By V. C. Williams

Some of the physical, chemical, and electrical processes for conversion of saline water to potable or industrial water are economically surveyed from an engineering viewpoint. Since all these processes require energy for drive and equipment for containment, the correlative economic factors are developed which indicate directive influences in the choice of particular regional processes. The supply of natural waters and its distance also affect decision. Any one process will probably not prove dominant in the field because auxiliary considerations such as the saline water source; types and continuing availability of fuel; electric power use or recovery; area economic status and advancement; and the political pressures of population, group demands, and land use tend equivocally to obscure capital and operation cost decisions. Basic engineering considerations, data, and economic factors are presented to assist in the direction of these decisions. An exploding world population, increasing industrialization, advancing standards of living, and the desire of less-privileged nations for betterment focus attention sharply on a major problem: water. *19 Up to now, in retrospect, people have had it relatively easy in the handling of this problem. All the better dams in the most advantageous sites, the better aquifers, the shortest aqueducts have been built. In another phase of the problem, concern is evident that wastes cannot indefinitely be disposed of merely by keeping them dilute and discharging them promiscuously. 7-9 And, perhaps, as past civilizations have done,l5 water, watersheds, streams, and irrigation may have been mismanaged or, at the least, not adequately studied.3,5,36,37 In this last is perhaps the core of the problem. As Gross states, "Ignorance and too often, indifference are contributing factors. Archaeology and theology both furnish ample testimony to the existence of rich lands where deserts now stand; it was man who ravaged his land. Unless education is a companion to water development, development might as well be forgotten. But without water, there is no beginning."13 The U.S. is showing increasing concern about its water for predictions are that by 1980 the daily withdrawals will be 494 billion gal, a figure nearly equal to the dependable supply.Is This is based on a conservative projected population of 230 million. The major categories of withdrawals are: To make available this per capita average of 2150 gal per day will require an expenditure of $219 billion over the next 20 years. The U.S. is not alone in this concern. The United Nations shows as arid zones of the world: all of Africa north of the equator and south of the 20's parallel; all of the Arabian peninsula; all of the middle east and Iran, Iraq, Pakistan, Afghanistan, northern and central India; a great band about 1000 miles wide along the 40'~ parallel from the Caspian Sea east across Russia through China to the Pacific Ocean; all of Australia except the coastal plain; the Caribbean Islands; the western nations of South America; and the western third of the United States and of Mexico. With one quarter of the earth's 57,500,000 sq miles of land thus suffering from lack of good water, increasing attention goes to the treatment of brackish and sea waters. The U.S. has been a leader in this field4,12, 16123,24 through its Office of Saline Water in the Dept. of Interior because even now some of its cities and regions are short of potable water. 11j'7,M Industrial water is also of vital concern as a result of ever higher industrialization1,14122 Other nations, among them JaPan, Israel,13188 Germany, Union of South Africa, Australia, Netherlands, France, Yugoslavia, Russia, and groups such as the Organization for European Economic Cooperation (OEEC)' are also diligent. The objective is low cost water, which means that both technology and economics have prominent roles in saline water conversion processes. TECHNOLOGY: SALINE WATER CONVERSION A number of reviews of methods have been made, principally by staff members of the Office of Saline Water (U.S. Dept. of Interior). Jenkins,31'32 Gillam,34p

Jan 1, 1962

By John L. Ham, Robert M. Parke

The melting point of molybdenum is 2625° + 50°C. Heretofore the metal has been considered too refractory to be melted in commercial quantities; hence, it has been formed into rod, wire, and sheet by the methods of powder metallurgy, wherein the temperatures do not exceed 90 per cent of the melting temperature. The manipulation of liquid metals at temperatures of about 2000°C. and above presents some difficult problems in heat transfer, in purification, and in container materials. For metals melting at such high temperatures, it is generally regarded as expedient to circumvent the more common melting and casting process by resorting to powder metallurgy. This circumvention is not accomplished without some penalties, the more notable of which are the relatively high cost of the powder metallurgy method and particularly the size limitations of its product. In an effort to overcome the inherent disadvantages of the powder metallurgy method, especially in respect to the limit of size, a project was begun in 1943 at the Climax Molybdenum Co. laboratory to develop a method of melting and casting molybdenum capable of producing larger bodies of molybdenum than were then obtainable. Later, from Feb. I, 1944, to Aug. 31, 1945, the project was under the supervision of the National Research Committee, Division One. In peacetime, too, there are needs for molybdenurn, which make consideration of another process desirable; for example, large parts for heat engines generally, the omnipresent demand for metal of higher quality and lower cost, and the development of molybdenum-base alloys. This paper describes methods for melting and casting molybdenum, with details of the special process needed to make molybdenum castings ductile, and reports some of the properties of what may be regarded as a new, or at least modified, form of the metal. First Process for Melting and Casting Molybdenum The maintenance of a temperature greater than 2625°C. in a 'pace large enough to melt several pounds of molybdenum may involve the loss of heat at a Very considerable rate. For melting molybdenum, therefore, the source of heat must be of high potential and of fairly high power. Evidently, also, the source of heat must not impair the purity of the product. The electric arc operating in vacuum appeared to meet these requirements and was accordingly the first choice as a source of energy. A number of arc devices for melting molybdenum were examined, and several were tried. In the first experiment, a 20-kw., 60-cycle-per-second alternating-current arc was operated between two horizontal and opposed electrodes of molybdenum- In this arrangement the falling droplets of molybdenum solidified below the arc in an irregular mass. This experiment did not produce a useful casting, but the data obtained indicated that

Jan 1, 1947

By Allan Martin, R. A. Swalin

Diffusion rates of manganese, aluminum, titanium, and tungsten in nickel were measured at temperatures between 1100° and 1300°C. Activation energies, Q, and values of the frequency factor, Do, were calculated for each system. Values of Q were found to be within 15 pet of that for self-diffusion of nickel in agreement with present theories of diffusion. ONE of the most interesting problems in diffusion concerns factors governing the order of diffusion coefficients of various solutes in a common solvent metal at low solute concentrations. An early suggestion by Rhines and Mehl' was that diffusion coefficients might each approach that of the self-diffusion coefficient of the solvent itself. Later Thomas and Birchenall' pointed out correlations between the order of the diffusion coefficients and the freezing point depressions of the solvent by the various solutes. Other correlations have been sought. To settle this question it seems likely that much more data will be needed and, in particular, data collected at low solute concentrations. This type can be obtained by special analytical techniques as well as by use of radioactive tracers. The following study was made of diffusion of manganese, aluminum, titanium, and tungsten in a common solvent, nickel, at relatively low solute concentrations: 1—Production of alloys of nickel with manganese, aluminum, titanium. and tungsten at concentrations of the order of 1 atomic pet. 2—Use of pressure-welded diffusion couples in cylindrical form. 3—Diffusion anneals in the temperature range of 1100" to 1300°C. 4—Lathe sectioning of the diffused couples. 5—Spectrophotometric analyses of lathe turnings for the solute being studied. 6—Calculation of the diffusion coefficient for each of the solutes as a function of temperature. 7—Interpretation of results with current theories of diffusion. Experimental Work Materials—Two types of nickel were used in this research. The grade designated as Vacuum melted Mond nickel was used for all diffusion systems except the Mn-Ni system for which the Vacuum melted electrolytic nickel was used. Analyses of the two grades are given in Table I. The manganese used in making alloys was 99.9 + pet pure, aluminum 99.99 pet pure, titanium 99.9 pet pure, and tungsten of C.P. grade powder. Alloys used in this investigation were prepared by melting in vacuo or under a low pressure of argon. After melting, all heats except those of nickel-manganese were poured into a cylindrical copper mold 3 in. long and 1 in. ID. In the case of nickel-manganese, the alloys were solidified in the melting crucible. For nickel-aluminum heats alumina crucibles were used and for all other heats, zirconia crucibles.

Jan 1, 1957

By A. D. McMaster, M. L. Gimpl, N. Fuschillo

There is interest in the use of rhenium metal films as resistive elements in thin-film circcits, and already some zvork has been done using er)aporated rhenium films. It has been found that rheniim films protected from the atmosphere by an evaporated layer of silicon monoxide show excellent electrical stability. Unprotected films, however, are subject to aging- effects, notably the increase in electrical resistivity as a function of time. This phenomenon can be understood as primarily one of oxidation of the thin films. This paper is concerned with the study of the oxidation and crystallization behavior of such unprotected films. It has been found that the oxidation rates are a function of the substrate temperatures used during the deposition of Lhe metal films. The strictures observed in the films are correlated with the film resistivities and some data are presented to establish the existence of the various types of oxides of rhenium. ThERE is some interest in the use of thin films of rhenium metal as resistive elements in monolithic, thin-film integrated circuits. Some work has been done using evaporated films and it has been found that such films, if protected from the atmosphere by an evaporated layer of silicon monoxide, show excellent electrical stability up to temperatures of 500"." Rhenium films unprotected from the atmosphere tend to age and the electrical resistivity of the films increases as a function of time. Rhenium films, of the order of <100A thick, prepared by electron-beam evaporation techniques are found to oxidize very readily when exposed to dry air at room temperature. It would seem, therefore, that this aging phenomenon could be attributed to the oxidation of the metal films. In this investigation, the oxidation and crystallization behavior of thin films of rhenium evaporated onto silicon monoxide substrates were studied as a function of the substrate temperatures used during the evaporation. The films were examined using electron-microscopy and electron-diffraction techniques. EXPERIMENTAL RESULTS Rhenium metal was evaporated onto suitable prepared substrates which were heated to various temperatures. The evaporations were performed in a vacuum of approximately 5 x 1CT5 torr. The evaporation was carried out at a rate of approximately 10A per omin. The final film thickness was approximately lOOA and the resistance ranged from 5000 to 10,000 ohms per square. The substrates used for supporting the metal films were made by evaporating 75A of silicon monoxide onto freshly cleaved mica. The silicon monoxide film was then floated off the mica by immersing the composite in water. The film could then be picked up on a clean nickel grid. Silicon monoxide substrates were chosen because of their similarity to quartz and glass substrates commonly used for making thin-film resistors. Fuschillo, Gimpl, and McMas-ter have also shown that silicon monoxide films have only minor structural changes at temperatures up to 800°C. This fact simplified the interpretation of any changes observed in the electron micrographs or electron-diffraction patterns obtained from the deposited rhenium films. After the evaporations were completed, the substrates were cooled to room temperature, except where noted differently, before the coated substrates were removed from the vacuum system. All aging of the deposited films was done in a desiccator. The evaporated films were examined in an electron microscope equipped with a hot stage that would permit continuous observations of the samples up to temperatures of 1000°C. RESULTS A series of electron micrographs of the rhenium films deposited on the silicon monoxide substrates are shown to Figs. 1 to 3. In all cases, the metal films are approximately 100A thick and the micrographs were taken 1 hr after the deposition was completed. here was no apparent structure in the films deposited on the substrates held at the higher temperatures. The

Jan 1, 1967

By R. F. Mehl, C. S. Barrett, A. H. Geisler

The complicated nature of the property changes that accompany age-hardening has made it necessary to reconsider and to elaborate the simple dispersion theory.l It has been apparent for some time that more direct information is needed concerning the atomic mechanism of precipitation from solid solution if the theory of age-hardening is to be developed past a purely qualitative stage.‡ Fortunately, in recent years information has been developed which allows us to trace in detail the lattice changes accompanying the process of precipitation from solid solution. This information relates chiefly to the sequence of the several stages of lattice alteration by which the matrix lattice is transformed to the equilibrium precipitate lattice, and permits reasonable inferences to he drawn concerning the states of internal strain that accompany these stages. This information is most complete for the solid solution of copper in aluminum. The equilibrium precipitate is the 0 phase, "CuAl2." This forms in plates, parallel to the {100} matrix planes. The atom pattern and atom spacing on the plane in 0 lying parallel to this plane are roughly similar to those opposite it in the matrix.3 The formation of 0, however, is preceded by the formation of a transition lattice 0&apos;: which again lies parallel to the matrix {100} plane, but in this case the matching of atom pattern and spacing across the matrix-precipitate interface is nearly periect; thus there is lattice coherency across the interface and the interface is a plane of separation in only a very limited sense.&apos;8 Particles of 0&apos; may be recognized microscopically and form a well-defined Wid-manstatten figure.* The 0&apos; lattice is recognized by the occurrence of diffraction lines on powder photo-grams or of spots on Laue photograms which may be analyzed in the usual ways to determine the lattice type and the lattice spacings. Very recent research 6, 7, 1 has shown, however, that streaks occur on the Laue photogram at an earlier point in time during the aging process. These streaks have been attributed to a preferential clustering of copper atoms into small platelike elements of only a few atoms in thickness and a lew hundred atoms in diameter, probably of the composition of " CuA12," which may be designated as Guinier-Preston zones or aggregates.1 It is difficult if not impossible to determine the lattice type and lattice spacing in these aggregates. It is possible1 that these aggregates are in fact ?&apos; in a high State of dispersion; the inclination to argue this is strong, as we shall see later. Never-

Jan 1, 1941

THE composition and quality of finished steel depend upon selection and proportioning of the raw materials of the charge as well as on control of furnace practice. This chapter deals only with those raw materials of the basic open-hearth process which are important in determining the composition of the steel or slag. They are the metallic charge, oxygen-bearing materials, fluxes, and alloying and deoxidizing additions. Refractories, which may also affect the slag composition, are discussed in the previous chapter. Wide variations are possible in the type and composition of charged materials, but in all cases certain fundamental relationships among the elements of the charge must be maintained. Since the process consists essentially of refinement by oxidation of undesired elements, a balance must be established between the sources of oxygen and the elements in the charge that are subject to oxidation (see Chapters II and VII). For example, if it is desired to use a high ratio of blast-furnace hot metal to scrap, it is necessary to add an oxygen-bearing material such as ore or mill scale to eliminate the excess carbon and silicon that are present in the hot metal. An example of the opposite extreme would be the use of a metallic charge composed entirely of steel scrap. With this type of charge, it is common practice to substitute burnt lime for limestone as a flux and to charge some carbonaceous material such as coke to avoid an excess of oxygen in relation to the elements of the charge that are subject to oxidation. Elements such as copper and nickel, which are not subject to oxidation or other reactions resulting in their elimination, may be introduced into the charge only to the extent to which they are permissible in the finished steel. An example of adjustment of the charge for elements of this type would be found in the use of steel scrap high in copper. In this case, metallic components of the charge other than the scrap should below in copper, or a sufficiently high ratio of pig iron to scrap should be charged to dilute the copper from the scrap, so that the average copper content of the melt will be below the required maximum.

Jan 1, 1944

By E. Miller, J. M. Eldridge, K. L. Komarek

Activities of magnesium in liquid Mg-Sn alloys have been determined between 5 and 90 at. pct Sn and 990" and 1290°K by an improved isopiestic method wherein tin specimens, heated in a temperature gradient and contained in crucibles of special geometry, were equilibrated with magnesium vapor in a closed titanium system. The crucibles were designed so that the equilibrium compositions of the specimens were satisfactorily preserved on termination of the experimental runs by quenching. The activity values are in excellent agreement with those predicated on the phase diagram and allowed a delineation of the solidus curve of the compound Mg2Sn near its melting point. EQUATIONS have been recently derived relating the chemical potentials of the components to the liquidus and enthalpy data for binary systems exhibiting one congruently melting compound.&apos; The liquidus curve of the Mg-Sn system between the eutectics was carefully redetermined and the thermodynamic properties thus calculated were in reasonably good agreement with values derived from electromotive-force measurements of an,&apos; but differed greatly from the iso-piestically determined values of Ashtakala and Pid-geon.3 The present study was initiated: a) to resolve the discrepancies; b) to develop a method for measuring activities in systems having volatile (and possibly highly reactive) components; and c) to use the method in a general investigation of the thermodynamic properties of the homologous series of Mg-Group IVb systems, i.e., Mg-Pb, Mg-Sn, Mg-Ge, and Mg-Si. This paper describes the results for the Mg-Sn system. An isopiestic technique, originally developed by Herasymenko 4 and adapted for alloys having a component of high reactivity and low volatility,5-8 was modified in this study by using crucibles designed to preserve the equilibrium composition of highly volatile liquid specimens on quenching from high temperatures. Tin specimens, contained in tightly covered graphite crucibles and heated in a temperature gradient, were equilibrated with magnesium vapor of fixed pressure from a magnesium reservoir kept at constant temperature in a previously evacuated and sealed titanium tube. During equilibration magne-

Jan 1, 1967

By D. L. Feucht, R. L. Longini

The semiconductor heterojunction is considered in terms of simple models which may lead to an understanding of move complex heterojunctions. Metallurgical and electrical properties of hetero-junctions aye discussed including the interface structure, energy -band diagram, and carrier transbovt across the interface. It is found that in a heterojunction all mechanisms such as injection, tunneling, and junction recombination found in simple junctions play modified voles. INTERFACES between materials (grain boundaries, the electrical junction between two differently doped materials in a single crystal, the oxide-metal interface, or metal-metal junctions) are of considerable importance in many situations. These various interfaces all have one very fundamental thing in common. Quantum mechanically speaking, the wave functions of the electrons in one material may penetrate the other material but, in general, only to the extent of angstroms. From an electrical point of view the conduction mechanism changes as a current passes through such junctions. In some cases the change is tremendous, in others almost negligible. The interface, then, is the locus of a change of conduction mechanisms. Some of these, particularly in semiconductors, are well-understood. The ordinary p-n junction in a single crystal can be the locus of an injection mechanism or a tunneling process, depending on conditions. The mechanisms are probably best understood in semiconductors because of the possible simplified view of particlelike conduction. The bands are either nearly filled or nearly empty and band overlap is seldom involved. The same fundamentals are probably important in other situations too but they are very difficult to look at naively. Although the simple look at the semiconductor case only gives us a relatively rough picture which must then be refined, the other systems, which involve a more complex situation, immediately are in many ways too difficult. There are too many initial choices of complex systems and therefore it is not possible to be even reasonably certain of any one model. Because of the relative simplicity of semiconductors, their good and controllable structure, and because of the ability to make many measurements on them not normally available to either metals or insulators! they are probably the best understood materials. It is therefore desirable to use them as a tool to further the understanding of interfaces in general. Semiconductor-heterojunction concepts were first proposed by kroemer1 in 1957. This was followed several years later by reports on the fabrication and experimental characteristics of heterojunction structures by Anderson2 and Diedrich and jotten.3 I) THE HETEROJUNCTION STRUCTURE To get down to hardware, when we refer to a semiconductor heterojunction we imply that there exists an intimate contact between different semiconductor materials. We could put two pieces of material together, complete with oxide layers, we could remove the oxides, or we could even melt the interface and hopefully get wetting and a good "bond" on solidifying. In fact we could by some means grow a crystal of one material using the other as a seed. Essentially we are interested only in the last two because they are the simplest to look at analytically. The degree of perfection of fit varies greatly and is reflected somewhat in the arc welder&apos;s joint strength. The lattice match of the two materials, their orientation, and so forth. is obviously necessary for a good bond but so is the continuity of any polar bonds which are involved such as in the III-V semiconductors. The mechanical misfit between two similar lattices can be described in terms of edge dislocations. The edge-type dislocations must be very close together for the usual misfit and there must be dislocations for each of several different Burger&apos;s vectors in order to produce a lattice match. The .&apos;dangling bonds&apos;&apos; resulting will be involved in producing interface charge. Order of magnitude estimates of the charge density extrapolated from low densities of dislocations in homogeneous materials give 5 x 1013 cm-2 Ge-Si and 1 X 1012 cm-2 Ge-GaAs electronic charges. Edge dislocations also act as very active recombination centers between holes and electrons. One lattice "matching" difficulty usually exists even if two structures have essentially the same lattice constants as they will have different coefficients of therma1 expansion. Thus, on cooling from the usually high temperature of fabrication to room temperature, dislocations are produced, a good fit not existing at both temperatures. In brittle materials this shrinkage may even result in cracking. For the Ge-Si interface the mismatch is about 2 x 10 -6 per degree whereas it is less than 10"7 per degree between germanium and GaAs. The exact effect of the misfit is dependent on the thickness of the materials involved. For a very

Jan 1, 1965

By T. D. Murphy

The element silicon, with its usual partner, oxygen, plays the same role on this planet relative to inorganic materials as carbon and hydrogen play with respect to living organisms. The crystallographic structure of silicon dioxide (SiO,) consists of one atom of silicon well-nigh inseparably bonded to four contiguous atoms of oxygen, a gas of but slightly more than half its atomic weight, forming a three-dimensional network of SiO, tetrahedra (Dietz, 1968). This wispy arrangement is the fabric of the mineral quartz which is one of the harder, more abrasive, and chemically stable raw materials to be found in Mother Nature&apos;s cupboard. Most of us are vaguely familiar with the observation that nearly 60% of the lithosphere to an approximate depth of 10 miles is composed of these two elements, which proportion actually rises to about 75% if the atmosphere, hydrosphere, and biosphere are included (Parker, 1967). Elemental silicon is a brittle steel-gray metalloid with a density of 2.42 and does not occur in nature. In its limited commercial form, which is still brittle and metallic in appearance, its density drops to 2.33. It combines with oxygen to form the gaseous oxide SiO, or the solid dioxide SiO, (analogous to its congener carbon in CO and CO,); a tetrachloride SiCl, (analogous to CC1,); or, combining with oxygen and one or more metal ions, forms the largest rock-making family of all, the silicates. Further, next to the feldspars, quartz is the most abundant known mineral and, in some form or another, accounts for roughly 12% of surficial terrestrial rock. It is this so-called "free silica" to which your attention is chiefly directed in this chapter. In any such consideration of silica, its several crystalline phases with their attendant differing physical properties appear worthy of delineation. Alpha quartz is the only one of this interesting polymorphic family that is thermodynamically stable at normal pressures and temperatures up to about 573°C. The low phases of tridymite and cristobalite can exist in the so-called metastable state below 117°- 200°C but seldom occur in nature in these two different crystal forms (Sosman, 1965). Opaline silica, now considered by most researchers to be a variety of cristobalite, occurs in abundance and is the only exception. The three remaining polymorphs, keatite, coesite, and stishovite, also are metastable under ambient conditions. Keatite, however, is not known to occur naturally and has only been synthesized in the laboratory. The other two have been identified in submicron sizes and in microscopic amounts, occurring naturally as a result of high order shock-wave pressures generating quite elevated temperatures-such as might accompany the impact of a large meteorite on a hard sandstone terrain (Chao, et al., 1962). An intriguing characteristic of these silica minerals, and one which has very practical applications, is their extremely variable densities. The classic 2.65 specific gravity of alpha quartz drops to 2.20 in tridymite, cristobalite, and lechatelierite (natural silica glass), as well as in many man-made glasses of commerce which are merely noncrystalline or amorphous solids in the form of super-cooled liquids which can no longer change their shapes (Pauling, 1950). It rises again to 2.50 and 2.93 for keatite and coesite, respectively, and finally becomes a reported 4.35 for stishovite-nearly a 50% range in density for the known physical combinations that silica naturally assumes (Frondel, 1962; Konnert, et al., 1973; Pecora, 1960).

Jan 1, 1975

By W. J. Millard

It is well known that the excellent mica from Brazil played a most vital role in World War 11. Increased production from Brazil was necessary and with the assent of the Brazilian Government engineers from the united&apos; States went down to study the problem. One of the means advocated by a former Chief of Metals and Minerals Branch of the Board of Economic Warfare, Mr. Carl Schwegler, was the use of stripping machinery. On a pegmatite dike favorable for stripping, a small number of miners could produce as much mica per day as an underground mine employing many times the same number of men. Type of Deposit Favorable The most favorable type of pegmatite for stripping is that which lies more or less parallel to the surface of the slope of a hill. Pegmatite dikes that cut directly into a hill are not suitable for stripping except where a long outcrop extends along the slope. Then just the outcrop could be stripped to some advantage. The ratio at no time should be greater than 1: 3; i.e., I cu. m. of pegmatite to 3 cu. m. of waste, unless the pegmatite was extremely rich throughout the dike. The Economics of Stripping When a mineral is badly needed to win a war, not too much heed can be paid to costs. The object is to produce rapidly and in quantity. Again, a deposit containing a superior grade of mica may be worked although the pegmatite is more costly to work than another deposit containing a considerably greater amount of poor-grade mica. For example: one deposit may have a little mica that will run 11 per cent good stain and better when trimmed and contain 2 kg, of crude mica per cubic meter of pegmatite, while another may run 0.2 per cent of good stain and better, and have a mica content of 10 kg. per cubic meter. A number of stripping projects were found in the vicinity of Raul Soares, Minas Gerais. These were sampled in the various old workings by cutting out a cubic meter of pegmatite and saving the usable mica. Because of the proximity to the surface of most stripping projects, about 34 per cent only of the mica is good for trimming. The other 66 per cent is too badly weathered to be of use. In Table I are given data collected on five properties near Raul Soares. In Table I, "value per cubic meter of pegmatite" means the value of the qualified mica obtainable. This does not include the half trimmed and splittings. By "value per cubic meter of matter" is meant the value of the qualified mica per cubic meter of material excavated; i.e. both waste and pegmatite. This is the figure that should be used to determine whether the operation will be profitable or not, as the cost of stripping is about $0.14 per cubic meter. With new machinery not subject to breakdowns, the cost per cubic meter should be around $0.10 to $0.15. To this should be

Jan 1, 1948

By K. E. J. Rapperport, C. S. Hartley

The only slip system observed in zirconium crystals deformed at 77", 575", and 1075OK was (1010) [1210] with a critical resolved shear stress in tension of 1.0 kg per sq mm at 77°K; 0.2 kg per sq mm at 575 °K; and 0.02 kg per sq mm at 1075 OK. The active twin planes were {1012}, (1121}, (11221, and (11233) with varying temperature dependence. A detailed analysis for the slip direction using Laue spot asterism is appended. NeARLY all metals of the hexagonal close-packed structure exhibit basal slip, i. e.,(0002)<1120>- type slip. This is true of magnesium,&apos; zinc,&apos; cadmium,3 beryllium,4 titanium,= yttrium,6 and rhenium.Many of these such as titanium 5&apos;8-&apos;0beryllium,4&apos;" magnesium, and zinc13&apos;14 display other slip modes even at room temperature, and nearly all have been reported to slip on other systems under particular loading or temperature conditions of testing. As is shown in this paper, basal slip was not found at any of four test temperatures from 77" to 1075°K in hexagonal close-packed zirconium under the simple loading conditions of tension and compression, even though in one case the resolved shear stress on the inactive (0002) <llgO> system was twenty-five times higher than the critical resolved shear stress on the active (1010) [1210] system. This result is consistent with prior studies on the active deformation processes in zirconium deformed at room temperature. &apos;&apos;-I7 SPECIMEN PREPARATION A) Material—The zirconium used in this work was of two types: 1) as-deposited reactor grade crystal-bar, and 2) arc-melted and forged reactor grade crystal-bar. Typical chemical and spectrographic analyses of these materials as received, and after hydrogen removal and crystal growth are given in Ref. 17. Crystals of type 1) above have the letter prefix (A) and those of type 2) have the prefix (B) throughout this paper. B) Crystal Growth— he zirconium was machined into rectangular parallelepipeds about 0.2-in. scl in cross section and 2 in. iong. These were hand polished through 4/0 abrasive paper, electropolished, given a hydrogen removal anneal, and subjected to long-time anneals at 840 °C in vacuo to produce usable crystals.&apos;7 A second technique used to obtain large crystals was to cycle the samples two or three times between 1200" and 840°C, allowing them to remain at the higher temperature for about 4 hr and at the lower temperature for 5 days.17 These techniques yielded some grains which occupied the entire cross section of the bar and were as long as 3/4 in. C) Orientation Determination—After the growth of large crystals by thermal cycling, the samples were repolished with extreme care through 4/0 abrasive paper and electropolished. Metallographic examination after polishing showed the surfaces to be free of visible deformation traces. Standard Laue back-reflection X-ray techniques were used to find the crystallographic orientations of selected large grains with respect to a specimen face and edge. Fig. 1 shows the stereographic projections of the stress axes for the crystals used. The sharpness of the spots on the Laue photographs indicated that the crystals were of good quality. EXPERIMENTAL METHODS Nine crystals were deformed in tension at 77"K, nine in tension and five in compression at 300°K in previous tests,17 fifteen in tension at 575"K, and eleven in tension at 1075°K. All specimens were stressed by load increments. After a predetermined load was applied, the specimen was removed from the loading appratus and metallographically examined for deformation traces. An attempt was made to initially stress each bar so that some crystals slipped a small amount and others not at all. This was done to bracket the critical resolved shear stress. One bar of special orientation (B-11) was repolished and annealed at 1075°K for 1 hr after lower temperature deformation, before final deformation at 1075°K. In the other bars the loading by increments, followed by metallographic examination, was continued until the surface distortion would interfere with analysis, or until fracture. One example of a crystal pulled to fracture is shown in Fig. 2. This photograph shows a crystal (B-14C) which was pulled at 1075°K and failed by slip on two (10i0) planes. The approximate orientation of this crystal is illustrated in the figure. Specimens were deformed at 77°K in liquid nitrogen on a tensile machine using an insulated bucket with an internal hook to accept a clamped specimen.

Jan 1, 1961

By W. C. Winegard, J. E. Gruzleski

The stages in the development of cells in the Sn-Cd eutectic have been studied by unidirectionally solidifying specimens under known conditions of growth rate, temperature gradient, and impurity concentration. By means of a quenching technique, the shape of the solid-liquid interface during solidification could be observed. Cells are shown to develop from defects or depressions which exist on the solid-liquid interface of even a pure eutectic. Th,e container wall, grain boundaries , and fault lines in the micro structure play an important role in cell development. A two-phase eutectic dendrite found at high impurity concentrations is described. L HE cellular or colony structure formed during eutectic solidification caused much confusion among early workers in their attempts to classify eutectic structure, and a major advance in our understanding of eutectic solidification was made when the colony structure was identified with a cellular interface caused by the presence of impurity elements.1&apos;2 To date, however, no detailed investigation of the stages in cell development in eutectics has appeared, and little work has been done on the cell morphology. The present paper presents the results of such an investigation. EXPERIMENTAL The Sn-Cd eutectic was used in this investigation with lead as the impurity element to promote cell formation. Materials of 99.999 pct purity were zone-refined to an approximate purity of 99.9999 pct. Alloys as close as possible to the eutectic composition, 67.75 wt pct Sn, were prepared using zone-refined tin and cadmium. The alloys were then zone-melted to the exact eutectic composition, as described by Yue and Clark,3 using a total of twenty to twenty-five passes on each eutectic bar. Only those portions of the bars which contained no primary phases were used in subsequent experiments. Master ternary alloys were prepared by melting together the required amounts of lead and the Sn-Cd eutectic in a sealed Pyrex tube under argon, and these alloys were then diluted with pure Sn-Cd eutectic as required. Unidirectional solidification was conducted vertically upward using the two-element resistance furnace shown schematically in Fig. 1. With this apparatus, it was possible to obtain a range of growth rates and temperature gradients so that the cell structure could be studied under different growth conditions. Growth rates in the range of 0.4 to 9.1 cm per hr and temperature gradients from 2.25° to 1475°C per cm were used. To ensure steady-state solidification, power to the furnace was stabilized, and the entire apparatus was enclosed in a large box in which the temperature was controlled to within ± 0.2°C. The apparatus was arranged so that the specimen could be quenched in situ during solidification by pouring a large quantity of water down the central vycor tube. Excellent delineation of the solid-liquid interface at the time of the quench was obtained because of the structural changes accompanying the rapid solidification of the remaining liquid. The quenching rate was always extremely rapid as no evidence of a transition in the lamellar spacing at the interface was ever observed. The alloys to be solidified were contained in degassed, high-purity graphite tubes, 1 cm OD and 0.6 cm ID. The specimens were about 18 cm in length. After the alloy had been cast into the tubes, three 0.8-mm holes were drilled in the tube to the center of the specimen. One hole was placed 1 cm from the bottom of the ingot, and the other holes were placed at 8 and 9 cm, respectively, from the base of the ingot. Thirty-four-gage chromel-alumel thermocouples were sealed in the holes. The lower thermocouple was used to position the solid-liquid interface at the start of each experiment,

Jan 1, 1969

By C. S. Smith, E. W. Palmer

IN 1934, when Gregg and Daniloffl wrote their excellent monograph on the alloys of iron and copper, the most recent literature on the constitution of the alloys indicated a narrow single-liquid area for 20" above the liquidus with a closed liquid mis-cibility gap above this. Since that time, however, a number of investigators have confirmed the much earlier studies of Mushet2 and Stead3 who, among others in the nineteenth century, had described the true state of affairs. Liquid copper and iron are completely miscible in the absence of carbon, but small amounts of carbon cause liquid segregation. In 1934, one of the writers&apos; mentioned evidence for the absence of liquid separation in carbon-free alloys at temperatures up to 1700°C. Two years later, Mad-docks and Claussen5 unequivocally established the absence of liquid segregation and published a revised diagram, reproduced in fig. 1. They also studied the limits of the two-liquid area in ternary alloys of iron, copper, and carbon as a function of carbon and iron content. In the same year Simpson and Bannister" and Schumacher and Souden7 described in some detail the properties of alloys containing 50 to 75 pct Cu. More recently Hodges et al.16 have developed the copper-rich alloys for use as high-strength conductors. In 1937, Iwase, Okamoto, and Ameniya8 published data on the miscibility gap in ternary alloys of iron, copper, and carbon that supported the conclusions of Maddocks and Claussen, and definitely located the two-liquid area at temperatures of 1450" and 1540°C. They also reported that additions of 1 pct Al, Ni, Pb, Sn, or Zn caused no segregation in 50 pct Cu alloys at 1540°C. The use of copper in amounts approximating 1 pct has found industrial employment to an increasing degree in both wrought and cast steels, for such steels are capable of being precipitation-hardened following normalizing, and have high yield strengths. This is summarized by Gregg and Daniloff,1 Sallitt,9 and Lorig and Adams,10 while Alexander" gives additional information on the heat treatment of copper-steel castings. Lippert12 has described Digby&apos;s two-phase steels containing copper and chromium. The work described in the present paper was done in the years 1932 to 1934, at which time much of the information was new. The excellent work subsequently done in other laboratories but more promptly published makes the present paper in part only a confirmation of what is now well known. There has not, however, been published any unified study of

Jan 1, 1951

By A. A. Venghiattis

A rational approach to the selection of the appropriate perforator to use in each specific zone of an oil well is presented. The criteria presently in use for this choice bear little resemblance with actual down-hole condilions. These environmental conditions affect the elastic properties of rocks. One of these elastic properties, acoustic velocity, is suggested as the leading parameter to adopt for the choice of a perforator because, being currently measured in the natural location of the formation, it takes into account all of the effects of compaction, saturation, temperature, etc., which are overlooked in the laboratory. Equations and curves in relation with this suggestion are given to allow the prediction of the depth of perforation of bullets and shaped charges when an acoustic log has been run in the zone to be perforated. INTRODUCTION When an oil company has to decide on the perforator to choose for a completion job, I wonder if it is really understood that, to date, there is no rational way of selecting the right perforator on the basis of what it will do down-hole. This situation stems from the fact that the many varieties of existing perforators, bullets or shaped charges, are promoted on the basis of their performance in the laboratory, but very little is said on how this performance will be affected by subsurface conditions such as the combination of high overburden pressure and high temperature, for example. The purpose of this paper is to show the limitations of the existing ways of evaluating the performance of perforators, to show that performances obtained in laboratories cannot be extended to down-hole conditions because the elastic properties of rocks are affected by these conditions and, finally, to suggest and justify the use of the acoustic velocity of rocks, as the parameter to utilize for the anticipation of the performance of a perforator in true down-hole environment. EVALUATING THE PERFORMANCE OF A PERFORATOR It is natural, of course, to judge the performance of a perforator from the size of the hole it makes in a predetermined target. Considering that the ultimate target for an oilwell perforator is the oil-bearing formation preceded in most cases by a layer of cement and by the wall of a steel casing, the difficulties begin with the choice of an adequate experimental target material. For obvious reasons of convenience, the first choice that came to the mind of perforator designers was mild steel. This is a reasonable choice for the comparison of two perforators in first approximation. Mild steel is commercially available in a rather consistent state and quality, and is comparatively inexpensive. The trouble with mild steel is that it represents a yardstick very much contracted; minute variations in depth of penetration or hole diameter and shape may be significant though difficult to measure. The penetration of projectiles in steel being a function of the Brinell hardness of the steel (Gabeaud, O&apos;Neill, Grun-wood, Poboril, et al), it is often difficult to decide whether to attribute a small difference in penetration to a variation on the target hardness or to an actual variation on the efficiency of the projectile. Another target material which has been widely used for testing the efficiency of bullets or shaped charges in an effort to represent a formation—a mineral target as opposed to an all-steel target—is cement cast in steel containers. This type of target, although offering a larger scale for measuring penetrations, proved so unreliable because of its poor repeatability that it had to be abandoned by most designers. The drawbacks of these target materials, and particularly their complete lack of similarity with an oil-bearing formation, became so evident that a more realistic target arrangement was sought until a tacit agreement was reached between customers and designers of oilwell perforators on a testing target of the type shown on Fig. 1. This became almost a necessity about seven years ago because of the introduction of a new parameter in the evaluation of the efficiency of a perforator, the well flow index (WFI). The WFI is the ratio (under predetermined and constant conditions of ambiance, pressure and temperature) of the permeability to a ceitain grade of kerosene of the target core (usually Berea sandstone) after verforation. to its vermeabilitv before perforation. The value of this index ;or the present state if the perforation technique varies from 0 to 2.5, the good perforators presently available rating somewhere around 2.0 and the poor ones around 0.8, There is no doubt that, to date, the WFI type of test is by far the most significant one for comparing perforators. It is obvious that a demonstration of a perforator

By Shiou-Chuan Sun

THIS paper presents the design and operation of a frothmeter capable of measuring the frothing characteristics of pine oils and other frothing reagents. The experimental data show that the frothability of pine oil is governed by: 1-rate of aeration, 2-time of aeration, 3-height of liquid column, 4-chemical composition of pine oil, 5-pH value of solution, 6-temperature of, solution, and 7-concentration of pine oil in solution. The effect of mineral particles on the behavior of froth also was studied, and the results can be found in a separate paper.1 The results also show that the relative frothabilities of pine oils in the frothmeter generally correlate with those in actual flotation, provided that other factors are kept constant. In addition to pine oils, the other well-established flotation frothers were tested, and the results are included. In this paper, compressed air frothing is the frothing process performed by means of purified compressed air, whereas sucked air frothing is the frothing process accomplished by purified air sucked into the glass cylinder by a vacuum system. The term vacuum frothing denotes that froth was formed by degassing of the air-saturated liquid under a closed vacuum system. Apparatus The frothmeter, shown in Fig. 1, is capable of reproducibly measuring the volume and persistence of froth as well as the volume of air bubbles entrapped in the liquid and is capable of being used for compressed air frothing, sucked air frothing, and vacuum frothing. Fig. la shows that for compressed air frothing, the apparatus consists of an airflow regulating system, 1-3; a purifying and drying system, 4-8; a standardized flowmeter to measure the rate of airflow from zero to 500 cc per sec, 9; and a graduated glass cylinder, 13; equipped with an air regulating stopcock, 10; an air chamber, 11; and a fritted glass disk to produce froth, 12. The fritted glass disk, 5 cm in diam and 0.3 cm thick, has an average pore diameter of 85 to 145 microns. The pyrex glass cylinder has a uniform ID of 5.588 cm and an effective height of 63 cm. The inside cross-sectional area of the glass cylinder was calculated to be 24.53 sq cm, or 3.8 sq in. For sucked air frothing, Fig. lb shows that the apparatus for compressed air frothing is used again, with the following modifications: 1-compressed air and its regulating system, 1-3, are eliminated; and 2-a vacuum system, 16, equipped with a vapor trap, 15, and a vacuum manometer, 17, is added. The vacuum system can be .either a water aspirator or a laboratory vacuum pump. Any desired rate of airflow can be drawn into the glass cylinder, 13, by adjusting the opening of the air regulating stopcock, 10. The sucked air stream is cleaned by the purifing and drying system, 4-8, before entering the glass cylinder, 13. When this setup is used for vacuum frothing, the air regulating stopcock is closed. The frothmeter has been used for almost 3 years and has proved to give reproducible results, as illustrated in Table I. With a magnifying glass and suitable illumination, the frothmeter also can be used to study the attachment of air bubbles to coarse mineral particles.2 Experimental Procedures Except where otherwise stated, the data presented were established by means of the compressed air method. The volume and persistence of froth were recorded respectively at the end of 4 and 6 min of aeration at a constant rate of airflow of 29.3 cc per sec which is equivalent to 71.6 cc per sq cm per min, or 462.6 cc per sq in. per min. The aqueous solution for each test, containing 1000 cc of distilled water and 19.2 ± 0.5 mg frothing reagent, was adjusted to a pH of 6.9 ± 0.2. The volume of froth is expressed as cubic centimeter per square centimeter and is equivalent to the height of the froth column (the distance between the bottom and the meniscus of the froth). The volume of froth was obtained by multiplying the height of froth by the cross-sectional area of the glass cylinder, 24.53 sq cm. Before each test, the glass cylinder, 13, was cleaned thoroughly with jets of tap water, ethyl alcohol, tap water, cleaning solution, tap water, and finally distilled water. The cylinder with stopcock,

Jan 1, 1952

By Richard P. Hight

Abrasives include the substances, natural or artificial, that are used to grind, polish, abrade, scour, clean, or otherwise remove solid material, usually by rubbing action but also by impact (pressure blasting for example). They do not include abrasive tools, for instance, lathe tools and files-or polishing agents such as waxes, which act by filling pores. Detergents and cleaners whose action is chemical rather than physical are omitted although some chemical-action polishes and cleaners may also contain solid abrasives, for example, many automobile and metal polishes. General Considerations The most important physical properties of materials that qualify them for use as abrasives are hardness, toughness (or brittleness), grain shape and size, character of fracture or cleavage, purity or uniformity. For making bonded abrasive products such as grinding wheels, additional important factors are stability under high heat and bonding characteristics of grain surfaces. The economic factors of cost and availability are always important. No one single property is paramount for any use. For some uses extreme hardness and toughness are needed, as in diamonds for drill bits; for others, the factors of greatest importance are hardness and ability to break down slowly under use, to develop fresh cutting edges when grains become worn-for example: in garnet for sandpaper neither highly cleavable or friable grains nor extremely tough grains are wanted. For still other uses, great hardness is objectionable; for example, abrasives for dentifrices and for glass-cleaning soaps. For the most efficient use in the more critical applications, the different types of abrasives are rarely completely interchangeable; thus, while crushed quartz and garnet are both used in sandpaper, the papers are not at all interchangeable in their use applications. In the last analysis, the choice of a high grade abrasive depends upon the quality and quantity of work done by the abrasive per unit of cost. Initial cost of an artificial abrasive may be much greater than that of a natural abrasive but the artificial abrasive may do so much better work than the natural one, and do it so much faster that the ultimate cost will be less. It is for this reason that artificial abrasives have largely replaced natural abrasives. Abrasive Value Mineralogical hardness or "scratch" hardness as expressed in Mohs&apos; scale is an important property in evaluating abrasive materials, but, as noted before, it is only one of several essential properties. The mineral hardness of pure crystal almandite garnet is about 7.5, but if the crystal is crossed by incipient fracture planes, or if it contains inclusions of other minerals, the apparent or useful hardness may be much lower. While the quartz grains in a sandstone have a hardness of 7, the bond holding the grains together may be so weak that the stone is valueless as a commercial abrasive. In artificially bonded wheels and stones, the hardness, strength, and character of the bond are fully as important as the hardness of the abrasive grains. Thus, in an overall consideration of abrasive hardness of loose abrasive grains, both "scratch" hardness and toughness must be considered. In naturally or artificially bonded abrasive stones, bond characteristics are a third factor, which is most important. The problem of abrasive hardness is further complicated by the inadequacies of methods of testing hardness and of expressing relative values. The Mohs&apos; scale is inadequate both because the methods of testing are very crude and

Jan 1, 1983

By Harry M. Mikami

Chromite is the only ore mineral of metallic chromium and chromium compounds and chemicals. Because of this fact, chromite and chrome ore are used synonymously in trade literature. In commercial market quotations, chrome ore is the term commonly used. Chromite per se, because of properties imparted by its chromium content, is used in refractories and in special purpose molding sands for metal casting. There are many other minerals containing some, generally minor, amounts of chromium, but none are commercial sources of the element (Thayer, 1956). Chromium and chromite have many diverse uses that, directly and indirectly, critically affect vast segments of our modern industrial system. Most important are probably the metallurgical applications wherein chromium is a component of heat-, abrasion-, corrosion-and oxidation-resistant and high-strength alloys of many types. Stainless steels are the largest volume category of chrome-bearing alloys. Chromium chemicals are used in leather tanning, in pigments, dyes and mordants, printing, chemical process industries, photography, pharmaceuticals, metal plating, pure chromium metal production, and for many other purposes. Chromite is a necessary constituent in basic refractories indispensable for the production of steel, copper, cement, and glass. Under present conditions, the US and North America, with the possible exception of Cuba, have no commercial ore reserves. There are chromite deposits, as will be described, but they would be used only under highly abnormal conditions if all outside sources were cut off for an extended period. All chromite used in the US is imported from the eastern hemisphere in which are contained the principal world reserves. The main suppliers in 1980 were the Republic of South Africa (43%), the USSR (21% ), the Philippines (12%), Albania (11 %), Turkey (8%), and others (5%). The strategic nature of chromite is obvious. End Uses-Grades and Specifications As noted before, the three principal uses for chromite are metallurgical, refractories, and chemical with a fourth minor use as foundry molding sand. For metallurgical applications chrome ore is first reduced in electric carbon arc furnaces to various types of ferrochromium alloys. There are high, medium, and low carbon ferrochromiums with carbon ranging from 0.01 up to 10%. Chromium itself ranges from 50 to 73 %. Ferrosilicon chromium and ferrochromium-silicon grades have chromium from 33 to 67% and silicon from 3 to about 48%. Since iron is reduced with chromium, the Cr:Fe ratio of the ore will determine the ultimate grade of the ferrochromium whereas carbon and silicon can be controlled during processing. MgO, A12O3, CaO, and excess SiO2, are removed in slag. A small amount of pure chromium metal is prepared by alumino-thermic and electrolytic processes from essentially iron-free chrome components that have been made via the chemical route. The higher grades of ferrochromium with chromium in the 66 to 73% range can only be made from ores with not only high chromium content, but low iron, i.e., high Cr:Fe ratio. These ores, conventionally termed metallurgical grade, have Cr2O3 contents of 45 to 56% with Cr: Fe ratios of 2.5 to 4.3. A standard composition is generally 48% Cr2O3 and 3:1 Cr:Fe ratio. Very high grade ores are often blended with lower grades even with the high iron chemical grade. For some ferrochromiums, additions of high alumina refractory grade are used as slag conditioners to facilitate smelting while still contributing chromium values. A lower grade ferrochromium, the high carbon charge chrome, has become the predominant grade in use today for making chromium-bearing steel alloys. This

Jan 1, 1983

By Harold V. Pearce

(Chattanooga Meeting, October, 1908.) THE fire which occurred in the fall of 1906, at the works of the Boston & Colorado Smelting Co., Argo, Colo., destroyed entirely the gold- and silver-refinery of the plant; and in view of the development of modern practice in the refining of copper-mattes, etc., the management decided that it would be inadvisable to rebuild that part of the works for the continued use of the process which had been conducted therein for so many years as a metallurgical secret. This decision probably removes altogether from the sphere of practice the " Pearce " method for the separation of gold. At all events, it removes the business reasons which have prevented hitherto the publication of the principles involved. At the suggestion of Dr. Raymond, Secretary of the Institute, my father, Richard Pearce, the former manager of these works, has requested me to prepare a brief description of this process for the benefit of our members. Since I severed my connection with the Boston & Colorado Smelting Co. some time ago, I am indebted for some practical details to the present superintendent, Charles Rees, whose friendly assistance I would gratefully acknowledge. With regard to the history of the inception and development of this process by its inventor, Richard Pearce, I cannot do better than quote freely from his own notes and papers. HISTORY OF THE PEARCE PROCESS.&apos; "In 1874 my entire time was directed to the improvements and additions to the plant at Black Hawk. The changes which I had made in the construction of the furnaces at Black Hawk proved so beneficial that I was requested to introduce the improvements at the branch works at Alma. These changes were carried out as speedily as possible, and proved of great advantage as compared with the old system. "The separation and refining of the gold from the matte now engaged my attention, and since previous experience in the treatment of gold-bearing matte and

Feb 1, 1909

By C. G. Bieber, R. F. Decker

The effects of minor constituents on the malleability of nickel alloys are described. These effects are related to the atomic diameter, valence, and position on the Periodic Table. The basic methods for removal or neutralization of deleterious elements are then reviewed. Finally, practical methods for melting nickel alloys are described in detail and related to minor constituent control. L HE first malleable nickel was produced by Fleit-man in about 1870 by the addition of manganese and magnesium to the molten metal to counteract the harmful effects of sulfur. Merica and Waltenbergl explained the mechanism by which these elements accomplished the desired result. They showed that sulfur in concentrations in excess of about 0.005 pct produced films of a brittle low melting eutectic of nickel-nickel sulfide which completely surrounded the grains. When manganese was added to molten nickel it reacted with the sulfur to form manganese sulfide which precipitated as widely scattered globules in the grain boundaries. The further addition of small amounts of magnesium converted the sulfur to a very stable sulfide of magnesium which was relatively insoluble in both the liauid and solid states and therefore occurred as finely divided particles within the grains where it had relatively little detrimental effect upon the malleability of nickel or its alloys. The practice of treating nickel with manganese and magnesium came to be called "deoxidation" and was employed without appreciable modification for the commercial production of wrought nickel and high nickel alloys (in this paper—50 pct or more nickel) until about 1930 even though the results were never entirely satisfactory. At that time a more extensive study was made of the effects of minor constituents on malleability and metallurgical quality. The results, small portions of which have been published,2-4 are presented here with other pertinent data. EFFECTS OF MINOR CONSTITUENTS UPON NICKEL Systematic additions were made of 0.5 pct or less of each of most of the elements of the periodic ta- ble. It was established in this study that some minor constituents other than manganese and magnesium were extremely influential. The malleability, as evaluated by the reduction of area in tension tests, depended roughly on temperature as shown in Fig. 1. Four temperature zones are of interest; the cold malleable zone (up to about 1000° F), the red short zone from roughly 1000° to 1500&apos; F, the hot malleable zone around 2000° F and the incipient melting zone. Most of the malleability problems are associated with the red short zone and the discussion will concern this mainly. The reduction of area in normal tensile tests on high-purity nickel (see curve A of Fig. 1) appeared to have no

Jan 1, 1962

By Tell Ertl

TODAY&apos;S mining industry is witnessing a transition in labor utilization. The drill-jumbo operator, the mucking-machine operator, the blasting crew, the scaling and timbering crew are all specialists. The all-around miner is rapidly disappearing. As mechanization has resulted in a higher order of underground skills; specialization of labor has been a natural consequence, as has the need for more supervision and engineering. Mines now are cleaner, neater, safer, and have a greater productivity per man-shift than ever before. Nothing spectacular like the continuous miner has yet come to the underground metal mines, but t a gradual improvement in methods, equipment, and technical knowledge is achieving the increased efficiency. With the exhaustion of the rich ores and large profits and who-cares-about-the-costs, mining has become a business; that of producing low value ores at costs below selling price. Charles A. Chase, patriarch of Colorado mountain mining men, manager of the Shenandoah-Dives, was one of the first to preach and prove his preachings that mining is a business. He has been mining a lead-copper-zinc-gold-silver ore, much from elevations above 1.3,000 ft, for a quarter century without a shutdown.-The ore is of such low value that most engineers and investors still would consider it foolhardy. Yet he has kept Silverton, Colo., alive, has paid wages without a lapse, has produced $25 million of new wealth and maintained a steady return to the investors. This type of responsibility is increasingly apparent in the mining business and is one feather that can be worn proudly. .Much emphasis is being placed on improving, the productive mining operations-breaking, loading and transportation. Breaking in underground metal mining is done by drilling and blasting. To the writer&apos;s knowledge, no chain or rotary-type machine has been developed for mining strong, abrasive rock. Drilling Percussion drills are still the standard drilling machines underground. Diamond drills, that: were the rage a decade ago for drilling long holes, are being superseded by the rock drill. The development of the hard abrasion-resistant carbide bit permits full-gage long holes to be drilled by percussion drills at a lower cost than diamonds. The change in the use of percussion drills is chiefly in the method of mounting. The column and arm are disappearing and the jackleg and rubber-tired or track-layer jumbo mountings are taking its place. At the Homestake mine .lightweight jackhammers mounted• on pneumatic legs using 7/8-in. hexagonal drill. rods and 1 1/2-in, tungsten-carbide detachable bits have been found more portable and maneuverable. They have less air consumption, lowered, dynamite consumption, and more footage and tonnage per man-shift than with 3 1/2-in. drifters on a column mounting. Drills now are mounted on longer feed carriages, drilling up to 20 ft without changing steel. These mountings result in great savings because the driller can set up quickly, drill the entire depth of the hole without changing the drill rod or bit using carbide and one-use bits, and can move his machine quickly to the next hole. One man to the machine is becoming general practice. The result is longer rounds rounds drilled at a lower cost than the previously used short rounds. A jumbo developed in the Tri-State can be extended to mine ore left in the roof up to 65 ft above the floor. Drill-rod life was formerly considered to be about 250 min of actual use. The increase in the drilling time per rod per day has gone up considerably with the development of the jumbo and the long-feed carriage, resulting in which is apparently more rod breakage., Consequently, a great deal of research is being done in the attempt to develop an alloy-steel rod with longer service life to offset the greater cost. Some reports indicate that alloy steel or Swedish steel results in cheaper drilling than conventional drill rod. However, several tests have shown only slightly increased life for alloy drill rod. Undoubtedly, the blow of the rock drill, the length of the drill rod, and the resiliency of the rock being drilled are important factors in the life of drill rod, so it follows that alloy steel might work well in some mines and result in no savings in others. The bit forged on the drill rod is seldom encountered and steel detachable bits are not as common as in the recent past. The one-use bit is gaining popularity because of. the difficulty in rehardening reconditioned steel bits satisfactorily. It is thought that the, carbie-insert bit is most applicable to drilling hard &apos;rock&apos; where the steel bit is unable to drill out a full change, for instance, in extremely abrasive

Jan 1, 1952