Search Documents

By Liu Wei-feng

In this paper, the practice of separating precious metals from base metals in gold-antimony alloy by selective chlorination leaching under controlling potential in China has been introduced in detail. The precious metals and the base metals can be separated completely when the complex gold-antimony alloy is treated by this process. The impurity metals were removed effectively since the leaching efficiencies of copper, nickel and antimony are over 99%, with direct recovery of gold being 99.83% that is about 20% higher than that of the original process and silver, antimony, copper and nickel are also recovered effectively. The gold grade of the resulting crude gold powder can reach to 94%.The new process has been applied in the treatment of gold-antimony alloy for two years, and many former procedures have been cancelled, such as electrolysis, Anode slime leaching by nitric acid, smelting in crucible and blowing in muffle. The new process is more shorten, lower cost and friendly to the circumstance comparing to the original process.

Jan 1, 2008

By Jewel A. G. Gomes

Lead has long been an USEPA priority pollutant and an important environmental and health concern because of its toxicity at ppb levels. In light of health and exposure data for lead, the EPA has set standards for Maximum Contaminant Level (MCL) and a MCL Goal (MCLG) as 15 ppb and 0 ppb, respectively. An accurate and rapid measurement of lead in the field remains a technical challenge. In this work, a relatively new method of deploying a nanoband electrode system using anodic stripping voltammetry has been optimized by changing deposition potential, electrolyte, and plating time used for the measurement of Pb(II) in water samples. Green rust has been proven to be an efficient intermediate matrix for removal of lead contaminants. We also report here the removal efficiency of lead using green rust produced by electrocoagulation, both directly and indirectly. Lead containing floc was also characterized through XRD, SEM, and EDAX techniques.

Jan 1, 2008

By William Petruk

An investigation was conducted to determine whether mineral liberation data obtained by one image analysis technique are the same as data obtained by another image analysis technique. The liberated vs non-liberated, volume % and weight % techniques for measuring mineral liberations by image analysis were tested. The results show significant differences between the values obtained by the different techniques. The lowest liberation values were obtained by the liberated vs non-liberated technique and highest by the weight % technique. It is interpreted that the weight % technique produces the most realistic results. The weight % technique also produces data that can define mineral associations for the unliberated grains. These include (1) mineral quantities in particles that contain different amounts of unliberated mineral, (2) mineral quantities in particles that have different size ranges, and (3) mineral quantities and degrees of liberation for specific minerals in particles of different size ranges.

Jan 1, 1996

By M. Y. Mohassab-Ahmed

In an effort to develop a novel flash ironmaking process, the chemistry of selected slags was investigated. In different ironmaking processes, the molten bath (iron-slag bath) is expected to be in contact with gas atmospheres of H2/H2O, CO/CO2/H2/H2O, and CO/CO2. The latter was investigated to allow comparison with the blast-furnace conditions. The slag composition was selected to resemble that of the blast furnace with CaO/SiO2 in the range 0.8 to 1.4. The temperature range was 1550 to 1650°C. The oxygen partial pressure was maintained in the range 10-10 to10-9 atm. The effect of water vapor on the chemistry of the slag as well as the equilibrium reactions involving the slag has been studied for the first time. H2O dramatically affects the chemistry of the slag and strongly affect the phase equilibria in the slag as well as the equilibrium distribution of elements between slag and molten metal.

Jan 1, 2014

By Bin Xu, Qian Li, Yong-bin Yang, Tao Jiang, Jian-jun Hu

It could significantly increase the leaching rate of refractory gold concentrate containing sulfur and arsenic by roasting pretreatment with adding certain amount of sodium sulfate, and the mechanism of that was systematically researched with DSC, XRD and SEM in this paper. Results indicated that the mechanism of Na2SO4 on double refractory gold concentrate at roasting pretreatment can be summed up in the following three aspects：Firstly, Na2SO4 can react with SO2 and SO3 which is produced by the oxidation of sulfides and generate Na2S2O7(l), which plays buffer effect on sulfides exothermic oxidation, avoiding the secondary-encapsulated of gold. Secondly, the liquid phase of Na2S2O7 can cover mineral particles' surface that possesses a sintering effect, it leads to internal cracks of the particles. Finally, mineral particles will gather with sodium sulfate particles as the center that can improve the permeability of the layer.

Jan 1, 2015

By Zhitong Sui

Based on several case studies on the precipitating behavior of valuable nonferrous metal compounds (VNMC) in molten slags a green technology for the recovery of VNMC from molten slags was proposed. This technology involves three steps: (I) The selective enrichment of the dispersed VNMC into the designed mineral phase in the molten slag; (2) The selective coarsening of the designed mineral phase to a critical grain size in the molten slag; (3) The selective separation from tailing of the grown mineral phase in the solidified slag by dressing or hydrometallurgy processes. This is a clean and low cost technique and has a great capacity to deal with a large quantity of slags. The utilization of the recovered VNMC such as Titanium, Boron, Vanadium compounds was summarized as examples of application. It was confirmed by experiments that the precipitating behavior of the designed mineral phases like Perovskite(CaTiO3), Suanite(2MgO*B2O3) and Sincosite(CaOoV2O5*P2O5) in molten slags is obviously affected by operation factors such as temperature, chemical composition, heat-treatment, additives and so on. The precipitating kinetics and mechanism of the VNMC from molten slags during solidification processes were also investigated.

Jan 1, 2003

By J. Méndez-Nonell

The thermodynamic and chemical properties of SrSO4 and SrS in a gaseous flow of CO and CO2 at high temperature are discussed. The thermodynamic analysis of the system was made using data from the literature. The results obtained from the thermodynamic analysis were experimentally verified using the thermogravimetric technique. The experimental results suggest the formation of a complex compound between SrO and SrSO4. It was also found a change in the chemical mechanism of the process between SrSO4 and CO-CO2 and in the chemical mechanism of the process between SrS and pure CO2.

Jan 1, 1995

By Jose Bengoa

Low metal prices and environmental restrictions are always a challenge for copper smelters operation and its productivity. Thus, in order to reduce production costs and control gas emissions, improvements of the Teniente Converter (CT) operation were made at 110 Smelter Plant of Southern Peru Copper Co., 110, Peru, and the main objective was to increase its capacity for smelting copper concentrates without affecting normal operation. The present work corresponds to a recent study conducted during the normal industrial operation of the Teniente Converter in this plant and, it shows the effect of increasing air oxygen enrichment from 28 to 34% on its productivity. The results show an increasing of concentrate smelting rate from 800 to 1370 tpd and hence a notorious improving in copper production, and practically no effect on the refractory consumption. The increment of the concentrate throughput, increases also the SO2 concentration and the sulfuric acid production, showing the effort done by this operation in order to accomplish the environmental Peruvian regulation.

Jan 1, 2003

By J. E. Dutrizac

The mineral forms of silver, lead and cadmium in the zinc concentrates and the various roaster products made by the Kidd Creek Division of Falconbridge Inc. have been elucidated. In the concentrates, all three elements occur mainly in sulphide form, either in solid solution in the principal ore minerals or as discrete mineral grains. During roasting, Ag, Pb and Cd are preferentially concentrated in the hot cyclone and ESP dusts of the roaster train. Silver is converted to <0.5 µm grains of silver metal and to Ag2S04 which dissolves in or impregnates silicates. Lead is converted to Pb-bearing silicates or to PbS04 and PbO which are present either as tiny free grains in ZnO or as an intergrowth with lead silicate. Lead is also a minor constituent of the ferrite phase. Cadmium occurs mostly as cadmium-bearing zno and ZnFe2o4 , but a significant amount also reports as Cd-bearing silicates or zinc sulphate.

Jan 1, 1990

By José D. T. Capocchi

Viscosity of liquid lead, tin, and Pb-Sn alloys has been measured by the rotational viscometer method in the temperature range from 50 K above their respective liquidus temperature to 823 K. The results are accurate to within ±1.0 %. The variation of viscosity with temperature followed the Arrhenius-type equation µ = µo.exp(Q/RT). The composition dependence of the isothermal viscosity and the activation energy for viscous flow have not shown anomalous changes at the eutectic composition of the Pb-Sn system.

Jan 1, 2000

By L. M. Abrantes, A. P. Paiva

"A brief review of some innovative methods for the direct recovery of metals from loaded organic phases is presented; emphasis is given to electroreductive stripping and cementation, which are described and illustrated by examples: of current research. The recovery of silver using a two-phase electrolysis - by direct application of an electrical potential to a mixture of a metal loaded organic phase· containing Cyanex 471X, obtained by solvent extraction, and a stabilized sodium thiosulfate solution - is more extensively discussed. The overall efficiencies are analyzed and compared with data obtained by conventional stripping procedures. Some preliminary results achieved for the recovery of the precious metal using galvanic stripping, applied directly to similar organic solutions and involving zinc and iron powders as reducing agents, are also evaluated.Introductory ReviewThe application of hydrometallurgical methods to the recovery of metal values from ores and concentrates has been receiving a growing interest, either from researchers or from the mining industry [1].For the concentration / purification of the relatively low concentrated metallic solutions resulting from the leaching of those raw materials, solvent extraction (SX) is a well established technique [2]; the loaded organic solvent is then conventionally contacted with a suitable aqueous solution, the metal in its final form being usually recovered from this solution by electrowinning.As an efficient and / or selective stripping is sometimes difficult to achieve, depending on the specific characteristics of the system under consideration, some alternative procedures have been analyzed in order to overcome this problem. One of the chosen routes, mainly developed by Hirai and Komasawa, is to promote the reduction of the desired metal species in the organic phase, in such a way that the stripping stage becomes feasible; for the selective stripping of vanadium from a solvent containing a mixture of vanadium and molybdenum, the authors successfully used reductive [3], electro-reductive [4,5] and photo-reductive [6] techniques. The two latter methodologies have also been applied to the recovery of europium from a solvent containing europium, samarium and gadolinium [7,8].However, further processing is necessary to recover the metal in its solid state; therefore, methods causing the direct reduction of the metal species in the organic phase to their fmal metallic form would be of interest, as an intermediate step would be avoided"

Jan 1, 1997

By B. C. Jena

Activities of carbon, cobalt and nickel were evaluated in the ternary systems iron-carbon-cobalt and iron-carbon-nickel for the temperature range 1300-1600°C for cobalt and 1300-1700°C for nickel. The carbon activities were determined from the knowledge of activities (1) in the binary system iron-carbon, (2) in the dilute ternary systems and (3) from the knowledge of carbon saturation data. The activities were mathematically expressed with the Taylor series expansion of Wagner&apos;s interaction parameter formalism modified to suit concentrated solutions. The cobalt and nickel activities were determined from the knowledge of carbon activities by applying the Gibbs-Schuhmann integration and from cobalt and nickel activities in the binary systems iron-cobalt and iron-nickel. Partial molar enthalpies of mixing were determined based on the temperature behaviour of the activity coefficients.

Jan 1, 1992

By N. Menad

The formation of the dioxins can be dependent on the quantities of carbon, hydrogen, chlorine and oxygen present in a given system, as well as on parameters such as temperature and pressure. Inadequate supply of combustion air ( incomplete oxidation ), low combustion temperatures ( incomplete combustion ), and insufficient turbulence in the combustion are factors which can favour their formation. Dioxins were produced also calatytically from chlorinated phenol precursors, non-chlorinated compounds that were chemically, and reaction of phenol with inorganic chloride. In this paper different precursors such as combination of C, H, 0, Cl, rapid formation/combustion intermediates and routes to PCDFs are reviewed, and the influence of PVC amount on the formation of these isomers is discussed.

Jan 1, 2000

By Sergio N. Monteiro

The interface between the matrix and the reinforcing fiber plays an important role in the efficiency by which an applied load is transmitted through the composite structure. The shear stress at the fiber/matrix interface can be associated with this load transference and,consequently,affects the composite strength. In the present work, pullout tests were used to evaluate the interfacial shear stress of curaua fiber in epoxy matrix composites. A small critical length was found for the curaua fiber embedded in epoxy, which corresponds to a relatively weak fiber/matrix bond and lower interfacial strength.

Jan 1, 2009

By T. Fujita

The removal of phosphorus is essential 1n order to increase the recycling of steelmaking slags for their manganese, iron and lime contents. This study aims at establishing the phosphorus mineralogy and its distribution in steelmaking slags, the effect of slow cooling, and the methods of phosphorus removal. A series of steelmaking slag samples was prepared at different cooling rates, and the mineralogy, chemistry and grain size of the samples were investigated with SEM/EDS and x-ray diffraction. The test results using high gradient magnetic separation are discussed.

Jan 1, 1988

By Tianzu Yang, Weifeng Liu, Lin Chen, Qingkai Xiao, DUCHAO ZHANG

To solve the problem of low leaching ratio of direct gold cyanide leaching from arsenical refractory gold concentrate, this paper proposed a matte smelting process for gold enrichment in low grade copper matte. The effects of copper content in the mixed material, ratio change in slag type, smelting temperature and reaction time on recovery rate of gold and copper were investigated. The experimental results indicated that the recovery rate of gold increased with the increase of copper content in the mixed materials, temperature and reaction time. It was also noted that the recovery rate of gold and copper were respectively 98.16% and 96.39% when the addition of copper content in the mixed material was 3%, slag type of CaO/SiO2 and FeO/SiO2 were 0.6 and 0.9 in 1250°C and the time of reaction was 40min. Most of the arsenic was oxidized into As2O3 existed in the dust. The results showed that the matte smelting method can achieve efficient recovery of gold from arsenical refractory gold concentrate.

Jan 1, 2016

By A. McLean, Y. Uchida, M. Iwase, M. Myochin, K. Wiikimoto

"Phase diagrams of FeO-containing ternary systems could be derived from experimental data for the activities of FeO. The systems investigated are CaO-CaF2-FeO, SrO-SrF2-FeO; BaO-BaF2-FeO, CaO-CaCl2-FeO, SrO-SrC12-FeO, BaO-BaC12-FeO, CaO-A12O3-FeO and BaO-SiO2-FeO.IntroductionThe importance of phase diagram cannot be overemphasized. In a book, ""Alloy Phase Equilibria""[l], the author, Professor A Prince, states, ""A metallurgist has been defined as a person who thinks in terms of phase diagram"". Whether one accepts this statement or not, it is self-evident that an ability to interpret phase equilibria is essential to the professional metallurgists.The physical chemistry studies of iron and steelmaking process often require phase diagrams of FeO-containing slags. Iso-thermal section of the phase· diagrams of such systems can be derived from experimental data for chemical potentials of FeO. Due to the recent developments in the area of solid state electrochemistry, rapid determinations of the FeO activities have become possible. The present paper is aimed at documenting the derivation of the phase diagrams of FeO containing slags.Experimental AspectsAn electrochemical method incorporating stabilized zirconia can be used for the measurements of the activities of FeO in various slags and fluxes[2]. For the details of the experimental technique, reference should be made to reference 2"

Jan 1, 2000

By R. G. Reddy

Viscosities of alkaline metal oxide-silicate melts were estimated using our previously developed mathematical model. The structural based model considers depolymerization effects and related breakdown of the silicate network structure, on the addition of metal oxides to the melt. The developed expression: n =4.9x10 9 NO 0 T ½ exp(E/RT) poise was used to calculate the viscosities of various binary silicate systems such as, CaO-SiO,, MgO-SiO, and MnO-SiO,, as a function of temperature and composition. Excellent agreement was obtained between the calculated and experimentally determined viscosities.

Jan 1, 1991

By Zhi-xiang Cui

Dongying Fangyuan Nonferrous Metals Co., Ltd. has developed a new technology to produce anode copper from concentrates through only two furnaces. This new technology is called the Two-Step Copper Smelting Process. This paper presents the commercial application of the Two-Step Copper Smelting Process and its operating conditions. The key features of the Fangyuan Two-Step Process are as follows: (1) feed materials, including concentrates and flux, are mixed without pretreatment and fed into the Submerged Lance Smelting (SLS) furnace; (2) high grade white metal (WM) produced by the SLS furnace is transferred via WM conduit into one of the two Submerged Lance Converting and Refining (SLCR) furnaces; and (3) the two SLCR furnaces blow alternatively to maintain continuous operation of the whole production chain. The new smelter started operation in October 2015 with a processing design capacity of 1.75 Mt/year of mixed feed and has been operating for over 30 months.

By Mansoor Barati

The present paper is based on a term project for final year undergraduate students, requiring them to evaluate a process for producing silicon from rice husk. The traditional method for production of silicon involves carbothermal reduction of quartz in electric arc furnaces at temperatures exceeding 2000 °C. The technology consumes a considerable amount of electrical energy as well as fossil fuels, resulting in significant CO2 emissions. A flowsheet for production of silicon metal from rice husk is laid out in this paper. The technology will consist of combustors, which will generate steam using the rice husk biomass, power generator, and electric furnace for reduction of the rice husk. Materials and energy balance calculations presented here indicate that such process can be operated independent of external electricity.

Jan 1, 2014