By William H. Kobbé

THE CHAIRMAN (M. L. REQUA, San Francisco, Cal.).-We have had in California a great deal of trouble from the breaking. off and collapsing of well casings from shifting sand, and it is quite true with us as indicated in the paper, that no casing has been found sufficiently strong to withstand that. I know of wells in which casing that has not been in the hole over 2 or 3 days has collapsed and when that casing has, been pulled out it has been just as flat as your hand. I am also familiar with swelling bed rock in the gold drift mining ground of California. It does swell and keeps on swelling and never seems to stop. Just as long as tunnels are kept open in that kind of material there has to be a gang going through the tunnel constantly cutting out and easing up. They have put in timbers 24 in. in diameter in an effort to hold that kind of ground and it has always filled. The only way to succeed is to keep a gang of men busy all the time cutting out and easing down as it squeezes in. C. NARAMORE, Washington, D. C.-My experience has been very similar to yours in, the same field in the matter of breaking off of casing. I had charge of one well, in which I put in reënforced casing, anchored it in place and got 1 day's production, 150 bbl., out of it. The following morning my lease foreman telephoned that it had broken off. I thought at that time we would have more evidence, so I drove out to the well without ordering a new shoe joint. It had been customary to merely start from town with a new shoe joint, pull the pipe, take off the crooked bottom joint, start the casing back and sometimes never touch any iron (lost casing)- when redrilling the well. Where the flattened joints went

Jan 4, 1917

By C. J. Leith

A study of the effect of rock composition, rock structure and degree of weathering on the stability of cut slopes is being sponsored jointly by the U.S. Bureau of Public Roads and the North Carolina Highway Commission. In 58 mountain and piedmont counties of North Carolina the percentage of failed cut slopes is greatest in micaceous metasediments, gneisses, and schists, and in saprolite and soil derived from these rock types. Soil slope failures outnumber rock slope failures by two to one. Joints and similar planes of separation exert a strong influence on size and shape of the sliding mass. They may or may not act as failure surfaces, depending on their orientation with respect to the active forces. Climatological data, though indicative of weathering conditions, do not correlate well with slope failure frequency. Because of the presence of joints and similar planes of weakness in soil and rock materials, conventional methods for analyzing slope stabilities are not directly applicable. Empirically derived modifications of these methods are being investigated. A study of the stability of highway cut slopes, sponsored by the U. S. Bureau of Public Roads and the North Carolina State Highway Commission, began in 1962 at North Carolina State of the University of North Carolina at Raleigh. As part of this study all slides, rockfalls and other types of cut slope failures on Federal and State highways in the 58 mountain and piedmont counties in North Carolina were located and described, and the data catalogued in a punched card file system. A major objective of the project is to relate slope failures to properties and physical conditions of the geological units in which the slopes were constructed, and to correlate soil type and/or geological unit with type and frequency of slope failure. The complexities of the problem of slope stability and the limitations which these complexities impose on methods for analyzing slopes have been recognized for many years. A great variety of factors and processes may lead to slides, often making it almost impossible to analyze theoretically the conditions required for stability of slopes. One of the principal factors determining maximum safe slopes is the shear strength of the material in which the slopes are cut, but unfortunately there are very few data available concerning shear strengths of residual soils. Vargasl tested clay derived from gneiss and granite in southern Brazil; the properties of decomposed granite occurring near Hong Kong were determined by Lumb.2 These data are being used, when applicable, to supplement the test data obtained in the present study by Yorke.3 The locations of the North Carolina slope failures, more than 400 in number, are shown on Fig. 1. This map, adapted from the Geological Map of North Carolina,4 suggests the possibility of a relationship between frequency of slide occurrence and rock type. However, the evaluation of this possibility requires consideration not only of the type of rock, but also of its large and small scale structural features, its susceptibility to and degree of weathering, and the composition and structure of the weathering products. Soil slope failures in thoroughly weathered soil material and saprolite outnumber rock slope failures two to one. INFLUENCE OF ROCK TYPE The agricultural soil type involved in each soil slope failure was identified and each failure was catalogued in terms of the parent material from which the soil was derived. These data indicate that most of the slope failures, whether in the rock or in the derived soil, are associated with metamorphic rocks (see Fig. 2a). The data may be skewed somewhat because of the relative sizes of the total areas underlain by the various rock types, but Leith and Gupton5 have demonstrated that the preponderance of failures in metamorphic rocks is of much greater magnitude than could be accounted for by the areal factor alone. The dominance of metamorphic rocks is emphasized when soil slope failures are considered in terms of the specific rock types from which the soils were derived (see Fig. 2b). In particular, mica schists and mica gneisses account for more slides

Jan 1, 1965

By A. H. Rhoades, D. T. King, R. J. Gray

Tests and methods of detecting oxidized coal are studied. Particular emphasis is placed on the microscopically discernible changes that accompany the chemical and physical changes affecting the technological properties of coal during oxidation. Coal samples were used from the low-volatile Pocahontas No. 3 Seam, McDowell County, W.V., and from the high-volatile Cedar Grove Seam, Mingo County, W.V. Tests conducted include: carbonization, free-swelling index, phase inversion, froth flotation, Gieseler plasticity, oxygen by difference and by neutron activation, volatile matter, pH of coal slurries, alkali solubility, and electrostatic charge.

Jan 1, 1977

By C. D. Tedmon, D. P. Ferriss

THE yield stress, o of low-carbon steel has been shown to vary with the average grain diameter, d, according to the relation1-3 where o is taken to be the lower yield-point stress Of is the friction stress on an unlocked dislocation, and ky is a constant. The interpretation2,4 of ky in terms of dislocation theory relates this constant to the stress to unlock a source across a grain boundary. cottrel14 predicted that ky would increase with decreasing temperature. This was observed to be the case by Adams and coworkers5 in their investigation of niobium (columbium). However, petch6 and Backofen: both working with low-carbon steel, found ky insensitive to temperature. In his work with high-purity niobium, Johnson' found ky equal to zero. Evansg showed that k, was essentially zero for niobium containing nitrogen in an appreciable concentration range. The present experiments were designed to check this apparent anomaly in the value of ky in another Group V metal. Yield points were determined as a function of grain size at several temperatures for tantalum and a tantalum-tungsten alloy. The material used was double are-melted tantalum and a double are-melted alloy of 90 pct Ta and 10 pct tungsten (by weight), both obtained as unannealed, swaged rod. The impurity content of the materials is given in Table I. The tantalum was annealed at 1325"C. in a vacuum resistance furnace using a tantalum boat. The alloy was similarly annealed at 1660°C. Annealing times varied from 15 min to 2 hr, depending on the desired grain size. Nominal pressure in the furnace was 3 X 10~4 mm of Kg. Metallographic examination showed that the annealing treatment produced grain sizes ranging frorn 0.021 to 0.200 mm in the tantalum, and 0.060 to 0.160 mm in the alloy. Tensile bars were made by centerless grinding the annealed specimen;, and then electropolishing to remove all grinding marks. The specimens were than pulled :it 2 1/2 pct per rnin in an Instron testing machine. The tantalum specimens were tested at 77", 195", and 300°K. The alloy was tested at 300°K only. All specimens exhibited a yield-point phenomenon at all temperatures. Typical load-elongation curves at the three test temperatures are shown in Fig. 1. The lower yield stress is plotted as a function of (grain size) in Figs. 2 and 3 for tantalum and the 90 pct Ta-10 pct W alloy, respectfully. The position and slope of the curves was determined by least-

Jan 1, 1962

By David A. Thomas, Eugene S. Meieran

MECHAMCAL, electrical, and other property measurements are often more easily made on wires than on sheets. In order to carry out transmission electron microscopy on the same material used for property determinations, we have developed a method for preparing thin foil specimens of wires. The technique was developed for 0.030 in. diam tungsten wires, and is a modification of the thinning techniques used by Wilsdorf, et al 1 A length of wire is first ground to about 0.010 in. thick by mounting the wire in low melting temperature wax, hand grinding a longitudinal flat, removing and reversing the wire in the mount, and then grinding a second parallel flat. The 0.030 in. wide and 0.010 in. thick strip is cut into 1/8 in. lengths to fit in the specimen holder of the electron microscope. Next the specimen is gripped in platinum-tipped tweezers (the anode) and placed 2 mm below a hol- low copper cathode with a 0.010 in. ID nozzle. Electrolyte, 10 pct NaOH, flows by gravity feed through the nozzle onto the specimen, as shown in Fig. l(a). Polishing is carried out until a shallow impression is made on one surface, and then the specimen is turned over and the opposite surface indented. The metal between the two impressions should be about half the specimen thickness, as is shown by the heavy line in the cross section in Fig. l(b). The entire specimen is then electropolishedin 2 pct NaOH until a hole appears at the location of the indentations. The apparatus is shown in Fig. 2, and is essentially the same as that used by Wilsdorf et al. at The Franklin Institute. Light is reflected by a mirror onto the bottom surface of the specimen! which is viewed by a stereoscopic microscope placed above it. Polishing is carried out until light is seen, indicating that a hole has formed, and then immediately stopped. The specimen is washed in water. alcohol, and ether, and is then ready for examination. The specimen should be reversed in its platinum clip during electropolishing to insure equal polishing on both sides of the impression. For tungsten, indenting at 120 v and 0.04 amp takes less than 1 min, and final polishing, at 10 v and 1 amp, less than 5 min. The portion of the specimen available for transmission microscopy surrounds the hole, as is seen by the dashed lines in Fig. l(b). Slight electroetch-ing accompanying electropolishing reveals the mi-crostructure, as seen in Fig. 3(a) by light microscopy. Low-magnification electron microscopy, as in Fig. 3(b), enables the same areas and grains to be viewed and identified when subsequently examined at high magnification. Fig. 4 is a typical structure of

Jan 1, 1963

By Jonathan Ludlow, Paul J. Guay

Based on two studies that were funded by the U.S. Department of Energy, the authors provide an overview of the benefits expected from mining deeper webs on United States longwalls. The first study, completed in November 1979, identified the limits and potential gains from taking deeper webs with presently available equipment. The second on-going study discusses the conceptual design and benefits of a future system for taking very deep webs.

Jan 1, 1981

By J. R. Campbell

During the past few years, the writer has had occasion to take several excursions into the realms of the washability of beds 3 and 4 of the Pocahontas coal and the proper handling of these coals in prepared sizes Fig. 1.—Washability curve for 4 by 2½-in. egg, PocahoKtas coal. Note that definite break occurs at about 1.60 sp. gr., and washing at this gravity removes all heavy rock and slate, amounting to about 5 per cent. Curve 2 indicates a bony coal, and washed egg coal might not have a good appcarance, and would be condemned by visual inspection, although it would be well prepared mechanically. to attain the greatest realization for the operator and yet produce a market product acceptable to the consumer. Preparation is not new in the southern field, but some new angles have presented themselves in recent years on account of the progress of mechanical preparation. Mechanical methods are entirely devoid of the five senses given to

Jan 1, 1931

By Larry Kaufman, Morris Cohen

THE solid phase equilibria' and the martensitic transformation in the iron-nickel system have been the subject of considerable study. In addition, there have been numerous investigations on the calorimetric and thermodynamic properties of iron-nickel alloys. The purpose of the present work is to extend the existing information concerning the martensitic reaction in the iron-nickel system, and to develop a general thermodynamic treatment which will encompass the equilibrium and non-equilibrium phase

Jan 1, 1957

By E. D. Gardner

WHEN the National Forests Were created, all lands embraced in their boundaries were exempted from all forms of entry, except mineral claims. Later, by Act of June 11, 1906, and as amended by Act of Aug. 10, 1912, provision was made allowing homesteads on areas chiefly valuable for agriculture and not necessary for the public use. Patents to mining claim in the Forests are granted the same as on land not in the Forests, irrespective of timber or other values. It is the policy to encourage the highest use of the Forests. As a business proposition, it is a good policy to have mines developed in the Forests. Their development in remote or inaccessible regions causes the country to be opened up and, in addition to the local market which the mines create, means of transportation are afforded to outside markets. No examination of mining claims is made until patent has been applied for, unless they are actively interfering with the administration of the Forest. In this case, an examination is made, and if there is evidence that the claims are being held in good faith they are in no way interfered with. Timber is never sold from a mining claim except with the consent of the claimant, or unless it is clearly shown, after an examination, that the claim is abandoned. In the case of fire-killed timber, which rapidly deteriorates by standing, a contract bond arrangement can be made for the sale of the timber which protects the interests of both the mining claimant and the government. The promiscuous locating of mining claims has in the past caused considerable trouble. It has been, and still is, the custom in some parts of the West to locate a mining claim when the surface rights of any particular area are desired, irrespective of the mineral character of the ground. This has been done to hold power sites, town sites, summer residences, springs, etc. When the, ground is desired for any of these purposes, what is known as a Special Use Permit will be issued at a nominal sum, to legalize the occupancy. In most instances, it is far cheaper to take out one of these permits than to do the annual assessment

Jan 7, 1914

By C. S. Finney, John Mitchell

On December 31, 1959, there existed in the United States 15,993 slot-type coke ovens capable of producing 81,447,700 net tons of coke. These ovens were concentrated in 74 coke plants in 21 different states. As of the same date, there were 7448 beehive ovens in existence at 45 plants in the states of Pennsylvania, Virginia, West Virginia, and Kentucky. Total annual capacity of the existing beehive ovens was 4,368,800 net tons, but only 5148 ovens with a capacity of 3,131,600 tons were in operating condition. It is interesting to compare the average dimensions of slot-type ovens built during recent years with the 30 ft x 5 ½ ft x 16 ½ in. ovens erected at Syracuse, N. Y. in 1892. A composite oven built according to the average dimensions of all those erected between 1954 and 1958, for instance, would be 39 ft long. 12 ft high, and 18 in. in width. The coal capacity would be 16 tons as against the 4.4 tons which could be charged to the Syracuse ovens. Of the 15.993 slot- type ovens in existence at the end of 1959, by far the greater number were built by the Koppers Co. whose total of 11,280 ovens included 7891 Koppers- Becker and 3389 Koppers ovens. Of the remainder, there were 3260 Wilputte, 1350 Semet-Solvay, 63 Otto, and 40 Simon Carves ovens. By-product coke oven plants are usually classified either as furnace or merchant plants. According to the definitions used by the US Bureau of Mines, the former are "those that are owned by or financially affiliated with iron and steel companies whose main business is producing coke for use in their own blast furnaces. All other coke plants are classified as merchant. They include those that manufacture metallurgical, industrial, and residential heating grades of coke for sale on the open market; coke plants associated with chemical companies or gas utilities; and those affiliated with local iron works, where only a small part (less than 50 pct of their output) is used in affiliated blast furnaces." The annual coke capacity of the merchant plants during 1959 was 10,393,000 tons. However, the by-product oven of today is essentially an appurtenance of the iron and steel industry, rather more than 87 pct of total by- product coking capacity being concentrated at furnace plants. This was not always so. There was a time when the merchant plants played a much greater part in meeting the US demand for coke and gas. High noon for the merchant plants was reached during the early 1930's. By 1932 there were as many by- product oven installations being operated by the merchant sector of the industry as by the coke divisions of the iron and steel industry (44 of each), and in the same year the merchant plants produced 46.5 pct of all by-product coke made in the country. Since that time their contribution has drastically declined. In 1940 merchant plants were responsible for only 23.2 pct of total US production, and by 1950 their number had decreased to 30 plants which turned out 18.5 pct of the total by-product coke made. At the end of 1959 only 20 of the 74 existing by-product oven installations were merchant plants. They ac- counted for 12.5 pct of the year's production, or 6,849,786 net tons. This percentage has remained fairly constant since 1954. There are several reasons for the decline of the merchant coking industry. For example. On the grounds of economy, quality control, continuity of supply, and so on, the iron and steel industry usually prefers to control its own mines and carbonize its own coal at or near to the blast furnace rather than rely on independent operators for metallurgical coke. As the steel companies have enlarged their own coking facilities, so has the need for coke obtained from other sources declined. Furthermore, not only has the steel industry increased in self-sufficiency by building mare coke ovens during recent years, but it has also progressively improved the fuel efficiency of its blast furnaces. During the years 1947-49 the average coke consumption per ton of pig iron was 1892.8 lb. During 1958 the corresponding figure was 1613.4 lb. There are many individual furnaces where still better results are being obtained, and further reductions in the average may be expected. Perhaps the greatest threat to the merchant coking plant has been the fantastic increase in the use of natural gas and petroleum products for purposes which manufactured gas once served. So deadly has the com- petition from natural gas and oil been that it has almost eliminated by-product oven installations owned by public utilities. In the peak years of the early 1930's there were 23 such public utility plants. In 1960 only two were left. One of these, owned by the Citizens Gas and Coke Utility, was at Indianapolis, Ind.; the other was the plant operated by the Philadelphia Electric Co. at Chester, Pa. The non-utility merchant plants have also been sorely hit. With gas sales revenues reduced, domestic

Jan 1, 1961

By H. R. Page, A. E. Jr Lee

From the inception of zinc retorting on a commercial scale in the United States in 1890,' the retort employed has undergone wide variations in its composition and manufacture, facilitating in part equally remarkable improvements in furnace capacities. The early day hand made clay retort was charged with carbonates or silicates or with coarse dead roasted concentrates mixed with a large proportion of charge fuel resulting in a relatively low zinc burden and fired 24 hr in direct coal fired furnaces. Its modern counterpart is fabricated in hydraulic presses from clay mixtures containing sizeable amounts of either silicon carbide or silica flour, charged with sintered flotation concentrates to more than three times the early day zinc burden and fired 24 to 48 hr in gas fired furnaces. This paper does not attempt to describe in detail the early day clay retort practice as it is well outlined in treatises by Ingalls,2 Lodin,3 Liehig,4 Hofman5 and others. A brief review of clay retort practice is presented together with a description of the major developments since 1912. Clay Retorts The Belgian type retort, both in the circular and elliptical forms, has been used almost exclusively. Typical dimensions of press made clay retorts around 1910 are shown in Table 1. Variations in these dimensions were used at different plants according to local conditions to a maximum inside diameter of 9 in. and inside length of 54 in. However, the effective heat penetration in a 24 hr firing cycle and the tendency of the retort to bend limited the retort size. Use of the elliptical vessel was an attempt to present a stronger cross-section resisting the tendency to bend and to increase the burden without increasing the depth of heat penetration. One exception to the 48-54 in. length was the 60 in. retort used as early as 1905 at Palmerton by means of supporting the last 12 in. at the butt end with a specially designed furnace back-wall. This backwall construction with the 60 in. retort had been developed and used at Bethlehem by G. G. Con-vers and A. B. DeSaulles. An attempt was made at Blende, Colo. to use even larger retorts of the Rhenish type based on European practice and requiring much higher furnace temperatures. Satisfactory plastic clays capable of withstanding these temperatures were not available, and the plant never operated successfully. PREPARATION OF BATCH Composition of the clay retort by weight was 40 to 50 pct raw clay and the balance "grog." Generally speaking the mix consisted of 7 parts plastic clay to 9 parts grog by volume. Principal source of the clay used was the Cheltenham vein—sometimes referred to as "St. Louis city clay." A typical analysis was A12O3-31.0 pct, SiO2-50.0 pct, Fe2O3-2.5 pct, MgO-0.3 pct, CaO-1.5 pct and loss on ignition 14.0 pct. At the smelter the clay was weathered whenever possible and then crushed to 0.08 in. or finer. Grog consisted of calcined adobies, cleaned retort scrap and cleaned refuse fire brick such as old furnace brick, blast furnace linings, and others. Saggers from ceramic plants and calcined flint clay were later used. The grog materials were ground to 0.12 m. or finer. Occasionally coke dust up to 10 pct of the mix was substituted for a part of the grog following European practice.² Particle size of the grog has a major influence on the retort properties—the larger the grain, the better can the retort withstand thermal shocks, resist bending at furnace temperatures and resist corrosion from slag; the smaller the grain, the lower the loss of zinc vapor through the retort walls. Grog forms the skeleton of the retort, and the clay shrinks around its grains to act as a binder. In the drying process, the grog has a stabilizing effect on the drying rate, decreasing shrinkage and giving up previously absorbed water to the surrounding clay to minimize the danger of cracking or checking.² Grog and clay were mixed through a horizontal pug mill with 10 to 20 pct water added, depending on whether the retort was to be formed by hand or mechanically, more water being required for the hand process. The batch or "mud" extruded from the pug mill was cut in convenient lengths for handling, stacked in piles or in special rooms, covered with wet burlap and allowed to "rot" or age from 1 to 8 weeks to increase plasticity. HAND MOLDING If the retort was to be molded by hand, the mud was repugged after the rotting period and given to the molders. Their molds consisted of 3 sheet iron or wood cylinders, each one third the retort length and defining the outer shape of the retort. Beginning with the bottom section, mud was placed in the form and tamped with a rammer

Jan 1, 1950

Jan 4, 1951

By Walter von der Linden

INTRODUCTION There are three essential components for a modern longwall mining system: the coal cutting/loading machine, the self-advancing supports and the longwall conveying system. The latter consists of a face conveyor, a stageloader and a belt tall section arrangement (Figure 1). The longwall face conveyor is an integral component of the face equipment and has a threefold purpose: 1) continuous coal haulage. 2) track for cutter/loader . 3) reference/anchor rail for roof support advance. Further requirements for the longwall conveyor are horizontal flexibility for conveyor advance without interruption of haulage and cutter/loader tramming and vertical flexibility to cope with seam undulations.

Jan 1, 1981

By Eugene N. Cameron

Pegmatites occur in abundance in certain areas of South West Africa and in adjacent parts of northern Cape Province in the Union of South Africa. Some of the pegmatite deposits were prospected before World War I, and intermittent mining was done during the period between the two World Wars. The deposits of the Jooste lithium mines became an important source of lepidolite, and beryl, columbite-tantalite, wolframite, and other minerals were produced. Since World War I1 prospecting and mining have been carried on vigorously, with the result that South West Africa produced nearly 3000 tons of beryl during 1949 through 1953, together with more than 40,000 tons of lithium minerals, chiefly lepidolite and petalite. Small amounts of tantalite, columbite, and other minerals have also been produced during the postwar period. Most of this mineral production has come from two pegmatite areas roughly outlined in Fig. 1. One is the Karibib-Omaruru area of north central South West Africa. The second is the northeastern part of the Orange River pegmatite area, which extends into adjacent parts of Namaqualand, in northern Cape Province of the Union of South Africa

Sep 1, 1955

By C. R. Simcoe, T. J. Koppenaal

The effect of direct and alternating currents on the quench aging behavior in an Al-4 pct Cu alloy has been investigated by use of resistivity measurements. The reaction rate increases with direct current density in the investigated range of 1000 to 3000 amps per sq cm. Alternating current of a specific frequency is observed to decrease the reaction rate by a factor of about two. ErDMANN-JESNITZER et al.,1,2 investigated the effect of direct and alternating current on the quench and strain aging behavior of low-carbon iron. In both cases they observed that direct current accelerates the aging reaction and that an alternating current can completely inhibit the aging process. The purpose of the present research was to investigate these phenomena in the quench aging behavior of an Al-4 pct Cu alloy and to determine the correlation, if any, between the increase in the observed reaction rate and possible heating effects accompanying the aging with direct current. EXPERIMENTAL PROCEDURE The aluminum-base alloy used in this investigation contained 3.98 wt pct Cu (1.72 at. pct) with impurities of 0.003 pct Si, 0.002 pct Fe, and 0.001 pct Mg. The alloy was rolled into a ribbon about 0.36 mm thick and 3.7 mm wide. The ribbon was split end from end with the ends being used as electrical contacts and the central unsplit section, about 5.3 cm in length, serving as the specimen. Solution treatment was accomplished by quenching from a salt bath at 520° ± 2°C into water at 25° ±0.5°C; the specimen was immediately transferred to a liquid nitrogen bath. All aging was done at 75° ± 0.2°C in a rapidly stirred ethylene glycol bath. Resistivity measurements were made by the double potentio-metric method employing a standard resistor; for purposes of convenience, the resistance measurements were made at 77°K. The transfer of the specimen from the aging bath to a liquid nitrogen dewar was accomplished in less than 1 sec. The aging kinteics were studied with the specimen being aged under the influence of direct current, alternating current, and without any type of current. The amount of heating caused by direct currents was investigated by soldering a thermocouple on the specimen surface and measuring the temperature change after applying various current densities. The temperature was observed to increase (from 75°C, the aging temperature) about 0.8°, 3.0°, and 8.5°C with direct currents of 1000, 2000, and 3000 amp per sq cm, respectively. When employing alternating current, the circuit was monitored with an oscilloscope and adjustments made to produce a normal sine-wave pattern. RESULTS Prior investigations3'4 in the aging characteristics of A1-4 wt pct Cu have shown that the resistivity initially increases, reaches a maximum, and then decreases to values significantly lower than the as-quenched resistivity. This type of behavior is seen in Fig. 1 which shows the resistivity at 77°K as a function of aging time at 75°C observed in this investigation. At this aging temperature, the resistivity maximum is seen to occur in about 1 to 1-1/2 min and it further decreases to the as-quenched value in about 24 min. The behavior observed with the application of direct currents of 1000, 2000, and 3000 amp per sq cm during aging is shown in Fig. 2. With increasing current densities, (+) ?pmax decreases and the rate of the aging process increases. The time necessary to reach the as-quenched resistivity value decreases from 24 min for aging without current to about 16, 10, and 7 min for aging with 1000, 2000, and 3000 amp per sq cm direct current, respectively. Fig. 3 shows the results obtained when two changes were made during the aging with 2000 amp per sq cm

Jan 1, 1963

By R. M. Brick, Arthur Phillips, A. J. Smith

A PREVIOUS publication1§ has described the effect of quenching stresses on the lattice parameter values of high-purity aluminum-copper alloys particularly with reference to the solution and precipitation of CuA12. A similar study has been made of the aluminum-rich aluminum-magnesium alloys. Attention has been directed in the present investigation. to the magnitude of the quenching stresses as affected by the specimen size and shape, the number of solute atoms and the quenching rate. The effect of cooling stresses in causing plastic deformation or cracking has been considered in relation to the physical properties of the alloy. On reheating alloys in the two-phase field, the time required for precipitation to occur has been observed in connection with the degree of supersaturation, the rate of diffusion of the solute atoms as a function of the comparative atomic radii, degree of strain, temperature of reheating and grain size. A few qualitative comparisons on the relative effect of these factors have been drawn between the aluminum-copper alloys and the aluminum-magnesium alloys. STRAIN IN SOLID-SOLUTION ALLOYS A 10 per cent magnesium alloy in the form of chill-cast bars was furnished by the Aluminum Company of America through the courtesy of L. W. Kempf. Additional alloys were prepared using aluminum (99.95 per cent Al) and high-grade magnesium. The alloys listed in Table 1 were melted in an Acheson graphite crucible under a flux of fused MgCl2, CaC12, NaCl. Chill-cast rods were sealed under vacuum

Jan 1, 1935

By J. H. Swisher

HIGH-temperature anneals in wet hydrogen are widely used in research as a technique for decarburiz-ing Fe-C alloys. This technique is also used commercially in processing low-carbon steels for magnetic applications. The results of some calculations to be presented show that for temperatures up to 1100°C there is a critical temperature for maximizing the decarburization rate of alloys containing about 0.1 pct C. The low-temperature portion of the iron side of the Fe-C phase diagram1 is reproduced in Fig. 1. Preliminary calculations show that the critical temperature is between 727" and 905°C. In this range, the alloy contains two phases during heat treatment, ferrite and austenite. Decarburization therefore occurs by a process termed "diffusion accompanied by a phase change".' For intermediate stages of decarburization, the carbon concentration profile in a flat plate is shown in Fig. 2. The carbon content increases linearly from zero at the surface to a value, cB , at the two-phase boundary. cB is known from the phase diagram, see Fig. 1. At the interface where x = 5, the carbon content increases to ci, the initial concentration in the alloy. smith3 has derived an equation which describes the rate of movement of the boundary. With a rearrange-

Jan 1, 1969

By John T. Galey

In southwestern Pennsylvania 151 wells1 were completed during 1938, a total of 61 less than the preceding year. Of this number 81 were gas wells and 28 oil wells, which shows a considerable decline from 1937, when 108 gas wells and 64 oil wells were completed. However, 42 dry holes were drilled during 1938, which is two more than the previous year. Shallow Development—Gas No new extensions to old pools, or new wells that would indicate any substantial reserves, mere found during the year. However, a number of commercial wells and many dry holes were drilled to the Big Injun sand in Menallen township, Fayette County. One well had an initial open flow of 6 million cu. ft. In Rich Hill township, Greene County, one well producing, from the Big Injun sand, 2 million cu. ft. was brought in. Several other gas wells were completed in Shaler township, Alleghany County and Center township, Greene County, both of which had initial open flows of 1 million cu. ft. from the 30-ft. sand. Another well, in Aleppo township, Greene County, had an equal volume from the Gordon Stray sand. Oil Development has proceeded at a retarded rate because of the low price of Pennsylvania-grade crude. A total initial of only 205 bbl., an average of 7.3 bbl. per well, was developed. This is 1785 bbl. less than during 1937 and no new repressuring operations have been contemplated to prevent the declining production. The average price received for oil was $1.56 per barrel, with a high of $1.88 and a low of $1.34. This oil costs $1.94 per barrel2 to produce. The average price paid for Bradford

Jan 1, 1939

By John T. Galey

In southwestern Pennsylvania 151 wells1 were completed during 1938, a total of 61 less than the preceding year. Of this number 81 were gas wells and 28 oil wells, which shows a considerable decline from 1937, when 108 gas wells and 64 oil wells were completed. However, 42 dry holes were drilled during 1938, which is two more than the previous year. Shallow Development—Gas No new extensions to old pools, or new wells that would indicate any substantial reserves, mere found during the year. However, a number of commercial wells and many dry holes were drilled to the Big Injun sand in Menallen township, Fayette County. One well had an initial open flow of 6 million cu. ft. In Rich Hill township, Greene County, one well producing, from the Big Injun sand, 2 million cu. ft. was brought in. Several other gas wells were completed in Shaler township, Alleghany County and Center township, Greene County, both of which had initial open flows of 1 million cu. ft. from the 30-ft. sand. Another well, in Aleppo township, Greene County, had an equal volume from the Gordon Stray sand. Oil Development has proceeded at a retarded rate because of the low price of Pennsylvania-grade crude. A total initial of only 205 bbl., an average of 7.3 bbl. per well, was developed. This is 1785 bbl. less than during 1937 and no new repressuring operations have been contemplated to prevent the declining production. The average price received for oil was $1.56 per barrel, with a high of $1.88 and a low of $1.34. This oil costs $1.94 per barrel2 to produce. The average price paid for Bradford

Jan 1, 1939

By Nicholas J. Grant, Noboru Komatsu

Metallographic and X-ray studies were made of oxide dispersion strengthened Cu-12 vol pet SiO2 and Cu-3.5 vol pet Al2O3 alloys following time exposures at temperatures approaching the melting. point of the matrix metal. Changes in hardness, oxide particle size and crystal structure were studied to determine the time-temperature stability of these alloys. An interpretation of the mechanism of oxide agglomeration is proposed. One of the most striking features of dispersion strengthened metal-metal oxide alloys is their stability at elevated temperatures, both with respect to recrystallization and maintenance of mechanical properties after exposure at high temperatures. A small amount of work has been done on the re-crystallization phenomenon in dispersion hardened metal-metal oxide alloys'l and several theoretical treatments have been advanced regarding the stability of these alloys by Lenel and Ansell,8 and by Grant and his co-workers.9, 10 This paper reports on metallographic and X-ray studies following various heat treatments of Cu-AI2D3 and Cu-SiO2 alloys at elevated temperatures and the effect of subsequent cold work on the recrystallizalion temperature. An interpretation of the recrystallization behavior of this type of alloy, based on the decomposition and agglomeration of oxides, is proposed. EXPERIMENTAL PROCEDURE Cast ingot bars of copper-1.59 pet Si and Cu-0.77 pet Al, 7/8 in in diam, were annealed in argon for 80 hr at 1000CC for homogenization. The homogenized rods were machined into fine chips and ball milled. Milled particles in the range minus 20 to plus 60 mesh were separated for internal oxidation. The internal oxidation was accomplished by the same method used by Preston and Grant,9 except that the oxidalion temperature for the Cu-Si alloy was 750°C, and for the Cu-A1 alloy was 800°C. These powders were then hydrogen-reduced at 450°C, compacted in a copper container, evacuated at room temperature to 0.04 µ, and sealed for extrusion. They were extruded at 1400°F (760°C) with a ram speed of 55 in. per min for an extrusion ratio of 15.6 to 1 to give a rod 0.38 in. diam by about 3 ft long.

Jan 1, 1962