By R. Hurman Eric

Within the Ag-Pb-S ternary system, the boundaries of the immiscibility region together with the tie-line distributions were re-established at 925°C by the equilibrium-quenching technique where samples were kept in evacuated and sealed silica capsules. Activities of Pb were measured by the dew-point method along the Ag-Pb binary at 925°C, 1100° and l200°C, positive deviations were observed and the results were modeled by the Krupkowski formalism. Activities of Ag, Pb, and S, along the ternary miscibility gap were calculated at 925°C by utilizing the boundaries binary thermodynamics, phase equilibria and tie-lines. Activities of PbS within the pseudobinary Ag2S-PbS mattes were also measured by the dew-point technique and the results were again modeled by the Krupkowski formation where negative deviations were observed.

Jan 1, 2003

By Frederick T. Wallenberger

"Laser assisted chemical vapor deposition (LCVD) is a new containerless fiber process whereby growth of small diameter fibers or microstructures (microsprings, microsolenoids) occurs directly from the vapor phase. The laser beam has a focal point adjusted to coincide with the tip of the growing fiber inside the reaction chamber. Since the growing fiber is not in contact with reactor walls or foreign materials, it is chemically pure, and suitable for optical uses and uses requiring high structural uniformity. Continuous fibers and multifilament yams are possible. The use -of high reaction chamber pressures (1-10 bar) and a small wavelength Nd-YAG laser made it possible to fabricate small diameter fibers at growth rates >1 mm/s. This paper describes the synthesis of single crystal, polycrystalline and amorphous fibers by LCVD, and provides a comprehensive analysis of phase transformations occurring during their fabrication.IntroductionLaser assisted chemical vapor deposition (LCVD) is a new containerless fiber process [1-10] whereby growth of small diameter fibers or microstructures occurs directly from the vapor phase. The laser beam has a focal point adjusted to coincide with the tip of the growing fiber in the reaction chamber (Figure 1). The diameter of the growing fiber corresponds to that of the laser focus. Depending primarily on the laser energy (Le., the temperature at the growing fiber tip), it is possible to obtain single crystal, poly crystalline or amorphous fibers by this method.Since the growing fiber is not in contact with reactor walls or foreign materials, it is chemically pure, and suitable for optical uses and uses requiring high structural uniformity. Laser assisted CVD is a potentially continuous process; continuous fibers and multifilament yams are possible."

Jan 1, 1994

By Fiseha Tesfaye, Pekka Taskinen

"Thermodynamics of the equilibrium phase assemblage Ago_9Cul.lS-Cu2-xS-CuS have been studied by an EMF -method. The ternary phase was synthesized from the pure Cu2S and Ag2S in vacuum furnace at high-temperature and mixed with appropriate compositions of Cu2S and CuS to form the cathode electrode. The EMF-measurements were made on the solid-state galvanic cell Pt(-) I Ag I RbAg,ils I Ago9Cu1.1S-Cu2-xS-CuS I Pt(+), in a temperature range from 316 K to 498K.Based on the measured EMF vs. T relations, thermodynamic functions (?fG° , ?fS and ?fH°) of stromeyerite (Ag0.9Cu1.1S) in equilibrium with Cu2-xS and CuS have been determined. The obtained experimental values have been compared with the available literature values. New experimentally determined thermodynamic properties of the solid solution (Ag,Cu)2Sss were determined.IntroductionDue to intense mining of high grade sulfide ore minerals in the past, recently, the available sulfide ores are poor in metals and becoming increasingly complex; such that, the production of high grade metals by the conventional pyrometallurgical processes is compromised. Consequently, smelters are in need to modify their operating flow sheets and strategies for processing more complex feed materials economically, while meeting the strict environmental regulations. To make the appropriate modifications, accurate thermochemical data of phases and phase assemblages which exist in these complex ore minerals are essential.Silver-bearing sulfosalts are encountered in ore minerals for the production of base metals and are common sources of silver. Among the silver-based sulfosalts, stromeyerite (Ag0_9Cu1.1S) is relatively common ore mineral in most hydrothermal vein and replacement deposits [1]. Recently, the ternary chalcogenide compound Ago0.93Cu1,07S has been studied, intensively, due to its high ionic conductivity and gradual disorder in the sequential phase transitions [2]. Therefore, accurate knowledge of the thermodynamic properties of stromeyerite has considerable fundamental and practical interest in many aspects of extractive, chemical and physical metallurgy."

Jan 1, 2014

By Edwin de Jesús Deveaux

After 32 years of operations beneficiating lateritic nickel ore in a fully integrated pyrometallurgical complex, Falconbridge Dominicana (FALCONDO), situated at Bonao and La Vega Provinces, Dominican Republic, has become profitable with one of the lowest nickel grade content processing plants in the world, and literally without any by-product (granulated slag, will be utilized in the future as a post-processing subproduct). To December 2002, mineral reserves were 64.1 million tonnes containing laterite grading as low as 1.15 % Ni when full dilution is applied. At a cut-off grade of 1.20% Ni, the reserves will provide 15-20 years of production. The mineralized thickness over the seven active deposits averages 6 m. Development of very selective and unique mining practices, together with improvements in the process plant, are key to achieving the production goal (30 kt Ni/yr) and to meet the quality standards for the ferronickel produced. Keywords: Laterites, grade control, mining methods, environment

Jan 1, 2004

By D. J. Chaiko

Aqueous biphasic extraction (ABE) processes offer the potential for low-cost, highly selective separations. This countercurrent extraction technique involves selective partitioning of either dissolved solutes or ultrafine particulates between two immiscible aqueous phases. The extraction systems that we have studied are generated by combining an aqueous salt solution with an aqueous polymer solution. We have examined a wide range of applications for ABE, including the treatment of solid and liquid nuclear wastes, decontamination of soils, and processing of mineral ores. We have also conducted fundamental studies of solution microstructure using small angle neutron scattering (SANS): In this chapter we review the physicochemical fundamentals of aqueous biphase formation and discuss the development and scaleup of ABE processes for environmental remediation.

Jan 1, 1996

By André L. B. Bittencourt

The copper content in the waste slag represents the greatest loss in the process of Caraíba Metais' Smelter. By identifying the variables responsible for copper stabilization in the slag, a minimization on these losses is expected, producing a granulated waste slag with a copper content lower than 0.7%. Statistics resourses such as control charts, Pareto's diagram and correlations curves were applied for the data obtained in the first semester of 1992. The magnetite and the calcium oxide contents in the slag of the Flash Smelter Furnace were most prominent variables. Some operational changes introduced during and after this investigation have shown good results.

Jan 1, 1994

By Marcelo B. Mourao

Interactions of carbonaceous materials with liquid Fe-C melts have been investigated experimentally by determining the volatile yield due to rapid devolatilization (Flash Pyrolysis) and rates of dissolution at temperatures ranging from 1623 to 1873 K. The volatile yield increased with increasing the temperature. The comparison of results of different types of carbonaceous materials was possible by expressing the volatile yield in terms of Enhancement Factor, fE. The rates of dissolution of spectroscopic graphite and an industrial coke seemed to obey the correlation for natural convection under turbulent conditions. The experimental data for the graphite suggested that the rate of dissolution was controlled by the mass-transfer in the liquid boundary layer adjacent to the solid sample. The value for the empirical parameter correlating the dissolution coefficient and the operating variables was found to be 0.19 which was close to that reported in the literature. The comparison of the results obtained for the coke samples with those for the graphite revealed that the impurities and the porosity of the samples can effect the dissolution rates.

Jan 1, 1992

By George S. Dulikravich

An advanced semi-stochastic algorithm for constrained multi-objective optimization has been adapted and combined with experimental testing and verification to determine optimum concentrations of aJ10ying elements in heat-resistant and corrosion-resistant H-Series austenitic stainless steel alloys. The objective was to simultaneously maximize a number of alloy's mechanical properties. This research will result in a rigorous tool for the design of high-strength H-Series steels and other types of alloys unattainable by any means existing at the present time. Such a material-by-design tool will also be able to reduce or minimize the need for the addition of expensive elements such as Cr, Ni, Co, Nb, Ti, V, etc. and still obtain the optimum properties of an aJ1oy.

Jan 1, 2003

By S. Stoyanov, M. Cross

"Silicon components containing transistor circuitry are at the heart of electronic products such as computers, mobile phones, etc. These components are connected to printed circuit boards (PCB's) using solder material that acts as the conductor for both electricity and heat. During the lifetime of a product it will undergo many thermal cycles where the chip becomes hot during product operation and then cools when the product is switched off. At the product design stage engineers undertake thermo-mechanical simulations to predict the thermal stress in the solder joints due to this thermal cycle and to ensure that the stress magnitude will not result in early fatigue-type failure. The design engineer's aim is to identify component parameters which ensure that the solder will survive beyond a certain number of thermal cycles.The aim of integrating computational mechanics and optimization tools together is to speed up dramatically the design process. From viewpoint of a design engineer in the electronics manufacturing sector, these tools can be used to quickly estimate key design parameters (i.e. material properties, product dimensions, etc) that will guarantee the required product performance. In this paper a modeling approach coupling computational mechanics techniques with numerical optimization is presented and demonstrated. The integrated modeling framework is obtained by coupling the multi-physics framework - PHYSICA - with the design optimisation tool- VisuaLDOC. Thermo-mechanical simulations are presented that predict the creep strains in solder material. Different numerical optimization procedures: Direct and Response Surface based optimization plus Design of Experiments, are tested as a part of this modeling framework."

Jan 1, 2001

By M. Pakala, Z. Fan, Ray Y. Lin

Deposition of hard chromium coatings using electrodeposition is accompanied by emission of hexavalent chromium mists which is a carcinogenic. Hence alternative chromium deposition technologies are being investigated. Sputter deposition is a strong candidate to economically deposit hard chromium coatings in an environmentally friendly way. Chromium coatings of 2-3 µ m thickness were deposited on plain carbon steel coupons using RF magnetron sputter deposition. Depositions were carried out with 0 to 22 vol% nitrogen in the plasma. Structure of the coatings was studied using x-ray diffraction analysis With increasing nitrogen contents, formation of the two nitride phases was observed. The pure chromium phase was detected in coatings with up to 7% nitrogen in the sputtering gas. The solid solution of nitrogen in the pure Cr phase coating was identified by shifts of Cr x-ray diffraction peaks to higher d-spacing. The microhardness of the coatings deposited at a substrate temperature of 200°C showed an increase in hardness with increasing nitrogen content from 600 kgf/mm2 (5.9 GPa) at 0% nitrogen to I250 kgf/mm2 (I2.25 GPa) at 9.5 % nitrogen and a subsequent decrease in hardness to I 100 kgf/mm2 (11 GPa) beyond 9.5 % nitrogen in the sputtering gas. This corresponds to the formation of the hard Cr2N phase, at 9.5 % nitrogen, and CrN phase, at I5.7 % nitrogen. The reported bulk hardness values of Cr2N and CrN are I600 kgf/mm2 (I5.7 GPa) and I 100 kgf/mm2 (11 GPa) respectively. For pure Cr phase coatings, there is a slight increase in hardness for coatings deposited at 7. I % nitrogen from that without nitrogen in the sputtering gas. This could possibly result from the solid solution strengthening of the Cr lattice by nitrogen. For films deposited at 200°C, phases of the deposited films seem to be the overwhelming factor in controlling the microhardness.

Jan 1, 1998

By Lenny Winkel

With the aim to develop a solar-driven process for the extraction of copper from sulfide concentrates research on the decomposition of copper sulfides under inert atmospheres has been initiated. Thermogravimetric measurements on chalcocite (CuzS) revealed that copper is formed already at 1823 K. Chalcopyrite (CuFeS2) also disintegrates at this temperature, although at a lower rate. Copper and iron have been identified in the solid residue. The results confirm the feasibility of copper extraction by direct decomposition of sulfides under atmospheric pressure. The decomposition under inert atmosphere prevents generation of SO2, it also alters the behavior of volatile impurities during decomposition of copper sulfide concentrates. Chemical eqUilibrium calculations for chalcopyrite contaminated with enargite (Cu3AsS4) have shown that the absence of an oxidic slag allows for a complete evaporation of arsenic and subsequent separation from intermediate sulfides. The need to better assess the potential of direct sulfide decomposition has prompted the development of an experimental setup for studying the decomposition reactions. The experiment has been devised such that data on the decomposition kinetics and on impurity removal can be obtained at temperatures up to 2500 K.

Jan 1, 2003

By Florian Kongoli

New operating conditions and process parameters are often necessary in today's industrial practice of non-ferrous smelting and converting in order to accommodate various new chemical compositions of mineral charges and environmental requirements or to conceive new and more efficient industrial technologies. An important parameter in non-ferrous smelting and converting is the liquidus surface of multicomponent slags. This surface is affected by multiple factors such as temperature, gaseous potentials, the content of each component in the slag, etc., and cannot be quantified by the existing ternary liquidus diagrams. In this work a new type of representation of the liquidus surface of multi component systems has been presented by means of a thermodynamic model. This representation waives the need of the multidimensional representation of multi component systems and yields practical two-dimensional diagrams, which can be easily used in the industrial practice.

Jan 1, 2000

By Jewel A. Gomes

Keywords: Electrocoagulation, arsenic removal, fuel cell, windmill, energy simulation, combined Fe-Al electrode assembly Arsenic contamination of well-water in different countries has caused signs and symptoms of arsenic poisoning. Although several physicochemical treatments are presently used for the removal of arsenic compounds from drinking water, an electrochemical treatment, electrocoagulation, is a promising processing technology and currently is the most efficient (above 99% removal) and environmentally friendly technique, particularly if combined with alternative energy sources. Wind and fuel cell technologies can be considered the most promising developmental clean power sources. We will discuss new insights into the materials processing mechanisms and show the coupling of electrocoagulation with fuel cells and simulated wind energy sources. Different electrocoagulation plate materials were considered, along varied currents from the fuel cell to produce maximum arsenic removal. Coupling these technologies will remove carcinogenic arsenic from water sources, and will exhibit efficient usage of these energy sources by producing pure water for human and agricultural consumption.

Jan 1, 2005

By Ray D. Peterson

The hydrothermal enrichment of chalcopyrite by CuSO, occurs in the absence of oxidizing or reducing reagants. Kinetics of the enrichment process were determined under autoclave conditions in the temperature range of 398°K (125°C) to 473°K (200°C). Covellite (CuS) formed first, followed by digenite (Cu,,,S), with rejection of iron to the solution. The kinetics have been explained by a model which includes diffusion during the first stage formation of covellite followed by surface reaction rate control when digenite be. The effects of particle size, temperature, pH, and cupric and ferrous ion concentrations on the leaching kinetics were examined. Additions of ferrous ion to solution markedly increased the rate of reaction.

Jan 1, 1994

By Emmanuel N. Zevgolis

After the Krupp-Renn process was shown to be unsuitable for treatment of the Greek nickeliferous laterites, the LM process was developed. It involved roasting reduction up to metallic iron in a Rotary Kiln (R/K) and smelting in an Electric Furnace (E/F). Ferronickel (with 15% Ni) produced in the E/F, was upgraded to 90-95% Ni in an 02 converter. Raw Ni was then electrolyzed to pure Ni. The LM process was not applied for very long however, due to various problems. So, the Larco process was developed, i.e., pre-reduction in R/Ks, smelting of the calcine in E/Fs for ferronickel production (15% Ni) and enrichment to 20% Ni, in an O2 converter. Until now, many technological improvements have been invented and applied or adjusted to the process, which have made it a fully reliable and competitive one. sohe of the improvements were the invention and application of a new granulation process for liquid ferronickel, the modification of the existing R/Ks, E/Fs and converters and the design of new ones, and others that are described in the paper. Keywords: Ferronickel, metallurgy, laterites, LM process, Larco process

Jan 1, 2004

By Yasushi Sawada

An experimental investigation was carried out to study the rates of reduction of iron oxides dissolved in liquid Ca0-SO2-A203 slags by Fe-C droplets at temperatures ranging from 1325 OC to 1550 OC. The %FeO in the slag was varied from 5.5 to 18. Flash X-ray images were employed to observe the behavior of Fe-C droplets in the slags during the reactions and for determining the slag-gas-metal interfacial area. Effect of P205 in the slag and sulfur in the droplet was also investigated. The reduction rates were determined by measuring the volume of CO evolved as a function of time and the estimated slag-gas- metal interfacial area. The reduction rates have increased with increasing %FeO in the slag and the slag temperature. The experimentally established relationship between the reduction rates and FeO (wt%) in slag is given by

Jan 1, 1992

By Teixeira

An experimental investigation on the kinetics of oxidation of As(III) with H202 in synthetic effluent solutions followed by precipitation of Fe/As (V) compounds was carried out. The variables investigated were: As concentration (200 -3000 mg/l) , oxidation pH (2.0 -11.0), oxidation temperature (25 -800C) , H202 stoichiometric excess (50% -100%), precipitation pH (5.0 -7.0), precipitation agent (Fe2+ -Fe3+). Fixed conditions were, Fe/As molar ratio (6:1) and stirring speed (560 rpm). The results were empirically modelled. The precipitates obtained were amorphous. The precipitates were checked upon their environmental stability according to the United States Environmental Protection Agency (U.S.E.P.A.) Toxicity Test, and were considered to be adequate for deposition in impermeable waste dumps. The combined Fe/H202 detoxification process, in selected conditions, was able to reduce the As contents of effluents containing 1600 mg/l As to 0.1 mg/l, in about 2 1/2 hours of total processing time.

Jan 1, 1990

By Charles H. Rawlins

Reported is work done on processing of steel mill effluents in the areas of dewatering and separation. Much of the waste from these operations is in the form of sludges from scrubbers, in which the primary constituent is iron oxide. Recycling of the sludge&apos;s magnetic fraction has become economically attractive in order to reduce the overall volume placed in landfills. The objective of this research is to determine the effectiveness of combining magnetic and cyclonic forces, to recover iron oxide particles from waste water stream, while decreasing the volume to be disposed. Three different size hydrocyclones, operating within the field of a quadripole magnet, were tested using varying feed pulp densities of magnetite, magnetite/dolomite, blast furnace (BF), and basic oxygen furnace (BOF) slurries. In the first three cases, the percentage of magnetics recovered increased to greater than 95%. The limiting operational factors are; high pulp density for small cyclones, which can cause flow blockage within the magnet field, and extremely fine particle sizes (<2 microns), which cannot be recovered. The results indicate this technique can remove virtually all the magnetic particles from some steel effluents to a 40-50% weight percent solids pulp, on an in line continuous basis.

Jan 1, 1994

By George S. Dulikravich

An advanced semi-stochastic algorithm for constrained multi-objective optimization has been adapted and combined with experimental testing and verification to determine optimum concentrations of alloying elements in heat-resistant and corrosion-resistant H-Series austenitic stainless steel alloys. The objective was to simultaneously maximize a number of alloy&apos;s mechanical properties. This research will result in a rigorous tool for the design of high-strength H-Series steels and other types of alloys unattainable by any means existing at the present time. Such a material-by-design tool will also be able to reduce or minimize the need for the addition of expensive elements such as Cr, Ni, Co, Nb, Ti, V, etc. and still obtain the optimum properties of an alloy.

Jan 1, 2003

By Ho-Sang Sohn

The kinetic study on desulfurization of copper matte by gas bubbling was designed under the presumptions of lower FeO activity and of no slag formation, Copper matte with 59% Cu and 22.6% S in weight was oxidized at 1523K by bubbling of Ar + O2 gas through a submerged nozzle. The effects of oxygen partial pressure and flow rate of gas on the oxidation rate of matte were discussed. The desulfurization rate and the evolution rate of SO2 gas of copper matte were significantly influenced by the oxygen partial pressure, but the dependence on gas flow rate was rather complicated. The desulfurization rate and evolution rate of SO2 gas of copper matte were described by the mass transfer rate through the gas film around the rising gas bubbles. Thermodynamic correlation equations between the partial pressure of gaseous species and matte composition were incorporated to the kinetic calculation, The present model shows that the reaction path starts to transiently cross over an isobar line of PSO2 to asymptotically approach to the particular isobar line drawn in a matte composition plane of %S and %O.

Jan 1, 2003