By B. F. Decker, J. H. Keeler, W. R. Hibbard

Textures of hot-rolled, of cold-rolled, and of cold-rolled and annealed zirconium sheets were determined by use of an X-ray spectrogoniometer. All textures showed a tilt of the basal planes 240" from the rolling plane about the rolling direction. Deformation textures showed the [1010] direction to be approximately in the rolling direction. After recrystalliza-tion, the 111201 direction was approximately in the rolling direction. This texture was sharpened by annealing above the allotropic transformation. Textures of sheet produced by alternately cold rolling and then annealing were less strongly oriented than sheets that underwent severe deformation without intermediate anneals. THIS study of the deformation and annealing textures of high purity zirconium was carried out to supplement an investigation of zirconium and zirconium-base alloys. The spectrogoniometer method of pole figure determination was used and yielded more detailed and precise information than the photographic techniques used by previous investigators. Earlier investigations of the rolling textures of hexagonal metals titanium,1,2 beryllium," and zirconiumL having a c/a ratio slightly less than 1.6 disclosed a rotation of the basal planes from the rolling plane about the rolling direction so that the basal poles were inclined toward the transverse direction, and with one exception,& the [1010] direction was found parallel to the rolling direction. Similarly, hot rolling produced a spread of the basal poles in the transverse direction,2,3,5 With the [1010] direction parallel to the rolling direction. The textures of these metals after recrystallization differ somewhat from each other although still exhibiting the transverse rotation of the basal poles about the rolling direction. Zirconium" was found to have the [1120] direction in the rolling direction, beryllium" continued to have the [1010] direction in the rolling direction, and titanium' was shown to have the [1010] direction in the rolling direction (the cold-rolling texture) when annealed at 1000°F, changing to the [1120] direction in the rolling direction when annealed at 1500°F. It was suggested2 that the titanium retains the deformation texture after re-crystallization, and preferred grain growth at higher temperatures produces the second texture. Annealing above the allotropic transformation temperature did not appreciably change the high temperature recrystallization texture for titanium.' Coarsegrained zirconium showed more spread" in the transformation texture than in the recrystallization texture. The material used in this investigation was crystal-bar zirconium prepared by the iodide process. The major impurity was hafnium which was less than 0.3 pct. The composition obtained by spectro-graphic analysis is given in Table I. The hot-rolled specimen was prepared from a 50-g button of zirconium arc-melted in a water-cooled crucible under an argon atmosphere. This button was enclosed in a welded sheath of soft iron and the ensemble was rolled at 825°C. After each pass the sheath was put back into the furnace to allow it to return to the desired temperature. The zirconium ingot was reduced in this manner to a thickness of about 0.035 in., a reduction of approximately 90 pct. The sheet after removal from the sheath was alternately polished and etched to a thickness of 0.001 in. Cold-rolled specimens were prepared from crystal bar by a series of reductions of approximately 0.010 in. until the sheet reached a thickness of 0.010 in. after which it was cold-rolled to 0.001 in. thickness between sheets of alloy steel. The total cold reduction amounted to about 99.8 pct. Specimens were annealed in an evacuated Vycor or quartz tube. The transmission pole figures were obtained by the quantitative method of Decker, Asp, and Harker6 modified by Geisler7 using an X-ray spectrogoniometer with Cu Ka radiation. Unless otherwise specified all four quadrants were examined with 5" increments along the radius of the pole figure. Absorption corrections were made for changes in length of the X-ray path through the sample as inclination of the

Jan 1, 1954

By J. R. Hornaday, A. E. Morris, N. A. Parlee, D. C. Carmichael

Rates of absorption and effusion of hydrogen in solid iron were measurede by a Sieverts type of apparatus. With clean a iron these rates are diffusion controlled down to 420°C and are represented by the equation D = 6.70 x e-'100' crn2 sec-I Certain surface impurities can affect these rates at all temper-atuves. Thin oxide films lower, the apparent diffusivity of annealed iron markedly. Cold-worked iron (75 pct) annealed at 430°C has practically the same solubility and diffusivity as anealed iron. THE mechanism of absorption and evolution of hydrogen in solid iron alloys is not fully understood despite the large number of investigations on the subject. While there appear to be many instances of simple solid-state diffusion control of rate, there are many cases where investigators have either concluded that surface reactions are rate controlling or that some "nondiffusible" hydrogen resides in discontinuities. The purposes of this research were 1) to develop a sound method for studying this absorption and evolution behavior, 2) to examine it in pure annealed iron, and 3) to determine the effects of important variables, such as cold work, surface condition, and composition. This paper relates the progress toward these objectives. Much of the present knowledge of the movement of hydrogen through iron alloys comes from permeability studies which involve the measurement of the rate of passage (under steady state conditions) through membranes of the order of 1 mm in thickness. This method is open to question on various grounds. If surface reactions are involved, two different surfaces operating under two different conditions must be considered. The presence of defects in the membrane even of microscopic dimensions may lead to erroneous results. A few people have studied evolution of hydrogen into vacuum, under carefully controlled (unsteady state) conditions, and some of the best diffusivity data come from these sources. Most of these methods measure rates of evolution only and thus do not make a rigorous test for reversibility of behavior. It appeared that an "unsteady state" method that would permit the measurement of both rates of evolution and absorption under controlled temperature, pressure, and other conditions would offer several advantages. Accordingly the modified Sieverts apparatus described below was designed and built. APPARATUS This apparatus is shown in Fig. 1. The sample bulb is detailed in Fig. 2. Hydrogen of 99.5 pct purity and argon of 99.99 pct purity were used. The hydrogen was deoxidized and dried by means of a Deoxo unit followed by a "Dri-erite" tower. The argon was only dried. The gas burette was graduated in tenths of a cubic centimeter, and, with the aid of a travelling magnifier, readings could be estimated to the nearest 0.01 cc. The level of mercury in the burette was adjusted by means of a leveling bulb operated by a fine screw adjustment. An electrical system, consisting of two slightly separated platinum electrodes inserted in one leg of the manometer and a small light bulb was used to obtain rapid accurate adjustment of the pressure. The capillary tubing of the Vycor sample bulb was 3 mm bore as was all tubing back to the gas burette. The samples were discs made from vacuum-melted Ferrovac-E iron of greater than

Jan 1, 1961

By E. L. Swarts

In the course of a program on high-temperature processing and electrowinning of uranium at the Knolls Atomic Power Laboratory,'' it became necessary to give attention to the interaction of molten uranium with graphite. Although it is known3 that a protective interface layer may form, details of this reaction have not been reported. Unfortunately it was impossible to complete the planned experimental program. However, the general problem is considered of sufficient interest to warrant reporting those preliminary results actually obtained. EXPERIMENTAL PROCEDURE Interface carbide layers were formed by melting samples of cleaned uranium metal in small closed graphite crucibles. Equilibrations were conducted in vacuo or in an atmosphere of dry helium at temperatures ranging from 1150" to 1400°C and for periods of from 24 to 240 hr.

Jan 1, 1960

By E. T. Stephenson

Wert and Marx1 pointed out that a straight-line relationship exists between the activation energy of a relaxation process and the temperature at which the maximum relaxation occurs. The data available at the time indicated that this relationship held for a number of Snoek peaks, several grain boundary peaks, and pair relaxation in a brass. Theoretical justification for the observed relationship was found in the following equation, which Wert and Marx derived from the theory of interstitial atomic diffusion coefficients:' where AH is activation energy, R is the gas constant, T is the internal friction peak temperature, v is the interstitial atomic frequency, f is the frequency of the applied stress, S is entropy of activation. More accurate internal-friction data on interstitial diffusion in bcc metals have become available since Wert and Marx's paper. Table I gives activation energies calculated by several authors from a combination of elastic aftereffect data and the peak temperatures at several frequencies of measurement. (In the case of Fe-C and Fe-N, the referenced authors5'7'8'10 also used high-temperature diffusion data.) However, diffusion experiments at 150°C and above1'-13—rather than anelastic techniques—were used to determine the activation energy of hydrogen diffusion in Fe-H. In order to plot this recent data as a AH vs T graph we calculated the peak temperatures of the systems listed in Table I (with the exception of Fe-C, Fe-N, and Fe-H) by using published values3'' of AH and Do. These calculated peak temperatures varied by only a few degrees from experimentally determined peak temperatures. The calculated values were felt to represent the better average. A number of investigators have found the peak temperatures in Fe-C and Fe-N to be 38 to 40°C and 20° to 24°C, respectively. The values of 39" and 22°C (312° and 295°K in Table I) were determined by carefully executed experiments.6'8 The hydrogen peak temperature has been measured at 1 cps,12 20 cps,14 and 35,000 cps.15 All hydrogen peak temperatures were adjusted to 1 cps for Table I using AH = 3000 cal per mole. As Fig. 1 shows, the data of Table I fit a straight line at least as well as the earlier data used by Wert and Marx. Linear-regression analysis was applied to the data in Table I. The Fe-H data was omitted because the activation energy has not been experimentally determined in the temperature range of the peak. The analysis yields the equation: with a standard error of 860 cal per mole. The agreement of the data in Table I with the Wert-Marx equation is excellent. Strict application of Eq. [I] forces the linear regression analysis through the origin. In this case, the analysis gives a slope of 62.1 cal per mole per deg, and a standard error of *890 cal per mole. With this value, it follows from internal-friction theory that Hence, Do varies by only 30 pct among these bcc-interstitial systems. Thus, a concept suggested originally by Wert and Marx1 is confirmed by recently published data. The

Jan 1, 1965

By R. Maddin, C. H. Mathewson, W. R. Hibbard

Recent publicationsl.2 establishing the presence of cross-slip in strained metallic single crystals oriented wholly within the area of single slip as predicted from the generalizations of Taylor and Elam3 described these markings as they appeared during the initial stages of the deformation process. At that time, the plane having a common glide direction with the primary slipping plane was reported as the cross-slip plane although the specific direction was not confirmed. Consequently, in continuation of the research, it seemed advisable to investigate the micro-graphic appearance of cross-slip together with the Laue back-reflection X ray analysis and stress-strain data during the later stages of the deformation process. Accordingly, a single crystal of brass (72.75 pct Cu, 0.01 pct Fe, 0.01 pct Pb, 27.23 pct Zn) was polished mechanically and repolished electrolytically after the manner described in the earlier paper.' Three pairs of flat surfaces, parallel to the specimen axis, and (1) perpendicular to the plane containing the pole of the primary glide plane and the specimen axis, (2) perpendicular to the plane containing the pole of the cross-slip plane and the specimen axis, and (3) perpendicular to the plane containing the slip direction and the specimen axis, were polished mechanically and repolished electrolytically, resulting in a final minimum gauge diameter of 0.4864 in. in a gauge length of 3.36 in. The specimen was elongated in tension and load-extension readings were taken following the method described in the initial investigation.' Observed reorientations were obtained from a series of Laue back-reflection photograms at the center and ends of the gauge length and at various positions around the circumference of the specimen. These were interpreted after the manner of A. B. Greninger.4 Cross-slip (Fig 1 and 2) was found with the first appearance of the primary slip clusters and usually joined members of these clusters. In addition, a third set of entirely different markings (Fig 3) could be noted. The displacement of this third set by the primary slip lines was measured as 8300 at. diam (3.04 microns). Since the specimen was carefully observed at high magnifications before any deformation and no markings of any type could be noted, it would appear that this third set was formed during the deformation process prior to the initiation of classical primary slip. Additional extensions produced no unusual change in the appearance of either cross-slip or the third set of markings. The number of lines increased with increasing elongation and appeared, generally, in areas where earlier markings were present. The continuity of the clusters of cross-slip lines in Fig 4, 5 and 6 illustrates that they are neither noticeably displaced by nor do they displace the primary lines at this stage. In Fig 7, cross-slip appears in a long narrow localized band approximately 45 degrees from the stress axis. This somewhat resembles a twin band except for the lack of a sharp boundary. After a shear of 0.257, suffcient additional glide occurred on the cross-slip plane to displace the primary slip lines (Fig 8). Generally, where a large number of cross-slip lines could be observed in an area on one flat surface, few cross-slip lines appeared on the diametrically opposite position on the parallel flat (Fig 9). These, of course, were not matched observations on the same glide ellipses. It was extremely difficult to make such comparisons. The third set of markings (Fig 10) was extensively displaced by glide on the primary slip planes. A plot of the width of primary slip clusters versus their displacement of the third set of lines is shown in Fig 11. The slope and the linearity of the plot suggest that each primary glide plane slips to a constant maximum value of shear before further slip is transferred to another plane. A shear value of 0.28 was determined in this case. Heidenreich5 has presented a similar schematic representation of glide for aluminum. After the specimen had attained an elongation of 51.8 pct, corresponding to a shear of 0.973, cross-slip appeared very prominently in certain areas as shown in Fig 12, yet at diametrically opposite positions very little cross-slip could be noted, Fig 13. Classical conjugate slip was found at this advanced stage in the deformation, Fig 14, which corresponds to the axial location shown at 12 in Fig 15. It should be noted that cross-slip occurs within the conjugate slip clusters and on the same plane as the cross-slip associated with the closely spaced primary lines which constitute a background in less distinct focus. The third set of markings noted at all stages in the deformation of the

Jan 1, 1950

By R. P. Smith

The carbon content of a number of alloys ranging (before carburitation) from purified iron to purified cobalt was determined for fixed activities of carbon by equilibration with each of six CO-CO2 atmosphere at 1000°C. At fixed carbon activity, the carbon content decreases continuously with increasing cobalt content. For concentrations of 0 to 50 at. pct Co the results can be expressed by a linear interaction equation of the type In y2 = 7.76n2/(n1+n3)+ 2.30 n3/(n1+n3) where y2 is the activity coefficient of carbon (standard state such that y2— 1 as n2 — 0 in the Fe-C binary) and n1, n2, and n3 are the number of atoms of iron, carbon, and cobalt per unit weight of alloy. The results are also given in terms of the a functions. In the same concentration range, the results are in accord with the regular solution theory of Alcock and Richardson. THE carbon content of Fe-Si, Fe-Mn, and Fe-Ni alloys at fixed activities of carbon has been reported previously.'-, The present work extends R. P. SMITH, Member AIME, is Research Chemist, E. C. Bain Laboratory for Fundamental Research, United States Steel Corp., Research Center, Monroeville, Pa. these measurements to a series of Fe-Co alloys. These alloys, like the Fe-Ni alloys, are fcc ("aus-tenitic") over the entire range of composition at 1000°C. EXPERIMENTAL PROCEDURE The alloys were made from electrolytic cobalt and Plast-Iron in a small vacuum-melting furnace. A small amount of graphite was added to each melt to keep the oxygen content low. The ingots were analyzed for iron and carbon: the amount of cobalt was obtained by difference. Analysis of the top and bottom of the ingots indicated that they were uniform in alloy content. Except for the pure cobalt the ingots were hot-rolled to approximately 0.15 cm thickness, cleaned by sandblasting, then cold-rolled to about 0.045 cm. We were not successful in cold rolling the pure cobalt; therefore it was hot-rolled to the final thickness. The last traces of surface oxide were removed by acid pickel, then the samples were treated in a hydrogen-2 pct water vapor mixture at 1100°C to remove carbon and most of the oxygen. The carburizing procedure was similar to that previously described.1,2,4 The alloys in the form of strips about 1.7 cm wide, 7.5 cm long, and 0.04 cm thick, together with a similar specimen of purified iron, were equilibrated with each of six CO-CO2 mixtures of fixed composition, then quenched in the

Jan 1, 1965

By P. G. Winchell, A. J. Heckler

An experimentally simple method for determining the effect of alloying elements on the activity of carbon is validated in Fe-Ni-C austenite. The technique consists of the equilibration of carbon between specimens of different nickel contents within a sealed silica capsule. The attainment of carbon equilibrium within each capsule is evidenced by: 1) in each capsule specimens of the same nickel content attained the same final carbon content regardless of their initial carbon contents, 2) in every capsule the final carbon content was reached for most nickel contents by carburizing and by decarburizing. The activity of carbon attained within each capsule was calculated from the carbon content of a binary Fe-C alloy placed within the capsule, and from the activity coefficient of carbon in the Fe-C system as found by Smith for CO/CO2/C equilibrium. The activity of carbon in Fe-Ni-C austenite determined by this method at 1000°C agrees with prior work by Smith, who used mother method. The measurements are extended to 800°and 1200°C. The activity coefficient of carbon 7c, in Fe-Ni-C austenite is given by: where xC is the ratio of carbon to metal atoms and XNi is the ratio of nickel to metal atoms and where the standard state is chosen such that yC = 1 as xc approaches zero in Fe-C alloys. This equation appears to be valid for xni < 0.3, and 1073° < T<1473°K. ThE activity of carbon in Fe-C austenite has been measured by smithL at 800°, 1000°, and 1200°C. Smith has also studied the effect of nickel on the activity A. J, HECKLER and P. G. WINCHELL are Graduate Student and Associate Professor of Metallurgical Engineering, respectively, School of Metallurgical Engineering, Purdue University, Lafayette, Ind. This paper is based on a thesis submitted ty,to Purdue University, in partial fulfillment of the requirements for the degree of M.S. in Metallurgical Engineering which A. J. HECKLER received from Purdue in January 1962. Manuscript submitted August 13, 1962. IMD of carbon in austenite at 1000°C. In both these studies the activity of carbon was fixed by a flowing CO-C02* *Gas mixtures of hydrogen and methane were also used in Ref. 1 but these results are not incorporated in Ref. 2 or in the present study. gas mixture. In the present work, Smith&apos;s results for Fe-Ni-C austenite are confirmed and extended to 800" and 1200°C by a different experimental technique. EXPERIMENTAL PROCEDURE In essence the experimental technique consisted of enclosing specimens of various nickel contents in an initially evacuated silica capsule and annealing the capsule until carbon equilibrium was attained among the enclosed specimens. The carbon activity obtained within the capsule was determined from the final carbon content of the binary Fe-C alloy included in each capsule and the results of smith.&apos; In order to evaluate this method the absence of nickel transfer between specimens must be established and the attainment of carbon equilibrium between samples must be assured. The absence of nickel transfer was demonstrated in the case of an originally pure iron sample which was annealed at 1200°C in a capsule with a 27.3 at. pct Ni alloy. The final nickel content of the iron specimen was less than 0.1 at. pct, a change which has a negligible effect on carbon activity. The attainment of carbon equilibrium was demonstrated within every capsule and in over half the results by achieving the same final carbon content in a sample which carburized during equilibration and in a sample of the same nickel content which decarburized during equilibration. The base Fe-Ni alloys were vacuum melted from Ferrovac E or electrolytic iron and Mond or electrolytic nickel. The samples were rolled and/or swaged and their carbon content adjusted to the desired pre-equilibration level either by methane-hydrogen carburization or by direct carbon transfer from a graphite source in a sealed silica capsule. As mentioned previously, high-carbon and low-carbon samples were prepared for most nickel levels in each capsule. The specimens were cleaned and

Jan 1, 1963

By W. Evans, C. E. Ells

The agglomeration of hydrogen in pure aluminum and A1-Mg alloys has been studied through use of hydrogen introduced into the metal by cyclotron proton irradiation. Both the growth and dispersal of the agglomerates have been followed by metal-lographic techniques. During the cyclotron irradiation, agglomeration occurs at temperatures i 100°C for hydrogen concentrations as low as 1 ppm. On heating at elevated temperatures, 300°C to 600°C, intragranular agglomerates first coarsen and then disperse. The agglomerates formed at grain boundaries are much larger than the intragranular agglomerates; with hydrogen concentra- tions > 10 PPm, heating for 1 hr at 500°C results in extensive grain-boundary cracking. The hydrogen agglomerates have been shown to inhibit grain growth, but no inhibition of recrystallization has been observed. The ability of hydrogen to enter aluminum at a free surface, combined with its high-diffusion rate at elevated temperatures, accounts both for growth and dispersal of the agglomerates. Irradiations at elevated temperatures give results consistent with the explanation proposed for agglomerate behavior on post-irradiation heating. 1 HE formation of hydrogen-filled bubbles, or blisters. in aluminum and its alloys has been studied for over&apos; thirty years. The work up to 1952 has been reviewed by Kostron&apos; and since then Ransley and

Jan 1, 1963

By G. T. Murray

The aging behavior of a Cu-Ti (3.2 at. pct Ti) alloy has been followed by electrical resistivity, hardness, and metallographic changes. The resistivity data indicate two principal processes, the first causing a sharp decrease in resistivity, and the second, which occurs over a long period of time, a much smaller rate of decrease. Lamellar nodules, Widmanstätten platelets, and homogeneous continuous precipitation was observed. The Widmanstätten platelets grow at the expense of the latter. When this study was initiated, little information was available on the aging behavior of copper-base titanium alloys. Several articles&apos;-3 that appeared in the early 1930&apos;s showed that these alloys could be strengthened by precipitation, but a detailed study was not made. Within the past year, however, two other more comprehensive studies4&apos;5 have been reported in the literature, one consisting primarily of an investigation of mechanical properties, the other

Jan 1, 1961

By J. M. Dupouy, R. A. Rawe, M. B. Bever

The aging characteristics of a titanium alloy containing 13 pct V, I1 pct Cr, and 4 pct A1 have been investigated by hardness measurements, X-ray diffraction, and metallography. The P phase decomposes into 0 + a, and 0 + a, + TiCr, above about 1050°F; below this temperature a transition phase, believed to be w, precipitates first, followed by a, and TiCr,. The observed hardening is attributed to these reactions. Cold working of solution-treated specimens accelerates hardening and raises the hardness level attained. A TTT diagram is proposed. NEW titanium-base alloys, designated as "all-beta," have recently been developed. These alloys contain large amounts of P-stabilizing elements such as molybdenum, chromium, or vanadium. When cooled from the solution temperature, they consist only of P; in particular, the martensitic a,&apos; phase does not form.

Jan 1, 1961

By H. C. Rogers

It has been shown previously&apos;- 3 that when a mild steel or iron is charged with hydrogen, the normally observed yield point is eliminated or considerably

Jan 1, 1960

By A. R. Kaufman, P. Gordon

THE large-scale manufacture and use of uranium in conjunction with the atomic energy development during the war led to a need for knowing the equilibrium diagrams of uranium with various other metals. The alloys of uranium with aluminum and with iron were among the first that were studied for this purpose. Much of the work was done in the manner of a survey since it was necessary to determine the important features of the phase diagrams rather than to obtain completely detailed results. For this reason no attempt was made to locate exactly such features as liquidus lines, solid solubility limits and compound and eutectic compositions. It is believed, however, that there are no great inaccuracies in the diagrams reported here and that no important points were overlooked. Earlier work on alloys of uranium with aluminum and iron is almost nonexistent and in each case is considered to have been of little value by M. Hansen. It is interesting to note, however, that the compound UAl3 was first reported in 1902 by L. Guillet. Experimental Procedure Materials: The uranium used for making most of the aluminum alloys was obtained from material prepared by Metal Hydrides, Inc., and melted in vacuum at M.I.T. Because of the lack of an adequate supply of metal, it was necessary to use material from several different batches and hence it is impossible to state an exact analysis. However, a few results indicated about 0.01 to 0.03 pct iron and probably about 0.03 to 0.05 pct carbon. Toward the end of the work a small amount of metal was obtained from Brown University and from Iowa State College and this was used in determining the transformations in pure metal and in some dilute alloys. All of the aluminum used in this investigation came from a supply of high purity metal (greater than 99.9 pct aluminum) which was obtained through the courtesy of Dr. Mehl of the Carnegie Institute of Technology. The uranium used for making the alloys with iron was produced by the bomb reduction process which has been described by J. Chipman.² This metal, after vacuum melting, contained about 99.9 pct uranium by weight with carbon and iron as the chief impurities. Electrolytic iron containing about 0.012 pct carbon, 0.020 pct nickel and 0.009 pct copper was used in making the melts. Melting Equipment: The melting of the alloys went through a stage of development which culminated in the use of beryllia or beryllia-lined crucibles and in the use of high frequency heating in either vacuum or in an atmosphere of argon. It was found that uranium at a few hundred degrees above its melting point would pick up aluminum and to a lesser extent silicon from an alundum thimble while aluminum above 1000°C would extract silicon from the impure alundum. No reaction of either metal with beryllia was noted at temperatures as high as 1800°C. The distillation of aluminum from the aluminum-rich alloys was quite troublesome at temperatures above about 1300°C and was only partially avoided by the use of argon instead of vacuum. Melting in resistance furnaces,

Jan 1, 1951

By A. R. Kaufman, P. Gordon, C. H. Schramm

AS a part of the general program on alloys of uranium carried out at the Massachusetts Institute of Technology under contract W-7405-eng-175 for the Manhattan Project during the recent war, it was considered desirable to investigate the boundary binary phase diagrams of the ternary alloy system uranium-tungsten-tantalum. Previous work on these alloys was practically nonexistent. A brief statement to the effect that tantalum and tungsten form a continuous series of solid solutions was found in a general paper on tantalum by W. V. Bolton1 but no information was available on the uranium-tungsten and uranium-tantalum systems. The research to be described in this paper has served to delineate the main features of the uranium-tungsten, uranium-tantalum phase diagrams and to check Bolton&apos;s work on the tungsten-tantalum diagram. Experimental Details Metals: The tungsten and tantalum used for preparing the alloys were 99.96 and 99.65 pct pure, respectively. The chief impurities in the metals were about 0.02 pct molybdenum in the tungsten, and 0.2 pct columbium, 0.05 pct tungsten, 0.02 pct barium and 0.01 pct silicon in the tantalum. The uranium used was 99.9 pct pure, with the main contaminants being iron and carbon. (An appreciable amount of magnesium was present in the uranium as received, but this distilled off during melting and so is not reported as an impurity.) The composition of specimens indicated in the subsequent figures and tables of this paper are the results of chemical analyses on the cast alloys except for the tantalum-tungsten alloys. For the latter, chemical analysis was not very reliable as a result of the difficulty of separating tungsten and tantalum chemically. Consequently, the nominal

Jan 1, 1951

By Irving Cadoff, Jack Medoff

THE linear thermal expansions of oriented single crystals of zinc were measured in the range from 20" to 416°C using a Leitz HTV optical lever differential dilatometer. The single crystals, supplied by Dr. J. J. Gilman, General Electric Research Laboratory, Schenectady, N.Y., were prepared from 99.999 pct-purity zinc, and were in the form of rods approximately 2 in. long by 0.15 in. in diameter having the following orientations: x = 1.5, 12, 20, 30, 37.5, 49, 60, 73, and 82 deg where x is the angle between the specimen axis and the (0001) plane of the crystal. From the family of expansion vs temperature curves, the instantaneous expansion coefficients were calculated at 100°C intervals, and Fig. 1 shows a plot of these derived coefficients for each orientation. Coefficients were obtained from the raw data using the chord-slope method. The curves in Fig. 1 indicate a positive temperature coefficient for low x, a negative temperature coefficient for high X, and an expansion coefficient invariant with temperature, amounting to about 43 x 106, for a crystal orientation of approximately 52 deg. From the available data, it is possible to arrive at the values for the axial thermal-expansion coef- ficients a, and a, by extrapolating the curve of the expansion coefficient vs orientation to zero and 90 deg orientations. More precise values for a, and a, are obtained if the instantaneous coefficients are plotted against the square of the cosine of the orientation angle, as shown in Fig. 2. The extrapolated terminal points of the best straight line through the data points of such a plot define the axial coefficients at that temperature. The theoretical justification for the linearity of this curve comes from inspection of a rearranged form of the general anisotropic equation for expansion: ax=a, + (a, -a,)cosZx [1I in which a, is the expansion coefficient in the "c" or [0001] direction and a, the expansion coefficient in the "a" or [ll50] direction. From Fig. 2, the axial coefficients at 100°C, for example, were found to be a, = 13.9 x 10&apos;6 and a, = 62.4 x 10"6 per "C. In the same way, the coefficients were determined for 20", 200°, 300°, and 400°C. This data is summarized in Fig. 3. It is of interest to observe the common intersection of the curves in Fig. 3, which seems to bear out the earlier observation, from Fig. 1, of a

Jan 1, 1964

By Paul Gordon, A. S. Iyer

Apreliminary investigation has been carried out on the annealing behavior of explosively deformed copper as compared to that of conventionally deformed copper, using hardness, stored energy, and the sharpening of X-ray spots on Debye rings as the measures of annealing. Some metallographic observations were also made. Two purities of copper were studied. The first was tough pitch copper obtained as a small piece from the guard ring of a sample explosively deformed to approximately 500 kbars.* The second consisted of mentedand deformed these samples quite badly so that only a few small fragments were available for the annealing experiments. As a result, little in the way of quantitatively significant data was gleaned from the measurements. However, several important qualitative differences between the annealing of explosively deformed and conventionally deformed copper have been observed. It is these effects which are described in this report. Fig. 1 presents the results of hardness and stored energy measurements during the annealing of the high-purity copper after explosive and after conventional deformation. The data for the conventionally deformed copper were taken from the work of Gordon;&apos; in this copper it is evident that most of the stored energy is released concommittantly with the hardness drop. As shown in orddon&apos;s&apos; investigation, these effect:: are definitely associated with recrystal-lization. In the case of the explosively deformed copper, on the other hand, a large fraction of the stored energy is released before any appreciable hardness change takes place. At 160°C about 40 pct, and at 170°C about. 80 pct, of the stored energy appears to have been released prior to the onset of softening, i.e., undoubtedly prior to recrystallization. In view of the facts that the hardness and energy measurements were made on separate samples and that there is reason to suspect that the intensity of the explosive deformation from sample to sample may not have been uniform, a check run was carried out in which both energq release and hardness changes were measured cnn the same sample. The results of this run, shown in Fig. 2, confirm the conclusion that much of the stored energy is released before the hardness begins to change appreciably. In an effort to obtain some idea of the activation energy associated with the early release of energy, a single callorimetric sample was annealed in two steps, first at 149.5"C and then at 159.5"C, Fig. 3.

Jan 1, 1962

By R. O. Scattergood, P. Beardmore, M. B. Bever

THE stored energy and microhardness of a Au-Ag alloy deformed by explosive loading were measured previously as functions of shock pressure&apos; and compared with corresponding data for drawn wires.&apos; The difference of the two processes has been explored further by investigating the annealing behavior of explosively loaded specimens and drawn wires. Sheet specimens, 0.042 in. thick, of a Au-Ag alloy containing 82.6 wt pct Au were explosively loaded in stacks of four.3 Wires prepared from the same melt of alloy were drawn through dies.&apos; The annealing kinetics were determined by microhardness measurements on separate specimens for each annealing temperature and time. Several values of the stored energy were measured by tin-solution calorimetry Experimental details are given elsewhere. Wires were drawn until the microhardness or stored energy equalled the corresponding values of the explosively loaded specimens as nearly as possible. Wire drawn to a true strain 7 of 0.09 had approximately the same hardness and stored energy as specimens explosively loaded to a shock pressure of 70 kbar. The microhardness of specimens

Jan 1, 1963

By A. E. Deruyttere, J. Van der Planken, M. Laurent, Van den Bergen

FahRENHORST and schmid1 observed that zinc single crystals work hardened less rapidly when strained in liquid air (- 185°C)than in a bath at -82°C, whereas at higher temperatures the rate of work hardening decreased with increasing temperature, as would be expected. Cadmium and magnesium showed no such decrease at -185°C. At that time the observed anomaly for zinc at liquid air temperature probably seemed insignificant. However it later was confirmed2 by experiments in liquid nitrogen (-196°C) and in the mixture solid carbon dioxide-acetone (-77"C) and therefore appeared to be real. seeger3 then suggested that the anomaly might be due to the different wetting of the zinc crystals by the cooling media. Recently a new confirmation was obtained,4 however the cooling media again were different: the rate of strain hardening was found to be lower in liquid nitrogen and liquid oxygen than in pentane cooled to various temperatures down to -126°C. Ekperiments will now be reported in which the medium surrounding the specimen at the different temperatures was the same, namely gaseous air. The single crystals were made from "Overcor 99.99" zinc. They were grown in a vertical traveling furnace on seeds of nearly the same orientations. The diameter of the crystals was 5 mm and the length between shoulders 140 mm. The brass shoulders were stuck to the crystals by means of araldite. A thin steel wire was fixed to each shoulder and served to fasten the specimen to a Houns-field tensile testing machine. The crystals with the shoulders and part of the wires were surrounded by two concentric cylindrical containers. The coolant. either liquid air or ground solid carbon dioxide, was poured into the outer container only. During cooling the containers rested on a support which was removed when the straining was started. In order to check the temperature which the crystals would attain inside the inner container, a hollow bar of zinc in which a thermocouple was fitted was first mounted in the apparatus as a substitute for a crystal. It appeared that a constant temperature, respectively - 183° and -72°C, was attained inside the bar, if a soaking time of the order of 1 hr was allowed and if the outer container was constantly kept filled. Accordingly, this procedure was adopted for every tensile test. To take account of the large scatter, fourteen tensile tests were performed with liquid air and seven with solid carbon dioxide. The orientation of the crystals and the results are presented in the table, in which the symbols have the following meaning: 1 : temperature x : initial angle between basal plane and specimen axis : initial angle between slip direction and specimen axis a : shear strain at fracture 0: average rate of strain hardening = —-——- 100 t0 and Te representing respectively the critical shear stress and the shear stress at fracture. Despite the scatter of the a- and 8— values which is of the same order of magnitude as in the work reported by Seeger and Trzuble,4 it is evident that the strain hardening rate is significantly lower at -183°C thanat-72°C. The table also contains the average values calculated from Seeger and Trauble&apos;s results at the corresponding temperatures: z.e., four results at -183oC and two at-70°, -71°C. These authors calculated 9 in a slightly different way, but this is unimportant. The agreement between the a-values shows that both sets of experiments are comparable despite the differences in experimental techniques. The rates of strain hardening also agree and it may therefore be concluded that the anomaly is not

Jan 1, 1962

By A. H. Daane, B. J. Beaudry

The uranium-antimony system has been investigated by metal-lographic, therma1, and X-ray methods. There are four intermediate phases present: USbz and U,Sb, which undergo peritectic decomposition at 1355°and 1695OC, respectively, and USb and UPSbs which melt congruently at 1850"and 1800°C, respectively. There is a eutectic between U4Sbs and USb which melts at 1770°C. USb,, UsSb4, and USb are line compounds while U4Sbs has a solubility range of approximately 1.5 at. pct at 1770°C. Single crystal studies of the cmpo,und U.,SbS show it to have a hexagonal unit cell with a, = 9.268A and c, = 6.201b;. The solubility of uranium in liquid antimony increases from 0.1 at. pct at 650°C to 1.5 at. pct at 900°C. The solubility of antimony in a, P, and y uranium is approximately 0.02, 0.1, and 0.05 at. pct respectively. IN nuclear reactors, uranium has been used mainly in the form of solid-fuel elements of the pure-metal or uranium-rich alloys. However, in attempts to overcome some of the difficulties inherent in solid-fueled reactors, reactor concepts hive been proposed in which the fuel would be a liquid metal, such as a solution of uranium in another metal. The liquid-metal fueled reactor (LMFR) designed by the Brook-haven National Laboratory of the U.S. Atomic Energy Commission is an example. Fuel for this reactor is a solution of approximately 800 ppm enriched uranium in bismuth.&apos; To design such liquid-fueled reactors, a background of information on the solubility of uranium in various metals is obviously necessary. The present study was undertaken to pro- vide information for such purposes, and in addition, to study the uranium-antimony system as a whole. A preliminary literature search showed that some work had been done previously on uranium-antimony alloys, but no attempts had been made to make a complete study of this system. The solubility of uranium in antimony was studied by Cammack and Bridger&apos; up to 950°C and by Hayes and Gordon up to 900&apos;-C. Their data are plotted in Fig. 1. Ferro, in an X-ray structure study of some uranium-antimony compounds, found USg to be tetragonal with a, = 4.2724 and c, = 8.471A, U3S4 to be b.c.c. with aO = 9.095A and USb to be f.c.c. with a,= 6.191A. Colani reported the compound UsSba; however, work by Ferro and by this Laboratory showed that this compound does not exist. foote&apos; reported several intermediate phases in the uranium-antimony system, but did not identify them. Greninger&apos; re-ported finding an intermediate phase in a 5 at. pct Sb

Jan 1, 1960

By G. Koves

The behavior of case-hardened AISI C-1213 free -machining steel under complex impact-fatigue -wear load conditions was investigated. The inherently poor dynamic properties of the steel are mainly affected by the stress distribution in the case, component shape, and tempering. Cold-riveted components showed unexpectedly high dynamic strength compared to basic parts. A compromise beatment—which provides good dynamic properties, reasonable wear resistance, and fair riveting characteristics—zuas developed. A number of mechanical components in data-processing machines are made of free-machining carbon steel. Although, selected primarily due to manufacturing requirements, components made of these grades frequently undergo complex heat treatment and must sustain impact-fatigue loads. A typical free-machining steel is the AISI C-1213 grade, which is a resulfurized and rephosphorized open-hearth steel. While the undesirable effects of sulfur and phosphorus on the mechanical properties are well-known, data on dynamic properties are scarce.1"3 Rapid rotating or oscillating motion while carry- ing a high cyclic load requires a combination of wear resistance with high endurance limit and impact toughness. The inherently poor dynamic properties of the free-machining steel are further degraded by the machining, which introduces local stress-concentration areas. While the heat treatment (usually case hardening) improves some mechanical properties, it necessarily impairs others. Another problem arises when components, such as studs, must be fastened by riveting. The high crack-sensitivity of the free-machining steel, especially in the presence of a hardened case, makes this operation difficult. In view of the preceding considerations, it is of interest to investigate the behavior of a typical component under complex impact-fatigue-wear loading conditions in order to explore the effects of material, machining, and heat treatment, to obtain specific data on the dynamic characteristics of free-machining steel, and to arrive at a process which would adequately utilize the inherent qualities of this material. EXPERIMENTAL PROCEDURE To simulate actual service conditions, a typical component was selected, based on frequency of application, complexity of load, and processing difficulties. The dimensions and shape of the component—a stud used in many electromechanical document-handling machines—are shown in Fig. 1.

Jan 1, 1964

By N. F. Foster

The use of piezoelectric semiconducting materials for the fahrication of ultrasonic transducers has raised the upper fundamental frequency limit for transducers from about 200 mc to above 10 kmc, Several types of semiconductor transducer configurations have been proposed and examined experimentally. Depletion-layer transducers have been made and operated at frequencies below 1 kmc hut they appear to he better suited for operation at considerably higher frequencies around 10 knzc. Diffusion-layer transducers have been made and operated in the range 50 to 1000 mc and have exhihited considerably improved conversion losses and bandwidths compared with other transducers available in the frequency range. A variety of novel structures are possible using these new types of transducers, some of which could lead to substantial advances both in research and in the fabrication of ultrasonic delay lines and memory elements. THE field of ultrasonics today spans some five decades of the frequency spectrum from the audible to the kmc range and finds applications ranging from fundamental research into the atomic structure of matter to the degreasing of machine parts. To cover this wide range it has been necessary to develop a great many types of ultrasonic trandsucers utilizing a variety of materials and physical phenomena. The first ultrasonic transducers were made during World War I for a submarine-detection system. They consisted of plates of single-crystal quartz bonded between metal plates and were one of the first applications of the phenomenon of piezoelectricity discovered nearly 30 years previously. Despite the many advances which have been made in transducer technology, piezoelectric transducers using single-crystal quartz are still used almost exclusively for application above about 30 mc. Transducers at these frequencies are normally made in the form of thin quartz plates which are then bonded onto the medium in which the ultrasonic wave is to be propagated. The crystallographic orientation and geometry of these plates determines the type of wave generated and the way in which the efficiency of the electromechanical conversion varies with frequency. Analysis of the design parameters shows1 that the frequency of maximum efficiency (the fundamental or resonant frequency) is that frequency at which the transducer is approximately half the wavelength of the ultrasonic wave in the material. As the frequency increases, the ultrasonic wavelength, and therefore the optimum transducer thickness, decreases and in practice the fabrication of quartz transducers with fundamental freauencies above 100 mc becomes extremely difficult due to the extreme thinness required. For frequencies above 100 mc quartz transducers can be used in overtone-mode operation, and for very high frequencies (500 to 24,000 me) a technique using a quartz rod inserted in a high-Q microwave cavity4 is available. These techniques, however, exhibit comparatively low fractional bandwidths and rather poor conversion efficiencies. The present trend in ultrasonics is towards high frequencies and greater bandwidth to allow the use of shorter pulses which can give increased discrimination in radar-system delay lines and greater storage capacity in computer applications. The increasing demand for more efficient transducers with greater bandwidth

Jan 1, 1964