By Chuanfu Zhang, Liwei Liang, Yanxin Wu, Jinliang Wang

"According to the reaction shaft operation characteristics during the flash smelting process, 15 groups of slag samples containing high Fe3O4 were prepared by some chemical reagents, and then the slag viscosities were measured using a RTW-10 type synthetic test instrument for melt physical property by the rotating cylinder method. The effects of Fe/SiO2 ratio (mFe/mSiO2), Fe3O4 content (wFe3O4), Cu2o), MgO content (WMgO) and Cao content (wCaO) on the slag viscosity were also studied. Results show that slag viscosity is decreased with the increase of temperature, mFe/mSiO2, wCu2o, wMgO and wCao, and with the decrease of wFe3O4, under the range of slag contents: mFe/mSiO2 1.36~1.78, wFe3O4 17.83%~21.18%, wCu2o 3.51%~8.34%m wNgI 2.21%~6.57%m w/caI 6.22%~9.387% and temperature range if 1250 o/c~1450 oC. Only wFe3O4m and w/caO have great influence on the slag viscosity when temperatures as high as 1400 oC. Only wFe3O4 and wCaO have great influence on the slag viscosity when temperatures as high as 1400 oC or so. To form a freeze slag with higher viscosity inside the reaction shaft, wFe3O4 should be more than 20% and wCaO should be less then 6%.IntroductionSince its appearance in 1949, Outokumpu flash smelting technology has making continuous innovation and has become the most competitive intensified smelting technology [1], widely considered to be the standard clean smelting process [2]. At present, flash smelting technology is adopted to newly build or reconstruct most of the world's copper or nickel smelting enterprise [3]. Reaction shaft is the most important part of the flash smelting furnace. During the flash smelting process, reaction shaft must be able to withstand the following harsh conditions at the same time: 1) high temperature varying from 1400 °C to 1500 °C. 2) strong oxidative atmosphere containing 50% - 80% oxygen. 3) solid particles and melt with speed up to l00 m/s. 4) high acidic or basic slag with strong chemical corrosiveness. 5) smelting gas containing 50% - 80% SO2. 6) matte with strong dissolution."

Jan 1, 2012

By Young-Dae Kim, Dong-Sic Kim, Jong-Jin Pak, Kyung-Hyo Do

"Sulfur is one of the most harmful elements in stainless steel (SIS) products and the specification of sulfur content is getting more severe for high grade SIS. In order to accurately control the desulfurization reaction in high chromium containing SIS melts, it is important to know the thermodynamic interaction between chromium and sulfur in Fe-Cr melts over a wide range of chromium content. In this study, the equilibrium sulfur distribution, Ls, between a Ca0-Alz03 slag and Fe-Cr-C,.,-S melts were measured under CO atmosphere in the temperature range of 1823-1923 K. The specific effect of chromium on the activity coefficient of sulfur in the melts was determined with the consideration of carbon effect on sulfur. A separate experiment was carried to determine. Ls between a slag and FeCr- S melts (Cr: 0-30 mass%) at 1873K to check the validity of the thermodynamic parameter determined in the present study.IntroductionFerritic stainless steels containing chromium (Cr) up to 30 mass% have been developed for a good corrosion resistance and a high formability to replace austenitic SIS. Especially, Sulfur (S) causes a reduction of high-temperature strength and the hydrogen induced cracking (HlC) in stainless steel for line pipes. [l]Many studies on the desulfurization of hot metal and liquid steel have been carried out for several decades and they used HzS-H2 gas equilibrium technique for measuring the effects of many alloying elements on the activity coefficient of S in liquid iron. However, the study on desulfurization of Fe-Cr melts was very scarce.[2] In order to accurately control the desulfurization reaction of high Cr stainless steel, it is essential to know the thermodynamic relation between Cr and S in Fe-Cr melt over a wide range of Cr content and temperature.In the present study, the thermodynamic interaction between Cr and S in liquid iron was determined by measuring the equilibrium distribution ratios of S between Fe-Cr-C,.1-S melts containing a wide range of Cr up to 30 mass% and a 55 mass%Ca0-45 mass%Alz03 slag of which the sulfide capacity was pre-determined using Fe-C,a1-S melts in the temperature range of 1823-1923 K. The validity of thermodynamic parameter determined in the present study was checked by measuring the S distribution between a Ca0-Alz03-Mg0 slag of known sulfide capacity and liquid Fe-Cr-S alloy at 1873 K. Using Wagner's formalism, the results of experiment were thermodynamically considered to determine the effect of a specific concentration of Cr on the activity coefficient of S in liquid iron."

Jan 1, 2014

By Christopher R. Casias

A basic methodology is presented (employing both standard and theoretical assessment, analysis. and data interpretation techniques) for classifying waste containing trace levels of radionuclldes. Despite increased regulatory requirements for handling. transporting. and disposing of such waste: (I) no formal characterization methodology has yet been Implemented. and (2) no limits have been set to define the point at which a waste material is considered to be low-level and below which it Is "below regulatory concern" (BRC) or can be considered to contain no more than a diminimus level of radioactivity (i.e . is nonradioactive). 'I1le concept of diminimus limits specific to waste streams and waste forms is introduced. and a mechanism fur evaluating waste In relation to BRC and diminimus limits is outlined. This methodology can be used to perform a complete and adequate characterization of waste for classification according to its level of radioactivity.

Jan 1, 1992

By Patrick R. Taylor

Ilmenite concentrate and methane are fed to a non-transferred arc thermal plasma reactor to produce a powder that is primarily TiC and Fe. This material has promising characteristics for powder metallurgy applications. Free energy minimization plots were used to predict the feasibility of the reaction. An estimate of the optimum molar ratio between the ilmenite concentrate and methane was made based on the mineral composition. Argon-helium mixtures were used as plasma gases. The effects of power input level, carrier gas flow rate, powder feeding rate, and methane-ilmenite molar ratio were studied and the behavior of the system characterized. Two different powder injection angles were tried. A mathematical model to describe the temperature profiles in the reactor was formulated and solved. The product has been characterized by x-ray diffraction and atomic absorption. A conversion of 97 % of Ti to TiC was achieved. It was found that minor amounts of titanium oxides, iron carbide and free carbon are also present. TEM and SEM were used to study the morphology.

Jan 1, 1996

By G. C. Yao

Iron and silicon impurities can form needle and branch shape intermetallie compounds in molten aluminum when there is no manganese. It is difficult to separate them from molten aluminum by electromagnetic separation. The Fe-Si-AI and Fe-AI intcrmetallic compounds were transformed into Mn-Fe-Si-AI and Mn-Fe-AI compounds by the addition of manganesc into molten aluminum, In molten aluminum the morphology of these intermetallic compound particles is lumpish and spherical. Migration resistance of these impurity particles is small, which is beneficial to separation. FeSiMnAl4 and FeMnAl6 arc paramagnetic. These impurity particles can be moved by magnetic force and can be separated from the molten aluminum.

Jan 1, 2003

By Robert P. Stevens

It is important for a refractory supplier to make systematic petro-graphic examinations of products which have been in service in the furnaces and kilns of customers. The petrographic examination of refractory service samples involves the microscopic study of polished and/or thin sections, supplemented by electron probe microanalysis, as well as the bulk chemical and XRD analysis of zones in the samples. The evolution of the A. P. Green Refractories Company petrographic laboratory is described, and the application of petrographic methods is illustrated in the examination of service refractories from a Portland cement rotary kiln and an AOD stainless steel vessel. The objectives of such studies are to assist the customer in the solution of his refractory problems, and to accumulate data which are of use in the design of improved refractory products.

Jan 1, 1981

By Feng Liu, Bingji Yan, Zhiwen Shi, Hongwei Guo, Jianliang Zhang

During production of a large quantity of steel, slag is produced at the same time. This paper chooses blast furnace slag (BFS) as the main material for the research. The purpose of the research is to explore its optimal physicochemical properties and the use of BFS in building stone field. The paper elaborates the experimentation process of producing glass-ceramics and presents the results. The results show that SiO2 content in BFS and amount of Cr2O3 and Fe2O3 added as nucleating agents have certain effect on the properties of glass-ceramics. The results also show that the exothermic peak temperature of base glass is the lowest when adding 20% SiO2 to the BFS, and 2% Cr2O3 and 3% Fe2O3 as nucleating agents, which makes easy crystallization and optimal properties of the glass-ceramics.

Jan 1, 2015

By Chuanhong Li, Zuohua Lin, Zhancheng Guo

"Catalytic mechanism of CeO2 in combustion of coals was investigated in this paper. Catalytic combustion of four kinds of coals with different metamorphic grades by CeO2 was examined, suggesting that catalytic function of CeO2 increases with increase of metamorphic grade of the coals. One important reason for CeO2 promoting combustion of the coals is that pyrolysis of anthracite is advanced by CeO2, which not only raises the pyrolysis rate and pyrolysis conversion ratio, but increases contents of light components in pyrolysis gas; and both pore space and specific surface area of the pyrolysis char are enlarged by CeO2, which is another reason. In order to realize in situ catalysis for reducing catalyst consumption, it is crucial to increase catalyst particle number and enhance the bonding force between catalyst and coal. In addition, remarkable energy saving effect was observed when a nanometer calcium-based rare earth catalyst obtained by hydro-thermal synthesis was applied to catalytic combustion of coal injection into blast furnace.Introduction Coal combustion is acknowledged as one of the most important coal applications. Since addition of catalysts could reduce the ignition temperature of pulverized coal and accelerate the coal combustion, catalytic combustion is generally accepted as an effective measure to realize fast combustion of coal. Furthermore, different catalysts added may produce different effects on ignition temperature of coal. It is reported activity of catalysts with the same cation follows this order: OH->CO3 2->Cl->SO4 2-; while that of the catalysts which have the same anion follows: Cs+>Rb+>K+>Na+>Ba2+>Li+>Sr2+>Ca2+>Mg2+>Be2+ [1-4] .Due to the special physical and chemical structure, CeO2 plays an important role in the catalysis field. Many literatures point out that CeO2 not only has great catalytic effect on energy conversion, succeeded in catalyzing combustion of gaseous fuels such as CH4, CO, etc. but also can catalyze combustion of some liquid and solid fuels such as JP-10, black carbon, carbon deposit in the automobile exhausts and so on [5-9].Pyrolysis, the first step of combustion, directly influences ignition temperature and combustion rate of coals. So a great variety of catalysts were applied to catalyze pyrolysis of coals. And plenty of studies suggest that the alkali and alkaline-earth metal compounds inherent in the coals show apparent catalytic effect on coal pyrolysis. Meanwhile, addition of alkali and alkaline-earth metals into coal combustion process also indicates obvious catalysis effect, accelerating coal pyrolysis, improving pyrolysis conversion ratio, increasing contents of pyrolysis gases and changing composition of the pyrolysis gases [10-15].Although alkali and alkaline-earth metal compounds have good catalysis effect on coal combustion, their application in the catalysis field was limited because of their erosive attack to the combustion equipments. In contrast, CeO2, as a substitution of the traditional coal catalysts, presents widely potential application due to its good catalysis ability, non-corrosive and nontoxic. However, investigation on CeO2 catalyzing coal combustion is rarely reported. In this work, catalytic mechanism of CeO2 in coal combustion was studied, in an attempt to provide theoretical foundation for developing new catalysis technologies."

Jan 1, 2009

By Katsunori Yamaguchi

A new technique for the removal of tramp-elements from steel scrap has been required from the viewpoint of saving energy and protection of environment. In order to obtain fundamental information on the removal of copper, tin and zinc from molten iron, the extraction method by using of phase separation in the liquid Fe-Pb-C system was investigated at 1453K A mixture of iron, lead and carbon melted in a carbon crucible separates into two phases of lead and iron containing carbon. The compositions on the miscibility gap in' the Fe-Pb-C system are 95A%Fe-4.5%C-0.l %Pb and 99.9%Pb-0.1 %Fe. The distribution ratios of copper, tin and zinc between the lead and the iron phases, Lx=[masso/uX in molten Pb]/(masso/uX in molten Fe), are 2.2, 2.2 and lA, respectively. Seventy percent of copper and tin from iron scrap can be eliminated with comparable lead addition. Gold, silver and palladium are enriched in the lead rich phase, on the contrary platinum and rhodium are more distributed to the iron rich phase than to the lead phase.

Jan 1, 2003

By S. E. Khalafalla

A method for preparing ferrochromium alloys containing less than 2 pct carbon has been devised in a single vacuum furnace reactor. This method can conserve chromium and should reduce the capital and energy requirements relative to chromite electrothermal reduction. Reduced products containing less than 2 and as low as 0.01 wt pct carbon were obtained by reacting pellets of chromite and carbonaceous reductant mixtures at pressures of 0.1 to 1 ton and temperatures of 1,230° to 1,320° C. The extent of reduction increased with increased temperature and decreased pressure; however, operating conditions were limited due to the onset of significant chromium vaporization at higher temperatures and lower pressures. Foundry coke, anthracite, and carbon black were found to be superior to graphite as reductants. The reduction of chromite to metallics was found to proceed via the carbide intermediates Fe3C or Cr3C2. Lime accelerates the. rate of solid state reduction of chromite and can shorten the furnacin1r time at 1,3000 C under vacuum from 13 hours to less than three hours. Additional lime and silica are added to the hot reduced chromite after releasing the vacuum and raising the furnace. temperature to 1, 700° C. Soaking the charge for about 20 minutes gave a button of low carbon ferrochromium alloy beneath a well-defined slag layer.

Jan 1, 1985

By Brian Lightfoot

Ausmelt technology is a versatile bath smelting technology with application in many waste treatment fields at low capital and operating cost. Heavy metals extracted from wastes may be recycled to mainstream use and the slags produced will be inert and suitable for use as aggregate, shotblasting grit or other applications.

Jan 1, 1994

By Satu Strömberg

Four different nickel concentrates were oxidized in a laboratory scale laminar flow furnace in simulated flash smelting conditions. The major nickel- and iron-bearing minerals in the con- centrates were pentlandite, violarite, gersdorffite, and pyrite and pyrrhotite, respectively. Thermal decomposition, ignition and oxidation behavior of nickel and iron sulfides were examined by using optical and scanning electron microscopy. General reactivity of the concentrates was monitored with sulfur removal which was most effective in violarite-based concentrate. Pentlandite-concentrates needed higher experimental temperatures for complete desulfurization and gersdorffite-based concentrate contained 5 - 10 % of the original sulfur even in the most oxidizing conditions studied (1 100°C, 50 vol-% 02). The reactivity of the iron minerals was found to depend on the other minerals present in the concentrate. In this paper, the observed re- action products and mineralogical changes are presented and preliminary conclusions of possible reaction mechanisms of nickel-bearing minerals are discussed.

Jan 1, 1997

By M. Okido, O. Takai, Z. Zhao, M. Ishikawa, R. Ichino, K. Kuroda

"Electrolytic method was applied to calcium phosphate coating on titanium plates as an excellent technique for high density and intensive contact of coated films on biomaterials. The effect of H2O 2 as oxidation reagent on coating characteristics was examined to obtain biomineral films. Solution was containing 7.0 X 10·3 mol/dm3 ofCaC12 and 3.0 X 10·2 of Ca(H2PO4)z, kept at 55 ""C. All deposits were hydroxyapatite (HAp) in this study, independent of H2O 2 concentration, applied cathodic potential and solution pH. In the case of H2O 2 addition, an increase in cathode current started at the low potential, namely, ca. -0.2 V (vs. SCE). In contrast, the current increased at more than ca. -1.4 V in the solution without H2O 2 addition. H2O 2 appeared to be an effective reagent for increasing nucleation density and improving adhesion of deposits on titanium plates.IntroductionIn recent years, many researches have been undertaken to develop the techniques of calcium phosphate coating on titanium or bioglass for medical implantation. High density and intensive adhesion of coating are necessary for adding bioaffinity to these materials and for inducing bone morphogenesis on them when implanted in human body.1) Electrolytic deposition has been a newly developed method as high-speed deposition process. By this method, the supersaturation of calcium phosphate can be increased just in the vicinity of metal substrates and the heterogeneous nucleation is promoted on them. In this process, H2O is reduced according to eq. (1) on the cathodically polarized electrode"

Jan 1, 2000

By Fuqiang Guo

Scorodite (FeAsO4, 2H2O) is suitable mineral carrier for immobilization of arsenic-rich wastes. Its stability is, however, highly pH dependent (typically at 4 ≤ pH ≤ 7) and satisfactory only under oxic disposal conditions. In thiswork an encapsulation process using mineralized gels of aluminum hydroxy-oxides is developed to enhance the stability of scorodite under wider pH and redox potential range conditions. The encapsulation involves blending and ageing of synthetic scorodite produced by McGill’s atmospheric scorodite process with aluminum hydroxyl gels derived from controlled hydrolysis of aluminum salts. The amorphous hydrolyzed Al-gel encapsulates the scorodite particles,which upon short-term aging transforms into crystalline Al (OH)3/AlOOH mineral phases providing a robust protection microscopic barrier. Long-termstability testing demonstrates the encapsulation systemto be highly effective in suppressing arsenic release under either oxic or anoxic (100 mV < Eh < 600 mV) potential and neutral-alkaline pH (7 ≤ pH ≤ 9) ranges.

By Kenneth C. Mills

Interfacial phenomena can have a dramatic effect on the separation of phases. Furthermore, since they involve surface-active materials, concentrations at ppm levels are enough to cause dramatic effects on separation processes. The effects of (i) emulsification, (ii) contact angle and wettability and (iii) Marangoni flows on phase separation are reviewed.

Jan 1, 1999

By Richard D. Hagni

Although the economically important uranium minerals are difficult to recognize under the ore microscope, they can be identified by a combination of qualitative and quantitative techniques. Useful quantitative techniques include indentation hardness, percent reflectance, spectral reflectance curves, and color coordinates. The latter two properties are especially distinctive for the primary urahlferous minerals uraninite, coffinite, brannerlte, and davidite. Together with the quantitative properties of indentation hardness and reflectance, the character and color of internal reflections are distinctive for many of the secondary uranium minerals. Ore microscopic techniques also provide an excellent means for determining the intergrowths of these minerals with other ore and gangue minerals. Such intergrowths are important to an understanding of the genesis of uranium deposits, and they may be important to uranium extractions.

Jan 1, 1981

By M. Yoshida, S. Hanada, T. Takasugi

"A study has been conducted to examine the effect of ternary alloying elements on high temperature deformation of the C15 NbCr2 based intermetallics in Nb-Cr-X (X=V, Mo and W) alloy systems, which have attractive properties as high temperature structural materials. The high temperature deformation of the C15 NbCr2 intermetallics can be improved by two alloying methods. One method is based on geometrical consideration for site occupation and atomic size factor of component elements and additive elements in the single phase C15 lattice; addition of Mo and V can promote dislocation movement without introducing significant hardening. The other method is based on microstructural modification through ternary alloying; moderate addition of these elements results in a variety of duplex microstructure consisting of the C15 phase and bee solid solution without forming any intermediate phases, and can enhance the high temperature deformability. Particularly, alloys with duplex microstructure equilibrating with Cr-rich bee solid solution is shown to exhibit superior deform ability. Also, lattice property of the additive atoms in the C15 structure and phase relation between the C15 structure and the bee solid solution are investigated by OM, XRD, TEM and ALCHEMI observations and then discussed in association with observed mechanical behavior.IntroductionLaves intermetallics with AB2 stoichiometry belong to the largest group in a large number of intermetallics with various kind of crystal structures, and have a variation of the cubic CIS, the hexagonal C14 and the dihexagonal C36 structures, depending on stacking sequence of XYZ type, each of which consists of four interpenetrating atomic layers (1-3). Some of the Laves intermetallics have good functional properties and therefore are considered to be used as, for instance, magnetic materials, magneto-optical materials, hydrogen storage materials and superconducting materials (2). Also, the Laves intermetallics are considered to be good candidate as high temperature structural materials operating at high temperatures and in severe environment because they have high melting point, low density, and potential resistance to corrosion and oxidation. However, the Laves intermetallics are very brittle at low temperatures because they consist of complex crystal structures similar to many other intermetallics."

Jan 1, 1996

By Onuralp Yiicel, Ozlem Okur, Murat Alkan

"In this study, Co-Cr-Mo alloys were produced using a mixture of Co304, Cr203 and Mo03 powders with Al powders by a Self-propagating high temperature synthesis process. SHS is a process of material synthesis that has revealed a number of reactants combinations capable of much higher energy release than conventional explosives. Al203 is added to the mixture to decrease the adiabatic temperature of the system. The thermodynamic simulations and the calculations of adiabatic temperature were examined with FactSage 6.2. In the SHS experiments, different Co304/ Cr203/Mo03 ratios were examined, and their effects on the metal recovery and alloy compositions were carried out. The samples were characterized by using chemical analysis, XRD, XRF and SEM/EDS techniques.IntroductionSelf Propagating High Temperature Synthesis (SHS) has significant advantages compared to the high technology furnace applications, such as very short processing time, simple operation, low energy requirement and low cost [l, 2]. In a SHS process, the ignition starts the combustion and propagates throughout the reactant mixture yielding the desired product. However, the disadvantages of the process such as inhomogeneous or unreacted products due to undesirable reaction rates needs to be overcome by changing some parameters such as ignition temperature, particle size, additive, atmosphere etc. [3, 4]. This work aims to establish a scientific and engineering background in the production of some cast Co-Cr-Mo master alloys via SHS (Self Propagating High Temperature Synthesis) metallurgy which is attractive process technique regarding fast and low-cost production ability of cast alloys."

Jan 1, 2013

By Masatoshi Ogasawara

Saganoseki smelter & refinery operated two flash smelting furnaces, producing a combined 330,000 metric tons per year (hereinafter mtpy) of copper. [n 1996, however, it successfully shifted to a single fumace operation while maintaining production at the same level. Since then, the production capacity has been further increased to the present 470,000 mtpy by technological improvements. Also, in order to reduce the converter load which represents a bottleneck in efforts to increase production, the matte grade was gradually increased and currently runs at 65 to 66% attaining the low copper content in the slag (hereinafter slag loss) of 0.7 to 0.8%. This &apos; paper introduces some improvements, recent operation results and thermodynamic analyses.

Jan 1, 2003

By Nicholas Zabaras, Deep Samanta

"Solidification of metal aluminum and aluminum alloys is modeled on uneven surfaces characterized by sinusoidal curves. Wavelengths and amplitudes of these sinusoidal surfaces are varied to study their effects on processes like solidification, macro-segregation and inverse segregation. Solidification and macro-segregation are modeled using a slightly modified form of a stabilized finite element method developed recently to model high Rayleigh number solidification and porous media flows. For pure metal solidification, the effect of varying amplitudes and wavelengths is observed in heat transfer, fluid-flow ~nd phase change processes. The relative importance of shrinkage driven flow and solutal convection on the redistribution of solute for an alloy solidifying in a rectangular cavity is compared. The analysis is then extended by modifying one of the surfaces to a sinusoid. In this case the effects of varying amplitudes and wavelengths are studied in heat transfer, fluid flow, phase change, macro-segregation and inverse segregation processes.1 IntroductionTransport phenomenon during solidification of alloys is a major cause ofcasting defects such as segregation, micro-voids, hot tears, porosity, internal and surface cracks. Heat flow across metal and mold surfaces directly affects the phase change process and plays an important role in determining freezing conditions within the metal. In alloys, natural convection and shrinkage play an important role in determining the final solute redistribution, macrosegregation and evolution of solid macromorphology. Surface unevenness plays an important role during the early stages of solidification. It influences the heat transfer rate and fluid flow in the melt, which in turn affect the morphology and shape of the solid-liquid interface. The effect of surface unevenness on solute redistribution is important during solidification of alloys, where solute driven flow in the mushy zone is prominent. Thevik and Mo in [7] and [8] used a one dimensional model for studying surface segregation and macrosegregation in alloys under the influence of exudation and solidification shrinkage. Air-gap formation in their model was expressed through a variable convective heat transfer coefficient at the boundary. Tsai et al. in [3] and [4] have modeled macrosegregation in an aluminum-copper alloy driven by shrinkage and solutal convection. They used a single domain model based on mixture theory and solved the transport equations using finite difference methods. Our aim is to model solidification of aluminum followed by macrosegregation and inverse segregation in aluminum-copper alloys on uneven surfaces by finite element methods. These surfaces are modeled as sinusoids characterized by amplitudes, ?s and wavelengths, As, By varying As and ?s, changes in heat transfer, fluid flow, phase-change and macrosegregation are studied."

Jan 1, 2004