By G. Vaux, M. L. Fuller

AN apparatus and procedure for the determination by X-ray reflection of preferred orientation of crystals in rolled metal with the Geiger counter X-ray spectrometer was described by Schulz.' This is an excellent procedure and we have used it continually for several years. In our use of the procedure, two modifications have been made and used during most of this period. One of these provides for automatic scanning and recording of the reflections, and the other makes possible the application of the procedure to coarse-grained specimens and permits measurement of almost all orientations without resort to the transmission technique. The automatic scanning and recording are accomplished by a motor drive of the inner ring of the Schulz apparatus (see R, in Fig. 2 of his paper and R2 in Fig. 1 of this note) in synchronism with the chart recorder of the North American Philips 90" X-ray spectrometer. A rate of 10" per min is used. A scan of 180" is obtained corresponding to poles on the stereographic projection whose locus is a great circle. The modification for coarse-grained material is accomplished by allowing a larger area of the specimen to contribute to the X-ray diffraction. In the Schulz apparatus the incident X-ray beam is confined by a slit system to rays in the plane of the spectrometer. Schulz demonstrated that this restriction of the X-ray beam permits a survey of the X-ray reflections without correction up to about 80" on either side of that specimen position in which the specimen is perpendicular to the plane of the spectrometer. This is the angle + of rotation of the inner ring R2. One of these slits is horizontal and extends across the X-ray source side of the specimen. In the modification this slit is removed, thus permitting greater divergence in the X-ray beam and the irradiation of a larger area of the specimen surface. Fig. 1 shows the apparatus with the motor drive and with the slit removed. Discontinuities in the recorded X-ray intensity plot due to the few participating crystals in coarse-grained metal are much lessened. The increased divergence does not cause reflections from other crystal planes to enter the Geiger counter slit. An important advantage of the original Schulz scheme is thus lost and a system for correction is required. To do this, a compact of atomized copper powder was prepared and tested by the original Schulz method for the absence of preferred orientation. The horizontal slit was then removed and a curve recorded showing the variation of intensity with angle +. In our arrangement the intensity was uniform within the range + equals ±30°. Beyond this the intensity fell off rapidly reaching zero at ±90°. The curve thus produced is then used to correct measurements made on preferred orientation specimens. In practice this is accomplished by constructing from this calibration curve a family of curves which, as a transparency, can be superimposed on the recorder chart to read corrected intensity directly. Not only does this method permit the handling of coarse-grained material but it also makes possible the plotting of intensities almost to the circumference of the stereographic pole figure projection. Thus, nearly the entire pole figure can be plotted without the necessity of using the transmission technique. Moreover, intensities are much greater, an advantage when surveying crystal planes of poor reflecting power.

Jan 1, 1954

By T. A. Read, M. S. Wechsler, D. S. Lieberman

A theoretical analysis of the austenite-martensite transformation is presented which predicts the habit plane, orientation relationships, and macroscopic distortions from a knowledge only of the crystal structures of the initial and final phases. THIS paper presents a new theory of the formation of martensite. This theory makes possible the calculation of the austenite planes on which the martensite plates form, the orientation relationship between the austenite and martensite crystal axes, and the macroscopic distortions which are observed. The only input data needed are the crystal structures and lattice parameters of the austenite and martensite. Considerable effort has been devoted over the past thirty years to the development of an understanding of the crystallographic features of martensite reactions. Much of this work has been done on steels and iron-nickel alloys, for which a great deal of data has been accumulated concerning the shape and orientation of the martensite plates, the relative orientations of the austenite and martensite crystal axes, and the observable distortions which result from transformation. These observations are reviewed in refs. 1, 2, and 3. The first major step toward an understanding of these phenomena was made in 1924 by Bain,' who showed that the a body-centered cubic structure can be produced from the 7 face-centered cubic structure by a contraction of about 17 pct in the direction of one of the austenite cube axes and an expansion of 12 pct in all directions perpendicular to it. Since that time, most of the efforts at further interpretation have been made by investigators who have worked from the phenomenological data, incorporating some of the information from the lattice properties, and have sought an analysis into likely deformations which would produce the observed results."- "11 but the three most recent papers on the subject have already been reviewed in some detail." Machlin and Cohenl0 measured the components of the distortion matrix and verified that the habit plane is a plane of zero distortion and rotation for the (259) case. They showed that the measured distortion matrix, when applied to the parent lattice, does not yield the product lattice and hence some inhomogeneous distortion must occur. Frank,u working from the lattice properties and taking some clues from the observations, considered the correspondence of close-packed rows and planes in the austenite and martensite. He predicted substantially the observed lattice relationship and habit plane for certain steels which have a (225) habit. Geisler12 suggested that there is a natural tendency for the habit plane to be a (111) and postulated certain slip processes to account for the fact that the experimentally observed habit plane is irrational and deviates from the assumed one. The present work differs from previous treatments of martensite formation in that it permits calculation of all the major manifestations of the process. Habit plane indices, orientation relationships, and observable distortions are all calculated from a knowledge of the crystal structures of the initial and final phases alone. The calculations contain no adjustable parameters. The agreement found between calculated results and the observations reported in the literature constitutes powerful evidence in favor of the mechanism of martensite formation proposed. The theory is applicable to systems other than steel (as is discussed later in this paper) which exhibit a diffusionless phase change but because of the wide-spread interest in the austenite-martensite transformation, particular attention will be given to the iron-base alloys. For other systems which undergo a similar face-centered cubic to face-centered tetragonal transformation, the mathematical treatment is identical with that presented here. Hence the theory successfully describes the transformation in the indium-thallium alloy.'" Homogeneous Transformation to Martensite The distortion which any homogeneously transforming volume of austenite undergoes in order to become martensite is shown in Fig. 1, as was first suggested by Bain.' (This distortion will hereafter be referred to as the "Bain distortion.") This specification of a contraction along one cube axis ;ombined with an expansion in all directions perpendicular to this axis describes what is properly called the "pure" distortion associated with this transformation. The distinction between a "pure" and an "impure" distortion plays an important part in the discussion which follows. A "pure" distortion is characterized by the existence of at least one set of orthogonal axes fixed in the body which are not rotated by the distortion. (These are called the "principal axes" of the distortion.) No such set of axes exists in the case of an "impure" distortion. On the other hand, an impure distortion can always be represented as the result of a pure distortion combined with the rotation of the specimen as a rigid body. For a given impure distortion the corresponding pure distortion

Jan 1, 1954

By E. P. Pfleider, Rolland L. Blake

IT is generally believed that the amount of diamond drilling will increase appreciably in the next decade, as the seaarch for minerals throughout the world becomes more difficult and intense. An attendant problem may be one of short diamond supply, resulting in higher bit and drilling cost. With this background, the U. S. Bureau of Mines' and the School of Mines at the University of Minnesota' have established comprehensive research programs in diamond drilling. One of the several aims is the design of a more efficient bit, which would lower diamond consumption and increase rate of advance, both essential in reducing drilling costs. The objective of the specific research problem" discussed in this paper was an investigation of the cutting action of the cliamonds set in a diamond drill bit, cutting action meaning the manner in which the diamonds cut or. loosen the minerals in the rocks being drilled. In the literature on cutting action such descriptive terms are used .as: grinding, wearing, cutting, breaking, shearing, scraping, melting, and chipping. These actions were seldom described or defined. Grodzinski describes the cutting action of a single diamond in the shaping of certain types of material as "breaking out chips of the material." Brittle mate-. rials break as small separate chips, and tough materials, because of heat generated, give a continuous chip. Deeby said about diamond drills: "When diamonds are forced into the formation and rotated, they either break the bond holding the rock particles together, or they cause conchoidal fracture of the rock itself. The former action occurs when drilling in sandstones, siltstones, shales, etc. and the latter action when drilling in chert, flint, or quartz." He said that diamonds cut on the "grinding principle" but he does not define or elaborate on this action. The cutting action of diamonds on glass was first investigated about 1816 by Dr. W. H. Wol-laston, an English physicist. The best glass-cutting diamonds have a natural or artificially rounded cutting edge. This edge first indents the glass and then slightly separates the particles, forming a shallow and nearly invisible fissure. Since none of the material is removed, this action is one of splitting rather than cutting. No other reports of research work on the cutting action of the diamond were found, and further work was considered justified and advisable. It is impractical, even if possible, to observe directly the cutting action of a diamond drill bit in rock; therefore it was necessary to devise an indirect method. It was believed that a study of the following three observations would lead to a better understanding of the cutting action: 1—the appearance of the minerals or rock surface in the bottom of the hole, 2—the size, shape, and other characteristics of the drill cuttings, and 3—the condition of the diamonds in the bit. The cutting action in a particular rock probably varies with bit pressure and speed. If the bit were slowly lifted off the rock, the effect of decreasing pressure might obliterate those bottom hole characteristics that are specific at the test pressure. Likewise, if the drill were stopped with the bit still in contact with the bottom of the hole, then decreasing speed effects would tend to obliterate the characteristics at the set test conditions. Therefore, in order to preserve those cutting effects impressed on the rock at test conditions, it seemed necessary to lift the bit off the bottom of the hole almost instantaneously once drilling conditions, i.e., revolutions per minute, pressure, and water flow became constant. In addition to observing the cuttings, the bit, and the bottom of hole, it seemed desirable to collect some quantitative data for purposes of correlation with the observations and for a record of bit performance. Consequently such data as revolutions per minute, force applied, and rate of advance of the bit were recorded. Six rock types, listed in Table I, were chosen for the tests. It was felt that these rocks had most of the variable characteristics of texture, bonding, and mineral hardness met in the common rocks generally being drilled. The sandstone was so poorly cemented as to be friable, even though most of the cement was silica. The limestone, though well cemented, was quite porous. Originally it was planned to conduct the tesk work with a full-scale drill unit, using EX bits, 7/8-in. core, 11/4-in. OD. The drill worked well, but was too cumbersome for rapid, accurate drilling of many short holes (1 ½-in.) in varied rock types. A new

Jan 1, 1954

By N. L. Carwile, G. W. Geil

A metallographic study was made of deformation twinning (Neumann lamellae) in ingot iron slowly deformed in tension at —196O and —150°C. The results showed that twinning is initiated mainly during the initial stages of plastic deformation. However, the breadth of the twins generally increases with increase in strain up to fracture of the specimen. HE results of an investigation of the effect of low I temperatures on the flow, fracture, strain hardening, and strain aging characteristics, and the true stress-strain relationship for specimens of ingot iron deformed in tension were reported recently.1,2 In that study specimens of ingot iron, in different initial conditions, were slowly deformed in tension at various temperatures between —196" and +100°C. A phenomenon observed, but only briefly reported, was the formation of deformation twins (Neumann lamellae) in the specimens deformed at the lower temperatures. Preliminary metallographic examination of these specimens indicated that there was apparently some correlation between the deformation twinning and the strain of the specimen and that this factor merited further investigation. Some recent investigations have indicated a direct association of Neumann lamellae and the fracture of the metal. Bruckner".' * postulated that the twinning immediately precedes the fracture and the latter is initiated by the stopping of the propagation of twins, either at subgrain boundaries or at other structural features. Tipper and Sullivan5 postulated that Neumann lamellae are initiated by the shock or a shock wave set up at fracture in the still highly stressed unbroken metal, and that a high rate of deformation is a necessary condition for their formation. An extensive metallographic examination, therefore, was made of many of the specimens used in the study of ingot iron at this Bureau and of additional specimens deformed to selected strains under various conditions. The present paper summarizes the effects of deformation under these conditions upon the breadth and scope of the deformation twins. Other features of twinning will be discussed in another paper. Material and Testing Procedure All of the specimens were prepared from one lot of ingot iron, as hot-rolled, of chemical composition other than iron as follows: C, 0.02 pct; Mn, 0.02; P, 0.005; S, 0.018; Si, 0.002; Cu, 0.10; 0, 0.058; and N, 0.002. Cylindrical tensile specimens with a 2 in. gage length were used. The reduced section was slightly tapered from each end; the diameter (0.438 in.) at the midsection of the gage length was about 0.003 in. less than at the ends. The specimens were finished to the final dimensions by grinding and polishing in the axial direction. The ends of the specimens were machined with 3/4 in. x 10 threads and the shoulder fillets were machined to a radius of 0.75 in. The specimens were extended slowly in tension (deformation rate less than 0.5 pct reduction in area per minute) while immersed in an appropriate cryogenic liquid maintained at the desired temperature. The minimum diameter of the specimen was measured during the test by means of a specially designed reduction of area gage accurate to 0.0001 in." A detailed description of the testing equipment and the method of maintaining the desired temperature is given in a previous paper.' Each specimen, after deformation to a specified strain at a selected temperature, was sectioned longitudinally and examined metallographically. The preparation of specimens for metallographic examination was carried out in the usual manner by mechanical polishing and etching. Results and Discussion Deformation twins in specimens of ingot iron extended slowly in tension at —196" and —150°C are shown by the representative micrographs of Figs. 1

Jan 1, 1954

By Hobart M. Kraner

THE mineralogy of blast furnace sinter is of interest because its mineral content is one of the important factors contributing to its character. There are so many other factors affecting the properties of the sinter, however, that it is well to mention them here. The proportion and character of the raw materials, that is, raw ores, concentrates, returns, and fuel, as well as the mixing and the water content, all have a marked effect on the physical properties of the product and the degree to which sintering action can be carried on. The process of sintering is a relatively fast operation. In as much as appreciable time is required to carry on processes of fusion in such masses of low thermal conductivity, large lumps of hematite ore frequently remain unfused and partly unchanged in state of oxidation in the sintering process. The kind, the grain size, and the amount of fuel used affect both the completeness of the fluxing reaction and the prevailing atmosphere. The rate of reduction in laboratory tests is not only dependent upon the state of oxidation of the sinter but also upon the sizing and porosity. Atmosphere and temperature affect the state of oxidation of the iron oxide, and the atmosphere alone may determine the ferrous minerals that finally develop. The rate and extent of cooling, the type of coolant, the subsequent handling, and screening all have serious effects upon the type of sinter that eventually enters blast furnace bins. The degree to which actual fusion or fluxing takes place in the sintering operation has a marked effect upon density. A sinter which has been extensively fused by high content of fuel in the batch will no doubt have a higher weight on the bulk basis than one which had a lower fuel content. As high temperatures are required to do this job, the iron oxide under these conditions will be largely magnetite. Sintering at low temperatures to produce larger proportions of hematite means a decrease in the amount of liquid formed and a much more sensitive bonding process. In this case the liquid must be distributed more uniformly and thereby used more efficiently than would be the case where higher temperatures were permitted to prevail more or less indiscriminately. Where coarse ore particles are used in a sinter mix it is not expected that any particles coarser than 1/4-in. can be fused and incorporated in the system to such an extent that the gangue contained within these lumps will have been converted or fused by the sintering process. It is for this reason that coarse ore, returns, or both, in a sinter usually result in a sinter which breaks easily and at the same time may contain some of the original minerals of the lump, such as quartz and hematite. In examination of sinters at Bethlehem Steel Co. minerals such as quartz and corundum have been found, none of which are considered normal associ- ates of wustite or magnetite. Some degree of heterogeneity or lack of equilibrium is not unusual in the sintering process. The differences in specific gravity between hematite and magnetite might be ample reason for poor strength in a not very well sintered mass containing coarse particles of. ore or returns. The shrinkage taking place in a lump of hematite in its conversion to magnetite by temperature and/or atmosphere is appreciable. Sintering of ores as it is carried out is crude chemistry, for the grain size is relatively coarse, the application of heat is certainly not uniform, and the time factor is inadequate for other than partial completion of reactions. Coarse lumps of coke or coal cause local heating around these centers, and fuel which is too fine may result in such slow burning that sufficiently high temperatures are not always obtained. High temperatures are essential to the work required. The Swedish practice of sintering is established on the basis of producing an easily reducible product high in hematite. This is achieved through uniformity of grain size in the sinter mix and close control of the temperature through careful regulation of fuel and sintering rates. This produces a sinter which is very tough in character and which has a high degree of porosity. Although the hematite content is not produced upon cooling by drawing air through the mass, there would be greater possibility of accomplishing this reaction with this type of sinter than is the case in American practice. In the latter, the temperatures are so high that temperature alone converts most of the mass to magnetite. The grains are so coarse in the final product that together with the fluxed condition it would be difficult to reoxidize them to hematite upon cooling. An examination of the iron-oxygen diagram' shows that hematite does not exist above 2651°F. It also shows that there is no liquid in the pure magnetite-hematite system until 2881°F is reached. On the other hand, in the system magnetite-wustite liquids exist at considerably lower temperatures than this. It will be seen, therefore, considering only the iron oxides, that the bonding action obtained in America in sinters comes about through considerable temperature and/or reducing conditions that produce compositions containing even less oxygen than is contained in magnetite or than results from the fusion of silicates. The bonding obtained from the iron oxides is encouraged by the reducing conditions that prevail in the vicinity of the fuel particles in a mass of this sort, where temperatures are above 2600°F. As magnetite and wustite are opaque, they do not lend themselves to petrographic study by transmitted polarized light. The silicates found in sinter and the glass that has not crystallized transmit light and can be studied by these methods in which indices of refraction and other optical properties of anisotropic crystals lead to their definite identification. The index of refraction is the only property that can be measured in glass under the microscope, and this is a clue to its probable approximate composition.

Jan 1, 1954

By A. E. Lee

THE Blackwell Zinc Co., Inc., a subsidiary of the American Metal Co., Ltd., operates a horizontal retort zinc smelter at Blackwell, Okla. The plant has 14 furnace blocks of 800 retorts each, fired with natural gas on a 48 hr cycle. Over 13,000 tons of zinc-bearing material, chiefly sulphide flotation concentrates, are treated monthly to produce slab zinc and high lead-cadmium fume. In 1942 a program of rebuilding and modernizing the smelter was started. By 1947 furnace smelting capacity had been increased to a point where roasting and sintering facilities were inadequate, and it was necessary to purchase oxidized materials to supplement sinter production. The seven 210 ft Ropp roasters and three 42 in. x 44 ft Dwight-Lloyd machines then in use had been in service at least 20 years and were in need of major rebuilding. Thus it was entirely practical to consider all new equipment and a change of method rather than rebuilding and repairing obsolete units. A study of the problem indicated that roasting as such could be eliminated and roasting and sintering accomplished in one step by a modification of the Robson process,' which had been used since the early 1930's by the National Smelting Co., Ltd., at their plants at Avonmouth, England, and Swansea Vale, South Wales. Francis P. Sinn, General Manager, Zinc Smelting Operations, The American Metal Co., Ltd., who was familiar with the practice in England, suggested the use of one large machine for the entire operation from concentrate to sinter. One step sintering appeared to best meet Blackwell's plant requirements and indicated substantial savings in labor, gas, coal, and repair costs. Choice of Machine Size The sinter machine size was set at 12x168 ft for a rated capacity of 540 tons per day. This tonnage, produced on a five day week, would meet the seven day requirements of the 14 furnace blocks. The one large machine was quoted at a lower cost than two or more 6 ft wide machines of similar total capacity. Further, the larger machine could be housed in a smaller structure and only one set of equipment for charge preparation and delivery and for disposal of sinter cake was needed. One machine on a five day week made possible a concentration of the skilled operating personnel and required less men than a plant including two or more machines and related equipment circuits. Fewer units of equipment meant less maintenance, and the two down days weekly allowed ample time to repair and, if necessary, to make up lost production. Experience had indicated better sintering quality and rates with larger masses of material, not only on wider machines, but also in deeper beds. The ratio of windbox perimeter to area for the 12x168 ft machine is 0.179, compared to 0.353 for a 6x102 ft machine and 0.617 for a 42 in. x 44 ft machine. This meant less air leakage with resulting fan power savings and less spoilage of charge along the pallet sides. Performance Initial operation of the new sinter plant was made in November 1951 and regular production attained late in December. The average product sinter output during 1952 and the first half of 1953 has been 18.2 tons per hr. The average for one month has been as high as 22.4 tons per hr. Considerable experimenting with varied operating conditions accounts in part for the below capacity — 24 tons per hr — average output, and work to further improve production rate continues. A typical sinter analyses is 66.0 pct Zn, 0.3 pct Pb, 0.1 pct Cd, 0.3 pct S, 8.0 pct Fe, 2.0 pct SiO,, 0.8 pct CaO, and 0.2 pct MgO. Use of this material has made possible increases in furnace burden and improved furnace operation over the former practice using sinter made from Ropp roasted concentrates. Better lead and cadmium elimination in sintering has permitted the furnace production of slab zinc lower in lead and cadmium. Anticipated economies of operation have largely been gained. The sinter plant is operated by seven men per 8 hr shift — one head operator, three equipment operators and three sweepers — plus one oiler on day shift only. While it has been necessary at times to operate seven days a week to produce the required sinter tonnage, the five day work week usually has been adequate. Consumption of natural gas for sinter bed ignition is 200,000 to 300,000 cu ft per day. Green Ore Sintering Practice The 30 to 31 pct sulphur content of the —200 mesh zinc concentrates is the fuel used to sinter the charge, no coal addition being required. In the feed to the machine, sufficient concentrates are added to crushed return sinter fines containing 0.3 to 0.5 pct sulphur to produce a charge averaging 5.0 to 6.5 pct sulphur. Since the return sinter used in Blackwell's practice is varied from — 1/2 to — 1/8 in., the actual sintering mixture of fine sinter and concentrates is somewhat higher in sulphur. The coarser sinter particles are too large to resinter and merely aid porosity in the sinter bed. The ratio of concentrates to return sinter in the charge ranges from about 1:4 to 1:5.5. Variations are based on the appearance of pried up bed sections, bed exit gas temperature trends, windbox suctions, and return sinter size. Sufficient sulphur must be used to obtain fritting of the charge into a soft sinter cake and to aid in the elimination of lead and cadmium. Excessive feed sulphur will result in partial slagging of the cake impairing porosity and prolonging sintering time.

Jan 1, 1954

By J. Walter Snavely

PRESENT-DAY processing in many industries, calcining, sintering, briquetting, beneficiation and nodulizing, increasingly calls for the handling of large volumes of hot bulk materials. Various types of conveyors have been employed. This discussion will cover the factors governing their selection. For temperature ranges up to 400°F, or approximately 200 °C, a wide range of conveyors is available. Special constructions of rubber conveyor belts, steel conveyor belts, vibrating and shaker conveyors, apron conveyors, and drag chain conveyors, all are used successfully. As temperatures go well above 400 2F, however, choice of conveyors is narrowly limited. This paper will consider the problem of handling bulk materials only where the temperatures exceed 400°F. The arbitrary selection of 400 °F as a dividing point undoubtedly can be challenged, as special conveyor belting constructions are available which are suitable for temperatures in excess of 400°F. However, when the relatively short life of such belts and the cost of their replacement, with the attendant down time, are balanced against the reliability and long service life of the properly designed steel constructed units to be discussed, there is little question in any operator's mind that the special belts are more expensive to use. Because the conveyors under study are for the handling of bulk materials, inevitably including a high proportion of fines, obviously wire mesh belts cannot be included for consideration. Even though this type of conveyor is widely used at high temperatures, i.e., for carrying glassware through a lehr, it is unsuited for the conveying of bulk materials, and therefore will be excluded from further discussion in this paper. Preliminary to the study of the conveyor itself is the determination as to whether the material is to be cooled while it is being handled, or whether the processing requires retention of all heat and the maintenance of a given temperature range. In the majority of cases cooling is incidental to or part of the handling process, when the handling, for example, follows completion of sintering, roasting, calcining, refining, or some other process. To meet such operating conditions successfully, the conveying medium used must have: 1—a construction capable of withstanding maximum initial temperatures of the material being handled. 2—a construction providing efficient heat transfer for cooling. 3—a construction providing dependable operation and long life with minimum service requirements, and 4—a construction providing controlled and efficient conveying. Under the usual conditions of cooling during the handling, the construction selected to withstand the initial maximum temperatures does not necessarily involve using alloys, as excellent results can be achieved with normal carbon steels and cast irons, when they are properly applied and proportioned. The earliest and simplest type of conveyor for handling very hot materials is the cast steel drag chain conveyor, still widely used for handling hot cement clinker, as illustrated by Figs. I and 2. Because of the rugged and generous proportions of the chain link design, low carbon steels are entirely suitable for the links. The pins, however, must be alloy steel. The simple, rugged construction of this type of conveyor makes it readily capable of withstanding high initial temperatures, even though the chain is operating buried in the material. The drag-chain type of conveyor has advantages and limitations. Although the efficiency of the heat transfer is relatively poor, the life of the conveyor is reasonably long, and because of its crude simplicity it does not require much servicing. However, as a conveyor, it is limited in capacity, and largely limited to horizontal runs. Furthermore, because of the crude design, heavy weight, and the chain operating at the temperature of the material, greatly reducing permissible operating chain pulls, this type of conveyor is limited to relatively short centers. Another type of conveyor that has been used for very hot materials is the cast pan conveyor. Because of its very generous proportions the cast pan, which is made of either cast iron or malleable iron, can withstand initial maximum temperatures. It also provides efficient heat transfer for cooling. Further, it is on efficient conveyor construction, which can be used for inclines. Because the chain employs rolling friction instead of sliding friction, and is not in the maximum temperature zone, much longer centers are possible. It is this type of conveyor that is frequently used in the casting of various metal pigs, pig iron, and aluminum; it is obvious, therefore, that very high initial temperatures are being handled. With this kind of conveyor the return run is frequently sprayed with water to accelerate heat transfer. The build-up of residual heat in the very heavy cast pans is thus overcome. The outboard roller steel pan conveyor is an improved pan conveyor' which provides high rates of heat transfer and substitutes formed steel pans for the heavy cast pans. It is a very efficient conveying medium. The details of this particular construction are clearly shown in Fig. 3. An early application of this type of conveyor is shown in Fig. 4. In this case the conveyor units are handling roasted phosphate rock at average temperatures of 1000" to 1500°F, and frequent maximum temperatures as high as 1900°F. Several widths are used. The capacity of the unit at a speed of 50 fpm is approximately 30 tph per inch of width at peak loadings, average capacity being about 1/3 of peak loading. The assembled conveyor is shown in Fig. 5, with views of both the top and the underside to show all the construction details. In particular, the following general design principles were carried out in this construction:

Jan 1, 1954

By J. H. Bechtold

Tensile properties of annealed molybdenum were investigated from 1000" to—200°C. In the vicinity of room temperature a well-defined transition in tensile properties occurs. Reduction in area decreases from over 80 pct to 0 pct and, simultaneously, the yield strength increases about 60,000 psi. MOLYBDENUM, tungsten, iron, and many other metals and alloys with the body-centered cubic and hexagonal close-packed crystal structures change from ductile to brittle behavior over some relatively narrow temperature range. The temperature at which this transition in ductility occurs depends on chemical composition, microstructure, and method of testing. When fine grained, completely recrystallized molybdenum of commercial purity is tested in uniaxial tension at a slow strain rate, the transition occurs at slightly below room temperature.' Iron2 and tungsten3 tested under similar conditions become brittle at temperatures close to the boiling point of nitrogen, — 195°C and at about 200°C, respectively. A sharp change in ductility is uncommon in metals with the face-centered cubic crystal structure, however, a relatively sharp transi- tion in notched bar impact properties has been observed below room temperature in a face-centered cubic copper-antimony alloy.4 A transition from ductile to brittle behavior is usually explained by the concepts originally developed by Ludwik,5 and discussed and elaborated on by others including Orowan,6 Hollomon and Jaffe,7 and Gensamer8 In brief, there are two aspects to strength, first the resistance to flow and second the resistance to fracture. Both are functions of temperature, strain, strain rate, stress system, composition, and microstructure. With decreased test temperature the flow stress required to initiate plastic deformation increases more rapidly than the fracture strength and brittle fracture occurs at that temperature where the yield strength equals or exceeds a brittle fracture strength. This investigation was conducted to determine the effects of temperature, strain, and rate of straining on the flow and fracture strengths of molybdenum above, through, and below the ductile-to-brittle transition. Other variables were held constant during testing. This information is believed to show

Jan 1, 1954

By L. Thomassen, N. Spooner, J. M. Thomas

NI-CR and some Ni-Cr-Fc alloys, when used as electrical resistance heating elements in reducing atmospheres, at times suffer rapid breakdowns due to so-called "green rot." These reducing atmospheres are most frequently used in bright annealing and heat-treating furnaces which are kept for long periods of time at 1500' to 1800°F. The green rot is a preferential oxidation of the chromium in the alloy to such an extent that the remaining metal frequently becomes ferromagnetic. The Curie point (magnetic transition point) at room temperature for a pure Ni-Cr alloy is known to be at about 7 pct Cr.¹ This represents a severe loss in chromium for one popular grade of resistance alloy, which is nominally 80 pct Ni-20 pct Cr. The formation of oxides along the grain boundaries makes the ribbon brittle and gives the fracture a green, earthy appearance—hence the name. The authors have studied this phenomenon, simulating the industrial conditions by heating resistance ribbons in various reducing atmospheres, such as moist hydrogen or the atmosphere specified in the ASTM test.² This atmosphere contains 16 pct H2, 10 pct CO, 4 pct C02, 1 pct CH1, 1.5 to 2.5 pct H2O, balance N2. Little success was had in producing severe corrosion with the commercial 80 pct Ni-20 pct Cr alloys. It had been noticed, however, that 90 pct Ni-10 pct Cr alloy wires deteriorated very rapidly when placed in the bottom of narrow thermocouple protection tubes. The bottoms of the tubes with the wires were heated in air. This took place both in porcelain tubes and in Inconel* tubes either with the cold end open or loosely stoppered with asbestos. On examination the wires showed microstructures which would be classified as green-rot corrosion. Subsequent investigations with various alloy wires confirmed the observation that corrosion occurred in some wires, including 80 pct Ni-20 pct Cr alloys, much more rapidly in such tubes than had occurred previously in test atmospheres mentioned above. When 90 pct Ni-10 pct Cr alloys are oxidized with an abundant air supply, the oxide coat consists of both nickel and chromium oxides. In this case thermodynamic equilibrium between the oxides is not established. However, when oxidized 90 pct Ni-10 pct Cr alloy specimens were heated to 1500" to 1800°F inside small diameter tubes, the oxide coat transformed to a bright metallic outer layer of nickel or nickel-rich alloy, beneath which appeared a green oxide, followed by intergranularly attacked metal. The obvious explanation is that in the narrow tubes, thermodynamic equilibrium is being established according to the equation NiO + Cr (in alloy) ? Ni + Cr2O3 This reaction is favored due to the fact that the oxygen pressure over nickel oxide is more than 10"' times the oxygen pressure over the green chromium oxide. The initial oxygen in the tubes is depleted very rapidly by oxidation of the wire and of the tube, if it is metallic. A confirmation of the occurrence of the reaction, reduction of NiO by the chromium in the alloy, was obtained by putting oxidized nickel foil into an evacuated quartz tube along with a piece of bright 90 pct Ni-10 pct Cr alloy ribbon, and heating the tube at 1820°F for a number of hours. The nickel oxide on the foil was completely reduced to pure nickel, leaving a bright foil. The 90 pct Ni-10 pct Cr alloy became strongly magnetic and showed the typical green-rot structure. Weights of the samples before and after testing showed the weight loss of the foil to approximately equal the weight gain of the ribbon. Evidently the bottom of long, narrow protection tubes, stoppered or not, may under certain conditions act just as the sealed quartz tubes in respect to being a confined space in which oxygen is not freely replenished. This condition of oxygen depletion can be prevented by introducing a small amount of air into the bottom of the tube. Many conditions becloud the green-rot phenomenon, such as carburization, sulphidization, and the presence of other corrosive agents. However, these experiments have shown that the basic reaction is a case of internal oxidation which can occur simply by adjusting the oxygen pressure to a low enough level so that the atmosphere will leave the nickel intact and oxidize the chromium. The action of the other agents in commercial atmospheres can then be taken up as individual cases. From these and numerous other tests completed to date or still in progress, it is believed that a more critical evaluation of electrical resistance alloys for their resistance to green-rot corrosion can be made. A much better understanding of the mechanism for this type of corrosion should also result. A more complete report on these experiments will be published later. In the May 1953 issue: TP 35213 Discussion: Solubility of Carbon and Oxygen in Molybdenum by W. E. Few and G. K. Manning, discussion by N. A. Gokcen: p. 747, first column, the fifth, sixth, and seventh lines should be the first, second, and third lines, followed by the present first, second, third, fourth, eighth, ninth, and tenth lines.

Jan 1, 1954

By J. H. Carpenter

LMENITE, rutile, zircon, and other heavy minerals are found in small amounts in the sand that covers most of Florida. Small enriched deposits occur on the beaches and coastal dunes. One beach deposit east of Jacksonville was worked during World War I and another near Vero Beach during World War 11. Both ceased operation when the resumption of imports reduced prices. Early in World War II reduction of rutile imports made a domestic source of the mineral necessary to maintain the expansion of armaments. Explorations made near Jacksonville discovered a relatively large body of low-grade ore about 10 miles inland from the beaches. A plant installed by Rutile Mining Co. of Florida using both flotation and tables encountered difficulties because of low plant capacity and organic slimes in the ore. In 1944 Humphreys Gold Corp. solved the problem of concentrating the low-grade ore by using the newly developed Humphreys spiral concentrator and by mining with a hydraulic dredge. This combination of low cost mining and concentration permitted the plant to continue operation in competition with foreign ores when imports were resumed following the war. The success of the Jacksonville operation renewed interest in Florida as a source of titanium. An extensive survey of the state was made by E. I. du Pont de Nemours and Co., Inc., under the direction of J. L. Gillson in 1945 to 1946. Sampling was carried on by drive pipe drilling to depths of 20 to 25 ft. Encouraging values were discovered near the location of the present Trail Ridge mine, 50 miles southwest of Jacksonville, near the town of Starke. The United States Bureau of Mines was interested in exploring for heavy minerals in Florida, and on the recommendation of both the state geologist of Florida and of Du Pont geologists, drilled deeper where marginal indications were found on Trail Ridge. In 1947 it was discovered that sufficiently higher values occurred at depth to make the deposit commercial. The orebody at Trail Ridge is a long sand deposit averaging about 1 mile in width and 35 ft in depth. It is approximately 1 1/2 miles wide at the north end of the portion now being worked, tapering to a blunt point 3 miles to the south. The ore reaches a maximum depth of 65 ft near the center and feathers out into barren sand at the edges. The ground surface is relatively flat and is covered with vegetation including pine, scrub oak, palmetto, and occasionally in swampy areas, cypress. The remain of a dense woody growth underlies and marks the bottom of the Ore 'One. It is difficult to drill through this layer, but in some cases where it is less than 5 ft thick it has been possible to drive through the wood. Sand lying below is coarser than that in the ore zone and contains no values. The wood layer consists of unconsolidated carbonized fragments of branches and other forest trash associated with a considerable amount of ar-

Jan 1, 1954

By J. Winlock

To have been chosen by you to give the Howe Memorial Lecture is the greatest honor I have ever had and I should like to have you know that I appreciate it deeply. Many years ago I had the privilege and the pleasure of working with Professor Howe in the private laboratory which he had established in his home at Bedford Hills, New York. Without doubt he was one of the world's greatest metallurgists and so you can imagine what a difficult task it has been for me to live up to his teachings. Every morning Professor Howe would outline the work he wanted done and the recollections of those conferences are clear to me to this day. Sometimes he would ask me to ride in his automobile and the chauffeur had full instructions to go no more than fifteen miles an hour. If he did so, Professor Howe was sure to rap upon the man's shoulder with his cane. I assure you, however, Professor Howe's thinking was not at that rate. His homely advice, his patience and his perfect control of the English language still impress me. Many times I heard him dictate a complicated paper on metallurgy and never find it necessary to change a single word. There are no better words to describe the character of Professor Howe, in my opinion, than those used by Professor Sauveur when he presented the John Fritz Medal to him in 1917: "Lover of justice and humanity Public servant and public benefactor, Master of the English Language, Loyal and devoted friend, Untiring and unselfish worker in an important field of science." I hope you will bear with me with the same patience and understanding which he used to give to me. The peculiar behavior of steel at the yield point has long been known and has been the subject of much research, both in this country and abroad.',' Many theories, including some of mine and my colleagues, have been suggested, but none of them, in our opinion, fully explains to our satisfaction why the phenomena occur. Of particular importance has been the work of Nadai,3 Siebel and Pomp,' Sachs and Fiek,5 Rawdon,0 Kenyon and Burns,' Gensamer," Gensamer and Meh1,0 Davenport and Bain,'" Fell," Deutler,12 Brinkman,13 MacGregor,14 Hollomon,15 Cot-trell,16 and Palm." The question of what is occurring during this singular behavior is not only of interest from an academic point of view, but is of great practical importance for at least two reasons: 1—The highly localized plastic flow which occurs during the deep drawing of light-gage steel gives rise to surface markings which seriously mar its appearance, Fig. 1. If the forces causing the deformation are primarily tensile forces, these surface markings occur as depressions in the surface. Whereas, if the forces causing the deformation are primarily compressive, irregular lines of elevations occur. These surface markings are known as Luder's lines, Hartmann lines, the Piobert affect, and, in the shop, as "stretcher strains." 2—The steel is in the most suitable condition for deep drawing after the yield point phenomena have been removed. When this is done, the steel may be deep drawn more easily and to a greater extent.' It should be mentioned that steel is not the only metal which shows this peculiar behavior at the yield point. Stretcher strains occur, also, during the deformation of some copper-nickel-zinc alloys." The purpose of this paper is not an attempt to describe what causes the steel to behave in this peculiar manner, but an attempt: l—to describe what is taking place at the yield point; and 2—to show the influence of the rate of deformation on the tensile properties of some plain carbon steels. As is well-known, there are two methods of deforming a metal in tension: 1—by actually hanging an increasing amount of dead weight on the metal; or 2—by deforming the metal at some given rate or rates by means of oil pressure cylinders, screws, etc. With the first method, the load is always present and, clearly, no drop in load can ever occur while the steel is deforming. With the second method, the registered load is the resistance of the steel to the deformation being imposed upon it. The second method is the one most widely used, and is the one referred to throughout this paper. In order to describe clearly what is occurring at the yield point in steel, it will help, I believe, if a description is first given of what occurs when alumi-

Jan 1, 1954

Jan 1, 1954

By Orville R. Lyons

THE Russellton preparation plant of Republic Steel Corp., located north of Pittsburgh, Pa., prepares 3 1/2x0-in. Thick-Freeport coal by means of a 13-ft 6-in. diam Chance cone and 16 No. 7 Deister tables. The plant feed ranges between 370 and 410 tons per hr, of which approximately 31 pct is ¼x0-in. size, and the plant reject ranges between 14 and 16 pct of the feed. The 3½xY4-in. washed coal, the cone product, is dewatered and desanded by a double-deck Parrish-type shaking screen 46 ft long and 7 ft wide. The 1¼x¼-in. portion is further dewatered by two 4x12-ft single-deck vibrating screens. The ¼x0-in. washed coal from the tables is distributed to three 54x70 in. Bird centrifuges. The dewatered centrifuge product is combined with the product of the de-watering screens prior to loading into railroad cars. During the early part of 1951 complaints were received from officials at Republic's coke ovens concerning the moisture content of Russellton washed coal. The records revealed that during the first half of 1951 the shipped washed coal moisture averaged

Jan 1, 1954

By Rudolph G. Wuerker

MUCH descriptive matter has appeared on the subject of suspension roof supports, or roof bolting, as it is more commonly called. The widespread introduction of roof bolting into coal mines and metal mines is truly phenomenal. Mine operators were quick to recognize the advantages of supporting wide openings without hindrance to machine maneuverability and ventilation. Although suspension roof support has long been installed at St. Joseph Lead Co. mines in southeast Missouri,'" its application to coal mining presented new problems, such as proper anchorage and bearing for the bolts, bolt diameter, and spacing of bolts. After continuous testing and experimenting at the mines, standard roof-bolting materials were determined.'!' The study reported in this paper is not concerned with such details as bolt diameter, which may be considered already solved in practice. In the tests discussed here, small models patterned on actual bolts were found to function in the same way and as satisfactorily as their prototypes. The aim of these tests was rather to investigate the influence of roof-bolting systems on the stress distribution around mine openings and to study the fracture patterns obtained in actual testing. Little was found about this in the literature, as testing of suspension roof methods and quantitative measurements are only now coming to the fore. Several suggestions and actual measurements have been made to evaluate critically the functioning of roof bolting systems, single roof bolts, and parts thereof. Outstanding among them is Bucky's outline of structural model tests.'" Since none of the suggested testing equipment was available, however, for the experiments discussed below, a different approach was chosen. The response of a mine roof under stress has often been compared to that of a beam. The slow coming down and bending through of beam or plate-like banks of shale, sandstone, or top coal is a familiar occurrence, extensively cited in the literature." It was felt that testing of roof-bolt systems installed in a concrete beam which was loaded in bending would be a fair approximation of the behavior of a mine roof underground. Another school of thought considers the roof behavior over an underground opening in connection with the stress distribution all around a circular or rectangular opening. This is more accurate, and leads to the concept of a dome-shaped zone of material destroyed under tensile stress. This is likewise a common sight in unsupported roadways where the continuous fall of roof results in what has been called the natural outline of roof fracture. This theory could not be tested and is treated separately in Appendix B. It is important to note that according to both assumptions the immediate roof fails in tension; the use of a beam in these tests, therefore, should give information valid for either of the two theories. With the testing equipment at hand it was possible to load concrete beams 6xlx0.5 ft under two-point loading, giving an equal bending moment over the center part in which the model bolts were installed. A comparison was made of the ultimate loads needed to break plain beams and beams in which roof bolts were installed. Arrangements were made with: 1—plain beams; 2—bolts with plate washers, some with holes drilled at 90" angles and others with holes drilled at 45" angles; 3—bolts with channel irons underneath; 4—bolts in holes filled afterward with cement; and 5—bolts anchored in a stronger stratum. The foregoing arrangement is made in order of increasing strength, as assumed from the theory of reinforced concrete. Likewise, laminated beams with wooden model bolts and with combinations of the foregoing set-ups were tested. All in all, 21 experiments were made out of the much greater number of combinations possible. There were, too, some trial tests. Enough observations from this limited number were made to interpret the behavior of mine roof, supported by various types of suspension bolts, at fracture. In present-day concepts, which have been proved by mathematical derivations and stress analyses, any opening driven underground will change the distribution and magnitude of the stresses existing around it. It does not matter whether the stresses become visible, as in rocks whose strength is less than the forces acting upon them, or whether they are invisible, as in the gangways lacking evidence of rock pressure. In this latter case the rocks can withstand changes in stress-distribution. To consider the mine roof as a beam, there are, with transversal loading, tensile stresses in the lower fiber and compressive stresses in the upper layers above the neutral axis of the beam. Beams of brittle material such as rock and concrete fail exactly as shown in Fig. 1. Nearly all model beams showed the same fracture pattern as that of a tension crack. The influence of support, by roof bolting or conventional

Jan 1, 1954

By J. Burbank

A TECHNIQUE has been developed for the microscopic study of the three-dimensional structure of the Pb-Sb alloys by the formation of a chemical replica in which the internal structure of the metal may be seen directly. In the replica process one of the phases present in the structure as-cast is converted into a translucent material, and the second phase remains virtually unaffected, permitting microscopic examination by transmitted light. Alloys of lead and antimony were made from the chemically pure metals, cast in a sooted and pre-

Jan 1, 1954

By W. D. Robertson, E. Scala

Electrical resistivity of a number of pure liquid metals and alloys has been measured as a function of temperature and composition. The data show a close correspondence between the liquid and solid states with respect to thermal, structural, and compositional relationships. STUDY of diffuse scattering of X-rays by liquid metals1 has demonstrated that some degree of order persists above the melting point and that the atomic constitution of liquids is more analogous to the solid state than to a gas. Consideration of the change in various thermodynamic properties that accompanies transformation from solid to liquid leads to the same general conclusion.² evertheless, specific knowledge of the constitution of the liquid state is limited when compared with that of the solid and gaseous states owing, in part, to the difficulty of interpreting the X-ray data and in part to the indirect character of deductions based on thermodynamic data. Of the structure-sensitive physical properties, electrical resistivity of liquid metals is perhaps the most easily interpretable, particularly when comparison is made with the solid state. According to the available data, most of which was obtained prior to 1914, cubic metals exhibit a normal linear and positive temperature dependence in the liquid state and the data have been accepted without question. The divalent metals, zinc and cadmium, are apparently exceptional in that resistivity is not linear with temperature and it passes through a minimum. Mercury also exhibits a nonlinear temperature dependence but the slope is always positive. Important comparisons with magnesium could not be made at the time the following work was undertaken because the necessary experimental data were not available. Data on liquid solutions are very limited and are largely from a single source."-" Based on Bornemann's work, Norbury7 pointed out that the resistivity of liquid copper alloys appeared to be dependent on the valence of the solute and that the increase due to the solute was of the same order as in the solid state. However, large extrapolations were involved and no quantitative relationship was developed. Therefore, before proceeding with additional deductions regarding the resistivity of liquid metals and interpretation in terms of structure, it appeared necessary to verify and extend the previous work with particular emphasis on divalent metals and the effect of alloying elements of different valence in dilute liquid solutions. The present work includes: 1—A determination of the resistivity of high purity liquid magnesium, tin, indium, copper, zinc, and cadmium as a function of temperature. 2—The effect of 1 atom pct of copper, cadmium, aluminum, tin, antimony, and

Jan 1, 1954

By J. P. Hammond, C. J. McHargue

The wire textures for cold rolled and recrystallized iodide titanium and the sheet textures for this material produced by cold and hot rolling, and recrystallization at a series of temperatures were determined. &apos;The effect of the a + ß transformation on the sheet texture was noted. UNTIL recently it was believed that all hexagonal close-packed metals deformed by slip on the basal plane, (0001), and that rolling should tend to rotate this slip plane into the plane of the rolled sheet. The pole figures of cold rolled magnesium&apos; are satisfactorily explained on this basis. There is a tendency for the <1120> directions to align parallel to the rolling direction, and the principal scatter is in the rolling direction. Zinc% as a rolling texture in which the hexagonal axis is inclined 20" to 25" toward the rolling direction. Twinning is believed to account for the moving of the basal plane away from parallelism with the rolling plane. The texture of beryllium3 places the basal plane parallel to the rolling plane with the [1010] direction parallel to the rolling direction, and the scatter from this orientation is primarily in the transverse direction. Cold rolled textures reported for zirconium&apos; and titanium5 how the [1010] directions to lie parallel to the rolling direction and the (0001) plane tilted by approximately 25" to 30" to the rolling plane in the transverse direction. Rosi has recently reported that the mechanisms for deformation in titanium are distinctly different from those commonly reported for hexagonal close-packed metals. The principal slip plane is the prismatic plane, {1010), with some slip also occurring on the pyramidal planes, (1011). However, there is no evidence for basal slip. The slip direction is reported to be the close-packed digonal axis, [1120]. In addition to the twin plane commonly reported for metals of this class, {1012), Rosi found the twin planes (1122) and {1121), with the dominant twin plane being (1121). Information regarding the recrystallization and hot rolling textures of hexagonal close-packed metals is limited. Barrett and Smigelskas report that rolling beryllium at temperatures up to 800°C and recrystallization at 700°C produce textures not differing from the cold rolled sheet texture.3 McGeary and Lustman find that hot rolling at 850°C produces the same basic texture in zirconium as rolling at room temperature.&apos; These investigators also report that the texture for sheet zirconium recrystallized at 650 °C differs from the cold rolled orientation inasmuch as the [1120] direction, instead of the [1010] direction, is parallel to the rolling direction. In the case of titanium, it is not possible to deduce which direction is preferred in the recrystallized state from the pole figures presented by Clark." The purpose of this paper is to report an extensive investigation of the preferred orientations in iodide titanium. Since the deformation mechanisms for titanium are different from those commonly given for hexagonal close-packed metals, it is not surprising to find distinct differences between the textures of titanium and other metals of this class. Materials and Methods This investigation was carried out on iodide titanium obtained from the New Jersey Zinc Co. with an analysis as follows: N2, 0.002 pct; Mn, 0.004; Fe, 0.0065; A1, 0.0065; Pb, 0.0025; Cu, 0.01; Sn, 0.002; and Ti, remainder. The crystallities of titanium were broken from the as-deposited bar and melted to form 20 g buttons on a water-cooled copper block in a vacuum arc-furnace. Hardness tests conducted on the material before and after melting differed by only two or three Vickers Pyramid Numbers, indicating no or insignificant contamination. The buttons were hot forged, ground, and etched to sizes and shapes suitable for the rolling schedule, and vacuum annealed at 1300°F. Specimens for determination of the wire textures were reduced 91 pct in diameter to 0.027 in. in 24 steps using grooved rolls. In order for the orientation of the central region to be studied, portions of these wires were electrolytically reduced to a diameter of 0.005 in. using the procedure described by Sutcliffe and Reynolds.&apos; The sheet textures were determined on titanium cold rolled 97 pct to a thickness of 0.005 in. A reduction of approximately 10 pct per pass was used, and the rolling direction was changed 180" after each pass. Specimens used for determination of the recrystallized textures were annealed in evacuated quartz tubes at 1000°, 1300°, and 1500°F. The grain size of the 1000°F specimen was sufficiently small to give satisfactory X-ray patterns with the specimen stationary. However, it was necessary to scan the surface of the other recrystallized specimens. The microstructure of each annealed specimen was that of a recrystallized material. The diffraction rings all showed the break-up into spots typical of recrystallized structures.

Jan 1, 1954

By O. D. Sherby, J. E. Dorn

For elevated temperature-constant load creep tests of a solid solution alloys, the creep strain is a function of a temperature-compensated time parameter 0 = je H/RT dt. The activation energy H is equal to o constant of about 36,000 cal per mol. The substructures resulting from a given creep stress condition are functions of the creep strain independent of temperature. Each new creep stress gives a new unique set of grain substructures; this is one of the factors responsible for the failure of the mechanical equation of state for creep. IN this report an attempt is made to correlate the creep properties of dilute a: solid solutions in aluminum with the subgrain structures that are developed during creep. The possibilities of such correlations have already been suggested by Wood et al. and others1-" who demonstrated that the subgrain structures are functions of the creep stress, creep strain, rate of creep, and temperature. Investigations by Sherby and Dorn&apos; have shown that the creep strain, E, at constant load for dilute a solid solutions of aluminum is given by the functional relationship: e = f(8,u,) [1] where: 0 equals te-AH/RT = temperature-compensated time; t, time; AH, activation energy, - 35,800 cal per mol; R, gas constant; T, absolute temperature, above 400°K; and u,, initial creep stress. Consequently, it was anticipated that the subgrain structure that develops during a constant load creep test should also correlate with any two of the three significant variables C, 8, and Another possible correlation between the subgrain structure and the creep variables is obtained by differentiating Eq. 1 with respect to time, whence the creep rate, 2, becomes: = (2L) (2) =f (, u,) e-AHRT [2] or: e = F (c e H/RT, 0) [3] For the minimum creep rate, ;,, 8 is solely a function of U, as revealed by Eq. 1. Consequently, at the minimum creep rate Eq. 3 reduces to: = F (eAH/RT) [41 Correlations between U, and i, eAH/RT were found valid for solid solution alloys of aluminum where AH was a constant of about 35,800 cal per mol. The parameter ;, eH/RT is identical to the Zener-Hollo-mon parameter8," used by them in evaluating the tensile properties of copper and other metals. Eq. 4 suggests that the subgrain structure developed during secondary creep might be correlatable with either of the two variables 2, e H/RT or u,. Some of the solid solution aluminum alloys which were discussed in an earlier report&apos; were also used in the present investigation. Sheets of these alloys were homogenized, cold rolled from 0.100 to 0.070 in. in thickness and then recrystallized to about the same grain size. Their chemical composition and grain size are recorded in Table I. Creep specimens were selected with their tensile axes in the rolling direction. The details for creep testing have been described10 and will not be repeated here. All creep tests were performed under constant load conditions. Experimental Results and Discussion Metallographic Structure of Creep Specimens: In order to obtain a preliminary concept of creep on the metallographic structure of high purity aluminum, the various ruptured specimens previously used to obtain the creep data for pure aluminum were polished and etched electrolytically in a dilute solution of fluoroboric acid. Oblique illumination was used to reveal the substructures which, for convenience, are shown in correlation with the vs. ;, eH/RT curve in Fig. 1. It is necessary to emphasize that the data for the curve refer to the various secondary stages of creep whereas the micrographs refer to the fractured creep specimens. Nevertheless a regular and systematic correlation is observed between E, eAH/RT (or the creep stress) and the micro-structure at fracture. For In (e, eAH/RT) = 42.3, which refers to creep at a high creep rate and a low creep temperature, the fractured aluminum specimen, as shown by the micrograph in the upper right-hand corner of Fig. 1, exhibited extensive deforma-

Jan 1, 1954

By M. Cohen, C. Wagner, J. E. Reynolds

If the total volume of a diffusion couple changes during the diffusion, the measurement of distance becomes ambiguous. Use of distance parameters as suggested by Hartley and Crank is discussed. For small concentration differences, the standard form of Fick&apos;s second law is retained with conventional length units and the in- terdiffusion coefficient D. It is shown how D can be calculated from experiments involving large concentration differences and analyzed in terms of distance parameters. &apos;The merits of incremental diffusion couples involving small concentration differences are emphasized. THE conventional form of Fick&apos;s second law for one-dimensional diffusion of component B in a binary solution of A and B is where c, is the concentration of component B; x, the distance; t, the time; and D, the interdiffusion coefficient which may depend on ca. Hartley and Crank&apos; have pointed out that Eq. 1 applies only if the total volume of the diffusion couple does not change during the diffusion process; otherwise, the definition of x becomes ambiguous. No change in total volume takes place if the specific volume of the solution is a linear function of the weight fraction Wb, or if the molar volume is a linear function of the mol fraction N. In some alloys, however, these relationships do not hold, and then it is necessary to introduce a modified measure of distance, 4 in order to retain the general form of Eq. 1. The application of Hartley and Crank&apos;s suggestions to diffusion in alloys has been discussed by Wagner.&apos; Relation Between Measure of Distance and Units of Concentration The definition of [ depends on the choice of units for the concentration c,, as follows: 1—If the concentration ca is measured as the weight fraction W, (or weight percent), [ = 5, has to be defined so that equal increments of contain equal increments of mass m of the solution, e.g., dm = pSdx = Sdw [2] where p is the local density of the solution, and S is the cross-sectional area in sq cm which is taken to be constant in this problem of one-dimensional diffusion." * da Silva and Mehla have demonstrated the constancy of the cross-sectional area in the usual type of diffusion couple. However, experiments involving diffusion into thin wires4, 5 may exhibit changes in cross-sectional area, and therefore are excluded from the present treatment. Thus and the unit of is gram per sq cm instead of cm. 2—If the concentration c, is the mol fraction N, must be defined so that equal increments of contain equal numbers of mols of solution, e.g., dn= (S/V)dx= Sd [41 where V is the local molar volume of the solution. Thus dt, = dx/V [51 and the unit of is mols per sq cm. 3—If, as may be advisable in the case of interstitial solutions, the concentration C is measured in terms of the molar ratio of components B and A (c,, = Y, = nH/nA, where n and nl are numbers of mols of B and A), = Y has to be defined so that equal increments of contain equal numbers of mols of A, e.g., dnA= (NAS/V)dx = Sdf [6]

Jan 1, 1954

By M. R. Geer Olds, H. F. Yancey

THE increase in the number of coal-cleaning plants employing dense-medium processes occurring since 1946 is especially interesting when viewed historically. Both sand and magnetite were introduced as material for heavy mediums at about the same time, sand in the Chance process in 1921 and magnetite in the Conklin process in 1922, but from that point on their records diverge. The Chance process enjoyed a steady growth from its inception, whereas no additional magnetite plants were built in the United States for over 20 years. Then, following the close of the World War 11, magnetite was again introduced, this time with marked success. During the following years some 47 plants employing magnetite medium were built. This rapid growth of dense-medium cleaning has been concurrent with widespread adoption of full-seam mining on one hand and a return to a more competitive market on the other. At a time when changing mining practice has provided cleaning plants with dirtier coal and changing market conditions have simultaneously demanded a cleaner product, the industry has through necessity turned to improved preparation. The inherently greater sharpness with which dense-medium processes can separate coal from impurity is thus helping to hold the line against ever-increasing mining costs and at the same time assisting materially in retaining badly needed markets. Although dense-medium cleaning unquestionably offers a distinct advantage when the washing problem is difficult, other methods can provide almost equally high efficiency when the coal is easy to wash. Moreover, fine coal cannot yet be treated by heavy medium in a proved process, although the Driessen cyclone is in the pilot-plant stage. Most of the present types of dense-medium equipment have been in use only a few years, and the dearth of information in the literature concerning their performance characteristics is entirely understandable, Nevertheless this information is necessary if the process is to be intelligently applied to individual cleaning problems. Without data on the efficiency of a process in a particular type of separation, it is difficult to assess the advantage to be expected from it. Similarly, the role of particle size in heavy-medium separation is important in some cases, yet there is little published information on this aspect. To mention only one more of the numerous points on which essential information is lacking, the bearing of medium characteristics on performance has been discussed only in qualitative terms. It was with the hope of providing information on some of these points that the Bureau of Mines built a dense-medium pilot plant for cleaning coal at its Northwest Experiment Station in Seattle in 1950. The plant has been operated continuously since that time, and over 50 runs have been made on 7 coals exhibiting a wide range of washability characteristics. An idea of the magnitude of this work will be gained from the fact that examination of the plant products has involved some 600 float-and-sink separations and about 2500 ash determinations. A laboratory pilot plant is especially well adapted to investigate many aspects of performance because close control over test conditions can be exercised and because a large number of tests can be made rapidly. On the other hand, factors such as consumption of medium and other cost items can be investigated satisfactorily only in a commercial plant. Actually, the two forms of investigation should be complementary, with the laboratory work pointing the way for confirming tests in commercial units. Pilot Plant The dense-medium pilot plant employed for this work comprises a 24x30-in. drum-type separating vessel, a 12-in. densifier, a 12-in. magnetic separator, a 26-in. x 9-ft vibrating screen, and the necessary pumps and conveyors for handling materials. Arrangement of these units corresponds with the flowsheet used in most commercial plants, except that a thickener is not provided for the feed to the magnetic separator. Coal and refuse discharge from the separating drum to the vibrator, which is divided longitudinally down the center. Medium draining through the first 3 ft of the screen is recirculated directly to the drum. Sprays on the middle 3 ft of the screen rinse medium from the products, and the last 3-ft section is for dewatering. Dilute medium from the rinsing and dewatering sections is pumped to the magnetic separator, where magnetic solids are recovered. These are pumped to the densifier, from which they return to the medium-drainage sump by gravity through a demagnetizing coil. The drum-type separating vessel is a scale model of a commercial unit. Feed enters axially at one end of the drum just below the surface of the bath, and float material overflows through a circular opening at the other end. Particles sinking to the bottom of the bath are picked up by lifting flights bolted to the inner wall of the drum, elevated out of the bath, and sluiced to the vibrating screen. Baffles suspended in the bath prevent float material from entering the sink-lifting flights. About 8 gpm of medium is used to sluice the feed into the drum. An additional 15 to 24 gpm, depending upon operating conditions, is added through two pipes dipping into the bath behind the baffle on the side where the sink-lifting flights enter the bath. The bath available for separation is 2 ft long and 13 in. wide, giving an area of 2.08 sq ft. Depth of bath from the surface to the top of the sink-lifting flights, measured vertically below the axis, is 6 in.

Jan 1, 1954