By Orlando C. Gaspar

The textures of the ores, the fine mineral intergrowths, the complex distribution of the deleterious minor elements, and the low base metal contents in some ore types, pose many technological problems to the beneficiation of the volcanogenic massive sulphides occurring in the Iberian Pyrite Belt. In particular fine intergrowths of the base metal sulphides with pyrite impose extremely fine liberation sizes (Kao=15 to 25um). The mineralogical, textural and metallogenic studies have provided an understanding of the distribution of vertical and lateral metal zoning in the ore bodies. Mapping of the ore types, carried out by mine geologists, and the metal zoning patterns computed from data base have shown that ore types are distributed as ore lenses, and that vertical and lateral base metal zoning exists in several orebodies. Since ore processing efficiency is affected by ore textures, and because the same mineral often shows different textural features, a relationship between the textures of the feed ores and those of the middlings must be established for all ore types defined at the deposit scale. For supplying, on time, the information needed for the optimization of the concentration processes, empirical methods of determining the mineralogical and textural characteristics of the several ore types have been developed.

Jan 1, 1995

By Norimasa Yamasaki, Masao Kurosaki

"The effects of plating conditions on the crystal orientation of electrodeposited zinc were investigated by varying elecyrolyte flow rate and current density. Precipitation of the Zn (00 • 2) basal plane is promoted at lower current density and higher flow velocity. Effect of the flow velocity on the mass transport was evaluated based on the polarization measurement in which Cu was used as the tracer. As a result, it has been clarified that the crystal orientation of electrodeposited zinc can be uniquely arranged by the overvoltage (iU0.5) that can be simply calculated by considering -the current density and boundary layer thickness. At the same time, the electrode potential during electrodeposition that can be calculated by using a model based on the competitive reactions of hydrogen reduction 'and zinc reduction exhibits an extremely good correlation with the crystal orientation of electrodeposited zinc.Introduction Electrogalvanized steel sheet has better surface properties than hot-dip galvanized steel sheet, and is used in home electric appliance and automobile applications. Factors such as crystal morphology, crystal orientation and surface roughness have a large influence on its appliance, formability and corrosion resistance [1-3].Electrolysis, condition, bath composition and alloying elements are reported as factors that affect the crystal orientation of the electrogalvanized coating. Factors that can be controlled on time in the production site are electrolysis condition that-is current density and plating solution flow velocity.Some studies[4-6] report that the crystal- orientation of the Zn(00 • 2) plane is increased by promoting, the mass transfer of zinc ions in the plating solution or decreasing the concentration overvoltage, but did not investigate in detail the plating solution flow conditions in the plating cell nor quantitatively determine the effects of both current density and plating solution flow conditions on the crystal orientation of ' electrodeposited zinc."

Jan 1, 2000

By Nicholas Zabaras, Deep Samanta

"Solidification of metal aluminum and aluminum alloys is modeled on uneven surfaces characterized by sinusoidal curves. Wavelengths and amplitudes of these sinusoidal surfaces are varied to study their effects on processes like solidification, macro-segregation and inverse segregation. Solidification and macro-segregation are modeled using a slightly modified form of a stabilized finite element method developed recently to model high Rayleigh number solidification and porous media flows. For pure metal solidification, the effect of varying amplitudes and wavelengths is observed in heat transfer, fluid-flow ~nd phase change processes. The relative importance of shrinkage driven flow and solutal convection on the redistribution of solute for an alloy solidifying in a rectangular cavity is compared. The analysis is then extended by modifying one of the surfaces to a sinusoid. In this case the effects of varying amplitudes and wavelengths are studied in heat transfer, fluid flow, phase change, macro-segregation and inverse segregation processes.1 IntroductionTransport phenomenon during solidification of alloys is a major cause ofcasting defects such as segregation, micro-voids, hot tears, porosity, internal and surface cracks. Heat flow across metal and mold surfaces directly affects the phase change process and plays an important role in determining freezing conditions within the metal. In alloys, natural convection and shrinkage play an important role in determining the final solute redistribution, macrosegregation and evolution of solid macromorphology. Surface unevenness plays an important role during the early stages of solidification. It influences the heat transfer rate and fluid flow in the melt, which in turn affect the morphology and shape of the solid-liquid interface. The effect of surface unevenness on solute redistribution is important during solidification of alloys, where solute driven flow in the mushy zone is prominent. Thevik and Mo in [7] and [8] used a one dimensional model for studying surface segregation and macrosegregation in alloys under the influence of exudation and solidification shrinkage. Air-gap formation in their model was expressed through a variable convective heat transfer coefficient at the boundary. Tsai et al. in [3] and [4] have modeled macrosegregation in an aluminum-copper alloy driven by shrinkage and solutal convection. They used a single domain model based on mixture theory and solved the transport equations using finite difference methods. Our aim is to model solidification of aluminum followed by macrosegregation and inverse segregation in aluminum-copper alloys on uneven surfaces by finite element methods. These surfaces are modeled as sinusoids characterized by amplitudes, ?s and wavelengths, As, By varying As and ?s, changes in heat transfer, fluid flow, phase-change and macrosegregation are studied."

Jan 1, 2004

By F. Kongoli

Viscosity is an important parameter of copper smelting and converting processes. It affects the settling of matte or metal droplets in the slag, distribution of elements etc, Despite this importance, confusion exists on the viscosity of copper smelting slags as a result of disagreements found among the measured viscosity data of several authors especially in the slags of high ferric iron content and close to magnetite precipitation. In this work a critical review of the existing data on the viscosity of copper smelting slags has been first carried out and the effect of oxygen potential on the viscosity of copper smelting slags has been clarified through a coupled quantification of viscosity and liquidus temperature. The confusion in the literature has been clarified and the importance of the relation between the viscosity and the liquidus temperature is discussed,

Jan 1, 2003

By Burcu Ertug, Necip Ünlü

"On average, one out of two glass bottles coming on to the market is provided by recycling processes in Europe. Glass recycling has been started by the early of 1970s in Turkey, and the recycling amount has been reached to 70 thousand tons recently, while 4.2 million tons which represents only 25 percent of total glass manufactured, is the amount of glass collected annually for recycling in the world. The glass recycle process basically involves collecting, sorting, then crushing and grinding after which glass cullet is produced as the secondary raw material. Removing of the contaminants from the glass cullet, and then melting are the next steps. In this study, recent developments of 100% recyclable without any deterioration in quality, and never decomposable glass, are discussed detailed in terms of glass production processes.1.IntroductionIn many countries, waste glass constitutes a large proportion of solid wastes, and recycling the glass is a major environmental problem all over the world [1]. Among the diverse types of waste, glass is one of the most valuable recycling materials because it can be revived and recycled completely and hardly decomposes [2]. Between 80% and 85% of the mass output from the worldwide glass industry is either in the form of containers for the food, beverage, and pharmaceutical industries, or flat glass for building construction or for motor vehicle manufacture. Other product segments, whilst only constituting about 15% of the mass output, produce high value technical and consumer products by comparison with container and flat glass [3].In the present study, the recycling of Liquid Crystal Display (LCD), Cathode Ray Tubes (CRT) and Printed Circuit Boards (PCB) were examined. The production of glasses and glass-ceramics from glass cullet, synthesis of different compounds from recycled glass were other subjects of interest. The use of recycled glass for construction industry and using glass as aggregate were emphasized. Finally the recovery of glass fibers were investigated."

Jan 1, 2012

By Yoichi Takeda

Copper solubility in SiO2-CaO-FeOx slag equilibrated with copper matte in 10% SO2 atmosphere at 1573K was estimated. Essential parameters are activity coefficients of copper oxide and sulfide, oxygen and sulfur potentials and activity of copper in the slag-matte system. A large number of experiments provide proper parameters to calculate copper solubility in slag, A classical thcrmodynamic model postulating CuO0.5 and CuS0.5 moleculcs assists in estimating copper solubility in slag. Additions of Si02 and CaO reduce copper solubility almost in any condition. Copper loss, that is function copper solubility and slag volume, in the silica saturated SiO2-FeO. binary slag is minimally equilibrated with less than 66% copper matte while copper loss in the 50% FeO.-SiO2-CaO ternary slag saturated with 2CaOSiO2 is minimally equilibrated with over 66% copper matte. This slag composition has potential for continuous copper converting, direct copper production or high-grade matte production.

Jan 1, 2003

By A. S. Usrnani

Due to both turbulence and the highly variable geometry of castings, a realistic numerical simulation of the metal flow is prohibitvely expensive with current technology. However, when the chief purpose is to achieve realistic thermal fields a precise How simulation is not necessarily required. In this paper we assume a laminar flow regime and obtain the flow field by solving the incompressible Navier-Stokes Equations using a velocity-pressure segregated semi-implicit finite element method. The free metal surface is predicted by advecting a pseudo-concentration function via the computed How field. This involves an explicit finite element solution of a pure advection equation. The thermal field is calculated by solving the convective-diffusive energy equation by an explicit finite element method using the computed flow field and the location of the free surface. All the advection terms are discretized using a Taylor-Galerkin method. The interface between the metal and mould is modelled using special interface elements. The model is demonstrated by solving practical example problems. The results show that a sharp thermal front is maintained during the course of filling without excessive diffusion. The heat diffusion in the mould can be controlled by varying the metal mould heat transfer coefficient.

Jan 1, 1994

By Roberto Parreiras Tavares, Frederico da Costa Fernandes, Guilherme Antonio Defendi, Vangleik Ferreira da Cruz, Júlio César de Sousa Pena

"Near-net-shape casting is an important area of research in the iron and steel industry today. Among the near-net-shape casting processes, the single-belt caster seems to be the most promising, since it is the only one that can achieve levels of productivity similar to those obtained with conventional continuous casting machines. One of the most important aspects in the single-belt casting is the feeding system used to deliver liquid metal over the belt. This system determines the velocity distribution and the levels of turbulence of the liquid metal and affects the quality of the strips. In the present work, a metal delivery system having a simple geometry was proposed. Using the CFD code CFX 5.6, a mathematical model to simulate three-dimensional turbulent fluid flow and heat transfer in that system has been developed. This model was used to analyze different configurations of the metal delivery system and the free surface shape of the fluid was also determined. A physical model of the feeding system was built and used to validate the predictions of the mathematical model. The fluid flow calculations have been validated by dye injection experiments and laser doppler anemometry. Measurements of the free surface levels have also been performed. These experiments provided supporting evidence for the predictions of the mathematical model.IntroductionTo maintain its competitiveness in the present market, the metallurgical sector, particularly the steelmaking companies, are developing new techniques of production. Some of these new processes are focussed on the strip casting technologies. Among these technologies, the SingleBelt process is considered the most interesting option, reducing the number of rolling steps and, consequently, the final cost of the product, especially the part associated to the energy consumption (fuel and/or electric energy). This process can also reach levels of productivity that can not be matched by other strip casting methods(1). One of the most important aspects concerning these new processes is related to the liquid metal delivery system. This system can have a significant effect on the final quality of the strips, since it determines the velocity distribution and the levels of turbulence of the liquid metal."

Jan 1, 2004

By Hong Yong Sohn, Miguel Olivas-Martinez, Zhixue Yuan

A novel flash ironmaking process that directly reduces iron oxide concentrate particles by gas is under development. The goal of this work was to study the possibility of reoxidation of iron particles in various gas mixtures. As the product iron cools down in the lower part of the flash reactor, conditions may become favorable for reoxidation because of equilibrium and high reactivity of iron particles. The effects of temperature (823 – 973 K) and H2O partial pressure (40 – 100 pct., Ptotal = 86.1 kPa) on the reoxidation rate were examined. The pressure dependence was first order with respect to water vapor, and the activation energy was 146 kJ/mol. A complete rate equation that adequately represents the experimental data was developed. For oxidation in O2-N2 mixtures, the effects of temperature (673 – 873 K) and O2 partial pressure (5 – 21 pct., Ptotal = 86.1 kPa) were determined. Reoxidation in pure CO2 was also investigated at 873 – 1073 K for comparison.

Jan 1, 2014

By Wenbo Luo, Kang Liu, Jilai Xue

"Coal fly-ash(CFA) from thermal power plants is rich in Al2O3, which has great potential as an alternative resource for alumina production. In this work, Alz03 contained in the coal fly-ash was extracted using an acid sintering-leaching process. This process was enhanced by aid of power ultrasound during the leaching. The recovery rate of Al2O3 was increased with ultrasound, compared with the similar process without ultrasound under the identical operation conditions. Leaching temperature can be lowered by about 10-l5°C and the processing time reduced by about 50%. The process kinetics were investigated in details for a better understanding of the fundamentals on the effects of power ultrasound. The obtained results demonstrate the potential application in reducing processing energy and increasing production rate.Introduction Coal fly ash is a typical solid waste generated from coal combustion in thermal power station. Vast amount of CF A accumulation lead to serious environmental problems such as air and water pollution, cropland occupation, radioactive contamination, etc. However, CFA is rich in Al2O3 and SiO2 content, so that it has a potential use as recourses for alumina and silica production [1]. Aluminum industry, especially in China, has made a rapid expansion in recent years accompanying with a large amount of bauxite consumption, resulting a urgent demand to develop secondary alumina resources like CF A to maintain a sustainable development of aluminum industry that faces grim challenge [2].Acid leaching is an efficient technology to use in alumina extraction from CF A. Since the particle of CF A is not naturally existed mineral but was formed in molten state at high temperature, the internal Al-O-Si bonds are so strong to separate alumina from the ash particle. Because of this reason, the direct acid leaching [3-6] operated at ambient temperature has low extraction efficiency, approximate 30% to 40%, which is attributed to self inhibition effect from CaS04 generated by reaction between CaO and H2S04 [7-8]. High pressure leaching can efficiently decompose mullite to release A12O 3 content in the fly ash particles, but this requires autoclave material having strong acid corrosion resistance, high temperature (100°C-300°C) and pressure (1.0MPa-2.SMPa) resistance while its operating security is low and its acid consumption is large [9]. Concentrated acid boil process is conducted at near acid boiling point (200 °C - 300 °C) in 4 mouth flask wrapped by electric heating jacket with high mass ratio of acid and ash to achieve high Al203 recovery rate from CFA. Its disadvantages are similar to the high pressure leaching technology except no-pressure, and also the operating solution at nearly boiling point acid may easily spill and splash with additional acid loss and potential safety hazard [10]."

Jan 1, 2014

By W. G. Davenport

The flash furnace is used for smelting concentrate to (i) high-Cu matte and (ii) molten metallic copper. It is also used for converting solidified/crushed matte to molten metallic copper. This is flash converting. It consists (Table 20.1, Fig. 20.1) of: (a)tapping molten 65 to 72% Cu matte from a flash smelting furnace (b) granulating the molten matte to ?1/2 mm particles in a 103 m3/hour water torrent (c) crushing the granulated matte to 50 µm in a vertical roller mill (d)drying the crushed matte (e) feeding the dry particulate matte to a second flash furnace for oxidation converting to molten copper. In 2000, flash converting is being used by Kennecott Utah Copper (George, et al; 1995; Newman et al, 1998, 1999a,b). A second installation is being designed for the Chuquicamata smelter (www.outokumpu.com [October 12, 2000]), The potential uses of flash converting are: (a) as the second half of a flash smelting/flash converting coppermaking sequence (b) as a continuous converting alternative to batch submerged tuyere converting. This chapter uses our flash furnace matrix to determine the %O2-in-blast, industrial oxygen and oil requirements for converting solidified 65% and 72% Cu matte to molten copper. It then discusses choice of feed matte grade and other aspects of the process.

Jan 1, 2001

A modified Cuprex Metal Extraction Process (CMEP) leach process was used to extract Cu. Ni and Co from a complex sulphide concentrate. The standard leach was modified to a two-stage countercurrent leach which provided emf control of the copper SX feed and minimized iron dissolution. A flowsheet was developed to recover the base metals and silver from the leach solution and gold and platinum group metals from the leach residue which was predominantly elemental sulphur. Techniques required to maintain an iron balance in the system including pressure oxidation and solvent extraction are described.

Jan 1, 1996

By Wenya Du, Qingbo Yu, Peng Li, Qin Qin

"A new heat recovery system is proposed. This system uses the endothermic heat of gasification reaction instead of sensible heat to recover the energy of molten blast furnace slag. The gasification technological parameter in molten blast furnace was calculated and the exergy of the system was analyzed. The gasification reactions were studied kinetically by the isothermal thermogravimetry using STA409PC thermal analyzer. The results showed that, according to different gasification agent, this system can produce syngas with different C-H ratio. The exergy efficiency of this system is high and its internal exergy loss rate is about 11%. This method can bring huge economic and environmental benefits which are important to the survival and sustainable development of iron-steel enterprises. The molten BF slag acts as not only thermal media but also good catalyst. The kinetic parameters on gasification reaction with different types of coal used differ from each other.IntroductionEnergy consumption in the iron-making process is about 50%~60% of the total energy input. The blast furnace is very important in the iron & steel process. So energy conservation and emission reduction about blast furnace is very important. In recent years, in order to recovery energy, many new technologies such as TRT (Top gas pressure Recovery Turbine) and CCPP (Combined Cycle Power Plant) were used in iron-making. But the energy of molten blast furnace (BF) slag has only been used limitedly so far.Molten BF (Blast Furnace) slag is the byproduct of iron-making at the high temperatures range from 1723 to 1923K, and has a large amount of sensible heat remaining. The yield of molten BF slag is about 300 kg per ton of pig iron. In conventional processes, molten BF slag is quenched rapidly using a large amount of water to produce a glassy-granulated slag. The quenching slag must be dried before it can be used in cement manufacture. During the process, a large amount of water was consumed and the energy of molten slag can not be recovered. At the same time, it causes environmental pollution problems. So the critical problems of the process are not only energy recovery of molten slag and reducing emission of H2S and SO2, but also guaranteeing the subsequent use value of slag. For this propose, many new technologies were investigated to recover the thermal energy of molten slag. The promising methods are dry granulation [1-4] and reforming of methane [5-9]. The method, utilization of reaction heat instead of latent heat and sensible heat, is quite attractive from viewpoints of energy storage without heat loss, and makes a connection to other industry. But both of them are in laboratory. In this paper, coal gasification in molten BF slag was used to recover the energy of molten BF slag. The gasification technological parameter in molten BF was calculated and the exergy of the system was analyzed. The gasification reactions were studied kinetically by the isothermal thermogravimetry using STA409PC thermal analyzer."

Jan 1, 2011

By M. El Ganaoui, P. Bontoux

"A computational model to investigate solid/liquid phase change transitions for binary alloy under directional solidification is presented. Conservation equations are developed by using an homogeneous formulation. A second order accuracy method of time and space based on finite volume approximation has been evaluated by comparing results to spectral solution for time-dependent solutal convection developping in a melted alloy. For extended model to solid/liquid interface effects time amplification of solutal perturbation injected near the interface is described before considering solutal convection is melt.IntroductionThe enthalpy method gives a front fixing approach for energy equation without introducing coordinate transformation. The interfare position is recovered a posteriori [1]. A number of authors have extended this approach so as to include the convection phenomena within the two phase 'mushy region' [2, 3, 4, 5, 6].We have developed a time-dependent enthalpy-porosity formulation for directional solidification [4, 6, 8]. The interaction between solid and liquid phases is modelised by a Darcien type force in the phase change area. The behaviour of the melt is similar with the flow of an incompressible fluid in a porous medium. This force is proportional to the relative phase velocity. It corresponds to a damping force depending on the anisotropic permeability of the 'mushy zone'. The permeability depends on the liquid fraction and on the size of·solidification microstructures. An informative discussion of a new slant on the general approach of continuum mechanics needed to analyze the formation of mushy zone is given in [12]. The method is extended to the presence of species diffusion: the solutal Stefan condition which expresses the solute incorporation or rejection across the interface is accounted implicitly in a species equation valid in all the domain [14, 15]."

Jan 1, 2001

By Kazuteru Tozawa

Surface tension, density and viscosity coefficient of acidic copper sulfate solutions simulating electrolyte solution for electrolytic production of copper have been measured and are summarized as a function of the solution composition and temperature. Nickel sulfatc is taken to be a representative coexisting sulfate that affects the physical properties of the copper sulfate electrolyte solution. The sulfates in the solutions, including sulfuric acid, increase the physical properties under consideration. Gelatin, representing organic additives for electrolyte solution, was found to sensitively affect the surface tension of the solution at low concentration of up to 200mgIL. The surface tension was markedly lowered by the addition of gelatin and the increasing concentration of gelatin led to a more pronounced decrease in the observed values. The surface tension gradually increases with time after addition of gelatin and the increase is enhanced by higher acid concentration and higher temperature. The observed change in the surface tension is considered to reflect the preferential adsorption of gelatin to the bubble-solution interface and the decomposition of gelatin due to hydrolysis to form various molecules having smaller molecular weights.

Jan 1, 2003

By Ari I. Kogut

Impurity minerals in fluorspar ores and concentrates from a deposit in Southern Africa have been studied by reflected light, transmitted light, and cathodoluminescence microscopy. The principal impurities are quartz, calcite, aegirine, apatite, ankerite, magnetite, goethite, and synchysite [Ca(La,Ce,Nd)(C03l2Fj. Cathodoluminescence microscopy was found to be very useful in studying the character of the fluorite and especially for recognizing the presence of apatite and calcite impurities. Fluorite exhibits blue, calcite shows yellow, and apatite has white, light purple, and pink cathodoluminescence. The cathodoluminescent character of apatite varies with its geological environment and position in the orebody. The results of this microscopic study show that phosphorus present in flUorite concentrates occurs principally in binary locked apatite-fluorite particles. Successive fluorite cleaner concentrates contain progressively smaller amounts of locked apatite-fluorite particles. Free apatite has been effectively partitioned to the final tailings.

Jan 1, 1995

By Ko-ichiro Ohno

It is recently recognized that the iron reduction and melting as well as the slag separation of a composite of granular iron ore and coal are completed in a very short period of about 10 minutes when the composite is rapidly heated up to approximately 1673K. These phenomena are expected to be applied to a new iron-making process. The mechanism of iron ore reduction and iron-slag separation during rapid heating has not yet been revealed and the fundamental research has just started. Carburization of the reduced iron is regarded as one of the most important steps in this process. In the present work, the composite was prepared from four kinds of coal or graphite as a carbon source and electrolytic iron powder as a completely reduced iron ore. The temperature at which the liquid formation and iron carburization occurred was monitored. Direct observation of smelting reduction behavior was made by a confocal laser-scanning microscope combined with the infrared image-heating furnace to clarify the effect of molten ash on iron carburization. It was found that the meltdown temperature of composite became lower as the melting temperature of coal ash decreased. From the observed result, it was presumed that the liquid slag would act as an important media for the carbon transfer from coal to iron. The carburization mechanism during the smelting reduction was estimated as follows. When slag containing iron oxide melted down and contacted carbon, iron oxide in the slag was reduced and the formation of the metallic iron particle as well as the its carburization occurred simultaneously at the slag-carbon interface. Carburized iron particle was carried from slag-carbon to slag-iron interfaces due to the slag convection flow caused by the difference of the interfacial tension between the carbon-slag and iron-slag interfaces. Carburization of reduced iron could proceed with a repeat of the above-mentioned process.

Jan 1, 2003

By Ljiljana Solujic

The need for the removal of mercury from the precious metals extraction circuits may be influenced by process, environmental, as well as by occupational hazard reasons. In these circuits mercury is mainly present as cyanide complexes. The effectiveness of any stabilization method will be influenced by the high thermodynamic stability mercury-cyano species exhibit in an aqueous solution. In this study, we have investigated the utility of the trisodium salt of trimmercapto-s-triazine (TMT) for precipitation of mercury from the corresponding cyano-complexes. The influence of pH molar ratio of TMT to Hg, coagulant and flocculant additions, excess of free cyanide, as well as the presence of other metal-cyano species on the effectiveness of mercury precipitation were investigated in detail. Also, a "teal world" precious metals mill effluent initially containing ~7 ug/mL (ppm) of Hg was treated and A was found that greater than 99.8% of the mercury was removed from the solution as am insoluble Hg/TMT complex.

Jan 1, 1996

By Sylwia Zymankowska-Kumon, Rafal Danko, Józef Danko, Mariusz Holtzer

"Burning of ceramic materials is carried out at temperatures 900+ 1300°C, in dependence of the required functional properties. The Faculty of Foundry Engineering together with the Faculty of Material Engineering and Ceramics developed the technology of production of burned ceramic materials with using spent moulding and core sands. The mentioned above waste materials of the foundry industry fulfilled -in plastic masses intended for obtaining ceramic materials -the role of the addition weakening clay raw materials. The laboratory investigations were fully verified by the results of industrial tests. It should be pointed out that none negative effects were observed at the stage of mixing raw materials and preparation of plastic masses. The measurements of exhaust gases emissions performed during burning the products containing spent moulding sands as well as during the normal production did not exhibit any significant differences, which could have indicated the harmful impact on the natural environment.IntroductionSands are used by the foundry industry to make metal casting molds and are a mixture of silica sand, bentonite clay and carbonaceous additives or resins. During the casting process, the molten metal cause thermal decomposition of carbonaceous additives or resins, which results in the formation of potentially hazardous organics, that are emitted to the atmosphere and condense in the molding sand. Each year the U.S. foundry industry landfills about 10 million tones of sand because it is no longer suitable to make metal casting molds. A large high-silica sand content in spent foundry sands (SFSs) generates rational premises for their reuse in other than foundry practice fields. Efforts to divert the SFSs from landfills and encourage their beneficial use in manufactured soils, geotechnical applications, the construction industry (road construction, highway construction), the building materials industry (cement, bricks, limestone manufacture), in the filling of mining cavities or in landfill construction (roads on landfills, permanent covers) are make [1-7]."

Jan 1, 2013

By Y. Pokhvisnev, S. Vandariev, A. Yatshenko-Juk, V. Valavin, V. Romenets

The technology of the liquid-phase reduction process known as Romelt was developed in the Moscow Institute of Steel and Alloys in 1979. The pilot plant was constructed at the Novolipetsky Steel Works (Russia) in 1984. Investigations into processing zinc-containing blast oxygen furnace dust and slag from the Lead and Zinc Works at the pilot Romelt plant proved the perspective of using this technology for processing zinc and lead-containing materials. In this article, the description of Romelt technology, basic technological information of trials at the Romelt plant using zinc-containing materials, compositions of charging materials, metal, slag, gas and dust are presented. The influence of flue gas composition on the composition of zinccontaining dust is shown.

Jan 1, 2000