Search Documents

By E. J. Efsic, C. M. Wayman

The fcc to bcc y to a transformation in an Fe-24.5 at. pct Pt alloy was studied and found to be martensitic. Large martensite plates are formed in this alloy which are ideal for crystallographic studies; the Ms temperature is about -5°C. Ordering of the parent phase prior to transformation to martensite causes a pronounced lowering of the Ms temperature. For the first time in the case of alloys of iron, measurements of the habit plune, orientation relationship, and magnitude and direction of the shape stvain have been obtained on preselected martensite plates. It is shown that by measuring the initial and displaced (as a result of the shape strain) positions of three or more non-parallel fiducial scratches on one reference surfice the maguitude and direction of the shape strain and the state of distovtion at the parent-mavtensite interface can be determined with a reasonable degree of accuvacy. The agreement between the phenomenolog-cal crystallographic theory of martensitic transformations and the experimental results habit plune, orientation relationship, and nlagnitude and direction of the shape strain) is essentially perfect, and is thought to be the best reported to date for iron alloys. THE comparatively few investigations on binary Fe-Pt alloys have been concerned with magnetic properties, ordered phases, and the equilibrium diagram itself. Various investigations have shown that the equilibrium diagram is of the open y field type; in addition there is a peritectic transformation, a minimum melting point, and three ordered phases: Fe3Pt, FePt, and FePt3. The results of a number of investigators1-6 have shown that the temperature dependence of the y to a (and reverse) transformation in iron-rich alloys is reasonably well-established. The Fe3Pt phase was first noted by Kussman and Rittberg,7 and its existence was later confirmed by Franklin et al,8 Steijn and Donahoe,9 and Berkowitz et al.10 The FePt phase was reported by Isaac and amman' and later confirmed by a host of others.3,6,7,12,13 Kussman and Rittberg7 noted the existence of the superlattice FePt3. Prior to 1956, the 1 to a transformation in iron-rich Fe-Pt alloys was termed "irreversible". In 1957 Klokholm and Donahoe" termed this transformation martensitic, presumably because of its occurrence at temperatures well below those where diffusion normally takes place. This observation served as a point of departure for the present investigation, and in the very early stages of the work to be discussed it was readily verified that the y to a transformation in iron-rich Fe-Pt alloys is indeed martensitic. Quite large martensite plates exhibiting the well-known surface tilt were observed. These plates are ideal in the sense that the boundaries between the parent and product phases were usually very straight. It thus appeared that Fe-Pt martensites would be ideal for crystallographic studies, and this was the purpose of the present investigation. Details of the crystallography of martensitic transformations (particularly for iron alloys) and the phe-nomenological crystallographic theories15-l7 have been discussed many times and thus will require very little elaboration here. The end result of these theories, given in matrix form, is

Jan 1, 1968

By Olin M. Hart

Uranium ores occur in the Lower Cretaceous Inyan Kara group of heterogeneously stratified fluvial and fluvial-marine sandstones in the Black Hills of western South Dakota and northeastern Wyoming. There are three principal mining districts, each in the ancestral and present drainage area of a major river partially responsible for stripping the region to its present topographic form. Primary minerals in the deposits are coffinite and uraninite with minor amounts of paramontroseite and haggite. The ore minerals coat sand grains and fill interstices of complexly cross-stratified sandstone along solution fronts similar to "roll" type deposits of the other districts. Minerals of oxidized deposits are typically carnotite and tyuyamunite with different proportions of secondary vanadium accessory minerals. Ground water was the transporting medium and deposition of primary uranium and vanadium minerals occurred in reducing environments produced and controlled by physio-chemical characteristics of the sedimentary rocks.

Jan 1, 1968

By L. A. Tarshis, H. E. Cline

A stability criterion for a lamellar eutectic interface was derived previously1 assuming that the wavelength, A,. of the perturbation which grows most rapidly is much larger than the lamellar spacing. A. This assumption was required to permit averaging of both the interface temperature and composition over the complicated geometry of a lamellae. If this assumption is invalid, as has been suggested.2,3 then the problem becomes too complicated to solve completely. The first of these analyses1 did not calculate the wavelength. A,. of the initially unstable perturbation. whereas the more recent analysis.' which led to a contradiction of this assumption. did not include one of the key factors for determining this wavelength. To rigorously determine the wavelength, the effect of the curvature of the perturbed interface (not considered by either of the above treatments) must be included. By omitting this term, one would be led to an incorrect conclusion regarding the magnitude of A,. but to an accurate criterion for stability as evidenced by the excellent agreement with experimental observations.' In the case of single-phase alloys. the critical wavelength. A,. for instability can be calculated from the Mullins and Sekerka4 (M.S.) analysis which includes the effects of capillarity. In the following discussion, the M.S. analysis is applied to lamellar eutectics and the critical wavelengths calculated for reasonable growth conditions in Pb-Sn eutectic alloys. In order to apply the M.S. analysis to eutectics. one may substitute i) the effective liquidus slope.1 m*. for the single-phase liquidus slope and ii) the ratio of the bulk alloy composition. C,. to the average interface composition in the liquid (Ci = CE where CE is the equilibrium eutectic composition) for the distribution coefficient to give:

Jan 1, 1970

By John K. Dienes

The permeability of sands and soils seems to be adequately de- scribed by Darcy's law, but the permeability of rocks is complicated by a number of factors related to the probability of crack intersections. During the last few years we have developed a statistical theory of fragmentation which has been successful in explaining the observed behavior of rocks. In this paper, a theory of permeability is developed which draws on the concepts employed in previous work. The permeability involves three factors, the average fluid flux per crack, the number of cracks per unit area, and the fraction of cracks that are not isolated. Probabilistic ideas are used in connection with the hydrodynamic theory of flow through a single crack to develop an integral expression for permeability. The result has the form of Darcy's law for anistropic media. Although the current work is motivated by the need to develop optimized oil-shale retorts, we believe that the theory can be applied to a variety of other problems.

Jan 1, 1982

By C. B. Alcock, R. G. Hudson

Sulfur pressure measurements above FeS in equilibrium with iron have been carried out by the Knudsen orifice method. A comparison is made of the weight loss of the cell per unit time obtained in the above experiments, that calculated from Richardson and Alcock's measurements of the S2 pressure above FeS in equilibrium with iron, and the dissociation constant for diatomic sulfur from spectroscopic and thermal data. EXTENSIVE equilibrium measurements have been made to determine the sulfur potentials of a great many systems of metallurgical interest.' In order to confirm their reliability, to supply data which may be of use in further thermodynamic calculations, and to establish the reliability of the Knudsen orifice in obtaining accurate thermodynamic values at high temperatures, the present investigation on the pressure of the gaseous species above FeS in equilibrium with iron has been carried out. The Knudsen orifice method has been used for these pressure measurements. Experimental The apparatus and general technique for this investigation are the same as that reported for the determination of the vapor pressure of silver.' To reduce the residual gas pressure in the evacuated chamber, a titanium getter, maintained at run temperature, was introducbed. Several types of Knudsen cells were used—platinum, zircon, and fused silica. The orifice in the zircon cell was fashioned with a small diamond wheel. The same precautions were used in this investigation as were employed in the work on Mo2S2.3 The FeS-Fe mixture was prepared by heating a sample of pure FeS,, supplied by K. K. Kelley of the Bureau of Mines, with excess iron powder, cp grade, obtained from the Fisher Scientific Co. These two substances were heated in a closed Armco iron crucible at 960°C, held in a vacuum of less than 10" mm Hg for 24 hr. The mass was then removed from the cell and ground in an agate mortar. In this form it was charged to the various Knudsen cells. Heating the Knudsen cell for an additional two days was sufficient to obtain constant rates of weight loss of the cell. The data obtained in this investigation are recorded in Table I. To establish whether or not a sulfide of iron is volatile at these temperatures, 0.7646 g of the FeS-Fe mixture, described above and containing 69.2 pet Fe, was placed in the zircon Knudsen cell. Run Nos. 103 to 109 were performed on it. After the completion of these runs, the total amount of iron left in the cell was obtained by chemical analysis. It contained 0.537 g Fe, compared to 0.529 g in the original charge. Thus, there was an apparent gain in iron of 1.5 pet. This is attributed to unknown experimental error, and the conclusion is that no sulfide of iron is volatile. The vapor pressure of pure iron4 is about one thousandth that of the sulfur pressure' at these temperatures. The vapor pressure of iron inside the Knudsen cell will be almost exactly that of pure iron, since in the iron-rich phase the percentage of sulfur is of the order of 0.025 pet.At this low percentage of sulfur Henry's law is probably obeyed by the sulfur. Thus, the iron will obey Raoult's law. In any event, the vapor pressure of iron will be lower than that of pure iron and, since the vapor pressure of pure iron is negligible compared to the pressure of sulfur, the weight loss of the cell due to the vaporization of iron should be negligible. Since neither iron nor FeS is volatile to an appreciable extent, the total weight loss of the cell must be due to the vaporization of sulfur. Discussion and Calculations On the assumption that S, is the only gaseous species present in appreciable quantity, its pressure

Jan 1, 1957

PRESIDENT AND DIRECTOR D.C. JACKLING SAN FRANCISCO, CALIF. PAST PRESIDENTS AND DIRECTORS NEW YORK, N. Y. R. C. ALLEN- CLEVELAND, OHIO VICE-PRESIDENT, TREASURER AND DIRECTOR KARL EILERS-* NEW YORK, N. Y. VICE-PRESIDENTS AND DIRECTORS HENRY KRUMB NEW YORK, N. Y. PAUL D. MERICA . NEW YORK, N. Y. H. G. MOULTON NEW YORK, N. Y. HARVEY S. MUDD Los ANGELES, CALIF. WILFRED SYKES CHICAGO, ILL.

Jan 1, 1938

STANDING COMMITTEES. Executive. CHARLES F. BAND, Chairman. JAMES F. KEMP, JOSEPH W. RICHARDS, ALBERT R. LEDOUX, BENJAMIN B. THAYER. Membership. BENJAMIN B. THAYER, Chairman. WALTER R. INGALLS, JOHN H. JANEWAY, JR., JOHN D. IRVING, HERMAN A. PROSSER. Finance. EDWARD L. YOUNG, Chairman. KARL FILERS, JAMES GAYLEY. Library. JAM ES, F. KEMP, Chairman. JOHN HAYS HAMMOND,3 E. GYBBON SPILSBURY,2 ALEX. C. HUMPHREYS,4 BRADLEY STOUGHTON.

Jan 8, 1913

By F. J. Fayers, J. W. Sheldon

A theoretical discussion is presented of the behavior of the interface between two fluids of different physical properties when displacement is occurring along a thin tilted bed. An approximate equation of motion is deduced for the motion of the interface, suitable boundary conditions are derived and the conditions necessary for the approximation to be valid are determined. Steady-state behavior and the circumstances under which a steady-state interface can develop are discussed. Finite-difference solutions of the equation of motion for two characteristic water-drive problems are presenled. The theory of displacement in a thin bed may be regarded as being the porous-medium-equivalent of the classical "shallow-water wave" theory of hydrodynamics. INTRODUCTION The solution of moving interface problems are important in predicting the behavior of oil reservoirs under various conditions of production. Kidder4,5 has obtained analytic solutions for the fingering problem and for another particular case of the motion of the interface between two immiscible fluids of unequal density in a porous medium. In the present analysis, we analyze the problem of the motion of an interface along a slightly dipping bed whose length is long compared with its thickness. The requirement of a thin bed is necessary in order to give a simple differential equation for the motion. The two fluids are of unequal density and mobility. In the derivation of the equation of motion, it is assumed that the lighter fluid is being injected at constant rate at the high end of the porous layer, while heavy fluid is produced at the low end of the layer. The analysis applies equally well, however, to the reverse procedure in which the heavier fluid is injected at the low end of the tilted layer. It will be shown that the behavior of the system is critically dependent on which fluid has the higher mobility and that the interface can in certain circumstances achieve a simple progressive steady-state shape. The fluids may be considered to be immiscible or miscible. It is assumed, however, that the thickness of the interface region is negligible in comparison with other dimensions of the system, and that the strength of the saturation or concentration discontinuity remains constant during the motion. In conjunction with Buckley-Leverett theory and areal sweep-out calculations, the tilted interface problem is one of the fundamental problems of reservoir engineering; it defines the very important underpassing and overpassing phenomena associated with water-drives, gas-drives and secondary recovery operations. The tilted interface problem has been dealt with previously by Dietz.2 In the present paper, we endeavor to derive the pertinent mathematical results more rigorously, and in doing so we obtain modifications in both the differential equation and boundary conditions for those given by Dietz. We also attempt to show the connection between these results and some of the recent work on the stability of interfaces. Finally, we attempt to demonstrate the practical importance of the thin bed theory by showing the difference in behavior of two characteristic waterflood problems. In the favorable mobility case recovery is improved by increasing production rate, while in the unfavorable case undercutting or overcutting is minimized by reducing the displacement rate. PROPERTIES OF THE EQUATION OF MOTION Fig. 1 illustrates a porous layer of constant thickness H and tilt 8 with Fluid 1 of mobility ?l and density pl below Fluid 2 of mobility ?2 and density p2. The fluids are incompressible and flowing with volumetric flux q along the layer. Both the slope a of the interface with respect to the bed and the curvature of the interface are assumed to be small. What is meant by "small" is indicated in the derivation given in Appendix A of an approximate equation of motion for the interface. Other symbols are defined in the "Nomen-

By E. J. Rapperport, E. D. Levine

The boundaries of the (a +ß) field in the Al-Li system were determined between 150°and 550°C utilizing quantitative metallography and lattice-parameter measurements. The solubility of lithium in aluminum decreases from 12.0at. pct Li at 550°C to 5.5 at. pct Li at 150°C. P Al-Li is saturated with aluminum at 45.8 at. pct Li and has this boundary value constant over the temperature range 150°to 550°C. THE solid solubility of lithium in aluminum has been determined by several investigators, 1-6 but, as shown in Fig. 1, there is little agreement among the various determinations. The earliest investiga-tions'-' are suspect because of the use of impure materials. Although high-purity materials were employed in more recent work,4'5 the experimental techniques may have led to contamination of the specimens. Probably the best work has been that of Costas and Marshall,6 who obtained close agreement between results obtained by two independent phase-boundary techniques: electrical resistivity and mi-crohardness. No detailed studies of the solubility of aluminum in the bcc ß phase, Al-Li, have been reported. Cursory investigations1,2,6 have indicated only that the (a+ß) -p boundary lies between 40 and 50 at. pct Li and is relatively independent of temperature. The present work was undertaken in order to provide an independent check on Costas and Marshall's determination of the solubility of lithium in aluminum, to extend knowledge of this solubility limit to temperatures below 225°C, and to make an accurate determination of the solubility of aluminum in Al-Li. EXPEFUMENTAL Alloy Preparation. In view of the difficulties encountered in previous investigations of the A1-Li system, close attention was paid to the use of methods of alloy preparation and treatment that would minimize contamination. Aluminum sheet (99.99 + pct Al) was vacuum-induction melted in a beryllia crucible to remove hydrogen. Lithium (99.9 pct Li) was charged with pre-melted aluminum into a beryllia crucible, in a helium-filled drybox. The crucible was sealed in a Vycor tube and transferred from the drybox to an induction furnace. Melting of alloys was performed by induction heating in a helium atmosphere. Solidification was accomplished by means of a suction apparatus, shown in Fig. 2, in which the alloy was forced by changes of pressure into a 3/16-in. inside diam closed-end beryllia tube. This technique produced rapid solidification of a small portion of the melt, resulting in alloys with a high degree of homogeneity. Typical lithium distributions are presented in Table I. Transverse sections 1/8 in. long were cut from the alloy rods, and each section was split in half longitudinally. One half of each section was analyzed for lithium, and the opposing halves were employed for phase-boundary determinations. Lithium contents were determined by flame photometry with an accuracy of 1 pct of the amount of lithium present. Thermal Treatments. Homogenization and equilibration heat treatments were performed in electrical-resistance furnaces with temperatures controlled to ± 2OC. Calibrated chromel-alumel thermocouples were employed to measure temperature. Homogenization was performed in helium-filled l?yrex tubes for 1 hr at 565°C. The encapsulated specimens were then transferred directly to furnaces maintained at lower temperatures for equilibration. Equilibration times were 2 hr at 550°C, 8 hr at 450°C, 27 hr at 350°c, 90 hr at 250°c, and 285 hr at 150"~. These times were chosen on the basis of conditions employed by previous investigators. Alloys were quenched from the equilibration temperatures by breaking the capsules into a silicone oil bath. By performing all possible operations either in sealed capsules or in a helium-filled drybox, the specimens were given minimum exposure to the atmosphere. Quantitative Metallography. Metallography of Al-Li alloys is difficult because of the atmospheric reactivity of the ß phase. It was found possible, however, to prepare surfaces of good metallographic quality by preventing contact with moisture during preparation. Grinding through 4/0 paper was performed in the drybox. The specimens were then transferred under kerosene to the polishing wheel. Three polishing stages were employed: 25-p alundum with kerosene lubricant on billiard cloth, 1-µ diamond paste on Microcloth, and 1/4-p diamond paste on Microcloth. Between stages the samples were cleaned by rinsing in trichloroethylene and buffing

Jan 1, 1963

Jan 1, 1933

By C. S. Roberts

THE advent of a sensitive X-ray method of analysis recently has allowed the determination of retained austenite in amounts as low as 0.3 pct.' As a result this phase has been found in quenched low carbon steels where its presence has not been generally suspected. In the course of a study of the tempering process,' retained austenite determinations were made by the X-ray method on a series of high purity Fe-C alloys and plain carbon steels. The chemical analyses of these materials and details of the hardening procedure are given in Table I. Results were obtained after quenching to 72°F (22°C) and — 321 °F (—196°C). Austenitizing temperatures were between 100" and 150°F above A, or Acm. All proeutec-toid cementite or ferrite was in solution. The combination of the results with those of Averbach, Castleman, and Cohen,' and earlier results of Esser

Jan 1, 1954

By E. Gaujot

IN connection with the question of coal waste and economy in mining, we would call the attention of those interested to an apparatus invented by M. Dernencourt, Superintendent of the Anzin Division of the Anzin Coal Company, North of France. This apparatus is known in France and Belgium under the name of prop screw jack (vis botte), and has been used with good results in the above-named countries for some years past. M. Ponson gives, in his " Traité de l'exploitation des Mines," a description of it (page 533), but as the description given is old, the work not widely known in this country, and as some valuable improvements have been made since, I thought it might be useful to give a description of it, having seen it in operation in 1867, while in Europe to attend the great Exposition, and on a scientific tour to the mining districts of France, Germany, Belgium, and Italy. The prop screw jack is composed of the following pieces: I. The body or column B, Fig. 4 [Plate (1)], of oak or yellow pine, sawed square, the bark taken off, and any length, proportionate to the vein. The smallest are 10 inches diameter at the base, and 9 inches at the top, the height being from 12 to 15 inches less than the size of the vein. In the axis of this column, and at the top end, is a cylindrical opening or hole, C, 2 3/4 inches diameter, 10 inches deep, for the screw, S. II. Two wrought-iron rings, R R, to strengthen the two extremities of the column ; the rings must be put on hot. III. A cast-iron washer, E, with hole in centre a little larger than the screw, to be put on the top of the column, and on which the nut is to rest; the top side of this washer must be faced on the lathe, also the bottom of the nut, to prevent friction. IV. The screw, S, having a total length of 12 inches and a diameter of 21/2 inches (for very high veins this diameter may be in¬creased to 3 inches), and has on its top a wrought-iron plate, T,

Jan 1, 1873

Jan 1, 1959

By J. W. Freeman, D. N. Frey

Fundamental reasons for the improvement in creep resistance of an austenitic alloy by cold working were investigated mainly by X-ray diffraction. The creep resistance was found to be improved by the internal stresses in the lattice of the alloy induced by the cold work. THIS investigation was concerned with the fundamental reasons for improvement in creep resistance of an austenitic alloy as a result of cold working. Also, the investigation was carried out to elucidate the conditions under which cold working could be expected to improve the creep resistance. To achieve these ends, creep resistance and internal structure were correlated for a variety of cold-worked conditions. Since the aim of the investigation was not to obtain specific and extensive information on any one alloy, creep testing was done with a single stress at 1200°F. Structural studies were carried out primarily with X-ray diffraction characteristics. The alloy used, low carbon N-155, was selected on the basis of being representative of at least some of the alloys used in gas turbines. Low carbon N-155 alloy in the form of %-in. sq bar stock was used in this investigation. The chemical composition, in percent, was: C, 0.13; Mn, 1.43; Si, 0.34; Cr, 20.73; Ni, 18.92; Co, 19.65; Mo, 3.05; W, 1.98; Cb, 0.98; N, 0.14; and Fe, balance. The bar stock was produced from a 13-in. sq billet, finished to 7/s in. round cornered square between 2060" and 1910°F. Prior to use in this particular investigation, the bar stock was solution-treated 1 hr at 2200°F and water quenched. This procedure was used in order to put the stock in a condition where effects of prior processing were minimized. Experimental Procedure The specific approach to the problem was twofold. First, the influence of cold working, under various conditions, on the creep rate under a single stress at 1200°F and on the internal structure was in part determined. Second, the effect of annealing at various times and temperatures on the creep rate and internal structure of the cold-worked samples was in part evaluated. The first step was basic to the investigation—creep resistance and structure were to be correlated. The second step was taken to see if the annealed samples showed some internal changes which could also be correlated with changes in creep resistance. This it was felt would facilitate solution of the basic problem. The creep and structural studies were carried out on samples reduced approximately 5, 15, and 40 pct at room temperature and 15 pct at temperatures up to 2200 °F. Annealing of various of the samples was done at 1200°, 1400°, 1600°, and 1800°F for time periods up to 1000 hr. Studies of the annealed samples were concentrated on materials rolled approximately 5, 15, and 40 pct at room temperature and 15 pct at 1400°F. The creep tests were carried out at 1200°F under 40,000 psi, the latter being approximately the 1000 hr rupture stress of the material

Jan 1, 1952

ALABAMA Anniston.-Carrington, F. G. Auburn.-Brown, R. L. Battelle.-Green, G. G. Bessemer.-Abbott, C. E. Dobbs, G. G. Ferguson, V. Birmingham.-Adams, J. H. Aldrich, T. H. Aldrich, T. H., Jr. Allen, A. W. Bonnyman, J. Bowron, J. Bush, M. W. Crawford, G. G. Crockard, F. H. Ellis, E. E. Fairbairn, C. T. Gallacher, J. Geismer, H. S.

Jan 1, 1917

By Paul E. Richardson, Edwin E. Maust

Cyclic voltammetry and surface potential (photovoltage) measurements have been carried out on galena electrodes in sodium tetraborate solutions with added HC1 and NaOH to adjust the pH over the range 2 to 13. The first technique shows that the surface species formed on moderate anodic polarization and reduced on subsequent cathodic polarization are the same over the entire pH range. At anodic potentials, a soluble metal species and excess sulfur are formed; at cathodic potentials, sulfur is reduced to a soluble species. More importantly, excess surface sulfur is formed spontaneously under zero current conditions in alkaline solutions. This has been shown to occur on both polished surfaces and on virgin surfaces produced by in situ cleavage under the electrolyte. The photovoltage gives some insight into the charge and potential distribution at the galena surface. This is found to depend on past electrochemical history and the n- or p-type semiconducting character of the electrode and is interpreted in terms of changes in the surface stoichiometry that occur during reduction or oxidation. The effect of surface stoichiometry on subsequent xanthate interactions is discussed.

Jan 1, 1976

By Lewis Stockett

During the year 1903, a building having machinery corresponding to ail anthracite-coal breaker was erected at the town of Stockett, Cascade county, Mont., for the purpose of breaking-up and cleaning bituminous coal. The coal is mined from a vein of the Kootenai group of the Lower Cretaceous measures having the following section: The vein is nearly horizontal in position, and each bench differs in quality as shown in Table I.

Jan 1, 1905

By F. S. Pettit

The oxidation of Ni-3 to 25 wt pd Al alloys has been studied in 0. 1 atm of oxygen at temperatures between 900° and 1300°C. These alloys have been found to oxidize by three different mechanisms which depend on the temperature of- oxidation and the alloy composition. Two of the three mechanisms do not permit a continuous layer of Al,0, to be formed on the alloy surface and the oxidation rates are greater than that for pure nickel. The third mechanism results in the formation of an external A1203 scale and lke oxidation rates are about three orders of magnitude smaller than those for pure nickel. The minimum amount of aluminum required for the formation of external scales of A L,0, has been determined. NICKEL-base alloys are currently the main source of materials for use at elevated temperatures in gas turbine engines. These alloys are usually coated to obtain oxidation resistance. Coatings on nickel-base alloys are frequently formed by reaction of the alloy with aluminum whereby alloyed nickel aluminides are formed. The alloyed nickel aluminides provide protection to the nickel base alloy because external scales of A1203 (alumina) are formed during oxidation and mass transport through A120, is slow in comparison to mass transport through most other oxides. In view of the protective properties of A1203, it is important to know how much aluminum is required in these alloys in order to form external scales of AlzO,. The present paper is concerned with the oxidation kinetics and the oxidation mechanisms of Ni-A1 alloys and the minimum amount of aluminum required in these alloys for the formation of external scales of Alz03. THEORETICAL CONSIDERATIONS When a Ni-A1 alloy is heated in oxygen at elevated temperatures, the following reactions can take place on the surface of the alloy where the oxide phases are assumed to be virtually pure: These oxide phases are in the form of nuclei scattered over the surface of the alloy and, in view of their rapid formation, they need not be in equilibrium with the alloy. As the oxidation process continues, equilibrium between the alloy surface and the oxide phases is approached and the stability of the oxide nuclei is determined by the composition of the alloy at the alloy/oxide interface because of the following reactions: 3NiA1204 + 2A1 (alloy) = 4AlzO3 + 3Ni (alloy) [41 4Ni0 + 2Al (alloy) = NiA120, + 3Ni (alloy) [ 5 1 Application of the mass-action law to Eqs. [4J and [5J yields the following equilibrium conditions for these reactions: where aA1 and aNi are the activities of aluminum and nickel, are the standard free energies of formation of NiO, A1203, and NA1204, respectively, R is the gas constant, and T is the absolute temperature. If the composition of the alloy at the alloy/oxide interface is such that (akl/ahi) is greater than the equilibrium values defined by Eqs. [6] and [7], then Reactions (41 and [5] will go to the right as written. Conversely, if the alloy composition is such that the activity ratio (aLl,/aki) at the alloy/oxide interface is less than the equilibrium values, then Reactions [4] and [5] will proceed to the left. The equilibrium activity ratios in Eqs. [6] and 171 can be calculated since values for the standard free energies of formation of the oxide phases are available. Standard free energies of formation for NiO and A1203 have been tabulated by Elliott and ~leiser.' The standard free energy of formation for NiA1204 can be obtained from the data of Tretjakow and Schmalzried.' The results of these calculations are tabulated in Table I. Table I shows that the following inequality is valid over the temperature interval 900" to 1300°C: (Reaction [5]) (Reaction [4]) « 1and therefore the aluminum activity for these compositions can be taken as equal to the square root of the activity ratios (i.e., aNi = 1). If equilibrium is estab-

Jan 1, 1968

By Freeman Bishop

Quietly picking his way through the thorny thicket of conservation issues is William E. Ruckelshaus, director of the Environmental Protection Agency in which President Nixon gathered the various anti- pollution units from the Interior, Commerce. Agriculture and Health. Education and Welfare departments. Mr. Ruckelshaus. EPA's first administrator, moved over from being Assistant Attorney General in charge of the civil division at Justice to this new post. Essentially, EPA is charged with administering swiftly proliferating antipollution programs. This means policing industry cities, farms and everything else. Ruckelshaus has been quietly fitting together the various pieces of this new agency, pulling then1 out of other Federal departments. Some 5800 employees are involved. The budget in 1971 for these segments will total about $1.5 billion.

Jan 1, 1971