Search Documents

By A. R. Troiano, E. A. Steigerwald, F. W. Schaller

D. N. Williams(BatteZle Memorial Institute)-The authors have presented an extensive collection of arguments pertaining to the role of stress in hydrogen embrittlement. The basic assumption of these arguments is that stress is essential as a driving force for diffusion of hydrogen. However, in view of the rapid diffusion rate of hydrogen in steel at low temperatures as evidenced by the ability to alloy with hydrogen by electrolytic charging, it seems unlikely to me that stress acts in this manner. Instead, I would like to suggest that stress may be essential for the nucleation of hydrogen in steel. I believe that such an assumption would equally well satisfy the experimental data presented by the authors. I should also like to comment on the interpretation of the data presented in Figs. 5 and 6. Fig. 5 shows the effect of hydrogen content on ductility in a rupture test. The curve as drawn by the authors indicates an abrupt transition from ductile to brittle behavior at about 0.001 amp per sq in. (5 ppm). The data points would equally well support a gradual transition from ductile to brittle behavior extending over the range from 0.0008 to 0.02 amp per sq in. (4 to 8 ppm). A gradual transition would be the ex-

Jan 1, 1962

By John L. Miles

John L. Miles (Arthur D. Little, 1nc.)—Pollack and orris" have reported measurements on electron tunneling through A1-A12O3-A1 sandwiches in which the oxide was formed by gaseous oxidation in a glow discharge. From these measurements they deduced the asymmetry of the barrier and, since this is small, conclude that the mechanism suggested by Mott19 for the growth of oxide in thin A12O3 films is inapplicable. In earlier papers20 Pollack and Morris report similar work for oxide films grown thermally. In this case they find a greater asymmetry and conclude that the Mott mechanism is valid. I would like to point out that both these conclusions are quite unjustified. Mott suggests that the growth of the oxide film on aluminum results from the passage of ions through the already present film of oxide under the action of an electric field. This field results from a constant voltage which is in effect a contact potential between metal on one side of the barrier and adsorbed oxygen ions on the other side of the barrier. The theory does not require that the oxide grown is nonuniform either in stoichiometry or structure. It does however specifically assume that the partial layer of ionized oxygen on the surface remains adsorbed on the surface of the growing oxide. In other words, the so-called "built-in field" remains in the oxide only as long as the ionized oxygen is present. When a counter electrode of aluminum is deposited on the oxide, it will react with the adsorbed oxygen on the surface of the oxide, thus forming a small additional amount of oxide. It is clear, then, that there is no requirement in the Mott theory of oxide growth which would necessitate tunneling currents through an Al-A1203-A1 sample to be different when the polarity is reversed. Neither does the theory eliminate the possibility that some additional mechanism could cause the tunneling barrier to be asymmetric and hence tunneling currents to be a function of polarity in such a sandwich. Thus these tunneling-currents measurements are not germane to the question of whether the Mott mechanism is the true method of growth of aluminum oxide films. In fact, it is not surprising that there should be a difference between the oxide properties at the two interfaces (with resulting asymmetry in the tunneling barrier) since the growth conditions and growth rates must have been quite different at these two positions. S. R. Pollack and C. E. Morris (authors' reply)— The point raised by Miles above is one has caused some confusion in the past. The following is an attempt to clarify this point. The built-in field which is responsible for the growth of the thermal oxide at low temperatures arises, according to Mott, because of the passage of electrons from the Fermi surface of the oxidizing metal to surface states introduced by the adsorbed oxygen. It is assumed that the energy of these surface states lies below the Fermi energy of the metal. Electrons therefore continue to flow from the metal to the surface until the built-in electric field raises the potential energy of the surface states to the value of the Fermi energy in the metal, at which time equilibrium is obtained between the surface states and the metal. That is in equilibrium as many excess electrons pass from the metal to the surface per unit time as vice versa. The surface of the oxide prior to deposition of a metallic counterelectrode can then be pictured as follows. The Fermi energy lies in the energy gap of the oxide and is essentially pinned at the energy of the oxygen surface states. The vacuum work function of the oxide is then given by the sum of the electron affinity of the oxide (i.e., the difference in energy between the vacuum and the conduction-band minimum) plus the energy difference between the conduction-band minimum and the Fermi energy. The deposition of a metal onto the surface of the oxide can result in a transfer of electrons across the extremely thin oxide only if there is a contact potential difference between the deposited metal and the parent metal or oxide. That is if the vacuum work function of the deposited metal differs from that of the parent metal, then charge can be redistributed across the oxide in order to equilibriate the Fermi energy across the structure. (It should be

Jan 1, 1965

By Joachim J. Hauser

William F. Hosford, Jr. (Massachusetts Institute of Technology)—Dr. Hauser has used a very interesting method to study the interaction of dislocations on different slip systems, but it should be pointed out that the analysis of the experiments is subject to a serious criticism. He states that "the effect of the compression can be adequately described by one slip system." The effect of frictional constraint during the compression makes this quite unlikely. When a block of metal is compressed its lateral expansion requires a sliding of the metal over the compression platens. The role of friction in the interface between the deforming metal and the platens is to increase the normal force required for the compression. Analyses1213 have shown that, in general, the additional force, p, required for the compression is a function of l/h where is the coefficient of friction, I is the length of the speci- men in contact with the platens. For a constant COefficient of friction, isho' shows that P should increase exponentially with pl/h for both plane strain and axially symmetric compression. For a compression specimen, Fig. 7, whose cross section perpendicular to the compression axis is a rectangle whith one dimension L, much larger than the other W, a much larger force would be required for appreciable flow parallel to L than for flow parallel to U7. Therefore lateral strain in the W direction, EW, should be much greater than the lateral strain in the L direction EL. Since L/H = 14.5 for Dr. Hauser's crystals, and since no lubrication was used, it seems questionable that appreciable lengthening of the crystals could occur. Because the theories of frictional constraint have been derived for isotropic polycrystalline materials, it was decided to make experimental measurements on a single crystal. A section 3.590 in. long was sawed from an aluminum single crystal with a square section of 0.249 in., so that L/W= 14.4. This crystal was tested in compression between dry ground steel platens. Fig. 8 shows the orientation of the crystal and the axis of compression. The face for compression was chosen so that the operation of the single-slip system which would be predicted in the absence of friction would lead to a larger strain in the length direction than in the width direction. The dimensional changes of the width and length as well as the height were measured frequently during the compression with micrometers. Width strains were calculated from the average of readings near each end and at the center. A plot of the length strain, EL, against the width strain E w is given in Fig. 9. The slope indicates that the EL amounted to only 2.5 pct of cw. Other compression tests on similar crystals with shorter lengths also showed severely limited elongation. Even for a crystal with L/W = A.0, EL was only about 26 pct of cw. Because of the frequent interruptions of the tests for dimensional measurements should have decreased the frictional constraint by allowing a reseating of the platens, even smaller elongations under continuous testing seem probable. These tests on long narrow crystals show that essentially plane strain conditions prevailed. We may assume that Dr. Hauser's crystals deformed similarly. That the compression can be described by the

Jan 1, 1962

By I. L. Dillamore

I. L. Dillamore (University of Birmingham)—The different textures developed in various fcc metals have long awaited satisfactory explanation and it has now become clear that these differences are related to parallel differences in the deformation characteristics of the metals. Liu is correct, therefore, in seeking to account for the observed textures in terms of the flow mechanisms but I believe, for the reasons outlined below, that the particular interpretation of flow mechanisms proposed by Liu is open to substantial objections. By considering the forty-eight possible designations of the twelve octahedral slip systems found in fcc metals as distinct and separate deformation modes, Liu has fallen into the error of assuming that only positive glide dislocations associated with each system are present. In fact both positive and negative dislocations will be present and the only difference between for instance the systems B4 and B4' (in Liu's notation) is that under a stress of given sign the direction of motion of a dislocation is reversed on changing from B4 to B4'. For both orientations positive and negative dislocations will be present. In considering possible dislocation interactions it is, therefore, inadmissible to differentiate between R4 and R4' as Liu does. Liu considers those dislocation interactions which give the biggest reduction in energy to be the most favorable and neglects, on the grounds that they will form strong barriers to slip, interactions between dislocations with perpendicular Burgers vectors. Setting aside interactions between positive and negative dislocations of the same slip system, which must occur regardless of the combination of slip systems chosen, the biggest reduction in energy occurs for the Lomer-Cottrell interaction and it is Lomer-Cottrell barriers which are thought to provide the stronger dislocation obstacles. On the other hand the intersection of dislocations with perpendicular Burgers vectors is thought to be a low-energy process which contributes only a fairly small temperature-dependent part of the total work hardening. On this basis it seems doubtful whether the reduction in energy through possible dislocation interactions provides a reasonable criterion for choosing the operative slip systems. From the point of view of texture development it is unsatisfactory to ignore the slip rotations leading to an end position and to neglect to consider the stability of the chosen end point. It is also unsatisfactory to treat the two stress axes as interchangeable since, if the stress system is idealized as biaxial, one stress is compressive and the other is tensile. For the same reason the rotations of the two stress axes are not made compatible simply by assuming that the same slip directions are responsible for the rotations of the two stress axes. It is, in short, essential to treat the two stress axes as acting together on the same slip systems. Turning to the question of the difference between the copper-type and the brass-type texture, there now remains little doubt that the difference is attributable to differences in stacking-fault energy (y), as noted by Liu, but it is doubtful whether the temperature dependence of the texture in copper and in silver is due to increasing stacking-fault energy with increasing temperature. The results of Swann and Nutting42 cited by Liu were obtained in Cu-A1 alloys and the apparent increase in stacking-fault energy on raising the temperature may be influenced by short-range ordering. In pure metals such effects are absent and the only data available on the variation of y with temperature are those of Buhler et a1.43 for silver. They report a minimum at 200°C which does not fit the hypothesis put forward by Liu. It is much more likely that thermal activation of cross slip is important in determining which texture develops, as proposed by Dillamore and tors. These workers have proposed an explanation for the differences in observed texture among the fcc metals and the pole figures predicted consist of an orientation spread which is in better agreement with observation than the limited number of discrete orientations suggested by Liu. The theory of Dillamore and Roberts is also able to account for the differences between aluminum and copper which Liu still leaves unexplained. Y. C. Liu (author's veply)—The writer appreciates the interest of Dr. Dillamore, but must discuss some of his comments in order to avoid cross purposes. The phrase, "forty-eight slip systems," which appeared twice in the text—in the caption of Fig. 1 and the first paragraph in the Discussion—might unfortunately have led Dr. Dillamore to disagree

Jan 1, 1965

By I. R. Kramer

A delay time for yielding in cold-worked face-centered-cubic metals was found. Slip on (123) planes was observed. Glide on these planes occurred during the delay-time period before slip starts on the (111) planes. AN important approach to the study of the anchoring and blocking of dislocations is available through the delayed-yield phenomenon which has been observed in body-centered and hexagonal close-packed metal by several investigators. Clark and his associate1-5 showed that a delay time for yielding is present in mild steels and fine-grain molybdenum. Type 302 stainless, SAE 4130 normalized, SAE 4130 quenched and tempered, and 24s-T aluminum aid not have a delay time. Kramer and Maddin6 studied the delay-yield effect. in metal single crystals. While they found a delay time in body-centered-cubic metals none could be found in the face-centered-cubic metals. Later7 a delay time was found in hexagonal close-packed metals. cottrell8 has proposed an explanation for the difference in the yield phenomena of b.c.c. and f.c.c. metals based upon the anchoring of edge dislocations by the proper types of impurity atoms (C and N). In the body-centered-cubic lattice the interstitial atoms are near a cube edge and can interact with an edge dislocation, while in a face-centered-cubic lattice the distortion around an interstitial atom is of spherical symmetry and cannot anchor a screw dislocation which has practically no hydrostatic component. Cottrell's theory seems to account rather well for the behavior of body-centered-cubic . metals. EXPERIMENTAL PROCEDURE The apparatus used in these experiments is essentially of the same design as described previously.' Single crystals 1 in. long and having a diameter of % in. were placed in a pendulum which consisted of a bar 8 ft long designed with a crystal holder to accommodate the specimen at low temperatures. This portion of the apparatus was supported on fine molybdenum wires. A bar of the same diameter and length comprised the other portion of the apparatus. This bar was supported on a set of roller bearings arranged around the periphery of the bar to allow accurate alignment. This bar was propelled by means of a spring-loaded gun and allowed to strike the lead bar in front of the single-crystal specimen. SR-4 type A-8 resistance strain gages were cemented to the specimen and the strain measurements were obtained by amplifying the strain-gage output by means of a high-gain preamplifier. A tektronix 545 oscilloscope was used together with a polaroid camera to record the strain and time sweep. An Ellis Associate Bridge was used to calibrate the strain gages and calibration readings were obtained before each test. The sweep of the time signal was initiated by means of a miniature thyraton which was fired when the two bars came into contact. The single-crystal specimens were cut from single-crystal bars about 12 in. long, grown by a modified Bridgman technique. The aluminum crystals were made with material of 99.99 pct purity while the purity of the copper was 99.999 pct. A cut-off wheel was used to prepare the specimens which were then machined to the desired length. The two opposite faces of the specimen were parallel to each other and perpendicular to the axis of the specimen. The specimens were compressed 1 pct. No machining followed thereafter. In some cases prestraining was carried out in liquid nitrogen by impacting the specimens directly in the apparatus so that subsequent observations could be made without allowing the specimen to warm up to room temperature. The single crystals were compressed 1 pct at room temperature in a hand press without much control of the rate of deformation. In some cases specimens were recompressed to obtain the desired length change. As far as could be determined in these experiments this factor did not seem to influence the results. The SR-4 strain gages were glued with a cellulose type cement onto the specimen surface and baked at 45°C for 12 hr. As a check on the baking treatment gages were allowed to dry at room temperature. All delay time tests in this paper were conducted in a liquid nitrogen bath at -195°C. A schematic delay time oscilloscope trace is shown in Fig. 1. At point B the elastic stress wave caused by the impact reaches the strain gage on the specimen. The portion BC is the elastic strain. In this investigation the strain at point C was used to calculate the critical resolved shear stress by multiplying by the proper modulus depending upon the orientation of the single-crystal specimen. The time between C and D is the delay time portion of the curve. This portion of the curve is fairly flat but does have a definite microstrain associated with it. After the point D is reached the specimen deforms rapidly and the strain reaches a maximum at E. Following this, depending upon the length of the bar behind the specimen, the strain remains constant for a period and then decreases when the reflected elastic wave returns from the end of the pendulum bar. A permanent plastic strain is recorded on the oscilloscope trace and also measured by a strain-measuring bridge. The strain, E p,

Jan 1, 1960

By A. N. Holden

A DISLOCATION mechanism has been described by Cottrell' by which metals can yield locally, I. form Liiders bands, giving rise to a characteristic stress-strain curve with a sharp yield point and appreciable strain at constant or decreasing stress. It is undoubtedly the best mechanism that has been suggested to date." In its present development, however, the dislocation mechanism provides a more satisfying explanation for the sharp yield point than for the extensive localized flow occurring at the lower yield stress. The primary objective in this paper is to extend the dislocation mechanism to account for localized cataclysmic flow by a dislocation collision process and to give experimental evidence to support such a process. Only the yielding of iron containing carbon -will be discussed, although other metal-solute systems are known to behave similarly. Cottrell Mechanism In brief, Cottrell explains the yield point in the following way: The dislocations in iron which must propagate to produce slip usually lie at the center of local concentrations of carbon atoms, since segregation about these dislocatlons relieves some of the local stress resulting from them. A dislocation surrounded by a "cloud" of carbon atoms is thus anchored, and a higher stress is required to set it in motion than to move a free dislocation. Considering all available dislocatlons to be anchored in this fashion, the iron exhibits a yield point when the first dialocations break free and move through the lattice causing slip. This first breaking away of a dislocation enables other dislocations to break loose by "interaction" and the process becomes a cataclysm producing local deformation or Luders bands. The yield point in the stress-strain diagram for iron is absent in freshly deformed material, but returns gradually with time; the phenomenon is one aspect of what is called strain aging. The rate at which the yield point returns following straining depends on the temperature of aging. According to Cottrell the rate of return of the yield point in strained iron is limited by the rate of diffusion of carbon at the aging temperature, the mechanism is onr: of reforming the solute atmospheres around carbon-free dislocations that had stopped moving coincident with the removal of stress. If the specimen is retested immediately after straining and unloading, carbon will not have had time to diffuse to, and re-anchor, dislocations and the yield point will not occur. The carbon diffusion limitation for the rate of strain aging apparently applies if the criterion for strain aging is either the change in hardness" or the change in electrical resistance" of the strained speci- men with aging time. The possibility exists, however, that the yield point actually returns to strained iron at some rate other than that deduced from hardness or electrical resistance data. Therefore, as a preliminary experiment, the rate of yield point return in a rimmed sheet steel strained 6 pct in tension was measured at 27°, 77°, and 100°C. A plot of yield-point elongation for each of these temperatures against aging time appears in Fig. 1. The aging process is described by curves which rise to a plateau value of elongation that seems independent of temperature, but at a rate that depends on temperature. Very long times lead to a further rise in the yield-point elongation above the plateau value. However, if the later increase in yield-point elongation is ignored and the log of the time to reach half the plateau value of elongation is plotted against 1/T, a straight line results for which an activation energy of about 25 kcal pel- mol may be assigned. Within the accuracy of this sort of experiment this is approximately the activation energy for the diffusion of carbon in iron (20 kcal per mol), and the carbon diffusion limitation suggested for the yield-point return on strain aging is valid. The Cottrell mechanism thus explains in a qualitative manner the occurrence of a yield point in iron and its return with strain aging. It fails, however, to explain some of the other experimental observations that have been made of the yielding behavior of iron. For example, it is known that the yield point in iron becomes less pronounced with increasing grain size. Annealed single crystals of iron have very small yield-point elongations .if indeed they have any,' compared to a polycrystalline steel. If the only requirement for a yield point is that the dislocations in the lattice of the annealed. material be anchored by carbon atoms, the difference in the behavior of single crystals and polycrystals is not explained. That a dislocation mechanism may be entirely consistent with little or no yield point in an annealed single crystal will become apparent later when dislocation interaction is discussed. Strain aging produces a definite yield point even in single crystals. This accentuation of the yield-point phenomenon in single crystals after strain

Jan 1, 1953

By B. H. Kear, H. G. F. Wilsdorf

After a few percent strain, dislocations in disordered Cu3Au are arranged in groups in ulell-defined slip planes, which contrasts with the more or less random distribution of dislocations in the corresponding ordered alloy. Unusually long and straigkt dislocation segments observed in the ordered alloy are interpreted in terms of cross slip of screw dislocations from their slip planes into cube planes. It is proposed that cross slip, and also dislocation reactions of the Lomer type, play an important role in work hardening of the ordered alloy. ACCORDING to to dislocations in the disordered lattice are only partial dislocations in the corresponding super lattice, so that in the super-lattice dislocations must occur as pairs, with each pair connected by a ribbon of antiphase boundary. Recently, striking confirmation of the theory was obtained by Marcinkowski, Brown, and Fisher3j4 in a study of dislocation configurations in thin foils of the Cu3Au alloy by transmission electron microscopy. In the present investigation, the observations made by these workers have largely been confirmed. Moreover, it has been found that dislocations in the plastically deformed ordered alloys are often unusually long and straight. This paper is mainly concerned with these new observations. A tentative explanation is offered in terms of cross slip of dislocations in the ordered alloys. PREPARATION OF SPECIMENS An alloy close to the stoichiometric composition Cu3Au was prepared by melting together high-purity copper and gold (99.995 pct) under vacuum in a graphite mold. The resulting ingot was rolled down and cut into strips 1 1/2 by 1/8 by 0.005 in. in thickness. All strips were annealed at 900°C for 3 hr and cooled to 500'~. A few of the strips were quenched from ~OO'C, while the remainder were slowly cooled in the temperature range 400" to 150°C at intervals of a few degrees every 24 hr to produce a high degree of order. After this annealing treatment the average grain size of the material was about 0.1 mm. Material in different states of order was obtained by reannealing fully ordered material at temperatures below the critical temperature: followed by quenching. The equilibrium degree of order attained at a particular reannealing temperature was obtained from the paper by Keating and warren.' A simple hand-operated tensile jig was used to give the strips the required amounts of plastic strain. Following straining, a number of specimens were cut from each strip by means of an electrolytic cutting device.= Finally, each specimen was thinned electrolytically using the polishing procedure described by Bakish and Robertson,7 and these thin sections were examined in the Philips EM-100B electron microscope operating at 100 kv. EXPERIMENTAL OBSERVATIONS Antiphase boundaries. The average domain size in the ordered alloys was found by direct observation to be about 0.25 p. Also, it was observed that the grown-in configuration of antiphase boundaries was changed little by plastic deformation, at least up to 6 pct strain. Fig. 1 shows an electron micrograph of a thin foil of partially ordered alloy (S - 0.8) after 3 pct strain. The micrograph shows a few dislocation pairs and a somewhat crystallo-graphic network of antiphase boundaries. The normal to this foil was found by diffraction analysis to be approximately 11121, with principal directions in

Jan 1, 1962

By J. H. Wernick, E. E. Thomas

THE etch-pit technique for revealing dislocations in bulk samples allows one to determine dislocation densities and to study their behavior under various mechanical and thermal treatments. We have developed a chemical polish-etch for the development of etch pits on the (1100) plane of Cd which appear to

Jan 1, 1961

By G. T. Hahn

On the basis of the recommendation of Lovell, Vogel, and Wernick,&apos; Fry&apos;s reagent*2 was recently c) if decoration of the dislocations by carbon or nitrogen atoms is a factor in the etch pitting. Experiments were performed with samples of a commercial 1020 steel, a vacuum-melted iron (C - 10 to 15 ppm, 0 - 20 to 50 ppm, N < 2 ppm), both annealed 4 hr at 1100°C, and a zone-refined iron (C - 3 to 5 ppm, 0 - 10 ppm, N < 1 ppm ) in the as-cast condition. Saomple surfaces were prepared by grinding to 600A grit and electropolishing. Initially, effects of etching the steel with modifications of the basic Fry composition were examined. It was found that increasing the alcohol or HC1 concentratior~ retarded dislocation pitting; reducing the acid content promoted secondary pitting. Cooling the reagent and the sample did not improve the quality of the etch pits. Best results were obtained with freshly prepared reagent modified by increasing the CuC12 content to 15 g. This composition was used in subsequent experiments. Annealed samples were etched 10 to 15 sec; cold-worked samples —2 to 5 sec.

Jan 1, 1962

By J. D. Meakin, H. G. F. Wilsdorf

An etching technique.has been used to investigate the dislocation structure of deformed @-brass single crystals. Isolated single ended pileups have been observed, and it is shown that, in certain cases, the configurations of such pileups agree with theoretical predictions. Many discrete pileups within heavily deformed regions have also been detected and the influence of surrounding dislocations on these groups are reported and discussed. Divergences between the experimental and theoretical spacings in the isolated pileups and the origin of the stress maintaining the pileups are discussed. THE spatial configuration of a linear array of identical dislocations has been evaluated theoretically by Eshelby, Frank, and Nabarro.&apos; Of particular interest is the equilibrium spacing of a series of dislocations under a uniform shear sti-ess when the leading dislocation is held fixed in the lattice; such an array is termed a single ended pileup. Eshelby, Frank, and Nabarro&apos; found that an explicit analytical solution to the problem of n dislocations in a pileup is not possible, but they were able to derive approximate formulae applicable under various limiting conditions. An alternative method of determining the equilibrium configuration was proposed by Leibfried and Leibfried and Haasen in which the discrete dislocations are replaced by a continuous dislocation density. This technique was used by Head and Louat to solve in first approximation, a number of problems of particular interest, eg., single and double ended pileups. Head has also solved numerically a number of specific configurations involving up to six dislocations. Recently Kuhlmann-Wilsdorf has obtained numerical solutions for single-ended pileups containing between three and seventy dislocations, thus making possible a comparison between appropriate experimental results and accurate theoretical values. The considerable use of the pileup concept in theories of plastic flow has stimulated a number of attempts to observe such arrays experimentally. There is of course considerable intrinsic value in revealing an isolated pileup because a direct check on the elastic theory of dislocations then becomes possible. The only technique generally applicable for studying pileups in bulk metal specimens is selective etching of the point of emergence of individual dislocations. Confining our attention to etching studies which have revealed pileups, the earliest reported work

Jan 1, 1961

By R. J. Stokes

This paper compares the room-temperature mechanical behavior of magnesium oxide crystals containing &apos;fresh&apos; and &apos;grown in&apos; sources. &apos;Fresh&apos; dislocation sources introduced by cleavage or mechanical contact move and multiply to generate slip bands at 3000 psi. Macroscopically the crystals yield smoothly at 6000 psi and can be quite ductile. When &apos;fresh&apos; sources are eliminated by chemical polishing the crystals have to rely on &apos;grown in&apos; sources to initiate slip. They then deform elastically up to extremely high stresses (-30 to 50,000 psi) yielding with a sharp stress drop down to the level at which Ifresh&apos; sources operate. Grown in&apos; sources are considered to be associated with impurity wecipitate particles or inclusions. Annealing crystals at 2000°C dissolves these particles thereby eliminating sources for slip. The crystals then become consistently stronger (> 70,000 psi) approaching within 1/10 of the theoretical strength. Dislocations of the grown-in network do not move under stress to nucleate slip. It is proposed that they are locked electrostatically. DISLOCATIONS were originally conceived to resolve the large discrepency between the theoretical and real strength of solids. The idea that slip propagates by the movement of dislocations is now well confirmed both by electron transmission and etch pit studies. But this by itself is not sufficient to explain the low yield strength of crystals for there is still the need to understand where slip dislocations originally come from. Theoretical estimates place the stress to generate dislocations homogeneously in the lattice at approximately 1/30 of the shear modulus,&apos; a value 104 to 105 times greater than the stress at which the very first manifestations of plastic deformation have been observed. Only an special cases can the theoretical strength be approached; in crystals of high perfection such as whiskers2 where dislocation sources do not preexist and in covalent crystals where the dislocations present at room temperature are almost completely immobilized by the bond character of the solid.3,4 For the most part it is necessary to assume that the yield strength of ionic and metallic solids corresponds to the motivation and multiplication of dislocation sources present beforehand. The question as to their origin appeared to be answered by the suggestion of Frank and Read5 that dislocations forming part of the grown-in structure could operate as a mill for the large scale production of dislocations. The Frank-Read mechanism is still widely accepted as the source of dislocations but a number of observations have been reported which are in serious disagreement with it. One of the most intriguing of these is that under normal testing conditions dislocations of the grown-in network appear to play no role in the plastic deformation of rock salt structure ionic solids. This was first reported in the etch pit studies on lithium fluoride by Gilman and Johnston6 and is true also for magnesium oxide. To explain the comparatively low yield stress of lithium fluoride it was proposed by a number of authors7,9 that small unresolved prismatic loops formed by vacancy condensation were acting either directly or indirectly as the dislocation sources. This proposal led Gilman10 to perform a series of detailed and careful experiments on lithium fluoride to try to identify the sources responsible for the initiation of slip. He concluded that prismatic loops played no general role and that other sources were more important. Dislocation sources in ionic crystals can be divided into two general categories. First, there

Jan 1, 1962

By Norman Brown, Victor V. Damiano

ThE present paper proposes a mechanism of dislocation multiplication at internal inclusions or cavities and presents experimental evidence of such sources in zinc. Using an etching technique recently described by Damiano, Tint, and Herman1 to study the three-dimensional aspects of dislocations in bulk zinc crystals, an investigation was made of helically shaped and closed-loop etch patterns found to be associated with inclusions. Crystals containing 0.1 pet Cd and grown from the melt were deformed slightly by bending and then aged at room temperature to precipitate cadmium at the dislocations. The crystals were cleaved along the (0001) plane and then etched with Gilman&apos;s2 etch. Crystals were continuously viewed on the (0001) plane while the etching was in progress and numerous helical and closed-loops etch patterns were continuously recorded as shown in the sequences printed directly from the cine film in Fig. l(a) and (6). These etch patterns are not to be confused with the etch patterns previously reported by Damiano and Herman3 which revealed dissolution spirals on the (0001) plane of high-purity zinc crystals. In the present case, precipitates arranged in the form of closed loops or helicies are progressively uncovered by etching after suitable aging of cadmium doped zinc crystals. Viewed with dark-field illumination as shown in Fig. 2, portions of a helical figure and subboundaries were revealed simultaneously. Continuous viewing while the etching was in progress revealed in Fig. 1(b) that the short line segments observed on single photomicrographs were in fact continuous and described a helix which had its terminus at an inclusion. The observations suggested that a dislocation once nucleated at the interface between the inclusion and matrix may act in such a way as to produce ad-

Jan 1, 1964

By W. Bonfield

A study has been made of the dislocation substructures produced in hot-pressed beryllium specimens strained to various levels in the range from 800 x 10-6 In. pev in. to fracture. A number of distinctive dislocation configurations were observed in this region which had not been noted at lower levels of strain. These included dislocation-dislocation interactions to form networks, dislocation "walls", subgrain boundaries and complex arrays, interactions between dislocations and large beryllium oxide particles, and the generation of dislocations from certain particles. The nature of these differences in substructure and their relation to the stress-strain characteristics of polycrystalline beryllium are discussed. In a previous study1 of the plasticity of commercial-purity, hot-pressed beryllium a transition was found in the deformation characteristics in the mi-crostrain region. The initial plastic deformation could be represented by a parabolic stress-strain equation, but above a critical stress there was a complete departure from this relation and a reduction in the strain-hardening rate. The dislocation configurations produced by various levels of micro-strain in this region were examined by transmission electron microscopy and a general correlation was established between the observed transition in deformation characteristics and the dislocation structure of the material. The two stages in the micro-strain region distinguished in these experiments were designated as Stage A&apos; and Stage B&apos;. Stage A&apos; type deformation generally was noted up to a plastic strain of -80 x 10"6 in. per in. and Stage B&apos; type from -80 x 10-6 to -800 x 10&apos;6 in. per in. The discovery of two stages in the microstrain region naturally posed pertinent questions as to the existence of any further distinct stages in the subsequent plastic deformation. The purpose of this paper is to present a study of the dislocation configurations produced in similar beryllium specimens strained to various levels in the range from -800 x 10 in. per in. to fracture and to discuss the relation between substructure and the stress-strain characteristics. It is concluded that this region of strain can be considered as a distinct stage in the plastic deformation of polycrystalline beryllium. Tensile specimens of gage length 1 in. and cross section 0.18 by 0.06 in. were prepared from commercial-purity, hot-pressed QMV beryllium and then annealed at 1100°C for 2 hr. 2 followed by a careful chemical polishing procedure.3 The specimens were strained at a constant rate to various levels of strain in the range from -800 x 10-6 in. per in. to fracture (at 0.5 to 2 pct elongation), using the Tuckerman strain-gage technique1 to measure plastic and total strain. Thin foils were obtained from the strained and fractured specimens by chemical polishing3 and were examined using an RCA-EMU 3 electron microscope. Considerable care waS taken to avoid both accidental deformation during the preparation of the thin foils and excessive heating during their examination. Selected-area diffraction patterns were determined for each micrograph. Tilting experiments were also performed whenever appropriate to establish the dislocation zero-contrast position and hence determine the Burgers vector. This operation was sometimes not possible due to the rapid contamination of the foils which occurred in the electron microscope. RESULTS AND DISCUSSION To enable the distinctions between the dislocation arrays at high and low strain levels to be adequately made, the main characteristics of Stage A&apos; and Stage B&apos; deformation are briefly reviewed. 1) Stage A&apos;. In the annealed starting condition there was a variable density (5 x 107 to 3 x 10&apos; cm per cu cm) of isolated dislocations within a grain. The initial deformation in a tensile specimen was heterogeneous, with the dislocation density increasing in a few grains to 5 x 10g to 1.5 x 101° cm per cu cm. The deformation occurred exclusively on the basal plane by the movement of one or more 1/3 (1130) type dislocation systems. The dislocations were long and regular in form and nearly all the intersections exhibited a simple four-point node configuration. No interactions between glide dislocations and beryllium oxide particles were observed. 2) Stage B. In Stage B&apos; there was a large increase in the number of grains exhibiting dislocation movement and also a change in the nature of the deformation, in which jogged dislocations and elongated loops became the characteristic feature. The splitting up of the elongated loops into smaller loops and the possibility of source action from the re-

Jan 1, 1965

By J. Weertman

It is shown that conditions suitable for the conversion of straight dislocations into helices are common in crystals hardened either through long-range dislocation interaction or by jog formation on dislocation lines. For dislocations other than screw dislocations or dislocations nearly screw in orientation, helices can be formed with the aid of core difhsion at temperatures low relative to the melting point of the material. It is assumed that, once formed, helices will degenerate into dislocation tangles. THE dislocation tangle is one major dislocation arrangement observed by the transmission electron microscope which had not been predicted previously from dislocation theory. Since first being observed, the tangle itself has become important in applied dislocation theory. The Cambridge school (P. Hirsch) bases part of its theory of work hardening upon this phenomenon.&apos; In spite of the fact that the tangle obviously is a structure of prime importance to a cold-worked crystal, until recently relatively little attention has been paid to the question of exactly why or how tangles arise. It was generally assumed at first that cross slip and perhaps jog formation will lead to tangles. However Wilsdorf and schmitz2 concluded that cross slip cannot markedly contribute to the tangles. The Wilsdorfs and Maddin3&apos;* have proposed that tangles arise by means of prismatic dislocation loops and superjogs which are produced by a precipitation of point defects. Dislocations with superjogs or which have joined with prismatic loops are themselves dislocation sources and they can produce new dislocations, a process they call "mushrooming", which then tangle with each other. There is no question that the Wilsdorfs et al. mechanism as well as the cross slip one can pro- duce tangles. However these may not be the only paths leading to tangle formation. In this paper we wish to consider another way tangles can form. Our work will be based on the theory of dislocation screw We wish to show that whenever a crystal is cold-worked there always is present a "driving force" leading to helix formation and thus to tangle formation. We do not expect to observe well-developed, regular helices in cold-worked metals. Rather we would expect that after a helix is formed random interactions with nearby dislocations will cause a well-developed helical dislocation to go over into an irregular form. A dislocation tangle is, of course, a grouping of dislocations with irregular forms. Therefore we feel that, in accounting for the formation of dislocation tangles, it is sufficient to show that many dislocations in a cold-worked crystal will take on helical form. The crucial step is helix formation. In order to have a straight dislocation assume a helical form, diffusion of vacancies, or interstitials, must occur. Our discussion of tangle formation therefore will be limited to crystals which have been deformed at temperatures ranging from about one fifth to half their absolute melting point. In this tem per a ture range appreciable core diffusion is possible. (There is no problem in explaining tangle formation at temperatures greater than half the melting point. At such temperatures dislocation climb through a bulk diffusion of point defects gives an extra degree of freedom to dislocation motion. This extra freedom of motion makes tangle formation easy.) At temperatures much below one fifth the absolute melting temperature diffusion processes are sufficiently slow that helix formation does not occur. Of course helix or tangle formation could occur in material deformed at very low tempera-tures which was subsequently warmed in order to make the thin specimen necessary for electron-microscope examination. Since within the temperature range of approximately one fifth to half the melting temperature the diffusion of point defects in the core of the dislocation is rapid, we can reasonably assume that within

Jan 1, 1963

By J. D. Meakin, H. G. F. Wilsdorf

Using a combined decoration and etching technique the dislocation structure of annealed and deformed a brass has been studied. Annealed crystals revealed a low density forest and well-developed subboundaries; lightly deformed crystals contained discrete groups of dislocations. The dislocation density and the number of dislocations in a group were obtained from the micrographs. Using slip-line data, the mean path of a dislocation and the configuration of groups along an active slip plane have been deduced. Observations on secondary and cross-slip are reported. It has been the aim of many investigations to obtain detailed knowledge of the dislocation patterns which are present in metals before and after their deformation. The "decoration" of dislocations with impurity atoms has been considered as one of the promising experimental approaches, and much work has been done to develop this technique for revealing dislocation sites in metals. Following the early work by Castaing,&apos; Castaing and Guinier,&apos; and Lacombe and Berghezan~ on aluminum-rich aluminum-copper alloys, dislocations in this material have been studied extensively by others.+&apos; In these alloys the dislocation sites act as nuclei for the precipitation of the second phase. The main results of the investigations on aluminum with copper are: i) the confirmation of the earlier contention that subboundaries consist of dislocation walls, ii) that many more dislocations are found in slip bands than in regions where less glide had taken place, iii) the observation of individual dislocations, lying nearly parallel to the surface investigated, and iv) that parts of dislocation loops, apparently emitted from a dislocation source, could be made visible. Recently, Jacquet, Weill, and Calvert have succeeded in revealing nearly concentric dislocation loops in quenched A1-4 pct Cu and thus indicated directly the existence of dislocation sources in a fcc metal specimen of normal dimensions. Another decoration method developed by Dash10&apos;11 and applied to silicon crystals makes use of diffusing copper to the dislocations from a surface deposition. The dislocation pattern can then be observed by an infrared technique. His results include evidence for symmetrical and spiral Frank-Read sources, and for arrays of dislocation loops which follow simple crys-tallographic directions. Recently Low and Guard" have studied the dislocation structure of silicon-iron using carbon for the

Jan 1, 1961

By F. L. Vogel

Densities and distributions of dislocations in plastically bent germanium crystals before and after annealing were studied. In the bent and annealed crystals, the theoretical relationship between radius of curvature and density of dislocations is confirmed. Before annealing, however, more dislocations are present than required, and these are distributed with a minimum at the neutral axis and maxima at the top and bottom surfaces. On annealing, three significant changes occur in the bent bars: 1) the average dislocation density is reduced, presumably by the annihilation of opposite signs; 2) dislocations migrate from the high density outside regions toward the low density neutral axis, thus producing the equilibrium distribution of dislocations; and 3) a polygonized structure is formed by movement of the dislocations into walls normal to the slip plane. ETCHING to reveal edge dislocations&apos;-" offers a unique opportunity to study, in germanium single crystals, the functioning of dislocations in plastic deformation. Plastic bending is ideally suited to this purpose because it produces a static array of edge dislocations in an ideally plastic material which is predictable from the theory." " Nye" has given a rather complete treatment of the geometry of bent crystals in terms of dislocations. The density of excess dislocations is related to the radius of curvature of the slip plane of a bent crystal, as shown in Fig. 1, assuming the absence of macroscopic elastic stresses. The curvature of any plane in the zone of the bend axis is found by resolving the Burgers vector into that plane, so that for the usual case where the slip plane is inclined at some angle 0 to the neutral plane of the bar, the equation applies, with T equal to the radius of curvature of the neutral plane of the bent crystal. Two predictions which are relevant to this study may be made from Eq. 1. First, in crystals bent to various radii, the average excess dislocation density is inversely proportional to the radius and second, for a bar bent to a radius which is large compared with its thick-

Jan 1, 1957

By K. R. Janowski, H. Conrad

As part of a program to establish the effect of crystal imperfections on laser output, a detailed study was made of the dislocation structure of ruby crystals obtained from varioius sources. Using KHSO4 as an etchant, a detailed mapping of the dislocation structure on the (0001) and the (1150) planes was carried out. A less extensive study was made of the rhombohedral planes. The average dislocation density on the basal plane was 1.5 to 3 x 106 cm&apos;2 and on the (1120) planes -5 x 10&apos; cm-2. Howe7!er, considerable variation existed between areas on a given plane. The subboundaries in the basal plane tended to lie along [1100] type directions while those on the (1120) plane tended to lie: a) parallel to the basal plane, b) along truces of the (1101) plane, and c) along normals to the traces of the (0001) planes. The orientations suggest that mang of the dislocations lie on the (0001), (1701), and (1150) planes A Laue back-rellection nnalysis Of c-axis wander in one crystal revealed a gradual increase in misorientation from me end of the crystal to the other, with a maximum variation of 1°35&apos;. Slight etching of a mechanically polished crystal revealed mumerous polishing scratches, suggesting the existence of a plastic flow layer. It is recognized that chromium concentration, lineage, and other crystalline imperfections play a role in the efficiency of ruby lasers.&apos; Consequently, it is desirable to establish in detail the imperfection structure of ruby crystals to be used as lasers. Some exploratory work along this line had already been done by Barnes&apos; and Dils and Martin.&apos;" How- referred to as the morphological system, as described by Kronberg.4 The Miller indices given in the present paper will be based on this morphological system. In this system, the three common growth planes are the (0001), the {1120}, and the {1101}.5 Since these planes are of high stability, it is expected that they are most suitable for study by the etch-pit technique. In the present investigation, a detailed mapping of the dislocation structure was carried out for the (0001) and the (1130) planes. A less extensive study was made of the etch-pit structure on rhombohedra1 planes. An analysis of dislocations in sapphire (the ruby host) was first made by kronberg,4 who postulated that slip on the (0001) plane occurred by motion of dislocations with Burgers vector 1/3 <1150> and that these dislocations might dissociate into quarter partials. An etch-pit technique using boiling phosphoric acid was developed by Scheuplein and Gibbs6, 7 for identifying dislocations intersecting the (0001) planes and the planes near (2021) in sapphire. Al-ford and Stephens8 were able to reveal dislocations on the (0001) and {1120} planes in sapphire and ruby by etching in fused potassium bisulfate (KHS04) at 675°C. The termini of basal dislocations [(000l), <1120>] were revealed by Palmour and Kriegel9 on {1120} and {1010} by thermally etching sapphire. Bond and Harvey10 were able to decorate dislocations in sapphire by adding 1 pet by weight of ZrO2 to the Al2O3 powder used in the growth of the crystals by the Verneuil technique and then heating the grown crystals for 4 hr at 1500°C. They found, using optical transmission microscopy, that many dislocations had straight segments which were parallel to one of the six [1120] directions in the basal plane. Single dislocation lines curved smoothly from one alignment to the other, turning through angles of 60 to 120 deg. Also observed were isolated hexagonal loops, approximately 10 µ in diameter, the sides of which lay along the same directions as did the longer dislocations. MATERIAL AND ETCHING PROCEDURE The ruby specimens used in this study (all containing approximately 0.04 pet Cr) had been obtained from four different sources: Linde Co., Meller Co., Valpey Crystal Corp., and those grown at Aerospace Corp.* For the initial phase of this study, several specimens were cut from the slab shown schematically in Fig. 1 which had previously been cut from a disk boule obtained from the Linde

Jan 1, 1964

By Nicholas J. Grant, Oliver Preston

PUBLICATION of data by Irmann&apos; indicating outstanding thermal stability and elevated-temperature strength properties in a sintered aluminum powder product (SAP) stimulated interest in the strengthening of metals by means of a highly dispersed oxide phase. This material was produced by compacting, sintering and extruding a fine flake aluminum powder, resulting in a dense product containing 10 to 16 volume pct alumina, which arises from the thin oxide film on the starting powder, highly dispersed in a matrix of pure aluminum. The method of producing SAP, and the stable high-temperature properties obtained from it, introduced the possibility of developing superior materials for high-temperature service by powder metallurgy methods. The composition of the materials of this type which are presently under consideration is predominantly metallic, containing from less than 1 pct up to about 20 volume pct of the oxide. As a result, other properties of these materials, such as electrical and thermal conductivity, thermal shock resistance, and to a certain extent ductility, notch sensitivity, machinability and hot working properties, are also predominantly metallic. These alloys do not constitute, therefore, a completely new class of materials as do the cermets, but rather present a new means of modifying the properties of a metallic matrix. In this sense, SAP type alloys are more closely analogous to the alloy aging systems. While the strength properties realized in the oxide-pure metal systems at the lower temperatures are substantially less than the best attainable in the aging systems, the thermal instabilities in the latter make them of less value for use at temperature much above their optimum aging temperatures, as indicated in Fig. 1. While the means of obtaining an oxide dispersion are more difficult and costly than conventional aging processes, in the light of the as yet limited understanding of such systems there is considerable promise of improved high temperature properties arising from the thermal stability of these structures. Since the development of SAP in 1946, its properties and the properties of a series of similarAl,O,-A1 products containing from about 1 to 20 pct aluminum oxide have been fairly extensively studied and reported.&apos;- "articular attention has been given to

Jan 1, 1958

By E. W. Hart, W. R. Hibbard

The room temperature flow characteristics of a series of Cu-Cr alloys are found to be related to the amount and characteristics of the chromium-rich precipitate. The results are consistent with the theory of Fisher, Hart, and Pry, which considers the trapping to dislocation loops around precipitate particles. THE use of dispersed phases for hardening metals, particularly high temperature alloys, has been practiced for several years. Current theories describing the effects of dispersions on the basis of dislocation theory have been proposed by Mott and Nabarro.l-4 rowan," and Fisher, Hart, and Pry.8 These theories recently have been discussed by Hart,&apos; who pointed out that the experimental data available for comparison with theoretical calculations for overaged alloys are confined to studies by Gensamer, Pearsall, Pellini, and Low,8 Shaw, Sher-by, Starr, and Dorn,9 and some hitherto unpublished data on Cu-Cr alloys which will be described herein. Certain difficulties were associated with the interpretation of the first two studies. Gensamer, Pearsall, Pellini, and Low were concerned principally with interparticle spacing and did not document particle sizes. Shaw, Sherby, Starr, and Dorn included all the data in their report which was necessary for the theoretical evaluation, but their study is subject to some question1" due to difference in prior history of various specimens and due to systematic differences in particle characteristics" which appeared to be associated with differences in the magnification of their microscopic examination. The current study was undertaken to obtain critical data in a manner which avoids some of these limitations. Specimens of eight Cu-Cr alloys remaining from a previous investigation&apos;&apos; were available in the form of 100 mil sheet of the compositions shown in Table I. At 200 mil this material had been previously an- nealed ½ hr at 1000°C, water quenched, and cold rolled 50 pct. Samples were further cold rolled to a thickness of 20 mil for a total reduction of 90 pct. Sheet tensile specimens of standard geometry with a gage length 2½ in. long and 0.20 in. wide were machined from this sheet. These specimens were then annealed in a dried N2-H2 atmosphere for the times and temperatures indicated in Table I. This anneal served two purposes: 1—to obtain a fairly uniform and nearly constant grain size of 0.015 to 0.022 mm average diameter, and 2—to precipitate a fairly uniform, nearly spherical over-aged dispersion of essentially pure chromium. A typical microstructure illustrating the grain size and the uniformity of the dispersion is shown in Fig. 1. A typical dispersion illustrating the range of sizes and shapes of the particles is shown in Fig. 2. The tensile specimens were tested in the Instron equipment described in ref. 11 at room temperature at a strain rate of 0.04 in. per in. per min. Three tests were run on each alloy with sufficient repro-ducibility that a single true stress-true plastic strain curve could be drawn through the three sets of data for each alloy. Typical curves are shown in Fig. 3.

Jan 1, 1956

By N. J. Grant, K. M. Zwilsky

A series of copper-alumina dispersion strengthened alloys were prepared using three different copper and two different alumina powder sizes. Improvements in strength of up to ten times that of pure copper were found in room-temperature as well as elevated-temperature stress-rupture tests. Conductivity values remained from 70 to 90 pct that of pure copper. The best alloys were based on the finest metal powder (1 p) and contained from 7.5 to 10-0 vol pet of 0.018 or 0,033 p alumina. DISPERSION strengthening of metals consists of strengthening a metal matrix by the addition of oxides or other refractory constituents, followed by strain hardening, in order to reinforce the base material and extend its temperature range of application. Since the discovery of SAP by lrmannl and Von zeerleder2 in 1949, many investigators have reported data obtained on a variety of metal-inert oxide alloys.3-7 The present work deals with the mechanical mixing of copper and alumina powders. While several techniques of introducing the second phase have been investigated to date, mechanical mixing so far has been recognized as the simplest, least expensive, and most universally applicable technique that can be used to obtain an ultrafine dispersion of inert particles. In the present case, the effects of changing the metal particle size, the oxide particle size and the volume percent of oxide were investigated. This work is an extension of a previous study.6 EXPERIMENTAL PROCEDURE The starting materials were three different grades of copper powder and two different alumina powders. The three metallic powders were -74 µ(- 200 mesh) electrolytic copper powder consisting of irregular equiaxed particles having a normal screen distribution and analyzing 99.5 pct Cu, and two powders having a 5-µ and 1-µ particle size, average, respectively. The latter powders were produced by the hydrogen reduction of purified sulfate solutions at elevated temperature and pressure and were furnished by the Sherritt Gordon Mines, Ltd. The alumina used was obtained from Godfrey L. Cabot Co., under the trade name of Alon C, one batch of powder having a particle size of 0.018 µ, the other a particle size of 0.033 µ. The crystal structure of these alumina powders was found to be cubic gamma. Each batch of powder was mixed in a Waring Blendor for a total of 15 min, followed by a low-temperature reduction in hydrogen and vacuum compacting in cylinders which were hydrostatically pressed at 35,000 psi to give a compact that could be handled conveniently. Six of the compacts were hydrogen sintered at 900°C while the remaining four were sintered at 1000°C. Subsequently, all compacts were hot extruded at 760°C with a reduction of area ratio of approximately 20 to 1. Evaluation of alloys included density and resistivity measurements, room-temperature tensile tests, stress-rupture tests at 450°C plus one other temperature per alloy, hardness tests, microstruc-tural examination, X-ray analysis of the dispersed phase after dissolving the metal phase, and oxidation studies on two of the alloys. A vacuum-melted, wrought copper rod was tested together with these alloys for comparison purposes. RESULTS Table I is a summary of the compositions, sintering temperatures, densities and conductivity values of the ten alloys prepared. All alumina additions are given in volume percent, and will be referred to as

Jan 1, 1962