writer that opportunities for improvement not fully realized by most operators exist in many plants and that a study of the individual conveyors can result in lower unit belt costs. GENERAL RELIABILITY It is the fool-proof nature and general reliability of the belt conveyor that is responsible for its neglect. Even when abused, a belt will carry large tonnages and last a long time, often outlasting the personnel responsible for its care. Some operators look upon the purchase of a new belt as an expensive outlay every so many years, rather than a constant and steady cost amounting in belt wear alone to several dollars every operating day. This belt wear for all conveyors in one stone-crushing plant known by the writer costs 1 1/2 cents per ton or $12 to $15 per hour, based on the present cost of belt replacements. The fact that these replacement costs are double those of prewar quality emphasizes the necessity of improving the conditions that make belts wear out. Some of those conditions are the responsibility of the conveyor designer, and if a serious original error has been made, this handicap cannot be overcome by the operator. If the belt is too narrow, too steep, or too fast for good loading, the operator finds that he has an inherently expensive belt. The other factors that decrease the life of a belt are more or less under his control. The two factors of most importance are the loading conditions and the alignment. Most of the cover wear and carcass cutting occurs at the loading point and if the alignment is not good under all conditions, edge wear or damage may result, Fig I. LOADING THE BELT It is difficult to load a belt in an ideal manner; that is, to flow the material on the moving belt at a steady rate, without impact, without turbulence, and with a velocity equal to and in the same direction as the belt. An inclined belt is especially difficult to load and particularly when its speed is over 300 or 350 fpm. Inclined conveyors require longer skirt plates to prevent spillage until the load settles. It does not seem reasonable to expect an inclined conveyor to carry the same load as a horizontal belt of the same width and speed, because of the difficulty in loading

Jan 1, 1947

CONTENTS PAGE CARMICHAEL, NORMAN, and KIDDIE, JOHN.-Development of Mine Transportation in Clifton-Morenci District. Discussed by Norman Carmichael, Charles Legrand, B. B. Gottsberger 1 BARER, THOMAS C.-Fresnillo - Glory-hole Mining Practice. Discussed by Charles A. Mitke, B. B. Gottsberger, E. R. Thomas, Enoch Perkins..: 3 BRADLEY, P. R.-Estimation of Ore Reserves and Mining Methods in Alaska Juneau Mine. Discussed by R. M. Raymond, A. H. Rogers, Enoch Perkins, H. G. Moulton 6 BIRCH, STEPHEN.-Geology and Mining Methods of the Kennecott and Beatson Mines. Discussed by R. M. Raymond, Alan M. Bateman, Enoch Perkins 8 LEES, CHARLES E.-Mining Methods and Costs at the Iron Cap Copper Co., Copper Hill, Ariz. Discussed by A. L. Walker, A. Neustaedter 10 BELL, CHARLES N. -Mining Methods of the Telluride District. Discussed by Charles S. Hurter 10 Development of Mine Transportation in Clifton-Morenci District Discussion of the paper of NORMAN CARMICHAEL and JOHN KIDDIE, presented at the New York Meeting, February, 1924, and issued, as. Paper No. 1310-M, with MINING AND METALLURGY, March, 1924. NORMAN CARMICHAEL.-We realized the objections too the gable-bottom car, but were almost forced to its adoption by the same reasons that caused us to retain the 20-in. gage. To use another car would have meant a vast number of changes, for our transportation system was quite extensive; all mine chutes and ore bins were arranged for that car. Had we been laying out, new works, many of our decisions would have been different. MEMBER.-If you were planning it now, would you not put in box bottom cars with a rotary dump? NORMAN CARMICHAEL.-We surely would. One objection to the gable-bottom car is the spill. No, matter how carefully the cars are kept up,: there is always leakage and spill. The cost of keeping and maintaining the cars in a good state of repair, so as to keep that loss at a minimum, is not necessary for a box-bottom car.

Jan 6, 1924

By Walter S. McKee

When mixed with common cast steel in quantities ranging from 11 to 131/2 per cent. and properly treated, manganese increases the ductility of the metal and adds greatly to its toughness and resistance to abrasive action, which properties comprise the distinctive characteristics that make manganese steel so valuable for many purposes at the present time.. * At present the manganese-steel foundries of this country have an annual capacity of about 60,000 tons and most of the growth has occurred within the past 10 years. In the early days of the industry it was impracticable to make manganese castings weighing over a few thousand pounds, but at present crusher heads, rolling-mill pinions, and similar castings weighing up to 30,000 Ib. each are produced, and it does not appear that the limit of weight has been reached by a considerable margin. Manganese steel is similar in analysis to ordinary first-class converter metal except that it is high in carbon and contains from 11 to 13.5 per cent. of manganese. From one standpoint manganese steel is similar to malleable iron in that the casting as it comes out of the sand is hard and brittle and must be made ductile by a heat-treating process. The heat treatment is an essential part of the process of making manganese-steel castings and must be properly carried out to secure satisfactory results. The necessity for heat treatment limits the thickness of sections which may be made of manganese steel. Originally the annealing depth was comparatively small, but researches carried on during the past few years have resulted in an increase in the thickness of section up to 51/2 in., which it is possible to treat successfully. Large castings are cored out to a minimum thickness of 51/2 in., thus not only eliminating some of the internal stresses which are invariably set up in a very thick casting, but also reducing the weight and inertia of the piece, an important consideration if the casting is to be a moving part in a machine. At the same time, the thickness of 51/2 in. is sufficient to permit the use of manganese steel for the heaviest classes of machinery.

Jan 1, 1916

T. L. Joseph (University of Minnesota, Minneapolis, Minn.)—Mr. Killian is to be commended for his inquiry as to why a decrease of 15.3 pct in coke consumption was accompanied by a decrease of only 1.9 pct in the CO/CO, ratio of the top gas. Although I encouraged him in his efforts to find a more significant and meaningful carbon-gas ratio, the method, calculations, and conclusions originated entirely with the author. Whether we agree entirely with the assumptions underlying his corrected ratio, I think we can all agree that a better ratio is needed, and that he deserves credit for recognizing the need and for doing something about it. To be most useful, the CO/CO, ratio for the top gas should reflect the way in which the carbon is gasified in the furnace, particularly the degree of oxidation and the extent of heat release. The effect of CO, from the decomposition of the limestone and the effect of the reaction of CO and water vapor in the upper part of the furnace on the quality of top gas should be isolated from the effect of more basic reactions such as ore reduction and solution loss. The reduction of sufficient iron oxide to produce a ton of pig iron and the accompanying changes in the proportions of the carbon gases can be expressed on a mol basis as follows: 16.5FeA + 16.5CO - 33FeO + 16.5CO, [1] 33FeO + 33.0CO = 33Fe + 33CO. [2] The CO, from eq 1 normally escapes from the furnace because it does not react with coke at the temperature of its release. However, as much as 50 pct of the CO, from eq 2 may react with coke because it is released at temperatures above 1000°C: 16.5CO. + 16.5CO2 = 33CO [3] Thus we see that the gasification of 16.5 mols or about 200 lb of C in solution loss will regenerate as much CO as is required for the last stage of reduction. The pronounced effect of reaction 3 on the final proportions of CO and CO, in the gas stream is obvious. It also follows that reaction 3 materially alters the heat release but it cannot be entirely eliminated in Lake ore practice. A previous study indicates that 100 lb of solution loss may be necessary to maintain the reducing power of the gas. A reduction of 100 lb from the normal level of 200 lb would mean that over 1,-000,000 additional Btu are released in the process. The 100 lb of additional carbon which will be burned at the tuyeres will release 437,000 Btu and the absorption of 583,000 Btu by eq 3 would be prevented. One of the chief objectives of sized ore burdens and more uniform distribution of the gas stream is to minimize solution loss by completing reduction higher in the furnace and in turn to release the maximum amount of heat from the carbon charged. It was odd, indeed, to find that the use of sized ore and sinter in the careful tests reported by Dobscha had changed the CO/CO2 ratio very little. The author has stressed the close correlation between his corrected CO/CO, ratio and production. A correlation of fuel consumption and the CO/CO, might be more logical. Fuel consumption on the prepared ore burden decreased 15.3 pct whereas the corrected CO/CO2 ratio decreased 19.0 pct. Although this agreement between the reduction in fuel and the reduction in corrected CO/CO2 ratio is not as close as the correlation with tonnage, it indicates the corrected ratio is superior to the normal ratio which decreased less than 4 pct. Some adjustment should be made for the reaction: CO + H2O = CO2 + H2 —700Btu [41 because there is evidence to indicate that about one half of the hydrogen is formed in the upper 21 ft of

Jan 1, 1953

By M. Cohen, C. Wagner, J. E. Reynolds

If the total volume of a diffusion couple changes during the diffusion, the measurement of distance becomes ambiguous. Use of distance parameters as suggested by Hartley and Crank is discussed. For small concentration differences, the standard form of Fick&apos;s second law is retained with conventional length units and the in- terdiffusion coefficient D. It is shown how D can be calculated from experiments involving large concentration differences and analyzed in terms of distance parameters. &apos;The merits of incremental diffusion couples involving small concentration differences are emphasized. THE conventional form of Fick&apos;s second law for one-dimensional diffusion of component B in a binary solution of A and B is where c, is the concentration of component B; x, the distance; t, the time; and D, the interdiffusion coefficient which may depend on ca. Hartley and Crank&apos; have pointed out that Eq. 1 applies only if the total volume of the diffusion couple does not change during the diffusion process; otherwise, the definition of x becomes ambiguous. No change in total volume takes place if the specific volume of the solution is a linear function of the weight fraction Wb, or if the molar volume is a linear function of the mol fraction N. In some alloys, however, these relationships do not hold, and then it is necessary to introduce a modified measure of distance, 4 in order to retain the general form of Eq. 1. The application of Hartley and Crank&apos;s suggestions to diffusion in alloys has been discussed by Wagner.&apos; Relation Between Measure of Distance and Units of Concentration The definition of [ depends on the choice of units for the concentration c,, as follows: 1—If the concentration ca is measured as the weight fraction W, (or weight percent), [ = 5, has to be defined so that equal increments of contain equal increments of mass m of the solution, e.g., dm = pSdx = Sdw [2] where p is the local density of the solution, and S is the cross-sectional area in sq cm which is taken to be constant in this problem of one-dimensional diffusion." * da Silva and Mehla have demonstrated the constancy of the cross-sectional area in the usual type of diffusion couple. However, experiments involving diffusion into thin wires4, 5 may exhibit changes in cross-sectional area, and therefore are excluded from the present treatment. Thus and the unit of is gram per sq cm instead of cm. 2—If the concentration c, is the mol fraction N, must be defined so that equal increments of contain equal numbers of mols of solution, e.g., dn= (S/V)dx= Sd [41 where V is the local molar volume of the solution. Thus dt, = dx/V [51 and the unit of is mols per sq cm. 3—If, as may be advisable in the case of interstitial solutions, the concentration C is measured in terms of the molar ratio of components B and A (c,, = Y, = nH/nA, where n and nl are numbers of mols of B and A), = Y has to be defined so that equal increments of contain equal numbers of mols of A, e.g., dnA= (NAS/V)dx = Sdf [6]

Jan 1, 1954

By John S. Alexander

By Sidney Diamond, Charles Wert

The anelastic behavior of Ni-C alloys of nominal 0.5 wt pct C has been determined over a wide temperature range. The most prominent damping effect, that due to the presence of C-C pairs, was measured both above and below the Curie temperature. The effect on diffusion of the C-C pairs by magnetic spin ordering is deduced to be very small. The diffusion coefficient for C-C pairs in nickel is given by the expression ThE solid-state diffusion of both interstitial and sub-stitutional solutes in ferromagnetic solvents has been the subject of a number of investigations. Measurements of the self-diffusion of iron,"&apos; the diffusion of nickel1,4 gold,"1 and cobalt4 into iron, the diffusion of vanadium in an Fe-V alloy,&apos; and the diffusion of cobalt and nickel in Co-Ni alloys9 show an unusual behavior. In both the ferromagnetic and paramagnetic regions, far removed from the Curie temperature, the diffusion coefficient, D, obeys an Arrhenius relation. However, in the ferromagnetic region D is markedly lower than would be expected from an extrapolation of D from the paramagnetic region; this results in an increase in the activation energy in the ferromagnetic region. The cause of this effect for self- and substitutional diffusion is uncertain. Since substitutional diffusion is presumed to proceed by the vacancy mechanism, it has been variously suggested that the increase in activation energy below the Curie temperature is due to one of the following causes: 1) an increase in the energy of formation of a vacancy because of local demagnetization around the vacancy,2,3 2) a decrease in vacancy mobility in the ferromagnetic state,&apos; or 3) an effect on the entropy of motion of a vacancy in the ferromagnetic state.5 Quite another explanation for the observed effect has been proposed by Borg.7 The diffusion coefficient is a function of the elastic constants of a metal. Since the temperature dependence of the elastic constants often changes at the Curie temperature, the temperature dependence of D might be expected to undergo a universal change in the vicinity of the Curie temperature. The magnitude of the change in D would, of course, depend on the magnitude of the change in the elastic constants. One might attempt to differentiate between vacancy effects and elastic effects by making measurements on interstitial alloys, in which vacancy effects play no role. Some measurements of this type have been made; this paper reports additional observations. Measurements of the diffusion of carbon in a Fe by a tracer technique8 and of the diffusion of carbon in a Co and in Co-Fe alloys by a decarburization method9 reveal a small effect, if any, on D of the magnetic change at the Curie temperature. If the effect of spin ordering is only to alter the parameters controlling formation or mobility of a vacancy, interstitial diffusion should indeed remain unchanged through the magnetic transition, as these measurements imply.

Jan 1, 1968

By Joseph C. McCaskill

The writer assumes that this volume is not intended to serve as a source of statistics on international trade and that the reader is not interested in wading through a lot of statistical tables copied from the various reporting agencies. Generalizations therefore are made whenever possible and not always is the source of the information meticulously cited. The United Nations regularly publishes trade data on mineral commodities. E. J. Gealy, and C. L Kimbell, of the U S Bureau of Mines (USBM), work with these data and estimate that they cover approximately 78% of total mineral commodities traded. In addition the General Agreement on Tariffs and Trade (GATT) publishes analyses of certain trade data The most complete report of production and trade in minerals 1s probably the international volume of the U.S. Bureau of Mines Yearbook The latest available edition is for 1968, and some of the data in this edition cover only as late as 1967. Unless otherwise stated, the source of data used in the chapter is this Yearbook Other staff members of the Bureau were most helpful and cooperative They are not to be held responsible for conclusions or points of view to be found in the chapter. THE NATURE AND SCOPE OF INTERNATIONAL TRADE The two and a half decades since World War II have witnessed an unprecedented growth international commerce The end of the war found the world economy seriously crippled. Many countries had suffered severe war damage; international trade was disrupted and nations had to resort to exchange controls and bilateral trading arrangements. The postwar recovery, however, was remarkably rapid Within two decades, world Income more than doubled, and world trade which was less than $60 billion in 1948 exceeded $200 billion in 1968, 8 and reached $278 billion in 1970.18 The growing world trade contributed to world prosperity which in turn fostered growth of trade. This dramatic growth of international commerce was made possible by the progressive liberalization of trade and capital movements by the major trading nations of the world which began immediately after the War and has not yet completely lost its steam. The modern-day stimulus of the expanded trade movement was the enactment by the Congress of the United States in 1934, of the

Jan 1, 1976

By Yap Chu-Phay

IN 1923, when the writer began his studies in metallurgy, he came upon an article by Professor Honda on the, Equilibrium Diagram of the Iron-carbon System, 1 which made a profound impression on him. What interested him most was this sentence: "In the recent diagram of the iron-carbon system, the solidus is usually shown as a curve bending considerably downward. But it can be shown by thermodynamics that if the liquidus is straight or slightly curved, the same must also be true for the solidus. Hence, in my constitutional diagram, the lower portion of the solidus is slightly bent upward." Ever since then the writer has been interested in thermodynamics, especially chemical thermodynamics. The applications of thermo-dynamics to the metallic systems have been, in the writer&apos;s opinion, sadly neglected, although we continually use the phase rule in our study of equilibria in the liquid and solid states of metallic alloys. Many investigators, among whom may be mentioned Heycock and Neville, and s Honda and his coworkers, have applied the simple Raoult-van&apos;t Hoff law of depression of freezing point, mainly to determine the heat of fusion, but no attempt has been made to investigate the applicability of the thermo-dynamic laws of solution (as opposed to the laws of solution derived from other sources) to metallic systems" showing either limited or complete solid solutions. Perhaps the reason for this neglect is that until recently there have been so few reliable data on the solidus, which is much more difficult to determine than the liquidus. The writer has under way at the present time an investigation of a number of systems, the solidi of which have been more or less reliably determined. Recently, the writer has not only shown the valid applicability of the thermodynamic laws of solution as applied to the system antimony-bismuth but has also suggested a method of attacking problems involving complete and incomplete equilibria.2 In the present paper, the same method of approach is employed. For convenience, we shall divide this paper into two parts:

Jan 1, 1931