The pressure of the gas in equilibrium with sphalerite has been determined in the temperature range of 680' to 825°C, using the Knudsen orifice method. A comparison of these experimental pressures with those calculated from thermal data and from other equilibrium measurements shows that the vapor above sphalerite is predominantly dissociated ZnS. Equations have been given for correctly calculating dissociation pressures using the Knudsen orifice method. It has been shown that the experimentally determined pressure is the same, whether the zinc sulphide is sphalerite or not, or a mixture of wurtzite and sphalerite. CONFLICTING points of view appear in the literature on the constitution of the vapor in equilibrium with solid zinc sulphide in the vicinity of 800°C. By comparing the dissociation pressure calculated from thermodynamic data and the vapor-pressure determination of ZnS by Veselovski,1 Lumsden2 has concluded that the vapor consists largely of dissociated ZnS. Sen Gupta,' however, concludes from his spectroscopic determinations that the vapor is largely ZnS molecules. In view of the fact that the thermodynamically calculated' dissociation pressure is higher than that experimentally measured by Veselovski, it seemed in order to repeat Veselovski's measurements. Experimental Procedure The method used for the determination of the pressures in this papel- is the Knudsen effusion cell. The apparatus and procedure were described in a previous paper- from this laboratory on the determination of the vapor pressure of silver. The only difference is that the Knudsen cell in this work is made from platinum and there is no external cover around the cell. The cell is an ordinary platinum crucible of 2.2 cm top diameter with a capsule cover. It was thought that platinum might stand up at these temperatures to the solid and gaseous ZnS, since it was found that the weight of the platinum cell itself did not change appreciably on heating ZnS in it at the working temperatures. To insure that reaction of the zinc sulphide with the cell was not giving' a false value, a stabilized zirconia cell was employed for check runs. Fig. 1 shows the comparison, which is satisfactory. Veselovski previously had measured the vapor pressure of ZnS using a silica Knudsen effusion cell. On repeating his experiment in this laboratory, it was found that ZnS at-tacked the silica cell, giving it a marked frosty appearance. This led to the belief that Veselovski's result:; may be in error. Also, he was operating at pressures above the range ordinarily considered safe for the Knudsen method. The effusion rate was measured by weighing the cell before and after each run. The weight loss during heating to temperature and cooling down was measured and subtracted from the weight loss during the actual run. The zinc sulphide used in this investigation was from two sources: Fisher cp grade, and a sample of pure sphalerite supplied by Mr. E. A. Anderson of the New Jersey Zinc Co. Before and after the series of runs with Fisher ZnS, X-ray analysis showed that both wurtzite and sphalerite were present. However, the ratio of sphalerite to wurtzite increased. All measurements were made below the transition temperature which has been reported" to be 1020°C. The data obtained in this investigation are tabulated in Table I. The pressure was calculated by the usual Knudsen formula" on the assumption that ZnS molecules were effusing. From these data, using pure sphalerite in the platinum Knudsen cell, the vapor pressure of ZnS, in mm of Hg, as a function of temperature is given by the solid line in Fig. 1. The best straight line, as determined by the method of least squares, is given by 14405 logpzns =-14405/T +11.032. A comparison of these results with Veselovski's shows that his results are about 50 pct lower. Discussion The vapor in equilibrium with solid zinc sulphide in the temperature range of this study will consist of Zn, S2, and ZnS mol, since other species of zinc and sulphur' are relatively unstable. The question to be settled is whether or not ZnS is largely dissociated. The derivation8 which follows gives the method of calculating the pressure of zinc and sulphur over solid ZnS, assuming complete dissociation, from Knudsen cell data. The free energy of the reaction 2 ZnS(solid) ? 2 Zn(gas) + S2(gas) is given by ?F?° = -RT In K = —RT In p12p2 where p1 is the zinc pressure and p is the sulphur pressure. If dissociation occurs in a closed system,

Jan 1, 1955

By W. F. Hergert, L. H. Banning

Experimental production of Al-Si alloys, containing from 33 to 55 pct Al, by direct reduction of aluminum silicates in a three-phase arc furnace is described. Advantages of a smelting technique utilizing hogged wood waste as part of the reductant and for temperature control are discussed. WORK on the problem of producing aluminum by smelting has been in progress since the middle of the eighteenth century. Early work met with little success and in 1782 Lavoisier, an eminent French chemist, expressed the belief that alumina could not be reduced by carbon. It was almost a century later when the Cowles brothers developed a process for the production of aluminum alloys by reducing alumina coincident with the reduction of other metal oxides. In practice, the other metal oxide was usually copper. In 1907 it was first shown that alumina alone could be reduced by carbon at a temperature of 2200°C. The metal produced was volatilized and lost or recombined with the oxides of carbon formed in the reaction.' For a number of years after the Cowles brothers abandoned production of Cu-A1 alloys because their product was not commercially competitive with the aluminum produced by the Hall process, there was little interest in thermal reduction processes. After World War I interest in such processes was renewed and a number of patents were issued on processes for the production of A1-Si alloys.' , "he function of the silicon in these processes was the same as the function of the copper in the Cowles brothers process, namely, to prevent the reduced aluminum from recombining with the oxides of carbon and to promote absorption of the aluminum vapors set free at the high temperature required for the reduction reaction. The advantage of using silicon in place of copper for this function is that silicon has a higher boiling point (2600"C) than copper (2310"C) and its oxides, combined with aluminum oxides, occur in nature in almost unlimited quantities. No A1-Si alloys have been produced commercially in the United States, as far as is known. However, considerable experimental smelting of aluminum silicate materials has been done by the TVA at Wilson Dam, Ala.' The most extensive development and commercialization of the electrothermal production of A1-Si alloys took place in Germany before and during World War II.V he furnaces used in the

Jan 1, 1956

By T. D. Tiemann

The chemical and mineralogical composition of Caribbean bauxite ores are described. Extraction of alumina by several processes from both Haiti and Jamaica bauxites is discussed and data presented. IMMENSE deposits of bauxite occur in the Caribbean islands of Hispaniola and Jamaica in the high plateau lands and have been excellently described by 0. C. Schmedeman.' The bauxite occurs as deposits in catchments or etched depressions in Tertiary limestone believed to have been deposited in the Eocene and Oligocene periods.' In appearance both the Haiti and Jamaica bauxites resemble a relatively high iron clay and have indeed been mistaken for such.' They are very soft and friable and disperse readily on vigorous agitation in water. The color range in general is light brown to red. Chemically, the outstanding characteristic of the bauxites is the low silica and high ferric oxide content. The extremely low silica makes them particularly valuable for the production of alumina in the Bayer plant since silica is responsible for the loss of both alumina and soda chemically combined as XNa,OYSiO2,ZAl2O2. The ferric oxide, only traces of ferrous iron are present, offers no interference in the production of high grade alumina. Typical oxide analyses of three types of ore are given in Table I2 and a list of the elements occurring in spectrographic quantities in Table 11." The size of the individual particles in the ore makes successful petrographic examination extremely difficult. The ores contain some relatively coarse grains of heavy minerals such as ilmenite, magnetite, and rutile, but other than occasional crystals of a few microns, the greater portion of the minerals are submicroscopic in size and approach colloidal dimensions. The mineralogic composition of the ores has been investigated by X-ray and differential thermal analysis.' These investigations indicate that the predominant mineral phases present are gibbsite (A1203.3H2O), boehmite (Al2O3.H2O), hematite (Fe2O3), and goethite (Fe2O3-H2O). There is no evidence of the occurrence of diaspore (Al2O3.H2O) in either the Haiti or Jamaica ores, but some type of "amorphous" alumina may be present in some of the bauxites of Jamaica." The temperature stability regions in the alumina-water system have been investigated and are given in recent literature. In the temperature range where the hydrated forms are stable, as determined by hydrothermal bomb methods," ibbsite is the stable phase to 155°C (311°F), boehmite from 155°C (311°F) to 280°C (536oF), and diaspore from 280°C (536°F) to 450°C (842°F). Although quite similar in many characteristics, the Haiti and Jamaica ore show a divergence in mineralogic composition that is reflected in the extractability of the alumina described in later paragraphs. Two principal differences occur in mineralogic composition. The iron-bearing mineral in the Haiti ores is predominantly hematite, while in the Jamaica ores goethite is predominant.4 Directly related to the extraction of alumina are the two minerals, gibbsite and boehmite. Boehmite is relatively high in the Haiti ores and in some of the less soluble Jamaica ores, while gibbsite predominates in the ores in Jamaica amenable to the American Bayer process of extraction. Pedersen and Related Processes In general, all processes for the extraction of alumina involving sintering or fusion of bauxite ores with limestone, soda ash, or a combination of limestone and soda ash followed by leaching, are based on the formation of alumina compounds that. yield alumina soluble in the subsequent leach. The principal idealized reactions in respect to alumina and silica for the three types of processes are as follows: Soda Ash Sinter: A12O3 + Na2CO3 = Na2O-Al2O, + CO2 SiO2 + Na2CO3 = Na2O . SiO2 + CO2 A12O2 + SiO2 + Na2CO3 = Na2O.Al2O8. SiO2 + CO2 Leach (with excess water): H2O + Na2O-A12O3 = 2 NaOH + A12O3 (insolution) H2O + Na2O-SiO2 = 2 NaOH + SiO2 (in solution) Soda Ash— Limestone Sinter: Na2CO2 + A12O3 = Na2O.A1203 + CO2 2CaCO3 + SiO2 = 2CaO . SiO2 + 2CO2 Leach (with excess water): Na2O' A1208 + H2O = 2NaOH + A13O3 (in solution) These latter reactions are the basis of the sinter process currently used for the recovery of soda and

Jan 1, 1952

By R. S. Sherwin

The extractive metallurgy of primary aluminum from its ores is discussed with special attention to the production of alumina from high grade ores by the Bayer process, including differences between American and European practice and a brief description of some processes for lower grade ores and the electrolytic reduction of the oxide to aluminum. METALLIC aluminum is not found in nature, but the oxides, hydroxides, and especially the silicates are plentiful. The estimated percentage of in in the crust of the earth is about 8 pct while that of iron is about 5 pct. By far the larger portion of this is combined with silica in the form of various clay minerals and igneous silicate rocks. From the point of view of extractive metallurgy of aluminum, these are low grade ores while the better qualities of bauxite are the high grade ores. There have been various definitions of bauxite but perhaps the best definition at the present time is that bauxite is a rock or earth commonly used as an ore of aluminum or its salts in which the aluminum is present predominantly as a hydrate or a mixture of hydrates and hydrous oxides. It contains varying amounts of oxides of silicon, iron, and titanium and traces of compounds of some of the less common elements. The silica is mainly combined with alumina as clay or clay minerals which are hydrous aluminum silicates, although a part of it may be present as quartz sand. On the American continents, the alumina is mainly present as gibbsite, Al2O3 . 3H2O, and the same may be said of the best known deposits of the Dutch East Indies and some of the deposits in India. In France and other countries in Europe as well as in Africa, the alumina is present mainly as boeh-mite, A12O3 . H2O, but in some of these deposits it is mixed with minor amounts of gibbsite. Some other deposits, such as those in the islands of Haiti and Jamaica, evidently contain two or more hydrates or hydrous oxides of alumina in varying proportions. Perhaps the main portion of the alumina may be present as gibbsite and boehmite with the proportion between the two varying rather widely. In the silicate minerals, including clay, the alumina is chemically combined with silica and has not been separated satisfactorily by mechanical or physical ore-dressing methods. Low grade bauxites are mixtures of hydrates, usually gibbsite or boehmite, with clay, iron oxides, etc. In some low grade bauxites, it is possible to separate a portion of the gibbsite or boehmite, which may be present as relatively hard and coarse particles, from soft or finely divided clay minerals by log washing or similar methods. This has been applied to the product of some mines or parts of them, but on other ores it is not applicable. In some cases the gibbsite or boehmite is almost as fine and soft and of nearly the same specific gravity as the clay minerals so that washing and gravity separations are not successful. The iron oxide, the clay minerals, and a part of the titanium minerals are often so finely dispersed in the ore that any of the physical mineral separation methods, including separations by gravity, particle size, flotation, and electrostatic or magnetic separation, have not been commercially SUCCESSFUL except on relatively small lots of ore. For these reasons, the only available methods of separation on the general run of ores have been methods which would be classed as chemical rather than physical or mechanical separations. Aluminum oxide can be reduced by carbon at temperatures above 1800°C to form metallic aluminum and aluminum carbide or nitride. The temperature for rapid reduction of aluminum oxide to metallic aluminum is about the boiling point of aluminum and above the temperatures necessary to reduce iron, silicon, and titanium so that the direct reduction of an aluminum ore with carbon will produce an alloy of aluminum, iron, titanium, silicon, etc., which may be mixed with carbides and nitrides. Also a large amount of the reduced aluminum may be lost as a vapor except in the presence of some alloying agent such as copper or other metals. While it is possible to refine such alloys or mixtures so as to produce commercially pure aluminum, the methods which have been found are too expensive for the present market. One direct reduction method which found limited commercial use in Germany during World War II was the direct reduction of a mixture of clay containing very little

Jan 1, 1951

By G. H. Kessler

ALTHOUGH considerable attention has been devoted to reaction mechanisms and equilibria of a number of endothermic reactions through which metals or their refractory compounds can be formed upon heated surfaces, only a comparatively small amount of work has been done to develop rate information for these systems. The interestin and very worthwhile work of Holden and Kopelman, Runnalls and Pidgeon,Dijring and Moliere, and Herrick and ICrieble4 is to be noted; however, their work was done under very specific conditions and the rate information which they have developed is not applicable to many systems which have been studied experimentally. That a more generalized approach is needed is shown by the diversity of these systems and of the experimental conditions which they require. These include the preparation of titanium, zirconium, tungsten, molybdenum, chromium, co-lumbium, aluminum, and silicon by decomposition or disproportionation of their halides, in some instances through hydrogen reduction; the preparation of nickel and iron by decomposition of their car-bonyls; and the preparation of copper by decomposition of the acetylacetonate. They may be carried out at temperatures ranging from 100" to over 2000°C and at pressures of from less than one mm Hg to superatmospheric. The physical mechanism of the overall process can be broken down into several steps, any one of which may be rate-determining; and the rate associated with each of these basic physical processes can be predicted. Consequently, by proper application of the present technology of rate processes, it is possible to arrive at a rate of metal deposition in the system of interest and to reach an understanding of the influence of' each major variable upon the deposition rate. It is the purpose of this paper to illustrate how this can be done and to present experimental results for a specific system for comparison with theory. The overall process of deposition of metal upon a heated surface which is immersed in vapors of a compound of the metal can be broken down into the following steps: 1) Transport of the reactant vapors to the surface. 2) Decomposition of the reactant in the immediate vicinity of the surface to a) establish chemical equilibrium if reaction rates are high; or to b) establish a dynamic equilibrium in accordance with the several reaction rates. 3) Diffusion of reaction products away from the vicinity of the surface, with or without simultaneous recombinations to form still other products. The overall process is said to be diffusion controlled if Step 1, or the equivalent Step 3, is slow; it is reaction-rate controlled if Step 2b is slow. When experimental evidence shows the reaction rate to be controlling, the well-known theories of Eyring' and others can be used as a basis for correlating and extrapolating the experimental data. Although these theories give only approximate estimates of reaction rates, they are of considerably greater value in correlating experimental data. Most deposition systems operate at surface temperatures sufficiently high that reaction rates near the surface are very high. Mass-transport rates then become controlling; and it is this regime of diffusion controlled rates which is most often of concern and Which will be considered here. When the system pressure is very low, i.e., in the micron range, then the transport processes are those of molecular movement, and the results of kinetic theory can be applied to specify a rate of arrival of reactant molecules at the heated surface. If the condensation coefficient can be estimated, then the deposition rate will be given by the product (rate of arrival) x (condensation coefficient), Conversely, experimental data can be used to determine a condensation coefficient, as was done by Holden and Kopelman' for the decomposition of zirconium tetraiodide upon a heated molybdenum surface, who found the coefficient for zirconium on molybdenum to be 1.0 at temperatures of 1382°C and above. In this pressure range, the geometry of the system. and in particular the distance between the source of reactant molecules and the heated surface, can exert a considerable effect upon the deposition rate;

Jan 1, 1961

By B. C. H. Steele, C. B. Alcock

In choosing solid oxide electrolytes for use in the measurement of thermodynamic quantities at high temperatures, the two most important criteria are the values of the partial ionic and electronic conduc tizities. Measurements of these conducticities have been made for some Group IVA oxides and solid solutions of these oxides with CaO, Y2O3, and La2O3. The total conductivities as a function of temperature. oxygen partial pressure, and composition were determined, as well as the electromotive forces of cells in which the oxygen partial Pressures of the electrodes were between 10-7 and 10-29 atm at 1000°C. Additional factors that influence the experimental arrangements, such as the operating temperature, the appropviate cell atmosphere, and electrode kinetics, are also discussed. IT has long been recognized that galvanic cells incorporating solid electrolytes can possess many advantages for the measurement of high-temperature thermodynamic data. Unfortunately, the electrical-transport properties have only been established for a few solid electrolytes, although attempts have been made, and are still being made, to use such materials as porcelain' and magnesia.' Kuikkola and Wagner have discussed3 and demonstrated4 various applications of solid electrolytes, and, in particular, their work stimulated the electrochemical measurement of oxygen activities using cells incorporating the solid oxide electrolyte, Zr0.85Ca0.15O1.85 The excellent characteristics of this oxide electrolyte have been confirmed by the investigations of Kingery et al.5 (oxygen ion diffusion), Carter and Rhodes6 (zirconium and calcium ion diffusion), and Weissbart and Ruka7 (electronic transference number). However the observations of Peters and Mobius,8 later confirmed by Schmalzried,9 indicated that the electronic component of zirconia-based electrolytes could become significant at low oxygen chemical potentials. Under these conditions, thoria-based electrolytes have obvious advantages arising from their superior thermodynamic stability. It was known that certain thoria solid solutions possessed defect fluorite structures containing anionic vacancies (cf. Zro.85Cao.l50O1. 85), although data on their electrical properties were conflicting. Kiukkola and wagner4 concluded that thoria-based electrolytes exhibited appreciable electronic conductivity, whereas Peters and Mobius8 mentioned that the electronic conductivity only became important at high oxygen partial pressures, but gave no further details. In addition, both Kiukkola and wagner4 and Peters and Mann'" had determined the oxygen chemical potentials associated with the Fe-FeO, Co-COO, Ni-NiO, and Cu-Cu2O equilibria, and it was not known whether discrepancies in their results could be attributed to the different cell design, or the thoria-based electrolyte used by Peters and Mann. These uncertainties have been resolved during the present investigation into the measurement of low oxygen chemical potentials, and transport properties of the relevant oxide electrolytes are presented and discussed. Other experimental difficulties associated with low oxygen chemical potential measurements are also described, with particular reference to the Nb-O system. 1. THEORETICAL CONSIDERATIONS Oxide systems of potential use as solid electrolytes possess a large energy gap between the valence and conduction bands. Little is known about the defects present in these wide-gap metal oxides as a function of impurity content and deviations from stoichiom-etry, or the mechanisms by which electronic charges move in these solids. For these materials it is convenient to represent the measured conductivity as the the sum of three terms: where a, is the conductivity due to positive hole conduction (p type), and oe is the electronic conductivity due to electron conduction (n type). U there is a large concentration of ionic vacancies fixed by composition then the ionic contribution will not be a function of oxygen pressure. Although the possibility of a pressure-independent electronic component also cannot be ignored, it is likely that such a term would only become significant at very high temperatures, and in general the positive hole conduction will increase with increasing oxygen pressure, and the electron conduction will increase with decreasing oxygen pressure. It follows that the total conductivity is related to oxygen partial pressure as follows:

Jan 1, 1965

By K. J. Brondyke, P. D. Hess

Two processes have been developed for improving the quality of molten-aluminum alloys before casting. The Filtration Process. which involves passing molten metal through a packed bed of granular filter material, is a rapid means of removing finely divided particles. It has the most potential in those instances where removal of inclusions is of primary importance. The Combination Fillration-Inert Gas Fluxing Process inuolzles introduction of an inert gas so that it will diffuse countercurrent to metal flow through the filter bed of granular material. Dissolved hydrogen is removed from the metal in addition to removal of finely divided particles. The Combination Process is most useful where both inclusion removal and attainment of conistently low-hydrogen-content metal are important. Metal treated by the Combination Process is of higher and more uniform quality than heretofore attainable with prolonged chlorine fluxing. Costs of the Combination Process can, for the most part, be offset by savings derived from high recoveries and increased production of superior-quality products. IMPROVEMENT in the quality of molten-aluminum alloys is secured generally through the use of some fluxing practice in a crucible, holding furnace, or ladle involving either gaseous or solid fluxing media. Typical fluxing agents may include the gases nitrogen, argon, or chlorine used either singly or as mixtures and the solids aluminum chloride or hexachloroethane. Regardless of the fluxing means used, the primary objectives are the adequate removal of both metallic and nonmetallic inclusions and reduction of hydrogen content to an acceptably low level. The ultimate goal is to produce ingots and cast products of high quality free from inclusions and porosity. The development of ultrasonics for measurement of internal quality, tightening of quality controls, and the application of the aluminum alloys to new or different commercial fields have been responsible for an ever increasing demand for improvement of quality of both cast and fabricated products. This demand for high quality has not been restricted to any single type of product. On the contrary, the demand encompasses about the entire variety of products including those for fabrication, those to be machined, buffed, or finished for decorative purposes, and those for critical applications where both surface and internal quality is of utmost importance. In many instances products acceptable in the 40's would now be scrapped as unacceptable by these higher present-day standards. With this ever increasing demand for higher quality, it became apparent at Alcoa that conventional means of melt treatment were inadequate in many instances and new approaches were necessary. Consequently the research program was intensified with attention focused on metal treatment during transfer in order to reduce the furnace processing time to a minimum in an effort to attain the desired results at a minimum of additional expense. As a result of this intensive research program which covered numerous variations and adaptations of conventional methods in addition to new methods of melt treatment, several new processes were developed, two of which will be described here. The first of these, a method of melt filtration, was patented in February, 1959.l The second process involving combination filtration—inert gas fluxing was patented in June, 1962. 2 Other melt-treatment processes developed during this period of investigation were patented as listed.3 FILTRATION PROCESS General Description. The Filtration Process, which involves passing molten metal through a packed bed of granular filter material, is a rapid method of effectively removing finely divided particles. It is an impingement-type filter; hence the size of the particles removed from the metal are considerably smaller than the interstices of the

Jan 1, 1964

By L. W. Rowe, S. S. Cole

A laboratory bench scale unit is described whereby finely divided chlorinatable residues are held for a short period by a restraining bed of a coarse-grained ore of comparable composition to permit 'flash' chlorination of the high surface area powder. Results on chlorinating a finely divicled titania residue using rutile sand as the restraining bed showed that 92 pct utilization of chlorine and equivalent conversion of TiO2 in the fine residue to Ticl4 were attained with a dust loss of about 3 to 4 pct and an equivalent amount of ch1om'nation of the titanium values in the restraining bed. THE chlorination of coarse grain titaniferous ores; i.e., 20 to 150 mesh sizes in fluidized beds is practiced commercially.' One effective method found for the chlorination of a very fine material in a fluidized bed is the "flash" chlorination technique.' By charging the finely divided charge material into the bottom of an established bed of optimum sized rutile, ilmenite, titanium beneficiate, or even an inert material such as sand, chlorination occurs before the dust can pass through the bed. The major requirement is that the bed be less chlorinatable than the charge. In this process, the charge consists of a finely divided (between one and 50 µ) titania residue obtained from a titaniferous ore beneficiation process. The charge is blended with a 20 pct wt basis addition of 20 to 60 .mesh size low volatile coke (to minimize hydrogen chloride formation) and fed to the bottom of the bed with the chlorine gas stream. A ball check device is used to permit entry of the charge and prevent the bed from discharging when the gas flow is cut off. The coarse pieces of coke serve to reduce compaction in the charge mixture and permit sat]sfactory feeding without plugging or jamming. Feed and gas rates are adjusted to provide for complete reaction of the charge material, with 90 to 95 pct chlorine efficiency, and maintain a gas flow in the range of 0.4 to 0.6 ft per sec. The equipment consisted of a 3-in. diam mullite tube enclosed in an electric furnace. A bow-shaped 3/4 in. Saran tube fed the charge from an air lock type of feed hopper (to prevent the escape of the chlorine gas into feed bin) to the bottom of the bed. The charge rate was set by providing a small awiliary hopper below the feed hopper where a weighed portion of the charge could be discharged in a specified time interval into the main chlorine stream. The chlorine rate was measured by a flowmeter. The reaction tube was filled with a bed of Australian rutile ore, this restraining bed serving two purposes; i.e., it rapidly heated the fresh charge to the reaction temperature and retained the particles in the bed for a sufficient time for selective chlorination to proceed. Due to the fine particle size and open, porous structure of the charge, this reaction was almost instantaneous, and, with proper adjustment of feed and gas rates, very little fine material passed through the bed without reacting and only a very small fraction of the restraining bed was chlorinated. A typical reaction procedure was to fill the bench scale fluidized bed unit with a 1 kg charge of Australian rutile ore analyzing 95.5 pct TiO2, 0.6 pct FeO, a beach sand deposit 40 to 150 mesh size. When fluidized, the bed was approximately 2 ft in depth. The ore was fluidized with a 1:l mixture of chlorine and nitrogen at a rate of 0.40 ft per sec. This gas mixture was necessitated by the comparatively short bed depth; a larger unit, with a deeper bed, could be fluidized with chlorine alone without significant free chlorine loss. Feed rate was 8.0 g per min of beneficiated ilmenite analyzing 85.0 pct TiO2, 2.6 pct FeO plus 1.6 g per min of 20 to 60 mesh petroleum coke. The

Jan 1, 1962

By Ivan B. Cutler, Milton E. Wadsworth

Coprecipitation of anionic and cationic polyelectrolytes has been applied to floccula-tion of several mineral systems. Results obtained in a study of the flocculation of kaolinite and hematite suspensions of polycationic and polyanionic electrolytes are presented. Greatly increased settling rates were observed following precipitation of positive and negative polyelectrolytes on the surface of finely divided minerals in aqueous suspension. The ratios of polycationic to polyanionic electrolytes required to produce maximum sedimentation have been shown to correspond closely with the equivalence points obtained by light scattering studies of systems containing the positive and negative polyelectrolytes by themselves. DISPERSION of colloids has been of interest to surface chemists for many years. Flocculation studies have been employed to evaluate the limits of colloid stability. In water suspensions, colloids become unstable and flocculate when the 5 potential, the potential of the kinetic solvation sheath, falls to a value at which van der Waals forces may act to draw the particles together. This may happen through an adjustment of the pH of the suspension or by addition of a salt. Optimum conditions for rapid formation of large flocs are found in the region of minimum < potential. In addition to these well known considerations, colloids in water suspensions are known to be flocculated by certain large organic macromolecules. These polyelectrolytes in some cases minimize the 5 potential and in other instances increase the attractive forces by supplying sites for hydrogen bonding.&apos; Use of organic polyelectrolytes in flocculation of mineral colloids has increased rapidly in recent years. These materials are now recognized as indispensable aids to fluid-solid separations in many extractive metallurgical operations. They have been found to increase both the settling rate in thickeners and the filtration rate of filters. In the elucidation of the characteristics of these organic reagents as floc-culants in this laboratory, it was discovered that interaction of certain polyelectrolytes had a surprisingly good effect on flocculation of mineral colloids. Experimental Procedure: The anionic flocculants used in this study were Lytron 886 and 887, produced by Monsanto Chemical Co. Both reagents are copolymers of vinyl acetate and maleic anhydride. Lime is added to Lytron 886, whereas Lytron 887 is all organic. These reagents possess two carboxyl groups for each acetate group and are therefore anionic in character. The cationic reagents used were the Peter Cooper Co. 1-X and 2-X glues. The structures are not definitely known, but the re- agents are amines and are cationic in character. The glues were prepared in the chrome-alum form. Both types of reagents may be classified as polyelectrolytes in that they are high molecular weight polymers and ionize in water. All data presented are in terms of sedimentation rate, measured in 250-ml glass-stoppered graduated cylinders. With suitable precautions such measurements are fairly reproducible and provide a sensitive means for selecting important parameters such as PH, reagent concentration, and floc size and density. Agitation was standardized with five complete end over end cycles of the suspensions in the stoppered graduated cylinders.

Jan 1, 1957

By C. G. Dunn, F. W. Daniels

IN recent publications1-5 the existence and behavior of subgrain boundaries in high-purity metals has been clearly brought to light. Lacombe and Beaujardl by means of special etching methods disclosed in polycrystalline sheets of aluminum the existence of substructures differing in orientation by small amounts (about 1/4"). Boundaries of these structures at relatively high temperatures had the remarkable property&apos; of moving about while the ordinary boundaries remained stationary. Cahn2 also observed substructures in bent and annealed single crystals of aluminum, zinc, magnesium, and rock salt. The position of subboundaries could be explained in terms of a dislocation mechanism of polygonization in which dislocations move into lines at right angles to the bent glide planes thereby relieving elastic stresses in these planes. Guinier and Tennevin8,6 disclosed the further interesting feature that polygonized structures coarsened significantly upon prolonged annealing. Somewhat similar subgrain phenomena have been observed in silicon iron of commercial purity. Although some evidence for the development of macro-mosaic structures in silicon iron already has been reported by one of the authors6,7 under the phenom-enological term "crystal recovery," much better evidence recently has been obtained due to improved etching techniques. In addition, phenomena regarding structural changes have been uncovered. The present investigation is divided into three parts: (1) The phenomenon of Laue spot sharpening on annealing cold-rolled crystals, (2) the phenomena of polygonization and subgrain coarsening The material used in the present investigation was high-grade commercial silicon iron sheet of nominal composition, 3.3 pct Si, 0.004 C, 0.011 P, 0.010 S, 0.04 Mn, 0.01 Al, 0.04 Cu, 0.01 Sn. Large single crystals of this material Were prepared for cold-rolling or bending as scheduled. Cold-rolling of 12 pct was carried out on a laboratory 8-in, diam rolling mill. The bending deformations were performed by pressing the crystals between a solid Fig. 2—lllustrative foue patterns to show Laue spot sharpening. a (Left)—Specimen as cold rolled, b (right)—After 48 hr at 1400°C. round bar and a mating half cylinder, both heavily greased. Individual specimens were cut from the deformed crystals, and the cut edges were deeply etched prior to annealing. Laue photographs were made using 40-kv tungsten radiation. The technique used to disclose the various subboundaries was an electropolish and electroetch in a bath of chrome-acetic acid.&apos; The anodic polishing done at 22 v was immediately followed by etching at a reduced voltage, which was dependent upon the nature of the subboundaries. Phenomenon of Laue Spot Sharpening on Annealing Cold-Rolled Crystals Fig. 1 gives the initial and final orientations of the specimens cold-rolled 12 pct. Each specimen was annealed at a temperature and for a time which caused significant structural changes as evidenced by alterations in Laue patterns. Representative Laue patterns and micrographs showing the essential changes are given in Figs. 2, 3, and 4. The essential points to be derived from these illustrations follow: 1. Annealing at 950°C clearly develops a substructure with the orientation of the cold-rolled specimen. 2. The subboundaries formed obviously separate regions of nearly the same orientation. Some of the subboundaries appear as a sequence of dots similar to those observed in aluminum by Lacombe and Beaujard,&apos; but whether this is due to extremely small differences in orientation is not known at present. 3. The substructure coarsens upon prolonged annealing. 4. Prolonged annealing also causes a decrease in orientation spread according to Laue spot sharpening&apos;

Jan 1, 1952

By Molly Gleiser

The standard free energies of formation of some gaseous metal oxides together with those of their condensed oxides have been plotted against temperature. The heats of formation of the gaseozcs oxides are tabulated. An explanation is given of the use of the data to predict the importance of the gaseous metal oxides at high tenzperatures. RECENT mass spectrometric work1 has resulted in the detection of several hitherto unknown gaseous oxides and the measurement of their free energies of formation. Of especial interest is the fact that several of the refractories in common use either as crucibles or furnace tubes, and metals used in Knudsen cells and in furnace windings, have been found to have one or more stable gaseous oxides. In view of the present emphasis on high-temperature techniques, the development of vacuum metallurgy.z heating by electron bombardment and plasma jets, and the resultant shift to ever higher temperatures, it is no longer possible to plan experiments without taking into consideration the significance of the presence of these gases in the system, the reactions they undergo. and their contribution to the vapor pressure. A good example of what went wrong in earlier work, when the existence of these gaseous molecules was not yet known, is presented by the work of Hoch, Nakata, and Johnston. Hoch and coworkers attempted to measure the vapor pressure of solid ZrO2 by letting the vapor in equilibrium with zir-conia effuse from a tantalum Knudsen cell. The free energies of formation of solid zirconia and tantala are such that a short calculation showed that the reaction

Jan 1, 1962

By Richard J. Borg

The vapor pressure of Cd in equilibrium with CdSb in the presence of excess Sb has been measured using the Knudsen effusion method over the temperature range 276° to 379°C. The free energy of formation of CdSb is given by AF° = -1.58 + 1.53 x l0-4 T, kcal per mole. The enthalpy and entropy are obtained from the temperature coefficient of the .free energy. CADMIUM and antimony have almost imperceptible mutual solid solubility but form a single stable intermediate phase, CdSb. This phase, according to Han-sen,l extends from about 49.5 at. pct to 50 at. pct Cd at 300°C and has the orthorhombic structure. The free energy of formation of CdSb can be calculated from the vapor pressure of Cd for compositions which contain less than 49 at. pct Cd. The appropriate reaction and formulae are given by Eqs. [I] and [2]- CdSb(s, ~ Cd(g)-, +Sb(s) [1] Since Sb is in its standard state, Af - N,,AF&apos;-,, = NcdRT In a,, = NcdRT InP/PO [2] In Eq. [2], P, is the vapor pressure of Cd in equilibrium with the alloy, and Po is the vapor pressure in equilibrium with pure solid Cd. It is implicit in this calculation that the free energy only slightly changes within the narrow limits of the single phase field. Thus, the value obtained from the antimony-rich boundary is truly representative of the stoi-chiometric compound. The results reported herein are obtained from a mixture near the eutectic composition, i.e. 59 at. pct Sb. Only two previous investigations" of the free energy of formation of CdSb have been made. Both relied upon the electromotive force method, and measurements were made over relatively narrow temperature ranges which strongly influences the reliability of the values of AH and aS. EXPERIMENTAL The eutectic composition is prepared by fusing reagent grade Cd and Sb by induction heating in vacuo with the starting materials held in a graphite crucible having a threaded lid. The material obtained from the initial melt is pulverized, sealed under high vacuum in a pyrex capsule, and annealed at 420°C for two weeks. X-ray analysis"gives the following lattize parameters: a = 6.436A, b = 8.230& and c = 8.498A using Cu Ka radiation with A = 1.54056. These values are in fair agreement with the result? previously reported by Al~in:4 i.e. a = 6.471A, b = 8.253A, and c = 8.526A. Vapor pressures are measured using an apparatus which has been described elsewhere,= however, with a single important modification. Knudsen effusion cells are made of pyrex with knife-edged orifices made by grinding the convex surface of the lid on #600 emery paper. Photographs taken at known magnifications using a Leitz metallograph enable the determination of the orifice area. Numerous calibration measurements of the vapor pressure of pure Cd give close agreement with values previously reported5,= thus indicating that no significant error can be ascribed to the substitution of glass cells for metal cells used in previous work. Because the vapor pressure of Cd is reliably established and because it is difficult to obtain Clausing factors for the glass cells, the final values used for the orifice areas are calculated from the calibration measurements of the vapor pressure of pure Cd. Effusion runs are started in an atmosphere of purified helium which is quickly evacuated as soon as the cell attains thermal equilibrium. Less than one minute is necessary to obtain high vacuum after evacuation begins, and the temperature seldom varies by more than 0.5oC from the value obtained prior to pumping out the helium. RESULTS The results of this investigation along with other pertinent data are tabulated in Table I. Fig. 2 is the familiar graph of log P against T-10 K. At least mean squares analysis of the data presented in Table I yields the following equation: log1DJP = 8.790 - 6472 x T"1 [3] The deviations of the individual measurements from the values calculated with Eq. 131 are given in column six of Table I; the average deviation is 4.0% of the calculated value. Although the partial molal properties change significantly with composition within the single phase region, the integral thermodynamic value should remain relatively constant. Hence the results of the following calculations, which use the data obtained for the eutectic composition, are probably representative of the equi-atomic compound. Eq. [4] describes the vapor pressure of pure Cd as a function of temperature and may be combined with Eq. [3] to

Jan 1, 1962

By Molly Gleiser, John Chipman

The standard free energy of formation of WC was obtained from determination of the equilibrium WC + CO2 = W + 2CO between 1215° and 1266°K. Its uallie is -8340 * 300 cal Per mole over the above range of temperature. AS a part of a program devoted to measuring the stabilities of the carbides, a study was made of the free energy of formation of tungsten carbide, WC. The homogeneity range of this compound is very small,&apos; and it is generally accepted and is dealt with here as a stoichiometric compound. The heat of formation, ?H°f, of WC has been accurately measured by Huff, Squitieri, and snyder.2 The only attempt, however, to measure the free energy of formation of this compound was made by Schenck, Kurzen, and wesselkock3 who brought tungsten carbides into equilibrium with H2 and CH4. Unfortunately their results are not sufficiently accurate nor consistent enough to permit the calculation of free energies. METHOD Heating mixtures of tungsten and carbon powders in hydrogen for 4 days at 1050°C led to formation of some WC without any trace of W2C. It was deduced, therefore, that at least below this temperature W2C will not be formed during experiments with mixtures of tungsten and WC. This was subsequently shown to be correct. The method chosen was the measurement of the equilibrium of the reaction

Jan 1, 1962

By J. W. Evans

ONE of the most important and frequent calculations that the extractive metallurgist is called upon to make is that of the standard free energy change of a reaction (?F°). For many reactions of metallurgical interest, the lengthy arithmetical calculations have been eliminated by the use of free energy-temperature diagrams which have been constructed by Ellingham,1 Richardson and Jeffes,2 Kellogg,3 and Osborn4 (e.g., for oxides, sulphides, halides) from critical surveys of existing data. The speed and simplicity of making calculations with these graphs make them of great practical value and, this should be stressed, in the majority of cases no greater accuracy is obtained by the individual calculations from specific heat data, entropies, and heats of reaction. With the increasing industrial application of vacuum methods to the winning of metals, notably at present magnesium and the alkaline earth metals, it is necessary to calculate low metal vapor pressures above reaction mixtures. The existing free energy diagrams usually give values where the solid and liquid metals are at unit activity. To obtain the free energy change associated with the reaction Metal (solid or liquid) = Metal (gas) it is customary to calculate this from either vapor pressure equations or from the appropriate free energy functions. This paper presents graphically the free energies of vaporization of a number of metals of economic importance which can be used in conjunction with other free energy diagrams. Certain metals have been excluded on the following grounds: titanium, tungsten, molybdenum, and platinum have very high heats of vaporization and boiling points and the uncertainty of these values arising from difficulties of high temperature measurements makes free energy values of doubtful accuracy; the data for cobalt, vanadium, and zirconium are uncertain; finally, arsenic, antimony, and bismuth could not be conveniently included. because of the presence of mixtures of polyatomic and mona-tomic vapors in the temperature range considered. Free Energy Diagram In Fig. 1, the standard free energies of vaporization per mol (?F°T) have been plotted for the temperature range 0" to 2000°C for the reaction M (solid or liquid) = M (gas) The data have been obtained from the free energy functions — (F-H298)/T for the solid, liquid, and gaseous elements and the heats of vaporization at 298°K, i.e., ?H298 (vapor). The values of these functions have been taken without change from the recent critical survey by Brewer;&apos; the bulk of this data is from Kelley7 with adjustments in the light of more recent work. Values of the function — (F-H298) /T at T = 298°, 500°, 1000°, 1500°, and 2000°K were employed. Where possible, a further independent value was obtained by using the boiling point, i.e., where ?F°T = 0. All calculations are based on the assumption that the metal vapors are monatomic and that the boiling points refer to those temperatures at which the partial pressure of the monatomic vapor above the metal is 760 mm. For the alkali metals, e.g., sodium, potassium, and lithium, diatomic gas molecules are present as minor species; details of these are discussed by Brewer." On the basis of the above values and allowing for the change in slope at the melting point, straight line graphs were constructed and extrapolated to 2000°C. The deviation from a straight line did not exceed ±500 cal, which in all cases appears less than the probable error in the ?F°T values.

Jan 1, 1954

By G. H. Turner, R. C. Bell, E. Peters

Zinc oxide activities in a typical lead blast furnace slag have been calculated from plant operating data. These activities were used to assess the probable effect of fuel composition, oxygen enrichment, and air preheating on the efficiency and capacity of the slag-fuming operation. THE physical chemistry of zinc fuming has been examined with three objectives in mind: 1—to predict conditions favorable to increasing furnace capacity, 2—to predict the changes required to fume zinc more economically, and 3—to explain reported differences in the efficiencies of various slag-fuming plants. This study, made at ail in the plants and laboratories of The Consolidated Mining and Smelting Co. of Canada Ltd., developed from a program undertaken some three years ago on behalf of the AIME Extractive Metallurgy Div. subcommittee on slag fuming. Lead metallurgists first became interested in the recovery of zinc from lead blast furnace slags in 1905 and 1906. An excellent review of the early experimental work has been made by Courtney,&apos; who described blast furnace, reverberatory furnace, and converter methods of fuming zinc from slag. Some of the investigators did not appreciate the importance of reducing the zinc oxide content of the slag to metal in order to fume it, since they tried compressed air blast without fuel in their earliest attempts. However, by 1908, the importance of reducing the zinc was established.&apos; In 1925, the Waelz process for the recovery of zinc oxide from oxidized zinc ores was developed in Germany.&apos; This process was not readily adaptable to lead blast furnace slags because of the difficulty in handling fusible charges in a kiln. What appears to have been the first slag-fuming operation as it is known was commenced by the Anaconda Copper Mining Co. at East Helena, Mont. in 1927." The first Trail furnace was completed in 1930, and this was followed by the construction of several other slag-fuming plants. During the period in which slag fuming has been extensively employed, little development of the chemistry of this process as a whole has taken place. Several good papers on the petrography of lead blast furnace slags have been published,""= but these studies could do little more than establish the forms in which lead and zinc occur in the initial charge and final products of the slag-fuming operation. In recent years, zinc-smelting problems have been ap- proached from a thermodynamic point of view. Maier has published an excellent thermodynamic treatment of zinc smelting." The important thermodynamic properties of zinc and its compounds have been determined and checked by other investigators.&apos; However, to the best of the authors&apos; knowledge, no thermodynamic treatment of the fuming of zinc from slag has been published. A thermodynamic study of any process requires that the essential chemistry of that process be known. In slag fuming there appear to be some differences of opinion as to whether the active reducing agent is elemental carbon or carbon monoxide. Furthermore, some observers have noted that high volatile coals appear to be more efficient than low volatile coals, indicating that hydrogen is also an important factor in the reducing efficiency of a fuel. That both hydrogen and carbon monoxide are effective reducing agents for the zinc oxide content of lead blast furnace slags can be demonstrated readily by introducing these gases into a slag bath held in a neutral vessel at 2100°F (1150°C). Elemental carbon also will reduce zinc oxide, but it is improbable that much free carbon is available for reduction of zinc, as the reaction between the finely powdered coal and air should be largely completed before the solid coal particles reach the slag. Some large-scale fuming experiments using gaseous hydrocarbons have been carried out by other investigators, but, as far as is known, these have not been developed yet into operating processes. The thermodynamic treatment in this paper is based on the following reactions: 1—to supply the thermal requirements C+V2O2- CO [1] C + 0,-CO, [2] H2+ ~z0,-H,O 131 and 2—to reduce ZnO ZnO + CO + Zn + CO, c41 ZnO + H, e Zn + H,O. [51 The furnace-gas composition also is controlled by the equilibrium constant of the familiar water-gas reaction H,O + CO + CO, + H2. C6l In order for the thermodynamic calculations to be quantitatively applicable, it is necessary that the chemical reactions to which they are being applied

Jan 1, 1956

By M. H. Caron

BASIC U. S. Patent 1,487,145 on ammonia leaching of nickel ores was issued to the author on March 18, 1924. Equivalent patents in other countries were obtained later. The Dutch Syndicate Brikcarbo became interested in the process in 1935; and a couple of years later the late Dr. H. Foster Bain sent samples of Surigao laterite iron ore to Delft and witnessed tests made there on this material for the Philippines Commonwealth. As a result, the author was asked in April 1940 by Dr. Bain to go to the Philippines to erect and take charge of a pilot plant for the process. The World War prevented carrying out this proposal. The Dorr Co. also became interested in the process at about the same period. The investigations by the Freeport Sulphur Co. on the process as applied to the Cuban nickeliferous laterites, which resulted in the Nicaro enterprise, and the results of this operation have been well described elsewhere.1,²,³,4,5 This Nicaro plant was, in operation for almost two years, and during this period produced about 10 pct of the world nickel production from laterites containing 1.35 pct nickel. This plant and its operation were war measures and, in view of this, activities were suspended in April 1947. The results obtained fully demonstrated the technical feasibility of the process and its economical aspects on a commercial scale. In this respect, it should be understood that it is probable that improvements may be made by further development, and that there are possibilities for advantageous application of the process to garnierite and similar ores with higher values in nickel than the laterite iron ores at Nicaro. While the articles cited above have given a certain amount of information, no general article containing all the important process data has been pub- lished. Since the process is of more than local interest, a fuller knowledge of the fundamental and practical factors of the method may be welcome to those interested in this new field of metals technology. The author, accordingly, takes pleasure in submitting this article to the AIME as it represents in a condensed form the results of many years of research. The brief outlines of the fundamental and other factors and the explanation of observed phenomena are presented with as little discussion of details as possible, consistent with clarity. It is a special satisfaction to the author to make some contribution of his own in return for the benefits of the many valuable publications issued by the Institute during his thirty years of membership. Ores Adapted for Ammonia Leaching: All nickel and cobalt ores which originate from weathering of peridotites or similar basic rocks having sufficient values are suitable for treatment by the ammonia leaching process after a preliminary reduction under proper conditions. The formation of these deposits was probably as follows: In the course of time the basic rocks were attacked by atmospheric agencies; MgO and SiO2 were gradually leached out, and secondary nickel minerals formed, such as garnierite, a hydrated silicate of nickel and magnesia. These secondary products are, however, not stable. They decompose in a further stage of weathering and ultimately only a relatively small residue of insoluble oxides remains, known as laterite iron ore with a small nickel content and very little cobalt. Under these mantles of laterite, richer nickel values may be found, usually indicated by the occurrence of garnierite. The more the ore is disintegrated by nature, the higher the iron content and the better the nickel extractions that may be expected therefrom. Table I shows extractions that may be expected from different types of ores, assuming treatment of -200 mesh products and that all precautions have been taken for obtaining maximum extractions. As for the distribution of the various nickel minerals and compounds that may be present, great variations may occur from locality to locality as well as vertically in a deposit. From such "run of

Jan 1, 1951

By M. H. Caron

D. C. Ralston—The fact that none of the organizations that have worked on these ammoniacal leaching processes have contributed discussion of Mr. Caron&apos;s papers today is a matter of some disappointment. Adaptations, modifications and improvements have been made by several organizations or individuals and to complete the record I want to document a number of them. The Nicaro Nickel Co. operated a Government owned plant at Nicaro, Oriente, Cuba, during the past war. A report on the project was written for Reconstruction Finance Corp. and is in the document file collected by the Office of Technical Services, Commerce Department and filed with the Library of Congress, where it can be consulted or bibliofilm or photostat copies obtained by asking for copies of PB 97271. Nicaro Nickel Co. has obtained a series of U.S. Patents, my list (probably incomplete) of which bears the following numbers: 2,400,098; 2,400,114; 2,400,115; 2,400,461; 2,400,612; 2,458,902 and 2,473,795. International Nickel Co. has also studied the problem and U.S. Patent 2,478,942 shows that some of the complications involving occasional low extractions have been unraveled. Forward, Samis, and Kudryk, of the University of British Columbia, have also published a study of copper-nickel sulphide concentrate.&apos; Others are interested and it is evident that this type of hydrometallurgy is likely to find a happy application in the not-too-far distant future. Caron&apos;s two papers practically amount to a summation of his life&apos;s work on the important subject of nickeliferous iron ores and the American Institute of Mining and Metallurgical Engineers is fortunate to have been chosen the medium of publication. M. Rey—The ammonia leaching process has been the subject of certain studies in New Caledonia, but at the present time, the conditions are not very favorable to its adoption. The process is a combination of a thermal and a hydrometallurgical process. As a result, the first costs and the operative costs are rather high. To counteract this unfavorable situation, it would be necessary to make a very high extraction. But unfortunately, the process is delicate and in spite of all of Caron&apos;s valuable work, there are still many unknown factors. It is difficult to obtain regularly a high extraction, exceeding 75 to 80 pct. It would be interesting to have the opinion of Inter-national Nickel on the process and to know what the Dutch are doing in Celebes. M. H. Caron (author&apos;s reply)—I am quite familiar with the different types of nickel and cobalt ores as found on New Caledonia, and it may be pointed out that the Celebes ores are quite the same in their properties. Their behavior when treating the ores by the ammonia-leaching process is also alike and in my opinion, there is no reason why a high extraction of the New Caledonian ores could not be obtained if the process is properly applied. For the sake of completeness I may add that one of my patents has not been discussed in the papers. This patent deals particularly with the treatment of serpentine nickel ores. (Netherlands No. 62693 40a, French No. 965.786 April 21. 1948. and Cuban No. 13.625 Jan. 1950.)

Jan 1, 1951

By J. H. Rushton, L. H. Mahony

Principles of fluid motion and turbulence which have been found to be of use in mixing and agitation problems are discussed, as well as suggested applications in extractive-metallurgy processes. Various types of impellers are described, together with other conditions that affect flow pattern and turbulence. The choice of equipment for particular requirements is considered, and equations for power input are given. Modern heavy-duty mixing and agitation equipment can take an increasingly important part in such extractive-metallurgy processes as solids handling, crystallizing and leaching, chemical operations, and flotation. Application of mixing and fluid-mechanics principles to extraction methods can lead to greater process rates and a resultant saving in time and money. MIXERS are being applied with increasing frequency to problems in the metallurgical industries. The increase represents in part the modernization of mechanical equipment used through the application of unitized drives, modern electric motors and speed reducers, and recently developed materials of construction. Some applications have resulted from process changes and the use of techniques for operations similar to those that have been demonstrated and proven in the chemical industry. Still more applications are being developed through the use of fluid-dynamics principles not previously recognized as applicable to these operations. It is the purpose of this paper to describe those principles of fluid motion and turbulence which have been found to be of use in mixing and agitation problems, and to suggest applications for them in the extractive-metallurgy processes. Modern mixing equipment has been designed to provide the fluid motion consistent with that best suited to different operations.&apos; When properly applied, these more efficient fluid-handling mixers result in lower process-production costs. Metallurgical operations usually involve large amounts of solids. The characteristics of the ore control the process and only enough liquid is added to provide sufficient fluidity for handling and processing. The reactive part of the ore, the mineral value to be extracted, is likely to be low in percentage, and the quantity of reagent required is similarly low, but excessive dilution makes additional reagent necessary and therefore is undesirable. Thus, the primary problems in minerals processing are to handle as high a concentration of solids as possible and to distribute reagents uniformly. These pulps, or slurries, are in a range of solids concentration where hindered settling rates apply, and care must be taken to agitate and mix sufficiently to maintain suspension and flow throughout the equipment. Such slurries have high densities which are the weighted average of the components and viscosities that are spoken of as "effective viscosities" but are difficult to evaluate. It is convenient to separate metallurgical operations involving mixers and agitators into three categories: solids handling, mechanical or physical operations, and chemical operations. In each of these categories fluid motion is required to maintain suspension, to distribute surface-active agents, to blend components and reactants, and to induce high rates of chemical reaction. After a discussion of some basic principles of mixing and agitation, examples of application to the three categories will follow. Fluid Motion The fundamental problems of mixing and agitation of liquids have to do with the mechanics of fluid streams and the means by which they are

Jan 1, 1955

By D. R. Spink

In the preparation of zirconium and hafnium metals, there are many indications that impurity levels control the physical and chemical properties of the metal. The purpose of this work was to develop methods of producing pure raw materials that could be reduced to highly pure metals. Early work by the Carbomcndum Metals Co. and others indicated that certain fused salts were highly efficient in the removal of impurities from gaseous zirconium tetrachloride. We have developed workable fused salts along with a continuous and higly efficient scrubber design which can be used to produce very pure zirconium tetrachloride. Metal made from the purified tetrachloride has been shown to approach crystal bar metal in purity. Scrubber designs are discussed with recommended materials of construction. VARIOUS methods have been used to purify zirconium (and hafnium) tetrachloride. Most of these methods involve thermal degassing initially (the removal of more volatile compounds at temperatures below that where zirconium tetrachloride exhibits a significant vapor pressure) followed by a sublimation step (which conveniently leaves the nonvolatiles behind.) While these procedures effect definite purification, such processing is batchwise and does not result in optimum purification. Early work by The Carborundum Metals Co. and others indicated that fused salts were highly efficient in the removal of impurities from gaseous zirconium tetrachloride. The objective of this work was to develop a continuous fused-salt scrubbing process that would yield high-purity zirconium and hafnium tetrachlorides. The term "fused salt" refers to the molten state of ionic compounds and as used here, specifically refers to alkali metal and alkaline earth halides. Fused salts, because of their many valuable properties, are becoming increasingly im- portant industrially. These valuable properties of the fused salts are: 1) stability at elevated temperatures; 2)low vapor pressure; 3) low viscosity; 4) ability to dissolve many different materials; and 5) good elctctrical conductivity. All but the last property enhances the use of fused salts as scrubbing agents for zirconium and hafnium tetrachlorides. Fused-salt scrubbing may be defined for our purpose as the intimate contact between a gaseous compound and a molten salt with the purpose of removing impurities from the gaseous compound. In this case, the gaseous compound is zirconium tetrachloride which submlimes at 331°C. When this gas is contacted with a molten salt, impurities such as aluminum, iron, and titanium are removed and the resulting product is considered fused-salt scrubbed. Zirconium and hafnium are sold to a purity specification. Generally speaking, normal production without scrubbing is capable of meeting specifications. There are, however, several considerations That make the knowledge of methods of additional purification highly desirable. These are: 1) the control of product analysis; 2) the production of a pure product for special applications; 3) the salvaging of off-specification material; and 4) the use of raw materials with higher impurity levels than 1 he present raw materials. You will note that items 1 and 2 are somewhat complementary to each other and that item 4 assumes that The present process has impurity removal limitations. To better understand the part that fused-salt scrubbing of zirconium tetrachloride plays in the manufacture of zirconium, Fig. 1 contains an illustrated flow sheet of the industrial production of zirconium metal. In referring to Fig. 1, we can point out the specific benefits derived from our ability to purify zirconium tetrachloride. Purification of the crude (hafnium-containing) zirconium

Jan 1, 1962

By C. Norman Cochran, James L. Brandt

ALTHOUGH gas in aluminum and its effect on aluminum products have been the subject of a number of papers, not many quantitative determinations of the hydrogen content of solid aluminum and its alloys have been recorded in the literature. For solid aluminum samples, four investigators have reported hydrogen contents which appear reasonable compared with the hydrogen solubility of 0.7 ml per 100 g, STP, in molten aluminum at 660°C established by Ransley and Neufeld&apos; and verified by Opie and Grant&apos; and Ransley and Talbot. Sloman," who used a vacuum fusion procedure, reported the hydrogen content of some high purity aluminum as 0.66 ml per 100 g, STP. Griffith and Mallett, employing the tin fusion method, reported the internal hydrogen content of six different aluminum alloys as ranging from less than 0.1 ml per 100 g, STP, for 1100 alloy to 0.7 ml per 100 g, STP, for 4043 alloy (previously 43S, a 5 pct Si alloy). Eborall and Ransley," using a solid extraction of the gases at 600°C, reported hydrogen contents ranging from 0.1 ml per 100 g, STP, to 1 ml per 100 g, STP. Ransley and Talbot reported that several thousand analyses on 99.2 pct and higher purity aluminum as well as Duralumin type alloys indicated hydrogen contents ranging from 0.1 ml per 100 g, STP, to 0.5 ml per 100 g, STP.

Jan 1, 1957