By W. J. Helfrich, R. A. Dodd

Binary aluminum solid-solution alloys containing various amounts of silver, magnesium, and zinc were prepared by careful directional solidification, and the hydrostatic and X-ray densities were compared. With the exception of the Al(Ag) alloys, the X-ray densities were consistently greater than the hydrostatic measurements, in agreement with earlier observations by Ellwood. In contrast to Ell-wood's interpretation in terms of vacant lattice sites associated with Brillouin zone effects, a tentative explanation based on the existence of solidification microshrinkage was favored. This hypothesis was confirmed by an examination of Al(Zn) alloys prepared by vapor diffusion of zinc into aluminum. The hydrostatic and X-ray densities were now in very close agreement, and it was concluded that the filling of Brillouin zones in aluminum solid-solution alloys does not necessarily result in the formation of defect structures containing an excess of vacant lattice sites. ThE existence of defect structures of the vacancy type in alloys in which the excess vacancies have an electronic rather than a thermal or mechanical, and so forth, origin is well recognized. Examples of incomplete lattices of this type are to be found in the Ni-Al,1-3 Fe-Ni-A1,4 c~-Ni-Al,5 Fe-Cu-Al,= and Co-A17 systems. These defect structures are of a special kind in that the intermediate phases possess an ordered atomic arrangement or superlattice, and in some instances the vacancy concentration may be unusually large, e.g., at 45.25 at. pet Ni in NiA1, approximately 8.8 pet of the lattice sites are unoccupied. Ellwood8-10 has reported similar defect structures in the aluminum solid solution alloys of the Al-Zn and A1-Mg systems and in alloys of the Au-Ni system." In Al(Zn) the (apparent) vacancy concentration rose, somewhat irregularly, to a maximum of about 2 pet vacant sites at 25 at. pet Zn, while in Al(Mg) the (apparent) vacancy concentration increased continuously to 1.7 pet at 15 at. pet Mg. An explanation in terms of Brillouin zone overlap was attempted, although Pearson12 has pointed out the difficulty of reconciling the observations with zone theory. However, the possibility of the effect being caused by the Fermi surface just touching a plane of energy discontinuity inside a prominent Brillouin zone has, in general, been accepted. In fact, Massal-ski13 has interpreted Ellwood's8 observations as confirmation of Leigh's14 theoretically predicted zone overlap occurring at approximately 2.67 electrons per atom. Unfortunately, Massalski was apparently unaware that Ellwood9 had revised his earlier results considerably, and the revised data did not confirm Leigh's analysis. Ellwood's clata were reexamined by the present authors who noted a possible correlation between the percentage defects as a function of alloy composition and the temperature interval of solidification measured from the respective equilibrium diagrams. This suggested an explanation in terms of shrinkage porosity rather than vacant lattice sites, and pointed to the desirability of reexamining appropriate alloy systems using: both Ellwood's method of specimen preparation (casting followed by wrought fabrication) and alternativ'e methods, i.e., diffusion, which might be expected to minimize, or even completely obviate, microporosity. ALLOY PREPARATION 1) Cast Allolys and Aluminum Single Crystals. Al(Ag), Al(Mg;l, and Al(Zn) alloys of various compositions up to 20 at. pet silver, 13.5 at. pet mg, and 30 at. pet Zn were prepared by melting under helium and casting into graphite molds. In the first two systems, the maximum alloying addition was quite close to the limit of solid solubility, but the possibility of transformation to a' during quenching somewhat restricted the suitable Al(Zn) composition range. The alloys were prepared from high-purity aluminum, a lot analysis showing 0.002 wt pet Cu, 0.002 wt pet Fe, and 99.996 wt pet A1 by difference. The silver, magnesium, and zinc were of 99.99+, 99.98+, and 99.998 wt pet respectively. Each composition was analyzed chemically. The as-cast ingots measured 7/16 in. diam and 5 in. length. One in. was removed from the top of the ingot, and the bottom 3 in. was machined to 0.275 in. diam; a point was also machined on the smaller diameter end. The remainder of the original ingot served as a top riser during subsequent remelting and controlled solidification. The machined ingots were now remelted using a Bridgman soft-mold technique to ensure directional solidification and, therefore, a minimum of micro-shrinkage. Alumina powder was used as mold material contained in an alundum thimble, and this crucible was placed in a helium-filled Vycor tube. The assembly was lowered through a suitable temperature gradient at approximately 0.5 in. min-l, and the risered portion of the casting was subsequently removed by sawing.

Jan 1, 1962

By Richard J. Borg

The vapor pressure of Cd in equilibrium with CdSb in the presence of excess Sb has been measured using the Knudsen effusion method over the temperature range 276° to 379°C. The free energy of formation of CdSb is given by AF° = -1.58 + 1.53 x l0-4 T, kcal per mole. The enthalpy and entropy are obtained from the temperature coefficient of the .free energy. CADMIUM and antimony have almost imperceptible mutual solid solubility but form a single stable intermediate phase, CdSb. This phase, according to Han-sen,l extends from about 49.5 at. pct to 50 at. pct Cd at 300°C and has the orthorhombic structure. The free energy of formation of CdSb can be calculated from the vapor pressure of Cd for compositions which contain less than 49 at. pct Cd. The appropriate reaction and formulae are given by Eqs. [I] and [2]- CdSb(s, ~ Cd(g)-, +Sb(s) [1] Since Sb is in its standard state, Af - N,,AF'-,, = NcdRT In a,, = NcdRT InP/PO [2] In Eq. [2], P, is the vapor pressure of Cd in equilibrium with the alloy, and Po is the vapor pressure in equilibrium with pure solid Cd. It is implicit in this calculation that the free energy only slightly changes within the narrow limits of the single phase field. Thus, the value obtained from the antimony-rich boundary is truly representative of the stoi-chiometric compound. The results reported herein are obtained from a mixture near the eutectic composition, i.e. 59 at. pct Sb. Only two previous investigations" of the free energy of formation of CdSb have been made. Both relied upon the electromotive force method, and measurements were made over relatively narrow temperature ranges which strongly influences the reliability of the values of AH and aS. EXPERIMENTAL The eutectic composition is prepared by fusing reagent grade Cd and Sb by induction heating in vacuo with the starting materials held in a graphite crucible having a threaded lid. The material obtained from the initial melt is pulverized, sealed under high vacuum in a pyrex capsule, and annealed at 420°C for two weeks. X-ray analysis"gives the following lattize parameters: a = 6.436A, b = 8.230& and c = 8.498A using Cu Ka radiation with A = 1.54056. These values are in fair agreement with the result? previously reported by Al~in:4 i.e. a = 6.471A, b = 8.253A, and c = 8.526A. Vapor pressures are measured using an apparatus which has been described elsewhere,= however, with a single important modification. Knudsen effusion cells are made of pyrex with knife-edged orifices made by grinding the convex surface of the lid on #600 emery paper. Photographs taken at known magnifications using a Leitz metallograph enable the determination of the orifice area. Numerous calibration measurements of the vapor pressure of pure Cd give close agreement with values previously reported5,= thus indicating that no significant error can be ascribed to the substitution of glass cells for metal cells used in previous work. Because the vapor pressure of Cd is reliably established and because it is difficult to obtain Clausing factors for the glass cells, the final values used for the orifice areas are calculated from the calibration measurements of the vapor pressure of pure Cd. Effusion runs are started in an atmosphere of purified helium which is quickly evacuated as soon as the cell attains thermal equilibrium. Less than one minute is necessary to obtain high vacuum after evacuation begins, and the temperature seldom varies by more than 0.5oC from the value obtained prior to pumping out the helium. RESULTS The results of this investigation along with other pertinent data are tabulated in Table I. Fig. 2 is the familiar graph of log P against T-10 K. At least mean squares analysis of the data presented in Table I yields the following equation: log1DJP = 8.790 - 6472 x T"1 [3] The deviations of the individual measurements from the values calculated with Eq. 131 are given in column six of Table I; the average deviation is 4.0% of the calculated value. Although the partial molal properties change significantly with composition within the single phase region, the integral thermodynamic value should remain relatively constant. Hence the results of the following calculations, which use the data obtained for the eutectic composition, are probably representative of the equi-atomic compound. Eq. [4] describes the vapor pressure of pure Cd as a function of temperature and may be combined with Eq. [3] to

Jan 1, 1962

Jan 1, 1962

By D. W. Mitchell

Mine fires are a serious hazard; surveys show that the coal-mining industry lags considerably behind industry in general in planning and training for fighting fires, and providing adequate fire-protection facilities. The results of the experiments discussed in this paper emphasize that every effort must be made to extinguish a fire in its incipient stage. The research also demonstrated that extinguishing agents and techniques, superior to those presently used in most operating mines, are available. An underground coal mine fire, if not extinguished quickly, can develop rapidly, create a serious hazard, and cause loss of life and property. The problem of controlling a fire increases in direct relationship to the time interval necessary to initiate control measures; as the fire increases in size and intensity it becomes progressively more difficult to cope with roof control, visibility, ventilation, and explosion prevention. Despite the constant vigilance of the industry, the number of coal mine fires is increasing. During the eight-year period, July 1952 to July 1960, following enactment of the Federal Coal Mine Safety Act, the Bureau of Mines investigated 401 fires that caused 30 fatalities and 75 injuries. More than half of these fires burned for more than one shift; 20 pct could not be extinguished by direct attack and had to be sealed. Agents and techniques for extinguishing simulated mining-machine and underground coal fires have been investigated in the Bureau's experimental coal mine. The research shows that visibility in the fire area is a primary factor affecting control operations. Associated with good visibility is accessibility to the fire; the closer the attack can be made, the less time and quantity of agent are required for extinguishment. Approach to the fire and visibility are hindered by the smoke and hot gases backing up against the ventilating current. In open entries an increase in air velocity assists in driving smoke ahead; at low airspeeds approach can be made by placing a brattice across the lower two-thirds of the entry, pushing the smoke ahead with water sprays, or discharging rock-dust from a rock-dust distributor. In a dead-end entry, fires can be approached by coursing fresh air along an airtight line brattice. However, it is safer, easier,

Jan 1, 1962

By C. G. Wilson

DURING the course of some experiments on the plastic deformation of gallium a standard stereo-graphic projection was prepared with (001) at the center and it was felt that this might be useful to others working with single crystals of gallium. The stereogram, given in Fig. 1, was made using the following crystallographic data (Bradley, 1935):

Jan 1, 1962

By J. Stuart Warner

The reaction COSO4(c)?CoO(c) + So3(g)was investigated from 950° to 1170OK by two different methods. The sulfate was decomposed in a previously evacuated space and Pso3 calculated from the measured total pressure on the assumption that Pso2 = 2P02. The sulfate was also decomposed under conditions of controlled oxygen pressure. The difference in the results obtained by these experimental techniques is attributed to the effects of thermal diffusion. The standard free energy change for the reaction is given by ?F° = 66,292 + 17.273T log T — 102.57 T (±300 cal/mole). It was found by DTA and X-ray diffraction studies that CoS04 undergoes a transformation at 617°± 4°C. THE metal sulfates may decompose directly to the oxide or pass through one or more intermediate basic sulfates. Provided the oxidation state of the cation does not change in the course of the reaction, the decompositions may be described in general as follows: One of the major objectives of this work was to determine the validity of Eq. [3] as much of the existing sulfate data has been calculated from decomposition pressures by Eq. [5]. The type of apparatus generally used for these measurements consists of a reaction vessel at high temperature which communicates with a manometer at room temperature. A temperature gradient is thus imposed on the gas phase causing thermal diffusion which brings about a partial separation of the different gaseous species present in an initially uniform mixture. The basic theory and experimental facts associated with this phenomenon are summarized elsewhere1 and it will suffice to state here that the heavier gaseous species diffuses down the temperature gradient. Since thermal diffusion destroys the homogeneity of the gas phase, it is not necessarily true that Pso2 = 2Po2 in any particular volume element of the gas phase even though there are twice as many molecules of SO, as of 0, in the gas phase considered as a whole. Under these conditions, the decomposing sulfate gives off SO, which dissociates to SO, and 0, and all three species are distributed throughout the system by thermal diffusion. However, the sulfate will continue to dissociate until the equilibrium value of PSo3 is established on the hot zone. Thermal diffusion may distribute SO2 and O2 throughout the gas phase in any way so long as Eq. [2b] is satisfied in the hot zone; i.e. Pso2(Po2)1/2=K3pso3. When a steady state is reached, we can characterize Pso2 in that

Jan 1, 1962

Pumping coal to market may help Appalachian coal operators increase their share of the eastern seaboard fuel business. Transporting it by pipeline is already an accomplished fact, but until recently it had to be dewatered to be used in boiler furnaces. The campaign for these eastern markets was begun in earnest last November by the widely publicized announcement of successful plant-scale firing of a central station boiler with coal slurry pumped to the burners. This latest advance makes coal similar to oil and gas in convenience in handling and controlling at the consumption end of the pipeline. Slurry could be considered a new commodity for the fuel market. HUGE POTENTIAL MARKET The heaviest concentration of power plants in the U.S. is along the line Washington, Baltimore, Philadelphia, New York and Boston which makes this region the best hunting ground for selling pipelined coal brought from western Pennsylvania and northern West Virginia. Furthermore, if this region is assumed to consume 125 million tons of coal annually, on a comparable basis, the consumption of oil and gas would be about 180 million tons. Even if all of this fuel is not consumed in central stations, it is still a very big market for coal at the right price. Consolidation Coal Co. and Texas Eastern Transmission Co. are trying to line up customers in this area so that a pipeline can be built. This is not to say that there are not many other areas in the U.S. that could not be supplied advantageously by a mine-to-market pipeline.

Jan 1, 1962

By G. W. Healy, W. D. Forgeng, N. R. Griffing

The liquidus surface of the C-Cr-Fe system to 1900°C has been mapped from carbon solubility and freezing point measurements, metallographic observations, and published data. In the graphite field, the surface drops precipitously to meet a slope descending from the Cr3C2-C join through the mixed carbide fields to a meandering eutectic valley; this flows from the Cr-C to the Fe-C edge. On the low-cavbon side of the valley, the surface rises to the chromium corner. 1 HE purpose of this inquiry was to gain a more complete knowledge of the C-Cr-Fe liquidus surface. This required an extensive study of carbon and chromium-rich alloys which, in the past, have received the least attention. Sanbongi el al.1 measured the solubility of carbon in liquid alloys containing up to 25 wt pct Cr at temperatures of 1460" and 1545°C and found that it increased with chromium content and temperature. Lucas and wentrup2 also made solubility experiments in graphite crucibles, but at higher chromium contents in the range of 38 to 80 pct and at temperatures of 1550" to 1700°C; however, their experiments were relatively few, and the effect of temperature was not consistent. The present investigation included compsitions ranging from 0 to 94 pct Cr and 1.4 to 11.7 pct C at temperatures up to 1800°C. Saturation experiments in graphite crucibles, thermal analyses during freezing, and metallographic and X-ray diffraction studies were employed to obtain desired information which, together with published data from other investigations about the binary edges and the ternary system at lower carbon levels, made possible the construction of a comprehensive C-Cr-Fe liquidus surface. C-CR-FE LIQUIDUS SURFACE The derived ternary liquidus surface is shown in Fig. 1 where the solid curves are liquidus isotherms. The dashed curves and the binary edges are the liquidus field boundaries of the primary crystals, the arrows along these boundaries indicating their direction with decreasing temperature. Each intersection of three internal boundaries is the composition of liquid involved in four-phase isothermal equilibrium with the three primary crystals whose liquidus fields touch there. It may be observed that a total of six four-phase equilibria occur at melt temperatures. The general topography of the liquidus surface consists of a eutectic valley sloping down from the Cr-C edge at 3.2 pct C to the Fe-C edge at 4.25 pct C. The liquidus surface rises in two directions from the valley, one hillside terminating at the Cr-Fe edge while the opposing hillside rises toward the carbon corner out beyond the top edge of Fig. 1. Both hillsides are interrupted by intersections of surfaces or joints representing the liquid colmpositions of various three-phase equilibria. Seven primary crystals occur, namely a(bcc), ?(fcc), graphite, (Fe, Cr)3C capable of dissolving as much as 15 pct Cr, and three different chromium carbides in which iron is partially soluble by substitution for chromium. The composition ranges of the primary l~hases at melt temperatures are shown

Jan 1, 1962

By C. W. Spencer, F. G. Hochgraf, R. F. Cheney

Columnar grained specimens of nickel, containing 0.25 pct Si and 0.22 pct Mn, have been exposed to liquid bismuth in the temperature range 670° to 1050°C. Under isothermal conditions the liquid penetration rate is constant. The activation energy for the process is 22,000 cal per g-atom. Small amounts of plastic deformation, introduced into specimens prior to exposure, increase the penetration rate. The slou. step in liquid film penetration is associated with a reaction which occurs at or near the leading edge of the film. Either transfer of nickel across the liquid-solid inteqace or diffusion in the grain boundary ahead of the liquid film is suggested. Aliquid metal, if brought into contact with the surface of an unstrained solid metal, will usually penetrate to some extent into the grain boundaries of the solid. Under isothermal conditions the extent of penetration after any particular time of exposure is related to the relative magnitudes of the interfacial tensions concerned.1,2 If the liquid-solid interfacial tension is less than one-half the grain boundary tension the liquid may penetrate at a relatively rapid rate for an indefinite distance into the grain boundary surfaces. If the liquid-solid interfacial tension is greater than one-half the grain boundary energy, liquid penetration occurs at a continually decreasing rate so that after the liquid has penetrated to a relatively short distance below the surface the process essentially ceases.3 Many observations of a qualitative nature concerning inter crystalline attack by liquid metals have been reported, for example, liquid bismuth upon copper,' liquid mercury upon brass,4 and liquid mercury upon nickel.' Scheil and Schessl determined the rate of penetration of liquid bismuth into the grain boundaries of hot rolled copper rod? At constant temperature, penetration rate was found to be independent of the depth penetrated, the rate in- creasing with increasing temperature corresponding to an activation energy of 20,000 cal per g-atom for the process. It was suggested that at lower temperatures the liquid travelled mainly along lines of three grain intersections while at temperatures greater than 1000°C essentially all grain boundary surfaces were covered. Recently, in a study of copper bicrystals having a common [loo] axis it was found that at 649°C bismuth penetrated 22, 25, and 63 deg boundaries while it did not penetrate 2, 12, 15, and 72 deg boundaries.' Elbaum reported that liquid gallium penetrates aluminum grain boundaries to a depth of 0.6 cm after 11 hr at 27°c.8 Assuming that the rate controlling step in the process was diffusion down the liquid film to the specimen surface, a diffusion coefficient of 10-5 cm2 per sec was calculated. This paper reports a study of the penetration of bismuth-nickel liquids into the grain boundaries of a nickel alloy, containing 0.25 pct Si and 0.22 pct Mn as principal alloying elements. The phase diagram

Jan 1, 1962

By P. E. Arnold, G. S. Ansell

RELAXATION in metals has been studied in detail by many workers in recent years.1-5 These studies have shown that there is an energy-loss peak observed in a metal placed in mechanical resonance at low frequencies which may be correlated with various metallurgical processes. These experiments have been largely used to study single-phase materials. In order to study the effect of a finely dispersed second phase in a metal matrix upon this phenomenon, the relaxation behavior of an aluminum-aluminum oxide SAP-Type alloy in both the fine-grained as-extruded and coarse-grained recrystallized conditions was investigated by the use of internal-friction measurements. The alloys studied, designated MD 2100, consist of a matrix of commercial-purity aluminum containing a finely dispersed second phase of aluminum oxide. The aluminum oxide is present in this alloy in the form of fine platelets approximately 130A units thick and several microns on edge. The mean free path betwen dispersed platelets is approximately 0.5 p. The grain size of this alloy is extremely stable at temperatures as high as the melting temperature of the aluminum matrix. In the as-extruded condition the grain diameter is several microns, while in the recrystallized condition it is several millimeters in diameter. The damping characteristics of the alloy samples were determined using a torsional-pendulum device. The internal-friction constant was determined for this alloy in both the fine-grained as-extruded and coarse-grained recrystallized conditions over the temperature range from 343" to 923°K at frequencies of 0.9, 1.3, and 1.8 cycles per sec. An internal-friction peak was observed in testing the fine-grained alloys which was not observed for the coarse-grained alloys. This peak, which might be associated with a type of grain-boundary relaxation, was observed at each of the three different test frequencies for the fine-grained sample. The temperature at which the relaxation peak occurred for each of the three different frequencies is shown in Table I. From these data an activation energy of relaxation for each pair of frequencies was determined by comparing the temperature shift of the relaxation peak with frequency between each of the test frequencies, assuming that an Arrhenius-type rate equation is applicable. The activation energy of relaxation determined from these data is also shown in Table I. The mean value of the activation energy was about 6 kcal per mole. The activation energy for the relaxation process determined in this investigation indicates that the relaxation associated with the grain boundaries in this aluminum-aluminum oxide SAP-Type alloy is quite a different process than grain boundary relaxation in single-phase aluminum alloys. In these latter alloys, the activation energy for relaxation has been found to be the activation energy for self-diffusion, approximately 36 kcal per mole1,2 Where the activation energy is the same as the activation energy for self diffusion, it has been proposed that the relaxation phenomena is dependent upon vacancy formation and motion. It is apparent therefore, that, in this aluminum-aluminum oxide SAP-Type alloy, the relaxation must be due to another type of atom transport. It has been shown previously in studies of the high-temperature, low-stress, steady-state creep behavior of as-extruded aluminum SAP-Type alloys, that the activation energy for steady-state creep is one that may be characterized by the nucleation of dislocations from the grain boundaries. It is proposed that the relaxation behavior observed here is due to a similar effect. In this case, the internal-friction peak is a resonance behavior due to the time-dependent nucleation of dislocations from grain boundaries in the sample. A process of this type would have an activation energy which is undoubtedly stress-dependent and of the form Q = Q, + (dQ/du)u

Jan 1, 1962

By Z. F. Danes

Combination of gravity data and density logs makes it possible to determine the structural relief. Under a wide class of geologic conditions, the solution is unique, or limited to a single parametric system of solutions. As a useful byproduct, the method yields a new way to construct derivative maps, continue the field up or down, subtract regional anomalies, and perform smoothing. In the past, the problem of interpreting gravity anomalies in terms of structural geology was solved along two main lines: 1) A body of a certain shape and density contrast was assumed and the corresponding gravity anomaly calculated, analytically for simple bodies, graphically and/or numerically for more complex ones; then the computed anomaly was compared with the observed one, and the assumed shape corrected according to the differences between the two. 2) The anomaly is assumed to come from a warped interface between two media of different density; the relief of the warping is assumed small compared to the depth of burial, so that the structure can be approximated by a flat horizontal surface of variable density distribution. The first method is a standard technique, described in every text book on applied geophysics, and is well applicable, for bodies with predominant vertical dimension. The second one, probably first used by Tsuboi and Fuchida,' is mathematically more elegant. It applies to the fashionable field of integral transforms (Bullard and Cooper, 2 Tomoda and Aki, 3 Dean 4) and is useful mainly in cases when the vertical relief of the structures is comparatively small. 30th methods, tacitly or openly, assume a density discontinuity across the boundary of the two media, while within each medium the density is constant. However, the recent invention of the gamma-gamma

Jan 1, 1962

By Ove Sandberg, Olav Bowitz

The operational characteristics of the Soderberg vertical spike anode are briefly discussed stressing the importance of the flow properties of paste in the fluid zone, the thermal shrinkage in the carbonizing zone, and the surface disintegration in the consumption zone. The requirements for paste recipe and binder quality are combined with design and operation of cell. A low temperature susceptibility of viscosity and low thermal shrinkage of paste together with a low microporosity of the binder coke are important properties. PRACTICAL application of Soderberg's idea of a selfbaking carbon electrode proved successful just before 1920. Shortly after, experimental work was started with the aim of developing a continuous electrode that could be adopted as anode in aluminium reduction cells. The intermittent operation of a large number of small prebaked anodes made the idea of developing a continuous anode for electrolytic production of aluminium especially tempting. Moreover, the electrode consumption in this process, even on a theoretical basis, is very high. Many installations were carried out in the 1930's and during the Second World War. During the tremendous post-war expansion of the aluminium industry, the Soderberg electrode has been steadily more widely adopted. Thus, today more than 60 pct of the Western World's output of aluminium is produced in cells with selfbaking anodes, see Big. 1. The quality of the anode paste of Sfiderberg elec- trodes is considered a major factor influencing the specific carbon consumption. The purpose of this paper is to survey the fundamental requirements which must be met in order to obtain good anode operation. We have limited this paper to a discussion of Elektrokemisk's research on the vertical spike type anode. I) FUNDAMEKI'TALS OF ANODE CARBON PERFORMANCE A) Brief Introduction. The only practical method for producing a conductive carbon anode of the size required is to form and carbonize a mixture of a carbonaceous binder and a precalcined dry aggregate coke. In the Soderberg electrode, the forming and carbonization take place in the electrolytic cell

Jan 1, 1962

By M. E. de Morton

Recovery and early recrystallization of heavily deformed, 99.98 pct Cr was investigated by studying metallographic structure. X-ray line sharpening, electrical resistivity, plastic properties, internal friction, and shear modulus. Appreciable recovery of resistivity, internal friction, and shear modulus together with some hardening and relief of internal strains occurred before the visible growth of a textured substructure above 350°C (recrystallization in situ). The complex behavior of shear modulus, internal friction, and its strain amplitude dependence during annealing are discussed qualitatively in terms of the relative mobility of dislocations. BY plastically deforming fully recrystallized 99.98 pct Cr above the brittle to ductile transition temperature, at -350°C. as in wire drawing, chromium can be made very ductile at room temperature. However, this ductility is lost on annealing at high temperatures when recrystallization takes place.' The present investigation was made to determine the general pattern of the changes in a number of physical and mechanical properties during recovery and recrystallization of heavily deformed chromium as part of an effort to elucidate the reasons for lack of ductility in the fully recrystallized condition. PREPARATION OF MATERIAL Wire specimens 0.027 in. in diam were prepared from arc-melted, electrolytic chromium by extruding, hot swaging and finally wire drawing at 300" to 350°C, i.e. above the brittle-to-ductile transition temperature. The total reduction in area of the wire was 98 pct and the last 3 pct of reduction was made at 100" to 150°C before cooling to room temperature. The impurity content of the material is shown in Table I. Internal friction and modulus measurements were made on a single specimen after annealing in situ at successively higher temperatures. For all other measurements, a fresh specimen was used for each temperature and annealing of these specimens was done in evacuated (0.001 mm Hg) and sealed silica tubes for 1 hr at the various temperatures up to 700°C. EXPERIMENTAL METHODS AND RESULTS The occurrence of a. transition in some physical properties of chromium at - 40°C2 imposed limitations on the temperature region where some of the measurements could be made. The reason for this transition in chromium is at present unknown but is probably associated with an antiferromagnetic state observed below - 40°C.* Heavy deformation produces an anomalous decrease in resistivity when measured at temperatures below -40°C4 though a normal increase is observed above this temperature. On the other hand internal friction in heavily deformed chromium5 over the temperature range 40" to 50°C is invariant with temperature. Above and below this range internal friction is strongly temperature dependent, increasing with increasing temperature. A temperature in this range was therefore convenient for both resistivity and internal friction measurements and for consistency the measurements of the mechanical properties were also made at about this temperature. No structural change has, however, been observed in careful X-ray measurements6 between -195" and 50°C, i.e. departure from cubic symmetry was not greater than 3:10,000; X-ray line sharpening measurements were therefore more conveniently made at room temperature.

Jan 1, 1962

By R. J. Jackson, D. E. Williams, W. L. Larsen

The phase diagram of the Ta-Zr system is presented with a discussion of the methods used in its determination. The solidus contains a minimum at 1820°C near 25 wt pet Ta. A complete solid solution exists at elevated temperatures between tantalum and ß zirconium. This solid solution decomposes monotectoidally at 800°C and 12 wt pet Ta. The maximum solubility of tantalum in a zirconium is slightly less than 2 wt pet, and decreases with decreasing temperature. The solubility of zirconium in tantalum is 5 wt pet at the monotectoid temperature and about 2 wt pet at room temperature. THIS investigation was part of a program of research on refractory metal alloy systems having potential application in nuclear reactor technology. Preliminary prop-ess has been reported in the Ames Laboratory annual research reports.l Most of the previously reported work on the Ta-Zr alloy system consisted of partial phase diagram investigations and the determination of the mechanical properties of the zirconium-rich alloys. Anderson eta1.2 studied alloys containing up to 30 wt pet Ta as part of an investigation of several zirconium alloy systems. These investigators also determined some of the mechanical properties of the alloys at room temperature and 650°C. In a discussion of Anderson's work, Pfei13 suggested that the bright phase in the microstructures of the intermediate alloys is a tantalum-rich solid solution or an intermediate phase in a matrix of ß zirconium solid solution. Litton,4 Keeler,5 and Chubb6 determined the mechanical properties of zirconium-rich alloys at ambient and elevated temperatures. Van Thyne and McPherson7 reported the tensile properties

Jan 1, 1962

By A. M. Gaudin

Jan 1, 1962

By Stanley D. Michaelson, Norman Weisis

The purpose of beneficiation is to increase the economic value of an ore by elimination of waste rock or by separation of minerals that require separate reduction, without destroying the physical and chemical identity of the minerals. Flotation has replaced older methods of beneficiation to a very great ex- tent, nearly entirely in the case of the copper, lead, and zinc minerals and less completely in the case of such other minerals as iron, coal, and titanium. Flotation is also used to recover barite, fluorspar, feldspar, cement rock, spodumene, vermiculite, silica, beryl, and potash in the nonmetallic field, and cobalt, vanadium, germanium, antimony, mercury, molybdenum, manganese, nickel, gold and silver, cadmium, and bismuth for metals. The rapid growth of flotation to pre-eminence cannot be attributed to its low cost, because gravity, magnetic, and electrical methods may in some cases cost only half as much. But for ores containing finely disseminated minerals, these other methods are successful only in exceptional cases, for example the magnetic taconites or titanium-bearing sands. For low grade ores with coarse texture or spotty mineralization the advantages of low-cost gravity methods and highly efficient flotation are often combined, as in the beneficiation of coal and some ores of lead and zinc, phosphate, tungsten, and manganese. When an ore is responsive to either flotation or non-flotation concentration, or to combinations of the two, the choice depends upon cost of the process only when dealing with ores of low value; in other cases it is dictated by either the process efficiency or the product specification. Generally speaking, flotatio.1 is so efficient as compared with other methods of concentration that process cost is rarely an important factor in its selection. It is said, "The metal in the mill tailing has already been mined." Once the mining cost has been paid it doesn't increase total costs very much to do a thorough job of milling. With the exception of the few types of ores that are not amenable to flotation, the chief reason for preferring electrical and gravity methods to flotation may lie in the specification of the product. Flotation demands fine grinding, and specifications may not permit this with many nonmetallic ores or coal. Another reason is the size of investment-where capital is hard to obtain or the life of the property is short, the justification for a flotation plant may not exist, and one must be content to skim off the cream. y not exist, and one must be content to skim off the cream. Gravity processes often cost less than flotation because a large part of the waste rockcan be rejected without costly grinding, no chemicals are required,

Jan 1, 1962

By Arnulf Muan, W. C. Hahn

Activities of "FeO" in "FeO"-MgO solid solutions have been determined in the temperature interval 1100" to 1300"C by equilibrating oxide samples with pure metallic iron in atmospheres of known oxygen partial pressures. The end members "FeO" and MgO form a complete solid solution series. The system shoztls a considerable positive deviation from Raoult's law. A large amount of data has been accumulated during the past 50 years on stability relations existing among various crystalline and liquid phases in oxide systems of importance in metallurgical processes. By comparison, very little is known about the thermodynamic properties within the various homogeneous phases present in the systems, particularly the crystalline phases. The present paper deals with determination of activities as a function of composition in solid solutions of wüstite ("FeO") and periclase (MgO). Such solid solutions ("Magnesiowustites") have simple sodium chloride structure and are known to be continuous between the end members at elevated temperatures (> 1000°C) and strongly reducing conditions such as prevail in contact with metallic iron. Wiistite has a defect structure in which the ratio of oxygen to iron varies and never has as low a value as 1:1 corresponding to the simplified formula FeO. Within the range of stability of this phase, the composition changes between a maximum oxygen content of approximately 25.6 wt pct (corresponding to the formula FeO.83O) and a minimum oxygen content of approximately 23.2 wt pct (corresponding to the formula Fe0-96O). The activity data to be reported in the present paper are based on using as standard state the wüstite which is in equilibrium with metallic iron at a particular temperature, i.e., "FeO" of minimum oxygen content at each temperature. For sake of simplicity, the formula FeO will be used to represent the wustite phase in the remainder of this paper. Consider the reaction 2 FeO solid solution = 2 Femeta1 + Ozgas in which FeO dissolved in another oxide dissociates to metal and gas. The activity of FeO in the solid solution, relative to "pure FeO" in equilibrium with metallic iron as a standard state, is then expressed as Here Po, and po2 * are the partial pressures of oxygen of the gas phase in equilibrium with metallic iron and the oxide solid solution or "pure FeO", respectively. The equation holds only if the metal phase is essentially pure Fe. The oxide combinations used in the present investigation fulfill this requirement. Magnesia is so much more stable than FeO that for all practical purposes aFe = 1 in the metal phase present in all mixtures used in this investigation. I. EXPERIMENTAL METHOD 1. General Procedure. The experimental method used was analogous to that developed by Foster and Welch1 and used recently by Hahn and Muan.2 It consisted of four steps: a) Determination of the equilibrium between FeO and Fe. b) Determination of d-spacing change with composition in oxide solid solutions (FeO-WO). c) Equilibration of various members of the solid solution series with a metal phase and a gas phase of known oxygen partial pressure. d) Determination of compositions of solid solutions resulting from step (c) by means of data obtained in step (b). 2. Starting Materials. General Aniline and Film Corp. carbonyl iron powder, type HP, was used as the source of metallic iron. A representative analysis was as follows: Fe, 99.6 pct; C, 0.01 to 0.04 pct; 0, 0.1 to 0.3 pct; N, 0.00 to 0.05 pct. Other elements were present as traces only. Wiistite was prepared from "Baker Analyzed" Reagent grade Fe2O3 of reported analysis as follows: Assay (Fe2O3), 98.8 pct; insoluble in HC1, 0.02 pct; not precipitated by NH,OH, 0.02 pct; Zn, 0.003 pct. Production of wüstite was achieved by a two-step

Jan 1, 1962

By E. H. Crabtree, J. D. Vincent

Probably no metallurgical process in the history of the mining industry has been responsible for such increased mineral production as has flotation. It has made possible the economic treatment of low grade and complex ores which, with the old methods of gravity concentration, would have been classed as worthless. Starting with the sulfide ores of copper, lead, and zinc, the process has been applied to almost all metallic and nonmetallic minerals. Today, the sulfides of the common metals not only can be readily recovered, but can be separated from each other. Thus, three or four mineral recoveries from the same ore, such as galena, chalcopyrite, sphalerite, and pyrite, are possible. Molybdenite is recovered initially with copper sulfides and the two are subsequently separated. Flotation of metallic gold and of native copper and graphite is being commercially practiced. The carbonates of some of the base metals, principally those of lead, can also be concentrated. Flotation of the oxides, silicates, phosphates, and other so-called non- metallic minerals represents the greatest advance in the art in the last few years. Today, commercial plants are successfully treating such minerals as feldspar, garnet, ilmenite, muscovite, cassiterite, cement rock, fluorspar, phosphate rock, sylvite, and a host of others. Flotation of the various types of iron ores along with other concentration methods is today the subject of a tremendous amount of investigation on the iron ranges. EARLY PATENT HISTORY OF FROTH FLOTATION Although what we call the froth flotation process as distinguished from bulk oil processes was not used commercially until 1905, many investigators had recognized its possibilities long before the twentieth century. The principal patents issued throughout the years give us a method of recording early flotation history. BULK OIL PROCESSES: In 1860, William Haynes patented (British Patent 488) a process for separating oil-wetted sulfide minerals from water-wetted gangue minerals by agitating the dry ground ore with oil and then the mixture with water. In 1877, the Bessel brothers patented (German Patent 42, Class 22) a process where a mixture of graphite ore was mixed with 1 to 10% oil; after adding water, the

Jan 1, 1962

By Lawrence H. Van Vlack, Otta K. Riegger

Periclase-type oxides were examined microscopically after being exposed to siliceous liquids. The rate of grain growth was found to be inversely proportional to the grain diameter. Grain growth proceeds more rapidly at higher temperatures, but is retarded by increasing liquid contents. aMag-nesiowiistites with higher MgO contents grow less rapidly than those with higher FeO contents. The growth rate is reduced by the presence of a second solid phase. The silica-containing liquid penetrates as a film between the individual magnesiowus tite grains. This is independent of time, temperature, amount of liquid, or the MgO/ Fe0 ratio. When present, olivine and spinel-type phases can provide a solid-to-solid &apos;&apos;bridge" between magnesioustite grains. THIS paper presents the results of a study of the microstructures of periclase type oxides in the presence of a silicate liquid. The purpose was to learn more about the effect of service factors such as 1) time, 2) temperature, and 3) liquid content upon A) grain growth, and B) liquid location among the solid grains. This study was prompted by the fact that periclase refractories are known to have very little solid-to-solid contact when the phases which are present are limited to periclase and liquid. Such a micro-structure gains industrial significance because it permits fracture during service when stresses are applied at high temperatures. The details of ceramic microstructures have not received extensive attention. This is in contrast to the extensive attention given to a) the phase relationships pertaining to refractory compositions, and b) the details of the microstructures of comparable metallic materials. A brief review will be made of the pertinent phase relationships and microstructural considerations in general, as well as of refractory compositions. a) Phase Relationships. This investigation was limited to those compositions in which (Mg, Fe)O was the solid phase. MgO and FeO form a complete series of solid solutions. Pure MgO has the name of periclase. The related FeO structure is called wustite. Both have the NaC1-type structure: however, wustite possesses a cation deficiency so that the true composition is Fe<10 even in the presence of metallic iron. The phase relationships involving solid (Mg, Fe)O and a silicate liquid are shown in Fig. 1. In this case. the liquid is saturated with (Mg, Fe)o. There-fore its SiOz content is below that encountered in orthosilicate liquids. As a consequence the liquid phase specie:; are primarily the following ions: and 0-&apos; plus occasional Fe+ ions. Two features are of importance: a) the liquid contains relatively small species and b) the liquid contains large quantities of the same species as the solid. viz., Fig. 2 shows the system, FeO-SiOz, which will be used in some of the discussions that follow. This diagram is the right side, vertical section of Fig. 1. Here, as pre\iously, the composition at the FeO end of the diagram is nonstoichiometric, varying from Feo.950 when the liquid oxide is in contact with the solid iron, to about Fe 0, when the solid oxide is in equilibrium with an atmosphere of equal proportions of CO and C02 at the solidus temperature. The Fe/O ratio will be maintained in wustite in the presence of SiO,. However, the FeM/Fe++ ratio in the liquid will be lower because of the effect OIF the SiO, on the activity of the FeO. With the addition of MgO to wustite, the over-all composition (IvZg, Fe)@, has a value of x lying between 0.9 and 1.0 when the COz/CO ratio is 1.0&apos;. b) Microstructures. In general, published attention to refractory microstructures has been directed toward the phase analyses that accompany compositional variations. This is illustrated by Harvey6 in his work on silica brick and by wells7 in his work on periclase brick. In each case, a series of altered zones is encountered which provides a sequence of phase associations. If due consideration is given to reaction kinetics, such an examination reveals phases that are compatible with equilibrium studies. Admittedly, however, it is often necessary to determine more complicated polycomponent systems to account for all the phases present.8 Relatively little attention has been given to microstructural geometry in ceramic materials. Certainly less attention has been given to this aspect of ceramic microstructures than to the size, shape, and distribution of the constituent phases in metals. Burke has pointed out that the grain size of oxides follows the same growth rules as for metals, viz.,

Jan 1, 1962

By A. M. Gaudin, T. P. Meloy

Based on the equation for single fracture, a formula has been obtained for repeated fracture. Solution of this equation is obtainable analytically for a few examples and numerically for all others. Graphs of the size distribution equations have been obtained; they agree broadly with the experiments of others. In another paper1 we have considered a model and a comminution distribution equation for single fracture of brittle materials. Most comminuting devices, however, depend on the occurrence of repeated fracture. This is especially true of continuous cylindrical mills of the ball, tube, or rod type. But even in primary crushers there is some repetition of the breaking process, so that this paper should be of interest in connection with all comminuting devices. HALF LIFE AND PROBABILITY OF FRACTURE To facilitate the study of fracture it is useful to introduce the concept of the half life of a particle, In the ball mill, for example, we may start with 10,000 feed particles. The time, 7, by which one half of these particles have been broken is the half life of the feed under the prevailing experimental conditions. The probability of breakage bears an inverse relationship to the half life. In a ball mill, for instance, it can be shown that the

Jan 1, 1962