By Wenbo Luo, Kang Liu, Jilai Xue

"Coal fly-ash(CFA) from thermal power plants is rich in Al2O3, which has great potential as an alternative resource for alumina production. In this work, Alz03 contained in the coal fly-ash was extracted using an acid sintering-leaching process. This process was enhanced by aid of power ultrasound during the leaching. The recovery rate of Al2O3 was increased with ultrasound, compared with the similar process without ultrasound under the identical operation conditions. Leaching temperature can be lowered by about 10-l5°C and the processing time reduced by about 50%. The process kinetics were investigated in details for a better understanding of the fundamentals on the effects of power ultrasound. The obtained results demonstrate the potential application in reducing processing energy and increasing production rate.Introduction Coal fly ash is a typical solid waste generated from coal combustion in thermal power station. Vast amount of CF A accumulation lead to serious environmental problems such as air and water pollution, cropland occupation, radioactive contamination, etc. However, CFA is rich in Al2O3 and SiO2 content, so that it has a potential use as recourses for alumina and silica production [1]. Aluminum industry, especially in China, has made a rapid expansion in recent years accompanying with a large amount of bauxite consumption, resulting a urgent demand to develop secondary alumina resources like CF A to maintain a sustainable development of aluminum industry that faces grim challenge [2].Acid leaching is an efficient technology to use in alumina extraction from CF A. Since the particle of CF A is not naturally existed mineral but was formed in molten state at high temperature, the internal Al-O-Si bonds are so strong to separate alumina from the ash particle. Because of this reason, the direct acid leaching [3-6] operated at ambient temperature has low extraction efficiency, approximate 30% to 40%, which is attributed to self inhibition effect from CaS04 generated by reaction between CaO and H2S04 [7-8]. High pressure leaching can efficiently decompose mullite to release A12O 3 content in the fly ash particles, but this requires autoclave material having strong acid corrosion resistance, high temperature (100°C-300°C) and pressure (1.0MPa-2.SMPa) resistance while its operating security is low and its acid consumption is large [9]. Concentrated acid boil process is conducted at near acid boiling point (200 °C - 300 °C) in 4 mouth flask wrapped by electric heating jacket with high mass ratio of acid and ash to achieve high Al203 recovery rate from CFA. Its disadvantages are similar to the high pressure leaching technology except no-pressure, and also the operating solution at nearly boiling point acid may easily spill and splash with additional acid loss and potential safety hazard [10]."

Jan 1, 2014

By B. C. Qi

"In water treatment, flocculation or coagulation with aluminium or ferric salts has been widely used for many years to remove natural organic matter (NOM), including humic acids. However, the adsorption of NOM to aluminium hydroxide flocs during conventional coagulation/flocculation processes is very complex, with the flocculation of aluminium hydroxide particles and the adsorption of NOM molecules on flocs occurring simultaneously. Any effect on the surface characteristics and micro-structures of the humic acids and aluminium hydroxides could affect the adsorption efficiency.It has been widely observed that if a reaction system (liquid-liquid or liquid-solid) is exposed to an ultrasound field, under appropriate conditions, a variety of physical (emulsification, aggregation/flocculation) or chemical (the production of radical and exited species; single electrotransfer) actions may be activated. Though the ultrasound effects have been used in biological and chemical decontamination in many conventional environmental protection practices, the idea to explore the ultrasound effects in the removal of humic acids by preformed aluminium hydroxide flocs is relatively new. In this paper, the effect of an in-situ ultrasonication on removal of the humic acids extracted from the acidification fermentation of lignocellulosic residues, by a preformed aluminium hydroxide, was evaluated; the effect of ultrasonication on the surface complexation of the humic acids with the preformed aluminium hydroxides was investigated."

Jan 1, 2003

By L. Yuan

In the U.S. coal mining industry, most spontaneous combustion fires occur in longwall or worked-out gob areas. In order to reduce the fire hazard caused by spontaneous combustion, it is important to understand how ventilation and gob characteristics affect the spontaneous heating process. Given the difficulty to conduct field tests in such an environment, a computational fluid dynamics (CFD) study was conducted to investigate the effects of ventilation and gob characteristics on the spontaneous heating process in longwall gob areas. Two longwall panels with a bleeder ventilation system were simulated. The spontaneous heating is modeled as the low-temperature oxidation of coal in the gob using the Arrhenius rate law and kinetic data obtained from previous laboratory-scale studies. The heat generated from the spontaneous heating is transported by convection and conduction, and oxygen and the oxidation products are transported by convection and diffusion. Unsteady state simulations were conducted with different ventilation conditions and gob permeability distributions. The ventilation parameters varied in the simulations are the pressure at the bottom of the bleeder shaft and regulator resistance in the second entry inby the longwall face.

Jan 1, 2009

By S. K. Kawatra, S. J. Ripke, T. C. Eisele

"An estimated 600,000 tons of bentonite clay are used annually in the U. S. as binder for production of iron ore concentrate pellets. Since this is a significant cost item for the plants, and the addition of bentonite to the pellets contributes undesirable silica into the finished pellets, there is considerable incentive for finding methods to reduce bentonite use. One way to reduce bentonite levels is to selectively use those bentonites that are most effective in this application, so that a lower dosage will still produce a sufficiently strong pellet. Unfortunately, there are no satisfactory methods available for accurately predicting which bentonites are actually most effective, short of using them to actually make pellets. One of the popular methods for attempting to evaluate bentonites is the “Plate Water Absorption” (PWA) test. While some plant operators accept the PWA results as indicating the relative quality of bentonites, others disagree and claim that, over a fairly broad range of values, PWA does not correlate with bentonite performance.Since both Ca+2 and Mg+2 ions are known to reduce the swelling and water absorption capacity of bentonite, it was believed that the presence of these ions in plant recycle water could be changing the bentonite performance. Since the standard PWA test uses only distilled water for its measurements, it could not detect these effects. Experiments were therefore carried out on a number of different bentonites using a modified PWA tests, with plant recycle water replacing the distilled water. These experiments showed little effect of the plant water on the PWA value, and chemical analysis of the water showed that the levels of dissolved salts were quite low.Water and accompanying salts were then extracted from a magnetite concentrate filter cake by rinsing with distilled water. Analysis of this water showed an extremely high level of dissolved salts, particularly salts of calcium and magnesium. When concentrations were compared with the recycle water from the plant filters, it was determined that levels of Ca+2 and Mg+2 retained in the filter cake were over 500 times higher than levels in the recycle water. This extreme elevation of soluble salts in the filter cake is believed to be due to adsorption of these ions into the electrical double layer of the magnetite particles."

Jan 1, 2003

By Ch. D. Taylor

Past studies with blowing face ventilation systems have shown that using a machine-mounted scrubber and water sprays can reduced methane levels at the face. The current research was conducted to determine how the sprays and scrubber interact to reduce methane levels, and what spray configurations provide the best face ventilation when used with a scrubber. Testing was conducted in a ventilation test gallery designed to simulate a full-scale mine entry. In the entry, a model mining machine, equipped with a simulated dust scrubber and water spray systems, was located at the face of a 6.1 m (20 ft) box cut. Face ventilation was provided by a blowing curtain located 12.2 m (40 ft) from the face. Methane released from a manifold at the face was measured at six locations near the face to compare the ventilation effectiveness of the spray systems while operating with and without the scrubber. Airflow movement across the face was affected by the spray configuration and scrubber operation. Average face concentrations were lowest when directed sprays were used with the scrubber. Varying the direction of the scrubber exhaust affected face methane levels.

This study was conducted to determine the effects of a machine-mounted scrubber and water sprays on face methane levels. Testing was conducted in the NIOSH ventilation test gallery which was designed to simulate a full-scale mine entry. In the test entry, a model mining machine, equipped with water sprays and a simulated dust scrubber, was located at the face of a 20-ft box cut. Blowing ventilation was provided using a curtain with a 40-ft setback distance. Methane released from a pipe manifold located inby the mining machine was monitored at six locations that were 1 ft outby the pipe manifold. Tests were first conducted to evaluate the effects of using sprays and scrubber separately on face methane levels. Additional tests were conducted to determine how a scrubber used with various water spray systems would affect face methane levels. The use of either sprays or scrubber reduced face methane levels significantly. The combined use of sprays with the scrubber further reduced face methane levels a small amount. Primarily the sprays affected methane levels by changing airflow distribution close to the face.

This study was conducted to determine the effects of a machine-mounted scrubber and water sprays on face methane levels. Testing was conducted in the NIOSH ventilation test gallery which was designed to simulate a full-scale mine entry. In the test entry, a model mining machine, equipped with water sprays and a simulated dust scrubber, was located at the face of a 20-ft box cut. Blowing ventilation was provided using a curtain with a 40-ft setback distance. Methane released from a pipe manifold located inby the mining machine was monitored at six locations that were 1 ft outby the pipe manifold. Tests were first conducted to evaluate the effects of using sprays and scrubber separately on face methane levels. Additional tests were conducted to determine how a scrubber used with various water spray systems would affect face methane levels. The use of either sprays or scrubber reduced face methane levels significantly. The combined use of sprays with the scrubber further reduced face methane levels a small amount. Primarily the sprays affected methane levels by changing airflow distribution close to the face.

Jan 1, 2001

By John L. Ellenberger, Gabriel S. Esterhuizen

Observations of pillar conditions in limestone mines showed that the presence of weak bands in the limestone can result in pillar damage at stresses that are lower than one would otherwise expect. The objective of this National Institute for Occupational Safety and Health study was to investigate the mechanism of failure caused by the presence of weak bands by using a series of numerical models based on realistic physical properties. The effect of the weak bands on pillar strength was also investigated by developing a series of pillar models with different width-to-height ratios and determining their strength by simulating a servo-controlled loading condition. The material properties of the bands and the limestone were varied and their effects on pillar strength were determined. Model results demonstrated failure development similar to the pillars observed in the field. The weak bands were seen to develop tensile stresses in the limestone as they extrude under increasing stress. The limestone fails in tension at a much lower stress than its expected uniaxial compressive strength. The results showed the load bearing capacity of the pillars can be reduced significantly by the presence of multiple thin weak bands. The degree of strength reduction is largely dependent on the compressive strength, the frictional resistance and the thickness of the weak bands. Single weak bands do not affect pillars as severely as multiple bands. However, the model results show that a single thick weak band, which comprises more than about 2 percent of the pillar height, can cause a significant reduction in pillar strength. The weakening effect of the bands become less severe as the pillar width-to-height ratio is increased. Field observation of spalling and failure associated with weak bands in limestone pillars show that the failure mechanism in the models resembles the observed failure. The model results provide insight into the important factors affecting pillar strength in the presence of weak banded materials.

By Gabriel Esterhuizen

Observations of pillar conditions in limestone mines showed that the presence of weak bands in the limestone can result in pillar damage at stresses that are lower than one would otherwise expect. The objective of this National Institute for Occupational Safety and Health study was to investigate the mechanism of failure caused by the presence of weak bands by using a series of numerical models based on realistic physical properties. The effect of the weak bands on pillar strength was also investigated by developing a series of pillar models with different width-to-height ratios and determining their strength by simulating a servo-controlled loading condition. The material properties of the bands and the limestone were varied and their effects on pillar strength were determined. Model results demonstrated failure development similar to the pillars observed in the field. The weak bands were seen to develop tensile stresses in the limestone as they extrude under increasing stress. The limestone fails in tension at a much lower stress than its expected uniaxial compressive strength. The results showed the load bearing capacity of the pillars can be reduced significantly by the presence of multiple thin weak bands. The degree of strength reduction is largely dependent on the compressive strength, the frictional resistance and the thickness of the weak bands. Single weak bands do not affect pillars as severely as multiple bands. However, the model results show that a single thick weak band, which comprises more than about 2 percent of the pillar height, can cause a significant reduction in pillar strength. The weakening effect of the bands become less severe as the pillar width-to-height ratio is increased. Field observation of spalling and failure associated with weak bands in limestone pillars show that the failure mechanism in the models resembles the observed failure. The model results provide insight into the important factors affecting pillar strength in the presence of weak banded materials.

Jan 1, 2007

By R. Harris

Blister copper melts of 800 g to 1000 g containing less than 1 wt % S and up to 3 wt % Ni were desulfurized at 1523 K in air or by a pure oxygen jet blown at 75,500 and 1000 cm3/min, from 1 cm above the melt. Rates of desulfurization and oxygen pickup were measured and visible surface phenomena were photographed and videotaped. It was observed that SO2 was evolved from Cu-S melts in a manner reminiscent of the effervescence seen in carbonated drinks. The effervescence lasted up to 20 minutes and resulted in the ejection of material up to a height 50 cm above the melt surface. Sporadic discharge of large bubbles was also observed in a Ni containing melt top-blown with oxygen at 1000 cm3/min. The Cu-S melts top-blown with oxygen experienced faster sulfur elimination as compared to stagnant melts exposed to air and experienced only a single period of turbulent SO2 evolution, which occurred almost immediately after oxygen injection commenced. The Cu-S melts exposed to air experienced multiple episodes of effervescence. The stagnant blister copper melt containing nickel did not exhibit effervescent behaviour and experienced a lower rate of sulfur elimination compared to Cu-S melts tested under similar conditions. The present article examines the role of surface phenomena in determining the observed behaviour.

Jan 1, 1999

By Sachihiko Tokunaga, Hirofumi Taguchi, Kenji Maruyama, Hidenori Takahashi, Yoshiyuki Morikawa

"Abstract The present study proposed a new liquefaction countermeasure to improve sandy ground and conducted a trial execution. The new method is a floating-type and lattice-shaped cement treatment method, where cement-treated soil is not fixed to a non-liquefiable stratum. A fixed structure such as treated soil should be formed at the side of the floating-type treated soil to reduce its lateral displacement. In the study, one-dimensional dynamic response analyses were first conducted to confirm the mechanism of the new method. Then, a series of centrifuge model tests were performed to demonstrate the effect under a stress condition at the prototype scale. The analyses and model tests confirmed the effect of the liquefaction countermeasure. Finally, trial executions were carried out to confirm high-quality vertical execution.INTRODUCTIONLiquefaction induced by an earthquake generates sand boiling and ground settlement. Other problems have also been reported, including a decrease in bearing capacity and an increase in the horizontal earth pressure against retaining walls. To prevent these problems caused by liquefaction of the ground, various countermeasures have been proposed, such as cement deep mixing and high-pressure jet mixing methods. These methods have the big advantage of being applicable to ground that contains soil with a fine-grain fraction. Furthermore, the unnecessary displacement caused by the construction can be reduced. In Japan, a lattice-shaped cement-treatment method has frequently been used at many construction sites to prevent liquefaction, where cement-treated piles are intersected to form a lattice, as shown in Fig. 1. The lattice-shaped walls can reduce the shear stress generated by an earthquake, restricting the liquefaction at that location. However, the construction cost of the cement treatment is relatively high compared to other methods such as the sand compaction pile (SCP) method, and needs to be reduced. In particular, the cost of the high-pressure jet mixing method, which can be applied to the liquefiable ground under existing structures, is significantly high. Therefore, decreasing the total volume of the cement treatment is necessary to reduce the construction cost."

Jan 1, 2014

Efficacy of Enhanced Gravity Separator in Processing Indian Iron Ore Slime The slime sample was subjected to concentration using Falcon concentrator for their enrichment. The effects of three important variables, eg bowl rotation frequency, back water flow rate and per cent solid were studied on the process performance. Increasing the rotation of the Falcon bowl, enable more material to the underflow by increasing the yield, whereas, the iron content decreases steadily with increasing the rotation of the bowl. The increase in the back water flow effectively removes the clay materials from the underflow at the expense of the yield. Similarly, increasing the per cent solid concentration in the feed produces a better product both in terms of yield and Fe content. Results show that EGS/Falcon can be used for processing Indian iron ore slime and producing pellet grade concentrate.

Sep 13, 2010

By A. Sariisik

This study analyses the results of a pilot trial of a newly developed armed-chained stone-cutting machine. The machine was developed in Turkey and trialed at the Kaklik/Kocaba travertine quarries in the Denizli District. An armed-chained cutting machine is an alternative to the diamond wire cutting method more frequently used in the production of natural stone quarry blocks, and increases production efficiency and quality. Since there is no need to collapse the blocks using the armed-chained cutting production process, there is no risk of the block developing cracks. This results in a considerable increase in the efficiency of natural stone block production. The armed-chained cutting machine is easier both to assemble and run when compared to other block cutting methods. This process resulted in the production of a larger number of blocks at a lower cost within the same time frame, particularly in travertine quarries and in all other natural stone quarries. The block efficiency in travertine quarries was calculated as 65?80%using the armed-chained cutting machine, compared with 7?14% using the normal diamond wire cutting method.

Jan 1, 2010

With the signing of the armistice on Nov. 11, the direction of the main concentration of effort of the United States was changed. In order to win the war, all industrial efforts had to be organized and centralized. With the war won and peace in sight, this centralization of effort stopped and the full play of individual initiative was allowed to resume its sway in the community. During this period of reversal of direction of effort, there was a natural loss of momentum and the United States, as well as the rest of the world, is in for a period of readjustment. The immense progress that was made in one direction under the stress of the necessities of war, which focused the energies of a nation in one direction, is an outstanding example of what can be accomplished if a community with many varying interests can be united on one objective which it desires to attain. The realization that the fusing of many interests into one stream of effort is difficult should not prevent us from taking the long view ahead that is necessary in order to be able to measure the progress made. If we don't have a mountain peak to guide us, we are very likely to run in circles in the plain without reaching the goal to which we strive. The most efficient development of natural resources is an ideal that, from a material point of view, appeals to the engineer. This ideal includes giving of opportunities to everyone to take a share in the development of these resources.. It also contemplates rewarding foresight

Jan 4, 1919

By S. Shi, J. Y. Hwang, B. Li

Silver, copper, and zinc are commonly known elements with antibacterial and antifungal capabilities. Attempts have been made to dope silver on minerals, glass, and ceramics and the resulting materials have been investigated for their antibacterial and antifungal properties. Since silver is expensive and very reactive, silver doped materials have been found inappropriate in some applications. Copper-vermiculite is investigated as an alternative. Vermiculite has high cation exchange capacity on the magnesium ion in the crystal structure. Copper ion may have a high tendency to replace magnesium because of similar charge interference and ionic radius. Copper-vermiculite is prepared by reacting vermiculite and copper chloride solution. By impregnating copper ions into the nanometer openings between the layers of vermiculite, it is possible to render the composite with antibacterial functions if the copper ions could be released gradually from the composite. The antibacterial efficiency of Cu-vermiculite against Escherichia coli was studied using the Halo method. The results show that Cu-vermiculite is effective for preventing the reproduction of the bacteria. Heat treatment of Cu-vermiculite at up to 400°C does not show significant changes in antibacterial activities.

Jan 1, 2002

By D P. Obeng, L Reemeyer, R Holmes

The Zinifex Century Mine employs a large number of Detritor mills for fine and ultra-fine grinding to liberate silica and sphalerite at 80 per cent passing 7.5 microns before final zinc flotation. A joint project between CSIRO Minerals and the Zinifex Century Mine was carried out to evaluate the Detritor mill performance. Plant surveys were conducted around the Detritors in conjunction with laboratory tests. The survey data showed that the Detritors in the ultra-fine milling circuit performed well. They reduced a feed F80 sizing of 46 microns to a product P80 sizing of 7.5 microns at a gross energy consumption of 37.2 kWh/t. Scale-up of ultra-fine milling Detritors was studied using a 0.55 kW laboratory batch unit and a 355 kW full-scale Detritor by processing Century zinc concentrate with 1 mm sand media. The results indicated that the 0.55 kW laboratory mill underestimated the energy consumption of the full-scale Detritor by about 20 per cent for a product P80 of seven microns. The performances of a horizontal IsaMill and a vertical Detritor were compared as ultra-fine milling devices for processing Century zinc concentrate. The experimental data demonstrated that, when using the same grinding media, the energy efficiency of the two mills is similar despite the difference in mill designs. The Detritors used for regrind duty at the Century Mine performed poorly when processing feed at 80 per cent passing 88 micron. The energy consumption was high and the product size distribution was broad with particles above 100 microns in the feed unbroken and particles below ten microns overground. A coarser ceramic media of 3 mm was therefore tested in a laboratory Detritor to process the regrind Detritor feed as an alternative to the 1 mm Colorado sand used at the Century Mine. The ceramic media reduced the energy consumption significantly and produced a narrower product size distribution, which is more desirable for the downstream flotation process.

Jan 1, 2007

By M. Gao

The Zinifex Century Mine employs a large number of Detritor mills for fine and ultra-fine grinding to liberate silica and sphalerite at 80 per cent passing 7.5 microns before final zinc flotation. A joint project between CSIRO Minerals and the Zinifex Century Mine was carried out to evaluate the Detritor mill performance. Plant surveys were conducted around the Detritors in conjunction with laboratory tests. The survey data showed that the Detritors in the ultra-fine milling circuit performed well. They reduced a feed F80 sizing of 46 microns to a product P80 sizing of 7.5 microns at a gross energy consumption of 37.2 kWh/t. Scale-up of ultra-fine milling Detritors was studied using a 0.55 kW laboratory batch unit and a 355 kW full-scale Detritor by processing Century zinc concentrate with 1 mm sand media. The results indicated that the 0.55 kW laboratory mill underestimated the energy consumption of the full-scale Detritor by about 20 per cent for a product P80 of seven microns. The performances of a horizontal IsaMill and a vertical Detritor were compared as ultra-fine milling devices for processing Century zinc concentrate. The experimental data demonstrated that, when using the same grinding media, the energy efficiency of the two mills is similar despite the difference in mill designs. The Detritors used for regrind duty at the Century Mine performed poorly when processing feed at 80 per cent passing 88 micron. The energy consumption was high and the product size distribution was broad with particles above 100 microns in the feed unbroken and particles below ten microns overground. A coarser ceramic media of 3 mm was therefore tested in a laboratory Detritor to process the regrind Detritor feed as an alternative to the 1 mm Colorado sand used at the Century Mine. The ceramic media reduced the energy consumption significantly and produced a narrower product size distribution, which is more desirable for the downstream flotation process.

Jan 1, 2007

Efficiency, Economics, Energy and Emissions - Emerging Criteria for Comminution Circuit Decision Making

Sep 13, 2010

By Wynand Erasmus, Terry A. Jones

The Kelsey Centrifugal Jig (KCJ) utilizes the application of centrifugal force (and the resultant enhanced gravitational field) to conventional jigging technology principles to successfully process materials where the valuable constituent particulates are very fine and/or where there is a small specific gravity differential between these and the gangue minerals. The KCJ has been successfully employed in mineral sands applications in Australia for approximately 12 years. More recently, the KCJ has been tested and installed on zircon tailings dump retreatment projects in Australia and the USA, while being considered for similar projects in RSA, and is about to be installed in zircon tailings processing duties in India and Africa and in a tin removal duty in a rutile circuit in Australia. Extensive test work has been carried out on these applications and some typical performance data is presented in this paper. Information is also provided on the principles of operation of the KCJ and on the keys to a successful KCJ installation.

By Peter Barker, Terry Jones

"The Kelsey Centrifugal Jig (KCJ) utilizes the application of centrifugal force (and the resultant enhanced gravitational field) to conventional jigging technology principles to successfully and efficiently process materials where the valuable constituent particulates are very fine and/or where there is a small specific gravity differential between these and the gangue minerals.The KCJ is applicable to a broad range of fine mineral recovery duties, with current installations in the mineral sands, tin, tantalum, gold and nickel industries. Other areas of application are being developed with mineral commodities including tungsten, base metals, iron ore, chromite and apatite/feldspar.Information on the principles of operation of the KCJ, typical performance figures in a number of application areas, comparison to centrifugal concentrators, key elements for a successful KCJ operation and recent developments with the KCJ are presented in this paper to demonstrate the capabilities of the KCJ.INTRODUCTIONAfter a number of years of development by inventor Chris Kelsey, the first commercial KCJ unit was installed at the Renison Bell tin mine in Tasmania, Australia, in 1992. The subsequent decade saw the installation of further KCJ units in applications including tin, tantalum and mineral sands.Development and improvement in KCJ hardware continued and culminated in the introduction of the high-capacity Model J1800 KCJ and standard features such as an automatic screen cleaning system. This opened up further markets and resulted in Model J1800 KCJ installations in the gold and nickel industries, as well as further KCJ installations in the mineral sands and tin industries. In recent years, work has continued on application of the KCJ to many other duties in industries including tungsten, base metals, iron ore, chromite, apatite/feldspar, etc."

Jan 1, 2007