By Daniel D. Pollock

The il'lott and Jones theory of thermoelectricity predicts that the absolute thermoelectric power of alloys of transition and noble metals should be a maximum when the concentration of the noble metal is approximately 55 to 60 at. pct. An examination of the emf of a series of relatively pure alloys of copper and nickel shows that the predicted maximum occurs at about 57 at. pct Cu. This excellent agreement with the theory is considered to substantiate the Mott and Jones theory of thermoelectricity for binary alloys of transition elements. This theory is extended to show that the emf behavior of dilute, ternary copper-nickel base alloys, which contain approsimately 60 pct Cu and 40 pct Ni, may be described in terms of a scattering mechanism. The scattering effect of a third element is demonstrated to be a function of its valence and its period in the periodic table. Small amounts of solute elements have additive scattering effects upon the emf of the Cu-Ni base. The Mott and Jones equation is modified to include this scattering parameter. This adaptation accurately describes the thermoelectric behavior of ternary and quaternary CLL-Ni base alloys. An empirical form of the modified Mott and Jones equation is derived which permits the calculation of thermoelectric power with an average error of less than 0.4 pct at 500 "C. CONSTANTAN has long been used as a thermocouple element. Its approximate composition varies from 50 pct Cu, 50 pct Ni to 65 pct Cu, 35 pct Ni. Small amounts of manganese, iron, and other elements have been used to modify the composition in order that the resultant emf vs platinum conforms to nationally accepted table. Adjustments of this type are made on a purely empirical basis. Constantan was originally made in Germany and was imported into this country for thermoelectric and electrical resistance purposes. During World War I, the supply of this material became seriously depleted. The work of Bash4 was done in this period in order to develop a satisfactory substitute for the imported material. Bash's empirical work on Cu-Ni alloys is still the basis for all commercial constantans made in this country. No reexamination of the electrical properties of this system has been made, despite the fact that it is now well known that Bash's alloys contained impurities which strongly affected their thermoelectric behavior.

Jan 1, 1962

By K. S. Krishnam, A. G. Guy

VOLUME 6 of the Transactions of the Baikov Institute of Metallurgy, Moscow, is devoted to the subject of "the experimental and theoretical study of the physical characteristics of dilute solid solutions,11 and summarizes work that has been done largely in the years 1958-9. In view of the attention that Soviet investigators have given to this subject, it seemed useful to carry out an independent experimental investigation in an effort to judge the scientific basis and practical significance of this field of study. The present note is a preliminary report of this investigation. The first property studied by the Soviet group was X-ray spectra of solid-solution alloys.' An anomaly observed at low concentrations (--0.05 at. pct) of the alloying element led to the theory that each impurity atom in a transition-metal base alloy is the center of a "block" of affected atoms with a radius of about 10"7 cm. This theory was further developed in a later paper.2 By this time similar anomalies had been found in diffusion coefficients3 and in thermal expansion.4 The entire development up to 1959 was reviewed in a comprehensive paper, and further theoretical ideas were also published at this time. Finally, the volume mentioned above was published in 19607 giving new experimental data on anomalies in optical properties and Hall constant, and a new theoretical treatment also appeared.' Although western scientists have done both theoretical work, summarized recently by Friedel,9 and considerable experimental work on dilute solid solutions, there is little support for the marked anomalies reported in the Soviet papers. Of the physical properties studied by the Soviet investigators, thermal expansion was chosen for the present investigation because of the relative ease of obtaining the necessary precision of measurement. A Leitz dilatometer was used for this purpose, and a special technique involving interchanging of the two specimens being compared permitted a precision of 0.05 x X in average thermal expansion over the range 27° to 600°C. The specimens were heated and cooled in vacuum or in a protective atmosphere at a rate of 50 °C per hr. Ferrovac E iron was used as the comparison specimen and in every case had a coefficient of expansion higher than (or equal to) that of the alloy. Since unintentional impurities are an important factor in studies of dilute alloys, special attention was given to the purity of the iron and the alloys used. The alloys were the same of those used by Abrahamson10 and by Michalak," and their preparation is described in these references. Chemical analyses of the Ferrovac E iron and of typical Fe-W and Fe-Mo alloys are given in Table I. The purity of the iron and alloys is undoubtedly higher than in the

Jan 1, 1962

By K. P. Gupta

The Cb-rich boundary of the (Cb,Al) a phase field at 1250OC is near 41 pct Al. The Al atoms tend to occupy the C. N. 12 sites in this structure. A homologous (Ta,Al)a phase was identified. No a phase was found in the Mo-Al system at 1200°C. The first binary o-phase with a non-transition element as a major component was found1,2 in the Cb-Al system. The composition of this phase was reported2 as approximately 34 at. pct Al, based on X-ray diffraction patterns taken of alloys in the as-cast condition. Further study of the composition of this o-phase, therefore, appeared desirable. Since Si was previously found3,4 to occupy preferentially the lowest C.N. sites (I and IV) in the a phase, and preliminary resultsa indicated that Al may show similar ordering, one of the aims of the present work was to obtain more complete information on ordering in (Cb, Al) o. Among the binary systems of Al with Ti-, V-, and Cr-group elements, the Ti-Al, Zr-Al, V-Al, and Cr-Al systems are known to comprise no o-phase. In the present work a Ta-Al and a Mo-Al alloy were studied in an effort to find additional o phases with Al as a major component. EXPERIMENTAL PROCEDURES AND RESULTS An alloy with the intended composition of Ta + 40 at. pct Al was prepared by arc melting in He atmosphere. In both the as-cast condition and after annealing for 10 days at 1250°C and quenching in cold water this alloy consisted of two phases, as seen in the X-ray pattern and the microstructure. One of these phases was identified as the o-phase; the observed and calculated d-spacings are shown in Table I. The lattice parameters of this o-phase are a = 9.972 A, c = 5.214 A and c/a =0.5228, as determined from a Debye-Scherrer pattern using Fe K a radiation. The d-spacings for the unknown second phase are given in Table 11. The alloy contained approximately 25 pct of the unknown phase after annealing, as estimated on the basis of microscopic examination. A Mo-Al alloy was prepared by arc melting, with an intended Al-content of 35 at. pct. The alloy button was annealed for 7 days at 1200°C and water quenched. The X-ray pattern of the alloy in both the as-cast and the annealed state showed the reflections of Mo3Al (Cr30 type structure) and an unknown phase different from a. Six Cb-Al alloys were prepared in the composition range 30 to 50 pct Al. All alloys were arc melted in He atmosphere. After annealing for three days at 1175oC in evacuated silica capsules and quenching in water, the alloys with 30 to 40 pct Al contained three phases, namely the o-phase, Cb3Al (Cr3O-type structure) and an unknown phase. The alloys with more than 40 pct Al contained two phases, namely, what appeared metallographically, the o-phase and the same unknown phase. In the alloys containing less that 38 pct Al, the unknown phase was not present after annealing for 4 days at 1250°c,

Jan 1, 1962

By Joachim J. Hauser

Experiments on latent hardening were peyformed by compressing single crystals along a direction perpendicular to the tension axis. The slope and length of easy glide in the tension test were found to depend only on prior deformation in the same slip plane. Prior deformation on a different slip plane changes the stress level of the resulting stress-strain curve. The yield points appearing upon reloading after prior extension and unloading were related to the end of easy glide. SEVERAL researchers have studied the latent hardening due to deformation of a crystal by slip on a slip System after prior deformation. These experiments can be divided into those in which the prior deformation was on the same plane as the subsequent and those in which the two deformation processes were in different planes. In the former category are the experiments of Buckley and Entwistle,1 Parker and washburn,2 and Haasen and Kelly.3 The latter case has not been studied systematically; it was the main purpose of this investigation to produce this type of latent hardening and explain the results in terms of the existing theories of work hardening. In general, tension producing slip on a certain slip system can be preceded by tension, transverse compression or longitudinal compression, each with predictable dislocation movement and intersection. The intersection of dislocations can lead to glissile or sessile jogs, Cottrell-Lomer locks and other sessile dislocations. The effect on the stress-strain curve could depend on which combination of the former mechanisms is operating. Haasen and Kelly3 have studied the yield points which occur in aluminum and nickel single crystals upon reloading after prior unloading in a tension experiment. They attributed this effect to the anchoring of dislocations occurring during unloading. As Cottrell and stokes4 have shown that dislocations cutting through the "forest" could only lead to reversible changes, they attributed the anchoring to the formation of sessile dislocations during unloading. However, different kinds of sessile dislocations could be formed during unloading, and it was the purpose of this experiment to determine whether Cottrell-Lomer locks are responsible for the yield effect and for the end of easy glide. The case where a longitudinal compression is followed by tension along the same axis is commonly referred to as a Bauschinger test. This type of effect was studied by Buckley and Entwistle1 on aluminum single crystals and by Parker and washburn2 on zinc single crystals. In such a test, the tension and the compression activate the same slip plane with opposite slip directions. The use of sideways compression in the present experiments permits the activation of different types of slip systems and the study of their effect on the easy glide region and on the transition between the elastic and easy glide region. The theory of seeger5 for the flow stress in fee materials is applied to explain the latent hardening. EXPERTMENTAL PROCEDURE All the single crystals used in this investigation had an axial orientation close to <210>, called the "0.5" orientation. This is the orientation for which the tensile axis is 45 deg from both the slip plane and the slip direction. The single crystals were grown from the melt under a helium atmosphere using milled graphite boats,=at a rate of 8.6 mm per min. The silver used in the experiment was 99.98 pct pure. The single crystals had a square cross section about 0.9 by 0.9 cm and a length of 14 cm. The orientation of the specimen was determined within ±2 deg by the Laue back-reflection method. The specimens were annealed at 940&apos; ± 2°C in a helium atmosphere for 24 hr and then furnace cooled over a period of 7 hr. The specimens were electropolished in a solution of 9 pct KCN in water. The specimens were tested in a soft-type tensile machine (the load is prescribed) up to 3 pct strain. The stress was increased continuously at approximately 30 g per mm2 per min. The strain was measured over a 5 cm gage length with a mechanical extensometer employing an optical lever. The strain and stress were measured with accuracies of i 2 X 10-5 and ± 2 g per mm2, respectively. The remainder of the stress-strain curve up to 20 pct strain was obtained in a hard-type tensile machine (the strain rate is prescribed). The strain and the stress were measured in that machine with an accuracy of ±2 pct. The compression tests were performed in the hard-type machine using accurately machined steel blocks without lubrication. The blocks were used so as to apply a uniform compression over a length of 13 cm. The strains were measured on the hard-type machine and with a micrometer.

Jan 1, 1962

By W. A. Tiller, W. C. Johnston

The solute distribution ahead of an advancing solid-liquid interface is controlled by varying the momentum boundary layer thickness in the liquid adjacent to the interface. Single pass zone-melting experiments on Pb-Sn alloys are described in which the liquid is caused to rotate in the plane of the solid-liquid interface due to the influence of a magnetic .field rotating in this plane. The variation of the diffusion boundary layer thickness with field strength is determined. DURING the freezing of an alloy a partitioning of solute occurs at the solid-liquid interface, the magnitude depending upon the difference in the solid and liquid solubilities at the interface temperature. Because the diffusion coefficient is so small in the liquid relative to normal freezing rates, either a pileup or a depletion of solute occurs at the interface when the partition coefficient, kO, is either less than or greater than unity, respectively. This solute distribution is completely characterized by i) the solute concentration in the liquid far from the interface, C) the ratio of freezing velocityf, to diffusion coefficient, D, iii) the partition coefficient, ko, and iv) the thickness of the diffusion boundary layer, 6,, at the interface (this assumes that an electric field is not applied across the interface). For a particular system, C ko and D are fixed so that the character of the solute distribution can be changed only by a variation of either f or 6c. As is well known, the freezing velocity can be changed by varying the thermal environment of the alloy. Whereas, the thickness of the solute rich layer can be changed by varying the fluid flow conditions in the liquid. It is the purpose of this paper to describe a technique for controlling the fluid flow conditions in the liquid. During most solidification experiments the driving force for fluid flow arises from either mechanical mixing, thermal convection or electromagnetic mixing. The momentum boundary layer thickness, 6m at the solid-liquid interface, within which negligible movement of the liquid occurs, has been calculated for the special case of mechanical mixing where crystals are solidified by the Czochralski technique.l,2 The calculation of 6m for the case of thermal convection has also been made.3 In some calculations it has been assumed that the momentum boundary layer thickness, 6,, may be equated to the thickness of the diffusion boundary layer 6c, at the interface. However, as may be seen from Appendix I this is only true in very special cases and in general where a is a constant of magnitude determined by the particular liquid alloy. Neither calculations nor experimental data exist for the dependence of upon electromagnetic mixing. In this paper experiments are described in which the liquid is caused to rotate in the plane of the interface due to the torque developed on it by a magnetic field, H, rotating in this plane. The variation of is controlled by the variation of H. A magnetic field rotating in a plane perpendicular to the interface has been used for the purification of aluminum. Experimentally, we determined the variation of 5C with H by using the zone-melting technique of pfann5and a theoretical relationship of Burton et a1.2 pfann5 has shown that, after the passage of one molten zone through a long cylindrical charge of uniform concentration, CO, the solute distribution, C,, in the solid is as shown in Fig. 1. The equation describing this distribution is

Jan 1, 1962

By C. B. Alcock, L. I. Cheng

By the use of radiochemical methods for the study of the gas-liquid equilibria at low temperature, and for the determination of the sulfur contents of metal beads which had been equilibrated with H2S/H2 mixtures of known sulfur potential, it has been possible to obtain the liquid solubility and the free energy of solution of sulfur in liquid tin and lead at temperatures between 500°and 680°C. THE gas-liquid equilibrium method has proved in the past to be most successful in the determination of the thermodynamic behavior of dilute solutions of sulfur in liquid metals.1,2 One of the basic requirements for success with this method is that the volatility of both the metal and its lowest sulfide should be small, otherwise sulfide will be deposited at the cool end of the furnace, where it may react with the outgoing gases to form either sulfur-rich lowest sulfide or higher sulfides. The resultant value of the apparent equilibrium constant will then be lower than the correct one. This argument applies even at sulfur potentials below that in equilibrium with a separate condensed phase of the lowest sulfide at the reaction temperature, T. The mass of sulfide which is deposited at the cold end of the furnace, and hence the extent to which further reaction occurs with the outgoing gases, depends on the time taken for equilibrium to be reached between metal and gas. Since this will depend principally on the bulk of the metal phase which is used, one should clearly attempt to uie as small metal samples as possible. These considerations are important in the study of dilute solutions of sulfur dissolved in liquid tin and lead which both have moderately high vapor pressures as metals and form volatile sulfides. The limit on the size of the metal samples which may be used is set chiefly by the difficulties of analysis for very small amounts of sulfur. The oxygen or carbon dioxide combustion method, followed by iodimetric determination of the sulfur dioxide which is formed,has been found to be successful for the determination of small amounts of sulfur in copper, iron, cobalt and nickel.4 This method was unsatisfactory for sulfur dissolved in tin and lead, mainly because the sulfur dioxide was to some extent absorbed by the copious tin or lead oxide deposits which were formed on the walls of the combustion tube. Furthermore some of the sulfur was found to segregate on the surface of the beads as flaky sulfide crystals which would easily be lost in the transfer of a bead from a boat in the gas equilibration apparatus to one in the combustion apparatus. Oxidation in aqueous media to sulfate ion followed by precipitation as barium sulfate was, therefore, adopted as the analytical procedure. The gas-metal equilibrium experiments were all carried out with radioactive sulfur and thus the analysis involved the counting of barium radiosulfate. Furthermore the use of the radioisotope meant that the approach to the gas-metal equilibrium could be followed continuously by gas counting.&apos; The metal beads were held separately in glass crucibles during equilibration and were transferred from the furnace to the beaker for dissolution in nitric acid still in the crucibles, and thus the possibility of sulfur loss by detachment of the sulfide segregates was eliminated. The temperature range of this investigation was 500° to 680°C. EXPERIMENTAL APPARATUS AND METHOD The apparatus consisted of two furnaces placed in series in a gas recirculation system, Fig. 1. One furnace F1, which was vertical was used to heat the alumina crucible, A, holding six metal beads in separate glass crucibles. The beads weighed between 300 and 700 mg each. The crucible assembly was introduced and removed from the furnace mechanically under a stream of oxygen-free argon. The other furnace, F2, was horizontal and was used to heat a cobalt Co9S8 mixture, held in an alumina boat, and made with radiosulfur containing about 1/2 millicurie per g of sulphur. This mixture, which was finely powdered, was used as a source of known H2S/H2 mixtures6 for a given furnace temperature. The recirculation system also contained a gas re-circulation pump (P), an end window Geiger-Miiller counter (N)—placed downstream of F1 so as to monitor the H2S pressure in the gas leaving this furnace— a sample volume for chemical analysis of the gas phase (G), gas drying tubes (D), filling taps and other standard ancillary equipment. The gas sampling volume was principally used in the cali-

Jan 1, 1962

By B. J. Yamada, D. W. Fuerstenau

Long-chained neutral molecules (decyl alcohol) increase the flotation of corundum with sodium dodecylsulfate and trimethyldodecylammonium chloride as collectors. This phenomenon is postulated to result from coadsorption of the neutral molecules with the collector ions. Flotation and streaming potential experiments have shown that sodium laurate is an effective collector for corundum at more dilute concentrations than sodium dodecylsulfate or sulfonate.1>2 It has been postulated that this phenomenon results from the adsorption of both laurate ions and lauric acid molecules, whereas sodium dodecylsulfate can be adsorbed only as dodecylsulfate ions, since this collector does not hydrolyze under flotation conditions. Similar effects have been observed in alkaline solutions with dodecylammonium chloride and trimethyldodecylammonium chloride as collectors.&apos; If in- creased flotation occurs with the collectors which hydrolyze because of adsorption of the neutral molecules, purposeful addition of long-chained molecules should increase the flotation rate of minerals with such collectors as sodium dodecylsulfate or trimethyldodecylammonium chloride because these long-chained molecules should coadsorb with the collector ions. The effect of neutral molecules on flotation in these cases must depend on an adsorption mechanism which differs from that proposed by Cook for the adsorption of xanthic acid molecules by galena. For neutral molecules to function as collectors in the flotation of insoluble oxide minerals, adsorption of organic ions must first occur to provide a means of anchoring the fatty acid or amine molecules. Without adsorption of collector ions, flotation does not occur even in the presence of large quantities of neutral molecules, as is indicated by the cessation of flotation at low pH values with soaps as collectors or at high pH values with primary amine salts as collectors.&apos; Neutral molecules, such as fatty acids, must be adsorbed through van der Waals attraction between the hydrocarbon chains of the adsorbed soap ions and the hydrocarbon chains of the fatty acid molecules. The mutual association of hydrocarbon chains results

Jan 1, 1962

By H. Macpherson

Durhm has a well earned reputation for supplying some of the finest coking caals in the world. The caals, in general, vary in rank from 301 to 501/2. Durham has traditionally produced foundry coke for the major proportion of the foundries in Great Britah. Durham coals can be described as clean, soft coals, which yielded, with the old hand methods of coal getting, low ash small coal because the extraneous shale was normally harder than the coal and occurred in larger pieces. Under these conditions, with a plentiful supply of cheap labor, it used to be sufficient, at most collieries, to hand clean the large sizes of coal which could then be remixed with the untreated small coal to produce carbonization coals, ready for the coke ovens, at under 5 pct ash. With the introduction of mechanical methods of coal mining, the coal gradually required more cleaning. The first method adopted to resolve this problem was the introduction of pneumatic dry cleaners for the small coal. Although such machines had little effect on the fine coal (say below 1/8 in.), they could clean the intermediate sizes of coal. This, coupled with hand cleaning the larger sizes above 1-1/2or 2 in., resulted in a combined run-of-mine mixture below 6 pct ash, capable of maintaining the quality and reputation of the cokes produced. In more recent years, the intensification of mechanization and power loading, coupled with gradual exhaustion of the cleaner seams, has created the need for a more complete method of coal cleaning. This particularly applies in the fine sizes (say below 1/50 in.) which normally vary, under present day conditions, between 15 and 35 pct ash and are much too dirty to be included in the raw state in a carbonization mixture. This pronounced change has been accelerated because legislation controlling the dust conditions of mine airs for the prevention of pneumoconiosis has resulted in tk~e extensive use of water underground and a consequent increase in moisture content of the run-of-milie output. The presence of damp fine coal decreast the efficiency of prescreening and dry cleaners, so that this type of preparation for low ash coking coals is decreasing, although it is still used satisfactorily for industrial coals in the medium ash range. Table I shows the gradual increase in mechanization, the reduction in manpower, the increased use of explosives per ton of coal extraction, and the increase in the proportion of coal cleaned by mechanical means in Great Britain. Although similar figures are not available for Durham Div. until after the date of nationalization of the coal industry, it is probable that the increase in mechanical cleaning, particularly by dry cleaners, was more marked in the Durham collieries than elsewhere in the country. As dry clealiers were replaced by coal washeries in the Gritish ccal industry, no special attempts were made to recover the slurry, with the result that large outflows of dirty water were allowed, deposits of slurry came in to lagoons and neighboring streams, and a proportion of fine material was lost from the coking coal. This position, coupled with the higher moisture of the washed coking coal, resulted in adverse effects on coke oven throughputs and coke quality. It is now realized that the natural coal fines are an essential ingredient of coking coals in obtaining the correct coke structure in metallurgical cokes. This, together with economic pressure, led to the introduction of flocculation and filtration plants for the recovery of slurries, and later, when the ash contelits of the filter cakes were too high, to the introduction of froth flotation equipment. After this position had been reached, the tailings from the froth flotation pIants were, in many cases, still allowed to constitute an undesirable effluent. Recent legislation on river pollution has changed this picture; it is now necessary to provide a circuit which is completely closed so far as solids are concerned. The gradual increase in the coal cleaned by wet methods and froth flotation in Durham Div, is shown in Table 11. It is now an accepted feature of new Washeries that. froth flotation should be an integral part of the washing process from the initial installation of the plant.

Jan 1, 1962

By E. T. Turkdogan

Jan 1, 1962

By M. E. Fine, A. A. Henderson

Investigation of the tensile properties of silver based aluminum alloy crystals was undertaken because it appeared attractive for studying strengthening effects due to Suzuki locking with minimum complication. Yield drops were observed in all alloy crystals (1, 2. 3. 4, and 6 at. pct Al) after strain aging at room temperature. No yield drops were found in similarly grown and tested silver crystals. The yield effects are attributed to Suzuki locking but the major portion of the solid solution strengthening to other mechanisms. INVESTIGATION of the tensile properties of single crystds of silver alloyed with aluminum was undertaken because it appeared to be a system in which segregation at stacking faults associated with partial dislocations1 would be the dominant factor in anchoring dislocations. First, silver and aluminum have closely similar atomic sizes and thus solute atom locking of a dislocation due to elastic interactions should be unimportant. Second, while both X-ray2 and thermodynamic3 investigations show short-range ordering in silver-based aluminum alloys, the degree of local order is quite small (X-ray measurements give v = EAB - 1/2(EAA + EBB) = - 0.025 ev and thermodynamic measurements give v r -0.007 ev) and should not be important in strengthening dilute alloys. Third, the stacking fault energy of silver is probably low (as indicated by the profusity of annealing twins) and is very likely diminished further and quite rapidly by aluminum additions since the A1-Ag phase diagram shows a stable hexagonal phase at only 25 at. pct Al. Also, a careful investigation in this laboratory4 has shown that the ratio of twin to normal grain boundaries in recrystallized alloys increases with aluminum content. Thus, with minimum complication from other factors, Ag-A1 alloys seem attractive for studying strengthening effects due to segregation at stacking faults of extended dislocations. EXPERIMENTAL METHOD Single crystals measuring 250 by 5 by 1.5 mm of pure Ag (99.99 pct) and Ag-A1 alloys (A1 of 99.999 pct purity) of nominal compositions* 1, 2, 3, 4, and 6 at. pct were grown in high-purity graphite molds from the melt under a dynamic vacuum (1 x l0-5 mm Hg). The technique consisted of moving a furnace having a hot zone (which melted about 0.5 cm of alloy) over a horizontal, evacuated quartz tube con- taining the mold and alloy at a rate of 3/8 in. per hr. Chemical analysis showed roughly the first inch of the crystal to be solute poor, the last inch solute rich; and the center section uniform in composition within the sensitivity of the analytical method (± 0.2 at. pct Al). The center section of the crystal was cut into five specimens. Gage lengths of reduced cross section, measuring from 1.5 to 2 cm in length, were mechanically introduced by means of jeweler&apos;s files and fine abrasive cloth with the crystal firmly held in polished steel guides. One-third of the cross section was then removed by etching and electro-polishing, the crystals were all subsequently annealed for several days at 850°C in a dynamic vacuum (<1 x 10-5 mm Hg) and furnace cooled to 200°C. The crystal orientations were determined using the usual back-reflection Laue technique. The Laue spots were sharp and of the same size as the incident beam. However, microscopic examination showed the crystals to contain substructures with subgrains of the order of a micron in diameter. The details of this substructure are presently under investigation. Tensile testing was done with a table model Instron using a cross-head speed of 0.002 in. per min. For testing at various temperatures the following media were used: 1) 415oK, hot ethylene glycol; 2) 296ºK, air, acetone, water; 3) 273ºK, ice water; 4) 258ºK, ethylene glycol "ice" in ethylene glycol; 5) 200°K, dry ice in acetone; 6) 77ºK, liquid nitrogen. EXPERIMENTAL RESULTS A) Yield Behavior—A portion of an interrupted stress-strain curve for a 6 at. pct A1 crystal of the indicated orientation tested at room temperature is shown in Fig. 1. Initially, at (a), there is a small, gradual yield drop of about 10 mg per sq mm2. However, on stopping the test, and aging for a few minutes at (b), a sharp yield drop is found. Aging for longer times at (c) and (dl results in larger yield drops (and larger AT&apos;S). At, defined in Fig. 1, is usually larger than the yield drop by about 20 pct; however, this increase in the lower yield is transient since extrapolations of the flow stress curves join as may be seen from Fig. 1. (Both Laue and low-angle scattering photographs revealed no evidence of precipitation in a strain-aged 6 at. pct A1 crystal.)

Jan 1, 1962

By Walter Showak

The published phase diagrams for the copper-zirconium system1,2 indicate that the solid solubility of zirconium in copper is not accurately known. Studies made on relatively impure alloys by Pogodin, Shumova, and Kugucheva3 yielded a maximum solubility value of 1 wt pct Zr at the eutectic temperature. Allibone and sykes5 reported that an as-cast 0.2 wt pct Zr alloy is single phase at room temperature. Limited results obtained by Raub and Enge14 indicated that zirconium solubility in copper is less than 0.13 wt pct Zr at 940°C. Tn 1960, on the basis of a microstructural examination of several copper-rich Cu-Zr alloys, saarivirta6 placed the maximum solubility of zirconium in copper at 0.15 wt pct at the eutectic temperature, 980°C. The present note describes results obtained during a re-investigation of the Cu-Zr system for the purpose of accurately establishing the solidus and solvus curves and the eutectic temperature in copper-rich alloys. High-purity copper (99.99 pet) and zirconium (99.64 pet) consolidated reactor grade sponge were used to prepare several alloys, containing up to 2 wt pct Zr, by induction melting in graphite crucibles in vacuum and chill casting into a split steel mold. The melting procedure consisted of first melting the copper charge and then adding the bulk zirconium wrapped in pure copper foil. Chemical analyses were made of both the cold-rolled alloy ingots after homogenization at 925°C for 450 hr in evacuated quartz capsules and of small specimens which had been used in the phase diagram studies. &apos;The carbon content of each alloy was also determined and was found to be less than 0.001 wt pct in every case. Metallographic and electrical resistivity measurements were used as the primary methods for this investigation, although some thermal analysis studies were also performed. Heat treatments of all the alloys were carried out with the specimens wrapped in molybdenum or alloy foil (of the same composition as the specimen) and sealed in quartz tubes either in vacuum or under a purified helium atmosphere. Following high-temperature anneals for long periods of time, slight depletion of zirconium from the specimen surface was observed. Therefore, careful preparation of samples for microscopic examination and chemical analysis of the samples themselves was necessary to check the composition of samples used in determining phase boundaries. Points on the solvus curve were determined on quenched specimens by both isothermal reaction after solution heat treatment at 950°C for 8 hr and by isothermal annealing of alloy specimens at successively higher temperatures for times ranging from 24 to 500 hr. Liquation studies for positioning of the solidus and eutectic temperatures were performed by holding a pre-

Jan 1, 1962

By B. Wilshire, P. W. Davis

It has been shown that grain-boundary migration during high-temperature creep can reduce or even prevent the formation of intercrystalline voids, giving a considerable increase in ductility.&apos; A similar observation has been made in a recent investigation of the creep properties of various grades of nickel and nickel alloys. The results can be illustrated by the observations made on: a) Pure vacuum-cast nickel (99.993 pct Ni) b) Impure vacuum-cast nickel (99.97 pct Ni) c) Pure nickel containing internal voids (produced by a process of intering). d) A substitutional solid solution alloy of pure nickel containing 1.16 pct Sn. All the materials were given a high-temperature anneal (>850°C) to produce a stable grain size of 7 to 10 grains per linear mm. The apparatus and techniques used to obtain the present results have been described elsewhere.&apos; In this series, grain growth was observed only in the highest-purity, vacuum-cast metal. Thus we may consider that in the other materials grain-boundary migration was prevented by either preexisting voids or solute atoms. The effect of migration on the creep ductility of the above materials can be seen from Fig. 1, which

Jan 1, 1962

By T. H. Alden

In several recent studies of fatigue fracture in single-phase metals, tests have been made using the condition of essentially constant plastic strain amplitude.1-4 This procedure departs from the more common practice of holding the amplitude of stress constant. From these studies have emerged two important generalizations about the behavior of metals during cyclic straining. First, measurements of the stress amplitude, required to impose the fixed plastic strain amplitude, have shown that the rate of cyclic strain hardening in annealed metals is rapid in the early cycles but decays quickly to a very low value.1"5 This behavior is displayed particularly for a range of strain amplitudes below about 2 pct and at low and high temperature. Frequently, the hardening rate becomes so low that one can determine a "saturation" stress. This stress increases with strain amplitude. In addition, an experimental relation between fracture life and plastic strain amplitude was obtained by Coffin and Taternelli,&apos; namely N 1/2 ep = constant. For several metal:;, this equation has been shown to hold down to a strain amplitude of 0.1 pct. Whether it also holds in the "low amplitude" range (lives of more than about 105 cycles) has not been established. The importance of the saturation stress level (a value derived from strain hardening measurements) to the question of fracture life (the usual quantity of interest of fatigue testing) lies in the observation that cracks start to form when the cyclic hardening rate is essentially zero, and not before.4"5 This point suggests immediately a means of relating tests at constant stress and constant strain amplitudes. When making comparison, the stress in a constant stress test is to be identified with the saturation stress in a constant strain test. If these ideas are correct, then it should be possible, using the relation between fracture life and strain amplitude and experimental curves of saturation stress versus strain amplitude, to predict the fracture life as a function of stress, i.e. predict the S -N curve, for low stress fatigue. Saturation stress amplitude-plastic strain amplitude data, obtained in tension-compression, exist only for a few metals and for relatively high amplitudes of strain. Comparable S -N curves (push-pull loading) were known by the author only for OFHC copper. Values for this metal taken from Ref. 2 are shown in Fig. 1. The strain amplitudes, the lowest

Jan 1, 1962

By Harry M. Bendler, W. A. Wood

Electron metallography has been applied to the study of the torsional fatigue of polycrystalline OFHC* copper. The development of slip bands, fis- sures, and microcracks has been followed as a function of strain amplitude and number of cycles. Those factors that have been found to be relevant to a geometrical theory of the fatigue process are described. From the point of view of this theory it is important to distinguish between the effects of cycling at large amplitudes and at small amplitudes (true fatigue deformation). EARLY investigations showed metal fatigue cracking is caused by continued reversal of a small plastic strain. Fundamental study of fatigue, therefore, has been largely concerned with the cumulative effects of these plastic reversals on the metal structure. In particular, recent work has shown that the plastic reversals produce slip movements that are finer than the slip movements produced by unidirectional increments of plastic strain; individual slip movements in fatigue, for instance, are too fine to see by optical microscopy.2 It has also been shown that the fine slip movements of fatigue tend to concentrate in bands and that in this way they can build up, after enough cycles, a progressive surface disturbance. It is this disturbance which, in effect, makes the slip movement visible. It is also in this disturbance that the first cracks appear to form. From this point of view, therefore, the problem of fatigue becomes one of finding why the fine slip movements should concentrate in bands and why the. bands should finally open into cracks. Thus far, study of the slip bands has been limited to the changes they produce at the surface only. These studies have given interesting results. Ewing and Humfrey3 many years ago showed that the bands in iron could extrude debris. Forsyth found that bands in aluminum alloys could extrude thin tongues of material. Thompson showed that, after lightly dissolving away the surface of copper specimens, some bands persisted as superficial cracks might, and that the life of a specimen under fatigue deformation might be prolonged by dissolving away the surface at intervals. Thus these and related results have suggested that the metal structure in fatigue bands may disintegrate and that this may happen long before obvious cracking. These surface studies, however, have not shown definitely how cracking may begin, for they do not show sufficiently what is happening in depth. However, some advance in this direction has been made recently by a new approach, summarized later, which reveals slip bands and their surface disturbances in section. In the work done thus far, the sections have been studied by optical microscopy only. In the present work they have also been studied by electron microscopy with extended results. This paper also describes some observations on the surface disturbances prior to sectioning. These observations are relevant to a suggested theory of fatigue cracking. REVERSED SLIP MOVEMENTS Slip movements in fatigue deformation must reverse direction in each cycle. The question arises: DO the "backward" and "forward" movements take

Jan 1, 1962

By W. A. Tiller, J. D. Harrison

HOT pressing of powder particles has gained importance recently, since it affords a method in which high densities are rapidly attained. In a recent study on hot pressing of alumina powders, Mangsen, Lam-bertson, and Best1 have shown within the limits of their experiment, the validity the rate equation for densification in hot pressing, originally proposed by Murray, Livey, and Williams.2 i.e., where D = fraction of theoretical density, t = time, P = pressure and 77 is the viscosity, all in appropriate units. This equation was derived from earlier work of Shuttleworth and Mackenzie3 which is based on the closing of spherical pores under the action of surface tension. The integrated form of this equation yields a straight-line relation between log (1 - D) and t. Such conditions were found by Felten4 to be true only after extended periods of pressing. In an endeavor to quantitatively evaluate the exactitude of this equation in the initial sintering stage, i.e., prior to sealing of the pores, spherical anti-

Jan 1, 1962

By David V. Ragone, Richard E. Balzhiser

The liquidus uranium concentration in the U-Bi system is given by the following expression for the temperature range 400° to 800°C: No break was observed in the curve over this temperature range. The partial molar enthalpy change for uranium in the liquidus reaction, UBi2— U + 2Bi, was found to equal 12,300 cal per g mole. Copper produced a continuous decrease in the liguihs uranium concentration at 600°C. The presence of copper in the solvent was observed to affect the uranium activity coefficient according to the following expression: duced no change in the liquidus combosition below 0.6 at. pct Pd. Higher palladium concentrations sharply depressed the uranium concentration. SOLUTE behavior in molten alloys has been shown to be strongly influenced by the presence of additional species. Much attention has been given to such phenomena in iron-base systems where a number of alloying elements and/or impurities are likely to be present in small but significant quantities. Frequently, the interaction of these solutes has altered their thermodynamic behavior to the extent that reaction equilibra are appreciably influenced. Consequently, much of the information available for binary behavior must be reevaluated when additional components are likely to be present. Similar interactions can be expected to occur in bismuth-base solvents. Interest in the use of bismuth solutions of uranium as reactor fuels has stimulated investigators to explore the effect of various elements on the liquidus uranium concentration. Criticality requirements necessitate close control of the uranium concentration which, at the anticipated operating temperature of 500°C, approaches saturation. Consequently, elements which suppress the liquidus concentration could produce serious reactivity problems. Since the fuel solution is cer- tain to contain additives, such as magnesium and zirconium, for corrosion inhibition as well as small concentrations of fission products and corrosion products, a better understanding of the possible interaction phenomena is mandatory. This need stimulated experimental programs at the Brookhaven National Laboratory and elsewhere to determine precisely the liquidus uranium concentration in the bismuth-rich portion of several ternary systems. Early experimental efforts were directed toward an accurate dcmtermination of the U-Bi liquidus over the temperature range from 300&apos; to 800°c. As shown in Fig. 1, the results to date exhibit considerable scatter. The investigations of Bareis,&apos; Teitel,2 Greenwood,3 and Cotterill and hon4 agreed well below 700°c. Greenwood and Teitel extended their studies to higher temperatures but failed to concur in their results. A more recent study by Schweitzer and weekss at Brookhaven National Laboratory between 300&apos; and 725°c, produced values 15 pct lower

Jan 1, 1962

By W. F. Tanner

A river delivers a given load of sand, and hence heavy materials, into the sea. The load is fixed by drainage basin characteristics and processes. Wave energy available for redistributing that load is fixed in an entirely different way. An equilibrium diagram of these two parameters (load vs energy) pennits a tentative prediction of what will happen to the heavy minerals. Alluvial rivers transport a mechanical load which consists essentially of wash load (finer than about 0.05 mm in particle diam), bed load (coarser than about 0.10 mm) and the transition sizes in between. A few rivers carry no appreciable mechanical load, and are excluded from this discussion. An example of the latter is the Suwannee River of Florida, which empties across an oyster bar into the Gulf of Mexico and does not build a delta despite the absence of significant waves or currents in that part of the Gulf. An alluvial river may deliver its load into a protected sediment trap (such as an estuary, sound or lagoon), onto a low-energy coast (where it builds a delta) or onto a high-energy coast (from which spot the river load is swept away). The nature and disposition of the load depends, obviously, on three sets of factors: 1) drainage basin characteristics and processes, which determine quantity and make-up of the load; 2) coastal structure and geomorphology, which determine the kind of river-sea coupling which

Jan 1, 1962

By V. B. Kurfman

Grain refinement of Mg-Al melts by carbonaceous additions has been attributed to nucleation by aluminum carbide. The effects of process and alloy variables are interpreted and predicted in terms of the dispersion and chemistry of this phase. The grain coarsening action of Be, Zr, Ti, R.E., chlorination, temperature extremes, and prolonged holding times is described. Measures necessary to insure an adequate dispersion of the catalyst are discussed. CARBON inoculation treatments have become fairly well known and used for grain refinement of magnesium alloys containing Al. Although there is general agreement that a nucleation process occurs, the process is not understood and the inoculants are used in a rather empirical fashion. The treatment is applied to the class of alloys containing 3 to 10 pct Al, i.e., AZ31A to AM100A. Typical methods involve melting, alloying, and adjusting the temperature to 1400° to 1450°F. Then 0.01 to 0.5 pct C as CaC2, C6C16, or lampblack is added by any convenient means, and the melt poured within 10 to 30 min. Investigators generally have been impressed by an assumed similarity of this refinement process to superheat grain refinement, which depends on heating approximately the same alloys to a temperature in the range of 1550" to 1650°F, then pouring promptly after the melt is cooled to the pouring temperature. Various predictions have been made that carbon refinement would replace superheating in commercial practice due to reduced process costs, but this replacement has not fully taken place because of production difficulties and conflicting observations. Davis, Eastwood, and DeHaven1 agree with Nelson2 and wood3 in suggesting that an excess of inoculant may be harmful. Wood however says that overtreat-ment is not a problem in production use of hexa-chlorobenzene inoculation, and Hultgren and Mitchell4 claim no evidence of harm from excess additions. Various grain coarsening reactions are known to occur, including the possibility of overtreatment mentioned above. Trace amounts of Be,2 Zr, and Ti may prevent refinement by either a carbon treatment or a superheat. Occasionally treatment with cl25 may cause coarsening, although the Battelle refinement process&apos; uses a CC14-C12 blend. Grain coarsening also tends to occur on holding at temperatures below 1350°to 1400°F, especially after a superheat treatment, and for this reason Nelson2 stresses the desirability of a refinement method useful at lower temperatures for open pot melting practice. Since a carbon treatment can be made to work at temperatures below 1400°F, it seems desirable to investigate the mechanism of the refinement and the mechanisms of the coarsening reactions in order to establish control conditions for use in commercial production. The identity of the nucleating phase must first be established and then the factors affecting its chemistry and physical dispersion must be determined. THE IDENTITY OF THE NUCLEATING PHASE Davis, Eastwood, and DeHaven suggested that the nucleating phase in this system is Al4c3,1 but Mahoney, Tarr, and LeGrand8 disagree, largely because they found no evidence of the compound in alloys after carbon treatment and because there is no indication that aluminum carbide should be unstable over the temperature range used in the superheat treatment. This latter objection is based on the assumption that both the carbon treatment and the superheat treatment introduce the same nuclei. Electron diffraction studies have been made to identify the nucleating phase. Samples of grain refined A292 have been selectively etched SO that clean surfaces are obtained and so that secondary phases are in relief. Electron diffraction patterns from these surfaces have established that the carbon treatment of A292 introduces into the metal a large number of small, plate-like particles with a structure very similar to Al4C3. In most cases, the plate-like nature of the particles prevented positive identification but in the cases where the identification could be made the particles proved to be AIN A14C3. However, enough variation in lattice constants was observed so that all compositions from pure A14C3 to the 50:50 solid solution A1N.Al4C3 were probably present.14 In A14C3 and especially AlN.Al4C3 the A1 atoms occur in layers within which they have the same hexagonal symmetry and spacing as the Mg atoms in a single basal plane of a magnesium crystal. The solid solution spacing lies between the 3.16 of AIN and the 3.3? for Al4C3, in satisfactory agree-

Jan 1, 1962

By E. W. Greene, J. B. Duke

This paper deals with the application of froth flotation techniques to the beneficiation of kaolin clay and phosphate slimes, two very fine particle sized materials. The kaolin problem involves the removal of a small amount of a contaminating mineral (anatase), while the phosphate problem involves the concentration and recovery of a much larger percentage of apatite. Due to these differences, and also different response to flotation, the two problems are discussed in separate parts of the article. An idea of what is meant by "Ultrafine Minerals Or Slimes" as used in the title can be had by an examination of Fig. 1. Particle size distributions are presented for a crude kaolin clay, a coarse fraction and a fine fraction. The crude kaolin as mined was blunged with water, degritted through a 325-mesh Tyler screen, and dispersed with sodium silicate. The dispersed crude was then centrifuged in the laboratory into the coarse and fine fractions shown in the figure. The distribution curves were obtained by the well known sedimentation technique of Casa-grande1 using a long arm centrifuge to obtain equiva- lent spherical diameters down to 0.2 p on the finer fraction. Fig. 1 shows the coarse fraction kaolin to be 50% finer than 3 p, while the crude kaolin is 509 f&apos;lner than 1.4 p, and the fine fraction 50% finer than 0.46~. For comparison 53 p on the horizontal scale would represent Stokesian diameters which would just pass a 325-mesh Tyler screen, taking into consideration the Andreasen sieve correction factor of 1.22 times the screen opening. 2 Another helpful comparison is the surface areas, which in square meters per gram, are 0.044 for 53 p particles, 0.77 for 3p, 1.65 for 1.4 p and 5.0 for 0.46 p particles. Fig. 2 is an electron micrograph of a similar fine fraction kaolin showing the hexagonal plate-like particle shapes.

Jan 1, 1962

Jan 1, 1962