Search Documents

By S. Frederick Ravitz

FOUR liquids are ordinarily present in the lead blast furnace during lead smelting. At the bottom is the lead bullion, which is metallic lead containing about one per cent of impurities, including gold, silver, copper, bismuth, arsenic and antimony. Above this is the speiss, which consists essentially of arsenides and antimonides of iron and copper. The speiss is followed by the matte, which consists principally of sulfides of iron, copper and lead1. The top layer is the slag, of which the major constit-uents are silica, lime, alumina, zinc oxide and iron oxide. Similar products are obtained from the dross furnace, which treats the dross obtained in decopperizing lead bullion. The distribution of gold and silver among these various products is of considerable importance in the smelting of lead. In general, the matte and speiss cannot be treated in the lead smelter, and usually are sent to a copper smelter. It is usually desirable, therefore, to keep their gold and silver contents as low as possible, and to collect the precious metals in the bullion. If the bullion, speiss, matte and slag exist together in equilibrium, the gold and silver should distribute themselves among these four liquids in a definite manner, which, other conditions being equal, should depend only on the amounts of gold and silver in the charge to the furnace. It is thus apparent that a knowledge of whether such equi-librium exists is necessary before attempting to study the effects of various compositions of matte and speiss on the distribution of gold and silver among the furnace products2. Moreover, systems consisting of four liquids in equilibrium are very rare, and are of considerable scientific interest.

Jan 1, 1936

By R. K. Waring

A KNOWLEDGE of the mutual liquid solubility of zinc and lead is of importance in various phases of zinc metallurgy. The determination of this solubility has been the subject of numerous investigations, but unfortunatel, the results vary widely, particularly at higher tempera-tures, and it has been impossible to decide what data are most reliable. It was decided to investigate the matter and in view of the disagreement in the published results, it was felt necessary to take rather unusual precautions to insure the reliability of the data. For this reason deter-minations were made by four different methods, and the procedures of several of the previous investigators were duplicated. The previously used methods can be divided into two classes: methods involving freezing the entire melt and taking samples of the lead-rich and zinc-rich phases in the solid state, 1,2 and methods in which the. samples are taken while the bath is liquid and at the desired temperature. 3,4 Data obtained by methods involving freezing the entire melt show much lower solubility of lead in zinc than methods in which the liquid is sampled at temperature. The latter method was used by Spring and Romanoff5 and by Hass and Jellinek.6 The results of these two investi-gations are in agreement at temperatures near the melting point but at higher temperatures Hass and Jellinek find a higher mutual solubility.

Jan 1, 1934

By L. S. Darken, H. A. Wriedt

The equilibria at 1 atm total pressure and 600° to 1300°C (1112° to 2372°F) between gas mixtures with various partial pressures of the reactive constituents (principally sulfur dioxide, carbon dioxide, water vapor, oxygen or carbon monoxide, and hydrogen) and coexisting solid phases (groups variously including calcium oxide, calcium carbonate, calcium sulfide, calcium sulfate, iron, ferrous sulfide, and the iron oxides) are examined. Tables and charts show the combinations of temperature, oxygen activity, and carbon dioxide partial pressure under which the various groups of the solid phases coexist and the corresponding sulfur dioxide pressures. In the presence of calcium sulfide, calcium sulfate, and calcium oxide, the partial pressure of sulfur dioxide has a peak value at each temperature which increases from 101 atm at about 800°C (1472°F) to 1 atm at about 1200°C (2192°F). With water vapor present, hydrogen sulfide may predominate among gaseous sulfur compounds, particularly at low temperatures and oxygen activities; under all other circumstances considered, sulfur dioxide is the dominant gaseous sulfur-bearing species.

Jan 1, 1974

By E. H. Jr. Dix

THE use of magnesium as an alloying element in aluminum alloys has been limited, in general, to comparatively small quantities. In duralumin-type, strong-aluminum alloys, magnesium is present to the extent of ½ to ¾ per cent. and various grades of Magnalite and the "Y" alloy of the National Physical Laboratory of England contain up to 1 1/2 per cent. In this country small quantities of aluminum alloy sheet containing 4 per cent. magnesium are produced commercially. All commercial aluminum contains sufficient silicon to convert a portion of the magnesium added to the compound Mg2Si. It is well known that the solubility of both magnesium and magnesium-silicide decrease with decrease in temperature. It is, therefore, impossible to separate the age-hardening effect of the magnesium-silicide from that of magnesium, except by the use of aluminum of such high purity that the silicon content is negligible. The present paper is the fifth1, 2,3,4 of a series from the laboratories of the Aluminum Co. of America reporting the results of investigations of the equilibrium relations in aluminum-rich alloys made from the high purity aluminum manufactured by this company .5

Jan 1, 1929

By E. H. Jr. Dix

THE consideration of alloying elements for aluminum has led to a series of investigations of the equilibrium relations between aluminum and those alloying elements. Therefore, the aluminum end of the aluminum-antimony diagram has been studied. The general form of the aluminum-antimony equilibrium diagram has been worked out by Campbell and Mathews1 and by Tammann.2 Campbell and Mathews described principally the beginning of solidification. They found the curve of beginning of solidification to rise gradually from the melting point of pure aluminum to a maximum at about 67 per cent. aluminum. After a slight lowering of the curve at a little greater antimony concentration the curve again rises to a maximum at 18.4 per cent. aluminum, which corresponds to the compound AlSb. The curve then drops to the melting point of pure antimony. Tammann explained the maximum occurring at about 67 per cent. aluminum as the result of the slow formation of the single compound AlSb. The space lattice of the compound AlSb, according to Owen and Preston,3 is face-centered cubic, the antimony atoms being intermeshed with an identical aluminum lattice. Very little, if any, work has been done on aluminum alloys containing small amounts of antimony.

Jan 1, 1930

By William Fink

THE constitution of the aluminum-cobalt alloys has been the subject of relatively few investigations. Brunck1 analyzed the residue which remained after treating the 17 per cent cobalt alloy with dilute hydrochloric acid. The results of the analyses indicated the existence of a compound Co3Al13. Guillet2 published a liquidus for the aluminum-cobalt system which contained two maxima corresponding to CoAl6 and CoAl2 and two eutectic points at 30 and 74 per cent Co. The most extensive investigation of the system was carried out by Gwyer,3 whose results are summarized in Fig. 1. It will be noted that at the aluminum end there is a suppressed eutectic at 644° C. By extrapolation of the duration of the eutectic arrest to zero, the composition of the compound was placed at Co3Al13. Another thermal arrest was noted at 550° C., which Gwyer attributed to a peritectic reaction. The present investigation of the aluminum end of the aluminum-cobalt system is the eleventh of a series dealing with the constitution of aluminum; rich alloys prepared from electrolytically refined aluminum.4 Preparation of Alloys.-The alloys used in this work were all prepared from electrolytically refined aluminum, the analysis of which is shown in Table 1. In preparing some of the alloys, metallic cobalt (98 to 99 per cent) was used either directly or in the form of an intermediate alloy, the composition of which is given in Table 1. In order to obtain alloys of higher purity, cobalt was introduced into some of the alloys by means of chemically pure cobaltous chloride which was readily reduced by the aluminum. A small electric furnace with nickel-chromium heating elements was used in the preparation of the alloys.

Jan 1, 1932

By E. H. Jr. Dix

OF all the alloying elements used in commercial aluminum alloys, copper stands out as by far the most important, and it is perhaps for this reason that the constitution of the aluminum-copper system has received the attention of a number of experimenters covering a period of approximately 20 years. It would be expected that during this time the equilibrium relations had been thoroughly and exactly worked out. In a general way this is true, but there is a surprising lack of agreement in the details of the high aluminum end of the diagram, particularly in regard to the solid solubility of copper in aluminum, which has been given variously as 2 per cent. to 5 per cent. at the eutectic temperature. The importance of this is much greater than might at first appear to one unfamiliar with modern commercial aluminum alloys. This is true because, with one exception, the susceptibility of the strong alloys to heat treatment depends, in part at least, upon the solid solubility relations of copper in aluminum. In 1919, Merica, Waltenberg, and Freeman1 published the first detailed information on these solubility relations. They found that the solubility of copper decreases with falling temperature from about 4 per cent. at 5.25° C. to about 1 per cent. at 300° C. and is apparently still diminishing at lower temperatures. In 1921 there was published a brief account of the results obtained in the National Physical Laboratory, Teddington, England.2 This laboratory, however, reported that 5 per cent. of copper is soluble in aluminum at 540° C., and that this amount decreases to about 3 per cent. at 20° C.

Jan 2, 1926

By E. H. Jr. Dix

THE work of Merica1 and other investigators indicates that the phenomenon of age-hardening in. alloys of the duralumin type is primarily dependent upon the variation in the solubility of copper with temperature. In addition to copper, however, these alloys contain small amounts of magnesium, silicon, manganese and iron, which may affect the age-hardening either directly or indirectly. The effect of these elements on the solubility of copper and on the manner in which this solubility varies with the temperature is of considerable interest, therefore. The effect of magnesium is of especial interest because apparently it exerts a marked effect on the natural or room-temperature aging of alloys of the type described.2 A series of investigations3 has been in progress in the research laboratories of the Aluminum. Company of America to determine the functions

Jan 1, 1932

By William Fink

THIS paper is the nineteenth of a series from the Aluminum Research Laboratories, presenting the results of the investigations of equilibrium relations in aluminum-base alloys made from electrolytically refined aluminum. In previous papers equilibrium) relations have been deter-mined and correlated for 12 binary systems. Equilibrium relations have also been determined for portions of the aluminum corners of three ternary systems (aluminum-iron-silicon, aluminum-magnesium-silicon and alu-minum-copper-magnesium). The object of the present paper and those to follow is to increase our knowledge of the aluminum corner of the more important ternary systems. In 1926 Dix and Keith? suggested a new method for designating the phases encountered in alloy systems. The system has been used to a very limited extent 1,2,3. The system has since been slightly modified and will be used in this and future papers. In the system as modified, a phase is designated by placing in parentheses the chemical symbols of the elements essential to the formation of that phase. The symbols in the parentheses are separated by dashes in order to clearly distinguish them from a chemical formula. Elements that are not necessary to the formation of the phase in question, but which may be present in solid solution, are not indicated in the designation. If two or more phases would have the same designation according to these rules, they are dis-tinguished by prefixing Greek letters, and are definitely identified by X-ray diffraction patterns.

Jan 1, 1936

By Dix, E. H.

THE percentage of manganese used in commercial aluminum alloys is small, and yet this element is an important addition to some very valuable alloys. When used alone with commercial aluminum containing iron and silicon as impurities, the usual percentage in wrought materials is from 1 to 1.5 per cent., whereas castings may contain as much as 2 per cent. An aluminum-manganese alloy containing nominally 1.25 per cent. manganese is much used in sheet form for the manufacture of cooking utensils and other articles requiring a little greater strength and hardness than could be obtained with commercially pure aluminum. It is also used for various purposes in the form of rods, tubes and pipes. The aluminum-manganese alloys, both wrought 'and cast, offer excellent resistance to many kinds of corrosion attack. The U. S. Naval Gun Factory uses an aluminum alloy containing from 1 to 2 per cent. each of copper and manganese, for both castings and forgings. Manganese is also used, up to about 1 per cent., as a minor alloying .element in several of the strong aluminum alloys of the duralumin type. It is felt that the role of this element when thus used has not been fully understood, but it is believed that the results obtained in this investigation will throw additional light on the subject. The earlier work on the system aluminum-manganese was general in nature, and no detailed investigations of the relations existent in the useful aluminum-rich alloys have been reported. Guilletl1in 1902 surveyed the system, and Hendrichs2 in 1908 published an equilibrium diagram which, although based on .few data, is often used in the literature. Fragmentary work has also been done by other investigators."

Jan 1, 1927

By William Fink

NICKEL is used as an alloying element in several complex commercial aluminum alloys, among which are found some very interesting proper-ties, such as relatively high strength at elevated temperatures, relatively low coefficient of expansion, the absence of permanent growth, ability to take a good polish, and a bright, pleasing as-cast surface. For that reason the aluminum-nickel system was included in the list of binary aluminum systems that are being studied as a preparation for the investigation of more complex commercial alloys. This paper is the fifteenth of a series from the Research Laboratories of the Aluminum Company of America reporting the results of investiga-tions of equilibrium relations in aluminum-base alloys of high purity. The aluminum-nickel equilibrium diagram from 0 to 18 per cent nickel was determined, using the purest material available.

Jan 1, 1934

By A. C. Heath, E. H. Dix

THE importance of aluminum-silicon alloys in the light alloy field is now generally recognized. Where silicon was once considered detrimental to the properties of aluminum, useful alloys now contain as much as 13 per cent. Furthermore, silicon is present as an impurity in aluminum of even the purest grades. Iron is another important impurity in aluminum and like silicon is found in small quantities in the purest aluminum available today. The manner of occurrence of iron and silicon in commercially pure aluminum and many of its alloys exerts a very pronounced influence upon their properties. The effect of large quantities of iron in aluminum-silicon alloys is so detrimental that it has been found necessary to limit the allowable maximum percentage to as low a figure as is consistent with quantity production and satisfactory physical properties. The intimate relation existing between iron and silicon in aluminum and aluminum alloys makes necessary a more complete knowledge of this ternary system. This paper is divided into two principal parts, dealing respectively with aluminum-silicon solubility equilibria and the constitution of aluminum-iron-silicon alloys. PART I.-ALUMINUM-SILICON ALLOYS The early work on this system was largely confined to determining the general form of the diagram and in this respect the results are in good agreement. Briefly, aluminum and silicon form a simple eutectiferous series without compounds. Until recently the solid solubility of silicon in aluminum had not been accurately determined. Fraenkel1 (1908) stated that aluminum will retain 0.5 per cent. silicon in solid solution. Rosenhain, Archbutt and Hanson2 gave the maximum solubility as about 1.50 per cent. and added that "this solubility does not appear

Jan 1, 1928

By E. H. Jr. Dix

THE importance of aluminum-silicon alloys in the light alloy field is now generally recognized. Where silicon was once considered detrimental to the properties of aluminum, useful alloys now contain as much as 13 per cent. Furthermore, silicon is present as an impurity in aluminum of even the purest grades. Iron is another important impurity in aluminum and like silicon is found in small quantities in the purest aluminum available today. The manner of occurrence of iron and silicon in commercially pure aluminum and many of its alloys exerts, a very pronounced influence upon their properties. The effect of large quantities of iron in aluminum-silicon alloys is so detrimental that it has been found necessary to limit the allowable maximum percentage to as low a figure as is consistent with quantity production and satisfactory physical properties. The intimate relation existing between iron and silicon in aluminum and aluminum alloys makes necessary a more complete knowledge of this ternary system. This paper is divided into two principal parts, dealing respectively with aluminum-silicon solubility equilibria and the constitution of aluminum-iron-silicon alloys.

Jan 1, 1927

By W. L. Fink, H. C. Stumpf, L. A. Willey

VERY few studies of the aluminum-sodium system have been reported. Heycock and Neville1 were unable to detect any solubility of sodium in liquid aluminum. Mathewson2 prepared an equilibrium diagram consisting of two horizontal lines at the melting points of the two metals. He was unable to detect solubility at either end of the system. Scheuer3 first developed a method for the chemical determination of sodium in aluminum and then studied the solubility of sodium in liquid aluminum. His method involved heating aluminum with excess sodium under hydrogen until the two liquids were at equilibrium, chilling the melt, and analyzing the aluminum-rich layer. He reported the solubility to be 0.l0 pct sodium at 700°C, 0.115 pct at 750°C, and 0.128 pct at 800°C. This paper on the aluminum-sodium system is the twenty-first in a series from the Aluminum Research Laboratories describing equilibrium relations in aluminum alloy systems. MATERIALS The alloys for this investigation were prepared from electrolytically refined aluminum (99.99 pct) and sodium of reagent quality conforming to specifications of the American Chemical Society.4 Chemical analysis of the aluminum showed the following impurities: 0.002 pct Si, 0.002 pct Fe, 0.002 pct Cu, <0.001 pct Mn, 0.002 pct Mg and 0.001 pct Na. The sodium content of all alloys was determined by either chemical or spectrographic standard procedures5 No. IIA and No. SII respectively. DETERMINATION OF LIQUIDUS The boundary of the miscibility gap was determined by a modification of the method of Scheuer3 and of that used by Henry and Cordiano.6 As finally developed the method was as follows: A fused alumina crucible 25 mm id with 75 mm depth and 1.5 mm wall thickness was placed on the bottom of a container made from a 4-in. length of 1 ½ -in. iron pipe and pipe caps. The space around the sides of the crucible was filled with 40 mesh crystalline alundum. A charge of 60 g of aluminum and 10 to 15 g of sodium was placed in the crucible, the sodium first being trimmed and rinsed with iso-pentane to remove kerosene. The container was tightly capped, filled with argon (99.6 pct pure), and heated to the desired temperature (between 670 and 800°C). A positive pressure of argon (about 8 mm of mercury) was maintained through a small pipe to the upper cap. After soaking for from 2 to 5 hr, the container was quenched by directing a stream of water onto the base, so that solidification of the aluminum-rich layer was rapid and essentially unidirectional. Analyses were made on drillings taken from the bottom of the ingots after machining off the surface layers. Pre-

Jan 1, 1948

By William Fink

ZINC is one of the effective elements introduced to enhance the strength of aluminum. This strengthening is principally attributable to the high solid solubility of zinc in aluminum and the pronounced variation of solubility with temperature. Consequently an accurate determination of the solid solubility curve is desirable. The solid solubility relations have been studied by numerous investigators. Shepherd&apos; first established the existence of a solid solution region at the aluminum end of the diagram (y phase) by specific volume and microscopic determinations. Bauer and Vogel2 published a constitutional diagram which showed the limits of solid solubility as determined by thermal and microscopic methods. Hanson and Gayler3 presented the aluminum-zinc diagram which is now most generally accepted (Fig. 1). Chill-cast samples were given thermal treatments designed to obtain equilibrium conditions, quenched, and microscopically examined.. The solubility was placed between 15 to 20 per cent at 600 C., 20 to 22 per cent at 140° C. and 36 to 38 per cent at 270° C. Sander and Meissner4 decidedly modified the limits of they phase field of Hanson and Gayler&apos;s diagram by using similar methods on chill-cast specimens annealed for a shorter period of time. Tanabe,5 utilizing dynamic hardness, electrical conductivity and dilatometric measurements of specimens at temperature, obtained values comparable to Hanson and Gayler&apos;s at room temperature, but appreciably lower at higher temperatures. Nishimura6 concluded from age-hardening results of aluminum-zinc alloy chill castings, which had been quenched from 400° to 500° C., that the solubility of zinc in aluminum at room temperature is less than 5

Jan 1, 1932

By William Fink

SINCE so many different curves have been published for the solid solubility of zinc in aluminum, it seems desirable to definitely establish the correct curve by two or more independent methods. The curve published in part I1 was based entirely upon X-ray measurements because the other methods employed at that time were not satisfactory. The present paper (the seventeenth of this series on high-purity aluminum alloys) describes the determination of the solid solubility of zinc in aluminum by the measurement of electrical resistivity at temperature and by microscopic examination. Since the publication of our part I in 1932, an investigation of the solubility relations in the aluminum-zinc system has been reported by Schmid and Wassermann2, who obtained their solubility results from lattice-parameter measurements on heat-treated and quenched speci-mens. The diagram that they published is shown in Fig. 1. In this investigation they also found by X-ray measurements that the parameter of the gamma phase changed continuously with zinc content and at such a rate that it would be identical with that of the beta phase at 60 atomic per cent zinc. It was concluded therefore that the beta and gamma phases, from the point of view of structural relationship, are one single phase. They also suggested a gap of immiscibility between 270° and 350° C. The complete boundary in this region could not be deter-mined satisfactorily by the method employed and therefore was not shown in their diagram.

Jan 1, 1936

By William Fink

Two of the aluminum-alloy systems previously studied-the alumi-num-titanium and the aluminum-chromium-exhibit a peritectic reaction at the extreme aluminum end of the diagram. Preliminary work indi-cated that the aluminum-zirconium and certain other aluminum systems were similar in this respect. The present paper, the twentieth of a series from the Aluminum Research Laboratories, reports the results of a recent investigation of equilibrium relations in aluminum-zirconium alloys of high purity, which confirm the preliminary observations. PREVIOUS INVESTIGATIONS There has been only one investigation of the aluminum end of the aluminum-zirconium system. Sykes1 prepared and studied alloys containing 0 to 70 per cent Zr. The lowering of the freezing point of aluminum by the addition of zirconium was found to be very little, if any (less than 2°C.). He placed the solid solubility of zirconium in aluminum at room temperature between 0.57 and 0.97 per cent. A few other investigators have attempted to determine the com-position of the intermetallic compounds occurring in this system. Hönigschmid2 obtained the compound ZrAl3 as a by-product during the preparation of ZrSi2. He made no attempt to prepare other aluminum-zir-conium compounds. Weiss and Newmann3 prepared an alloy by heating aluminum with a double fluoride of potassium and zirconium. When this alloy was treated consecutively with caustic soda and hydrochloric acid, there was a residue, which contained approximately 72 per cent Zr and 28 per cent Al (Zr3Al4). Marden and Rich4 prepared an alloy in the same way, treated it with caustic soda, and obtained a residue of silver-white crystals, which contained 70 per cent Zr and 30 per cent Al (Zr3Al4).

Jan 1, 1939

By Clarence Zener

THE heat-treatment of steels will not pass from the stage of an art into that of a science until the mechanism of the phase transformations associated therewith is thoroughly understood. Such an under- standing will involve two distinct types of inquiry: (I) the direction of the trans- formation, (2) the speed of the transformation. The first type of inquiry, which involves only the equilibrium relations between the various phases in steel, is the subject of the present and of a succeeding article; the second type, which involves the kinetics of transformations, will be the subject of a later article. In order that a theory of equilibrium relations may give useful information, certain experimental data must be put into the theory. It is customary for these data to be of a thermal nature. In the system discussed here in steel such thermal data are very scarce. In medium-alloy steels another type of data might possibly be used. In these steels the concentration of solute is so low that it may be possible to use the approximation of dilute solutions, an approximation that leads to linear relationships. The unknown functions, or constants, may then be determined in some cases from the binary iron- alloy system and in other cases from the ternary iron-carbon-alloy system. From the functions, or constants, so determined may then be computed the equilibrium relations in more complex medium-alloy steels. In the present article this second approach is used, the necessary experimental data being obtained from the simple binary and ternary equilibrium diagrams. FUNDAMENTAL EQUATIONS In this article are derived the equilibrium relations between the gamma, alpha and cementite phases. In these three phases all important alloying elements except carbon form substitutional solutions, each alloying atom occupying a potential site for an iron atom. Carbon, on the other hand, forms an interstitial solution. In the face-centered cubic gamma phase, the interstitial positions are at the center of the unit cube and at the centers of the cube edges. There are therefore four interstitial positions per unit cell, or one per iron atom. In the body- centered cubic alpha phase, the interstitial positions are probably at the face centers, and also at the centers of the edges, which are crystallographically equivalent to the face centers. There are therefore six interstitial positions per unit cube, or three per iron atom. In cementite, (Fe, Alloy)3C, the carbon atoms may be regarded as filling all the lattice positions of a given type. The introduction of the fundamental equations of equilibrium has presented the author with a quandary. These equations are formally so similar to other equations that have been derived1,2 for related systems that they may appear to some readers

Jan 1, 1946

By Clair Upthegrove, Elbert S. Rowland

THE widespread interest in the alloys of beryllium with copper is due principally to the fact that certain compositions show very favorable precipitation-hardening characteristics and are, in fact, the strongest nonferrous alloys known at the present time. Investigations have been conducted by Masing and Dahl and others on the physical characteristics of ternary beryllium alloys, in an attempt to produce precipitation-hardening effects with a smaller amount of beryllium than that required in the binary copper-beryllium alloys (2.0 to 2.5 per cent Be). The results of these investigations show that ternary alloys of beryllium with Cu-Sn, Cu-Al and Cu-Zn, among others, exhibit promising improvements in physical properties after precipitation-hardening treatment and, while the increases in properties obtained are not as high as those realized from the binary copper-beryllium alloys, excellent properties are: obtained with beryllium contents averaging about one-half the amount required in the binary alloys. This paper presents the results of an investigation of the equilibrium relations of certain alloys containing copper, tin and beryllium. The alpha-phase boundary of the ternary system is given for alloys containing from. 0 to 1 per cent beryllium. The equilibrium conditions beyond the alpha-phase boundary are presented for alloys containing up to 32 per cent tin and 1 per cent beryllium. The data were collected by means of

Jan 1, 1935

By Elbert Rowland

THE widespread interest in the alloys of beryllium with copper is due principally to the fact that certain compositions show very favorable precipitation-hardening characteristics and are, in fact, the strongest nonferrous alloys known at the present time. Investigations have been conducted by Masing and Dahl and others on the physical characteristics of ternary beryllium alloys, in an attempt to produce precipitation-hardening effects with a smaller amount of beryllium than that required in the binary copper-beryllium alloys (2.0 to 2.5 per cent Be). The results of these investigations show that ternary alloys of beryllium with Cu-Sn, Cu-Al and Cu-Zn, among others, exhibit promising improvements in physical properties after precipitation-hardening treatment and, while the increases in properties obtained are not as high as those realized from the binary copper-beryllium alloys, excellent properties are obtained with beryllium contents averaging about one-half the amount required in the binary alloys. This paper presents the results of an investigation of the equilibrium relations of certain alloys containing copper, tin and beryllium. The alpha-phase boundary of the ternary system is given for alloys containing from 0 to 1 per cent beryllium. The equilibrium conditions beyond the alpha-phase boundary are presented for alloys containing up to 32 per cent tin and 1 per cent beryllium. The data were collected by means of

Jan 1, 1935