By D. H. Turner, F. A. Crossley

The titanium-rich corner of the system Ti-Al-Si has been studied to determine the phase relationships in the temperature interval 600° to 1200°C. Metallographic examination of long time isothermally annealed specimens was the means of investigation. PART of a program on phase relations and transformation processes of titanium alloy systems included the study of the titanium-rich corner of the Ti-Al-Si system. The investigation covered ternary compositions in the range 2 to 8 pet A1 and 0.1 to 2 pet Si and binary compositions in the range 0.2 to 2 pet Si. Temperatures were in the range of 600" to 1200°C. Alloys containing 6 pet A1-0.1 to 0.5 pet Si were investigated down to 400°C. Partial vertical sections are presented for 2, 4, 6, and 8 pet Al. The Ti-Si system has been reported by Hansen et al.' It is characterized by a eutectoid decomposition, ß = ± a + Ti3Si3, at 860°C. The maximum solubility of silicon in a is reported to be about 0.5 pet at the eutectoid temperature. The solubility of silicon in 0 increases from 0.9 pet at the eutectoid temperature to approximately 3 pet at the eutectic temperature, 1330°C. Several investigations in the composition range of interest have been reported for the Ti-A1 system."' These investigations are in agreement on the phase fields, but differ to small extents on boundary positions. However, very recent, and as yet unpublished, findings" " indicate that there are perhaps two phases which occur at lower aluminum contents than the ? (TiA1) phase, and that the solubility of aluminum in a titanium is less than 6 pet. In the present investigation phase relations found are in agreement with the published literature exemplified by the work of Bumps et al.3 Therefore, it is probable that the partial system reported herein is metastable and does not represent true equilibrium. Experimental Procedure High purity Bureau of Mines titanium sponge of 103 Bhn hardness, granulated aluminum shot of 99.7 pet purity, and silicon powder of 99.8 pet purity were used in making the alloys. For the work in the range from 600" to 1200°C, 100 g ingots were prepared by arc melting. Melting losses were negligible and spot checks by chemical analysis showed good agreement between nominal and analyzed results. Nominal compositions are used throughout this paper. Ingots were forged to 3/8 in. rounds and cut into specimens for heat treatment. Isothermal anneals in the range from 600" to 900°C were preceded by solution treatment at 1000°C for 1 hr, followed by furnace cooling to the annealing temperature. Samples were sealed in evacuated Vycor bulbs for heat treatments up to 1000°C. Higher temperature anneals were done with the samples sealed in quartz bulbs under a partial pressure of argon.

Jan 1, 1959

By N. Parlee, V. C. Kashyap

The solubilities of nitrogen in liquid iron and liquid Fe-Ni, Fe-Mo, Fe-V, and Fe-Mo-V alloys were measured by the Sieverts method. Measurements were made at 1600° to 1800°C on binary alloys up to 20 pet Ni, 10 pet V, 10 pet Mo; and on ternary alloys containing 0 to 3 pet V with 0 to 5 pet Mo. The results on liquid iron confirm that Sieverts' law is obeyed in the range 50 to 750 mm pressure. The measured solubilities and their temperature coefficients are in general agreement with other modern authors. The logarithms of the activity coefficients of nitrogen in the binaries are approximately linear functions of the pet of alloying element. A method suggested by Wagner, Chipman, and others for predicting gas solubilities in complex alloys from solubility data on binaries was applied to the Fe-Mo-V alloys. Reasonably good agreement was obtained between calculated and experimental solubilities. NITROGEN'S solubility in liquid iron has been studied by a number of investigators. It is reasonably well established that the solubility of nitrogen follows Sieverts' law at least up to 1 atm partial pressure and that the solubility increases gradually with temperature. The solubility of nitrogen in Fe-X binary liquid systems has been investigated in only a few cases. Only the systems Fe-Cr,3-5, 7 Fe-V,3 Fe-Mn,3, 5 Fe-Ni,3, 5 Fe-Si,B, H Fe-C, L, H and Fe-P4 appear to have received any study. The only work on liquid Fe-V was done by Brick and Creevy.3 This was limited to 13.5 pet and 26.5 pet V, but no exact temperatures were recorded. No work whatsoever appears to have been done on liquid Fe-Mo alloys and even work on Fe-Ni alloys is rather scant. The work on liquid ternary systems is still more limited, and the only publication available appears to be that of Wentrup and Reif,7 who studied the Fe-Cr-Mn and Fe-Cr-Ni alloys. Rassbach, Saunders, and Harbrecht17 have reported work on the solubility of nitrogen in stainless steel but this was not a systematic study of any particular system. Commercial alloys usually contain several alloying elements. Thus, it often becomes important to be able to predict the nitrogen solubility in systems containing two or more added elements without the necessity of making measurements. Wagner,14 Chipman," Darken and Gurry," and Morris and Buehl 14 have suggested means by which this may be accomplished, and Langenberg14 has recently applied one of these methods to nitrogen solubility in complex liquid alloys. This paper reports the results of nitrogen solubility determinations on Fe-Ni, Fe-Mo, Fe-V, and Fe-Mo-V alloys and compares calculated and experimental solubilities in the ternary alloy. Attempted measurements on Fe-Cr alloys were not successful by the experimental method employed. Experimental Method The general method of solubility measurement was that of Sieverts.' The apparatus and procedure were essentially the same as used by Liang, Bever, and Floe."' The equipment consisted of a small vacuum furnace heated by a 6 kw induction unit, gas measuring apparatus, and a gas purification train. The crucibles used were Norton Alundum with alumina sand around them for insulation. The crucibles were charged with 100 to 200 g of material, about 180 g or nearly filling the crucible being found most satisfactory. Hot volumes were determined with argon and ranged from 95 to 130 cu cm (stp). Temperature measurements were made with a Leeds and Northrup optical pyrometer which was calibrated periodically against the melting point of iron in the same apparatus."-'* Good quality nitrogen, hydrogen, and argon gases were further purified and dried in standard purification trains. The sources of the high purity iron and other alloying elements used were as follows:

Jan 1, 1959

By J. L. Gillson

Andre Hubaux: In the writer's opinion, more stress should be put on field and microscope observations, as J. L. Gillson does. His discovery of relics of big labra-dorite feldspars from the Marcy anorthosite in all the other rocks is proof enough that previous field observations have been inadequate. The writer's field experience with anorthositie massifs is limited to the Egersund-Sogndal district in southern Norway; however, this is a very large and well exposed area. It seems to have so many points in common with the Adirondack region that a detailed comparison should be beneficial. This comparison was not possible 20 years ago, owing to the scarcity of geological data, at least for Norway. Both regions are now far better known—the Norway district because of the work of Professors Bugge and Barth 33-35 and especially because of the extensive field and microscopic research of P. Michot,30-35 who introduced me in the field to the problems of that region. In a particular unit of the Egersund district, a sodi-fication of the plagioclase, very similar to what Gillson calls "andesinization," has taken place. 12' The percentage of anorthite in the plagioclase has dropped from 42 to 43 pct in the original norite down to 27 pct, but never below that level. This metasomatical transformation is a part of a whole series of processes of mig-matitization which have produced, above the level of granitization, concentrations of Mg, Fe, and Ti and among them, patches and parallel bands of ilmenite and magnetite. Thus both regions present somewhat comparable features and the theories to explain them have several points in common. However, as there seem to be differences between some American conceptions and the views commonly accepted at the University of Liege, I would like to make some comments about J. L. Gill-son's article. The author speaks of the garnet as being an anti-stress mineral. However, garnet may be found in schists, where its helicitic texture, when present, demonstrates its formation during differential movement. Furthermore, the whole concept of stress and anti-

Jan 1, 1959

BUFFALO C E Moyer, Chairman (Buffalo, N Y I R M Jordan, Vice-Chairman H A Morlock, Secretary CHICAGO M E Nickel, Chairman (Chicago, Ill ) A M Kroner, Vice-Chairman W R McLain, Secretary-Treasurer

Jan 1, 1959

By J. J. Becker

Changes in magnetic properties with particle size are used to study the precipitation process in a Cu-Co alloy. In particular, the effect of a field during aging in producing anisotropy is shown to occur entirely during the growth of the particles, after precipitation is complete. HEAT-treatment in a magnetic field is done commercially to improve the magnetic properties of a number of materials. These can be divided into solid-solution alloys and precipitation alloys. The Permalloys are representative of the first type, and magnetic annealing greatly increases their maximum permeability. On the other hand, in precipitation alloys such Alnico 5 the important result is an increase in maximum energy product. The effect of the field in all cases is to bring about an additional magnetic anisotropy, uniaxial in nature, which makes the hysteresis loop more upright when measured in the direction in which the field was applied. The structural origin of the anisotropy brought about by magnetic annealing is not well understood. In the solid solution alloys, one possible explanation is based on ordering.' Another possibility is the orientation of like-atom pairs.' The precipitation systems known to respond to magnetic heat treatment are Alnico 2, in which the effect was first discovered," Alnico 5, cobalt ferrite (oxide),' and Cu-Co alloys.3 n these materials, the field affects the precipitation process itself in some way. Although there has been much work on Alnico 5. its nature is still incompletely understood. According to Geisler,' the precipitation reaction is of the

Jan 1, 1959

By A. Brown

RAPIDLY rising world demand for mineral products has accelerated depletion of the more readily accessible ores, particularly those of premium grade. Operations must proceed at a faster rate to deeper horizons, where there are problems of ground control that restrict economic recovery of the mineral and introduce new hazards to mine personnel. For some of the new Canadian mining fields severe problems of ground stress are still in the future, but much of Canada's mineral output comes from well established mines that have reached considerable depths. It must also be anticipated that the depletion of premium grade ores will eventually necessitate mining low grade material at competitive cost, and unsolved problems of ground control can materially increase costs. Studies of ground stress phenomena in underground workings are therefore considered a present-day necessity, especially since these investigations must be a long-term effort owing to the highly complex nature of the problem and the difficulty of making full-scale observations. In recent years the Mines Branch of the Department of Mines and Technical Surveys in Canada has conducted such an investigation. This report of the work is primarily concerned with stress problems in some Canadian coal mines and, in particular, with mine bumps. Mines Branch investigations of this and related problems are carried out by a small team of mining engineers and physicists who, with assistance from geologists, pool their special skills in an integrated program. These Canadian investigations combine a field and laboratory approach. Since data obtained under contrasting mining conditions allow useful comparisons of ground behavior under stress, this article will present data gathered under a wide range of Canadian coal mining conditions. Two contrasting longwalls in eastern Canada will be discussed and two dissimilar pillar extraction operations in western Canada. Locale of Observations In eastern Canada observations are being made in the collieries at Springhill, Nova Scotia. The district's No. 2 mine, which has a history of bump occurrences dating back to 1917, is currently being worked at a depth of 4200 ft. The mining method is longwall retreating along the strike and the practice is to retreat three walls in line, each about 350 ft long. There is no machine cutting or shooting—the coal is hand-picked and hand-loaded onto face conveyors. There are three rows of hardwood chock block supports parallel to the coal face. These supports are built during the two daily coal loading shifts, and the rear line is withdrawn during the midnight shift. The goaves are partially packed by stone midwalls 12 ft wide which are built forward daily in step with the face advance. The seam dips at 15° and averages 9 ft of strong, well cleated bituminous coal enclosed in competent beds of shales, sandy shales, and sandstones of Carboniferous age. The bumps rarely disturb the retreating longwall faces but manifest themselves as violent upthrusts of pavement in the levels leading to the walls. Observations have also been made in Springhill's No. 6 mine, which operated in a 5-ft seam of coal at a depth of about 2500 ft. Although No. 6 mine was

Jan 1, 1959

By G. A. Alers, J. H. Bechtold, R. W. Armstrong

The plastic flow of .molybdenum was studied in compression at temperatures below the ductile-to-brittle transition in tension. It was found that molybdenum is ductile in compression at all temperatures down to —196°C. The yield strength continues to increase with decreased test temperature below the tensile ductile-to-brittle transition temperature range. Difficulty was encountered in correlating the experimental data obtained with existing theories of plastic flow. THE body-centered-cubic metals as a group show a rapid and very large increase in yield strength with decreasing test temperature.' It is of fundamental importance to the understanding of the mechanism of plastic flow that this general characteristic be examined carefully. Unfortunately, brittle fracture in low-temperature tensile tests prohibits the measurement of flow properties at very low temperatures. By using compression tests, fracture can be suppressed and the plastic flow of the bcc metals can be studied far below their tensile ductile-to-brittle transition temperatures. Molybdenum was chosen for this experiment and plastic-flow data were obtained down to —196°C.

Jan 1, 1959

By C. Feng, C. Elbaum

Knoop hardness measurements were carried out on large grains of iodide titanium containing different amounts of oxygen. For each oxygen content the hardness is recorded ainingas a function of the crystal orientation and of the angle 4 between the indenter diagonal and the projection of the C (hexad) axis in the surface. The results can be expressed by the following relation; hardness = n-k cos 2ø, where n and k are constants for a given oxygen content and crystal surface orientation. A NISOTROPY of hardness is a well-known phe-nomenon and has been reported for many metals.1-3 At the present time, however, such information is not available in the literature for titanium. Consequently, a systematic study of the simultaneous effects of oxygen content and crystallographic orientation on the hardness of titanium was undertaken in this laboratory. Evaluations of oxygen content in titanium are frequently carried out through hardness tests. Although such procedures may be justified in small grain specimens, the results of the present investigation indicate that the anisotropy of hardness should be taken into account in the case of coarsegrained specimens as well as in the case of pronounced preferred orientation. Materials and Experimental Procedures Iodide titanium, 99.99 pet pure and containing of the order of 0.002 wt pet O, was used throughout this investigation. The metal was arc melted in an argon atmosphere and cold rolled into strips 1/16 in. thick. These strips were subsequently recrystal-lized and strain annealed in vacuum (10" mm Hg or better) at 850°C in order to produce crystals varying in diameter from 10 to 25 mm. Oxygen was introduced into selected large crystals by heating at 700°C in an atmosphere of pure oxygen under an observed pressure of approximately 50 mm Hg. Each sample was subsequently annealed in vacuum at 850°C for 100 hr, in order to homogenize the oxygen content throughout the specimen. It was found that longer annealing was not necessary, for no change of surface hardness in a given direction was detected after prolonged annealing. The oxygen content was determined by the difference in weight of the specimens before and after the oxidation-annealing cycle. The accuracy of oxygen determination is within ±0.1 mg in samples weighing 0.5 to 1 g. A vacuum fusion analysis of oxygen was performed on several samples and gave results in good agreement with the ones obtained by the weight change. It should be emphasized that expected weight losses through evaporation of the metal in vacuum at 850°C' are many orders of magnitude lower than the precision of these measurements. Following the annealing treatment, both oxidized and unoxidized crystals were carefully polished. All detectable traces of surface cold working were removed by repeated polishing and etching. Laue back reflection X-ray patterns were taken for each crystal for the purpose of determining the orientation and ascertaining the absence of substructures detectable by this method. Hardness measurements, using a 1 kg load, were subsequently carried out on a Tukon hardness tester equipped with a Knoop indenter. The Knoop indenter was used throughout this work because indentations obtained by means of a Vickers indenter are considerably distorted due to the anisotropy of the elastic constants in titanium. Such distortions are much less pronounced in the case of Knoop indentations, although for some orientations a cer-

Jan 1, 1959

By L. W. Berger, and R. I. Jaffee, D. N. Williams

The effects of hydrogen on the properties of binary Ti-A1 alloys containing 2.5, 5, and 7 pct aluminum and ternary alloys of the same compositions with added interstitial elements oxygen, nihrogen, and carbon were stzdied. Aluminum increases the apparent hydrogen solubility of the a-phase, resulting in a marked increase in resistance to impact embrittlement. In the Ti-5Al and Ti-7Al alloys, for example, the addition of 180 and 305 ppm hydrogen, respectively, did not cause embrittlement, while unalloyed titanium was embrittled by as little as 75 ppm. The role of aluminum in increasing hydrogen solubility of the a-phase probably accounts for the excellent hydrogen tolerance of a-ß alloys containing considerable amounts of aluminum. There is some evidence that aluminum retards the rate of hydride precipitation. If so, these alloys may be susceptible to slow-strain embrittlement. UNALLOYED a-titanium is extremely sensitive to small amounts of added hydrogen in that there is a marked decrease in notch properties. For example, as little as 100 ppm hydrogen is sufficient to lower the room-temperature notch-impact strength from over 100 to less than 20 in.-lb.' This loss of impact Strength has been associated with the Presence of hydride phase in the microstructure. Hydrogen in the amounts encountered in commercial practice

Jan 1, 1959

By W. O. Philbrook, C. W. McCoy

The reduction of chromous oxide from lime silica alumina slags by carbon-saturated iron behaves as a first-order process having a rate of 0.001 grams Cr min 1 cm 2 (pct Cr ) , substantially independent of slag composition and temperature over an important range for iron smelting. The equilibrium ratio (pct Cr)/[pct Crl is below 0.04 for slags having lime-silica ratios above 0.6. MANY studies have been conducted on chromium in slag-metal systems under oxidized conditions. The Purpose of these investigations has been twofold; namely, (1) to determine those conditions which lead to greater chromium recovery in electric-furnace and open-hearth practice, and (2) to determine the nature of oxide inclusions and de-

Jan 1, 1959

By E. S. Bartlett, D. N. Williams

QUANTITATIVE values for the oxidation rate of unalloyed molybdenum in air at temperatures above the melting point (1460°F) of the characteristic oxide are contained in the literature as a result of previous investigations. Lustman' reported values corresponding to 0.36 in. penetration per day (IPD) at 1500 and 1600°F in still air, noting essentially no variation in rate with temperature. Jones, Spretnak, and Speiser' reported values corresponding to 0.14 and 0.13 IPD at 1500 and 1800°F, respectively, in still air, attributing the decreased oxidation rate at higher temperatures to a lesser accumulation of the corrosive molten oxide on the surface at the higher temperature as a result of increased volatilization rate. Harwood3 ecently summarized work in the field, presenting generalized data corresponding to 0.48 to 0.96 IPD at 1800°F and 0.55 to 0.83 IPD at 1700°F in slowly flowing air. In a recent program at Battelle, it became desirable to know more about the characteristic oxidation behavior of molybdenum under varying conditions of temperature and atmosphere. Using oxidation-test apparatus designed for dynamic, continuous recording of weight change during testing,' values for the oxidation rate of molybdenum were obtained at temperatures from 1400 to 2150°F. In addition the effect of air flow on the oxidation rate was studied briefly at temperatures of 1600, 1800, and 2000°F. Exhaust of the contaminated atmosphere from the oxidation chamber was effected by an impeller pump attached to a 3/16-in.-diam opening in the oxidation chamber. The volumetric exhaust rate (cubic feet per hour) was normally maintained slightly in excess of the input rate to avoid condensation of MOO,,' on the sample suspension rod. The entering atmosphere was preheated prior to admission to the oxidation chamber by a 1 1/2-in.-diam cup packed with shredded asbestos. The experimental data are presented in Table I. Comparing conditions 2 and 3 (taking into account the temperature difference) and conditions 8 and 9. shows that in the absence of forced exhaust an atmosphere of moving air results in greater oxidation rate than a stagnant atmosphere. The use of forced exhaust, as shown by comparing conditions 3 and 4 and conditions 14 and 15: resulted in an even greater increase in oxidation rate. By virtue of the size of the atmosphere input and exhaust openings, it was calculated that the exhaust velocity was about 60 times that of the input velocity for essentially equal volumetric flow rates. Because of the proximity (about 3/4 in.) of the exhaust port to the specimen, it is logical to assume that cleansing of the atmosphere immediately surrounding the specimen was accomplished much more efficiently by the exhaust flow than by the input flow at a constant-volumetric flow rate. Also, it can be seen by comparing conditions 4 through 7 and conditions 11 through 13 that increasing the rate of atmosphere flow (by increasing input velocity with a proportional increase in exhaust velocity) above some optimum value has little, if any, further effect on the oxidation rate. These results suggest that there is a maximum oxidation rate for molydenum at a given temperature which is obtained when conditions are maintained such that the partial pressure of MOO3 in the atmosphere surrounding the specimen is at a low value. By controlling the partial pressure of MOO, surrounding the sample, it is possible to control the rate of volatilization of MOO:, from the surface. This, in turn, affects the rate of oxidation, since the thickness of the MOO3 layer determines the amount of oxygen which will be able to reach the reaction surface.' When the liquid oxide layer is less than some critical thickness, i.e., when the volatilization rate is high, enough oxygen is transported to the active surface to permit oxidation to proceed at the maximum rate allowed by the kinetics of the oxidation reaction. However, if the volatilization of MOO,, is suppressed, the thickness of the layer of MOO3 on the surface increases, and the diffusion of oxygen through the oxide layer becomes the rate-controlling step in the oxidation process. The lack of agreement between the present results and those of previous investigators is presumed to be due to differences in removal of the oxidation product (Moo,) from the immediate vicinity of the sample. By comparing conditions 1, 5, 10, 12 and 14, it is seen that when forced exhaust was used the oxidation rate of molybdenum increased with increasing temperature. A rapid increase was observed between 1400 and 1600°F, attributable to the effects

Jan 1, 1959

By Douglas D. Donald

The New Jersey Zinc Co. successfully holed through a 2 1/2-mile haulage tunnel connecting its new Ivanhoe shaft with the Van Mater Shaft at Austinville, Va. This 8x 10-ft cross-section tunnel was driven from both ends and met at a point approximately a mile from one shaft and a mile and a half from the other. In order to make certain that the faces met accurately on line and grade it was necessary to refine conventional mine surveying practices. The mines that are serviced by these shafts are located in the southwestern part of Virginia approximately midway between Roanoke and Bristol at the west foot of the Blue Ridge. While the presence of lead-zinc sulfide ores has been known in this area for more than 200 years, it was in 1902 that New Jersey Zinc Co. acquired the Austinville property, which has been in constant operation since that time. About ten years ago the company undertook an extensive diamond drilling program at Ivanhoe several miles to the southwest. This program was successful in locating sufficient ore to justify the purchase of a number of the properties in this area and plans were made to develop the new orebodies. The discovery of this ore as well as substantial addi- tional reserves at Austinville resulted in a decision by the company to increase its daily milling capacity to 3000 tons, of which about 1000 tons would be supplied from the Ivanhoe mine. After careful consideration of all possible methods of transporting this volume of ore from Ivanhoe to the mill, it became evident that diesel locomotive haulage through a 2½-mile tunnel between the two mines would best suit prevailing conditions. Since the lowest operating level, known as the 1100 level, of each mine would be at approximately the same elevation, it was obvious that such a tunnel should be driven on this level. Not only would this tunnel facilitate feeding Ivanhoe ore into the underground crusher and skip loading installation at Austinville, but it would also open up a known orebody 5000 ft southwest of the Van Mater shaft. In addition it would provide a valuable diamond drilling base from which a large and a potentially favorable but untested block of ground might be explored. In order to hasten the completion of the tunnel, it was felt that it should be driven from both ends. ENGINEERING CONTROL PROCEDURES It was vital that the tunnel junction be made accurately on line and grade; thus it was felt that engineering control of an unusually high degree of reliability was required to prevent an accumulation

Jan 1, 1959

By J. D. Lubahn

Prior tests by Dorn, where the strain rate in a tensile test was suddenly changed, have shown a small, but definite rate-history effect to exist. If this effect is neglected in the calculation of creep behavior from tensile results, an error should occur. This paper shows that this error is smaller than experimental scattering, and may be neglected. DORN1 has found a small but definite rate-history effect in the aluminum alloy 250 at liquid-nitrogen temperature using tensile tests with an abrupt rate change. Such an effect is to be expected from pre-viously known2-6 temperature-history effects, together with general experience that effects produced by changing the strain rate a large amount are simi-

Jan 1, 1959

By J. H. Scaff, J. E. Kunzler

The measurement of the electrical, thermal, and magnetic properties of metals at low temperatures, primarily in the range of liquid helium below 4.2°K, is a powerful tool for investigating many of the fundamental properties of the metallic state. Such measurements also have many practical applications, particularly as an analytical tool. One example of the practical utility of such measurements is illustrated by a short study we have made of the low-temperature resistance of copper used in preparing varistors. Copper-oxide varistors are prepared by the thermal oxidation of copper. This results in the

Jan 1, 1959

By A. J. Griest, P. D. Frost, H. A. Robinson

The flow characteristics and uniform elongation of alpha-beta titanium alloys in the solution-treated condition were shown to be markedly affected by the solution temperature. Two classes of alpha-beta alloys were distinguished, based on the effect of solution temperature on the uniform elongation. Martensitic alpha-beta alloys, which are relatively weakly beta-stabilized, showed decreasing values of uniform elongation as the solution temperature was initially increased. However, after solution-treatment at still higher temperatures in the alpha-beta field, the uniform elongation of these alloys was again high, and often attained its maximum value. Nonmartensitic alpha-beta alloys, which are more heavily beta-stabilized, showed a continuous decrease of uniform elongation with increasing solution temperature. The behavior was rationalized in terms of the alpha-beta ratio and the alloy content of the beta existing at the solution temperature. The data indicate that in commercial practice close temperature control may be required to get maximum uniform elongotion, and hence, maximum potential formability, in solution-treated sheet. Bend-test data also were obtained for the solution-treated conditions. A MOST important objective of current titanium research is the development of age-hardenable alloys with superior formability in the solution -treated condition. Alpha-beta titanium alloys have been shown to be amenable to high-strength aging treatments after solution-treatment in the alpha-beta field.' However, heat-treatment data on the properties of solution-treated sheet, such as uniform elongation, minimum bend radius, and flow properties, which have a bearing on the potential formability, have not been widely available. This paper presents only the most significant results of a research program conducted at Battelle for the Air Force in an effort to develop sheet alloys that can be formed readily as solution-treated and subsequently aged to very high strengths. Data for 10 compositions representative of the more than 25 alloys studied in this program are presented. A primary objective of the paper is to demonstrate the pronounced dependence of the flow characteristics and uniform elongation on solution-treatment temperature. This effect is believed to be vitally important in the commercial heat-treatment of age-hardenable titanium sheet alloys. Experimental Procedures Melting and Fabrication—The nominal and actual compositions, beta transi temperatures, and rolling temperatures of 10 of the 30 alloys studied are presented in Table I. Stock :€or two of the alloys, E (Ti- 8Mn) and J (Ti-6A1-4V) was obtained from commercial heats. The remaining heats, except D and I, were double melted as 10-lb heats in a consumable-electrode furnace. Melting stock was 120 Brine11 hardness sponge. The oxygen and hydrogen analyses spotted throughout the heats indicate the range of interstitial levels resulting from the melting practice used. Heats D and I were melted as 20-lb ingots with the same grade of sponge. These ingots were cut in half and one portion used in the present evaluation. The ingots, which were about 4 in. diam and 4 in. in height, were upset forged and drawn at 1750°F to sheet bar 5/8 in. thick by 2 1/2 in. wide in such a manner that the top of the ingot corresponded to the top of the sheet bar. Slabs of the sheet bar, 5 1/2 in. in length were scalped to 1/2 in. thickness and rolled at the temperatures indicated in Table I to approximately 0.055 in. sheet. Elongation during rolling took place at 90" to the original forged length. The fabrication procedure used is described in some detail since the experimental heats showed considerable directionality in mechanical properties. The rolling procedures for the commercial heats were unknown, but were such as to produce essentially isotropic properties. All heats, as rolled, showed microstructures typical of alpha-beta alloys worked in the alpha-beta field; that is, the structures consisted of equiaxed alpha particles in a beta matrix. Heat Treatment— The effects of solution and aging heat-treatments on the properties of the alloys were evaluated uSing longitudinal and transverse tensile and bend coupons sheared from the sheet. Two or three solution-treated conditions were evaluated for each alloy. In addition, the alloys were also tested after annealing at 1200°F for 4 hr and furnace cooling. The solution-treated and annealed conditions were those in which the alloys might be expected to

Jan 1, 1959

By E. A. Peretti

BEFORE embarking on a detailed investigation of the system indium-antimony-bismuth, experiments were carried out to determine the existence of quasi-binary sections. The bordering binary systems are known1 and show the occurrence of three intermetallic binary species corresponding closely to InSb, InBi and In2Bi. Attention was focused on the low-indium end of the ternary diagram where the possible quasi-binary sections, excluding ternary compound formation, would involve the pairs: InSb-Bi, InBi-Sb and InSb-InBi. The latter pair revealed itself as a true quasi-binary, so it was investigated fully by thermal analysis, x-ray and microscopic examinations. All compositions were made by proper combination of three elements involved. The indium had a guaranteed purity of 99.97 pet; the antimony contained 99.99 pet Sb, and the bismuth had a purity of 99.99 pet. Alloys were made by melting together antimony, bismuth and indium in evacuated, sealed pyrex-glass tubes at a temperature of 600°C with vigorous agitation. The melts, weighing about 80 grams, were allowed to freeze in the sealed tubes and finally were transferred to glass tubes for the taking of cooling and heating curves. A protective atmosphere of helium was used, and the melts were stirred mechanically while cooling at rates of from 0.5 to 3°C per min. Temperatures were measured with a calibrated chromel-alumel thermocouple and were recorded graphically on a Minneapolis-Honeywell extended-range recorder working in conjunction with a Leeds and Northrup type K-2 potentiometer. Conventional polishing techniques gave satisfactory results in preparing specimens for microscopic examination. Etching was carried out with Vilella's reagent or aqueous mixtures of chromic oxide with either nitric acid or sulfuric acid plus dichromate. Conclusions deduced from the thermal analysis and microscopic examinations were confirmed by X-ray photograms using Co-K alpha radiation. The phase diagram is shown in Fig. 1. The liqui-dus consists of an uninterrupted line running from the freezing point of InSb (525°C) to a eutectic point experimentally indistinguishable from the freezing point of InBi (110°C). X-ray patterns of the InSb show a slight expansion of the lattice with the addition of InBi, and microscopic work indicated the solid solubility of InBi in InSb to be less than 0.5 pet at room temperature. Acknowledgment We wish to thank the Indium Corporation of America for the loan of the indium used in this investigation. References 1 E. A. Peretti and S. C. Carapella, Jr.: Trans. ASM., 1949, vol. 41, P. 947. T. S. Liu and E. A. Peretti: Trans. ASM, 1952, vol. 44, p. 539. Metals Reference Book, vol. 1, 2nd ed., AIME, p. 345.

Jan 1, 1959

By R. A. Meussner, R. T. DeHoff, F. N. Rhines

ZINC diffuses through copper more rapidly than does tin. Accordingly, when a ternary diffusion couple is made, by bringing an 0 copper-zinc brass into contact with an a copper-tin bronze at fixed high temperature, it is to be expected that zinc will diffuse into the bronze faster than tin diffuses into the brass. Adjacent to the brass side of the couple the total alloy content (zinc plus tin) should diminish, therefore, while next to the bronze side the alloy content should increase. Since the path of compo- sition change must be continuous, in a single-phased alloy, it should follow a curved and, in general, an S-shaped course. The realization of this prediction is demonstrated in Fig. 1, where the composition paths of two ternary diffusion couples are plotted on the appropriate isotherm of the copper-tin-zinc phase diagram. The diffusion couples were both made from a binary copper-tin alloy analyzing 5.0 pct tin placed against binary copper-zinc alloys analyzing 18.9 and 29.3 pct Zn, respectively. These alloys were produced from electrolytic grades of copper and zinc and a pure grade of straits tin, melted under borax in clay-graphite crucibles and cast in a vertical iron mold. Cylindrical pieces 1 in. in diam and 1 % in. long were machined from the casting and were faced by metallographic polishing to good matching end surfaces. Pairs of the cylindrical pieces were held

Jan 1, 1959

By D. L. Martin

The study of cobalt-platinum alloys has been of interest since they represent a class of permanent-magnet material in which the disorder-to-order transformation plays a controlling role. The magnetic properties of alloys in the range 40 to 60 at. pct have been found to be greatly influenced by composition and heat-treatment. The peak properties of 4700 coercive force and 9,000,000 gauss-oersteds energy product were obtained by controlled cooling and aging. These high values combined with ductility and machin-ability give the alloys useful characteristics although their high cost limits their application. THE cobalt-platinum alloys have been of interest in the study of permanent-magnet materials ever since the discovery by Jellinghaus that they had unusually high coerceive-force values.' The high coercive force was associated by Jellinghaus with the disorder-order reaction which occurred in these alloys. This was later verified by Gebhardt and Koster in a detailed study.2 An investigation of the structure, mechanism, and kinetics of the disorder-order transformation and resulting property changes in cobalt-platinum alloys has been in progress for some years. Certain phases of this study related to equilibrium rela- tions, and to the mechanism and kinetics of the ordering reaction have been published previously.3-5 In this paper, the results of the processing and heat-treatment studies on 40 to 60 at. pct CO alloys are presented. The magnetic properties have been found to be influenced greatly by the composition, by the cooling rate from the disordering treatment, and the final ordering time and temperature. Coercive force values, Hc, of 4700 oersteds and energy values, (BH)m, approaching 9,000,000 gauss-oersteds have been obtained by controlled cooling and ordering. PROCESSING OF THE ALLOYS The composition range of interest for permanent-magnet properties centers around the equiatomic composition Copt. In this region the alloys are dis-

Jan 1, 1959

By L. H. Schwartz, M. V. Nevitt

THE phase Ti2Ni has been described by Laves and Wallbaum,1 who found the phase to be face-centered cubic with 96 atoms per cell, by Duwez and Taylor,2 who confirmed these observations and reported a lattice parameter of 11.333A, and by Rostoker,' who reported the structure to be isomorphous with the double carbide Fe,W,C, type E93, and to have a lattice parameter of 11.29A. In this study a group of isostructural phases has been found among alloys of certain second and third long-period transition elements. The systems investigated included all the combinations of zirconium and hafnium with the Group VIII elements rhodium, palladium, iridium, and platinum. There is evidence that many of these new Ti2Ni-type phases require oxygen for their stability in the temperature ranges in which they were studied. EXPERIMENTAL PROCEDURE Alloy samples weighing 5 g were prepared by arc-melting metals whose purity is indicated in Table I in a helium-argon atmosphere. Samples of the as-cast buttons, wrapped in molybdenum foil and sealed in evacuated quartz tubes, were

Jan 1, 1959

By Shiou-Chuan Sun

Most previous work on sedimentation of coal1 and mineral2,3 suspensions has been conducted in graduated 1-liter glass cylinders of 6-cm diam. With this type of large container it is often difficult to see through the suspension and tedious to perform a large number of tests. Furthermore, the heavy glass walls and the graduation lines of glass cylinders cause internal and stray reflections, respectively. To obviate these difficulties, an Atlab Emulsion Viewer from Arthur H. Thomas Co. was adopted as an alternative apparatus. Equipment: The viewer,4 shown in Fig. 1, consists of: 1) a stainless steel frame rack holding 21 flat-bottom Nessler tubes or an ungraduated replica 1.64 cm ID and 1.80 cm OD, 2) a movable masked 150-w lumaline lamp behind the tubes, and 3) a scaled glass panel with 100 vertical divisions in front of the tubes. The tubes are snugly held by springs in slots formed by spacer bars, which also serve as shields to eliminate stray light. The lumaline lamp is mounted behind a slit in a movable housing so that it can be positioned behind the suspension to be examined. The lowest or 100-division line on the front glass plate is leveled with the upper side of the bottom of all tubes. The scaled portion of each tube, roughly 19 cm high and 40 ml in volume, is used to study coal and mineral suspensions.

Jan 1, 1959