By A. Simkovich, C. W. McCoy

THE relationship among chromium, carbon, and temperature during the oxidation period of stainless steel melting was developed by Hilty et a1 1-3 whose studies were confined to plain chromium stainless steels. The simplified version of their relation is given by the equation:

Jan 1, 1962

By G. W. Neighbor, M. S. Abrahams

The actice slip plane in InSb is found to be of the {111} type by using the method of two-tmce anulysis. Measurements of the rotation of the tensile axis with increasing plastic shear strain indicate that the tnacroscopic slip direction is a <110>. Recrystal-lization is first observed at a sheav strain of about 70 pct for a crystal deformed at a temperatzcre of 473° C and at a shear strain rate of 2.90 times 10- %ecc-I; the dislocation density corresponding to this value of the strain is 1 x 108 em-&apos;. At a shear strain of about 170 pct, the recrystallization process is complete. This appears to be the fimt time re-crystallization has heen observed in a semiconductor. V HE operation of the {Hi} glide plane in Ge was first noted by Gallagher.&apos; This finding was confirmed by Treuting who also extended the result to Si. Using X-ray techniques, Treuting3 demonstrated that the macroscopic slip direction in Ge was of the <110> type. The choice of the (111) <110> slip system in Ge is exected since in the diamond-type structure the {Ill7 plane is the plane of highest density and the <110> direction is the direction of closest packing.4 There is little reason to expect that the glide elements of InSb are different from those of Ge, since the zinc-blende structure characteristic of InSb is quite similar to the structure of Ge. With regard to InSb, Allen5 has indicated that the glide plane is the {111} type. There appears to be no quantitative determination of the glide direction, however. The present work was undertaken to establish both the glide plane and glide direction in InSb and also to see if recrystallization occurs at large shear strains. EXPERIMENTAL PROCEDURE Mechanical Deformation. The single crystals of InSb used in this investigation were deformed in uni-axial tension. The tensile axis of the specimens was [145] and the periphery was bounded by (111) and (321) planes as shown in Fig. 1. The metallographi-cally polished specimens were deformed in a dynamic atmosphere of He, using an Instron machine. The tensile tests were performed at temperatures in the range of 300°C to the melting point (525OC) and at shear strain-rates varying between 1.94 X 104 sec-&apos; to 1.94 x 103 sec-&apos;. Additional details concerning the preparation and deformation of the specimens have been presented previously.&apos; Analysis of the Glide Elements. The traces of the active slip plane in both (111) and (321) planes were analyzed according to the usual method of two-trace analysis." The macroscopic slip direction was determined by measuring the rotation of the tensile axis as a function of plastic strain,8 These measurements were made from Laue back-reflection X-ray photographs. The X-ray beam was perpendicular to the (111) plane. A given crystal was used for only one measurement of the rotation of the tensile axis after it had been strained to a predetermined value. Therefore, care was taken at all times to insure that the X-ray beam was parallel to the [Ill ] direction of all the samples. RESULTS AND DISCUSSION Glide Plane. After 3.4 pct plastic shear-strain, at a temperature of 369°C and a shear strain-rate of 1.94 x 104 sec-&apos;, the slip traces on the (111) and (3.21) planes appear as in Figs. 2(a) and 2(b), respectively. The results of an analysis of these glide markings demonstrate that the slip plane is (111). The operation of this plane is expected on the basis of the orientation of the specimen, since glide on this plane and in the [I011 direction will result in

Jan 1, 1962

By Michael Hoch

The phase diagrams of binary systems of some of the transition elements of Groups IV, V, and VI were used to compute the partial free energies of these elements and the free energy of formation of their Laves-type compounds. From these data, isothermal sections of ternary phase diagrams were calculated and compared with experimental results. DURING the investigation of ternary and quaternary high temperature systems formed by the transition elements of Groups IV, V and VI, the binary phase diagrams for these elements available in the literature were studied. In this study, the free energies of formation of the compounds formed in these binary systems were calculated; these values were then used to determine the general shape of the ternary and quaternary phase diagrams. Above 900°C, the transition elements of Groups IV, V, and VI are all bcc and form only Laves-type compounds in binary systems. The investigation was based on the binary phase diagrams published by Hansen.1 The Cr-Nb system was constructed from the data of Elyutin and Funke.&apos; Several unpublished phase diagrams were taken from Schmidt&apos;sLo and English&apos;sl1 compilations. THE BINARY SYSTEMS valuations of the Thermodynamic Functions. Rostokers evaluated the boundaries of the (a + b) field in Ti-base alloys with a two-constant equation. The authors&apos; interest is mainly in the center of the diagrams; therefore the miscibility gaps in the Zr-Nb, W-Cr, Ta-Zr, Ta-Hf, and Ti-W systems were used to evaluate the thermodynamic behavior of the binary systems. Lumsden&apos;s4 Equations 29.2, 32.1, and 33.1, page 287, were used for the excess integral free energy FeX, and for the excess partial free energies Fx and replaces b and b replacesP in Lumsden&apos;s notation):

Jan 1, 1962

By E. E. Wahlstrom

The Harold D. Roberts tunnel, in Summit and Park Counties, Colorado, is a concrete-lined pressure tunnel finished to a circular cross section of 10.25 ft diam. The tunnel is 23.3 miles long and is designed to transport water for domestic use by the City and County of Denver from reservoir storage at Dillon to a tributary of the South Platte River at Grant. The tunnel passes beneath the Continental Divide at the crest of the Front Range and intersects rocks of diverse types and origins and geologic structures of extreme complexity. Geologic investigations preceded and were continued during construction and contributed materially to the safe and economical advance of the tunnel headings. Geological data obtained and evaluated during construction include plans and sections on a scale of 1 in. to 50 ft, rock temperatures at 2000-ft intervals, records of progress related to geology, records of ground-water conditions, summaries of the use of steel and timber supports, and summaries of grouting operations. Adverse conditions required use of steel and timber supports for 71.74% of the total length of the tunnel. Most supported sections reached a condition of equilibrium within a few hours to a few months after being excavated, and the concrete lining serves chiefly to provide an additional safety factor and to provide necessary hydraulic characteristics to the tunnel. Efforts to attain a maximum rate of advance of the tunnel headings necessitated use of more steel and timber supports than would have been required in a less accelerated tunneling operation. This report summarizes geologic investigations prior to and during construction of the Harold D. Roberts tunnel in Summit and Park Counties, Colorado (Fig. 1) and analyzes the tunneling operation as it is related to the various kinds of geologic conditions encountered in the tunnel. The tunnel is concrete lined to a circular cross section of 10.25 ft and is designed to transport 788 sec ft from reservoir storage at Dillon 23.3 miles along a dog-leg course passing under the Continental Divide to outlet and control works at Grant, Colo. The primary purpose of the tunnel is to augment the domestic water supply of the City and County of Denver, but plans include provisions for power generation at the outlet portal at a future date. Location of the tunnel was made after extensive preliminary geologic and engineering investigations by the Board of Water Commissioners of the City and County of Denver, and the U.S. Bureau of Reclamation. In 1946 the Board of Water Commissioners started tunnel driving on a limited scale from the east (outlet) portal and by 1955 had completed 9986 ft of tunnel. An urgent need for additional sources of water supply required acceleration of the tunneling operation, and, in 1955, Tipton and Kalmbach Inc. of Denver were assigned the responsibility of reviewing the project and preparing plans and specifications for the tunnel and appurtenant features. Additional geologic studies were made, and the geology of several possible alternate tunnel lines were compared before determining that the tunnel should be driven along the course previously adopted by the Board of Water Commissioners. On July 12, 1956, a contract for construction was awarded to Blue River Constructors Inc., a combine

Jan 1, 1962

By R. J. Stokes

S. Floreen (international Nickel Co.)— One fairly simple way to differentiate between em brittle me nt due to surface microcracks or due to a dislocation barrier effect might be to load a brittle rock salt crystal in tension to some stress just below the fracture stress and then immerse the loaded crystal in water. If a surface film is retarding plastic flow then one should observe some plastic deformation of the rock salt as

Jan 1, 1962

By H. R. Peiffer

Hardening of soft metals can be accomplished by dispersing finely divided hard particles in them. The dispersing of finely divided alumina in silver in the presence of oxygen yields a high strength material which is unusual in that its mechanical properties above the melting point of the continuous Ag-O alloy matrix are similar to other solids. The tensile strength is studied for two of these alloys, one of which contains 15 pct by weight alumina and the other 20 pct by weight alumina. The average fracture strengths above 960°C of these alloys were found to be 0.4 x106 dynes per sq cm and 3.8x106 dynes per sq cm respectively. The strengths appenred to be independent of temperature above 960° C. The creep behavior of the 20 pct alumina material was studied above 960°C. The initial creep rate, 6 , of this material can be represented by where s is the applied stress and E the activation energy for the process. This energy is of the order of 1.7 to 2.1 ev. HARDENING of soft metals by the addition of finely divided, hard particles has resulted in the production of materials with excellent creep resistance and with inhibited recrystallization.&apos; It has been demonstrated that such composites have useful strength up to temperatures very near the melting point of the soft metals, but one might expect that the strengthening by the dispersed particles ceases to be of importance above the melting point of the softer phase. This, however, is not so.2 In this paper the strengthening of a liquid Ag-O solution by the presence of dispersed alumina is discussed and experimental data concerning the mechanical properties of such a material at temperatures above 960°C presented. EXPERIMENTAL PROCEDURE Specimens were prepared using powder metallurgical techniques. Finely divided silver oxide was mixed in the appropriate proportions with "Linde B" alumina. For these experiments the specimens contained 15 or 20 wt pct alumina in pure silver.* These alloys were used in these experiments since they were the ones that could be handled readily enough to yield experimental data. Silver oxide was used in preference to silver because it is readily available in a very finely divided form and because the presence of excess oxygen in the silver is important to the properties2 of the material. The powders were mixed wet, using alcohol as the medium, in an ordinary food blender until a uniform mixture was obtained. They were then dried and heated to reduce the silver oxide to silver. Only a fraction of the finely divided silver remains unoxi-dized upon removal from the oven since the finest particles of silver oxidize immediately upon contact with air. The remaining fine silver served as a binder during pressing. The mixture was then pressed at 20 tons per sq in. into shoulder-grip (reduced section 1/4 in. by l/4 in. by 1 1/4 in.) and rectangular bar specimens (l/4 in. by 1/4 in. by 2 in.). The green specimens were heated very rapidly in a globar furnace to 1000°C, held at temperature untic they had reached theoretical density and then furnace cooled. The strength of the two compositions at temperatures above 960 °C was determined by pulling shoulder grip specimens inside a furnace mounted on a tensile machine. Specimens were gripped by means of wires wrapped around the shoulders of the specimen. Temperatures were measured by means of a chro-mel-alumel thermo-couple placed in the vicinity of the specimen. Control of temperature (within ±°15C) was accomplished by means of a Weston Recorder-Controller. Before loading, specimens were held at temperature for approximately 15 min in order to insure uniform specimen temperature. The low loads were measured by a special load cell designed by Baldwin Lima Hamilton. All testing was performed on a FGT testing machine of the same com-pany. Creep studies were performed in bending utilizing rectangular specimens of the 20 pct alumina alloy. Specimens supported at both ends by knife edges of inconel were placed in a globar furnace, heated quickly to temperature, and the deflection of the beam measured optically as a function of time. The weight and size of the specimen were predetermined and the maximum stress on the beam calculated from

Jan 1, 1962

By O. N. Carlson, A. L. Eustice

The tensile properties of iodide vanadium were determined as a function of hydrogen concentration. It was shown that the presence of 10 ppm H is sufficient to cause embrittlement of vanadzum over a limited temperature range. The temperature of the observed ductility mininlum is approximately -l00°C, this being a function of strain rate and hydrogen concentration. The yield stress of hydrogenated vanadium is raised sharply in the brittle temperature range. THE present investigation was initiated to determine the effect of hydrogen on the tensile properties of high-purity vanadium as a function of temperature and the role of hydrogen in the brittle-ductile transition. Loomis and Carlson&apos; reported a change from ductile to brittle behavior in iodide vanadium at -110°C with a return of ductility at temperatures below -140°C. Vanadium wire containing 270 pprn of hydrogen was brittle at room temperature while wire containing 100 ppm was ductile under the same conditions. Roberts and Rogers&apos; reported a ductile-brittle-ductile fracture sequence in vanadium containing 400 to 600 ppm of hydrogen. Their data show that hydrogenated vanadium is ductile at 150"C, brittle at room temperature and ductile again at -196°C. Magnusson and Baldwin found a minimum in ductility in vanadium containing 80 ppm hydrogen from tensile tests performed at several strain rates. Information available on the vanadium-hydrogen equilibrium system4 is somewhat incomplete. The absorption of hydrogen is exothermic in accordance with the decline in solubility with rising temperature. The limit of solid solubility at temperatures below 400°C has not been determined due to the difficulties in obtaining equilibrium at these temperatures. Data on the hydrides of vanadium are rather limited. Roberts6 studied the structure of VD,., by neutron diffraction, and observed the ordering of the deuterium atoms below -65°C into a primitive cubic cell with a lattice constant about twice that of the disordered bcc vanadium solid solution. EXPERIMENTAL PROCEDURE Vanadium of 99.9 pct purity was prepared by the iodide refining process6 for use in this investigation. This vanadium contained the following analyzed impurities; <20 pprn calcium, 150 ppm carbon, 200 ppm chromium, 30 ppm copper, 10 ppm hydrogen, 200 ppm iron, <20 ppm magnesium, <20 ppm nickel, <5 ppm nitrogen, 150 ppm oxygen, <50 ppm silicon, and <20 ppm titanium. specimen Preparation—Tensile specimens were machined from swaged rods of iodide vanadium. The

Jan 1, 1962

By A. H. Daane, R. L. Myklebust

The yttrium-manganese system has been investigated by thermal, metallographic, and X-ray diffraction methods. There are three intermetallic compounds present: YMn2 which melts congruently, YMn4, which undergoes syntectic decomposition, and YMn,, which undergoes peritectic decomposition. The compound YMn4 is ferromagnetic at room temperature with a Curie temperature of 214°C. There are eutectics at 25.2, 60.9, and 82.0 wt pct Mn which melt at 878°, 1100°, and 1075°C, respectively. Crys-tallographic data are given for YMn4, and YMn12 . The terminal solid solubilities are low. In a general program of study of yttrium metal in this laboratory some alloy systems of this metal with elements of the first transition period have been examined. This work was originally instigated by experiences in cladding yttrium with jackets of some protective metals such as Inconel for high-temperature service in air.&apos; In some cases a low-melting phase was observed to form between the Inconel and the yttrium resulting in failure of the samples. In characterizing this reaction, a survey was made of the systems of yttrium with chromium, manganese, iron and nickel,, and it was found that a eutectic was formed between these metals and yttrium on the yttrium-rich side of the system. This present study of the Y-Mn system was carried out to examine in more detail the alloying nature of yttrium, and to correlate trends that have been observed in previous related studies. It was observed by Voge13 that in the systems of lanthanum, cerium, and praseodymium with each of the metals in the first transition series, the tendency to form compounds diminished in the order nickel, cobalt, and iron while no compounds were formed with manganese, chromium, or titanium. Beaudry and Daane4 observed a similar behavior in the systems of yttrium with some members of the first transition series except that the tendency for compound formation was greater. Both the Y-Ti5 and Y-Cra systems consist of simple eutectics, while in the Y-Fe,7 Y-CO, and Y-Ni4 systems, there are four, eight, and nine compounds, respectively. In addition to the above trends, the similar atomic radii and electronegativities of yttrium and thorium invite a comparison between their alloying behaviors with a common element such as manganese. In crys- tallographic studies, Florio et al.&apos; have identified three intermediate phases in this system which are ThMn2, Th6Mn23, and ThMn,,. Gschneidner and Waber10 have examined published information on alloy systems of the rare-earth metals and have correlated this information with current alloying theory. From their study, they predicted that the Y-Mn system would contain one intermetallic compound. On the basis of this prediction, the trend in the alloying behavior of yttrium with the elements of the first transition series and the alloying behavior of thorium with manganese, one might expect from one to three intermetallic compounds to form in the Y-Mn system. A consideration of Hume-Rothery&apos;s rules of alloying based on size-factor, electronegativity, and valency suggested a small terminal solubility and possible compound formation. The present study was undertaken to confirm these predictions of low terminal solid solubility and compound formation and to establish the general alloying behavior of yttrium with manganese. EXPERIMENTAL Materials. The manganese used in this investigation was obtained from the Foote Mineral Co. as electrolytic plates of 99.9 pct stated purity; the yttrium metal was prepared in this laboratory. Table I gives the analyses of these materials. For the solubility studies at the yttrium-rich end of the alloy system, distilled yttrium, whose major impurity was 200 ppm Ti, was used. Preparation of Alloys. The alloys were formed by comelting the two metals in an are-melting furnace under an atmosphere of argon. The buttons thus formed were inverted and remelted three to five times to promote homogeneity. Due to the high vapor pressure of manganese, it was assumed that the weight lost during are-melting was all manganese. This assumption was based on the very good agreement observed between calculated compositions and chemical analyses of several alloys. The compositions of the dilute alloys used for solid solu-

Jan 1, 1962

By M. G. Benz, J. F. Elliott

A. J. Goldak and J. Gordon Parr (U)iuersity of Alberta) —Margolin and Ence&apos;s paper reached us only a few days after we had submitted a paper on the structure of Ti2Cu to the AIME. Here, however, we only wish to point out an error in the paper (page 321): "Karlsson has reported the crystal structure of the first intermediate phase occurring in the Ti-rich portion of the Ti-Cu system to be face-centered tetragonal." Karlsson actually reported the structure of Ti3Cu (i.e., "the first intermediate phase") to be primitive tetragonal with four atoms per lattice point: Cu at 0, 0, 0; and Ti at 1/2, 1/2, 0; 0, 1/2, 1/2; and 1/2, 0, 1/2. Thus, Karlsson suggests a primitive lattice with an ordered arrangement of atoms located at corners and face-centers: Ence and Margolin suggest a random body-centered tetragonal structure—-with which our results agree. E. Ence and H. Margolin (authors&apos; reply)— We do not agree that Karlsson has not reported the structure of Ti3Cu as face-centered tetragonal. The fact that Cu atoms are located at the corners and titanium at the face-centers does not indicate that the lattice is not face-centered. We are pleased that the discussers&apos; results agree with our own.

Jan 1, 1962

By G. R. Frank, R. E. Willett, E. H. Hollingsworth

The most generally accepted equilibrium diagram for A1-Fe alloys has a eutectic system on the aluminum side with an essentially insoluble constituent of the formula, FeAl,, as the second phase. In 1938, Bradley and Taylor1 did report a phase change of FeAl,, but this change has never been confirmed. According to them, FeA1, is the stable phase only at higher temperatures; at lower temperatures, it is converted into Fe2Al7 and aluminum. It has now been found that there is, in fact, a phase change of the Al-Fe constituent on the aluminum side of the equilibrium diagram. This change, however, is not the one reported by Bradley and Taylor. The alloys used were cast by continuous processes and had these analyses: Fe - 1.98 to 2.02 pct, Cu-0.01 pct, Si - 0.01 pct, Mn - 0.01 pct, Mg - 0.00 pct, Zn - 0.00 to 0.01 pct, Cr - 0.00 pet, Ti - 0.00 to 0.04 pct. The constituent in these alloys was identified by X-ray analysis with a Guinier camera and by chemical and X-ray powder diffraction analyses. Two procedures were used to separate constituent for the last two analyses. In one procedure, it was separated by treating a sample with a solution of methanol saturated with iodine. And in the other procedure, it was separated by first applying, at 12 amp per sq ft in 15 pct sulfuric acid at 70°F, an oxide coating to a sample, and then dissolving this coating in a solution of 35 ml of 85 pct H3PO4 and 20 g of CrO3 per liter. Several observations directed attention to a phase change of the A1-Fe constituent. Differences that appeared too great to be accounted for by micro-structure alone were found in the voltages required to apply the same thickness of an oxide coating to products from rapidly and slowly chilled ingot. Even more striking was the difference in appearance of the coatings themselves. One applied to a product from a rapidly chilled ingot was dark gray in appearance, in fact, almost black, while one applied to a product from a slowly chilled ingot was essentially white. Also, even a short period of thermal treatment at an elevated temperature of products from rapidly chilled ingot led to the same anodizing behavior as that of products from slowly chilled in-

Jan 1, 1962

By Robert L. Dean, Michael Hoch, Samuel M. Wolosin, Chung K. Hwu

The general shape of the 1450°C isotherm of the Ti-TiO-ZrO2-Zr region was evaluated from the surrounding binary phase diagrams and from thermo-dynamic data on the metal-oxygen binaries. The phase boundaries were accurately determined using X-ray and metallographic techniques. At 1450°C the system shows a large bcc ß field, which extends from the two metal-oxygen binary systems as a Gaussian error function, and is stable up to 30 at. pct 0 when Ti and Zr are present in equal amounts. At higher O Concentrations, the ß field is in equilibrium with t-ZrO . The following four regions, with three solid phases, are present: two a ß t-ZrO,, a TW t-ZrO,, and TiO t-ZrO2 c-ZrO2. On cooling the ß phase transforms into the a phase, going through the w transition phase. The isotherm at 1500°C for the region TiO-TiO,-ZrO, was obtained by using X-ray diffraction. At 1500°C a large c-ZrOz region is present as well as a large two-phase field, Ti0 c-ZrO,. The following regions, with three solid phases in equilibrium, were found These regions are relatively small. The solidus and liquidus relationships were determined by observing samples suspended in a tungsten crucible by means of a fine tungsten wire and heated in vacuum. Eleven univariant points were found. C-ZrO, decomposes through a peritectic reaction into liquid t-ZrO2. The activities of Ti and TiO in the TiO t-ZrOz and in the two a ß t-ZrO regions were measured using the Knudsen effusion method. In the a TiO t-ZrO, region the activities of Ti and Ti are the same, as in the a — Ti TiO binary. In the two a t-ZrO, regions, the Ti activity is high and the Ti0 activity very low, although all phases present contain at least 30 at. pct 0. This indicates a short-range order in the solid phases, Zr atoms being preferentially surrounded by 0. 1 HE system Ti-Zr-0 is of interest because of the wide ranges of solid solubility exhibited by the boundary systems; as titanium and zirconium both belong to the same group of the periodic table, large single-phase regions should occur within the system, with a great variation of properties (as the composition changes within the single-phase region). Furthermore, the possibility of modifying ZrO, to make it a more usable refractory by the addition of other metals makes this system also of interest. Because of the high affinity of titanium and zirconium for oxygen, the oxygen partial pressure is very low at all compositions; thus, there exists a ternary metal-metal-oxygen system in which the oxygen pressure is not an important variable, so long as it is low enough. When a sample is heated in vacuum to a temperature high enough for vaporization to occur, the vapor phase will consist of metal and metal-oxide gas, the oxygen concentration being very low. The phase relationships in the surrounding binary systems have already been reported in the literature; therefore, the study of the ternary diagram

Jan 1, 1962

By F. J. Plecity, J. T. Michalak, W. C. Leslie

W. M. Williams (McGill University)-The authors are to be congratulated on completing this detailed investigation of recrystallization behavior. The present writer has recently completed some research at the University of Toronto on the recrystallization and grain growth behavior of a number of "pure" irons, and he would like to take issue with the authors&apos; contention that recrystallization cannot be followed by means of hardness measurements. Two series of specimens of Ferrovac E, a com- mercially available iron, were annealed to complete recrystallization at 525" and 620" C, measurements being made both of Rockwell hardness and of volume percent recrystallized as a function of annealing time. Good correlation was found between these two quantities and, following the earlier practice of Cook and Richards for copper, hardness measurements were used in an extensive investigation of recrystallization. No anomalous behavior was observed as a result of this practice. Specimens which showed complete softening always showed, (metallographically and by X-rays), completely re-crystallized structures. These observations do not, of course, detract in the least from the results of the work under discus-

Jan 1, 1962

By S. R. Goodman, Hsun Hu, R. S. Cline

The quenching technique has been used to study phase relations in the composition area 2FeO.SiO2-FeO-SiO2-MnO.Si02-ZMnO.SiO2 of the system iron oxide-manganese oxide-silica under strongly reducing conditions such as exist in a gas mixture consisting of equul parts of carbon dioxide and hydrogen. Liquidus and solidus temperatures of most mixtures in the composition area studied are in the range of 1173° to 1345°C. EQUILIBRIUM relations existing among the oxides of iron, manganese, and silicon are of particular interest in two areas of steelmaking: slags and ingot inclusions. Mixtures of these oxides represent about 90 pct of the slag in the acid steelmaking process, and so dominate the chemistry of the whole refining process. These constituents also play an important role in the early slags existing at the time of the "lime boil" in the basic open hearth process. If these slags are liquid, they "wet" the lumps of lime rising from the bottom of the bath, and react with them. A liquid slag rich in CaO is then formed at the very beginning of the refining. Because the temperature is still low, all conditions for a good dephosphoriza-tion are fulfilled at this stage of the operation. Metal deoxidized with ferromanganese or silico-manganese is likely to contain, as inclusions, phases made up from among the oxides of iron, manganese, and silicon. A knowledge of stability relations existing among the phases present in this system, therefore, enables one to predict the hardness of the inclusions encountered. Moreover, because the shape of the inclusions in steel has a profound influence on the physical properties of the metal, it is important to establish whether or not the oxidic material is present as liquid or crystalline phases during heating and rolling of the steel (-1150 to 1350°C). A knowledge of melting relations in synthetic mixtures of iron oxide, manganese oxide, and silica will give a clue to these problems. Methods for determining such relations and the results obtained are described iln this paper. I) PREVIOUS WORK A number cf previous studies have dealt with the three "binary"* systems bounding the system iron oxide-mangar,.ese oxide-silica. The system iron oxide-silica was studied by Bowen and shairerl in 1932. Their data were obtained by equilibration of mixtures in contact with metallic iron. Phase relations for the system iron oxide-silica ill atmospheres of different oxygen pressures car1 be derived from data on the system FeO-Fe2O3-SiO2 as determined by Muan.2 The diagram shown iri Fig. l is a section of this system in an atmosphere of CO2 and H2 in ratio 1:l. The system manganese oxide-silica has also been the subject of several investigations. Most of the early studies suffered from a lack of proper control of the atmosphere under which the equilibrations were carried mt. Phase diagrams for the system at two well defined levels of oxygen pressures have been determined recently. Glasser3 determined stability relations in an atmosphere consisting of carbon dioxide and hydrogen in ratio 5:1, diagram Fig. 2, and Muan4 studied phase relations in the system in air.

Jan 1, 1962

By Alex Boozenny

The results of potential measurements between 1) a titaniurn electrode in NaCl-TiCl, melts and a graphite-cizlorine reference electrode and 2) a titanium electrode in NaC1-Nu "melts and a graphite-chlorine reference electrode show that the following relationship expresses the equilibrium relationship between the TiCl, and the dissolved metallic sodium concentrations, expressed in mole fraction units, in dilute NaCl welts at 850°C. The results of potential measurenments between a graphite electrode in NaCl-TiCl, melts that were saturated with TiCl, and a graphite-chlorine reference electrode, when combined with the standard free energy data given in literature, gave the following expression for the equilibrium relationship between the TiCl, and TiCl, concentrations, expressed in mole fraction units, in dilute NaCl melts at 850°C. These relationships are for melts in equilibrium with pure titanium. In impure systems, less sodiurn and more TiCI, can be copresent with a given concentration of TiCl,. AFTER 10 years of existence, the titanium metal industry still relies on the original Kroll and the sodium reduction processes for the only important means of converting titanium-bearing ores to titanium metal via production of titanium tetrachloride as an intermediate. Through years of modification and development these two processes have evolved to a point where any further major economic advances in the field of titanium metal production must be achieved through implementation of processes which are distinct departures from simple magnesium or sodium reduction of titanium tetrachloride. Concurrently with the refinement of the Kroll and sodium reduction processes, industries and government have sponsored research and development in the field of producing titanium by electrolysis of oxides,&apos; carbides,&apos; and halides3&apos;4 in fused salt media. However, the incomplete understanding of the physical chemistry of fused salt systems has in many cases hindered the development of promising new titanium production processes to the point where they will have a clear advantage over the processes presently employed. Fortunately the volume of information on fused salt physical and electrochemistry is increasing at an accelerating pace. The first approaches tbward investigating the electrochemical behavior of fused salt systems have been the measurements of equilibrium potentials of metals immersed in melts containing their halides.&apos; Some work on the kinetics of fused salt electrochemical processes has been reported.&apos;09" Some descriptions of the structural composition of fused salt systems are also available. The work described herein is a continuation of the study of metal electrode potentials in fused salts. Specifically, this contribution to the growing store of fused salt chemistry information presents a description of the equilibrium relationships between the concentrations of titanium dichloride, titanium trichloride, and metallic sodium in fused sodium chloride. The investigation of the titanium dichloride-titanium trichloride equilibrium relationships is not completely new. Kellog and Krye and Melgren and opie15 have presented the results of chemical analysis of salts containing titanium chlorides. Flengas and lngrahaml&apos; have published the results of an investigation of these equilibrium relationships obtained by measurement of electrode potentials in a fused NaCl-KC1 mixture. The investigation described herein differed from that of Flengas and Ingraham principally in the use of straight NaCl as the solvent in place of the more costly and more difficult to purify mixture. This investigation was conducted in three parts. First, the equilibrium potentials of titanium in sodium chloride containing known concentrations of titanium dichloride were measured. A graphite-chlorine electrode was employed as reference. Second, the equilibrium potentials of titanium immersed in sodium chloride containing known concentrations of elemental sodium were measured. Third, the equilibrium potentials of graphite immersed in titanium tetrachloride-saturated sodium chloride containing known concentrations of titanium trichloride were measured. The results of these three related investigations are presented in the above order. The results are combined with the thermodynamic properties of titanium chlorides and sodium chloride, obtained from literature, to give the titanium dichloride-titanium trichloride-elemental sodium equilibrium concentration relationships. In the test, whenever a melt contains titanium chlorides in predominantly divalent form, the melt

Jan 1, 1962

By Hsun Hu, R. S. Cline

A detailed studj) of texture formation in 2 pet Al-Fe single crystals with initial orientations of approximately (111) [112], (112) [111], and (112) [111] was made by examining the textures developed on the surface and at various interior sections of the crystal after rolling to various amounts. Depending&apos; upon the initial orientation of the crystal, the surface and interior textures may differ only in sharpness, or may differ essentially in orientation. The orientation of the (111) [112] crystal does not change upon rolling up to 70 pet, but after rolling more than 90 pet a distinct component of (001) (110] orientation is developed. The texture formed in the two (112) (1111 type crystals consists of (111) (1121 and (001) (1101 components. The latter, however, is largely confined to the surface layers. The textures formed on both sides of the crystal are identical, and the texture composition profile is approximately symmetrical with respect to the central section of the strip thickness. The formation of these texture components is analyzed. DURING the past seven or eight years, deformation and recrystallization textures in rolled Si-Fe single crystals have been extensively studied by various investigators.1-7 From these studies, much knowledge on texture formation in bee crystals of various initial orientations was obtained. However, these results also raised many questions, regarding particularly the correlation between deformation and recrystallization textures, as well as the deformation texture itself of some particular crystals. To take a (111) [112] type crystal as an example, it was shown by Dunn and Koh2, 3 that this orientation does not change during deformation by rolling. This finding is consistent with the conclusion reached by Barrett and Leven-son8 with respect to iron crystals that (111) [112] is one of the stable end orientations. However, different recrystallization textures were observed by Dunn and Koh3 in (111) [112] type crystals of different initial thickness, which widened differently during rolling even though their deformation textures were identical. Another interesting example, also from the results of Dunn and Koh2&apos;3 is that of texture formation in a (112) [111] crystal. This crystal developed a two-component deformation texture of (111) [112] plus (001) [110]. Its recrystallization texture, however, was found to be predominantly (110) [001], which is related to the (111) [112] component by a simple [110] rotation. This crystal, therefore, behaved as if the other deformation texture component, (001) [110], were not present. There are also discrepancies among the results of different investigators, as well as numerous unexplained fine features of the deformation texture of crystals of various initial orientations. In order to have a better understanding of all of these points, a detailed study of deformation textures is greatly needed. One of the obvious things that has been completely overlooked in previous texture studies is the possible effect of surface texture. All past work on the texture of Si-Fe single crystals was conducted in a rather simple manner, i.e., the rolled crystals were etched to a very thin sheet; then their textures were examined by transmission X-ray techniques. For recrystallization texture studies, unless precautions are taken by etching off a sufficient amount of the surface layer before annealing, the texture developed in the interior may be affected by the surface layer, which may well have a different initial texture and which may have undergone recrystallization earlier than the interior of the specimen. Because of this effect, it is now planned to reexamine the texture of various rolled and annealed single crystals at the surface, and at various sections below the surface by using reflection techniques. In some cases, both surfaces of the rolled crystal will be examined. In one of Dunn&apos;s early papers,9 he noted that at an early stage of rolling the crystal seems to divide roughly through the middle to become a sample which in effect consists of two layers having some what different orientations. This effect has never been further explored. The investigation described in the present paper constitutes the beginning of a series of thorough investigations of texture formation in deformed bee single crystals designed to clear up some of the uncertainties which have been discussed. We have chosen a high-purity 2 pet Al-Fe alloy for this investigation. It is known that the allotropic transformation of iron is eliminated by alloying with approximately 1petAl. Such an alloy, being very similar to silicon ferrite, can be heated to the solidus temperature without phase transformation. One reason for choosing A1-Fe instead of Si-Fe for the present investigation is that we have been able to make single crystals of a vacuum-melted high-purity A1-Fe alloy by the strain-anneal method without much difficulty, but were not successful in doing so with a vacuum-melted high-purity Si-Fe alloy. For many research purposes,

Jan 1, 1962

By M. T. Hepworth, R. Schuhmann

Hydrogen solubility measurements were made on a series of Ti-O alloys, and a portion of the 800°C isotherm for the Ti-O-H system was determined. Activities of oxygen and titanium were calculated from the experimentally measured activities of hydrogen, using ternary Gibbs-Duhem integrations. The data were extrapolated to obtain thermo-dynamic properties of binary Ti-O solutions. The thermodynamic properties of a Ti-0 solid solutions thus determined were compared with properties predicted from interstitial models. The Gibbs-Duhem equation, long used to calculate activities in binary systems, has been extended. recently to ternary systems.1"3 When the activity of one component in a ternary system is known as a function of composition, the activities of the other two components can be calculated from that of the first by an integration procedure, provided certain restrictions are observed on the path of integration. Often the activity of one component in a ternary system can be measured readily, while the activities of the other two components are difficult to measure. Gibbs-Duhem calculations are especially applicable to such systems. The further possibility arises of developing a new and indirect approach to activity measurement in binary systems. The proposed new method for binary systems consists of adding varying amounts of a third component whose thermodynamic behavior is easily measured. The activity of this added component is determined experimentally as a function of composition. Then the activities of the two components of the original binary system are calculated by Gibbs-Duhem integrations and extrapolations. For the work to be described in this paper, the Ti-0-H system was selected as a promising system for evaluating this approach. Investigations of the Ti-H system have shown that the activity of hydrogen can be measured precisely with little difficulty. Pure titanium transforms from a low-temperature a form (hcp) to a higher-temperature /3 firm (bcc) at 882.5"~ The phase transformation occurs in a temperature range where hydrogen pressures are easily measured. Also, the diffusivity of hydrogen at temperatures above 600" or 700"~ is large enough that equilibrium can be reached within a reasonable time.

Jan 1, 1962

By M. T. Hepworth, W. B. Sample

HYDROGEN solubility and linear contraction measurements were made at constant temperature on an alloy of titanium of constant oxygen-to-titanium molal ratio but variable hydrogen content. A cylindrical specimen of titanium (0.25 by 1.6 in.) containing 0.75 at. pct 0 and less than 0.03 at. pct N was cast from a master button of iodide process titanium which had been alloyed with titanium dioxide. Four vacuum fusion analyses, which were made along the length of the cylinder after the hydrogen solubility studies were made, revealed a variation of oxygen content of less than 0.02 at. pct. The specimen was introduced into a quartz furnace tube, annealed and outgassedat 1050"~ for about 1 hr, and then held at 800" * 0.5" for about 30 hr, during which latter time experimental data were taken. The leak rate to the furnace chamber was not sufficient to contaminate the specimen during the run as determined by leak-rate studies and vacuum fusion analyses for oxygen and nitrogen before and after the runs. The furnace chamber was attached to a modified Sieverts apparatus used to introduce measured quantities of purified hydrogen to the specimen. A quartz pushrod transmitted changes in length of the specimen to a Chevenard dilatometer. The push-rod passed through a vacuum grease seal to the dilatometer which amplified motion of the rod by a factor of 319. During hydrogen addition, the pushrod did not contact the specimen. Measured quantities of hydrogen were added to the specimen and equilibrium hydrogen pressures recorded as a function of hydrogen content. The solubility data, which appear in Fig. 1, agree well with a separate investigation made with a different apparatus. The solubility limit of the hcp a phase appears as an abrupt discontinuity in slope at 3.4 at. pct H. The solubility plot has been extended as a dashed line at this discontinuity in order to emphasize the discontinuity. The hydrogen content at which bcc P appears is not clearly defined. An arrow indicates solubility data were taken upon hydrogen addition. Upon reaching the arbitrary maximum hydrogen content of the run, the quartz pushrod was pressed against the specimen in order to record the change in length with hydrogen removal. A pressure of about 100 g per sq cm was required to overcome the friction of the vacuum seal in order to obtain reproducible linear contraction data. The contraction ratio ~2/1", change in length divided by original length, was set equal to zero for the maximum hydrogen content. The relative contraction of the specimen was observed upon removal of hydrogen in the following manner. The system was opened to the pumps for a few seconds and an unknown quantity of hydrogen was removed. The system was then isolated from the pumps by closing a stopcock and allowed to return to equilibrium. When the temperature returned to 800°C, the pressure stabilized, and contraction ceased, measurements of contraction and pressure were made. The hydrogen content of the specimen was then deduced by measuring the equilibrium PIydrogen pressure and referring to the solubility plot. Linear contraction was then plotted against interpolated values of atomic percent hydrogen. The justification for this procedure is the established reversibility of the hydrogen equilibrium.&apos; Uniaxial compression was assumed to have no effect on hydrogen pressure. The isothermal linear contraction data are plotted on Fig. 1. An arrow indicates data were taken upon removal of hydrogen. The solubility limits of the two phase a i /3 region can be identified by discontinuities ill slope of the dilatometric plot at 9.1 and 3.4 at. pct H, agreeing well with other studies.&apos; Dashed extensions of the plots emphasize the discontinuities. Isothermal studies of expansion made upon hydrogen addition gave curves of much smaller slope and less pronounced discontinuities. A uniaxial compressive stress tends to accentuate volume changes in going from the more open bcc phase to the hcp phase.2 Incomplete data on ex-

Jan 1, 1962

By R. W. Fountain, W. D. Forgeng, G. M. Faulring

Precipitation of the phase Co3Ti (Cu3Au type) from a Co-5 pct Ti a11oy has been investigated using single-crystal X-ray diffraction techniques. Oscillation and transmission Laue patterns of specimens aged for short-time periods at 600" C indicate the formation of titanium-rich and titanium-poor zones coherent with the {100} matrix planes. Longer aging times at 600° C establish that the equilibrium phase also forms on the {100} matrix planes as platelets. These observations are corroborated by electron metallography; electron diffraction studies show the phase Co3Ti to be ordered. A probable sequence of the precipitation reaction is discussed. A previous publication by two of the present authors reported on the phase relations and precipitation in Co-Ti alloys containing up to 30 pct Ti.1 The results of this investigation established the existence of a new face-centered cubic inter metallic phase, ranging in composition from about 17.0 to 21.7 pct Ti at temperatures below 1000° C The decomposition of the fcc supersaturated solid solution was studied employing hardness and electrical resistivity measurements. The changes in hardness upon precipitation in alloys containing 3, 6, and 9 pct* Ti were found to be associated with an initial increase in hardness followed by a plateau and then a second, more pronounced hardness increase. Investigation of this behavior by electrical resistivity measurements suggested that two different kinetic processes were involved, which, when interpreted in terms of the kinetic relation,2-4 indicated that initial precipitation was in the form of thin plates. On continued aging, the plates impinged during the growth process. The general features of these findings have been confirmed by Bibring and Manenc,5 while, in addition, they report the phase to be ordered. The present investigation was undertaken to provide more definite information on the structural relationships between the precipitate and the matrix. EXPERIMENTAL PROCEDURE Single crystals of a (20-5 pct Ti alloy were prepared from the melt employing the Bridgman technique. Poly crystalline rod, 1/2 in. in diam, prepared from vacuum-melted material, was machined to 3/8- in. diam to remove any surface contamination that may have resulted from hot-working. The crystals were grown under a purified hydrogen atmosphere in high-purity alumina crucibles heated by induction. Considerable difficulty was encountered in attempting to grow monocrystals because of the high melting point of the alloy and the high solute concentration. However, one crystal about 6 in. long was obtained which was essentially a single crystal except for one or two very small grains around the periphery. The as-grown crystal was solution heat-treated for 24 hr at 1200°Cin a purified argon atmosphere and water-quenched. One-quarter-in. slices were taken from each end of the solution heat-treated crystal for chemical analyses, and the remainder of the crystal was mounted and oriented by the back reflection Laue Method. The chemical analysis of the crystal was as follows: Pct Ti Pct 0 Pct C Pct N Pct H Pet CO 5.29 0.08 0.004 0.002 0.0003 Balance By proper tilting of the crystal, it was possible to obtain slices 1/32 in. thick of [loo] and [110] orientation. The solution heat-treated crystal slices were sealed in silica capsules for the aging treatments, with titanium sponge placed at one end of the capsule to act as a getter. All slices were water-quenched from the aging temperatures, the capsules being broken under the water to ensure a rapid quench. Thinning of the slices for transmission X-ray studies was accomplished by a combination of mechanical and electrolytic techniques, the final thickness being about 0.1 mm. Laue patterns of the solution heat-treated crystal indicated that no strain was introduced by the thinning technique. ELECTRON METALLOGRAPHY After X-ray examination, the structural changes attending the precipitation were followed by examination of direct carbon replicas of polished and etched surfaces of the single-crystal slices and extracted phases. The earliest indication of significant structural change was observed after aging at 600°C The structure of a heavily etched, solution-treated crystal is shown in Fig. l(a). Aside from the etch pit pattern, no regularity of background structure is observed. On the other hand, in the background of the specimen heated for 500 hr at 600°C, the etching pattern shows a directionality indicating the influence of minute precipitate particles, Fig. l(b). On electrolytic dissolution of this specimen in 10 pct HC1 in alcohol, a large volume of very small, flattened cubes

Jan 1, 1962

By R. W. Heckel

A method is described whereby the relationship of both the "at-pressure" powder compact density and the "zero-pressure" compact density to the applied pressure may be obtained from continuous measurements of punch movement during a single compaction operation. The rate of density increase with applied pressure for the metal powders is found to be proportional to the volume fraction of pores for pressures exceeding a lower limit which varies from 15,000 to 30,000 psi, depending on the powder. 1 HE compaction of powdered materials is carried out primarily to increase the density of the material. If the ultimate goal of the over-all process is the attainment of minimum porosity, compaction is responsible for most of the densification. For example, loose powdered metals have porosities of about 65 to 75 pct. Axial loading in a die or hydrostatic pressure may effectively reduce the porosity of most powders to 20 pct or lower with pressures of 50,000 psi and greater. The relationship between the density of a powder compact and the pressure needed to achieve that density is most commonly obtained by pressing several compacts, each at a different pressure. Measurement of the densities of the individual compacts when they are removed from the die then provides the density-pressure relationship. However, this method suffers from several disadvantages. Because a large number of compacts and pressing operations are required, it is inherently slow. Furthermore, since density measurements are made after the specimens are removed from the die, data obtained refer only to pressures greater than those necessary to form a coherent compact. The third disadvantage is the inability of this method to provide information about the compact density at the applied pressure in the die. Because the determination of density-pressure relationships has been a slow, tedious process, investigators have sought to express the compaction behavior of powders by other means. The general terms "comparability" and L&apos;compressibility" have been used to rank powders qualitatively according to their compaction characteristics. To restore a quantitative nature to the subject and to prevent confusion, Schwarzkopf1 has proposed that compac-tibility be defined as the minimum pressure needed to produce a given green strength, while compressibility should be used to indicate the extent to which the density of a powder is increased by a given pressure. Probably the most widely used of the compaction parameters is the "compression ratio,&apos;&apos; which is generally defined as the ratio of the compact density obtained by pressing at a given pressure to the apparent density of the loose powder.2 However, the description of the compaction behavior of a powder by these parameters provides only limited information about the process because of their applicability to just one specific condition such as a given green strength or a given pressure. The method of obtaining density-pressure relationships which will be described in the present paper was designed to eliminate the shortcomings of the previous techniques while maintaining equivalent accuracy and precision. EXPERIMENTAL TECHNIQUES The general principle employed makes use of the fact that the linear movement of the punch during a

Jan 1, 1962

By J. C. Uy, A. A. Burr

IN the primary solid solutions of zirconium-base alloys, there is a striking regularity of the effect of solute valence on the stabilization of the allotropic phases.1 The valences derived by pauling2 are for elements as they are bonded in the solid metallic state. Effects of variations in isotopes, alloying elements, and allotropes on their valences are difficult to determine and such data are presently unavailable. Pauling&apos;s values are somewhat empirical and approximate, but if some definite correlations can be found between those values and experimental observations, this will lend support to the tacit assumption that the possible variations in valence mentioned above are small. Pauling has amassed a large amount of evidence of such correlations. It is the purpose of this technical note to show another application of the Pauling valences and to offer a possible explanation for this observation. The relationship between the Pauling metallic valence of the solute and the stabilization of allotropic phases in zirconium is shown in Table I, which has been compiled from available data in the literature3 plus the results of work done at Rens-selaer Polvtechnic Institute.&apos; The chemical valences are included for comparison. It can be seen that a solute whose metallic valence is lower than that of the solvent tends to stabilize the a phase while one whose metallic valence is higher than that of the solvent tends to stabilize the 0 phase. It should be noted that, inasmuch as the Pauling valences are periodic with atomic number, this is tantamount to saying that the elements in groups I-A, 11-A, III-A, III-B, IV-B, V-B, and VI-B are a stabilizers while those in groups IV-A, V-A, VI-A, VII-A, VIII-A, I-B, and 11-B are ß stabilizers. The chemical valences do not show such consistency. Although the zirconium-rich end of the Zr-Au diagram is not available, it call be expected that gold, having a metallic valence of 5.56, would stabilize the ß phase. At absolute zero, the Fermi energy level is the criterion of equilibrium, i.e., the structure having the lower Fermi level will be more stable. Conse- quently, allotropic transformation occurs in a metal when thermal excitation raises the Fermi level to a point at which the atoms can be better accomodated by a different structure which yields a lower Fermi level.4-6 Thus in allotropic transformation, a change in structure occurs as a result of the change in the energies of the bonding electrons. Since the Pauling valence is the number of bonding electrons per atom, and these are the only electrons whose energies are affected by thermal excitation,* it can be inferred that the introduction of a solute which has a higher Pauling valence than that of the solvent raises the initial Fermi level; consequently, the transformation temperature is lowered. The converse is also true. The fact that at the transformation temperatures this statement is still fairly valid implies that the contribution due to the difference in specific heat terms of the two allotropes is comparatively small.

Jan 1, 1962