By E. J. Ripling, S. I. Liu

IT has been shown in a number of recent publications that much information on the mechanical behavior of metals can be gleaned by first deforming test specimens under one set of conditions, and then evaluating the effect of this deformation by means of a subsequent tensile test. A straining procedure of this type has been applied to study the flow behaviors of a number of metals.1, 2 In these studies the prestraining and testing were both tensile strains, while the straining temperature was varied between the prestraining and testing steps. These data indicate that there is a more or less general flow behavior exhibited by all metals which are pre-stretched at one temperature and then tested in tension at a second temperature. Prestraining a metal at a high temperature produces a lower yield strength during the subsequent low temperature strain than would the same total strain at the lower temperature. On reversing the order of the strains, low temperature prestraining produces a higher yield strength during the subsequent high temperature straining than would a single high temperature strain of the same magnitude. Unlike the flow behaviors, the fracturing characteristics of metals when prestrained under one set of conditions and tested under a second set of conditions is quite material dependent. The fracture behavior of a number of steels2" as well as of a commercially pure zinc,4 have been investigated by these two-step tests and was found to depend upon the position of the transition temperature with respect to the prestraining and testing conditions. Since these fracturing phenomena are complicated by the appearance of the transition temperature, it has been difficult to reliably define the basic effect of a two-step straining procedure in fracturing. Metals crystallizing in the face-centered cubic system do not exhibit transition temperature effects so that the mechanical characteristics obtained on these materials could serve as a base for two-step straining behaviors. Consequently groups of specimens of the aluminum alloy 24s-T4 were prestrained various amounts at room temperature in either tension or compression after which these strained specimens were further strained to failure, or tested in tension, at either room or some lower temperature. Other groups of 24S-T4 specimens were prestretched at various low temperatures after which these were tested in tension at room temperature. These straining techniques then made it possible to compare the behaviors of aluminum with the behaviors previously presented for steels. Material and Procedure The commercial aluminum alloy 24S-T4 in the form of 3/4 in. rods was used in this investigation. The material was subjected to the following treatments before machining: 1—resolution treating at 920" & 10°F for 45 min, 2—quenching in water at room temperature, and 3—aging at room temperature for four days. The re-heat treated material was then machined to either of the specimen shapes shown in Fig. 1. Fig. la shows the threaded-end specimen used for prestraining in compression. Fig. 1b shows the specimen used for both prestrain in tension and final testing. The material subjected to precompression in the form of the specimen shown in Fig. la was re-machined to the specimen shape in Fig. 1b for final testing. Prestraining in tension and final testing were done without any intermediate machining. All straining was performed on a 10,000 1b Riehle tensile testing machine. Tensile strains were conducted in a specially designed concentric fixture which produced an eccentricity of less than 0.001 in." The change in diameter at the minimum section of

Jan 1, 1954

By R. I. Jaffee, H. R. Ogden, D. J. Maykuth

Phase diagrams for the Ti-W and Ti-Ta systems were determined. The Ti-W system is characterized by a wide, two-phase region of ß plus tungsten which is derived from a peritectic reaction between the liquid and tungsten solid solutions. The ß field terminates in a eutectoid reaction between a titanium and tungsten terminal solid solution. Tantalum and ß titanium form a complete series of solid solutions. Other features of this system are the extensive a-ß field at low temperatures and an appreciable solubility of tantalum in a titanium. BOTH tungsten and tantalum were first thought to form ß-isomorphous systems with titanium as a result of early work' using powder-metallurgical techniques. Later work2 on arc-melted Ti-Ta alloys, made using a commercial titanium base, showed that, in the range of 0 to 10 pct, tantalum was soluble in ß titanium and that the a solubility extended to between 2 and 5 pct Ta at 790 °C. The present investigation covered the entire alloy range in both systems and was chiefly concerned with high-purity alloys at the titanium-rich end. The constitution of titanium-rich alloys made with a commercial titanium base was reported by Holla-day, Kura, and Jackson.3, 4 As will be shown in detail later, the early prediction of a isomorphism was true for the case of the Ti-Ta system, but not for the Ti-W system. The results of this investigation will be presented first. The experimental methods used are described in the Appendix. Ti-W System The entire Ti-W phase diagram is shown in Fig. 1. Details of the titanium-rich side are shown in Fig. 2. The chief features of the system are a ß eutectoid and a high-temperature peritectic between liquid and tungsten solid solution. Melting Range: Examination of cast structures of low and medium-tungsten-content ingots showed cored ß phase as the primary constituent. Fig. 3a illustrates a typical cast structure for alloys in the range of 20 to 30 pct W. From 30 to 72 pct W, coring was very severe. Alloys containing 72 through 88 pct W, however, showed definite evidence of a peritectic reaction between the liquid and a terminal solid solution of titanium in tungsten. Fig. 3b shows the cast structure for an 80 pct W alloy. A 95 pct W alloy, shown in Fig. 4, consisted primarily of primary tungsten solid solution plus a small quantity of ß probably rejected during cooling. Incipient-melting experiments located the peritectic temperature between 1850" and 1900°C and indicated that the reacting phases are liquid containing about 25 pct W and tungsten terminal solid solution containing about 8 pct Ti. Figs. 5 and 6

Jan 1, 1954

By Robert P. Uhley, LeRoy Scharon

TEST gravity surveys were made in the Washington County barite district of Missouri on property owned by the Baroid Sales Division of the National Lead Co. This property is located just northeast of Richwoods in the northeastern corner of Washington County, Fig. 1. The area to which the surveys were confined comprised approximately 5000 acres, of which some 525 acres were surveyed gravitationally. Gravity observations were made at 2600 points within the area, observations being confined to relatively clear and gently sloping ground. Part of the area was heavily wooded, and the terrain too rugged for either the occurrence of a commercial barite deposit or a feasible gravity survey. The relief along the central drainage, Ditch Creek, was about 140 ft, the maxi- mum difference in elevation being 400 ft in a distance of 3 ½ miles.

Jan 1, 1954

By D. J. Bourne, G. E. Atwood

The new potash refinery of Duval Sulphur & Potash Co. produced its first tonnage of muriate of potash in November 1951. Full capacity was attained in early 1952. Excellent extraction efficiency is being obtained by the process, which is basically froth flotation. System temperature control is practiced and has proved to be of great metallurgical value through high potassium recovery and. low reagent cost. WHEN Duval Sulphur and Potash Co. recently entered the established potash industry, the vast amount of pioneer work essential in an entirely new endeavor was unnecessary. Thus it was possible to screen and assemble proved techniques into a highly efficient process based on the combined knowledge of the industry. It is hoped that the refinements Duval has added to these cumulative achievements will contribute to the rapid advance of the potash industry and related enterprises. The process selected utilizes as raw material syl-vinite ore typical of the Permian Basin. This ore is principally comprised of interlocked crystals of potassium chloride, about 40 pct, and sodium chloride. Also there is as much as 1 1/2 pct of dispersed clay slime which, because of its nature, highly complicates beneficiation of these ores. The refining method is basically flotation in which the mineral sylvite is floated away from the halite-clay gangue to produce a 60 pct K,O muriate of potash product for the plant-food trade. It departs from established practice in the use of an improved reagent scheme, developed by the company's technical staff, and in

Jan 1, 1954

By L. Himmel, R. F. Mehl, C. E. Birchenall

The rates of self-diffusion of iron in artifically prepared wustites of various compositions have been determined using the decrease in surface activity technique. Similar measurements are reported for artificial magnetites of nearly stoichiometric composition and for natural hematite single crystals. These data, together with appropriate thermodynamic data derived from the present study or from the literature, are used to calculate the rates of oxidation of iron and its oxides, taking as a basis the theoretical rate equations developed by Wagner. The calculations are compared with experimental rate constant data for these same reactions and are shown to provide essential confirmation for the Wagner theory. For the most part, the results are also consistent with the previously proposed transport mechanisms in the oxides of iron. WHEN a metal is exposed to an oxidizing atmosphere at elevated temperatures, a superficial oxide layer is formed which then thickens according to some characteristic rate law. Provided that the oxide layer is dense and continuous and does not present any paths for gaseous diffusion, continued growth must inevitably involve the migration of the reactants—either the metal or oxygen or both—through the lattice of the solid oxide. This is true whether the reaction rate is controlled by the diffusion process itself or by a slow step in a reaction at one of the interfaces. If the overall rate is limited by diffusion, and if the concentrations or thermodynamic activities of the reactants at the boundaries of the oxide layer are independent of time, the familiar parabolic rate law is observed. Under these conditions, Wagner1 has shown that the rate constant may be expressed in terms of the mobilities of the reacting components and the appropriate concentration or activity gradients which are established across the growing oxide layer. In presenting the phenomenological basis for the theory, Wagner has emphasized the role played by lattice defects in diffusion processes in oxides. The essential validity of this theory has been confirmed by experiment for a number of simple systems including the growth of Cu2O on copper.'-' One of the objectives of the present study has been to extend the Wagner approach to the more complex process of the oxidation of iron and its oxides, and particularly to wustite, which is normally the major constituent of the oxide scales formed on iron at temperatures above approximately 570°C. For this purpose the rates of self-diffusion of iron in w?stite, magnetite, and hematite have been measured by tracer techniques and the necessary thermodynamic data have been obtained from equilibrium studies involving the oxides and their atmospheres. These data have subsequently been used to test the underlying assumptions of the Wagner theory as well as the detailed mechanism of the scaling of iron previously proposed by Davies, Simnad, and Birchenall.5 Lengthy treatments of diffusion and conduction phenomena in ionic crystals have been published." * The latest, by Jost,8 also summarizes much of the existing experimental data. In general, however, the oxides of iron have not been considered specifically and hence a brief review of the available

Jan 1, 1954

By J. A. Rowland, C. W. Funk

THIS investigation is a part of the United States Bureau of Mines work in conserving the Nation's resources. The isothermal sections presented were developed as a guide to a comprehensive investigation of the properties and fabricating characteristics of copper-base alloys containing manganese and tin. These alloys are being investigated as possible replacements for the commercial bronzes containing substantial quantities of tin. Development of the isothermal sections has, therefore, been limited to the area between 0 to 20 pct Mn and 0 to 25 pct Sn. Since Heusler1 reported the ferromagnetic properties of the Cu-Mn-Sn alloys in 1903, the system has been the subject of several investigations. These studies were largely concerned with correlation of magnetic properties and crystal structure.2-6 Vero,' however, established the solidus surface of the system, between 20 pct Mn and 40 pct Sn, by thermal and microscopic methods. The a, ß, and y solid solutions were also observed by Vero and reported to extend into the interior of the ternary system. For the present study, the annotated diagram of the Cu-Sn system prepared by Raynor' and the Cu-Mn diagram by Dean and coworkers9 were used as the binary borders of the ternary system. Procedure The metals used in this investigation were electrolytic manganese, washed cathode copper, and three-star tin. The manganese, produced at the Boulder City pilot plant of the Bureau of Mines, had a purity of 99.9 pct; the copper contained less than 0.004 pct Bi and 0.001 pct S; the tin contained 0.070 pct Pb, 0.070 pct Sb, 0.050 pct Fe, and 0.065 pct Si. Heats of 1 lb were melted in alundum crucibles with a 3-kw induction furnace. The heats were chill-cast in iron or copper molds to form 6-in. ingots 3/4 in. in diameter. Molds were washed with graphite or zirconia, depending on the manganese content, and preheated to 150°C. The maximum impurity content of any alloy was 0.03 pct Fe, 0.02 pct Si, and 0.02 pct Al; in most cases, they contained less than half this quantity of any of these impurities. Composition of the alloys and their treatment prior to homogenizing are shown in Fig. 1. Designations adjacent to each composition refer to the heat numbers. With a few exceptions, ingots containing 20 pct Sn or less were hot-swaged. These ingots were swaged, after a 24-hr preheat at 650°C, to obtain a total reduction of 70 pct in cross section. Intermittent reheating was necessary, and reductions were limited to either 0.025 or 0.050 in. in diameter per pass. Selection of a 200-hr homogenizing treatment was based on extensive experiments which indicated that virtual equilibrium was reached after 150 hr. Structures were retained by quenching in water. Grain sizes in the specimens homogenized at 350" and 450°C were generally small. These homogenizing treatments were preceded by a 50-hr anneal at 650°C to facilitate phase identification by increasing the grain size in these specimens. The specimens were furnace-cooled from this temperature to the homogenizing temperature, and the heat treatment was continued for the standard 200-hr period. The homogenized samples were bisected to provide an internal section for metallographic examination. Optimum definition of the microstructure was obtained by successive polishing and etching. Quarter-strength ASTM copper reagent No. 13 gave the most satisfactory results.10 Filings from interior sections of the samples were used for diffraction studies. These filings were annealed in evacuated glass tubes at homogenizing temperatures for periods exceeding 50 hr and quenched in water. During this treatment the manganese content was reduced by significant amounts, probably by vaporization. This change in composition was considered in applying the diffraction data, which were used only as a means of identifying phases where the data were consistent with the metallographic evidence. Phase Identification The a solid solution is readily distinguished by the copper-colored, twinned, polyhedral grains, as shown in Fig. 2, and a face-centered cubic X-ray pattern. Tukon indentations, using a 25-g load, indicate a Knoop hardness of 155 for a quenched from 650°C. Using white light developed by a Wratten 78 A filter, the ß grains in etched specimens have a dark brown tint in contrast to the lighter copper-colored grains of the a phase. Knoop hardness values of 284 were obtained for the ß structure in specimens quenched from 650°C. The ß structure was also distinguished from the a phase by its body-centered cubic lattice. The acicular structure appearing in Fig. 3 was evident in several alloys of higher tin content after quenching from either 750' or 650°C. Since a trans-

Jan 1, 1954

By J. J. Gilman

The data presented indicate that the critical shear stress and strain-hardening Thedatapresentedrate of a zinc monocrystal depend on the orientation of its slip direction with respect to its external boundaries. The tendency of a crystal to form deformation bands also depends on its shape. THE plastic behavior of pairs of zinc monocrystals in which both members of the respective pairs had the same orientation with respect to the longitudinal axis, but each had different orientations with respect to their rectangular external shapes, were compared in this investigation. The purpose of the investigation was to see what influence the shape or surface of a zinc crystal has on its mechanical properties. In a previous investigation of triangular zinc monocrystals,1 anomalous axial twisting was observed which seemed to be related to the triangular shape of the crystals. Wolff,' in 400°C tensile tests of rectangular rock-salt crystals bounded by cubic cleavage planes, found that, of the four equivalent slip systems, the two with the "shorter" slip directions yielded and produced slip lines at lower stresses than the other two. This observation and the work of Dommerich³ as formulated by Smekal4 as a "new slip condition" for rock-salt: "among two or more slip systems permitted by the shear stress law, with reference to the formation of visible slip lines by large individual glides, that slip system is preferred which has the shortest effective slip direction." More recently, Wu and Smoluchowski5 reported essentially the same effect for ribbon-like (20x2x0.2 mm) aluminum crystals at room temperature. Experimental Chemically pure zinc (99.999 pct Zn), purchased from the New Jersey Zinc Co., was the raw material. Glass envelopes, containing graphite molds and zinc, were evacuated while hot enough to outgas the graphite but not melt the zinc. At a vacuum of about 0.2 micron the envelopes were sealed off and then lowered through a furnace at 1 in. per hr so as to melt and resolidify the zinc and produce mono-crystals. One-half of one of the molds is shown in Fig. la. Each mold consisted of four pieces from a cylindrical graphite rod that was split longitudinally and transversely at its midpoints. Rectangular milled grooves 0.050 in. deep and % in. wide formed the mold cavity when the split halves were assembled with twisted wires. Fig. lb shows the specimen shape obtained when the top and bottom mold-halves were rotated 90" with respect to each other. Good fits prevented leakage and excess zinc was necessary to provide enough liquid head to fill the mold completely. In removing soft crystals from the molds it was impossible to avoid small amounts of bending. However, manipulations were carried out whenever possible with the crystals protected by grooved brass blocks. All specimens were annealed prior to testing. From the top and bottom sections of each crystal, X-ray specimens and tensile specimens 7 to 8 cm long were sawed. The tensile specimens were annealed inside evacuated tubes for 1 hr at 375°C. Next the crystals were cleaned and polished by 2-min dips in a solution of 22 pct chromic acid, 74 pct water, 2.5 pct sulphuric acid, and 1.5 pct glacial acetic acid.' Cleaning was followed by a 10-sec dip in a 10 pct caustic solution, then washed in water and alcohol, and dried. This treatment results in a bright surface covered by an invisible oxide film. The testing grips were a slotted type with set screws and were supported in a V-block during the mounting operations in order to avoid bending the crystals. A schematic diagram of the recording tensile-testing machine is shown in Fig. 2. The machine has been described elsewhere.' The head speed was 0.3 mm per sec for all tests. The crystal orientations were determined by the Greninger X-ray back-reflection method with an estimated accuracy of 1. Description of Crystal Geometry A schematic picture of a rectangular zinc mono-crystal is shown in Fig. 3. ABD designates the front edge of a basal plane (0001) of the crystal, the only active slip plane for zinc at room temperature. Of the three possible (2110) slip directions, the active one is indicated by an arrow. Cartesian coordinates are taken parallel to the specimen edges. The normal, n, to the basal plane (n is parallel to the hexagonal axis) has the direction cosines a, ß and ?. X0 = 90 — y is the angle between the longitudinal axis and

Jan 1, 1954

By G. R. Fitterer

Trends in slag composition in acid open hearth practice, particularly the variation in iron and manganese oxides during refining, are reviewed. A procedure which is currently being used to control the refining reactions is described and partially explained through slag phase diagram considerations. In addition, the ionic nature of these slags is considered and it is proposed that silica combines with the oxide ion and forms a series of complex silicate ions. The effect of basic oxides such as FeO, MnO, and CaO is apparently additive in furnishing the oxide ion for this purpose. IT is now possible to control192 the refining of steel in an acid open hearth furnace to a surprising degree. This control has been brought about through the knowledge and use of several facts and tests. These are: 1—A planned charge analysis based on a knowledge of the type of fuel, the bath depth, etc. 2—Knowledge and control of rate of fuel input as well as its method of atomization, if any. 3—Determination of the slag fluidity. 4—Bath temperatures (use of the Pt-Pt-Rh thermocouple). 5—Periodic determination of carbon content (use of the Carb-analyzer or Carbometer). Through the use of these control methods, a heat may be made to "melt-in" with or without residual manganese and silicon. The rate of refining or carbon elimination may be controlled accurately, and the desired tapping (or "go-ahead") carbon may be approached at a rapid or slow rate according to preference and type of steel being made. Thus operating time may be predetermined and greatly reduced. Further, all of the refining can be done without any ore or other oxidizing additions, and the heat may be brought to the desired tapping temperature simultaneously with the attainment of the desired carbon analysis. This control procedure is being used in most acid plants in the United States today and has been de- scribed.', ' Although the slag metal relations are sufficiently well known to control the heat as stated, yet it is possible to account for only about two-thirds' of the 0, which must have been used for the elimination of the carbon and other metalloids. Phase diagram studies' of the slags, slag weights, the metal particle theory,' ore additions, limestone additions, etc., may all be taken into consideration; yet, the mechanism of oxidation and source of all the oxygen remain to be explained. This paper reviews some of the principles upon which the control methods were based and proposes other possibilities regarding the unexplained phenomena. Old and New Acid Open Hearth Practice Some of the recent statements in the literature regarding acid open hearth operation are based on old heat data which are not typical of modern American practice. These old heat logs have been responsible for many misconceptions regarding the acid hearth practice and represent heats which do not coincide with modern methods. In recent years, American practice has been altered materially and these changes will be briefly described. Modern American Practice: A typical log of a modern American acid open hearth heat' is shown in Fig. 1 which indicates that the refining time was only two hours, during which the carbon was eliminated rapidly and the bath temperature increased at a fast rate. The manganese and silicon contents of the metal were essentially eliminated and their oxides had become constituent parts of the slag at the "melt-down" period. During the course of the heat, the MnO content of the slag remained practi-

Jan 1, 1954

By N. J. Grant, I. S. Servi, A. Chaudhuri

IN a recent paper by Servi and Grant,' it was illustrated that the slip band spacing and stress based on creep test data were related by the equation: d =1/ where d is the spacing in millimeters and v is the stress in psi, based on a more complete equation proposed by Orowan. It was shown further,' that for a. given grain size, the slip band spacing became larger with decreasing stress (and was independent of temperature), until such time that the slip band spacing becomes greater than about one-half the grain diam- eter. When this occurred, the mechanism of deformation in creep of 2s aluminum at high temperature changed from slip to grain boundary deformation (sliding). Additional metallographic evidence is now available which confirms this in a most interesting fashion.

Jan 1, 1954

By E. A. Jones

THE Southeast Missouri division of the St. Joseph Lead Co. normally hauls and hoists over 5 million tons of lead ore each year. This ore is mined in the stopes and headings of 20 mines, hauled to a main line system, see above, and transported up to 6.4 miles to ore-hoisting shafts. Average haulage distance is 2.16 miles. A few years ago a distinguished mining engineer visiting this area for the first time remarked, "You do not have a mining problem; yours is a haulage problem." Its relative importance may be gaged by the fact that mine haulage represents about 25 pct of the total cost of mining ore, the most costly single underground operation. The Southeast Missouri lead belt is a mining district located about 65 miles south of St. Louis. This district is roughly 6 miles wide and 10 miles long. The ore horizon lies about 400 ft below the surface where most of the ore is mined from flat-lying beds of dolomitic limestone. This paper deals with the central part of the district, namely, that portion which contains a group of interconnected mines all in a central haulage system, serving four hoisting shafts. The two major hoisting operations are carried out at Federal No. 17 shaft and Leadwood No. 12 shaft. No. 17 accounted for about 70 pct of the ore hoisted in the district during 1950, averaging about 14,000 tons per operating day. The underground dumping and skip-pocket system at this shaft is similar to those of the other shafts except that it has two rotary dumps. The other ore-hoisting shafts have only one. It might be mentioned that waste rock is hoisted at still other shafts, hauled off, and dumped on the surface by trucks. The hoisting shafts are on a connected system of about 200 miles of underground 24-in. gage main line railroad. There is also the Bonne Terre system, with its own ore-hoisting shaft, which consists of 13.5 miles of 24-in. gage main line, located in the extreme north portion of the lead belt area. Smaller outlying mines such as Doe Run No. 12 and Hayden Creek operate on trackless or shuttle car haulage. In addition to the system of main line haulage, each contributing mine group has its own extensive system of stope or heading railroad. Trackless mining is making considerable headway in the Lead-wood and Desloge mines. Here the shovel loads into a shuttle car which in turn dumps into mine cars spotted on the main line track system. When the merits of underground haulage and surface transportation are compared, it must be remembered that in early days there were many individual

Jan 1, 1954

By M. Metzger, J. Intrater

IN the large number of important studies on high-purity aluminum (e.g., recrystallization and grain growth, creep, internal friction), it does not seem to have been generally recognized that the iron content, despite its very low figure, has a strong influence on a number of properties. In part, its influence is due to the very low solubility of the Fe-A1 6 phase. For aluminum of about 99.99 pct purity, the iron content may be 0.001 to 0.004 pct. For values in this range, a second phase will be present below 410" to 480 °C. This was determined by extrapolation of a log solubility vs inverse temperature plot of the solid solubility data of Edgar.' One consequence is the inhibition of grain coarsening below the solubility limit. This is shown in Table I, which gives, for three iron contents, the annealing temperature required for the absence of grains smaller than 1/2 mm average diameter together with the minimum temperature for the presence of some grains larger than 2 mm diameter. The specimens were 1/4x 1 1/2-in. strips cut from hard-rolled 1/16-in. sheet supplied by the Aluminum Co. of America.

Jan 1, 1954

By R. C. Troxell, S. C. Sun

EFFORTS to obtain definite quantitative data when employing the currently used bubble pick-up method1,2 as a pre-flotation investigation tool led to the adoption of the magnifying mirror method and the microscopic method modifications. Quantitative data obtained by these two methods were converted into bubble pick-up indices and bubble pick-up coefficients. Rough correlations were established between the calculated indices and the results of contact angle testing as well as actual flotation under the same conditions. The basic steps of the magnifying mirror method are as follows: 1—mixing 200 ml distilled water, sized and cleaned mineral particles of approximately 0.5 g, pH regulator, and flotation reagents in a glass beaker; 2—swirling the mineral particles to the center of the beaker to leave a clear circumference; 3—pressing an air bubble against the mineral particles for about 1 sec, and then moving the mineralized air bubble to the clear part of the beaker; and 4—dropping all the attached mineral particles of the air bubble by tapping the bubble holder, and counting the number of the dropped particles by looking at the magnified image in the mirror positioned beneath the beaker. This method is impractical for mineral particles which are transparent in water or finer than 200 mesh. The microscopic method is essentially similar to the above described magnifying mirror method, with the exception that the mineralized air bubble was drawn up into the bubble holder and subsequently discharged onto an externally placed watch glass, where the number of pick-up particles was counted with the aid of a microscope or hand lens. Drying was necessary when the discharged liquid interfered with the counting. The results of the bubble pick-up tests can be simply expressed in the form of the actual count. However, this can be misleading because the number of pick-up particles varies not only with the size of bubble but also with the size of particles. This short-coming is largely remedied by the use of the bubble pick-up index. as calculated from the following equation: PI = (pn/p) 100 [1] in which PI and pn are respectively the pick-up index and the number of pick-up particles under any test conditions, and p is the maximum number of pick-up particles of the same mineral under optimum flotation conditions, with the same size holder and particle. The bubble pick-up coefficient is a term coined to denote the difference between the bubble pick-up index of mineral particles in a liquid and that of the same mineral-liquid mixture plus a chemical reagent at the same pH value. For example, the difference between the pick-up index of a naturally floatable bituminous coal in a solution of water and kerosene and that of the same coal in water alone is a bubble pick-up coefficient. Compared with the contact angle method, the quantitative bubble pick-up method is inferior in accuracy but superior in sensitivity. Other advantages of the bubble pick-up method are that the apparatus can be easily assembled, the mineral sample is conventionally prepared, and the test procedure is relatively simple. References S. R. B. Cooke: The Flotation of Quartz Using Calcium Ion As Activator, Trans. AIME (1949) 184, p. 306. 'G. A. Last and M. A. Cook: Theory of Collector-Depressant Equilibrium at Mineral Surfaces. Paper presented at St. Louis Meeting, AIME (February, 1951).

Jan 1, 1954

By N. K. Chen, R. Maddin, K. T. Aust

Lattice rotations occurring on the tension and compression sides during the bending of molybdenum single crystals at room temperature were followed in detail. Observations were also made concerning crystallite rotations and slip traces. &apos;The results indicated the participation of (110) as slip planes and the<111>as slip directions. Crystallite fragmentation during bending was also noted. EVERAL investigations have been conducted on pure bending of face-centered cubic metals.&apos;-" Structural changes as a result of "bend-gliding," and the importance of bending and constraints during conditions of axial stressing, have been noted.&apos;," It was evident that the mechanism by which the bending deformation occurs is more complex than the case of simple shear. Studies of the bending of body-centered cubic metals from the aspect of the crystallographic mechanism appear to be lacking. Molybdenum single crystals therefore were subjected to deformation by bending in order to determine the reaction of the body-centered cubic lattice to bending stresses. It might be expected for the bending of single crystals that lattice rotation as represented by the axis of compression would proceed toward the pole of the active slip plane and that rotation of the tensile stress axis should indicate the slip direction.&apos; It was believed therefore that a study of the tension and compression sides of bent molybdenum single crystals should give data concerning the operative slip system. Specific problems which are pertinent to the overall picture of plastic deformation were also investigated, e.g., whether the constraints offered by pure bending give rise to the deformation band, and also the nature of the asterism occurring on the tension and compression sides during the stages of deformation. Experimental Procedure Eight single crystal specimens were grown from sintered molybdenum rods 143 in. diameter using the method described previously.6 The purity of this material was reported as 99.9 pct as described elsewhere.&apos; The specimens were % to 1/10 in. in diameter x 7 in. long, with single crystals approximately 1 to 2 in. in length occupying the entire center sections of each specimen. The specimens were elec-trolytically polished using an electrolyte of 300 cc methyl alcohol, 60 cc H2SO4, 130 cc HCl, and a current density of 4 amp per sq in. Each specimen was then loaded in a bending apparatus similar to that used by Yen and Hibbard,&apos; as shown in Fig. 1. The load was applied by means of a spring and screw arrangement through four ball-bearing surfaces set 1.5 in. apart. Either the inner two bearings or the outer two (A, B, Fig. 1) were attached to a movable steel plate (D) through which the load was transmitted. Since the apparatus was mounted on a track of the X-ray apparatus, the tension or compression side of the specimen could

Jan 1, 1954

By H. A. Shaw, H. G. G. Whitton

This paper describes the use of the electric-arc furnace for the production of tough-pitch, horizontal cast copper shapes and the production of copper anodes from tank house anode scrap. This installation is the only one of its kind in the United States. SINCE the initial use of electric-arc furnaces for refined copper melting on a commercial scale at Copper Cliff in 1936, this type of melting has been of extreme interest to everyone in any way connected with copper casting and fabricating. Early in 1948, Kennecott Copper Corp. decided to build an electrolytic copper refinery at Garfield, Utah. One of the major decisions to be made at that time was the type of furnace to be used for melting cathodes for casting into refined copper shapes and for melting anode scrap for the production of anodes. Based on the results obtained from arc furnaces by the Tnternational Nickel Co. of Canada, at Copper Cliff, and by the American Smelting and Refining Co., at Baltimore, coupled with certain important economic factors such as having an adequate amount of relatively cheap power available at the Magna Central Power Plant, high cost of poles and oil in the Salt Lake District, and the lack of natural gas at that time, the final decision was to install electric-arc furnaces rather than the standard type of rever-beratory furnaces. Experience has shown certain parts of the original installation to have been inadequate or in need of modification. Although the present status of arc-furnace melting at the Utah Refinery is far from perfect, nevertheless substantial progress has been made. At the Utah refinery, copper is melted in three 15-ft diam, size "M" Lectromelt furnaces, two of which are used for melting cathodes and one for remelting anode scrap. Each furnace is energized from a 13,800-225 v, 3-phase, 60-cycle, 6000-kva (at 40°C rise) oil-immersed water-cooled transformer. Auxiliary equipment for each refined copper furnace includes a charging machine, launders, ladle, 40 ft diam Walker-type casting wheel, bosh, and inspection conveyor. The anode furnace differs in that it is charged by hand from an elevated platform and the anodes are picked off the 24-ft diam casting wheel by a takeoff hoist and loaded directly into specially designed trailers, Figs. 1 and 2. Electrical Equipment Electric power to operate the arc furnaces is generated at the Kennecott-owned Magna Central Power Station two miles distant and transmitted to the Refinery outdoor substation at 44,000 v. At this point it is stepped down to 13,800 v and carried through concrete-lined underground tunnels to the switchgear and then to the primary side of the furnace transformers. The power is conducted from the Y-connected secondary bus bars of the transformer to the electrode arms by means of 22 flexible copper cable conductors per phase. Each cable has a cross-sectional area of 1,750,000 circular mils, giving a total area of 38,500,000 circular mils per phase. The power is carried from these cables to the three individual electrode holders by means of water-cooled copper bus tubing. The electrode clamps are incorporated in the electrode holders and are released by air pressure working against a spring in the clamp control cylinder. The movement of the electrode arms is either automatic or manual. The automatic control is used during melting and is regulated by three Westing-

Jan 1, 1954

By O. Vartianen, R. T. Hukki

A preliminary investigation of the collecting effects of various fatty acids in tall oil has led to a conclusion that the collecting power of fatty acids used in flotation increases with increasing un- saturation of the hydrocarbon chain. Linoleic acid was found to be an excellent collector for oxide minerals. TALL oil is a mixture of fatty and resin acids extracted as byproducts in the sulphate pulp industry. In the field of flotation a well-known example of this type of product is Reagent No. 708 of the American Cyanamid Co. Its successful use as a flotation collector with many nonsulphide minerals has been described by Falconer and Crawford.&apos; The composition of crude tall oil varies within wide limits.&apos; " By a number of methods the crude oil may be refined to produce a variety of refined products. This investigation presents a preliminary comparative study of collecting properties of the fatty acids in tall oil. In Finnish tall oils these constituents are primarily palmitic, oleic, linoleic, and linolenic acids.:&apos; The first is a saturated fatty acid having 15 carbon atoms in its hydrocarbon chain, plus one in the carboxyl group. The others have 17-carbon-atom chains and are unsaturated. It is of particular interest to note that palmitic, oleic, lino-leic, and linolenic acids represent increasing degrees of unsaturation with 0, 1, 2, and 3 double bonds, respectively. To test the collecting properties of the four fatty acids separately, the vacuum flotation technique described by Schuhmann and Prakash4 was used. By this method the boundary between flotation and non-flotation conditions was approximately delineated, with the use of ilmenite and several other minerals. Collector concentration and pH were the principal variables. On the basis of information obtained, actual flotation tests were run on an ilmenite-bear-ing ore in a laboratory flotation cell. Through the courtesy of P. Kajanne from the Department of Chemistry, Finland Institute of Technology, the following reagents were obtained for this investigation: 1—Palmitic acid, of Judex, had a purity of 95 pct as determined by parallel iodo-metric and spectrophotometric measurements. 2— Oleic acid, product of May and Baker Ltd., indicated purity of 98 pct. By iodometric and spectrophoto-metric determinations the oleic acid content was found to be 83.8 pct. In addition, it contained 6 pct linoleic, 1 pct linolenic, and 9.2 pct saturated fatty acids.&apos; 3—Linoleic acid was prepared from soybean oil by low-temperature crystallization. Its linoleic acid content was 95 pct by the methods indicated above. 4—Linolenic acid was prepared from linseed oil by low temperature crystalIization. Its linolenic

Jan 1, 1954

By J. T. Norton, N. J. Grant, A. R. Chaudhuri

MOST of the recent work to establish the mech-anism of creep in metals at high temperatures has utilized aluminum as the experimental material. It was thought desirable to initiate an investigation of a hexagonal close-packed metal, because of the relatively simple slip system, and compare the observed deformation characteristics with those that have been observed for the face-centerd cubic metals. High-purity magnesium was chosen for this purpose, first, because its strength and other mechanical properties are similar to those of aluminum in the same temperature range, and second, because the existing equipment was ideally suited to observe magnesium during creep. It is proposed in this paper to present a pictorial and qualitative account of the changes that high-purity magnesium undergoes during creep at 500°F. The characteristics of deformation of aluminum described below have been observed by various workers and accounts of these may be obtained from the papers of Chang and Grant.&apos;- These characteristics are: slip, subgrain formation, grain boundary sliding and migration, fold formation, deformation bands, and kink bands. It is well known that in a flat magnesium specimen, slip on the basal plane (0001) in the [1120] direction results in the formation of straight bands on the surface of the specimen. Schmid and co-workers&apos; have shown that this system is operative in the temperature range of -185" to 300°C (-300° to 572°F). They have also shown that a second system, slip on the pyramidal planes {1071} or {1012} in the [1120] direction, is operative at temperatures higher than 225°C (437°F). Between 225° and 300°C (437" to 572°F), therefore, deformation by both these systems is expected. Bakarian and Mathewson5 confirmed the occurrence of pyramidal slip on the {1011} plane and found that it resulted in irregular markings on the surfaces of their specimens. Burke and Hibbard6 obtained evidence of pyramidal slip in single crystals of magnesium deformed at room temperature. Bakarian and Mathewson5 suggested that the irregular appearance of these bands was due to slip on both of the pyramidal planes occurring simultaneously but in the same direction, the close angular relationship between the planes making this process possible. Furthermore, since neither of these planes is close enough to the basal plane, slip on the latter does not exhibit the irregular appearance of slip bands resulting from pyramidal slip. Experimental Procedure High-purity magnesium, supplied by the Dow Chemical Co., was used in these experiments. The analysis was as follows: Al, 0.0002 pct; Mn, 0.0018; Fe, 0.0024; Cu, 0.0002; Sn, 0.001; Ca, 0.01; Ni, 0.0003; Zn, 0.01; Pb, 0.0005; Si, 0.001; and Mg, 99.972. The magnesium was supplied in the form of 1/2 in. diam rods. The specimens had an overall length of 21/4 in., the round ends being threaded to fit the specimen holders. The previously round 3/16 in. diam gage section of the specimen had two parallel flats machined on opposite sides for microscopic observation, yielding a test zone having the dimensions of lx3/16x7/64 in. The specimens were electrolytically polished (without prior mechanical polishing of the machined flats), in a solution composed of 375 ml of ortho-phosphoric acid and 625 ml of ethyl alcohol.&apos; The cathode was a stainless steel sheet bent so that the specimen was completely surrounded. The voltage for successful polishing was 1.5 v at 100 to 300 milli-amp current. Electropolishing for about 45 min sufficed to obtain a good metallographic surface on the specimens after they had been machined. The creep tests were performed under constant load, and two types of equipment were used. In the first, designed by Servi and Grant,V he specimens were beam-loaded, and a furnace could be lowered to surround the specimen. As the microstructural changes could not be observed during the course of the test, the tests had to be interrupted periodically by removing the specimen for microscopic examination. The second unit was a high temperature microscopy furnace designed by Chang and Grant.&apos; The furnace was fitted with an optically flat quartz window having area dimensions 1.25x0.5 in., so that the whole test portion could be viewed through it at magnifications up to x240. The metallurgical microscope had three mutually perpendicular axes of motion, and, in addition, it was possible to measure angular displacements by rotation of the eyepiece. It was thus possible to make precise observations of the specimen during creep, and micrographs could be taken by attaching a camera to the eyepiece of the microscope. The average grain size of the specimens that were tested was about 1 to 3 mm. This grain size could

Jan 1, 1954

By D. J. Carney, E. C. Rudolphy

IT has been demonstrated that inclusion size, distribution, and composition affect the machin-ability of resulphurized steels. Merchant and Zlatinl concluded that large sulphide inclusions aided machining by forming a (lubricating) coating on the tool face. Boulger et al.² and Van Vlack³ noted that the size, distribution, and composition of the inclusions in the steel affected the machinability. Steel specimens containing large globular sulphide inclusions usually exhibited excellent cutting properties, while machinability was adversely affected by the presence of numbers of oxide-type inclusions. Consequently a thorough knowledge of all the factors which affect the inclusions in the final product is desirable. Since almost all the inclusions have their origin in liquid steel, it was necessary to begin a study of inclusions in free-machining steels by studying the inclusions and chemical segregation in the as-cast ingot. Very little information is available on the size, distribution, shape, and composition of inclusions in large, capped, free-machining steel ingots, particularly the B1113 grade. Gregory and Whiteley4 made a general study of the inclusions in a small, high sulphur, free-machining steel ingot. Also, numerous authors have described the solidification and segregation characteristics of the four basic types of steel ingots, namely, rimmed, capped,7 semikilled,7,8 and killed7,9,10 ingots. Most of these studies were made with plain carbon or low alloy, low sulphur steel. It was desirable to study not only the ingot but also the change in size, shape, and number of inclusions on rolling an ingot to a bloom and thence to a billet. This procedure was followed and it is hoped that this study may serve the dual purpose of adding to the general knowledge of ingot solidification as well as contributing to the knowledge of the size, shape, distribution, and composition of inclusions from the ingot to the billet in a high sulphur, free-machining steel. Procedure A 12.000-lb 23x35x75 in. slab ingot of the B1113 grade was cast, sectioned, and studied both macro-scopically and microscopically. An adjacent ingot from the same heat and of the same size was rolled to a 77/8x77/8 in. bloom and thence to a 21/2x21/2 in. billet. These various bloom and billet sections were also sectioned and studied macroscopically and microscopically. Sectioning the Ingot: The ingot herein described was obtained from the United States Steel Corp.&apos;s South Works Bessemer Blow No. 0193, a B1113 mechanically capped heat. The 23x35 in. ingot (No. 2) was teemed according to normal procedures and after stripping and transportation to the rolling mill was not placed in the soaking pit but allowed to air cool in an upright position. When completely solidified, the ingot was cut into sections by means of a powder scarfing torch and further sectioned by saw cutting as indicated in Fig. 1. Cut No. 2 (1x10x12 in.) from sections A through H was cleaned thoroughly, macroetched in a solution of 50-50 water and hot muriatic acid and used to obtain a macrograph of a horizontal section from the surface to slightly beyond the center of the 23-in. ingot dimension. Cuts No. 5 and 3 (lx81/2xl0 in. each) from sections A through H were treated in a similar manner to obtain a macrograph of a horizontal section from the surface to slightly beyond the center of the 35-in. ingot dimension. The composite macrograph of these horizontal ingot sections, which shows a vertical section of the ingot from top to bottom, is shown in Fig. 2. It should be noted that sections No. 2 are normal to sections 5 and 3 in the composite. Drillings for chemical analyses were obtained from selected positions within the above-mentioned ingot sections as noted in Fig. 3. The oxygen content was determined by the vacuum-fusion method. Samples for microscopic examination were cut from

Jan 1, 1954

ON Coal&apos;s Horizon one development rises above all others. That is the swift expansion of output to make Soviet Russia the largest coal producer on earth next to the United States. Few Americans are aware of the speed and extent of that expansion nor of the accompanying creation of a strong, resourceful mining machinery industry, nor of the extent and character of the mechanization of Soviet coal mining. Two initial clarifications are necessary for better understanding. First, we must keep in mind the sharp distinction between the Russian people and the communist Soviet dictators who rule them. The great mass of the Russian people are not members of the Communist Party as people here are Republicans or Democrats. They are not permitted to be members. There are, by various estimates, only 2 to 4 million members of that party in all Soviet Russia. The other 196 to 198 million are the victims of their tyranny and their terror. It is the activity of the Soviet rulers that concerns us here.

Jan 1, 1954

By Bernard York, John J. Reed

W. 0. Philbrook (Carnegie Institute of Technology, Phila.)—Mr. DeVaney&apos;s paper is a valuable addition to the growing technology of the magnetic roasting of lean iron ores. His furnace is ingeniously designed to permit close control of the process and to achieve high thermal efficiency by counter-current heat exchange and the withdrawal of both solid and gaseous products at relatively low temperatures. The principle of using a lean reducing gas to avoid over-reduction of the ore even at high operating temperatures (for rapid reaction rate) is thoroughly sound. The gas analyses and flow rates reported, however, are internally incon- sistent and render suspect any details of a heat balance based upon them. While it is entirely proper to consider the entrant gas as a reagent and to account only for the heat evolved by consuming a portion of the gas, many operators are accustomed to a heat balance using the total calorific value of the reagent supplied; and comparison of heat balances made with different bases of calculation can be quite misleading. Since Mr. DeVaney&apos;s paper is likely to be cited frequently in future discussions of magnetic roasting processes, it seems worth while to point out the internal discrepancies and to give alternate values of heat requirements for different bases of calculation.

Jan 1, 1954

By G. W. Brownell, H. T. F. Lundberg, R. W. Pringle, K. I. Roulston

The rapid improvement of the airborne scintillometer and the perfection of its efficiency for counting low energy gamma radiation has made it possible to work out a technique to map in great detail the radiation pattern at the earth&apos;s surface. On such maps low radiation over certain areas appears to indicate the existence of oil accumulations, forming a pattern similar to that obtained by the geo-chemists. RADIOACTIVE analyses of samples from the surface of oil fields were carried out more than 10 years ago in Alberta by the alpha particle ioniza-tion chamber technique,&apos; but large enough tracts could not be covered in these investigations to make possible any evaluation of the method as a means of oil exploration. Considerable interest has recently been revived, however, as a result of certain striking advances which have been made in the instrumentation available -for the measurement of radioactivity. It is the object of this paper to indicate the nature of these improvements in radiation technology and then to describe the attempts that have been made to interpret the radioactive patterns obtained in the course of airborne recordings with the new instruments. Since the survey can be carried out from the air and records can be accumulated over vast areas in a short time, the result may easily lend itself to statistical treatment. Areas have been surveyed in Alberta, British Columbia, Saskatchewan, Quebec, Texas, New Mexico, Nebraska, Colorado, Utah, and Montana. Producing fields in Alberta and West Texas have been flown over several times in different directions, Fig. 1. The operations were then extended into unknown territory and drill holes were put down on the anomalies which looked promising. The results from these drillings were encouraging and have given hopes for the development of an entirely new method of oil exploration. Any large scale method for the survey of radioactive anomalies must be based on the measurement of gamma rays, as beta and alpha rays have much too short a range to be of any significance. Thus the essential improvement which has made the present stage of this work attainable is the development of new highly sensitive detectors for gamma radiation. In the past the only detectors of any consequence that were available were the ionization chamber and the geiger counter, but both of these suffer from the defect that only a small proportion of the gamma rays passing through the counter are detected, possibly 0.1 to 0.2 pct. The recent development of the scintillation counter2,3 has completely transformed the situation and has had a considerable impact on many branches of nuclear technology. The detection of alpha particles in zinc sulphide screens by visual observation of the individual scintillations which these particles produce dates back to the early spinthariscope of Rutherford and Crookes, but the combined use of an appropriate scintillating phosphor and photomultiplier tube had to await the technical development of the latter many years later. With this development came the modern era of the scintillation counter and a knowledge of phosphors which have a large light output under the bombarding action of gamma radiation. Some of these phosphors are relatively dense and are capable of stopping a large proportion of the incident gamma radiation. As the sensitive region is the whole volume of the crystal, a very high detection efficiency, 50 pct or more, can be obtained for medium energy gamma rays. Scintillation counters for geological purposes were first developed in 19494-6 in an attempt to utilize this remarkable improvement in efficiency, which has the attractive consequence that only a small portion of the normal background of the counter is due to cosmic radiation. In 1949 tests were made in northern Saskatchewan by Lundberg Explorations Ltd. with portable scintillation counters which gave excellent results in the search for uranium and served to indicate unknown uranium deposits in areas previously closely surveyed with geiger counters. Portable scintillometers (registered in Canada) are now commercially available and in regular use,&apos; and the adaptation of the instrument to radioactivity oil well logging has also been very successful.8 Initial attempts to measure radioactivity from aircraft with scintillation counters were made during this period in the same area and yielded most encouraging results. It would be appropriate to consider some specific requirements for airborne investigations. The essential problem to be met in the detection of any radioactive source is the necessity of obtaining a signal greater than the statistical fluctuations of the background counting rate for the instrument. It is possible to show that Nt>2k2 is the condition for detectability of a signal where N = average background counting rate for the detection. t = time constant of the counting rate meter, used to determine the average number of counts arriving in a certain predetermined time interval. N&apos; = average source counting rate at the detector. k = N/N&apos;, and N>>N&apos;. Sample values are given in Table I. Assume that the aircraft carrying the equipment is travelling at 120 mph, in which case it will cover 176 ft in 1 sec. Assume also, as a first approximation, that a point source target is in range when the air-

Jan 1, 1954