The block caving mining method is used to mine large orebodies in weak rock types. The layout for block caving requires that a considerable amount of development is carried out on the extraction drives and drawpoints at the bottom of the caving block. The development further weakens the rock mass, and stability problems arise in the extraction drives and extraction pillars. This paper describes the application of three-dimensional boundary element models in analysing alternative extraction level layouts for a block caving mine. The objectives were to establish whether the use of lateral pillars between drawpoints was warranted, and whether the lateral pillars should be offset or not. The stability of the rock mass within the pillars as well as the stability of the extraction drives were taken into account. The results showed that after undercutting, the horizontal and vertical stresses in the extraction level would be reduced. The lateral pillars would significantly improve the stability of the extraction pillars and extraction drives. There would be a minor improvement in stability if the lateral pillars were offset.

Jan 1, 1987

By O. G. Pauw

The relationships between mill power and pebble load, bulk density of the load, and circulating load were investigated on the pebble mills in the grinding circuit at Buffelsfontein Gold Mine. This paper describes the most significant relationships among the operating and control variables on the plant, and illustrates these by reference to experimental data gathered from the plant during operation. The results were used for the development of very successful multivariable peak-seeking controllers for the pebble load and bulk density of the load on these pebble mills. The peak-seeking control algorithms are described in detail. The control system has operated successfully at Buffelsfontein for more than 18 months and is still in operation.

Jan 1, 1985

By C. S. Erasmus, L. C. Woollacott

The distribution of gold loaded onto carbon particles from a carbon-in-pulp operation was measured by neutron activation analysis. The nature of the distribution is examined, and the implications for operating plants and CIP simulators are discussed.

Jan 1, 1992

By R. M. Stroh, D. F. H. Grave

In this paper ventilation planning methods are discussed, with particular reference to the application of computer techniques to the solving of the many problems associated with the forecasting of ventilation and refrigeration requirements in mines of high production rates going to depths and rock temperatures higher than previously experienced. The use of the Starfield-Dickson programmes for calculating heat flow into airways and advancing stopes is demonstrated in the case of ventilation planning on a large mine extending to a brief depth of over 3 km below the surface. The possible effects of new mining methods on ventilation requirements in the future is briefly discussed.

Results are presented on the elution of gold cyanide and base-metal cyanide complexes from strongand weakbase resins. It is shown that thiocyanate anions, zinc cyanide anions, and thiourea in acid solution are effective eluants of strong-base resins, but that it is generally necessary for electrowinning to be incorporated in the elution cycle if fast rates of elution are to be achieved. Weakbase resins are eluted with sodium hydroxide solution, which is shown to be far simpler and far more effective than the elution of strong-base resins. The effects of parameters such as concentration of the eluant, temperature, and electrowinning efficiency on the rate of elution of the resins are examined.

Jan 1, 1984

From a consideration of the functional requirements of a stope-support pack, simple design principles were developed. The material and dimensional properties of the different components of the pack were determined from a series of laboratory tests. The most important requirement for an adequate pack is that the cushioning layers of timber between the concrete brick layers should provide sufficient transverse reinforcement. The tendency of the compressed timber to creep is shown to be a serious limitation to pack performance and must therefore be an important consideration in the overall design of supports.

Jan 1, 1978

By A. O. Filmer

A study of the dissolution of gold from a pyrite concentrate and from various calcines is reported. The percentage extraction of gold was found to decrease with increasing sulphur content in the material leached because of the porosity of the materials, and particularly because of the passivation of the anodic dissolution of gold when the gold was In contact with other conducting minerals. This is explained in terms of the current-potential curves for the oxidation of gold and the reduction of dissolved oxygen.

Jan 1, 1982

By M. Cortie, L. Iorio

The amount of nitrogen contained in an austenitic stainless steel affects its properties significantly. The maximum content of nitrogen feasible in a range of experimental low-nickel austenitic stainless steels containing significant additions of copper is evaluated The nitrogen content is calculated based on published interaction coefficients, and by use of the FACT thermodynamic computer program and database. The differences between the two methods of prediction can be attributed to inaccuracies in the published interaction coefficients. The calculated nitrogen contents of some experimental alloys are compared with the actual nitrogen contents obtained when the alloys were produced in an induction furnace. The actual nitrogen contents obtained were higher than those predicted by either method, and this is believed to be due to a super saturation of nitrogen occurring in the melt, which was not relieved during the short period in which the charge was molten. It was evident that the experimental alloys can contain between 0,25 and 0,40 per cent nitrogen (depending on temperature, composition, and nitrogen pressure) when melted in a sealed induction furnace, and this is more than adequate for the purpose of forming and stabilizing the austenite phase.

Jan 1, 1994

By M. Nakamura, T. Akamatsu

Embankment dams are often constructed on soft rock foundations in Japan, so it is important to precisely predict deformation of the foundations due to fill placement at the design stage. In order to accurately evaluate the settlement and the strain of the rock foundation surface during construction, the influence of the scattering of the deformability of foundations on the deformation behaviour should be investigated. In this paper, a method of evaluating the settlement and the strain of the rock foundation surface during construction was studied with stochastic deformation analysis considering the scattering of the deformability of the dam foundation. Based on the analytical results, a dam foundation design using the deterministic method considering the scattering of its deformability was discussed. Da in Japan Uferdämme of auf weichen Felsfundamenten gebaut werden, ist es wichtig, die Verformung der Fundamente auf Grund der Platzierung der Aufschüttungen bereits in der Planungsphase genau vorherzusagen. Im Zusammenhang mit einer genauen Beurteilung der Senkung sowie der Belastung der Felsfundamentoberfläche während der Bauarbeiten sollte auch der Einfluss der Streuung der Verformbarkeit der Fundamente auf das Verformverhalten untersucht werden. In der vorliegenden Studie wurde die Bewertungsmethode zur der Senkung sowie der Belastung der Felsfundamentoberfläche während der Bauarbeiten mit Hilfe von Wahrscheinlichkeitsanalysen der Verformung unter besonderer Berücksichtigung der Streuung der Verformbarkeit der Dammfundamente untersucht. An Hand dieser analystischen Ergebnisse wurde das Design der Dammfundamente dann enthusiastisch mittels deterministischer Methoden hinsichtlich der Streuung der Verformbarkeit diskutiert. Comme les barrages en remblai sont souvent construits sur des fondations rocheuses tendres au Japon, il est essentiel de prévoir précisément les déformations des fondations causées par la mise en place du remblayage durant la phase de conception. Afin d’évaluer avec exactitude le tassement et la déformation de la surface du rocher de fondation durant la construction, l’effet de la dispersion de la déformabilité des fondations sur le comportement de déformation doit être étudié. Dans cette étude, l’auteur a étudié la méthode d’évaluation du tassement et de la déformation de la surface du rocher de fondation durant la construction en procédant à une analyse aléatoire/stochastique de la déformation et en prenant en considération la dispersion de la déformation des fondations du barrage. En se basant sur les résultats de l’analyse, la conception des fondations de barrage avec la méthode déterministe considérant la dispersion de sa déformabilité a été activement discutée.

Jan 1, 2003

By E. P. Gush

Diamonds, an enigma in a mineral resource sense. Chemically, diamonds are no more than carbon crystals in a cubic system-formed one might add under conditions of great pressure and temperature. They have certain physical properties which are fairly unique. They are very hard, they have a high refractive index, they luminesce, some of them fluoresce, they have a high specific gravity, they don't wet and they are a good conductor of heat. In a way, a rather clinical set of qualities. Of course, these qualities are what give diamonds their use and their beauty. It is on the emotional side that they get complex and stir memories of legends, of beauty, of wealth and romance, of war, happiness, bad luck and curses. It is on the emotional side that the value of a diamond is established, if such a thing is possible. Diamonds are extremely varied, there are more than 5000 categories into which they are sorted, so there is room at each point across the spectrum for their individualities to emerge, and accordingly their attractiveness to each buyer is unique.

Jan 1, 1994

From 19 November 1996, South African companies will be able to manage the impact their activities have on the environment in terms of international standards. The establishment of a registration scheme for environmental management systems was formally announced by the South African Bureau of Standards (SABS) (19 November 1996). At a function held at the SABS head office in Pretoria, Dr Jean du Plessis, President of the SABS, announced the launch of the SABS ISO 14001 registration scheme which is based upon ISO 14001, 'the internationally recognized yardstick for environmental management'.

Jan 1, 1997

By J. H. Bulloch

A study of fatigue-crack growth in a rail steel and an associated weld metal showed that fatigue cracks in the deformed rail steel had slightly higher growth rates than in undeformed rail steel. The crack growth in the weld metal was appreciably faster than either and exhibited plateaux that were above the upper bound reported for rail steels, The cyclic-life curves showed that, over an indicated service period of 8 years, both the deformed and the undeformed rail steels should not be prone to fatigue failures under the defined mechanical conditions, For the weld metal, the cyclic-life curves indicated the possibility of premature fatigue failures but, as al the input parameters represented a 'worst case' situation, this assessment could wel be ultra-conservative. In the rail steels at low levels, the extension of the fatigue cracks occurred by ductile striated growth. At a Kmax level of 35 MPa .J/n, cleavage facets formed initially on the surface of the fatigue fractures, and their incidence increased with Kmax until the onset of fast failure, The microstructure of the deformed rail steel exhibited cleavage facets at a slightly lower Kmaxvalue, and contained more cleavage facets at a given K level, than the microstructure of the undeformed rail steel. The average size of the cleavage facets agreed well with the pearlite nodule dimensions of 60 to 100 ILm. The microstructure of the weld metal was much coarser and contained columnar grains. At al f.K levels, the dominant fracture mode was cleavage, with small isolated regions of ductile striated fatigue cracks. The size of the cleavage facets varied from 150 to 600 ILm, and such a variation may be explained by the fact that cracking generally occurs in association with the pro-eutectoid ferite phase, and that this phase is distributed along some boundaries of prior austenite grains and the boundaries of the coarser columnar grains.

Jan 1, 1987

By J. D. Austin, D. G. Kringe

Rates of return realized on investments in the gold mines of the newer goldfields outside the Witwatersrand were calculated and analysed over various time intervals and on various bases. It is shown that these rates of return are strongly correlated with changes in the gold price and cannot be equated with the returns that are expected when investments are made, and that the changes in gold price also affect the rates of return on the Johannesburg Stock Exchange as a whole. These correlations are used, together with a limited application of the Capital Asset Pricing Model, to suggest the expected levels of threshold returns in real terms for new mining projects, for projects on existing mines, and for share valuations.

Jan 1, 1980

By David J. Haddock

On Wednesday, 6th July, 1988, 28 members of the Johannesburg Branch of The South African Institute of Mining and Metallurgy and their guests assembled at the Rand Refinery Sports Club, which is situated within the Refinery complex, to hear Dr Daniel Polnow, General Manager of the Refinery, give a very interesting lecture on the Rand Refinery Complex and its activities. Accounting for gold The South African Institute of Mining and Metallurgy will be holding a 3- or 4-day school in the third week of May 1989 on the topic 'Accounting for Gold'.

Jan 1, 1988

By B. R. Broekman, J. P. W. Bennie, P. D. K. Robinson, R. P. Viljoen

The theme of the Congress was 'Resources and Technology', the intention being to highlight those basic technical aspects in the disciplines of geology, mining, extractive metallurgy, and metals technology that are required for successful mineral-based operations. The technical programme covered a fairly broad field, as is appropriate for the CMMI Congress, and was generally considered to be of a high professional standard; informative and, with the exception of some minor hitches, well-run. Parallel sessions were held in the four disciplines. All were well attended, and despite tight presentation schedules, certain valuable discussions developed.

Jan 1, 1994

By C. Pohlandt

A literature survey of methods suitable for the determination of cyanides in process streams and effluents is presented. Of the large number of methods published, 92 are examined in detail, emphasis being placed on the selectivity of the methods, i.e. the extent to which they enable one to distinguish between ionic cyanide and metal-cyanide complexes. Methods designed for the determination of 'total cyanide' (i.e. ionic cyanide as well as coordinated cyanide) are evaluated critically. Other aspects of the methods are also considered, such as sensitivity, accuracy, speed, and freedom from interferences.

Jan 1, 1983

By R. M. S. Falcon, L. M. Falcon

The prediction of the mechanical behaviour of South African coal on the basis of current proximate and other chemical parameters gives rise to problems, and the use of ultimate analyses and inferred maceral and rank analyses, although it has improved the situation to some extent, is still not satisfactory. In an attempt to reach a new level of understanding, this paper gives an in-depth review of the fundamental petrographic characteristics of coal and compares these parameters with the main types of mechanical performance. A two-tiered system of primary and secondary parameters is proposed for the prediction of coal behaviour. The primary or inherent parameters include rank and organic composition. The secondary or extraneous factors include such parameters as mineral mater, cracks or cleats, degree of oxidation, and size. In addition, an explanation is offered of several anomalous behavioural conditions in some South African coals.

Jan 1, 1987

By L. A. Vermeulen

A simple argument shows that it is impossible for the flight of a rod in contact with a litter bar in a rotary mill to be initiated at that point on the upside of mill rotation when all the forces acting on the rod are in equilibrium. The argument was confirmed experimentally in a study showing that the lift of litter bars is a function of their height, that the rod velocity at the point of departure has a significant radial component, and that the subsequent flight of a rod is along a parabolic trajectory as predicted by elementary mechanics. A quantitative account of the observed effects, which is based on a dynamic theory of the sliding interaction between rods and litter bars, revealed interesting properties of the motions of rods down the surfaces of litter bars when the latter are in uniform circular motion during the rotation of a mill.

Jan 1, 1985

By P. H. S. W. Kulatilake

The paper introduces a computer simulation technique to estimate the target detection probabilities associated with search surveys. The technique takes into account the inherent randomness associated with the distributional properties of geologic targets. Use of the technique is illustrated through examples. The paper provides information as to how this technique can be used in obtaining the optimum sampling pattern and optimum spacing associated with target detection surveys.

Jan 1, 1987

By G. A. Wiebols, N. G. W. Cook, N. C. Joughin

Introductory remarks Dr N. G. W. Cook: This paper was published in your Journal in May of this year and you will, therefore, have had the opportunity of reading it over the past six months. I can state that experience has shown that the paper is substantially correct, but a number of questions have to be answered. The first question, Mr President, that I would be happy to answer, is how is it that one is able to cut hard, abrasive quartzite with a strength some six times greater than that of good concrete? The essence of the answer is that there is a tremendous difference between abrasion, or scratching, and cutting, or chipping. For example, it is well known that a diamond will scratch or abrade almost anything. It is also relatively easy to chip, crack or crush a diamond. As a demonstration I have here an ordinary bench grinder, and with the bench grinder I also have a piece of tool steel. The wheel on this bench grinder is a silicon carbide wheel, which is an extremely hard material, and the tool steel is much softer. In rock-cutting we use tungsten carbide for cutting the quartzite. The quartzite and the tool steel have roughly the same hardness. You can sharpen tungsten carbide with a silicon carbide wheel. In fact, this is done. It won't surprise any of you, therefore, when I show you that tool steel can be sharpened with silicon carbide. Now, what I propose to do is to change the configuration of this experiment and use the soft tool steel to cut silicon carbide, and if I can do that, I think you will agree that I have gone some way to being able to cut quartzite, which is about as hard as tool steel, with tungsten carbide, which is harder than quartzite. Let me do this. (Demonstrates.) That, I think, is a very clear demonstration of how it is possible, with a metal, to cut an extremely hard and brittle material. What, essentially, is the difference that we have here? In the first case, I held the tool with a relatively low force against the hard silicon carbide wheel. This generated a relatively low average stress, which was insufficient to fracture the carbide wheel. Nevertheless the protuberances on the silicon carbide wheel indented the tool steel and abraded it at a multiplicity of points, and quickly reduced the section of the tool steel that I held against the wheel. By changing the configuration and clamping my tool steel in a firm post, against the silicon carbide wheel, I changed these conditions very extensively. I now had a high force. I had to exert a considerable moment on that lever. The tool was anchored so that it could sustain these high forces, and they generated high stresses, which were adquate to fracture the silicon carbide. Now, what about wear? It so happens that, in these two experiments I have just done, the power I was using was about the same-a small fraction of a horse power.

May 1, 1968