By Eckhard Nembach

The phase diagram of the system Pb-In has been investigated between -27° and + 40°C, using nzainly X-ray dijfraction. In accordance with t her mo dynamic measurements by Heumann and Predel, a segregation occurs at low temperatures, though not in the form of a nziscibility gap. THE phase diagram of the system Pb-In has been the subject of extensive investigations,1&apos;1 but recently Heumann and prede13 concluded from their thermodynamic data that a new feature should occur below room temperature. These authors observed that the maximum values for the enthalpy and entropy of mixing, which occurred at a composition of 50 at. pct Pb, were +400 and —1.7 cal per g-atom deg, respectively. From this the authors estimated that a miscibility gap should occur below 30°C, centered at 50 at. pct Pb. Resistivity measurements seemed to support this view. These authors proposed the phase diagram outlined in Fig. 1. Three phases exist at 30°C: the tetragonal indium phase with c/a > 1, the tetragonal intermediate phase a, with c/a < 1, and the fcc lead phase. During an investigation of the superconducting properties of Pb-In alloys. it has been observed4 that aging a specimen with 50 at. pct Pb for 14 days at -18°C decreased the superconducting transition temperature about 0.13"K and tripled the transition width. In this paper, the results of an investigation of the Pb-In phase diagram in the temperature range from — 2T to +40°C are reported. Superconductivity and X-ray methods have been used. 1) SPECIMEN PREPARATION The materials were provided by the American Smelting and Refining Co. According to the manufacturer their purity was 99.999 pct. The weighed amounts of the constituents were sealed in quartz tubes under an atmosphere of 10 torr helium, mixed for 24 hr in a rocking furnace at 380°C, quenched in ice water, and homogenized at 20" to 30°C below the solidus line, established by Heumann and Predel. The annealing times were 144 hr for specimens containing Less than 30 at. pct Pb and 36 hr for the remainder. 2) SUPERCONDUCTIVITY EXPERIMENTS The specimens were quenched from the homogeniza-tion treatment into ice water and their superconducting transition temperatures T, measured. The procedure used has been described in Ref. 4. The transition was detected by the change of the mutual induc- tance of two coaxial coils containing the sample. T, was defined as the temperature at which 50 pct of the total change in inductance had occurred. The repro-ducibility with which T, could be measured was i0.002"K. Then the specimens with lead contents between 38 and 75 at. pct were aged for 7 days at temperatures between -30" and 40°C. If this treatment caused T, to change by more than 0.005"K or the width of the transition to increase by more than 0.002"K, it was concluded that the specimen had undergone a phase change and no longer consisted only of the fcc lead phase: as it did immediately after homogenizing. The result is shown in Fig. 2. From this one can estimate at what temperatures and concentrations phase changes occur. The X-ray measurements were based on these preliminary results. 3) X-RAY EXPERIMENTS Because of the softness of the material, relatively coarse powders. 75 p, had to be used, which were filed in a helium atmosphere from homogenized specimens. The powders were annealed at least 30 min at temperatures between 120" and 16OJC, depending on their concentration, and quenched in ice water. Then their X-ray patterns were taken at -178°C with a Picker diffractometer, model 3488K, and a cold stage. on which the specimen was in thermal contact with a liquid-nitrogen reservoir. In this way the following relation was established for the fcc lead phase: a = 4.697 + 0.00247C for 40 5 C 5 75 11 where n is the lattice constant (A) and C is the at. pct of lead. The coarseness of the powder made it impossible to use lines with 0 > 75 deg; therefore n was averaged from lines with 45 deg 5 0 5 75 deg. The results were reproducible to within i0.05 pct. Relation [I] is very similar to the one found by Heumann and Predel at room temperature. Following this, homogenized specimens with compositions between 15 and 56 at. pct Pb were aged for at least 10 days at temperatures between -27" and

Jan 1, 1970

By S. K. Sarkar, B. Dr. Singh

INTRODUCTION India like USA has traditionally relied on bord and pillars as dominant underground method. Coal has generally been mined at shallow depth from relatively thick and horizontally bedded coal seams. These&apos; factors contributed towards large scale adoption of bard and pillar. After nationalisation of coal industry in two stages in 1971 and 1973, large scale mechanisation and modernisation programmes were undertaken. Longwall mining was identified as one of the major that area for increasing underground coal production. The idea to introduce longwall mining was mooted to increase productivity and to promote conservation and safety. The nationalised coal industry has already worked about twenty longwall faces with different types of support. The tempo of introducing longwall is catching up and a number of longwall programmes with, Self advancing supports of different types and Capacity are in active stage of implementation. The country has not yet started producing mechanised Supports and therefore supports and machineries are being imported from U.K. and other countries of the continent. The of the major problem faced in the longwall projects is to choose suitable type and capacity of supports. The suppliers and manufacturers of these supports are not competent enough to choose and offer the right type and capacity of supports as their knowledge and information about Indian strata conditions are extremely limited. The Central Wining Research Station (Q.!RS), has undertaken a research programme for evaluating the rock mechanical conditions obtaining in the proposed longwall locales and has worked out a method for selection of proper type and capacity of supports on the basis of projected strata behaviour at the proposed locale. STRATA CCNTROL FAILURES Indian coal industry had made some attempts to introduce longwall caving in the early fifties after a working group set up by the Government of India had recommended its adoption to increase productivity and to modernise mines. Approximately 20 longwall faces were tried in the major Indian coalfields of Jharia, Ranigunj and Karanpurr between 1951 and 1968. The supports used consisted of 20T hydraulic props or 35140~ friction props. A number of these faces had suffered total strata control failures and a large number of support elements were lost. The Central Mining Research Station initiated a research programme to analyse these failures in the general background of behaviour of Indian coal measure strata at longwall faces. All the available data regarding the cases of failures were collected and physico-mechanical properties of overlying roof rocks were determined in the laboratory. Simultaneously, observations were continued to establish the behviour pattern of Indian coal measure strata at longwall faces. These studies were helpful in analysing the occurrences of collapse. BEHAVIOUR OF INDIAN COAL MEASURE STRATA The coal measure strata encountered in the principal Indian coalfields of Jharia, Ranigunj and Karanpura are in general strong in nature however, the immediate roof (mostly up to 1.5 to 2 m) in most of the cases is weak and false bedded shale. MI idea about the strength properties of immediate and overlying roofs may be obtained from the following table.

Jan 1, 1982

By P. Somasundaran

An experimental and theoretical treatment of the depressing effect of inorganic electrolytes on the amine flotation of quartz is presented. Experimental data obtained for the amine flotation of quartz as a function of pH with potassium nitrate as depressant was used to test the models for the effectiveness of inorganic ions as depressants. The validity of commonly used assumptions are examined. The surface tension data obtained for dodecylammonium acetate solutions as a function of KNO3, concentration indicated that the collector adsorption on bubble cannot be neglected in the treatments, since this adsorption changes significantly with the addition of the inorganic electrolyte. It also indicated the possibility of significant changes in the specific adsorption potential of the collector occurring with the addition of inorganic electrolytes.

Jan 1, 1975

By W. Rostoker, R. F. Domagala, R. P. Elliott

The phase equilibria of the Hg-Th system over the composition range 0-100 pct Th and temperatures up to 1000°C have been studied for a small-volume, closed system. The solubility of Th in liquid Hg is about 5 pct at 300°C and decreases sharply with decreasing temperature. Two intermediate phases occur, Hg3 Th and HgTh. The structures of these are hexagonal (nonideally close-packed) and face-centered cubic, respectively. The HgTh phase decomposes eutectoidally at 400°-500°C. The solubility of Hg in solid thorium seems to be negligible. AFULL-phase diagram for this system would have to be defined on temperature-composition-pressure co-ordinates. This paper describes the pseudo phase diagram of a closed system, that is, where the alloy enclosed in a small volume equilibrates with a vapor pressure of mercury dictated by composition and temperature. Because of the experimental difficulties in studying a system of this nature, many of the phase relations can only be sketched. Alloy Preparation Alloys over the full range of composition were made from triple distilled mercury and one of two grades of thorium. For the bulk of the work, a calcium-reduced metal in sintered pellet form of reported 99+ pct total thorium content was used. Arc-melted specimens of this thorium gave a hardness of 135 VPN. The microstructure showed small primary dendrites of ThO2. A number of alloy compositions were made with a high-purity, iodide-decomposition thorium metal. The are-melted hardness of a button of this material was 35 VPN. Although the microstructure of the arc-melted specimens showed no dendrites of ThO2, there was definite evidence of an unidentified phase enveloping the grain bound-aries. There were no distinguishable differences between the constitution of alloys made with the two grades of thorium metal. Under normal conditions thorium is not wetted by liquid mercury. The film of ThO2 on all thorium metal cannot be penetrated by either liquid or vaporous mercury. It was therefore necessary to comminute thorium in the presence of mercury under such conditions that oxide films could not reform on the newly exposed metal surfaces. This was accomplished by the use of a high-speed, carbide-tipped rotary cutter incorporated in a chamber purged with argon and connected at the bottom to a demountable Vycor bulb containing a weighed amount of mercury. This experimental device is fully described in a separate paper.1 Alloy compositions were calculated by weighing the empty bulb, the bulb containing the mercury, and the bulb containing the mercury and the thorium chips. Many alloys were analyzed chemically for thorium and/or mercury after subsequent homogenization; the agreement between analyzed and calculated compositions was invariably very close. Bulbs containing the requisite amounts of mercury and fine thorium chips were clamped off, removed to a sealing unit, evacuated and sealed. Amalgamation under these conditions proceeded rapidly even at room temperature. To insure homogeneity, the specimens were annealed to 300-400°C. Alloys containing less than 30 pct Th remained pasty after all treatments, indicating an equilibrium condition of liquid plus solid. Alloys with more than 30 pct Th were transformed into a dark powdery product. These latter specimens were annealed for times of up to 1 week to complete interdiffusion. Many of the alloy compositions are pyrophoric. On exposure to air they oxidize with considerable evolution of heat to a mixture of ThO2 and free mercury. It was mandatory that alloy specimens be handled in a "dry box" purged thoroughly with argon. All X-ray diffraction specimens were powdered, screened, and sealed in capillary tubes within the dry box. Experimental Procedures Thermal analysis experiments, useful only in the mercury-rich region of the system, were conducted with the alloys in their original containers. A reentrant thermocouple well formed an integral part of the bulb. These bulbs were heated in a silicone oil bath and cooled in a dry ice-acetone mixture. The rates of heating and cooling were slowed by immersing the specimen bulb in a larger tube containing silicone oil. This provided a suitable thermal lag. In all tests, pure mercury was run as a basic standard. While the invariant reaction at about the melting point of mercury was detected by thermal analysis, the heat effect at the liquidus was not sufficient to produce an inflection in the cooling curve. It was necessary to determine the liquidus temperatures at the mercury-rich end of the system by "breaks" in electrical reslstivity versus temperature curves for individual alloys. The apparatus for this purpose consisted of a pyrex tube about 2 in. diam and 12 in

Jan 1, 1959

By V. F. Marsters

THE main producing oilfields in Peru are located in the department of Piura and province of Thumbes, adjoining Ecuador on the south and west. In the department of Puno, a small field known as the Pirin or Hauncané Area was exploited some years ago by Fred Brown and associates and considerable production obtained. As. shown by the statistical table of production, this area reached its maximum production about 1909; since 1915, operations have been suspended. During the past year, however, the Peruvian Corpn. has acquired some interests in this section. It is reported to have made a few shallow tests with the hope of obtaining sufficient production to supply fuel for its railway lines, which operate between Mollendo on the coast and Puno and Cuzco in the interior. Only partial success has accompanied these efforts; nevertheless, exploitation is being continued. The petroleum of this region contains a paraffin base with small amounts of asphalt. While the gasoline content is small, the kerosene content runs as high as 30 per cent., with the fuel element varying from 50 to 72 per cent. While it is known that the structural conditions of the Huancané area are somewhat complicated, it is believed that exploitation based on a careful interpretation of the geology of the region will eventually yield commercial production of at least modest proportions. In the main fields in Piura and Tumbes, drilling operations were somewhat more active during the first half of the year, than in 1922. The latter half of the year witnessed curtailment, owing to the abnormal situation in the petroleum industry at that time. For the same reason, no attempt was made to obtain the maximum production from existing .wells. Production was pinched down and exportation of crude was correspondingly reduced during the latter half of 1923. Nevertheless, the total production of the Peruvian fields is considerably in excess of that for 1922, as is also the production of the Negritos area alone.

Jan 3, 1924

By Henry Seltz, Hugh J. MacDonald, Cyril Wells

Several investigators have measured the heat capacity of cementite, using different methods of attack, but the agreement between the values obtained cannot be considered good. Naeserl has made measurements of "average heat capacities" of iron carbide between 1026" and 85" K., using a water calorimeter. His computed true specific heat at 78.1" K. is 11.22 cal. per gram-formula mass, which, if correct, is much too high for any reasonably accurate extrapolation to 0" K. The cementitc used by Naeser was obtained from a steel containing 0.9 per cent carbon, by electrolytically dissolving out the iron in a neutral bath of ferrous chloride. The cementite remained as a coarse, crystalline, gray powder. Andes2 has measured the specific heat of iron carbide, from 102" to 323" K., as it exists in steel. The specific heats of several slugs of steel of known iron carbide content were determined, and the specific heat of the iron carbide (Fe3C) calculated by plotting specific heat versus percentage of carbon, and extrapolating to pure Fe3C (6.7 per cent C). The heat-capacity values for temperatures below 100" K. were obtained by comparing the temperature-specific heat curve for Fe3C to that of Fe. Since the two were very similar in the range examined experimentally and approach more closely at low temperatures, it was assumed that near the absolute zero the form of the curve for Fe3C would be similar to that of Fe. Andes calculates for the entropy of Fe3 C,S298 = 23.55 e.u. The heat of formation of Fe3C has been studied by several workers. Kelley3 has reviewed these measurements and calculations, and selects those of Roth* and Naeser6 as worthy of most consideration. Roth has given AH = 5400 cal. + 30 per cent as a result of his own and other work. Naeser has determined the heat of formation from Fe and different forms of carbon, and for graphite (0) he finds AH = 5600 cal. Kelley accepts the rounded figure AH = 5500 as the heat of formation at 298.1" K., but this value is quite uncertain.

Jan 1, 1940

By R. Q. Shotts

Nitric acid oxidation rate analyses of three coals, previously studied microscopically by the Bureau of Mines, revealed three components. Relative quantities agree with those found for the four components given by the Bureau and results are consistent with current ideas of coal constitution. Possible multi-component composition for bright coal and a reactivity-rank relation are suggested. THE physically dissimilar components of bituminous coals often are easily recognized mega-scopically. Under the microscope, reflected light or light transmitted through thin sections reveals the presence of the different components, even when these are intimately mixed. Optical methods for the quantitative estimation of the relative abundance of the various components, both by means of thin sections and by particle count, have been fully described.&apos;. &apos; It has long been recognized that there are chemical and physical differences between the various petro-graphic components of bituminous coals, although analytical differences usually are small.:&apos;. &apos; Only in the case of fusain have chemical differences been used for quantitative determination of a component. C. C. Hsiao and associates, at the Mineral Industries Experiment Station of the Pennsylvania State College, have described a method of analysis which is based upon the differences in the rate of nitric acid (8N) oxidation, fusain, and the other components of coal."," The reproducibility of their method and its applicability in checking microscopic determinations of fusain content have been supported by several independent investigations.&apos;. " The writer has proposed the use of differences in oxidizability for the estimation of other components." "&apos; The results of the oxidation of whole coals and of float-and-sink fractions of coals were reported. In most cases the plots of the logarithms of the percent dry, non-fusain, organic residue from oxidation, against time, revealed the presence of at least two distinct components. Both components appeared to oxidize according to a first order law, but the reaction constants for the components were distinctly different. One or more of the dull density fractions were found to contain but one component, and some of the lower rank coals oxidized in such a way as to suggest the presence of three components. A suitable way to check the identity and significance of the components delineated by oxidation would be to analyze a sample of coal both by the nitric acid oxidation procedure and by a microscopic method. The writer was wholly unfamiliar with either of the microscopic techniques commonly used, and to make such a comparison it was necessary to rely upon microscopic analyses made by someone else. It is hoped that some laboratory which is equipped to make both types of analyses will some day make them upon identical samples. During the past 20 years, four Alabama coals have been analyzed petrographically and the results published by the United States Bureau of Mines. They are: 1—Flat Top mine, Mary Lee bed; 2—Empire mine, Black Creek bed; 3—Wylam No. 8 mine, Pratt bed, all in the Warrior field; and 4—Soot Creek mine, Fairview bed, in the Coosa field."-" Of these, only the Flat Top mine is still operating. Because of the closing of these mines, it first appeared necessary to rely upon the indirect and unsatisfactory procedure of sampling the beds in other mines located as near to the closed mines as possible. Upon investigation, however, it was found that the Bureau of Mines still had, in storage, the very same samples which had been used in the published petrographic studies. The Bureau very generously furnished about 2000 g each of the Pratt, Mary Lee, and Fairview bed coals, largely lumps but with some fines. The blocks of coal, when received, still were covered by the paraffin coating which had been placed on the polished surface, in the case of the Mary Lee coal almost twenty years ago. Procedure The procedure for oxidizing the coal sample and removing the alkali-soluble humic acid has been described. In the present study, oxidation periods of 1/6, 1/3, 1/2, 3/4, 1, 2, 3, and 4 hr were used. All oxidations were made in triplicate. After the paraffin had been removed in boiling water and the coal washed carefully with cold benzene, the entire sample of approximately 2000 g, obtained from the Bureau of Mines, was crushed to pass a No. 4 sieve. About 200 g of this material was pulverized to pass

Jan 1, 1954

By J. R. Finlay

Every business man who has reached the age of forty, or perhaps even thirty, must know from his own experience that there are occasional periods of "good times&apos;&apos; and others of "bad times "-booms and panics. Those who give to business some complexion of science have invented a semiscientific name for these alternations-the business cycle-indicating that it is a normal phenomenon which by its own nature repeats itself. The longer one lives and the more one enlarges his own experience by the study of history, the more of these cycles he knows and the more disposed he becomes to take their recurrence for granted. If these alternations can be put into the category of common- places, why not treat them as such? We are in a sharp depression right now, why worry about it? Is there not a certain average value for business that can be depended upon in spite of depressions? By way of rejoinder one might answer that war is the great commonplace of history, but when we get into one we generally find it worthy of attention. In the present case, many a man has lost two-thirds of his income, and he is extremely nervous about finding it again. The Southern Pacific Railroad earnings have dropped 75 per cent in the past year; Pennsylvania, 60 per cent; United States Steel Corp., about the same. The drop in current earnings is

Jan 1, 1932

By K. H. Coats

In tnany oil and gas fields, significant investments are required in piping networks for collection, injection and disposal of various fluids. This paper treats the problem of optimally locating the trunkline(s) for a given systet to nlinimize both the total length of piping connecting the individual wells or lease batteries to the trunkline and the length of the latter. Single and multiple trunklines, varying line sizes, and grouping of wells are considered. Some attention is paid to the case of a curved trunkline. A field case is treated and conclusions are that the problem of locating a single trunkline is relatively straightforward while the location of multiple trunklines requires further research. INTRODUCTION la many oil and gas fields, significant investments are required in piping networks for collection, injection and disposal of various fluids. A single field may concurrently require piping systems for gathering of oil, gathering of gas, injection of water or gas and disposal of salt water. Two problems arise in the consideration of any one of these networks. The first involves the sizing of the various segments of the network to minimize piping and compression costs. The second problem, treated herein, is that of optimally locating the trunkline(s) for a given piping system to minimize the total length of pipe connecting the individual wells or lease batteries to the trunkline. This minimization problem may arise in field automation if it involves replacement of individual lease batteries by a central field battery which will require trunklines and connecting pipelines to individual wells. The problem also arises in connecting a gas pipeline through a subsidiary trunkline to wells in a gas storage field. The first analysis given below treats the case of a single trunkline and of separate connecting lines for all field units.* The analysis is then extended to consider multiple trunklines and common connecting lines for groups of field units. Varying sizes, and therefore costs, of the connecting lines are taken into account. A simplified development is given to illustrate the manner in which line sizing calculations may be integrated with the line placement problem. This study is primarily directed toward the placement of straight trunklines, although for certain field shapes or well distributions curved trunk-lines might be preferable. Some mathematical consideration is therefore given to the placement of a curved trunk-line in a field. The determination of optimal locations for two or more trunklines involves some difficulties which are discussed below. The need for further research in this area is emphasized. The problem of a single trunkline is solved in relation to an actual oil field. The problem of optimally locating two trunklines in the same field is also treated and the results are compared to the single-trunkline case. All calculations reported were performed on an IBM 7072 digital compker. The importance of right-of-way, roads and terrain in locating trunklines and connecting lines is realized. The present analysis is advanced on the premise that in planning piping networks one should start with the optimal conditions whenever possible and proceed therefrom.

By K. S. Choi, B. S. Shin

The adsorption characteristics of sodium silicate on scheelite, calcite, and fluorite minerals were investigated. Adsorption equilibrium took about 60 minutes. Adsorption data show that the masimum amounts of adsorption of sodium silicate occurs at about pH 9.8. The adsorptivity was in the order of calcite > fluorite > scheelite. The amount of adsorption of sodium silicate increased with the increase in temperature of sodium silicate solutions. The amount of adsorption of sodium silicate decreases in the low concentration range of ferrous sulfate, while in the high concentration range of ferrous sulfate, the adsorption of sodium silicate increases.

Jan 1, 1986

By Richard L. Ash

7.3-1. Introduction. All phases of mining competent materials are affected directly by the results achieved from primary blasts. It is imperative that their design suit each particular set of mining conditions. In general, the round design must provide an adequate tonnage of material, properly placed with suitable fragmentation, to ensure that loading, haulage, and subsequent disposal or processing are accomplished at the lowest possible cost. Blasting rounds are designed by the proper application of cratering relationships developed for the single, concentric, confined explosive charge. Blasting for surface mining and most open-cut heavy construction, however, is characterized by the use of rounds, composed of a number of explosive charges with relatively long lengths, which are placed in benches with specific finite dimensions. Therefore, modifications must be made to the classical, single point-charge cratering concepts. It is the purpose of this discussion to outline the basic principles, significant variables, and procedures for their integration in the design of rounds that are applicable to conditions characteristic of surface mining. Because relatively insensitive blasting agents will be used in most instances, particular attention must be given to priming, control of confinement, and selection of charge diameters that ensure complete explosive-reaction execution. 7.3-2. General Considerations. The primary requisites for any blasting round are that it ensure optimum results for existing operating conditions, possess adequate flexibility, and be relatively simple to employ. It is important that the relative arrangement of blastholes within a round be properly balanced to take advantage of the energy released by the explosives and the specific properties of the materials being blasted. There are also environ- mental and operational factors peculiar to each mine that will limit the choice of blasting patterns.

Jan 1, 1968

COMMITTEES. Precious and Base Metals. Charles W. Goodale, Chairman.. L. D. Ricketts, Vice-Chairman Darsie C. Bard, Secretary, Montana State School of Mines, Butte, Mont. Leonard S. Austin, Thomas J. Grier, Willet G. Miller, David W. Brunton, Hennen Jennings, Albert F. Schneider, Theodore B. Comstock, Edmund B. Kirby, George C. Stone, Stanley A. Easton, Charles W. Merrill, Benjamin B. Thayer. Samuel S. Fowler,

Jan 11, 1913

By E. V. Potter

For a nurnber of years, it has been known that manganese made by electro-deposition under certain conditions is ductile while under other conditions it is very brittle. The ductile metal is gamma manganese normally stable only between 1100 and 1138°C1; the brittle metal is alpha manganese, stable up to 727OC. The ductile metal is not stable, but gradually changes to the brittle form; the time required to complete the transfornlation is about 20 days at room temperature. Other observations have indicated that the transformation is completed in 10 to 15 min. at about 125°C, while at — 10°C, no appreciable change occurs in 9 months. The properties of gainma and alpha Illanganese in the pure state are ordinarilj difficult to determine because the gamma structure cannot be retained by normal quenching procedures and alpha manganese is so brittle, it is difficult to obtain specimens free from flaws. In a recent investigation2 some properties of gamma and alpha manganese were determined by studying the ductile electrolytic metal and determining the changes in its properties as it transformed to the brittle alpha form. These investigations provided an excellent opportunity for following the progress of the transition and studying its mechanism. The results of a series of such investigations are reported in this paper. Procedure Various properties of manganese were determined starting with the metal in the original ductile gamma form and following the subsequent changes in its properties as the metal transformed to the brittle alpha form. These observations were made at various temperatures, the data providing information regartling the mechanism of the transformation as well as the effect of temperature 011 the transition rate. Structure and resistivity values gave the most significant results, so this paper is concerned primarily with them. The structure was studied microscopically as well as by X ray diffraction. The resistivity was determined on strips of the metal by measuring the potential drop across a given length of the specimen. Current was passed through the specimen by wires soldered to its ends, and the potential connections were made by wires looped around the specimen near its center. The current was determined by the potential drop across a standard resistor connected in series with the specimen, the potential drop being measured on a potentiometer. In the temperature range from room temperature to 100°C an ordinary drying oven was used to heat the specimen. This was entirely satisfactory except at 100°C, where the time required to heat the specimen was long compared to the transition time, making the initial section of the resistivity curve unsatisfactory. To overcome this limitation, at 100°C and higher a thermostatically controlled oil bath was used to heat the specimens. The block on which the specimen was mountetl was plunged into the hot oil at the start of each test. The heating time was thereby reduced from 5 min. to about 6 sec, and dependable resistivity values could be obtained through 160°C. At this point the whole transition, including the warm-up time for the specimen, required only about 20 sec and it was not considered worth while trying to extend the temperature range further. Aside from the heating problem, the problem of making a sufficient number of accurate resistivity determinations became more and more difficult as the temperature was raised. Using the manually operated potentiometer, 100°C was about as far as it was possible to go. At this temperature and above, a self-balancing photoelectric recording potentiometer was used. Its response was quite rapid, and it proved to be entirely satisfactory all the way through 160°C, where the tests were stopped because of the specimen heating problem rather than any limitation of the potentiometer recorder. The metal used in these tests was prepared at the Salt Lake City laboratory of the Bureau of Mines. The method of preparation is discussed in a paper by Schlain and Prater.3 The sheets were about 2 3/8 by 5 3/16 in. and varied from 10 to 16 mils in thickness. They could be cut readily into pieces suitable for the various tests. X ray and microstructure determinations were made on pieces about 1/8 to 1/4 in. wide and about 1 in. long, while resistivity measurements were made on strips as long as possible and about 55 in. wide. The thickness of each sheet was not uniform over all its surface. This had no bearing on the X ray and microstructure determinations, but sections as nearly uniform and free from flaws as possible were chosen for the resistivity determinations. The gamma manganese was electro-deposited at 30°C, the time of deposition ranging from 5 to 12 hr for each sheet. Whenever possible, the tests were started directly after the metal was stripped from the cathode; otherwise the sheet was placed immediately

Jan 1, 1950

By Roscoe C. Clark

In October 1945. R. F. Farris. in an AIME paper entitled Method For Drtermining Minimum Waiting OIL Cenzent Time, presented a method for caiculating the minimum WOC* time required in oil well cementing operations. Briefly. this method consisted of shutting in a well. after the cement had been placed and noting the time required fur the wellhead pressure to reach a. maximum. This time was then multiplied by a factor of 1.5 to determine when the cement had reached sufficient strength to support the weight of the casing. As a result of this work, a number of areas have reduced their WOC time ~Wuirements with the subsequent saving of considerable rig time. The tests conducted by Farris were, for the most part, conducted under cementing temperatures in excess of 70°F. This was done because in the overwhelming majority of cases. cementing temperatures are in excess of 70°F (only in tile northern part of the country. primarily in the Rocky Mountain ares. in cementing surface casing are temperatures below 70° F. encountered, and such temperatures occur only during the winter months). The Stano-lind Research Laboratory since that time has performed a number of tests both in the laboratory and in the field to evaluate this WOC factor when cemeriting temperatures are lower than 70°F. The results of these tests indicated the need for greater WOC time in areas affeaed by abnormally low cementing temperatures. These tests indi.cated that a woc factor of 2 (Time from start to mix cement to maximum wellhead pressure x 2 = Time to drill plug) will allow sufficient time for the cement to develop adequate strength. A field test under abnormally low cementing temperatures (surface temyerature 35°F., mud discharge temperature <70°F. and cementing depth 500 ft.) in the Rangely Field, "* using the WOC factor of 2, indicated the time to drill the plug as 45 hours. Well conditions preventing getting back into the well until a 48-hour WOC time had elapsed. At this time, the plug drilled firm to hard indicating that the cement had reached its final set. It is contemplated that during next winter additional field tests will be performed to further check the results of the laboratory and field tests conducted to date,

Jan 1, 1949

By G. L. Corrigan, J. R. Coleman

Four factors that largely determine the end product obtained when cement and water are mixed are the chemical compo ition of the cement, the fineness to which the cement is ground, the amount of mixing water used, and the procedure used in mixing the slurry. In order to study the effect of two of these factors, the other two, the chemical composition and method of mixing, are kept constant, leaving as variables fineness and water-cement ratio. Through years of experimentation and usage it has been well established that the reduction of cement clinker to a very fine state by grinding improves its cementing value, principally because the reaction between cement and water takes place only at the surface of the cement particle, further action being hindered by the accumulation of reaction products that tend to coat the unreacted material. Therefore, the more finely ground a cement, and the greater the surface exposed in proportion to its mass, the more rapid is the hydration rate. Similarly, the greater the surface exposed, the greater the proportion of the cement that reacts, and the lower the amount of residue that is unreacted and so remains inert and unable to make any contribution to cementing properties.1 Although it is more expensive to manufacture a finely ground cement than a coarser cement, the advantages of fine grinding of construction cements were so marked that the fineness of cement has increased considerably in past years. When the manufacture of special oil-well cements was begun, it was necessary to consider properties of cement that previously were considered of minor importance, foremost of these being pumpability. Since, with the water-cement ratio constant, a finely ground cement will produce a neat slurry of higher consistency and shorter time of pumpability than will a coarser cement, there is a tendency to grind oil-well cements to a lower degree of fineness. Therefore, in order to produce oil-well cements that will make a slurry having a long time of pumpability, cements are manufactured that because of their coarseness generally are poorer cementing materials than some of the more finely ground construction cements. On the other hand, often it is necessary to pump oil-well cements for long periods of time to place them properly behind a string of casing in a deep well, and since high strength is not of foremost importance for such cement, there is room for considerable controversy concerning the proper fineness range.

Jan 1, 1941

By Robert S. Shoemaker

Recently we read a short article which stated that Marcona Corp. was studying the use of 25,000-hp autogenous grinding mills for an iron ore project in Alaska. As if that weren&apos;t enough, they were going to dispense with the primary crusher and feed run-of-mine ore to the grinding mills which were to be driven by wrap-around seven-cycle motors. We see also that Bougainville Copper Co. will be grinding 90,000 tpd of ore in only eight 4250- hp ball mills. At Bougainville too, their float section will be the first large one to be completely equipped with the new 350-cu ft flotation cells. After a half century of relatively peaceful growth in the minerals industry, we are now seeing almost exponential advances in both equipment and plant size. At the same time, we are seeing a constant blending of hydro and pyrometallurgical techniques and processes into minerals beneficiation until the sample grind-&apos;em-up-and-concentrate-&apos;em plant is becoming a rarity.

Jan 1, 1970

By C. S. Giggins, F. S. Pettit

The oxidation properties of Ni-Cr alloys with fine grains, coarse grains, and deformed surface layers have been studied at temperatures of 900" and 1100°C in 0.1 atm of oxygen. The oxidation rates of alloys containing between 10 and 30 wt pct Cr have been found to be dependent upon the grain size of the alloy. Finegrained alloys had smaller oxidation rates than coarsegvained alloys because of the selective oxidation of chromium at alloy grain boundaries. In this compositional range alloys with deformed surface layers behaved similar to fine-grained alloys due to recrys-tallization of the deformed surface layer. In the preceding paper1 it was found that during the oxidation of Ni-Cr alloys, the volume fraction of precipitated Cr2O3 could be greater at alloy grain boundaries than at other areas of the alloy surface. In the case of alloys with chromium concentrations equal to or greater than 30 pct,* the volume fraction of Cr2O3 *AIL compositions are given as weight percent unless specified otherwise. precipitated at grain boundaries and within grains on the alloy surface both exceeded the critical amount required for lateral growth of the Cr2O3 particles and the surfaces of these alloys were completely covered with a continuous, external layer of Cr203 during oxidation. However, in the case of alloys with chromium concentrations between approximately 5 to 30 pct, the volume fraction of precipitated Cr2O3 exceeded the critical value required for external scale formation only at grain boundaries.but not within the interior of the grains. Consequently, the surfaces of these alloys had external scales of Cr3O3 over the grain boundaries but internal Cr2O3 subscales with external scales of NiO away from the grain boundaries. Under these latter conditions, it was found that chromium could diffuse laterally in the alloy from those areas covered with an external layer of Cr2O3, i.e., grain boundaries, to areas where the Cr2O3 was present as a subscale. This diffusion of chromium resulted in an increase in the volume fraction of Cr2O3 precipitated in the sub-scale zone and continuous layers of Cr2O3 could be formed at the subscale front in these regions. For the alloys used in the previous studies,&apos; continuous layers of Cr2O3 were formed on Ni-20Cr alloys in the subscale regions after approximately 30 hr of oxidation at 900°C. For shorter periods of oxidation, the Cr2O3 layer was semicontinuous with the continuous portion at the subscale front emanating from points where the Cr2O3 had been formed as an external scale over alloy grain boundaries. Some lateral growth of a Cr2O3 layer in the subscale region was observed on Ni-15Cr and even Ni-10Cr alloys but this layer was never continuous after 30 hr of oxidation. These results indicate that the selective oxidation of chromium in Ni-Cr alloys with chromium contents between 5 to 30 pct may be dependent upon the grain size of the alloy. Fine-grained specimens in this compositional range should have a larger fraction of the surface covered with external Cr2O3 than coarsegrained specimens and the subscale areas required to be sealed via lateral diffusion of chromium should be smaller. It is therefore to be expected that a continuous layer of Cr2O3 can be formed on alloys in this compositional range after short periods of oxidation providing the alloy grain-size is sufficiently small. bo studieS2,3 have established that the oxidation behavior of alloys can be significantly influenced by pretreatments which produce mechanically deformed surfaces. It has been found that deformed surfaces usually promote the selective oxidation of elements in alloys and it is believed that these effects are due to rapid diffusion of elements in the deformed layer. In view of the previous results,&apos; which showed that alloy grain boundaries may play an important role in the selective oxidation of chromium in Ni-Cr alloys, deformed surfaces may promote the selective oxidation of elements in alloys as a result of the numerous grain boundaries formed on the alloy surfaces via recrys-tallization during heating to the oxidation temperature. The purpose of the present studies was to determine the effect of alloy grain size and surface deformation on the selective oxidation of chromium in Ni-Cr alloys at temperatures of 900" and 1100°C in 0.1 atm of oxygen. EXPERIMENTAL The average grain diameter of the alloys used in the previous studies1 was not less than 0.04 mm and alloys with compositions between 5 and 30 pct chromium had average grain diameters between 0.04 and 0.14 mm. Since the oxidation kinetics were already available for these relatively coarse-grained alloys, it was desirable to use these same alloys in the present studies. The surfaces of the alloys listed in Table I of the previous paper were deformed by using a Model F S.S. White Industrial Airbrasive Unit, which delivered a controlled mixture of 25 µ Al2O3 particles in a stream of dry air at high velocity against the surface of a specimen. The amount of surface deformation produced by this treatment was not determined but a re-crystallized layer about 15 µ thick was formed upon annealing deformed specimens. The grain size at the surface of the specimens was reduced to an average grain diameter of 0.01 mm by annealing the deformed specimens, i.e., grit-blasted,

Jan 1, 1970

By J. A. Roberson, A. M. Adair

A plate of an 18 pct Ni (250 grade) maraging steel was homogenized, cold rolled, and re crystallized to produce a fine grained, homogeneous structure. The strength properties were then measured as a function of cold rollinq prior to aging. Material in the solution heat treated condition exhibited substantial strengthening from cold rolling. The strength increase and the rate of strengthening were proportional to the amount of cold work. This benefit, of up to 50 ksi, was retained during aging for 3 hr at 900°F. The structures produced by cold rolling and aging have been systematically investigated by transmission electron microscopy. The dislocation debris produced by cold work influences the morphology and distribution of precipitate particles as well as the rate of precipitation. An essential feature of the high nickel maraging steels is a martensitic transformation from y to a with the resultant production of a supersaturated bcc solid solution. This solution decomposes to form precipitates during a subsequent aging treatment.&apos; The martensitic transformation in low carbon Fe-Ni alloys and the mechanical properties of these alloys have been studied extensively.2"4 The carbon content of maraging steel is kept very low to avoid the embrittling Fe3C phase and to minimize the acicular, or twinned martensite common to high carbon steels. Maraging steels are usually strengthened only by heat treatment, but cold working is also quite effective in this respect as was shown by Decker, Eash, and Goldman,&apos; Kula and Hickey,5 and the present work. There is, however, some disagreement between the present results and those of Kula and Hickey. Because of their unusual combination of strength and toughness, the maraging steels are suitable for applications where reliability at high stress levels is required. The strength level is achieved through a combination of solid solution hardening,&apos; substructure hardening,3 and precipitation hardening,6 of which the last is the most important. The toughness of these steels has been reported to be a result of the absence of brittle grain boundary precipitates,7 and the fact that the matrix is a massive martensite rather than a twinned martensite.&apos; One of the problems in the manufacture and use of maraging steel has been its tendency to develop laminations in sheets parallel to the rolling plane.9,10 The present investigation was intended to determine whether or not an improvement in the microstructure of this steel by thermomechani-cal processing would improve mechanical properties. I) EXPERIMENTAL PROCEDURES A plate ($ in. thick) of an 18 pct Ni-250 grade maraging steel* was obtained and examined metallo- "Analysis, wt pct: 18.1 Ni, 8.6 Co, 5.3 Mo, 0.4 Ti, 0.07 Mn, 0.05 Cr, 0.05 Si, 0.002B. 0.1 Cu. 0.05 Al. 0.002 Zr, 0.016 C, balance Fe. graphically. It was found to contain laminations as described by previous investigators. This plate was then annealed at 2100°F for 24 hr to promote homogeneity. Pilot studies on small coupons had shown that this was the minimum temperature required to accomplish homogenization in 24 hr. Since this treatment caused excessive grain growth, the steel was subsequently cold rolled and recrystallized. Cold rolling was accomplished at about 5 pct per pass to a total reduction of 66 pct. The standard solution annealing treatment (1 hr at 1500°F) was adequate to cause recrystallization of the cold worked steel. The recrystallized steel was then cold rolled and ground by various amounts to produce specimens with uniform thickness and selected amounts of cold rolling. All tensile specimens with less than 90 pct cold reduction were ground to a thickness of 0.050 in. Specimens with 90 pct cold reduction were 0.025 in. thick. All

Jan 1, 1970

By V. H. Wilhelm

During the first half of the year 1935, the oil industry in California was on a fairly profitable basis, owing mainly to the operation of the Petroleum Marketing Agency. Coincident with the discontinuance of enforced curtailment, California production surged upward from an average of about 500,000 bbl. per day (over the first five-month period) to approximately 625,000 bbl. per day (over the last seven-month period). On Dec. 9 the state production had reached a peak of over 700,000 bbl., a figure that had not been approximated since the early days of voluntary curtailment (Fig. 1). A price cut was instituted during the last half of August, but had no deterring effect on operators that were determined to take advantage of the breakdown of curtailment and produce to capacity. New reserve figures, compiled from actual potentials, available after cessation of curtailment, revealed the startling fact that California reserves were rapidly declining. This situation, coupled with the desire among operators to obtain a more equitable price for their dwindling reserves, caused a restoration in November of a portion of the August price slash. A further rise in price was effected in early December, and crude quotations at the end of the year closely approximated those in effect during the first right months. At the close of the year, the industry felt confident that the production situation was under control. In all fields where competition is keen because of close spacing, production is gradually declining. In the Los Angeles Basin especially there is no likelihood of a large amount of overproduction, unless a new pool is discovered or deeper drilling reveals a prolific source of crude. As long as the fields that are operated by a few companies, such as Kettleman Hills, North Belridge, Ventura Avenue, West Coyote, Dominguez, and some others, can be controlled, it is believed that the overproduction problem in California will be solved.

Jan 1, 1936

By S. Y. Han

INTRODUCTION More than 97% of the total uranium production of the United States comes from sedimentary deposits (1). These sandstone deposits were formed by reduction of migrating uranium-bearing solutions from volcanic silicate rock sources. Such deposits occur in two major forms, either as relatively flat, lens-like deposits or as crescent- shaped roll front deposits. The lens-like deposits are found as discrete masses enclosed in reduced sandstone which is generally surrounded by oxidized sandstone. The roll front deposits are found along crescent-shaped interfaces between reduced and oxidized sands tone (2). In-situ mining of selected sedimentary deposits has proven to be a viable method of extraction and competitive with conventional mining for relatively deep low-grade ores (2). In in-situ leaching, uranium is recovered by drilling injection and collection wells in the ore body, pumping a suitable lixiviant to dissolve the mineral, extracting uranium from the pregnant solution by ion exchange, and finally regenerating and recycling the lixiviant. Even though there is increasing interest and practice in developing the in-situ technique for obtaining uranium values from deeper, lower-grade reserves, there is a lack of knowledge of the basic leaching kinetics and combined transport processes. In-situ leaching operations, in general, appear attractive for the following three general types of deposits (2): (1) low-grade surface dumps or deposits which lie above the natural water table,

Jan 1, 1983