By E. T. Turkdogan, P. Grieveson

It is shown experimentally that, by making use of the coupled S-O reaction in ionic melts, it is possible to transfer slclJur or oxygen from a lozv to a high chemical potential through an ionic nzenzbrane. This uphill transfer of sulfur is accompanied by a counter downhill transfer of oxygen and vice versa. The Materials balance shows that the amoulits of sul -fur and oxygen lost or gained by one system are the same as those gained or lost by the other systenz — the two systejns being separated by an iofzic membmne. The systems used in these experi?nents were solid Mn-MnS-Mno and liquid Fe-S-0. Sufficient results were obtained Lo study the kinetics of the transfer and the indications are that the counter diffusion of sulfide and oxide iojzs in the membrane is the rate controlling process. WHEN an ionic oxide-melt reacts with an atmosphere containing sulfur and oxygen-bear ing gases the following reaction occurs: 1/2 S2 (gas) +O2- (melt) = S2- (melt) + 1/2 0, (gas) [1] Under the restrictions that i) electric conductance in the melt is purely ionic and ii) each constituent element in the melt does not change valence, the solution of an atom of sulfur in the melt will result in the evolution of an atom of oxygen, so that the electric neutrality is maintained. For a given temperature and melt composition, the equilibrium concentration of sulfur in the melt is determined by the ratio, po2 /ps2 , in the gas phase and not by the individual partial pressures of oxygen and sulfur. This has been demonstrated by a number of investigators, for example by Richardson and withers', Fincham and Richardson,la by St Pierre and Chipman,' and by Turkdogan and Darken.3 In his Howe Memorial Lecture for 1961, Darken discussed the possibility of uphill pumping of sulfur through an ionic membrane at the expense of oxygen. TO test the validity of this concept associated with coupled reactions, experiments were carried out in the following manner. A presintered mixture of Mn-MnS-MnO and prefused mixture of Fe-S-0, contained in platinum and iridium crucibles, respectively, and separated by a thin layer of soda-glass (to act as an ionic membrane), were placed side by side in an evacuated silica capsule and sealed. This was then kept at 1400°K for a required time to allow Reaction [11 to occur via the ionic membrane. When partial equilibrium is reached, the ratios Po2 /pS2, for systems on either side of the membrane, are equal and the flux of sulfur and oxygen through the membrane becomes zero, although the individual partial pressures po2 andp,, in these two systems may differ considerably.

Jan 1, 1962

By E. S. Machlin

The alternate processes by which solute atoms can limit the migration of grain boundaries have been considered. At the lowest solute concentrations the controlling process is "mechanical breakaway" in which the solute atoms affect the driving force and not the mobility. In the next higher range of solute concentration, solute atoms are bound to the boundary and diffuse by boundary diffusion along cusps in the boundary developed at the solute atoms. In this region the boundary velocity is controlled by the component in the direction of boundary migration of the rate at which the bound solute atoms can diffuse along the boundary. At still higher concentrations, it is predicted that boundaries break away from the binding solute atoms by thermal activation. The specific behavior Predicted is consistent with the observations of Aust and Rutter. The most striking agreement between prediction and experiment is that obtained for a range of solute concentration in which the boundary velocity is inversely proportional to the cube power of the solute concentration. MaNY models have been devised for the atomic steps in the motion of a grain boundary. McLean1 has listed some of these models and Aust and utter' have evaluated these and other models. If there are

Jan 1, 1962

By T. C. M. Pillay, John Chipman

The Si-0 equilibrium in liquid iron was investigated in some detail by Gokcen and Chipman1 who reported equilibrium constants of the following reactions: In each case the thermodynamic equilibrium constant K was obtained by extrapolating K' to infinite dilution. Their results on reaction [I] were consistent with those of earlier observers, and there seems to be little doubt as to the approximate validity of the equilibrium product determined. On the other hand, the results on reactions [2] and [3] indicated unusual curvilinear relationships between the activity coefficients of silicon and of oxygen and the silicon concentration. Since a linear relation is observed in all other similar instances, it was concluded that some source of error had affected the gas-metal equilibrium relationships. Recently the authors undertook a restudy of these equilibria with the view especially to establishing the equilibrium constant of reaction [2]. Their experiments, however, were discontinued before a tbroughly satisfactory answer had been obtained and consequently have remained unpublished until the present time. Quite recently Matoba, Gunji, and Kuwana2 published the results of a very thorough study of these equilibria. It is the purpose of the present note to Compare these three sets of experimental data, a comparison which leads to Confirmation of the results of Matoba and coworkers. The experimental arrangements described by Dutilloy and Chipman were employed. A controlled mixture of Hz, H,0, and argon was led into the induction furnace over the surface of the Fe-Si melt contained in a silica crucible. On account of the slow approach to equilibrium, runs were continued for at least 8 hr and, in some cases, as much as 12 hr. Samples were taken by means of silica tubes at the start and during the final 4-hr period of each run. Out of twelve runs only seven appeared to have approached equilibrium with sufficient certainty to be reported here. The results of these experiments, all at 1600°c, are shown by the triangles in Fig. 1. Equilibrium was approached from both oxidizing and reducing conditions and the direction of approach is indicated by the shape of the triangle. Attempts to extend the study to higher silicon concentrations were unsuccessful on account of the transfer of silica from the metal bath to the upper portions of the crucible by means of a silicon-monoxide mechanism. Matoba, Gunji, and Kuwana used similar methods and approached equilibrium from both sides. Their results at three temperatures are shown by the solid lines of Fig. 1. A line corresponding to 1600 deg is interpolated from their equations and is shown by the dotted line. The results of Gokcen and Chipman at 1600 deg in the range 0.02 to 2.0 pct Si are also shown. At concentrations up to about 0.6 pct Si, these investigators approached equilibrium from both directions, and their results in this range appear to be trustworthy. Above 1 pct Si, however, all of their experiments involved oxidation only, as shown by a decrease in the silicon content of the bath. It now seems certain that they failed to reach equilibrium at these higher silicon concentrations and that the curvilinear relation shown by their results is incorrect. It is evident that their results in the lower silicon range are in good agreement with those of Matoba and coworkers. In fact, a straight line drawn through their results would parallel the dotted line and would differ from it by only 0.05 in log K. The new data also lie close to that line. It may thus be concluded that the three sets of data are in good agreement and that the equations proposed by Matoba and coworkers for reaction [2] are satisfactory . They take the limiting value of log K', at 0 pct Si as log K ,. The slope of each line gives the value

Jan 1, 1962

By W. L. Phillips

Stress-strain data are reported for sodium chloride, lithium fluoride, and magnesium oxide tested in compression at diffevent strain rates in the telrlperature range from 70° to 873°K. Quantitative equations are given for the stvain-rate dependence of the critical resolved shear stress and the initial rate of work havdening. The properties so determined are compared with results previously reported for metals. ALTHOUGH the effects of strain rate and temperature on the stress-strain characteristics of metals have been extensively investigated1,2 these effects have not been studied in detail in ionic crystals. In the only previous investigations on the effect of strain rate on the deformation of ionic crystals. Gilman and gohnston3 and Hulse and pask4 have shown that the yield stress of lithium fluoride and magnesium oxide at room temperature is proportional to the ninth or tenth root of the strain rate. CRYSTAL PREPARATION Lithium fluoride, sodium chloride. and magnesium oxide single crystals were purchased from the Har-shaw Chemical Co. The compression fixture and sample preparation have been described in detail previously.5 The detectable impurities in MgO were eight parts in 105 of Fe and six parts in 105 of Si; in LiF, six parts in 105 of Mg; and in NaC1, two parts in 105 of Fe and four parts in 10&apos; of Mg. The cleaved samples measured - 0.1 in. by 0.1 in. by 0.3 in. Prior to testing all samples were annealed at -0.8 of their melting point and cooled to room tempera- ture at 50 C per hr.&apos; Samples were strained at rates (<) of 0.1, 0.01, 0.002, and 0.0002 in. per in. per min. EXPERIMENTAL RESULTS Fig. 1 is a plot of the critical resolved shear stress a,. (extrapolation of slope of easy glide region to zero strain) of sodium chloride, lithium fluoride, and magnesium oxide tested at different strain rates as a function of temperature. In all crystals at all strain rates a, decreases with increasing temperature according to an equation of the type397 where uo is a stress constant, K is a constant, and T is the absolute temperature. The points in Fig. 1 are the average of six tests. It is evident that there is a break in the log 0,- temperature plots at a characteristic temperature T,. The constant K of Eq. [I] is dependent on strain rate, Fig. 2. The relationship

Jan 1, 1962

By John Wulff, David A. Stevenson

The solubility of iron and cobalt in liquid lead, the solubility of chromium in liquid tin, and nickel in liquid silver were determined up to 1300°C in an atmosphere of hydrogen. Liquid samples were taken at different temperatures and analyzed. The data obtained were plotted to show the relationship between log mole fraction of solute and the inverse of the absolute temperature. Resulting values for the differential heat of solution (AH) and the excesspartial molar entropy (S)are: for the iron-lead system = _24,200 cal per mole and AT = 5.0 e.u. for the a phase, and AH = 18,300 and S = -0.1 e.u. for the y phase; for the cobalt-lead system AH = 16,500 cal per mole and AS =0.7 e.u.; for the chromium-tin system AH = 15,600 cal per mole and AS = 8.5 e.u.; for the nickel-silver system AH =18,000 cal per mole and AS = 4.0 e.u. RECENT developments in coating, brazing, and heat transfer have focused attention on specific cases of solid-liquid interaction in metal systems, particularly those involving dilute liquid solutions. One fundamental quantity of interest in such systems is the equilibrium phase distribution between solid and liquid phases. In any effort to fully understand such interactions, one must be able to describe the equilibrium state precisely. Furthermore, in order to develop genera! relations for such systems, one must know the equilibrium state in a number of different cases. This investigation was devoted to a study of the equilibrium phase distribution in four binary systems: solid iron-liquid lead; solid cobalt-liquid lead; solid chromium-liquid tin; solid nickel-liquid silver. The iron-lead system was previously studied by Shepard and parkman&apos; and later by Fleischer and Elliott2 with differing results. Both investigations were carried out by sampling the saturated liquid, and analyzing it chemically. The cobalt-lead system was previously reported by Pelzel,3 who noticed no discontinuity near the transformation. A limited investigation of the chromium-tin system was made by Wlodek and wulff4 using a weight loss method. This work was done in conjunction with the development of a process for coating molybdenum with chromium from tin solutions. To more fully under- stand the kinetics of the process, a more accurate determination of a solubility was desirable. No significant data were found in the literature on the nickel-silver system. Data on the latter system were, however, relevant to the investigation of the corrosion kinetics of copper-nickel alloys in liquid silver as carried out by Harrison and wagner,5 EXPERIMENTAL APPARATUS AND PROCEDURE Of the techniques available for the study of such systems the most effective appears to be that of liquid sampling,2,6,7 which is the method used in the present investigation. A schematic diagram of the sampling furnace is given in Fig. 1. Large pieces of solute metal, in excess of saturation solubility, were added to 200 g of the solvent metal, and the entire charge placed in an alundum crucible. Analytical reagent or materials of chemically pure grade were used in all investigations. The crucible was contained in a zircon muffle tube positioned vertically in the uniform hot zone of a Globar resistance furnace. The tube was provided with a number of ports which permitted sampling at temperature and in controlled atmospheres or vacuum; the ports were also useful for evacuation and introduction of gases as well as for thermocouple measurements. A chromel-alumel thermocouple Sheated in a porcelain tube was used for temperature measurements. A purified hydrogen atmosphere was employed in all experiments reported in this paper. The hydrogen was purified by passing it first over hot copper gauze to remove oxygen and then through a molecular sieve immersed in

Jan 1, 1962

By L. F. Mondolfo, B. E. Sundquist

The undercooling associated with the nucleation of the secondary phase from the liquid by the solid primary phase was studied in sixty binary alloys by means of a hot-stage microscope. It was found that in a system of a and ß, a usually nucleates ß at low undercoolings, but ß does not nucleate a, except possibly at undercoolings approaching homogeneous nucleation. This behavior can be explained in terms of relative interfacial energies and shows that crystallographic disregistry is only a minor factor in heterogeneous nucleation from metallic liquids. PREVIOUS experimental work1-6 on nucleation of solids from liquids has shown that normally nucleation is heterogeneous, and that small solid particles present in the liquid are responsible for the nucleation. These experiments and the theory that has evolved from them have made apparent that there is a "characteristic undercooling" associated with the nucleation of the solid from a given liquid by a given impurity. Little is known, however, about the chemical and structural relationships between the nucleating agent and nucleated solid that control the effectiveness of the nucleating agent in catalyzing the nucleation, as measured by the required undercooling. A review of the literature has yielded seventeen undercoolingsL-6 for the nucleation of solid from liquid metals by "known" nucleating agents. All values come from experiments in which the metal studied was divided into a number of particles (10 to 300 pin diam.) much larger than the number of extraneous impurity particles so as to obtain a large number of particles free of foreign nucleating catalysts. Known nucleating agents are then introduced by coating the droplets with particles or a thin film of the catalyst. Six of the seventeen undercooling values referred to cases where, for various reasons, the identity of the nucleating species was not at all certain. Another six cases involved nucleating agents with a crystal structure that was not known. Four other cases involved undercoolings listed as greater than or equal to undercoolings which were very likely those for homogeneous nucleation. One investigation3 involved adding to droplets powdered oxides, carbides, and so forth that were doubtlessly covered with adsorbed oxide or nitride films. The highly variable nature of these films resulted in highly variable undercooling (as was also found in preliminary work in this investigation). It is apparent that the information on heterogeneous nucleation in liquid metals is too limited to give rise to any definite conclusions on the nature of the catalytic process. With these problems in mind a new method was

Jan 1, 1962

By E. J. Westerman

Prealloyed powders of nickel-base superalloys were sintered to almost theoretical density in short sinterilzg times. It was ascertained that the rapid densification was caused by a small amount of liquid phase at the grain boundaries, which apparently ovriginated by incipient melting at temperatures considerably below those at which macroscopic melting of the compacts occurred. An increase in the quantity of liquid phase present during sintering-, caused by an increase in the sintering temperature, increased the densification rate, but resulted in a decrease in the room temperature tensile propevties. NICKEL-base superalloys, which presently comprise an important group of high temperature alloys, are difficult to fabricate by the forging, casting, and machining operations presently used. As it was felt that fabrication by powder metallurgical techniques might offer advantages in the production of super-alloy parts, a basic investigation of the most important process in the sequence of powder metallurgical operations, the sintering process, was undertaken on Rene 41, Udirnet 500, and Nimonic 90 and 100 powders. These alloys age harden by the precipitation of the ? Ni, rA1,Ti) phase. Nickel-base superalloys of the Nimonic type have been fabricated by powder metallurgical methods, and their mechanical properties reported in detail.&apos; Other alloys for high temperature service which have been fabricated by powder metallurgical methods include a Co-base alloy of the Vitallium type;2,3 alloys with a Co-Ni-Fe-Cr base;4 stainless steels;5&apos;6 Cr-W-Co alloys;" and a Co-base alloy, X-40.8 METAL POWDERS The superalloy powders investigated were: a) a prealloyed at.omized Rene 41 powder; b) a prealloyed atomized Udirnet 500 powder; c) a prealloyed atom-

Jan 1, 1962

By W. M. McKewan

Dense magnetite pellets were reduced in hydrogen-water vapor-nitrogen mixtures over a temperature range of 400° to 500° C at a pressure of 0.97 atm. The rate of reduction per unit area was found to be constant with time and directly proportional to the partial pressure of hydrogen at a constant ratio of water vapor to hydrogen. Water vapor poisoned the oxide surface by an oxidizing reaction and markedly slowed the reduction. The enthalpy of activation was found to be + 13,600 cal per mole. THE investigation of the reduction of iron oxides has been the subject of numerous papers. Most of these papers have dealt with the evaluation of various ores, both magnetite and hematite. There have

Jan 1, 1962

By E. J. Dulis, V. K. Chandhok, J. P. Hirth

Cobalt clearly increased the activity of carbon in austenite and in ferrite. This effect of cobalt on carbon activity Plausibly accounted for the effect of cobalt on accelerating the austenite to pearlite transformation. Cobalt was found to have only a slight effect on carbon diffisivity in various Fe-Co and Fe-Co-W-Mo austenites, but was found to decrease carbon diffusivity in Fe-Co ferrite. THE effect of cobalt in steel is unique in that it is the only element that reduces hardenability by accelerating the austenite to pearlite reaction. The results of several excellent investigations aimed at explaining the role of cobalt have been published,1"7 but a complete understanding is still lacking. In addition, cobalt significantly enhances the resistance to softening or tempering of highly alloyed highspeed and hot-work tool steels. The resistance to tempering is related to the secondary hardening reactions associated with the fourth stage of tempering during which carbides of molybdenum, tungsten, and/or vanadium form in a martensite matrix. The effect of cobalt on secondary hardening reactions in high-alloy tool steel has received considerable attention, but a full explanation of the reactions involved has not been developed. Inasmuch as austenite to pearlite transformation and secondary hardening involve carbide formation, the present authors believed that the role of cobalt in effecting carbon activity and diffusivity in austenite and in ferrite was important to a fuller understanding of the phenomena involved. TO investigate the effect of cobalt on the activity coefficient of carbon in austenite, an approach was used similar to that used by Darken17 in his experiments on the effect of silicon, manganese, and molybdenum on carbon activity and diffusivity in austenite. TO

Jan 1, 1962

By T. M. Morris, F. M. Lewis, W. C. Lay, Gordon M. Bell

Part I of this chapter is concerned with the description of and metallurgical data pertaining to the flotation circuits used in the London mill of the Tennessee Copper Co., at Copperhill, Tenn. The ores treated at the London mill are massive complex sulfides, in which pyrrhotite and pyrite are the predominant minerals. Other sulfides are chalcopyrite and sphalerite; magnetite is also of economic value. The approximate mineralogical analysis of the ore is shown in Table 1. [ ] The chalcopyrite and sphalerite are closely associated with pyrrhotite as shown by the tracings of micrographs (Fig. I), which are representative of the mill feed. Fig. la illustrates the type of locking between pyrrhotite and chalcopyrite; Fig. lb illustrates the way in which sphalerite is attached. Thesephotographs indicate that it is not practical to break all of these attachments. Hence, in order to produce concentrates with satisfactory grades and recoveries, most of the locked chalcopyrite particles must be recovered into the copper concentrate, and the locked sphalerite-pyrrhotite particles must be separated from the iron concentrate. A copper concentrate, a zinc concentrate, and an iron concentrate are made. Typical metallurgical results are tabulated in Table 2. HISTORICAL In 1922 the London mill started as a copper concentrator, with a capacity of 300 tpd, and in 1926 an additional flotation circuit was added to recover the iron sulfide remaining in the copper tailing. In 1927 a zinc flotation circuit was installed between the copper and the iron flotation circuits. This procedure was not satisfactory because the iron recovery was low, due to the

Jan 1, 1962

By P. K. Koh

With identical annealing heal treatment the development of major annealed texture component seems to depend primarily upon the degree of cold reduction. Cube texture was evident on annealing- 1/2-, 1,/4- , and 1/8-mil tapes at 760°C, but it dissap-)eared on 927°C annealing of 1/8-mil tape cold reduced 96.9 pct. Some cube texturee remained as tile strongest 927 °C annealed texture component in 1/4- and 1/2-mil tapes cold reduced 93.8 and 87.5 pet, respectively. The switching coefficient increases and the squareness ratio of the hysteresis loop decreases proportionally with increasing cube pole concentration. PREVIOUS studies 1,2 on the 1/8-mil ultra-thin molybdenum permalloy tape established cold rolled and annealed textures and their magnetic performance for switch-core and coincident-current memory applications, The major cold-rolled texture was found to be of {110}<335> which is quite similar to the cold-rolled texture of silver and 70-30 cartridge brass. The major annealed texture components were found to be of {120)-- <001> and {113)<785>. Although the direction for easy magnetization for this type of alloy by the single-crystal technique is not avaliable, knowledge from related studies indicated [Ill] as the easy magnetization direction, similar to that of nickel.&apos; Therefore, a cube orientation, if present in the tape core, would be most detrimental to its magnetic performance.3 In its cold-rolled state the tape had < 111 > directions in the rolling plane 14.5 deg from the rolling direction.&apos; But the coercive force of the tape in such condition will be excessive due to large amounts of internal stresses, and therefore makes its use impossible for memory applications due to long switching time. In lower nickel alloys, suchas 50-50 nickel-iron and 65 pct Ni-Fe sheets, previous investigators4"7 found the presence of cube texture on annealing at 900° to 1000°C. Although no cube texture was found in annealed 1/8-mil tape,"&apos; its presence in some annealed 1,/4-mil tape cores was firmly established a year ago as verified by significant differences in magnetic properties. The present investigation is devoted to the orientation study and related magnetic measurements on three thicknesses of the ultra-thin tape, namely, 1/8 mil, 1/4 mil, and 1/2 mil, cold rolled directly from annealed 4-mil stock in the cold-rolled state as well as after they were annealed at 760°C (1400° F) and 927°C (1700°F). The results obtained might serve to elucidate the development of annealed texture as well as to establish clearly the importance of preferred orientation on the magnetic performance of such memory tape core despite its well-known low magnetic anisotropy exchange energy. EXPERIMENTAL PROCEDURE Samples were taken from one production heat (0.010 wt pct C, 0.004 P. 0.016 S, 0.80 Mn. 0.29 Si. 79.69 Ni. 4.42 Mo. 0.054 Co, 0.002 Ti, 0.12 Al, 0.04 Mg, 14.56 Fe). Annealed 4-mil sheets were cold re-

Jan 1, 1962

By W. C. Hagel, H. J. Beattie

Seven austenitic alloys of varions base compositions and minor-alloy additions were solution-treated, aged systematically between 1200oand 1800oF, and examined by X-ray and electron metallography. Intragranular preczpitations of µ, Laves, s, ?&apos;, Ni3Ti, and x phases were observed as a function of composition and aging time and temperatwre. Phase solubility limits were detevtnitzed within 100Fo intervals. These inter metallic compounds fall into two distinct general classes, and whichever class predomznates depends on base composition. It has become increasingly evident that multicom-ponent austenitic alloys are well characterized by their precipitation processes. Since certain groups of elements act as one, the relationships among these processes are reasonably simple; complete identification of such processes is usually attainable by a systematic aging study with a combination of techniques centered on microscopy and diffraction. Several nickel- and cobalt-base alloys illustrating cellular precipitation and its interaction with general precipitation were reported previously.1 The group of alloys covered in the present paper demonstrates precipitation-hardening reactions involving two distinct classes of intermetallic compounds where the predominating class appears to depend on base composition. This dependency ties in with a crystal-chemistry regularity first observed some twenty years ago by Laves and Wallbaum but never amplified to our knowledge. Results of electron-microscope and X-ray diffraction studies on systematically aged hot-rolled alloys known commercially as S-816, S-590, Rene-41, Incoloy-901, M-308, and M-647 are reported here. Some of these alloys have previously undergone minor-phase analyses by other investiators. Alloy S-816 was investigated by Rosenbaum, Lane and Grant,3 and Weeton and Signorelli.4 Rosenbaum found only CbC in hot-rolled bars. Lane and Grant found CbC and a small amount of M6C in the cast structure and stated that both carbides form during aging, most of the precipitation being CbC. Weeton and Signorelli found CbC, M23C6 and a weak indication of a phase after a slow step-down cooling cycle from 2250°F. Rosenbaum also investigated hot-rolled samples of S-590 and identified CbC and M6C. Preliminary information on Rene-41, gained partly from the present work, was reported by Morris.5 Long-time precipitation phenomena in Incoloy-901 at 1350°Fwere investigated by Clark and Iwanski.B heir raw data re- semble those of our present heat with 0.1 pct B, while their interpretation of these data resembles our interpretation of data from another heat with only 0.001 pct B; they made no statement as to boron content. No previous minor-phase studies of alloys M-308 or M-647 have been reported. EXPERIMENTAL METHODS Table I gives alloy compositions in both weight and atomic percent. Specimens were solution-treated from 1700º to 2200ºF, aged at logarithmic-time intervals up to 1000 hours between 1200 and 1800 F, and examined in accordance with procedures previously described in detail. &apos; &apos; Phase extractions were carried out in electrolytic cells containing 800 ml of either 7 pct HC1 in denatured ethanol or 20 pct H3PO4 in water. After electrolysis for 48 hr at 0.1 to 0.2 amp per sq inch, residues were separated by filtration or centrifuging. X-ray powder patterns of residues were recorded on a diffractometer for accuracy and on film for sensitivity. Lattice parameters were calculated by least-squares analyses of indexed sin 8 values, and relative abundances were estimated from intensities of strongest lines of each phase. These phase abundances denote relative amounts with respect to each other rather than to the alloy. Mechanically polished specimens were etched in a freshly mixed solution of 92 pct HC1, 5 pct H2SO4, and 3 pct HNO3. Parlodion replicas for the electron microscope were chromium-shadowed in high vacuum at a glancing angle of 20deg. All electron micrographs are reproduced here with the shadowing source above. The correspondence betweenelectronmicrostructures and phases identified by X-rays was established by a high redundancy of correlation between relative amounts at different stages of aging and examination above and below critical transformation or solubility temperatures. EXPERIMENTAL RESULTS S-816 and S-590—The phases found in S-816 and S-590 after various aging and solutioning treatments are listed in Table 11. These data and the observed

Jan 1, 1962

By D. R. de Fontaine

By computing the values of the resolved shear stress for a great many orientations of the tensile axis on all 12 (111) <110> slip systems, Taylor and Elam&apos; were able to map out a stereogram of slip systems, given here, Fig. 1, in Diehl&apos;s notation (see, for example Hauser and Jackson&apos;). The purpose of the present note is to derive such a stereogram by mathematical reasoning and to give a simple method of defining the system with highest resolved shear stress for any direction of the tensile axis, thereby eliminating tedious computation of the Schmid factor. Let the tensile axis, of direction cosines [xyz], make the angles 0 and relative to the slip plane normal [HKL] and the slip direction [hkl] respectively. Fig. 2 shows a simple cubic cell whose edges define a Cartesian coordinate system. Let A be a unit vector of origin 0 supported by the tensile axis. Its end point [xyz] then lies on a sphere of unit radius, on the positive hemisphere of which the planes z = 0, x = y, y = z limit the so called primitive triangle of a standard [loo] stereographic projection. For any point of this triangle, the following hold: 0«2 «y *sx « 1 [l] Now, for given [xpz], the most highly stressed system will be the one for which the following expression of the Schmid factor has the largest possible value: (HKL) belonging to the form (111) and [hkl] to the form <110>, the denominator on the right hand side of Eq. [2] is equal to 1.fi.a. The unknowns H, ... h, . . . can now be determined by correctly distributing +1 and -1 to H, K, L, and +1, -1,O to h,k, 1 giving the numerator of Eq. [2] its greatest positive value (the angles 0 and cpare chosen acute) subject to the condition: Hh+Kk+Ll = 0 [3] since the slip direction must lie in the slip plane. Condition [3] can be satisfied only by having one of its terms vanish and the other two equal to +1 and -1. Taking the case of the tensile axis lying in the primitive triangle, x2y, z and therefore Hh will be chosen equal to +1 with H = h = +1 in order to retain a maximum of + signs. There remain two alternatives: either 1 = 0 or k = 0. 1) take 2 = 0 Then Kk = -1 and the numerator of [2] becomes: Retaining a maximum of + signs gives L = k = +1 and becomes: 2) take k = 0 Then L1 = -1and, likewise, the numerator of [2] becomes: xz - z2 + xy + yz [5] But the difference [5] - [4] can be written: (y - z)(x+y +z) [6] positive or zero by virtue of [I]. If [6] is positive (y > z), then the largest possible value for the numerator of [2] for any xyz inside the primitive triangle is given by [5], i.e., for: That is to say, the active slip system corresponding to an orientat:~on of the tensile axis inside the primitive triangle is:

Jan 1, 1962

By L. F. Mondolfo, B. E. Sundquist

The crystallographic orientation relationships resulting when lead is nucleated from the liquid by Ni, Cu, Ag, and Ge were determined. For each nucleating agent several definite orientatioz relationships were found. These relationships seemed to be controlled by good symmetry relations and low crystallographic disregistry between mating planes. For any given nucleating agent the under colling for nucleation was found fairly constant and independent of the orientation relationship and consequent disregistry. It was also found that, upon re melting and refreezing the Pb, the orientation relationship was changed. These findings prove that crystallographic disregistry is not the controlling factor in heterogeneous nucleation from the liquid. The results of this investigation tend to confirm the theory presented in a preceding paper that heterogeneous nucleation starts with the formation of an adsorbed layer of nucleated metal on the nucleat-ing impurity. Evidence is given that cavities in the nucleating agent act as centers of nucleation. IT has long been known&apos; that solid extraneous particles are active in catalyzing phase transformations that occur in a system, particularly condensation and crystallization. It is well established that these heterogeneities act as catalysts by providing surfaces upon which nuclei of the precipitating phase can form with activation energies smaller than those required for homogeneous nucleation. Numerous investigations have shown that in this process of heterogeneous nucleation: a) the nucleus forms with one, or several, definite crystallographic orientation relationships with the nucleating phase2-4 and b) that there is a small range of undercoolings or super saturations characteristic of the nucleation of a given solid on a given Substrate.5-10 Turnbull and vonnegut11 have developed a theory based on theories developed by Volmer12 and Turn-bull and Fisher1= for heterogeneous nucleation from gases and liquids, that relates the super saturation or undercooling required for nucleation to the dis-registry between the lattices of the nucleus and the nucleating agent. This theory predicts that nucleation should occur with the orientation relationship between the nucleus and nucleating agent that minimizes the disregistry. Further, it predicts that the undercooling or super saturation necessary for nucleation should be a function of the disregistry. Numerous investigations have dealt with the orientation relationships resulting from the condensation of vapors onto crystalline solid substrates2,3 and a few with the nucleation of one phase by a second phase in solidification4,14. Others have dealt with the supersaturation8-10 and undercooling5-7 associated with nucleation in condensation and solidification respectively. However, there is virtually no report that gives both of these factors for the same system. In this investigation a study was made of the undercoolings and orientation relationships resulting when Pb is nucleated from the liquid by Ni, Cu, Ag, and Ge. It was the purpose of this investigation to check the Turnbull-Vonnegut theory, i.e., the importance of crystallographic disregistry between nucleating catalyst and nucleated metal. The results indicate that disregistry is not an important factor in nucleation and that the nucleation process is probably somewhat more complex than current theories suggest. EXPERMENTAL PROCEDURE Small single crystals of nickel, copper, silver, and germanium were prepared from materials of four to five nines purity, and the Pb used was also 99.999+ pet pure. Cu and Ag single crystals were prepared by sealing small chips of Cu or Ag in an evacuated quartz capsule and heating the capsule at 2000°F for 1 hr before cooling. Nickel crystals of 200 diam were also prepared in evacuated quartz capsules, but melting was done by heating the capsules in an oxy-acetylene flame for a few minutes. These spheres were invariably polycrystalline so

Jan 1, 1962

By J. B. Clark

An exploratory study of the 60 wt pct Mg and 80 wt pct Mg sections of the solid constitution in the magnesium-rich region of the Mg-Al-Ca-Zn system was undertaken. The objective of the investigation was to determine the general configuration of the phase fields with respect to the magnesium solid solution in this complex system. The 335°C (635°F) tetrahedron was selected for study because the solid constitutions of the bounding ternary systems—Mg-Al-Zn,1 Mg-A1-Ca,2 Mg-Ca-zn3—were well known and, at least in these ternary systems, diffusion was rapid enough at 335°C for equilibrium to be reached fairly rapidly. Metallography and powder X-ray diffraction were selected as the best corroboratory methods for determining the solid phase equilibria. A total of forty-six quaternary alloys on the 60 wt Mg and 80 wt Mg sections were prepared, annealed to equilibrium at 335°C, and the phases present identified. Singly sublimed (99.99 pct) magnesium, electrolytic (99.99 pct) zinc, high-purity (99.99 pct) aluminum, and USP calcium were alloyed in graphite crucibles under a chloride flux and chill cast into a split graphite mold. Alloy samples were sealed under argon in Pyrex vials and annealed at 335°C ± 1/2° for a minimum of 500 hr. At the conclusion of the anneal, the alloy samples were quenched rapidly in ice water. Standard metallographic procedures for magnesium alloys were used. Powder X-ray diffraction patterns were taken on a G. E. Camera with a diameter of 14.32 cm using nickel filtered copper radiation. The phase equilibria in the 60 wt pct Mg section of the 335°C (635°F) tetrahedron is shown in Fig. 1. The complex equilibria in the zinc-rich region were not accurately determined and are shown only tentatively with dotted lines. The equilibria of the three bounding ternary 335°C sections from pure magnesium to 60 wt pct Mg are also shown as though folded away from the tetrahedron. The 80 wt pct Mg section has the same configuration of phase fields as that shown in Fig. 1. Thus it is reasonable to conclude that in higher magnesium sections, the same relative configuration of phase fields is maintained though the relative proportions of the individual phase fields may change slightly as the magnesium solid solution is approached. Note that all the ternary phases present in these ternary diagrams enter into the quaternary equilibria with the exception of the phase of the Mg-Al-Zn system which becomes unstable with the addition of as little as 1/2 pct Ca. No quaternary intermetallic phases were found. No liquid phase was detected in any of the quaternary alloys annealed at 335°C suggesting that if a quaternary eu-tectic exists, it must lie between 335°C and 339°C, the temperature of the ternary eutectic in the Mg-Al-Zn system.

Jan 1, 1962

By D. L. King, B. A. Schepman

A number of unique thickener mechanism designs with the operating results achieved in various installations are discussed. These unusual designs include new types of raking arms, lifting devices, and feed-wells employed to obtain higher underflow densities and minimum operator control or improved overflow clarity. Several installations of large thickeners in which the underflow lines pass upward through the center to eliminate tunnels are reviewed. The location of the lines and pumps with the maintenance and operating records are included. Several types of automatic lifting device controls are used to provide storage in the thickener. Some of the installations employing underflow density controls are achieving excellent operating results. Thickeners or sedimentation basins are used in minerals beneficiation plants for three basic purposes. These are 1) Concentration, or to raise the density of a liquid-solids slurry. 2) Clarification, or removal of finely divided solids from a slurry. 3) Hydroseparation, or removal of a specific fraction of solids from a slurry. The concepts that control the size and configuration of basins used for these purposes are different. Likewise, different equipment is properly employed to accomplish these various objectives. The pattern of liquid and solids flow in the clarification zone of a sedimentation basin used for thickening or raising the density of a pulp normally is not critical. That is, the solids normally will drop or plunge to the bottom quite readily, and the liquid separates itself from these solids so as to overflow the basin in a relatively clear condition. When clarification or removal of finely divided particles is to be accomplished, the flow patterns in the basin are extremely important. The velocity of the incoming stream must be dissipated and the liquid flow distributed ]In the tank so that the feed is not divided into streams that flow directly to the overflow carrying the fine:ly divided solids that are to be removed. Similarly, the configuration of the arms that provide the raking and thickening of the pulp is not as important in basins primarily devoted to clarification. In thickening, the design of the arms and the manner in which the pulp is moved or worked, can contribute appreciably to the thickening process and achievement of a higher density underflow. THICKENING As the grade oi ore bodies throughout the world generally decreases, and chemical processes, hydro-metallurgy, and other more refined methods of minerals beneficiation are required, problems in thickening become more acute. Difficult operating conditions, previously encountered only occasionally in thickening metallurgical slurries, or clarifying process streams in the mill, are now the rule rather than the exception. Fig. 1 illustrates some of the different types of raking arms that are successfully achieving the desired goals in pulp thickening. The conventional raking arms consist of a relatively simple truss with the blades attached to the bottom chords. This design provides proper Concentration of many &apos;normal&apos; slurries. A modificaiion of this design as shown in the center is being used with excellent results on large thickener basins where it is desirable to have a

Jan 1, 1962

By K. T. Aust

The occurrence of annealing twins in high-purity aluminum resulted in the formation of grain boundaries having orientation relationships which correspond to a high density of coincidence sites. The results provide support for the coincidence site model and indicate that large-angle coincidence boundaries have lower free energies than large-angle noncoincidence boundaries. Observations are presented concerning the coherent structure of twin interfaces in aluminum and the importance of inter-facial energy in preferred orientation. RECENT experiments1 have shown that when an annealing twin is formed during grain boundary migration in zone-refined lead, a large-angle random boundary is replaced at the growth front by a large-angle coincidence site boundary. The coincidence site orientation relationships obtained by twinning were of the type considered by Kronberg and Wilson,2 Frank,3 and Dunn.4 On the basis of the theory of annealing twins advanced by Fullman and Fisher,5 these observations indicate that the energy of a coincidence site boundary is less than the energy of a random boundary by an amount which exceeds the energy of the coherent twin boundary. This energy difference between the coincidence and random boundaries must be at least about 5 pct since the ratio of twin boundary energy to grain boundary energy in zone-refined lead is 0.05 * .014.6 Fullman7 has found that the twin boundary energy in aluminum is about 21 i 5 pct that of a large-angle grain boundary. A twin boundary energy as large as this would be expected to exclude the formation of many coincidence site grain boundaries, especially those which have a relatively low density of coin- cidence sites. Therefore, if the coincidence site model is a useful interpretation of certain large-angle boundaries, then it would be predicted that only coincidence boundaries which separate adjacent crystals with a relatively high density of coincidence sites may be obtained as a result of twinning in aluminum. The present experiments provided a means of testing this prediction since annealing twins occurred during the growth of recrystallized grains into striated, melt-grown single crystals of zone-refined aluminum. EXPERJMENTAL PROCEDURE A striated single crystal of zone-refined aluminum, about 1 cm sq and 37 cm in length, was obtained during zone melting of aluminum of 99.996 wt pct starting purity in a graphite boat under helium atmosphere.8 A molten zone of 2 to 3 cm in length, which was maintained by induction heating. was passed along the length of the bar for eleven passes at a rate of 0.9 mm per min. An additional final pass was given at a rate of 0.2 mm per min. The center portion of the zone-melted bar was characterized by an electrical resistivity ratio between room temperature and 4.2° K of 8000 to 9000. Single crystals of 1 to 2 cm in length were removed from the center section of the zone-refined bar and electrolytic ally polished in a 2:l solution of methyl alcohol and concentrated nitric acid. The specimens were then chemically polished in Alcoa R-5 solution. X-ray analysis of the single crystals indicated the presence of striations or lineage substructure having misorientations as high as 2 deg. New, recrystallized grains were introduced into each striated crystal by the technique of artificial nucleation and growth, previously described.9 During the growth of the recrystallized grains at 300&apos; to 600°C in argon, it was sometimes found that a

Jan 1, 1962

By Donald J. Knight

HEAT Treatment at 1500&apos; F of a mild steel containing 0.1 pct C, in an atmosphere which is oxidizing to both carbon and iron, results in the progressive oxidation of the metal surface with little or no change in the carbon content of the underlying metal. Further heat treatment of the scaled metal in either a neutral atmosphere or in a vacuum may or may not result in the decarburization of the metal depending upon the physical nature of the scale. It is apparent that if a continuous layer of oxide is present on the steel surface, the reaction OScale + Cmetal Cogas cannot progress since the SO formed gas would be unable to leave the oxide/metal interface. Thus, in order for the reaction to progress, the oxide must be cracked or porous. Vacuum heat treatment at 1500" F of samples with a thick continuous oxide scale showed no decarburization of the steel. However, when cracks were introduced mechanically into the scale prior to the vacuum heat treatment notable decarburization of the metal resulted and a structure as shown by Fig. 1 obtained, i.e., reduction of the crack walls to ferrite. With reference to the diagram of Fig. 2, it would appear that a mechanism of the following type takes place. Carbon atoms arriving at an oxide/metal/void interface, such as &apos;A&apos;, Fig. 2(a), can combine with oxygen atoms from the scale and leave the reaction site as Cogas thereby reducing the oxide to metal. On a greatly magnified scale, Fig. 2(b),this will appear as a ferrite projection along the crack wall. Carbon atoms entering this projection can react with oxygen atoms at point &apos;C&apos;, which is a new interface, and so on leading to a progressive growth of the ferrite along the crack wall and to the surface, Figs. 2 (c) and 1. It would appear that the only means by which thickening of the ferrite film can take place is by a diffusion of oxygen through the ferrite film to react with carbon at the newly formed ferrite/ void interface. Since the diffusion rate of carbon is reportedly much greater than that of oxygen, and since there is a low probability factor of oxygen and carbon atoms arriving simultaneously at the same site on the ferritehoid interface, there will be a tendency for more rapid lengthening than thickening of the ferrite layer, as is observed.

Jan 1, 1962

By J. P. Morgan, J. R. Dawson

A review of Jones & Laughlin&apos;s Vesta coal preparation plant flowsheet in 1959 indicated that, of the three sizes making up the company&apos;s metallurgical product, the -48-mesh fraction offered the greatest potential for improvement. Efforts to improve quality and yield were directed toward the use of froth flotation. After laboratory and plant tests were completed, it was decided that treatment of the entire -@-mesh fraction of the coal mix by flotation was a significant step forward in providing better coal quality and recovery. Reduction of ash in the metallurgical coal from 6.75 to 6.25% provided material savings at the coal washer, coke plant and blast furnace. The Vesta preparation plant of the Jones & Laughlin Steel Corp. is located on the Monongahela River, eight miles south of Brownsville, Pa. This plant is capable of cleaning 2400 tph of a mixture of Pittsburgh seam high volatile coals from the Vesta and Shannopin mines to produce a metallurgical coal of 6.75% ash and a steam coal containing 14% ash. Heavy media vessels are utilized to upgrade the coarse coal while launders and tables handle the -1/4-in. fraction of the raw coal feed. Cleaned -1/4-in. coal goes to boot classifiers where the 48 mesh material settles and is removed by bucket elevators. This 1/4x48 mesh material is then sent to centrifugal dryers for dewatering. As designed, the -48 mesh fraction overflows the boot as a 7 to 8% solids slurry and is recovered by cyclones and a thickener and then dewatered by filtration. The products of the heavy media circuit, the launder-table-boot-dryer circuit and the cyclone-thickener-filter circuit, are combined to constitute the shipped metallurgical coal. The Vesta-Shannopin mix is combined at Jones & Laughlin&apos;s Pittsburgh and Aliquippa Works with purchased low and medium volatile coals for the production of metallurgical coke. A review of the preparation plant flowsheet in 1959 indicated that of the three sizes making up the metallurgical product, the -48-mesh fraction, containing 16.7% ash, offered the greatest potential for improvement of coal quality. This fraction was considered low, averaging 55%, while the rejects averaged only 33% ash. It was evident that while the boot overflow fraction represented only 6% of the product mix, a reduction in ash to 6 or 7% would reduce the ash of the metallurgical coal by 0.5%. The original plant flowsheet handling the boot overflow (Fig. 1) consisted of ten 14-in. cyclones treating 70% of the overflow and producing a 48x150-mesh underflow and a -150-mesh overflow. The cyclone overflow was combined with the remaining 30% of the boot overflow to constitute the feed to a 150-ft thickener. The cyclone underflow and the 48x325-mesh thickener underflow were fed to vacuum disk filters for dewatering prior to combination with the coarse metallurgical coal. The thickener overflow stream containing the -325-mesh material was split, 40% being recycled directly to the plant water system and 60% being flocculated and clarified in an 85-ft thickener. The underflow of this thickener was pumped to waste. Efforts to improve quality and yield on the -48-mesh coal were directed toward the use of froth flotation early in the investigation. A review of the fine coal flowsheet indicated that three streams should be considered for treatment by froth flotation. These were the -325-mesh thickener overflow, the -150-mesh cyclone overflow and the -48-mesh boot overflow. Flotation of the thickener overflow was considered basically to improve recovery by upgrading the reject stream so that it could be fed to the filters along with the thickener and cyclone underflows. The overflow from the thickener contained 3.7% solids and had an ash analysis of 33%. Flotation of the cyclone overflow and boot overflow were considered to upgrade coal quality as well as yield. Treatment of the cyclone overflow, a 5.4% solids slurry averaging 27% ash, would eliminate the coal thickener and provide a feed of flotation concentrate and cyclone underflow to the filters. Treatment of the boot overflow would eliminate both the cyclones and thickener and feed only flotation concentrates to the filters. Flotation feed in this

Jan 1, 1962

By J. W. Downey, M. V. Nevitt

The phase boundaries for the 950" isothermal sections in the ternary systems Zr-Co-0 and `Zr-Ni-0 have been determined for the composition range from 50 to 100 at. pct Zr. The two systems show very similar phase relations, having no extensive solid solution phase fields. Each contains a ternary phase. These phases are apparently isostructural, but their structure has not been determined. Some aspects of the phase relations are discussed in terms of the alloying behavior of transition metals. THE work described in this paper is the outgrowth of a recent study of the occurrence of phases having the Ti2Ni-type structure (structure-type E9,) in certain ternary systems involving Ti, Zr, or Hf with another transition metal and O.", In the Zr-CO-0 and Zr-Ni-0 systems no Ti2Ni-type phases were found to occur. However, there are several interesting aspects of the phase relations in the two systems which have significance from the point of view of the alloying behavior of transition metals. The results of this investigation may also have some importance in studies of the oxidation of Zr-Co and Zr-Ni alloys. In both the Zr-Co-0 and Zr-Ni-0 systems only the 950" isothermal sections were investigated and, as a further restriction, the study was limited to the composition range from 50 to 100 at. pct Zr. A tentative Zr-Co binary diagram has been published by Larsen, Williams, and Pehin. In the composition range pertinent to the present work they report a eutectic at 980°C and 75.9 at. pct Zr, the products of which are the terminal solid solution based on /3 Zr and the compound Zr2Co, and a eutectic at 1080" and 64.8 at. pct Zr whose products are Zr,Co and ZrCo. The solid solution based on /3 Zr is shown to decompose eutectoidally at 826°C into a Zr and Zr2Co. The limits of solubility of Co in a and /3 Zr have not been established. The structure of Zr2Co is not identified in the publication just cited. Dwight has reported that ZrCo has the CsC1-type strcture. The Zr-rich portion of the Zr-Ni diagram has been determined by Hayes, Roberson, and Paasche." The phase relations are very similar to those of the ZrCo system. A eutectic reaction whose products are /3 Zr containing 2.9 at. pct Ni and Zr,Ni occurs at 961°c, and a eutectic between Zr,Ni and ZrNi is found at 985". The solid solution based on /3 Zr decomposes eutectoidally at 808°C. The solubility of Ni in a Zr is not known accurately but is believed to be very small. Smith, Kirkpatrick, Bailey, and Williams7 have found that Zr2Ni has a tetragonal structure of the A1,Cu-type and that ZrNi is orthorhombic. Domagala and McPherson8 have published a constitution diagram for the system Zr-ZrO,. At 950" their diagram indicates that the solid solution of 0 in 0 Zr is stable from 0 to 0.5 at. pct while the phase field of 0 in a Zr extends from 6 to 29 at. pct. These solubility limits were adopted in the present study and no binary Zr-0 alloys were made. No previous data on the phase diagrams of the ternary systems are known to exist. EXPERIMENTAL PROCEDURE The experimental details involved in the preparation of alloys in this laboratory by arc melting have been described in several previous papers"3 and they will not be repeated here. Information concerning the purity of the metals used is given in Table I. Oxygen was added in the form of reagent grade ZrO,. All of the cast specimens in both alloy systems were annealed in air-atmosphere tube furnaces at 950 3&apos; for 72 hr and water quenched. The specimens were protected from oxidation by wrapping them in Mo foil and sealing them in quartz tubes that had been evacuated at room temperature to a pressure of 1 x 10B mm of Hg. The phase boundaries were determined by metallography, and identification of the phases was accomplished primarily by X-ray diffraction methods which employed a powder camera having a diameter of 114.6 mm. The diffraction techniques which are in use in this laboratory have been previously described.&apos; An etchant that proved satisfactory for most of the alloys consisted of 5 pct by vol of AgNO

Jan 1, 1962