Search Documents

By M. F. Smith

BELOW the nose of the bainitic C curves in isothermal transformation diagrams, the rate of the austenite-to-bainite transformation usually decreases with decreasing temperature. However, in some steels and iron-carbon alloys, there is a noticeable acceleration in the initial reaction rate at temperatures just above Ms. Such speeding-up of the bainitic transformation would be understandable at temperatures just below Ms because of the catalytic effect of the martensite formed,' but the reversal in isothermal kinetics just above Ms seems quite anomalous. This behavior was observed by Howard and Cohen' in a 1.35 pct C steel and, on the basis of metallo-graphic examination, it was attributed to the formation of a thin plate-like product not belonging in the bainitic sequence. More recently, schaaber2 found two-stage reactions occurring in the vicinity of Ms in a number of steels, and suggested that the first stage might be the isothermal formation of marten-site, preceding the isothermal formation of bainite in the second stage. A decrease in the bainitic incu-

Jan 1, 1960

AN intermetallic compound, Ni3A1, has an ordered fcc structure of type Ll2, and shows peculiar dependence of the yield stress upon temperature; i.e., the yield stress increases by a factor of six upon raising the temperature from 77" to 900K1, 2 This compound is technologically important, since many nickel-base superalloys owe their high-temperature strength to the peculiar yield stress behavior of Ni3Al. The only study of the elastic behavior of this compound was made by Davies and Stoloff,1 who determined Young's modulus of poly crystalline Ni3A1 between 300" and 730°K. The determination of single-crystal elastic constants of Ni3A1 is therefore of interest in connection with dislocation dynamics and is reported in this paper. A single-crystal specimen, 1 by 1 by 3 cm, was cut from an ingot generously supplied by Dr. B. H. Kear of Pratt & Whitney Aircraft. Following initial machining with a Servomet and a surface grinder, the specimen was etched and annealed at 1100°C for 5 hr in vacuum followed by furnace cooling. Two parallel faces were oriented normal to within ±l deg of a [I101 crystallographic axis by the back-reflection Laue technique. The parallel faces were hand-lapped, etched, and polished by the usual metallographic procedures. Final thickness along the [I101 axis was (0.9325 * 0.0005) cm. Chemical analysis gave an average composition of 87.35 pct Ni. Total impurity content is esimated to be no more than 0.1 pct. The elastic constants were calculated from measurements of ultrasonic waves which were propagated along the [110] axis. A longitudinal wave and two shear waves whose displacements are aligned along the [ 110], [li~], and [001] directions, respectively, are necessary in order to completely specify the three elastic constants. Two 3/6-in. quartz transducers were bonded to the parallel faces of the sample with ~ac-seal.3 Although this bond was sensitive to thermal shock, it performed satisfactorily over the entire temperature range for both longitudinal and shear wave propagation. A frequency of 5 mHz was employed in the method of Williams and Lamb4 in order to measure the absolute value of the ultrasonic velocity. The pulse-overlap technique of Mcskimin5 was also used at this frequency in order to determine the shift in the ultrasonic velocity

Jan 1, 1970

By L. Ekstrom, J. P. Dismukes

The homogeneity and microstrcture of zone-leveled Ge-Si alloys haw been investigated by sellera1 physical techniques and by metallography as a function of growth rate in the range 3 x 10 1x10 cm-sec', and as a system of alloy composition throughout the system. The temperature gradient at the solid-liquid interface was about 50 deg-cm-' Cellular or dendritic structures char-acteristic of constitutional supercooling were ob-served except at very slow growth rates, which ranged from about 2 x 10 cm -sec for Ge 1 sio alloy to about 2 X 10'5 cm-sec'1 for Ge .sSio.s alloy. Using a simple model similiar to that employed for dilute solid the dependence upon compo-sition over the entire system of the critical growth rate for the onset of constiutional supercooling was calculated, and was .found to he in good agreement with the experimental results. THE recent discovery of the low thermal conductivity of Ge-Si alloys' at high temperatures has revealed that these alloys have high efficiencies for thermoelectric-power generation.', Therefore, a reliable method was needed for the preparation of homogeneous samples required for definitive measurements throughout this alloy system. Due to the low diffusion rates in the solid alloys, the segregated samples obtained by quenching a melt are not readily homogenized by annealing.475 However. isothermal solidification from a melt of constant composition can produce uniform material. Of the available semiconductor crystal-growth procedures, the zone-leveling technique6 applied to a complete solid-solution alloy system by Wang and Alexander' and by others provides a simple method of doing this. In the present work, the homogeneity and microstructure of zone-leveled alloys have been correlated with growth conditions, and the conditions for preparing homogeneous Ge-Si alloys have been established. This has provided insight into the solidification process of alloy semiconductors. EXPERIMENTAL PROCEDURE Sample Preparation. The Ge-Si alloy phase diagram4 shown in Fig. l(a) consists of a complete series of solid solutions. The zone-leveling technique used to prepare most of the samples consists of moving a zone of liquidus composition (C1) through charge material of the corresponding solidus composition (C,), as is illustrated in Figs. l(b) and l(c). To prepare the charge materials, high-purity germanium and silicon were pulverized in a steel hammer mill, cleaned magnetically, and melted together to make uniform chill castings. The zone leveling was carried out in a resistance-heated furnace similar to that of Mitrenin et al.' shown in Fig. 2. However, a few specimens of high silicon content were prepared by the Czochralski technique. The growth rate ranged from 3.5 x X6 to 1.2 X 10~3 cm-sec-'. Temperature gradients in the solid and in the melt were determined by recording the temperature as the molten zone passed over a Pt-Pt 13 pct Rh thermocouple contained in a small

Jan 1, 1965

By F. R. Hensel

PuRe silver and silver-lead alloys have been studied as to their suitability for bearing~.' A review of the properties of thallium and the silver-thallium constitutional diagram was made by the author to analyze the possibilities of silver-thallium compositions for antifriction materia1s. t The silver-rich end of the diagram as reported in the literatureg-" was found to be sketchy and it was necessary to carry out corisiderable experimental work to arrive at definite conclusions. Some of the results of this work are reported in this paper. Test Materials In the beginning of the work, only fused alloys were investigated. Later, research Table i.—Composition of Fused Silver-thallium Alloys Tested for Antifriction Properties Percentage Alloy No. of Thallium 1533...................... 0.48 1534.................... 1.06 a31 HT................... 2.04 231....................... 2.10 232 HT................... 3.83 Balance 232....................... 4.07 Silver 233 HT................... 5.86 a33....................... 6.38 a34....................... 9.84 a34 HT................... 10.07 was carried out on electroplating methods and diffusion processes. In preparing the fused alloyst care was taken to exhaust the toxic fumes caused by the thaillium content. The compositions of the series of fused alloys are listed in Table I. The silver-thallium alloys were melted in clay-graphite crucibles and cast into preheated steel molds of 3/4-in, diameter. In the cast condition, they showed a cored structure, as indicated by the micrographs of Figs. I to 3. The etching reagent used was a mixture of 2 grams K2Cr207, 8 C.C. H2S04, and IOO C.C. H20. The cored structure is unsatisfactory for the type of corrosion resistance required for bearing applications, and homogenizing experiments were carried out at various temperatures, the results of which are shown in Figs. 4 through 8. The alloys with a lower thallium concentration, which were heated for 2 hr. at 525°C show an almost completely homogenized solid solution type of structure. With higher thallium concentration, the homogenizing temperature was dropped to 475OC. to eliminate the formation of a liquid phase. It is evident that heating for 2 hr. at this temperature did not iesiilt iii complete elimination of the cored structure. As would be expected, cold-working of the cast structure is an expedient in establishing equilibrium conditions. The fine homogeneous grain structure shown in Fig. 7 corresponds to the cold-worked area under the Rockwell ball penetration when the hardness was taken before heat-treatment. A detailed structural study was made on a cast silver-thallium alloy containing 3.67 per cent thallium. Three micrographs (Figs. 9, 10 and 11) show the transition

Jan 1, 1946

By F. R. Hensel

PuRe silver and silver-lead alloys have been studied as to their suitability for bearing~.' A review of the properties of thallium and the silver-thallium constitutional diagram was made by the author to analyze the possibilities of silver-thallium compositions for antifriction materia1s. t The silver-rich end of the diagram as reported in the literatureg-" was found to be sketchy and it was necessary to carry out corisiderable experimental work to arrive at definite conclusions. Some of the results of this work are reported in this paper. Test Materials In the beginning of the work, only fused alloys were investigated. Later, research Table i.—Composition of Fused Silver-thallium Alloys Tested for Antifriction Properties Percentage Alloy No. of Thallium 1533...................... 0.48 1534.................... 1.06 a31 HT................... 2.04 231....................... 2.10 232 HT................... 3.83 Balance 232....................... 4.07 Silver 233 HT................... 5.86 a33....................... 6.38 a34....................... 9.84 a34 HT................... 10.07 was carried out on electroplating methods and diffusion processes. In preparing the fused alloyst care was taken to exhaust the toxic fumes caused by the thaillium content. The compositions of the series of fused alloys are listed in Table I. The silver-thallium alloys were melted in clay-graphite crucibles and cast into preheated steel molds of 3/4-in, diameter. In the cast condition, they showed a cored structure, as indicated by the micrographs of Figs. I to 3. The etching reagent used was a mixture of 2 grams K2Cr207, 8 C.C. H2S04, and IOO C.C. H20. The cored structure is unsatisfactory for the type of corrosion resistance required for bearing applications, and homogenizing experiments were carried out at various temperatures, the results of which are shown in Figs. 4 through 8. The alloys with a lower thallium concentration, which were heated for 2 hr. at 525°C show an almost completely homogenized solid solution type of structure. With higher thallium concentration, the homogenizing temperature was dropped to 475OC. to eliminate the formation of a liquid phase. It is evident that heating for 2 hr. at this temperature did not iesiilt iii complete elimination of the cored structure. As would be expected, cold-working of the cast structure is an expedient in establishing equilibrium conditions. The fine homogeneous grain structure shown in Fig. 7 corresponds to the cold-worked area under the Rockwell ball penetration when the hardness was taken before heat-treatment. A detailed structural study was made on a cast silver-thallium alloy containing 3.67 per cent thallium. Three micrographs (Figs. 9, 10 and 11) show the transition

Jan 1, 1946

By P. A. Beck

ACCORDING to a recent hypothesis of Sully,' xY. binary CT phases are characterized by 1.7 bonding 3d electrons per atom, which completely fill the first Brillouin zone. This hypothesis appears to imply that there are no empty 3d orbitals in the u phase, and that, correspondingly, this phase must be dia-magnetic, or at most weakly paramagnetic. On the other hand, Bowen and Hoar' reported that a u phase extracted electrolytically from an alloy steel became ferromagnetic when cooled to about —113°C. In view of the fundamental interest of the problem from the point of view of the electron structure of the u phase, it seemed worthwhile to study the magnetic properties of massive u phase specimens of various known compositions. Sigma specimens of the following compositions were tested: 1—40 atomic pct Fe, 40 atomic pct Cr, and 20 atomic pct Mo 2—35 atomic pct Fe, 35 atomic pct Cr, and 30 atomic pct Mo 3—48.7 atomic pct Fe, 50.2 atomic pct Cr, and 1.1 atomic pct W 4—40.7 atomic pct Co and 59.3 atomic pct Cr All specimens were found to be strongly paramagnetic at room temperature, particularly alloy No. 1. At liquid nitrogen temperature, alloy No. 1 be- came ferromagnetic; the other u alloys remained paramagnetic. Even though apparently not all u alloys become ferromagnetic at liquid nitrogen temperature, in view of their strong paramagnetism it is probable that the electron structure proposed by Sully is not correct. Similar qualitative studies were made with the p, P, and 8 phases." A p phase specimen of 57.2 atomic pct Co and 42.8 atomic pct Mo; a P specimen of 19.9 atomic pct Cr, 37.8 atomic pct Ni, and 42.3 atomic pct Mo; and a 8 specimen of 50.4 atomic pct Ni and 49.6 atomic pct Mo were tested at room temperature, and all were found to be paramagnetic, although considerably weaker than the u phase specimens described above. A test at liquid nitrogen temperature gave similar results for all specimens; none became ferromagnetic. Thanks are due to D. K. Das for preparing several of the alloys and to Pol Duwez of California Institute of Technology for kindly loaning four specimens of cr alloys. References 1 A. H. Sully: The Sigma Phase in Binary Alloys of the Transition Elements. Journal Inst. Metals (1951) 80, p. 173. - K. W. J. Bowen and T. P. Hoar: Low Temperature Ferromagnetism of Sigma Phase in an Alloy Steel. Research (1950) 3, p. 484. 3 S. Rideout, W. D. Manly, E. L. Kamen, B. S. Lement, and P. A. Beck: Intermediate Phases in Ternary Alloy Systems of Transition Elements. Trans. AIME (1951) 191, p. 872; Journal of Metals (October 1951).

Jan 1, 1953

IRON AND STEEL COMMITTEE ALBERT SAUVEUR, Chairman. A. A. STEVENSON, Vice-Chairman. HERBERT M. BOYLSTON, Secretary, Abbot Bldg., Cambridge, Mass. John Birkinbine, William Kelly, J. S. Unger, William H. Blauvelt, Charles Kirchhoff, Felix A. Vogel, James Gayley, Richard Moldenke, Leonard Waldo, Henry D. Hibbard, Joseph W. Richards, William R. Walker, Henry M. Howe, C. F. W. Rys, William R. Webster, Robert W. Hunt, E. Gybbon Spilsbury, Frederick W. Wood. J. E. Johnson, Jr.,

Jan 1, 1914

By Roy Moore

THE Tom Reed Extension and Big Jim mines of United Eastern Mining Co. are situated in the Oatman district, Mohave County, Ariz., about 28 miles southwest of Kingman, the nearest railway point. Articles descriptive of the mine surface plant, mill construction, and plant operations have been written by Otto Wartenweiler1, the designing engineer; Wheeler 0. North,2 when he was assistant general manager for the company, and Earle M. Bagley, mill superintendent.3 The last article covers average costs for the full time the mill was operated. The geology of the mines is described by F. L. Ransome4 of the United States Geological Survey. Production was started in January,. 1917, and the known orebodies were exhausted in May, 1925, showing a life of seven years and five months. On account of the comparatively short life and the fact that stoping operations were confined to two orebodies, little experimenting was done with mining methods. The two orebodies were in what is generally called the Tom Reed-United Eastern vein, which occupies a fault fissure having a normal displacement of several hundred feet. Seven or eight very productive ore shoots were mined along this vein in a distance of 1 ½ miles, the two worked by the United Eastern being 1 mile apart. The maximum dimensions of the Tom Reed Extension ore shoot were height, 750. ft.; length, 950 ft.; thickness, 48 ft. The vein structure varied from a solid quartz-calcite filling to a series of parallel stringers separated by andesite. From this body, 511,976 tons of ore were mined. (Fig. 1.)

Jan 1, 1928

New York Meets first Wednesday after first Tuesday of each month. J. E. JOHNSON, JR., Chairman EDGAR RICHARD, Vice-Chairman D M LIDDELL Secretary, 7 Wall St.. New York. N. Y. C. A. BORN, Treasurer JOHN V. N. DORR LEWIS W. FRANCIS Boston Meets first Monday of each winter month. R. L. AGASSIZ, Chairman JAMES G. CARLETON. Vice-Chairman E. E. BUGBEE Secretary-Treasurer, Mass. Inst. of Technology, Cambridge, Mass. W. E. C. EUSTIS G. A. PACKARD Columbia Holds four sessions during year. Annual meeting in September or October. W. H. LINNEY, Chairman OSCAR LACHMUND, Vice-Chairman LYNDON K. ARMSTRONG, Secretary-Treasurer, P. O. Drawer 2154, Spokane, Wash. STANLY A. EASTON S. SHEDD

Jan 12, 1917

By W. F. Holbrook, C. E. Wood, E. P. Barrett

The high-frequency laboratory induction furnace with a rotating liquid crucible enables research workers to conduct certain investigations heretofore very difficult or impossible to realize because vessels are not obtainable that are capable of resisting the physical conditions or the chemical actions to which they are subjected. Applications for patents covering commercial uses of centrifugal liquid crucibles were filed in the United States in 1919,' in France in 1925, in the United States and Germany in 1926,2 and in France in 1927.3 In 1928, Schuette and Maier,4 of the Bureau of Mines, reported the construction of a whirling table beneath a high-frequency induction furnace. Shape and Size of Centrifugal Liquid Crucibles When a vessel containing a liquid is rotated, the inner surface of the liquid takes the shape of a paraboloid under the simultaneous action of centrifugal force and gravity. The internal dimensions of the paraboloid rotating liquid crucible are governed by the diameter of the container and its speed of rotation. Melted Wood's metal was poured into cylinders 2 1/2 in. in diameter, which were rotated at 180, 300, and 468 r.p.m. When the metal was solid, a slurry of plaster of Paris was added, and rotation continued until the plaster had set. Fig. 1, a photograph of sections of the cylinders, shows the effect of speed of rotation of the containers upon the shape of the inner surface of the rotating liquid crucibles. Types of Furnaces Three types of high-frequency induction laboratory furnaces using liquid-metal crucibles were designed and constructed by the Blast

Jan 1, 1939

By W. F. Holbrook, C. E. Wood, E. P. Barrett

The high-frequency laboratory induction furnace with a rotating liquid crucible enables research workers to conduct certain investigations heretofore very difficult or impossible to realize because vessels are not obtainable that are capable of resisting the physical conditions or the chemical actions to which they are subjected. Applications for patents covering commercial uses of centrifugal liquid crucibles were filed in the United States in 1919,' in France in 1925, in the United States and Germany in 1926,2 and in France in 1927.3 In 1928, Schuette and Maier,4 of the Bureau of Mines, reported the construction of a whirling table beneath a high-frequency induction furnace. Shape and Size of Centrifugal Liquid Crucibles When a vessel containing a liquid is rotated, the inner surface of the liquid takes the shape of a paraboloid under the simultaneous action of centrifugal force and gravity. The internal dimensions of the paraboloid rotating liquid crucible are governed by the diameter of the container and its speed of rotation. Melted Wood's metal was poured into cylinders 2 1/2 in. in diameter, which were rotated at 180, 300, and 468 r.p.m. When the metal was solid, a slurry of plaster of Paris was added, and rotation continued until the plaster had set. Fig. 1, a photograph of sections of the cylinders, shows the effect of speed of rotation of the containers upon the shape of the inner surface of the rotating liquid crucibles. Types of Furnaces Three types of high-frequency induction laboratory furnaces using liquid-metal crucibles were designed and constructed by the Blast

Jan 1, 1939

By F. G. ROCKWELL

ALTHOUGH the diamond as a gem stone dates back many hundreds of years its use industrially, at least to any extend is recent. The old adage: "Use a diamond to cut a diamond" indicates that some industrial use was made of this material in cutting and polishing many years ago. It also put to various other industrial by the Romans. General industrial use however was never developed to any considerable extent until about the time of the first World War. It is definiely known however, that a Swiss watchmaker, M. Leschot by name, invented a diamond drill in or about the year 1862, Today, some 75 or 80 per cent of the total didamods produced are used in industry. There are two main classifications of diamonds : (1) carbonados or "black diamonmds," and (2) diamonds proper.

Jan 1, 1944

Edward Dyer Peters, the only child of Henry Hunter Peters and Susan Barker Thaxter, was born in Dorchester, Mass., June 1, 1849. From his father he was a descendant of the Peters family of Ipswich and Andover, Mass., whose earliest ancestor settled in Essex County in 1659; while upon his mother's side he descended from several old Hingham families, as well as from the Quineys and from Governor Bradford. Between the ages of fourteen and sixteen he was a student at the Episcopal School for boys in Cheshire, Conn. Near the school was an old tin mine, and he used to spend his Saturday afternoons exploring it. When Edward was sixteen, his father sold his property in South-borough, and for the next three years lived in Europe. Sept. 26, 1865, Edward entered the Royal School of Mines at Freiberg, Saxony. In the summer of 1867 he joined his family on Lake Geneva, and spent a part of the season in that vicinity, going to Chamounix and taking other trips. Extract from a letter to his father: Elbingerode, Harz, Aug. 30, 1868: I left Freiberg with my friend Lilienthal, on Wednesday the 19th of August, reached Leipzig in the evening and spent the night in that city: the next morning we took the cars and in the afternoon reached Eisleben, in Prussia, which was to be our first stopping-place; there are immense copper-mines and smelting-works at this place, and the method of working the mines is very peculiar ... The next morning we got up at five and spent the whole day in the smelting-works where I obtained a number of drawings of the furnaces they use here and a good many valuable data. Saturday morning we got up at four o'clock, and descended a mine about three miles from the town; the Director of this mine was one of the most intelligent and agreeable men that I ever met; he accompanied us in the mine and explained everything that was new to us. The system of mining at Eisleben is peculiar to this town, and is not used at any other place in the world; the copper ore comes in narrow, flat veins eighteen inches high, at the utmost, consequently the men work lying flat on their left side and using the pick with both hands: the ore is carried out of the side passages into the main ones, in very low waggons about twelve inches high, and four by two feet; the boys who pull these waggons have a board buckled to their left thigh and their left arm; they pass their bare foot through a strap in the waggon and wriggle along on their side dragging the waggon after them, with their foot, almost as fast as a man can walk above ground. In the afternoon we walked over to Hittstadt, about twelve miles, and remained there Sunday and Monday. Monday night, at ten o'clock we went out to one of the smelting-works, to see the refining of the copper; this is only done at night, so we worked there from ten in the evening till eleven the next morning, and came home all blackened up and with blistered hands, for our skin was not quite so tough as that of the workmen: at noon the same day we took the stage to Ascherls-leben, and then the train to Stassfurt, where there are immense salt-mines, as well as factories for the manufacture of bromium, which latter process is, however, kept a profound secret, so we had very little hope of seeing anything but the salt mines; we were talking with our landlord about our disappointment, that evening, when he told us that the director of the Bromium works was sitting in the next room with no company but his glass of beer, so we went over to him, introduced ourselves as Americans, and actually succeeded in persuading him that it could do his business no earthly hurt if he showed us his works; at last he consented, after making us give our word of honor

Jan 1, 1919

W. H. BASSETT, * Waterbury, Conn.-Manganese should not be expected to remedy all the defects that are due to poor melting practice. It is undoubtedly valuable in helping to eliminate porosity in many of the alloys. In the copper-nickel alloys, its use is becoming almost universal, for, beside helping to make sound castings, it tends to hold the carbon in solution in the solidified alloy. GWILLIAM H. CLAMER,? Philadelphia, Pa.-I have found that manganese copper is satisfactory for eliminating sulfur and that it works very well in the crucible and when you have reducing conditions; but in a large reverberatory charge, where the conditions are oxidizing, we were not able to eliminate the sulfur.

Jan 1, 1919

By J. R. Szedon, T. L. Chu, G. A. Gruber

Amorphous adherent filnzs of silicon dioxide have been deposited on silicon substrates by the oxidation of silane at temperatures ranging from 650 to 1050C. Various diluents (argon, nitrogen, hydrogen) were used to suppress the formation of SiO2 in the gas phase. Deposition rates of the oxide were determined over the temperature range in question as functions of' re-actant flow rates. Etch rate studies were used for a cursory comparison of structural properties of deposited and thermally grown oxides. From electrical evaluation of metal-insulator-silicon capacitors it was determined that the interface charge density of deposited films is similar go that of dry-oxygen-grown films in the 850° to 1050 C temperature range. Deposited films exhibit several ionic instability effects which differ in detail from those reported for thermal oxides. Stable passivating films of silicon nitride over deposited oxides appear to be practical for use in silicon planar device fabrication. Such films can be prepared under temperature conditions which have less effect on substrate impurity distributions than in the case of grown oxides. AMORPHOUS silicon dioxide (silica) is compatible with silicon in electrical properties and is the most widely used dielectric in silicon devices at present. Silica films can be prepared by the oxidation of silicon or deposited on silicon or other substrate surfaces by chemical reactions or vacuum techniques. The ability of thermally grown silicon dioxide films to passivate silicon surfaces forms one of the practical bases of the planar device technology. Properly produced and treated films of grown SiO 2 can have low densities of interface charge (-1 X 10" charges per sq cm) and can be stable as regards fast migrating ionic sgecies. 1 To maintain these properties, even with an otherwise hermetically sealed ambient, the Sia layers must be at least l000 A thick. Such thicknesses require oxidation in dry oxygen for periods of 7.8 hr at 900°C or 2 hr at 1000°C. Although oxidation in steam or wet oxygen can reduce these times to 17 and 5 min, the resulting oxides must be annealed to produce acceptable levels of interface charge., Oxidation or annealing involving moderate to high temperatures for extended periods of time can be undesirable. Under some conditions, there can be changes in the distribution of impurities within the underlying substrate. A chemical deposition technique using gaseous am-bients is particularly attractive and flexible for preparing oxide films. With a wide range of deposition rates available, films can be produced under condi- tions of time and temperature less detrimental to impurity distributions in the silicon than in the case of thermal oxidation. The pyrolysis of alkoxysilanes, the hydrolysis of silicon halides, and various modifications of these reactions are most commonly used for the deposition of silica films.3 Silica films obtained in this manner are likely to be contaminated by the by-products of the reaction, organic impurities, or hydrogen halides. The use of the oxidation of silane for the deposition process has been reported recently.4 The deposition of silica films on single-crystal silicon substrates by the oxidation of silane in a gas flow system has been studied in this work. The deposition variables studied were the crystallographic orientation of the substrate surface, the substrate temperature, and the nature of the diluent gas. The electrical charge behavior of Si-SiO2-A1 structures prepared under various conditions was investigated by capacitance-voltage (C-V) measurements of metal-insulator-semiconductor (MIS) capacitors. The experimental approaches and results are discussed in this paper. 1) DEPOSITION OF SILICA FILMS The overall reaction for the oxidation of silane is: The equilibrium constants of this reaction in the temperature range 500° to 1500°K, calculated from the JANAF thermochemical data,= are shown in Fig. 1. In addition to the large equilibrium constants, the oxidation of silane is also kinetically feasible at room temperature and above. However, the strong reactivity of silane toward oxygen tends to promote the nucleation of silica in the gas phase through homogeneous reactions, and the deposition of this silica on the substrate would yield nonadherent material. The formation of silica in the gas phase can be reduced by using low partial pressures of the reactants. Argon, hydrogen, and nitrogen were used as diluents in this work. 1.1) Experimental. The deposition of silica films by the oxidation of silane was carried out in a gas flow system using an apparatus shown schematically in Fig. 2. Appropriate flow meters and valves were used to control the flow of various reactants, i.e., argon, hydrogen, nitrogen, oxygen, and silane. Semiconductor-grade silane, argon of 99.999 pct minimum purity, oxygen of 99.95 pct minimum purity, and nitrogen of 99.997 pct minimum purity, all purchased from the Matheson Co., were used without further purification. In several instances, a silicon nitride film was deposited over the silica film. This was achieved by the nitridation of silane with ammonia using anhydrous ammonia of better than 99.99 pct purity supplied by the Matheson CO.' The reactant mixture of the desired composition was passed through a Millipore filter into a horizontal water-cooled fused silica tube of 55 mm

Jan 1, 1969

By S. E. Hasko

It is the purpose of this note to report the crystal-lographic data for nine new B5A compounds* having the Cu5Ca structure, with A a rare earth and B a transition element, Co, Ni or Cu. In previous papers, some magnetic data1 and preparation and crystallo-graphic data2 for other B5A compounds having the same structure have been reported. Crystallographic data for these compounds are shown in Tables I and 11. These results are in agreement with others of this series reported previously by Wernick and ~eller.' The abnormally large atomic volume of Yb metal3 is not manifested in Ni,Yb, when one compares it with the compounds reported here and the data of reference 2. This is not true for the compound YbAl,, having the cubic Laves structure (MgCuz), to be discussed in other papers.4'5 Thus, it appears that Yb has a valence of 3; i.e., the 2 s and Id electrons are lost to the conduction band.4'5 Lattice constants for four of these compounds prepared by levitation melting have been reported by Nassau, Cherry, and wallace.' The lattice constants

Jan 1, 1961

Discussion of the paper of E.. C. LEE, presented at the St. Louis meeting, October, 1917, and printed in Bulletin-No. 130, October, 1917, pp. 1825 to 1832. H. M. WILSON, Pittsburgh, Pa.-The statement ill the paper of T. T. Read, "Increasing Dividends Through Personnel Work;" that the offering of substantial money rewards for avoidance of accidents is much more effective than mere propaganda or education respecting accident prevention, is a, point fully substantiated in the experience of insurance inspection under workmen's compensation acts. The first year under the Workmen's Compensation Law in Pennsylvania, during which over 2000 mines were tinder the observation and protection of the inspectors of the insurance companies, has resulted in several inspections of each mine, a splendid cooperation .between the operators, the State mine inspectors and the insurance inspectors, and an average reduction in premium rate for insurance from $3.83 to $2.77, a reduction of more than $1 per $100 of payroll, on an average payroll of nearly $100,000,000, In other words, the insurance companies have

Jan 1, 1918

By S. T. Wlodek

The surface and subscale oxidation reactions were followed by means of continuous weight-gain and metallographic techniques over the range 1600" to 2200°F (871° to 1204 °C) for up to 400 hr. Full identification of all scale and subscale reaction products was obtained by electron and X-ray diffraction. At or below 1800°F (982°C) a linear rate of reaction (QL = 46.0 kcal per mole) governed the oxidation process, extending for up to 100 hr at 1600°F (871 "C). During linear oxidation the surface scale consisted of an amorphous SiO2 film overgrown with Cr 2O 3 and NiCr204. This initial linear process was followed, and above 1800°F completely replaced, by two successive parabolic rate laws (Qp = 60 and 57 kcal per mole). This parabolic reaction involved the formation of a complex scale consisting of Cr2 O3 and smaller amounts of NiCr2O4. Parabolic oxidation appeared to coincide with the disruplion of the silica film present during linear oxidation and was followed by subscale (internal) oxidation of crystobalite and NiCr2O4. The balance between the subscale and surface oxidation reactions controls the oxidation of this commercial alloy. The amorphous silica film appears to result in the linear rate and diffusion through Cr2O3 is the more likely rate-limiting step during parabolic oxidation. THE oxidation of a multicomponent composition is a complex phenomenon not presently amenable to a rigorous classical interpretation. Nevertheless, even a qualitative understanding of the scaling and subscale reactions that occur in a commercial composition can illuminate the reactions that limit its high-temperature stability in an oxidizing environment. This study of the oxidation of Hastelloy Alloy X presents the first of a series of studies with the above approach in mind. Hastelloy X exhibits one of the best combinations of strength and oxidation resistance available in a wrought, solution-strengthened, nickel-base alloy. Although during long time exposure some precipitation of M6C and M23C8 carbides as well as a complex Laves phase occurs, the amounts are probably small enough to have no appreciable effect on the chemistry of the matrix. Radavich has identified the oxidation products on Hastelloy X oxidized for 5 min to 10 hr at 1115°F as NiO and the NiCr2O4 spinel. Oxidation for 5 to 15 min at 1500°F produced a scale of spinel, NiO, and a rhombohedra1 phase, probably Cr2Os. Sannier et 2. have reported continuous weight-gain data for Hastelloy X at 1650" and 2010°F and internal-oxidation measurements after 150 hr at 2010°F. In addition, much of the data on binary Ni-Cr alloys recently reviewed by Kubaschewski and okins' and Ignatov and Shamgunova4 as well as studies of binary Ni-Mo alloys5 are also pertinent to the oxidation of this composition. EXPERIMENTAL Continuous weight-gain measurements and metallographic measurements of subscale reactions were the main experimental techniques used in this study. X-ray and electron diffraction backed up by a limited amount of electron-microprobe analysis served to characterize the nature of the scale- and subscale-reaction products. Two heats of commercial sheet of the composition given in Table I and identified as A and B were used in the bulk of this study. Internal-oxidation measurements were made on a third heat of material in the form of a 0.5-in.-diam bar. In order to assure homogeneity, all heats were reannealed 4 hr at 2175°F prior to sample preparation. weight-Gain Measurement. All specimens (1.5 by 0.4 by 0.03 in.) were abraded through 600 paper, electropolished, and lightly etched in an alcohol-10 pct HCl solution. An electrolyte of 150 cu cm H,O, 500 cu cm HsPO4 (85 pct conc), and 3 g CrO3 at a current density of 0.9 amp per sq cm or a solution of 10 pct HaW4 in alcohol used at 4 v and 0.3 amp per sq cm was used for electropolishing. The resultant surface exhibited a finish of 3 ± 1 p rms. Continuous weight-gain tests were made at 1600°, 1700°, 1800°, 1900°, 2000", and 2200°F on auer' type balances capable of recording a total weight change of 110 mg with an accuracy of k0.1 mg. All tests were made in air dried to a dew point of -70°F and metered into the 2-in.-diam reaction

Jan 1, 1964

By William Fink

Two of the aluminum-alloy systems previously studied-the alumi-num-titanium and the aluminum-chromium-exhibit a peritectic reaction at the extreme aluminum end of the diagram. Preliminary work indi-cated that the aluminum-zirconium and certain other aluminum systems were similar in this respect. The present paper, the twentieth of a series from the Aluminum Research Laboratories, reports the results of a recent investigation of equilibrium relations in aluminum-zirconium alloys of high purity, which confirm the preliminary observations. PREVIOUS INVESTIGATIONS There has been only one investigation of the aluminum end of the aluminum-zirconium system. Sykes1 prepared and studied alloys containing 0 to 70 per cent Zr. The lowering of the freezing point of aluminum by the addition of zirconium was found to be very little, if any (less than 2°C.). He placed the solid solubility of zirconium in aluminum at room temperature between 0.57 and 0.97 per cent. A few other investigators have attempted to determine the com-position of the intermetallic compounds occurring in this system. Hönigschmid2 obtained the compound ZrAl3 as a by-product during the preparation of ZrSi2. He made no attempt to prepare other aluminum-zir-conium compounds. Weiss and Newmann3 prepared an alloy by heating aluminum with a double fluoride of potassium and zirconium. When this alloy was treated consecutively with caustic soda and hydrochloric acid, there was a residue, which contained approximately 72 per cent Zr and 28 per cent Al (Zr3Al4). Marden and Rich4 prepared an alloy in the same way, treated it with caustic soda, and obtained a residue of silver-white crystals, which contained 70 per cent Zr and 30 per cent Al (Zr3Al4).

Jan 1, 1939

By W. J. Feuerstein

STRUCTURAL imperfections in crystals, in recent years, have received the attention of metallurgists concerned with single-crystal properties. Certain etching solutions cause local variations in the rate of etching at dislocations.' Dislocations are expected to be preferred segregation sites for impurities' and Dash" has shown that precipitation of copper occurs preferentially at edge-type dislocations in silicon. Diffusion rates along dislocations are probably higher than rates through more perfect crystalline regions.' These and other phenomena which may be influenced by dislocations may be studied by revealing dislocations as etch pits. This study was undertaken to develop an etch solution for silicon crystals to reveal low-angle grain boundaries associated with dislocation arrays and also etch pits with good contour definition. Additional etches have been reported by Dash," Vogel and Lovell.T rystals were sectioned on crystal lographic planes at various angles from the growth direction for microscopic examination of the etch pits. Experimental Crystals of 75-100 g mass and 3 cm diam were oriented and cut on crystallographic planes. Crystals were grown by Czochralski technique from a quartz crucible. Lapped wafers were chemically polished in a modified CP-4 etch for 1 min (bromine was deleted from the etch solution). The polished wafer was then etched* at room temperature for 5 min. The use of larger amounts of H2O and/or CH2COOH slows the reaction. The Cu(NO3),.3H2O was added to increase the reaction rate and give more definition to the etch pits developed. Some pertinent features concerning the attack of this etch on silicon can be summarized as follows:

Jan 1, 1959