By Zhihao Yue, Honglie Shen, Yahui Teng, Ye Jiang

"In this paper, manganous nitrate [Mn(NO3)z] was used to assist the etching of silicon wafer in hydrofluoric acid (HF) for the antireflective application, and alumina (Al2O3) layer was deposited on the surface of the etched sample by atomic layer deposition method for further antireflection. The surface morphological and compositional studies of these samples were performed by scanning electron microscopy attached with an energy-dispersive X-ray spectrometer. The surface reflectance measurements were carried out using UV-Vis-NIR spectrophotometer. Binary structures of pyramids and nanopores were obtained by etching the alkaline textured monocrystalline silicon wafer in HF and Mn(NO3)z mixed solution for not more than 15 min. But excessive increase of etching time of up to 30 min resulted in the whole destruction of pyramids. The average reflectances of the 5-min-etched sample before and after being coated with 75-nm-thick Al2O3 layer are 4.62% and 3.47% in the range of 200-1000 nm, respectively.1. IntroductionAs we know, the reflectance of silicon wafer after being sliced is so high that the maximal photoelectric conversion efficiency of silicon based solar cells is limited. Therefore, alkaline texturization process was used for silicon solar cell in industrial production. But the reflectance of this alkaline textured wafer is still greater than 10% and this process can only be used for monocrystalline silicon solar cell."

Jan 1, 2013

By Wiraseranee. Chompunoot, Kazuki Morita, Toru H. Okabe

"Aiming at the development of more effective recycling processes, dissolution behavior of rhodium into molten slag was investigated. Using a pure rhodium crucible and Na2O-SiO2 slag system, equilibration experiments were carried out for 18 h at 1423-1623 K under various oxygen partial pressures of 0.005-1 atm with varied slag basicity. Rhodium solubility increased with increasing oxygen potential, slag basicity, and temperature. Rhodium dissolved into slag as rhodate ion ([RhO2]-) by the endothermic reaction: Rh(s) + 3/4O2(g) + 1/2O2-(in slag) = [RhO2]-(in slag). In the dissolution reaction, the “rhodate capacity” of slag is newly-defined. The correlation between rhodate capacity and optical basicity is reported.IntroductionDue to its high chemical resistance and outstanding catalytic properties, rhodium (Rh), one of the platinum group metals (PGMs), is utilized in various applications such as catalysts, molten glass vessels and containers, and electronic devices. Owing to the rarity of Rh resources in nature, recycled Rh from scraps such as spent automobile catalytic converters is currently considered as an important source of Rh supply [1]. According to the recycling practices, Rh is currently mainly recovered from scraps along with other PGMs such as platinum (Pt) and palladium (Pd) by a dry process (e.g., smelting), a wet process (e.g., leaching and subsequent separation of PGMs from aqueous solution), or a combination of both processes [2]-[4]. Among these processes, smelting is commonly applied because PGMs can be effectively separated from a relatively large amount of various impurities coexisting in scraps. In the smelting process, Rh and other PGMs are collected in the collector metal (e.g., iron and copper), and impurities in scraps are removed into slag [4]-[6]. The process may be carried out at a temperature range of 1573-1973 K, in either an oxidizing or reducing atmosphere. Due to the high oxidation resistance at high temperatures, Rh is expected to be collected efficiently in the metal collector rather than being oxidized and forming RhOx in a molten slag. However, Rh loss into slag does occur in this process [7]."

Jan 1, 2011

By Guangshi Li, Xionggang Lu, Xueliang Xie, Xingli Zou, Yuyang Bian, Hongwei Cheng, Kai Zheng, Changyuan Lu

The corrosion resistance and corroded microstructure of MgO-C refractory in molten slag are investigated by immersion test in muffle furnace at 1600 °C . The microstructure and chemical compositions of the specimens after erosion experiment are characterized by scanning electron microscope (SEM) and energy dispersive X-ray (EDX). The results confirm that the oxidation of graphite is the most important degradation mode of MgO-C refractory. The structure of the refractory material is damaged due to the decrease of graphite, as a result, the periclase substrate reacts with the molten slag directly. The corrosion process is controlled by the dissolution of the refractory materials into slag, low melting point oxides are therefore generated which lead to the damage of MgO-C refractory finally.

Jan 1, 2015

By Jian Li, Guo Chen, Bingguo Liu, Hongying Xia, Jinhui Peng, Libo Zhang

"Decomposition of ammonium tetramolybdate to prepare Mo03 using silicon carbide crucible in microwave fields was investigated. The results were analyzed Using TG-DTG and X-ray diffraction. Meanwhile, the effects of heating rat, material thickness, socking time, socking temperature on the structure of preparing Mo03 were studied. TG-DTG curves show that the decomposition process of ammonium tetramolybdate is only one stage, in the temperature range 300-350°C, whose begin to decompose when temperature increases beyond 300°C. The molybdenum trioxide was prepared by thermal decomposition. The quality ofMo03 was not affected under the heating rat is 12°C/min. It was beneficial for decomposition ratio with the lower material thickness, longer soaking time, and higher soaking temperature. XRD curves showed that it is viable method for preparation of Mo03 by decomposition from ammonium tetramolybdate in microwave fields.IntroductionMolybdenum is widely used in national defense, aviation, industrial and agricultural production as rare refractory metal. Molybdenum trioxide is vital raw materials for the process of preparation of molybdenum. The traditional production technology of molybdenum oxide is that ammonium tetramolybdate is calcined in rotary kiln or 4-tube furnace [J,2J. But the longer production time, the higher production cost, the lower furnace thermal efficiency, and bigger the energy consumption, especially the powder is easy to leak, the working environment is poor by using rotary kiln [ 3 l _ The particle of molybdenum oxide is non-uniform by using 4-tube furnace because of the uneven temperature of every tube and the poor exhaust of boat bottom [4l _ However microwave heating is quick and uniformity, it is a meaningful research that the microwave is used in the process of calcining ammonium tetramolybdate."

Jan 1, 2013

By Chao Li, Qian Li, Yong-bin Yang, Kai Li, Qiang Xie, Yuan-yuan Zhu, Dong-ye Li, Qi-bing Tan

"The permeability of sintering mix is a vital technological property in sintering process. However, it can only be measured by off-line method on samples picked from the production. In order to acquire the properties of sintering mix accurately, on-line measuring of permeability is urgently required. Based on the reflection characteristics of bed permeability on pipe flowing parameters, a new method is presented in this paper for on-line measuring of sintering mix permeability. The measurement can be performed by blowing gas flow in the bed with the measuring pipe. Measuring results are obtained by picking the data on flowing rate and pressure in the pipe. The function of flowing rate to pressure may be certain for samples with the same permeability. Thus, the permeability was determined by contrasting this function to the result of off-line measuring, and the relative coefficient or R2 value was more than 99%.IntroductionThe permeability of sintering mix is a vital technological property in sintering process, which directly determines production and quality of sinter, or even determines whether the sinter production is carried out smoothly [1,3].The permeability have more obvious influence on vertical sintering speed, which is mainly related to air quantity passing through material bed. Under certain inducing capacity and negative pressure, the vertical sintering speed mainly depends on the permeability of sintering mix. Low permeability may make burning through point of sintering move back, and the sinter mix cannot be burnt through. High permeability may make burning through point of sintering move forward, improving production efficiency by increasing the speed of sintering machine [4] Good permeability means a small resistance of fan ,reduction of negative pressure of sintering machine, and full contact between air and sulfide, which can strengthen physical-chemical reaction during sintering process and increase desulphurization rate. In gas well through material layer process, gas-solid desulfurization reaction and gas-solid-liquid heat exchange are completed and hot gas through the combustion zone supplies the sintering process with heat. Finally uniform sintering of the material layer in height and width direction is achieved [5] While high permeability index leads to weak sinter strength, fast sintering speed, short residence time of high temperature region and little liquid phase. Moreover, liquid phase in the fast cooling process is too late to fully crystallize but forming glass phase which is harmful to sinter strength as well. Bad permeability means a big fan resistance and increase of negative pressure of sintering machine, which make the air pass through material layer difficultly. When air and mix contact difficultly, removal of sulfide reduces so that desulfurization is incomplete. Meanwhile, low caking efficiency, slow sintering speed and easily burnt sinter , reduce sinter output. Therefore appropriate permeability of sintering mix is the premise of stable burning through point and satisfactory sinter output and quality."

Jan 1, 2013

By Edmundo Manilla, Merete Tangstad, Daniel Davila, Eli Ringdalen

FeMn alloys are typically produced with lumpy ore or sinters. Minara Autlan, the Mexican FeMn producer, is however making Mn-nodules as a raw material for Mn-alloy production. The Mn nodules have been characterized by XRF, XRD, by wet chemical methods and by EPMA. The Mn/Fe ratio is somewhat lower compared to commercial Mn ore on the marked. The basicity of the ore is however close to 1, and additional fluxes may not be used. The Mn-nodules will be in a state of manganosite (MnO), tephroite ((Mn, Ca)2SiO4) and galaxite ((Mn,Mg)Al2O4). This leads to a low melting temperature area. A low porosity and low amount of higher Mn-oxides gives a high thermal strength to the nodules.

Jan 1, 2016

By C. D. Mishra

The recycling potential for any gainful utilisation of the waste products is dictated by their quality, especially the chemical characterisation. The methods commonly used for the analysis of fly ash e.g. wet chemical, AAS, ICP-AES etc are time consuming. The paper describes a rapid XRF-based method for routine analysis of fly ash which involves preparation of local standards, optimisation of sample preparation technique and use of a simple PC-based software to account for interelement effects. The matrix corrected values are found to agree well with the wet chemical data.

Jan 1, 1992

By José Luiz Rodrigues Bravo

The production of electrolytic copper with assured quality corresponding to international standards, in a conventional electrorefkery of a custom smelter, is a hard and cautious task, if no advanced technologies for selective control of electrolyte impurities are available. The improper control of the amount of As , Sb and Bi in the anode that enter the tankhouse , attributable either to a bad schedule of concentrate input or to the unavailability of clean concentrates in the international market , as well as the lack of means to maintain the suitable level of these elements in the electrolyte together with other operational circumstances, can result in off-grade copper, as well as affect the starting sheet chemically and physically. This paper presents in a practical way the relationship between the operational conditions and the cathode and starting sheet quality produced at CMSA, covering the period of the last five years of operation, discusses the technologies available in the market for antimony and bismuth removal and compare the results of testwork, achieved in the laboratories of CMSA, using two resins not associated with patented technologies.

Jan 1, 1997

By Hans Jürgen Maier, Hans-Bernward Besserer, Gregory Gerstein, Florian Nürnberger

The formation and development of voids in both the single-phase ferritic steel DC04 and the dual-phase ferritic-martensitic steel DP600 are discussed. Various mechanisms and kinetics of void formation are considered regarding the influence of dislocation glide, precipitates and other parameters. Different characteristic locations in the microstructure are investigated at which strain concentrations during plastic deformation can occur and cause the formation of voids and microcracks. For the specimen preparation ion slope cutting is applied. Voids and cracks revealing ductile damage are analyzed by Scanning Electron Microscopy (SEM). Stress concentrations in consequence of plastic deformation could be shown by extinction contours on images recorded by Transmission Electron Microscopy (TEM).

Jan 1, 2015

By Bo Jiang, Jiusan Xiao, Hongmin Zhu, Kai Huang, Shuqiang Jiao

Carbothermal selective reduction of simulative titanium slag and various titanium raw materials were presented and SiO2 was found to be partially reduced, forming a series of Fe-Si alloys during the process. Thermodynamic analysis of the selective reduction between TiO2 and SiO2 was performed using HSC 6.0 software, then a series of equilibrium experiments were designed and presented. The activity of Si reduced from SiO2 was affected by the presence of Fe reduced from FeOx and the generation of Fe-Si alloys, promoting the reduction of SiO2 in the whole process. The results of experiment are in great accordance with the calculated data obtained from thermodynamic analysis.

Jan 1, 2016

By Garg. D.

Premixed bronze powders are widely used to produce a wide variety of P/M components including bearings and bushings by the powder metal industry. The physical and mechanical properties of sintered bronze components such as dimensions, strength, microstructural characteristics, and sintered density are well known to change with sinlering furnace design, particle size distribution in powders, green density, preheating and sinlering time" and temperature, and protective atmosphere flow rate. " However, not much is known about the effect of protective atmosphere composition on physical and mechanical properties of sintered bronze components; This paper describes effects of protective atmosphere composition and sintering temperature on physical and mechanical properties of sintered bronze components

Jan 1, 1996

By Osamu Iida

Since 'start-up of the larger Mitsubishi Continuous Copper Smelting Process in 1991, furnace relining campaign was gradually prolonged to once every 2 years according to deregulation of governmental boiler inspection. On the other hand, in 1998 Naoshima smelter embarked on an intermediate strategic expansion plan to strengthell its international competitiveness. As part of this plan, modifications were implemented in the copper smelter designed to increase output of anodes from new charge source to 270,000 tpa. In May 1998, treatment of dried neutralized residue was started in C furnace, and during the shutdown for brick relining in April 1999, intensive modifications to the boilers as well as the installation of new spray coolers for furnace off gas treatment were implemented. Finally, the new larger oxygen plant was commenced its operation in May 2000 and the expansion was achieved around 30% increase of anode production from original design.

Jan 1, 2001

By Xiang-dong XING, Zhen-yang wang, Jian-Liang Zhang

Distribution behavior of titanium between CaO-SiO2-MgO-Al2O3-TiO2 and hot metal was studied between 1350 °C to 1600 °C. Experimental results indicate that the reaction temperature influenced the activity coefficients of titanium and resulted in the variation of equilibrium constant. Finally, the Gibbs free energy formula of titanium carbothermic reduction was fit out using the thermodynamic model of Wagner and congregated electron phase models.

Jan 1, 2015

By Lori Bassman, Cassandra George, Cullen McMahon, Md. Zakaria Quadir, Michael Ferry

"Complete and accurate analysis of subgrain microstructural features must include three-dimensional information. Three-dimensional electron backscatter diffraction (EBSD) data can be used to characterize these features; however their boundaries first must be determined. This cannot be accomplished simply with pixel-to-pixel misorientation thresholding because many of the boundaries are gradual transitions in crystallographic orientation. Fast Multiscale Clustering (FMC) is an established image processing technique that we have combined with quaternion representation of orientation to segment this kind of data. Segmentation algorithms often have issues handling images with both distinct and subtle boundaries. Our implementation of FMC addresses this by using a novel distance function and statistical analysis to take into account the variance in orientation of each feature. Although FMC was originally a twodimensional image processing algorithm it can be generalized to analyze threedimensional data sets. As an example, a segmentation of microbands in cold-rolled aluminum is presented.IntroductionThree-dimensional electron backscatter diffraction (3D-EBSD) is a method for mapping the local crystallographic orientations of points in a volume. The technique uses a dual beam platform consisting of a focused ion beam (FIB) and SEM with EBSD, where FIB is used for serial sectioning and EBSD for orientation mapping of 2D slices. These 2D slices may then be stacked to create a 3D volumetric data set.Typical uses of such a data set include characterizing the geometries and crystallographic orientations of surfaces between structures in 3D [1-5]. This involves identifying boundaries accurately, either in 2D slices with subsequent 3D reconstruction (as illustrated in Figure 1) or in the 3D data set. All such data sets present the challenges of i) aligning data slices to correct for instrument drift, ii) identifying relevant boundaries, and iii) implementing appropriate smoothing or interpolation algorithms. The focus of this paper is boundary identification."

Jan 1, 2011

By Qian Xu, Guangshi Li, Xionggang Lu, Xingli Zou, Hongwei Cheng, Cong Xu, Changyuan Lu

The roasting of nickel-bearing sulfides is a complex but important process which has not been adequately characterized. Combination of X-ray diffraction and scanning electron microscopy has been proved to be useful for such experiments. The leaching results of nickel, copper, iron and cobalt was analyzed by ICP methods. Process possibility of polymetallic sulfide concentrates through a three-step procedure (oxidation roasting - chlorination - water leaching) was suggested. Ammonium chloride could react with nickel/copper oxides to produce intermediate complexes. At the temperature range of 280~340 oC, these complexes further decomposed to the corresponding simple chlorides. Roasting sulfide concentrate using NH4Cl is effective for complex ores.

Jan 1, 2016

By K. Yamaguchi, Y. Takeda

"Partial pressure - temperature - composition correlation diagrams of the Ga-As, In-As, Ga-P and In-P systems were contracted based on the obtained experimental data of the phase diagram and thermodynamic properties for the III-V systems. The total vapor pressures of arsenic or phosphorus at melting point of GaAs, InAs, GaP and InP were determined as 101, 10.1, 1510 and 253 kPa, respectively, at the corresponding melting points of 1509, 1211, 1739 and. 1336K , These diagrams are applied to the analysis of the horizontal Bridgman method and the liquid phase epitaxial growth technique. On the other hand, the analysis of the equilibrium state of the. chloride-CVD process was carried out using the data of the Gibbs energy of the compounds obtained by· authors.IntroductionThe group III-V compound semiconductors ate important materials used in optoelectronic liquid high speed electronic device. The crystal growth of the III-V compounds can involve processes that require contact between the solid, liquid and vapour phases at near equilibrium condition. Examples of processes that involve contact between the solid, liquid and vapour phases include bulk crystal growth such as the horizontal Bridgman and the liquid encapsulated Czochralski method and liquid epitaxy, and between the solid and vapor include chemical vapour deposition and molecular beam epitaxy. Therefore, the knowledge of the phase diagram and thermodynamic properties for the III-V binary alloys is essential for the analyses of crystal growth techniques of III-V compounds.For these reasons, a series of different · types calorimetric measurements had been carried out: (1) The heat contents of alloys for the Ga-As, In-As, Ga-P and In-P systems by a drop calorimeter [1;2,3]; (2) the heats of formation of the GaAs, InAs, GaP and InP compounds by a twin solution calorimeter [4]; and (3) the standard entropy of these compounds by an adiabatic calorimeter [5]. Based on the third law method, the Gibbs energies of these compounds were derived from the heat capacity, standard heat of formation and standard entropy data obtained by authors. Integral molar thermodynamic quantities of the liquid III-V .alloys were also determined from combining the heat contents of alloys with standard heat of formation and standard entropy data of the compounds· by applying the thermodynamic analysis method developed by Oelsen [6]. In the present study, the thermodynamic calculations for the crystal growth processes of the III-V compound were carried out using newly experimental data of the phase diagram and thermodynamic .properties measured by authors"

Jan 1, 2000

By K. Sanjay

Factorial optimisation technique has been used to develop regression equations at different time intervals for extraction of manganese from precipitated manganese oxide/hydroxide in sulphuric acid using charcoal as the reductant. The three parameters chosen for a 23 full factorial design were : acid concentration, amount of carbon and temperature. The regression equations were used to predict >> 90% extractions as well as kinetic data.

Jan 1, 1996

A study was undertaken to remove the Se from waste solutions using a raw form of the biomass called Iota Chips derived from the seaweed, Eucheuma spinosum. Removal of Se from solutions was investigated as a function of time, pH, conc. of Se in solution (0.1 to 100 ppm) and lota Chips to liquid ratios of 10-2 to 10-5. For solutions containing initial conc. of 0.1 ppm Se, with the addition of Iota Chips at a solid to liquid ratio of 10-3, the Se conc. decreased to 0.03 ppm in about 3 hours. Iota Chips absorption capacity to the Se and its application to the treatment of the metallurgical processing effluents are discussed.

Jan 1, 1992

By C. M. F. Vieira

The main characteristics and physical and mechanical properties of clays from the county of Campos dos Goytacazes, located at the northern part of the State of Rio de Janeiro, Brazil, are presented. The characterization included mineralogical composition, chemical composition and particle size distribution. The properties related to water absorption, linear shrinkage and flexural rupture strength were obtained in samples that were prepared by 20 MPa uniaxial pressing and fired at 950 and 1100oC. The results showed that the clays are predominantly kaolinitic with high percentage of clay minerals. The kaolinitic structure associated with a small amount of fluxes confers a refractory behavior which makes difficult the sinterization and impairs the ceramic consolidation.

Jan 1, 2009

By Itsuki Uehara, Hiroyuki T. Takeshita, Tetsuo Sakai, Nobuhiro Kuriyama, Hideaki Tanaka

"AB5 type hydrogen storage alloys (A: rare earths, B: transition metals) are extensively applied to a negative electrode of a nickel metal hydride (Ni-MH) rechargeable battery for portable electric equipments, electric vehicles, hybrid vehicles etc. Performance of a hydrogen storage alloy electrode is affected by various factors, microstructure and surface composition of the alloy and structure of the electrode as well as composition of the alloy. Control of those factors enables us to commercialize the Ni-MH battery in various field.IntroductionA Nickel-metal hydride (Ni-MH) battery has been extensively developed because of (1) good compatibility with a nickel cadmium (Ni-Cd) battery, (2) high energy density (1.5-2 times higher per unit volume than a Ni-Cd battery) and high dischargeability, and (3) low environmental pollution. The charge/ discharge reactions can be written as [l, 2,3]:(+) Ni(OH)2+OH- = NiOOH+H2O+e· (E=+0.490V NHE),(-) l/6LaNi5+H2O+e-· = 1/6LaNi5H6+OH- (E=-0.828V NHE),where E° is a standard potential of an electrode vs. normal hydrogen electrode (NHE). Because of the above advantages of a Ni-MH battery, the battery have been widely used as a power source of portable computers, cellular phones, electric vehicles (Toyota ""LAV4L EV"", Honda ""EV Plus"" etc.) etc. Some hybride vehicles (Toyota ""Prius"" and Honda ""INSIGHT"") and fuel cell vhehicles (Toyota ""FCEV"") are power-assisted by a high-power Ni-MH battery. In 1999, the production of Ni-MH batteries reached 870 million cells in Japan. Most of commercialized NiMH batteries are incorporated with rare-earth-based AB5-type hydrogen storage alloy as a negative_ electrode. The production of rare-earth-based alloy is estimated to be approximately 8000 tons.The battery performances of the Ni-MH battery, for example, capacity, durability (cycle life), dischargeability (kinetics) and selfdischarge, ate closely related to the metal hydride· (MH) electrode, especially, the hydrogen storage alloy in the electrode. Substitution of alloy components, heat treatment, and surface treatment in order to change surface and bulk structure of hydrogen storage alloys have been examined by us and many reseachers in order to improve the performances of MH electrodes. This paper is a review of our and their efforts to improve performances of MH electrodes."

Jan 1, 2000