By S. S. Clarke

The sheet-ground deposits of the Tri-State district, because they are fairly uniform in thickness (7 to II ft.)—rather flat, with an easy dip to the west—and cover a large acreage, offered a problem of improved transportation. Heading advance in this kind of mine is very rapid and track haulage requires a larger crew of trackmen than do other mines, and a heavy investment in track. The use of some type of rubber-tired truck equipment for underground haulage was under consideration for some time by the Eagle-Picher Mining and Smelting Co. The nature of some ore bodies made them not adaptable to truck haulage and some mines that did offer possibilities were equipped with other types of haulage, and the expected savings by the use of trucks did not offset the loss of investment that would be incurred in discarding other equipment. The decision was made to sink a new shaft, designed for skip hoisting, on the Blue Goose ore body, and then develop truck equipment. Developing Tractors and Trailers A study was made of internal-combustion engines for power units in the tractors, but the extreme difficulty of controlling air circulation, and the heavy cost of drilling large churn drill holes for blower installations, led to the adoption of a tractor with a storage battery. The storage-battery tractor that was on the market for mine haulage was impossible to obtain because all were needed for defense work. Several standard electric-truck chassis were purchased and rebuilt in the Eagle-Picher shops. The steering wheel was shortened and set vertical, permitting the driver's seat to be moved forward, and the frame was shortened enough to take the battery box and the fifth wheel support that carried the gooseneck of the dump trailer. The fifth wheel, or turntable, is of the ball and socket type. Tig. I shows the ball fastened to the gooseneck. The socket is split to permit introduction of the ball and is held by through-bolts, and the socket is welded to a ½-in. plate, which in turn is attached to the tractor frame. Smaller wheels and tires were put on to reduce over-all height. If it had been necessary, the spring: could have been reversed, or taken off entirely, to gain additional clearance. The tractors are equipped with 48-cell, 23-plate, 400-A.H. batteries. With the initial tonnage and mileage, the batteries were about 50 per cent down at the end of a shift. Tractors have truck tires 7.50 by 20, 8-ply, front and rear, the rear being dud. After four months of use, the .tires are beginning to show signs of failure.* In

Jan 1, 1943

By Karl S. Kurtenacker

In attempting to find a rapid and economical means for solving many of the subsurface problems that confront the highway engineer, the author for the past two years has utilized a Megger Ground Tester on resistivity surveys in conjunction with highway construction. Electrical surveys in connection with highway work are largely shallow depth surveys, thus differing from most other types of resistivity work. Consequently, the readings are affected by a great many qualifying factors such as the density and moisture content of the media under observation and the amount of weathering and leaching. In most cases the surface layer is decidedly heterogeneous in character, and, because of the great number of side hill cuts, the second layer, which in most cases is rock overlain by some sort of surface soil, silt, or debris, seldom lies in a horizontal position. Shallow strata, lacking homogeneity and not lying in a horizontal position, do not lend themselves readily to accurate theoretical interpretations, therefore the author has used empirical rules to a large extent in interpreting depth soundings. The following empirical rules of interpretation are surprisingly adequate for highway work, since much of the work is in the nature of reconnaissance surveying and the results are construed to be approximations. The writer is careful not to risk interpretation on some special feature of the curve, since such features are usually due to random errors or lack of homogeneity among the subsurface strata. Effect of Surface Medium A resistivity depth sounding taken to a depth of 200 or 300 ft. is not much affected by superficial conditions, but these conditions have a great effect in depth soundings to 25 or 30 ft. In shallow soundings the character of the surface medium has a very marked effect on the entire resistivity graph. Fig. 1 illustrates a very striking example. Graphs A and B are depth soundings taken in approximately the same place. The surface stratum is a clay loam but at the place where graph B was taken

Jan 1, 1934

By Paul M. Tyler

The term "milling" as applied to nonmetallic minerals often refers merely to pulverizing without preliminary beneficiation. As applied to dimension stone, it embraces all the gteps involved in shaping and giving the desired finish to blocks. Processes such as sawing, planing, rubbing and polishing seem far removed from milling as the term is used in ore dressing, nevertheless they involve the element of concentration, for only 25 to 50 per cent of the gross quarry output may leave the mill as finished products after imperfect stone has been culled and the rough blocks trimmed. On the other hand, numerous nonmetallic minerals have to be concentrated in much the same manner as low-grade ores. Engineers and machinery manufacturers have begun to recognize more clearly the opportunities awaiting them in the nonmetallic field and have brought with them the methods and equipment developed in metal-mining camps, occasionally with little modification. General Economic Considerations Approximately one-half of the total value of the mineral production of the United States represents mineral fuels, and the other half is about equally divided between metals and nonmetals, the nonmetals recently having become relatively more important. In terms of volume the domestic output of nonmetallic minerals other than fuels is more than 10 times the annual output of metals. Considered on the basis of industrial utility and general commercial and military significance, moreover, the flow of nonmetallic mineral products is quite as needful to our national integrity and well-being as is that of metals, fuels, or other basic materials. Despite their importance individually and as a group, the nonmetallic mineral industries differ so widely in essential characters and economic environment that producers thereof have been slow to develop a community of interest among themselves or with the metal-mining fraternity. A spirit of change is in the air, rule-of-thumb methods soon may be relegated to limbo, and new methods—especially time-tested ideas borrowed from ore-dressing practice—are being introduced. A faithful record of plant practice in certain of these fields, however, must register

Jan 1, 1935

By Dae S. Young

A new probabilistic approach is introduced for slope stability analysis including adverse impact of blasting vibrations. The material strength within a slope area is randomized in this bi-variate joint probability analysis. To be a completely general engineering method, the new probabilistic approach employs the random variable transformation technique: the Hermite model of the Gaussian transformation function, which transforms the experimental histogram of strength values to the standard Gaussian variables. Because bi- normal joint probability is analyzed on the true probability region projected on the Gaussian transformed variable plane, it is an exact solution of slope stability based on the available sample data. Details of the probabilistic approach are given through a case study on an iron ore mine. The case study demonstrated that the probabilistic approach is effective and simple enough to be a routine engineering practice for slope analysis.

Jan 1, 1984

By Charles White Merrill, James W. Pennington

No metallurgical process developed in the 20th century compares with froth flotation in its effect on the mineral industry. Processes like gravity - concentration, amalgamation, and pyrometallurgical reduction are of ancient origin; others like cyanidation and electrolytic reduction were well established by 1900. Such metallurgical processes as heavy-media separation, ion-exchange, and solvent extraction belong to this century, but their influence is small compared with froth flotation. Data collected by the U. S. Bureau of Mines* in a canvass of 202 froth flotation plants reveal that, in 1960, 198- million tons of material was treated to recover 20-million tons of concentrates which contained approximately $1 billion in recoverable products. SIGNIFICANCE OF FLOTATION Froth flotation as described in this chapter refers to a wet process for separating properly ground mineral particles into two or more products. It involves the separation of mineral particles from each other in a liquid pulp by means of air bubbles. Finely crushed ore is agitated in water with the addition of air or other gases. Various chemicals and oils are added to cause the selected mineral particles to attach themselves to the air or gas bubbles. These bubbles, carrying the mineral particles, rise to the surface where they are removed in a froth, while the other particles remain suspended in the pulp. The earliest flotation divided the raw material into two products: a bulk concentrate that was removed as a froth and a tailing that remained in the flotation machine. The froth usually contained the valuable constituents. The successful application of such a process depended on the recovery of a single concentrate from which one or more valuable constituents could be recovered by a chemical or smelting process. With the advance of the art, however, the principle of selective flotation, by which two or more relatively pure products could be recovered from complex raw materials, was evolved. Other chapters in this volume describe the developments during the last 50

Jan 1, 1962

By Albert F. Hill

The manufacture of structural shapes in steel of uniform quality, which shall command the full confidence of the engineer, is a problem in practical metallurgy which is beginning to attract much attention in this country. The progress of the past fern years in the improvement of plant and processes has placed it within the power of the steel-maker to supply a material of such chemical composition as will meet the requirements; but this solves only in part the difficulties of the constractor. It is well understood that the influence of shop manipulations is a most decisive one upon the mechanical properties of the finished product; in many cases so great, in fact, as to cause an entire transformation in the character of the material, and to render it unfit for the service for which it was intended. On the other hand, mechanical treatment is frequently resorted to as an efficient corrective of certain undesirable properties, which may be due either to chemical composition or previous manipulation. This understood and accepted, it is evident that careful investigation of the effects of mechanical treatment is fully as necessary to the successful use of steel in engineering structures, as the investigation of the influence exerted by its chemical composition. All structural material has to undergo more or less mechanical treatment, such as shearing, punching, upsetting, etc. Each of these operations produces effects which are far more marked and decisive in steel than they are in iron, and means must therefore be adopted to counteract, or at least to modify, these effects before the material is permitted to enter the structure. The fact that both shearing and punching affect the tenacity and elasticity of steel has long been recognized; bat, through more recent investigations, it has been established that these effects are purely local, and are therefore susceptible of correction by other and simpler means than annealing. The importance of this discovery to the use of steel in structures is very great. The impracticability of

Jan 1, 1883

By R. D. Mollison, C. F. Fogarty

Sulfur is widely distributed in nature. It is present in the earth's crust, the ocean, the meteorites that come to us from cosmic space and in practically all animal and plant life. According to Clarke,9 the earth's crust contains 0.06 pct sulfur. Large quantities of free or combined sulfur are found in coal, natural gas and petroleum. Mineral waters contain sulfates and hydrogen sulfide. Sulfur is rather plentiful in the crust of the earth; however, only under special circumstances can it be produced profitably. Sulfur is one of the cheapest raw materials used by industry; and, therefore, the economic feasibility of a given deposit is strongly dictated by the law of supply and demand on local as well as world-wide levels. The forms which are commercially important are elemental sulfur or brimstone, and the sulfides such as pyrite (FeS2), pyrrhotite (FenSn+1), chalcocite (Cu2S), sphalerite (ZnS), and galena (PbS); the sulfates such as gypsum (CaSO4,2H2O), anhydrite (CaSO4), and kieserite (MgSO4,H2O). Elemental Sulfur Elemental sulfur is found in many localities, generally in solfataras and gypsum type deposits. The solfatara deposits are found commonly in the neighborhood of active or extinct volcanoes as in Italy, Japan and Chile, or fumaroles associated with mineral springs such as the Mammoth Hot Springs in Yellowstone Park. Here the sulfur is deposited in tufas or other porous host rocks. This type of sulfur deposit probably results from the oxidation of hydrogen sulfide or the reaction of hydrogen sulfide with sulfur dioxide. Most of the world's supply of elemental sulfur comes from the gypsum-type deposits. Here the mineral occurs as either crystalline or amorphous sulfur in sedimentary rocks in close association with gypsum and limestone. This association is characteristic and occurs in almost all the great gypsum beds of the world, although sulfur is not always present in quantities of economic importance. Various theories have been advanced to account for this association. Bischof5 suggested that the sulfur came from hydrogen sulfide which resulted from the reduction of calcium sulfate by carbon or methane in accordance with the following reactions: CaSO4 + 2C= CaS + 2CO2 CaS + C02+ H2O = CaCO3 + H2S CaSO4 + CH4= CaS + C02+ 2H20 2H2S + 02= 2H20 + 2S All of the sulfur-bearing domes on the Gulf Coast have calcium sulfate in great quantity in the cap. They all show the presence of hydrocarbons. The oxygen for the final reaction could have been supplied by circulating ground waters. The principal objection to this theory is that temperatures of 700° to 1000°C are needed to reduce the sulfate to sulfide with carbon compounds. The geologic evidence is that the temperature of the sulfur-bearing domes of Texas did not exceed 100°C. Proponents of the theory say that geologic time or a catalyst replaced temperature. According to another theory the sulfur in the salt domes is the result of bacterial action. Sulfate reducing bacteria have been detected in sulfur cores and in the formation water issuing from salt domes. It has, therefore, been suggested that these bacteria converted the sulfate to sulfide which subsequently was converted to elemental sulfur.

Jan 1, 1960

By W. Philippoff

ALTHOUGH Gaudin1 and more recently Sutherland2 have calculated the probability of collision of a falling mineral particle with a rising bubble, there is no published information concerning the details of the mechanism of attachment of a collector-coated particle to a bubble. During the past year the writer has developed a theory for the mechanism of attachment, which has been substantiated experimentally.' Funds for the investigation and for some of the equipment used have been supplied by the Mines Experiment Station of the University of Minnesota. Motion picture studies of the phenomena involved in the collision between mineral particles and bubbles, such as those of Spedden and Hannan,3 show that the contact can be completed within 0.3 millisec. Formulas developed for rigid bodies have hitherto been used' for the calculation of the motion of bubble and particle, but it is obvious that a bubble cannot be regarded as a rigid body. On the contrary, Spedden and Hannan's pictures show a great degree of deformation during the collision. The time of attachment was calculated as the time the particle drifted past the bubble. Time of Collision The theory presented in this paper enables calculation of the time of collision; using the concept that the bubble, or more generally, a liquid-air interface, acts as an elastic body. The elasticity, defined as the restoring force on a mechanical deformation, is caused by, the surface tension and is the result of the principle of the minimum of free surface energy. It is well known that an elasticity together with a mass determines a frequency of vibration. The vibrations of jets and drops caused by the elasticity of the interface are known to comply exactly with the classical theory of capillarity.5 However, the vibrations of isolated bubbles, as distinct from foams, have not been investigated previously. The following equation, presented elsewhere,' has been deduced for these frequencies: [3fB = 9.20•'./V•Vn- (n-1) • (n+2) /8[1]] in which fB is the frequency of a harmonic of the bubble in cycles per second, V the volume of the bubble in cc, n a number determining the order of the harmonic, and n = 2 the basic vibration. The first (basic) harmonic describes a change of the spherical bubble to an ellipsoidal bubble. The higher harmonics are more complicated, for the circumference of the bubble is divided approximately into as many parts' as the order of the harmonic. As an example, Spedden and Hannan's published motion picture of, a vibrating bubble corresponds to the sixth harmonic. Eq 1 shows that only the first and third harmonics are simple multiples (1 and 3), all the others being irrational fractions of the basic frequency. This means that the shape of the vibration can change with time and is in general unsymmetric in respect to the time axis. Such conditions prevail when there is a distributed elasticity or mass, as in the case of vibrating membranes or rods. The constant 9.20 is valid for water at room temperature, but a general solution involving the physical constants of the liquid has not been found. The case of the floating particle is much easier to treat I than that of the bubble. It can be assumed that the elasticity is caused exclusively by the interface and that the mass is concentrated in the particle together with some adhering water. The following expression for the frequency of a system, of one degree of freedom can be applied: [1E/m[2] fP = 27] Here f, is the frequency of the particle vibration in cycles per second, E the elasticity in dynes per cm, and m the mass in grams. The classical theory of impact phenomena gives the time of collision during the striking of a spring (in this case the surface of the bubble) by a mass, as: [t~ = 2/f = 7r\/m/E[3]] It is now possible to develop an expression for the elasticity of a floating cylindrical particle. The force equilibrium of a cylinder floating end on at the air-liquid interface is given by the well-known equation (Poisson' 1831) [aP = 4 D2.pL•g•h +7rD•y sin a[4]] which accounts for the buoyancy and the action of the surface tension where P is the force acting on the particle in dynes (weight-buoyancy), D the diameter of the cylinder in cm, pL the density of the liquid in grams per cc, g the acceleration of gravity = 981 cm per sec2, h the depression of the cylinder below the surface of-the liquid in cm, y the surface tension in dynes per cm and a the supporting angle' or the one required to insure equilibrium, a being smaller than the contact angle ?. Although demonstrated by Poisson, it has not

Jan 1, 1952

By W. P. Sykes

In connection with a study of tungsten steels, Honda and Murakamil reported an investigation of the system iron-tungsten. This report included a tentative equilibrium diagram, photomicrographs of various alloys in the series, and qualitative measurements of hardness and magnetic properties. The present investigation originally had as its object the study of the hardness and tensile properties of a series of carbon-free iron-tungsten alloys. But, as the work progressed it became evident that the system possessed other features of interest, so the scope of the investigation was enlarged. Materials The iron powder used in preparing the alloys was obtained as follows : Iron oxalate was precipitated from a ferrous-sulfate solution by the addition of a solution of oxalic acid. This oxalate, after thorough washing, was ignited to iron oxide, which after reduction in hydrogen at about 1000" C. yielded iron powder containing but about 0.2 per cent. iron oxide and about 0.005 per cent. carbon. Tungsten metal in the form of powder, such as is used in the manufacture of filaments for incandescent lamps, was the other constituent. This material analyzed 99.8 per cent. tungsten and contained no carbon. The metal powders, in the desired proportions, were mixed by tumbling and formed, under pressure of 20 tons per sq. in., into rods 3/8 by 3/8 by 10 in. To form the alloys without contamination, sections of the pressed rods were placed on alundum slabs and heated in an alundum tube wound with a tungsten resistor and packed in heat-insulating material. While the resistor was heated, a stream of hydrogen was continually passed through both the tube and the case containing it. The tungsten winding on the tube, as well as the material heated within the tube, was thus protected from oxidation. Such a furnace will operate constantly for several days at temperatures up to 1500' C. and for shorter periods

Jan 1, 1926

By S. B. Casey

[ ] IN 1880, an electric arc was struck over metal for the first time to experiment with controllable melting. The glare of this arc has reflected on the stacks of the steel industry and continued to light the path of steelmakers in their never ending quest -for faster, more economical, and better ways of producing steel. William Siemens is credited with first employing the electric arc to melt metal in a closed hearth and produce basic metallurgical reactions. By the turn of the century, an Italian, named Stassano, was experimenting with ore reduction by the electric arc. In 1899, Dr. Paul Heroult, in France, used the direct arc principle for producing ferro-chromium. His experiments quickly led him to develop a dosed-top arc furnace for the production of steel, and his first commercial shipment was recorded in December, 1900. American steelmakers, quick to sense the possibilities of this method of melting, invited Heroult to our shores, where, in 1905, he was responsible for installing the first arc furnace on the North American continent. This furnace, at Sault Ste. Marie, was built for ore reduction. But Charles Holcomb, founder of Holcomb Steel. Co. of Syracuse, N. Y. contacted Heroult in 1905 and contracted for the first American direct-arc electric furnace for steelmaking. On April 5, 1906, the first heat was tapped from this 3-ton unit. The furnace was basic lined and powered by a single-phase, 500 kw generator, -producing high amperage at low voltage. It is interesting to note that, although the first few heats were made with cold charges, subsequent heats were duplexed. R. H. Bully, first superintendent of Holcomb Steel, persuaded the directors to purchase the unit to effect a more economical and efficient means of making tool steel by duplexing prime melting in a combustion fired furnace, and transfer of hot metal to the arc furnace for temperature adjusting, refining, and adding carbon and alloying elements. Today, duplexing is foreseen by some as the steelmaking process of the future. The promise shown by America's first arc furnace for ingot production quickly led to the purchase of a similar unit by The Firth Sterling Steel Co., in 1909, and to the purchase of the first arc furnace for production of steel castings, by the Treadwell Engineering Co., in 1911. From its humble start in 1906, production of arc furnace steel has never ceased to increase its yearly percentage of total steel production in the U. S., although certain other methods have declined or almost disappeared. By its ability to be used intermittently, the arc furnace gained favor and enhanced its reputation during depression days. When the attack on Pearl Harbor plunged us headlong into the long days of World War II, the arc furnace stood ready, flexible enough to be overburdened hearth wise 30 pct and power wise 25 pct, pouring its endless flood of alloy for the guns, tanks, ships, and planes which ultimately brought victory. During the post war boom, the now, proven virtues of low initial cost, faster installation, better yield, improved availability, and lower operating cost, enabled industry-particularly the small, new, independent producers-to locate strategically and profitably to meet the demand of an America that had been starved for new homes, appliances, cars, and highways. In the Korean police action, the arc furnace again proved itself by providing the latest alloys metallurgists could develop to meet the demands that the jet age and the innovations of guided missiles required. In today's peacetime prosperity, the arc furnace is continuing to provide the economic flexibility required to meet an ever increasing demand for better steel in the face of mounting costs, scrap shortages, and pressure toward decentralized location of industry.

Jan 1, 1961

By John Norton

THE tremendous increase in the use of metals that have been prepared by the various cold-working processes during recent years has greatly stimulated the investigation of problems concerned with the fundamental nature of these processes. It has been observed in practice that different methods of bringing about the same dimension changes in a sample result in a rather wide range of properties. Cold working reduces the ductility of a metal, or what is perhaps more nearly correct, its "working capacity," and naturally the manufacturer wishes to produce an article that has as large a working capacity as possible, and to produce it with the smallest number of operations, It has also been known for some time that cold deformation produces a parallel alignment of the crystal grains of a metal, and that the type of this preferred orientation depends to some extent at least upon particular processes employed in the deformation. The present investigation has for its purpose the study of the relations between the various factors of a cold-working process and the preferred orientation of the metal crystals resulting from this deformation. The work is chiefly confined to a study of cold-drawn seamless tubing.

Jan 1, 1932

By C. W. Mac Gregor

THE observation of the flow layers, or Lüders' lines, produced in mild steel when it is stressed into the plastic range often provides considerable useful information for the study of the fundamental mechanism of the plastic flow of metals. It is a commonly observed fact that as soon as the upper yield point in a mild-steel tensile-test bar is passed, an unstable condition develops in the equilibrium, the load on the testing machine drops and if the surface of the bar contains a thin mill scale, the latter begins to flake off rapidly along certain "lines." These "lines" are in reality traces of wedge-shaped flow layers and are formed by the inter-section of the surface of slip and the surface of the bar. The average plane of the flow layer itself has been found by various experimenters to be inclined at an angle of approximately 45° to the axis of the test bar. In a body of more complicated shape stressed in possibly a different man-ner, the tangent planes to the flow layers at each point seem in many cases to be inclined at an angle of about 45° to the principal stress direc-tions at the point. As examples of the latter may be mentioned the logarithmic spirals obtained when a rivet hole is punched in a thin plate, or when a tube is subjected to internal pressure only, etc. Hence if the flow layers are observed from an experiment, the shear-stress trajectories -the curves indicating the directions of the maximum shearing stresses in the body-may then be approximately determined. Since the latter curves form an orthogonal family inclined at 45° to the principal stress directions, the family of principal stress trajectories, or the curves indicating the directions of the principal stresses, may be thus obtained. Although the discontinuous type of stress-strain curve at the yield point is commonly observed with test bars of mild steel, more recent experiments have shown that this is by no means the only material exhibiting this interesting phenomenon. A similar effect has been observed in zinc and cadmium crystals, by Becker and Orowan;1 in duralumin and other aluminum alloys, by Dawidenkow, 2 Elm,3 Fell, and others; in copper and copper-alloy crystals, by Elam;5 in brass by Elam;5 in brass wires by deForest;6 in higher carbon steels, tungsten steel, and

Jan 1, 1939

By J. L. Shafer, Christopher L. Caenepeel, Martha L. White

Often an in situ leach is the only practical economic method for copper recovery from small low grade oxide deposits. The decision to develop a copper property by an in situ blast and leach is strongly dependent on ore grade, tonnage, hydrology, and the copper extraction and acid consumption rates. The inherent leachability of the ore will in part determine the desired amount of fracturing of the ore deposit by the blast in order to obtain a copper extraction rate that is economical. For the last several years Occidental Research Corp. (ORC), has undertaken a modest effort to address the question of how to best identify and determine the information necessary to predict and control the operation of an in situ leach for the economic recovery of copper. Modelling of the Leaching Process During the past 10 years the activity in the mathematical modelling of the leaching of copper sulfides in copper dumps and heaps has increased dramatically. The modelling of copper oxide leaching has not received as much attention. The acid leaching of non-sulfide copper minerals while chemically less complex, compared to sulfides, does generate a vertical acid concentration gradient in the ore heap being leached due to the acid-base nature of the reaction. This is generally not observed in sulfide deposits that are biologically active, due to the buffering action of opposing reactions involving the generation of sulfuric acid from sulfide minerals and acid consuming host rock. Thus, the objective of ORC 's copper oxide modelling efforts is to determine the leaching parameters which will account for this vertical acid concentration gradient. Knowledge of this gradient will result in the correct choice of the feed acid concentration to the top of the ore dump or heap, such that the effluent will have the desired pH.

Jan 1, 1980

By J. A. Herbst

During the last decade it has been established that conventional mineral-processing control strategies based on classical control theory result in significant increases in plant throughput and operating-cost savings. It has, however, also been recognized that conventional strategies have important limitations for complex multivariable mineral-processing systems. These limitations center around the fact that single-input/single- output control linkings often result in highly undesirable interactions between controllers. During the last few years new and promising approaches to solving this problem have emerged. These approaches are based on the use of on-line dynamic models to make predictions which are useful for control decision-making. This paper presents a brief summary of the state-of-the-art for mineral-processing control in 1984. This summary is followed by a review of recent developments in model-based control strategies including those in optimal control, self- tuning regulators and decoupling control. Expected trends for the future in the control of mineral-processing operations are discussed.

Jan 1, 1984

By J. Grosso, D. J. Nagel

In many metallurgical studies, it is necessary to reveal the composition and structural properties of materials. Usually this is done by etching, but some substances do not etch well or easily. Anodizing is known to provide an alternate treatment in many cases. In general, this technique is simple, often more sensitive to composition differences than etching, has excellent resolution, and provides variable contrast in those elements and alloys which anodize. Here we report the use of anodizing in diffusion studies in the TiCb system. Fig. 1 shows a cross section of the diffusion zone in a TiCb couple. The anodizing has clearly revealed both composition and crystallographic features. The maximum bulk penetration of the titanium into the columbium is marked by a sharp line because of the steep concentration gradient. The titanium grain size and orientation differences are also evident. Variation in the grain size reflects the gradually decreasing columbium concentration.

Jan 1, 1967

By W. H. Furlonge

WHILE fulfilling professional engagements, my travels over this portion of the Transvaal have been quite extensive—always on horseback however, so that anything like a thorough investigation of the ground passed over has been necessarily impossible; still, the more minute examination of certain small areas, coupled with general observations, has enabled me to form some idea as to the prominent geological features of the country as a whole. Anything like a complete or comprehensive description is indeed out of the question, as there are no proper maps of the country and the facilities for observation are limited. A large plateau, called the "High Veldt," stretches from east to west across the Transvaal. It is generally level, or gently rolling, and has an average elevation of 6000 feet above the sea; it is destitute of timber, and in fact greatly resembles the western prairies of North America. Rock-outcrops are not common in it. It terminates very abruptly to the east and northeast, the descent of 2000 or 3000 feet into the mountainous country that occupies its borders being made in a

Jan 1, 1890

By H. A. Tobelmann

age Introduction ............................. 22 Crushing............................... 25 Leaching............................... 28 .Reduction.............................. 47 Electrolytic Deposition..............a.......... 51 Discard for Purification of Electrolyte.................. 60 Recovery of Copper from Discard Solution .............. 62 Resolution of Cement Copper...................... 64 Summary............................... 64 Appendix............................... 66 Discussion............................... 69 Introduction The location, mode of occurrence of ore, and preliminary tests leading to the development of the present leaching process and the building of the present plant on the property of the New Cornelia Copper Co. at Ajo, have been described in previous papers presented to the Institute and in the discussions thereof.l It is sufficient to say that these tests began early in July, 1912, and were continued to the close of January, 1916; that small tests at Douglas were followed by the construction of a 1-ton plant at the mine; and this was followed by the operation of a 40-ton plant for 11 mo. In all about 15,000 T. of ore were treated experiment-

Jan 1, 1919

By W. F. Mullen, C. W. Stickler

WITH few exceptions, unit operations in the Pennsylvania slate industry in 1950 did not differ appreciably from production methods described by Behrel and Bowles2-4 several decades ago. Many traditionally picturesque but relatively inefficient hand operations continued to contribute to high operating costs in an industry in which the margin of profit, for various reasons, was admittedly low. As part of a general program in which the Pennsylvania State College has been assisting the slate industry to solve some of its problems, time and method studies were used in an effort to determine the bottlenecks of production flow. The results are as applicable to other stone industries as they are to slate. A study of the basic elements in the production of roofing slate, structural slate, and slate blackboards among selected slate producers revealed comparatively few refinements. Any marked difference in operating method was characterized largely by the available equipment, a noticeable difference in the working properties of the rock quarried by a particular company, and by either the habit thinking or ingenuity of the individual operators. With the hope that significant economies in manufacture might result, all the unit operations were broken down into elements for study and analysis. The greater part of the study encompassed those operations from the quarry rim to the finished product; however, to obtain a reasonable synthesis of time allotments per operation, several analyses of quarrying from the finish of the wire saw cut are included for reference. The complete study of quarrying made by Bowles several years ago resulted in the introduction of the wire saw into the operation; there appears to be a need for as fundamental a change in the processing of finished slate as the wire saw was in the quarrying process. Fig. 1 illustrates the flowsheet of quarried rock from the parent bed to the quarry rim with the basic elements which contribute to the difficulty of removing slate from the ground. In Pennsylvania roofing slate is produced by one of three procedures, many operations of which are quite similar. In the traditional or classical method the quarried rock is reduced by sculping and auxiliary manual treatment to workable size and then is split and dressed (trimmed to size) in the conventional shanty. Archaic as this method might appear, there are several elements that result in substantial savings over more mechanized operations. In a modified version of this method, the block is reduced by sawing and gouging preparatory to splitting and dressing in indoor stations. This method is particularly adaptable to rock which fractures unevenly by conventional sculping methods. In the third and more modern method, reduced block received from the block maker is diamond-sawed to length and finished on a production line. Fig. 2 illustrates the flow pattern in each case. In the modified and more modern plans, dressing is done on mechanically-operated trimming machines, which appreciably reduce the fatigue factor of the operator. However, it should be noted that it is advantageous for the operator to be able to control the speed of the knife to prevent breakage of certain classes of stock. In the classical plan the splitter and dresser normally act as blockmakers also and carry their eighter slabs (equivalent in thickness to eight shingles) into the shanties themselves, all of which adds to fatigue and reduced efficiency. The extremely low investment and operating expense of the classical method has undoubtedly been of paramount importance in its continuation. Production of Mill Stock The production of mill stock is accomplished by less picturesque methods than enter into the production of roofing slate but it is, in the main, relatively more efficient because of the increased use of machinery for handling and for finishing. Mill stock can be classified into two categories as far as difference in production method is concerned: structural slate and blackboards. The significant difference in operation is caused largely by the nature of the rock used for each product with the best and easiest cleaved rock being reserved for blackboards to permit the splitting of large slabs to as little as 1/2 in. in thickness. Structural stock, on the other hand, is split into panels no thinner than 11/2 in. and

Jan 1, 1952

By Robert Henderson

SEVERAL very interesting articles have been written on the caving system of mining, but most of these papers have dealt separately with the slusher system or the chute and grizzly system. In this paper, a comparison will be made of the two methods, both of which are being used at the Climax mine. The mine is on the Continental Divide, in central Colorado, at an altitude of approximately 11,500 ft. above sea level. The long, cold winters, characteristic of the high Rockies, create a number of operating problems not usually found in other mining areas. THE ORE BODY The Climax ore body is just east of the Mosquito fault. This structural deformation has brought the granite on the east against the sedimentary rocks on the west. The ore occurs in an intensely altered granite and schist around a silicified granite core. The ore is in a highly fractured zone of moderate silicification. The principal mineral, molybdenite, is found in these fractures. Barren dikes of granite porphyry cut through the ore body and core with no apparent regularity. The grade of the ore is fairly uniform and gradually decreases toward the footwall core and also into the hanging-wall granite. The footwall and hanging wall are determined entirely by assays. The ore body is roughly dome-shaped, with the apex truncated at the surface. It is covered to varying depths with talus. A horizontal section of the ore body on the Phillipson level appears as an annular ellipse surrounding the footwall core. The ring of ore varies in width from 300 ft. to as much as 800 ft. The north-south axis of the core is about 1200 ft. and the east-west axis is about 1800 ft. In the ore zone, the rock is sufficiently strong to maintain reasonably large openings, and openings larger than haulage drifts usually have to be supported. The ore is cut by a great many fractures and shears and breaks into rather large blocks when caved, necessitating considerable secondary blasting. The waste that overlies the ore body breaks relatively fine in comparison with the size of the blocks of the caved ore and tends to run through the broken ore in the cave, causing dilution unless the draw is carefully controlled. MINING SYSTEMS For several years the ore was mined by the chute and grizzly system, a system that differs from that used in other caving mines only in the size of openings and equipment. In the chute and grizzly system, main haulage laterals were driven along the footwall core and also along the

Jan 1, 1944

By John W. Wagner, Robert K. Willardson

Single crystals of Pbl-xSnXTe have been grown from The melt under liquid B2O3 using the Czochralski technique. The PbTe-SnTe crystals were grown from near-stoichiometric melts and from melts with slight deviations from sloichiometry. Crystal growth rates ranging from 1 mm per hr to 1 cm per hr were employed, the latter being generally used. Several investigations were performed to characterize the single crystals grown In this study. The phase diagram of the PbTe-SnTe system was examined. X-ray analyses verified the single-crystal character of the crystals, and powder pattern lattice parameter determinations showed that Vegard's law was followed within the limits of the experimental error. The as-grown crystals were p-type with apparent carrier concentrations of -8 x 1018 to -8 x 1020 carriers per cu cm. Hall coefficients, resistivities, and carrier mobilities were determined as a function of composition. Dislocations were revealed by an electrolytic etch, and the crystals were found typically to contain 2 to 4 x 105 dislocations per sq cm. Microhardness measurements were performed; no maximum in the Vickers hardness us composition curve was seen. Mass spectrometry was used for impurity analyses, and the crystals were found to contain 1 to 2 x 1017 total p-type impurities per cubic centimeter. Distribution coefficients were calculated for the major impurities which were Na, Mg, Al, Si, Cl, and Zn. RECENTLY interest has been stimulated in the preparation and characterization of many alloys of the binary compound semiconductors. This interest is due primarily to the almost unlimited possibilities of adjusting the semiconducting characteristics of these materials by varying the alloy compositions. One alloy system which has been receiving extensive investigation is the PbTe-SnTe system, since these alloys show promise of being useful as emitters and detectors of electromagnetic radiation in the spectral range of 8 to 14 µ. This paper reports on the growth of PbTe-SnTe single crystals by the Czochralski technique and investigations of the general properties of these crystals. The phase diagram of the PbTe-SnTe system was investigated so that specific alloy compositions could be attained. I) CRYSTAL GROWTH The PbTe-SnTe single crystals were pulled from the melt using the Czochralski technique. Generally, the crystals were grown from near-stoichiometric melts, although special growth runs were made from both lead-rich and tellurium-rich melts. Growth of single crystals from up to 5 pct lead-rich melts presented no problems; however, melts with tellurium in excess of -1 pct caused volatilization problems which generally made crystal growth impossible. All melts were prepared from high-purity materials as follows: 1) lead— 6 N— Cominco (Cominco Products, Inc., Spokane, Wash.); 2) tin—5N—Cominco; and 3) tellurium— 5N+— American Smelting & Refining Co., Plainfield, N.J. No further purification of materials was undertaken in this study. The elements were reacted at -1000°C in a vacuum-sealed silica tube for a few hours, a gentle rocking action being used to ensure thorough reaction. The cast ingots were then transferred to a silica crucible for crystal growth. A schematic diagram of the growth apparatus is shown in Fig. 1. The Vycor tube is sealed at both ends by O-ring flanges so that a vacuum or a positive pressure may be maintained in the growth chamber. The pull rod and crucible may be rotated; all crystals produced in this study were grown with the crucible sta-

Jan 1, 1969