By B. H. Kear, H. G. F. Wilsdorf

After a few percent strain, dislocations in disordered Cu3Au are arranged in groups in ulell-defined slip planes, which contrasts with the more or less random distribution of dislocations in the corresponding ordered alloy. Unusually long and straigkt dislocation segments observed in the ordered alloy are interpreted in terms of cross slip of screw dislocations from their slip planes into cube planes. It is proposed that cross slip, and also dislocation reactions of the Lomer type, play an important role in work hardening of the ordered alloy. ACCORDING to to dislocations in the disordered lattice are only partial dislocations in the corresponding super lattice, so that in the super-lattice dislocations must occur as pairs, with each pair connected by a ribbon of antiphase boundary. Recently, striking confirmation of the theory was obtained by Marcinkowski, Brown, and Fisher3j4 in a study of dislocation configurations in thin foils of the Cu3Au alloy by transmission electron microscopy. In the present investigation, the observations made by these workers have largely been confirmed. Moreover, it has been found that dislocations in the plastically deformed ordered alloys are often unusually long and straight. This paper is mainly concerned with these new observations. A tentative explanation is offered in terms of cross slip of dislocations in the ordered alloys. PREPARATION OF SPECIMENS An alloy close to the stoichiometric composition Cu3Au was prepared by melting together high-purity copper and gold (99.995 pct) under vacuum in a graphite mold. The resulting ingot was rolled down and cut into strips 1 1/2 by 1/8 by 0.005 in. in thickness. All strips were annealed at 900°C for 3 hr and cooled to 500'~. A few of the strips were quenched from ~OO'C, while the remainder were slowly cooled in the temperature range 400" to 150°C at intervals of a few degrees every 24 hr to produce a high degree of order. After this annealing treatment the average grain size of the material was about 0.1 mm. Material in different states of order was obtained by reannealing fully ordered material at temperatures below the critical temperature: followed by quenching. The equilibrium degree of order attained at a particular reannealing temperature was obtained from the paper by Keating and warren.' A simple hand-operated tensile jig was used to give the strips the required amounts of plastic strain. Following straining, a number of specimens were cut from each strip by means of an electrolytic cutting device.= Finally, each specimen was thinned electrolytically using the polishing procedure described by Bakish and Robertson,7 and these thin sections were examined in the Philips EM-100B electron microscope operating at 100 kv. EXPERIMENTAL OBSERVATIONS Antiphase boundaries. The average domain size in the ordered alloys was found by direct observation to be about 0.25 p. Also, it was observed that the grown-in configuration of antiphase boundaries was changed little by plastic deformation, at least up to 6 pct strain. Fig. 1 shows an electron micrograph of a thin foil of partially ordered alloy (S - 0.8) after 3 pct strain. The micrograph shows a few dislocation pairs and a somewhat crystallo-graphic network of antiphase boundaries. The normal to this foil was found by diffraction analysis to be approximately 11121, with principal directions in

Jan 1, 1962

By C. G. Rhodes, D. Kramer

The kinetics of precipitation of transient a phase during the transformation in U-16 wt pct Mo between 400° and 550°C were studied using quantitative metallography and electrica1 resistiuity measurements. The volume percent of a phase goes through a maximum in time, corresponding to a critical degree of progress of y' formation. prior to its re-solution after prolonged annealing. The fastest rate of a precipitation oc-cuvs at 500°C with a concomittant lowest peak of 9.5 vol pct a. At 450°C, 14 vol pct a, greatest fov any temperature, was observed after 24 hr witlz an associated slowest rate of formation. a precipitation at 400°C ceases after approximately 160 hr and the amount of a present remains unchanged after long times at temperature; no y' was observed metallographically at this temperature. IN the U-Mo system at 16 wt pct Mo, an ordering reaction takes place below 600°C, see Fig. 1, whereupon the random bcc solid solution, y, transforms to the ordered bct phase, y'."2 The new unit cell is constructed of three old unit cells somewhat distorted. While attempting to study the kinetics of this transformation it was observed that an unexpected phase was precipitating out early during the transformation anneal reaching appreciable amounts before disappearing after long times. The y' appeared in the presence of this new phase and after long times constituted the whole sample. Owing to the high optical activity of this unexpected phase under polarized light, it was suspected to be the a phase. Subsequent X-ray powder pictures confirmed this belief. The kinetics of a phase formation and disappearance is the subject of this paper. EXPERIMENTAL PROCEDURE A) Alloy Preparation. Alloys for this study were prepared by vacuum induction melting normal reactor grade uranium and 99.5 wt pct Mo pellets in thoria crucibles. Two ingots were prepared, and sections of the top and bottom of each ingot were chemically analyzed for uranium and molybdenum content. The results of the analyses appear in Table I. B) Metallography. Samples of 16M were wrapped in tantalum foil, sealed in evacuated (5 X 10"6 mm of Hg) quartz capisules, and annealed at 1110"C prior to being transferred directly to the transformation temperature. They were examined metallographically after increasing times to determine the progress of the transformation at 400°, 450°, 500°, and 550°C. The samples were prepared for metallographic examination by mechanical polishing with diamond paste and electrolytic polishing with a solution of glacial acetic acid and chromic acid. Since the y' phase is tetragonal, its presence can be detected by viewing the sample in polarized light. To increase the contrast between y' plates, the samples were electro-etched in a 10 pct oxalic acid solution. To reveal a phase in bright field (it can be seen in polarized light in the "as-polished" state), the samples were electro-etched in a solution of citric acid and nitric acid. To determine the vol pct a phase, a variation of the one dimensional systematic point count method as described by Hilliard and cahn3 was used. The

Jan 1, 1962

By P. E. Doherty, B. Chalmers

Subboundaries may be revealed in aluminum by the formation of pits on the surface during cooling from elevated temperatures. The pits do not form in the vicinity of high- or low-angle boundaries. They are attributed to the condensation of vacancies from a super saturation produced during coolirzg. Using the vacancy pit and Schulz X-ray techniques for observing low-angle boundaries, a study was made of the transition from the nearly perfect seed to the striated structuke characterist-ic of aluminum crystals grown from the melt. It was found that the individual striation boundaries develop by the coalescence of very small-angle boundaries, as well as by the addition of individual dislocations. Several mechanisms for the formation of striations are discussed. Evidence was found suggesting that a super-saturation of vacancies exists near a growing interface, and it is proposed that the resulting climb of existing dislocalions produces "half'-loops" at the interface, which combine to form the low-angle striation boundaries. LINEAGE, or "striation" boundaries, have been studied in detail by Teghtsoonian and Chalmers 1,2 in crystals of tin grown from the melt, and by Atwater and Chalmers3 in lead. They found that single crystals grown from the melt consist of regions which are separated by subboundaries that lie roughly parallel to the growth direction. A difference in orientation of 0.5 to 3 deg exists between the striated regions; the misorientation is such that the lattice of one region could be brought into coincidence with the lattice of its neighbor by a rotation about an axis approximately parallel to the direction of growth of the crystal. They observed an incubation distance for the formation of striations which increased with decreasing growth rate. They also found that in any crystal, the sum of all rotations of the lattice in one sense, in going from one striation to the next, is very nearly equal to the sum of all the rotations in the opposite sense. A striation boundary, which is a low-angle grain boundary, can be described as an array of dislocations. If it is assumed that suitable dislocations are introduced into the crystal during solidification, the formation of striation boundaries can be explained as a result of the migration of the disloca- tions into arrays. The formation of arrays is energetically favorable since the energy of an assembly of dislocations can be reduced by the interaction of the stress fields when a suitable array is formed. This investigation presents and interprets new information concerning the nature and origin of striation boundaries in aluminum. EXPERIMENTAL TECHNIQUE Single crystals of high-purity aluminum (Alcoa 99.992 pct) were prepared by horizontal growth from the melt.'' The specimens were subsequently electropolished in a solution of 5 parts methanol to 1 part perchloric acid kept between -10° and 0°C in a bath of dry ice and alcohol. The current density was approximately 6 amps per sq in. Doherty and Davis9 have shown that in aluminum sub-boundaries with misorientations of not less than several seconds of arc may be revealed by the vacancy pit technique. During cooling from elevated temperatures pits form on electropolished surfaces of aluminum crystals as a result of the condensation of vacancies.11 Pits do not form in the vicinity of small- or large-angle grain boundaries, presumably because such boundaries act as sinks for vacancies. Boundaries of misorientations down to 3 sec of arc are revealed as pit-free regions, see Fig. 1. The Schulz X-ray technique12 was used to determine the angular misorientations of subboundaries. In this method, white radiation from a micro-focus X-ray tube is used to produce an image of a fairly large area of a single crystal surface. Subboundaries cause splitting in the diffracted image, see Fig. 2. Misorientations down to about 15 sec of arc may be observed with this technique. OBSERVATIONS AND DISCUSSION Figure 1 shows a striated aluminum crystal grown at 10 cm per hr etched by the vacancy pit technique. An incubation distance of about 1 cm is observed before the initiation of striation boundaries. Fig. 2 is a Schulz X-ray photograph of a striated crystal similar to that shown in Fig. 1. A large area of the crystal was studied by means of a series of photographs. Fig. 2, which is a reflection from the (100) plane, included about the first 4 cm of crystal to freeze. There is an incubation distance of about 1 cm, and a distance of about 2 cm over which the angle of misorientation builds up to its final value of approximately one degree. Some twist component can be seen in Fig. 2 at the right side of the photograph. From Fig. 2 it can be seen that the sum of all rotations of the lattice in one

Jan 1, 1962

By H. Warlimont

In recent investigations of the microstructure and crystallographic features of martensite by electgon microscopy,', '9 thin films (about 50 to l000A in thickness) have been used as specimens. It was found by W. Pitschl ,2 that the lattice relationships between the supefiaturated fcc matrix and the martensite formed in thin films were different from those observed after transformation in bulk material. Corresponding differences are to be expected in nucleation and in reaction kinetics in the formation of martensite in thin films, but have not yet been reported. In the course of the preparation of thin films of iron-base alloys for investigation by electron microscopy it was observed that films of alloys, whose martensite formation temperature (Ms) was below room temperature, formed martensite during the electrochemical thinning process conducted at or above room temperature. The chemical compositions and approximate bulkM,-temperatures of the three materials on which this observation was made are listed in Table I. The alloys were vacuum-melted from high-purity metals. It can be seen that the effect occurred in alloys that contain only sub-stitutional components as well as in alloys that contain carbon as an interstitial solute. The appearance of martensite formed in this manner is illustrated in Fig. 1, which represents a polished film of alloy No. 1 at XI0 magnification. The martensite plates can be recognized by their surface relief effects. In addition, heavily strained (owrinkledo) austenite can be seen near the edges of the film where it is thinnest and transformation stresses or strains can be accommodated by plastic deformation most easily. The nonuniform distribution of transformed regions is probably due to the varying thickness of the film. These observations were common to all materials listed in Table I. Because effects of supercooling or straining can

Jan 1, 1962

By J. J. Gilman

Rates of prisnzatic plastic glide ( {1010}<2110>) in pure Cd crystals have been measured at temperatures from 158° to 276°C. The glide rate is proportional to the 2.75 power of the applied shear-stress. The activation energy is 29.2 kcal per mol. It is suggested that the rates of prismatic glide in Cd and Zn crystals are determined by the strengths of the atomic bonds across the prism planes. ALTHOUGH zinc and cadmium crystals both have hexagonal structures with nearly the same c/o ratios, their mechanical behaviors are quite different. Whereas zinc becomes quite brittle below room temperature, and cleaves readily on (0001) planes, cadmium is very ductile even at 4.2°K, and cannot be cleaved at any temperature. As part of a search for the explanation of this difference in behavior, a study has been made of prismatic glide in cadmium. It complements a previous study of the same phenomenon in zinc.1 The primary glide plane in cadmium is the basal (0001) plane, and the primary glide direction is the direction of atomic close-packing <2110>. However, if a tensile stress is applied parallel to the basal plane, then the shear stress on the basal plane equals zero so basal glide cannot occur. At low temperatures, deformation by twinning occurs; but at high temperatures, it has been found in this study that gliding on prismatic planes (1010) occurs in the close-packed direction. This is completely analogous with the case of zinc, except that lower temperatures are required. EXPERIMENTAL The experiments were done in nearly the same way as for zinc.&apos; Therefore, only the differences in the two sets of experiments will be described here; for other details the reader is referred to the previous paper. Crystals 6 by 6 mm sq were used that were grown from "Super Purity" 99.999 + pct Cd purchased from the New Jersey Zinc Co. The crystals were grown with their basal planes parallel to both the rod axis and one of the flat sides of the square cross section, A close-packed direction in the basal plane was oriented parallel to the rod axis. Gage sections were carefully machined into the crystals, and the surface damage caused by machining was removed with the same chemical polishing reagent as had been used for zinc. Thus, specimens of the same form and size as the previous zinc ones were produced. The crystals were heated to the test temperatures in a silicone oil bath (fused salts were tried first, but they reacted badly with the cadmium). An Instron tensile-testing machine was used for applying stresses to the crystals at various constant strain-rates. RESULTS The general behavior of cadmium crystals is much the same as for zinc. Only the constants that measure specific properties are different. Just as

Jan 1, 1962

By A. Lawley, H. W. Schadler

TWINNING has long been recognized as a possible mode of deformation in crystalline solids and has been studied in a wide variety of crystals.&apos; Recently, deformation markings which have the topographical characteristics of twins have been seen in tungsten" and the body-centered cubic alloys of tungsten and molybdenum with rhenium.3-7 These markings have been identified as twins because: 1) they are visible after polishing and etching;2,3 2) their formation is accompanied by an audible click and a drop in load;4 and 3) the habit plane is {112}, the plane which has been identified as the twinning plane for several body-centered cubic metals.&apos; However, there has been no published evidence for the specific determination of the twinning direction in rhenium alloys of tungsten and molybdenum, because usually the deformation twins were not broad enough to be detected with a conventional X-ray beam. Consequently, [111] is inferred as the twinning direction since the latter must lie in a plane of symmetry perpendicular to the twinning plane (112). As Sims and Jaffee3 and Lawley and Maddin4 have shown, the addition of rhenium to molybdenum and tungsten increases the ductility of the alloy over that of the pure metal, but twinning is much more profuse in these alloys than in the pure elements, particularly at Mo-35 pct Re*and W-30 pct Re. Since twinning is often associated with brittle fracture in iron8 and the silicon-irons,9 direct experimental proof that the deformation markings in tungsten and molybdenum alloys of rhenium are twins seemed to be needed. Using the Laue back-reflection technique, the deformation markings in a Mo-35 pct Re alloy are shown to be deformation twins. The twins have a (112) habit plane and the twinning direction is <111>. The Mo-35 pct Re specimen used was taken from a 0.060-in. zone-refined single crystal deformed 6 pct in tension at 78°K. The Laue back-reflection technique, with a film to specimen distance of 2 cm, and white radiation from a copper target were used.

Jan 1, 1962

By Leonard Klein

Reduction of oxygen-containing copper has always heretofore been brought about with wood poles. This paper reveals the first successful, economical, and Practical substitute for poles: a gaseous reductant, of which the production and plant use are detailed herein. THE art of fire refining of copper, consisting of melting, oxidation, slag removal, and finally reduction with wood poles, has been practiced for many centuries. An authentic record, discussed in detail in De Re Metallica,* mentions that as early as 1200 A.D. workers in this field of metallurgy were already acquainted with and practiced the basic principles of copper purification. Undoubtedly, the art was well developed marly centuries before the first written records began to appear. Notwithstanding the many advantages gained by application of mechanical con. trivances and by the tremendous increase in size of operations over the centuries, the reduction phase of the process has persisted essentially the same to the present time except for a very recent breakthrough. Numerous articles have been published and many patents have been issued on the subject of substitutes for wood poling in the past half century. They have dealt with a variety of gaseous, solid, and liquid reducing agents. But to the knowledge of the writer, no procedure has ever been prosecuted to a complete success on a large operating plant scale with the single exception of gaseous reduction of oxygen-containing copper revealed in detail herein. A natural gas-air reformer with ample capacity for

Jan 1, 1962

By Hsun Hu

Direct observations were made on the recrystalli-zntion of a cold-rolled (110) [001] crystal of 3 pct Si-Fe by annealing thin sections of the specimen inside the electron microscope during examination. Subgrain formation, presumably by polygonization, occurs rapidly, followed by a slow increase in the subgrain size before recrystallization can be detected. No migration of the subgrain boundaries was observed, and the formation of recrystallization nuclei by coalescence of subgrains is suggested. Re-c~ystallization characteristics of various texture components were individually examined. AS reported in a previous paper: orientations of the various deformation texture components in a 70 pct cold-rolled (110) [0011 crystal of 3 pct Si-Fe were completely confirmed by transmission electron diffraction patterns taken at various areas of the specimen. These orientations can be summarized as follows: Over most areas of the deformed crystal (111) planes are parallel to the surface. These areas correspond to either $- the two main defor: mation textures, the (111) [112] or the (111) [112].2-5 Within a few areas, (100) planes parallel to the surface are frequently found. These areas represent the minor deformation texture component, the (100) [Oll] type, which is derived from rotated Neumann bands.2&apos;4&apos;5 Only in very rare instances are (110) planes found parallel to the surface. This orientation corresponds to the very weak texture component of the (110) [001] type. In a pole figure, this (110) [0011 orientation is located within the orientation spread between the two main (111) [1121 type textures. Usually the electron diffraction patterns taken at various areas of the specimen are very simple ones, i.e., for any one area the pattern consists only of sharply defined spots of a single orientation. In some areas, however, more or less continuous rings of weaker intensities are superimposed on a simple pattern, indicating the presence of a wide range of additional orientations. In order to understand in detail the recrystallization of this cold-worked crystal, the recrywtallization characteristics of each of the various deformation texture components must be examined. This can best be done by using a high-temperature stage and transmission electron microscopy techniques, whereby small areas corresponding to the various texture components can be selected individually for examination. The present paper presents results obtained by this method. MATERIAL AND METHOD Specimens were prepared from a previously studied1 single crystal of a commercial grade 3 pct Si-Fe alloy with an initial orientation (110) [00l], cold-rolled 70 pct from 0.014 in. to 0.004 in. in thickness. Thin foils were prepared by electrolytic polishing as described in the earlier paper.&apos; Specimens of this thin foil were then mounted in a high temperature stage similar to the one designed by Whelan.6 A direct current was used as the heating source. The temperature of the heating grid was calibrated by means of a Pt vs Pt-10 pct Rh thermocouple in a vacuum chamber (0.01 to 0.02µHg). Maximum variation within the temperature range of 250o to 000°C was about ± 25°C. After the desired areas were selected for examination, the specimen was heated to a low temperature for some time while the selected area was constantly watched. When no further change in structure and orientation could be observed, a higher temperature was applied. Photomicrographs and diffraction patterns were taken from time to time during examination, with the heater temporarily turned off* while the photographs were

Jan 1, 1962

By Larsen. Edward P.

The principle of "bed blending" in the agglomeration of materials is about 56 years old, but de- spite all education via technical papers, operating reports and results from functioning installations, the concepts of blending are still somewhat vague. Confusion exists between "mixing", "blending," and the basic role of each. The terms "blending" and mixing" are often used interchangeably, yet they describe two different processes. As properly understood and applied, a blend is a combination of different varieties of material which produces a desired quality, or the mingling of different elements to form a harmonious whole. In other words, blending is a process of combining granular materials by mechanical means, wherein the final product, or a portion thereof, must contain an exact proportional amount of every one of the several different materials which contributed to the mass and wherein all particles are so thoroughly intermingled with each other as to have lost their individual identities and become a part of the whole so that when a portion of the blend is taken at any time it will be substantially identical, chemically and physically, to any other portion taken throughout.

Jan 1, 1962

By S. Y. Ogawa

The effects of sulfur (up to 0.1 pet) on the deformation and fracture characteristics of iron, in cast form, were studied at strain rates up to 100 pct pcr sec and at temperatures of 1600o to -3300 oF. The effects of oxygen and manganese additions on the behavior of Fe-S alloys were studied under comparable test conditions. Brittle fracture characteristics, evident at all strain rates, resulted from the presence of the liquid iron sulfide phase at grain boundaries. Ductility could be restored in three ways: solution of the sulfide in solid y iron at higher temperatures, spheroid-zzation of the liquid sulfide, and increase. in the melting point ot the sulfide. THE literature shows that most previous studies of deformation and fracture at hot working temperatures have been based on measurements of energy absorption, reduction of height in forging upset tests, torsion tests of bar or wire samples, and so forth,&apos; but that relatively few tension tests have been used at high temperatures and strain rates. The present work was initiated to study the ef- fects of temperature, strain rate, composition, and structure on the deformation and fracture characteristics of iron, utilizing cast specimens tested in tension. As in a previous study,&apos; strain rates up to 100 pct per sec were chosen for the temperature range 1600° to 2400° to provide data which might be useful in the interpretation of the deformation and fracture behavior of steels under hot working conditions. The previous work was with Fe-P solid solution al10ys;2 this work is concerned with Fe-S alloys, and with the effects of oxygen and manganese additions. MATERIALS AND PROCEDURE Cast tes! specimens were employed throughout, since most of the difficulty during hot working occurs in the initial breakdown of the ingot. Alloy Systems. Ten 25 lb. heats containing sulphur were prepared. Of these, three had manganese additions, and two had oxygen additions. The sulfur content varied from 0.023 to 0.10 pct. Manganese contents were intended to be ten to twenty times the sulfur content of the particular alloy. Oxygen, being more difficult to control in small melts, was varied by the amount of solid deoxidizer added, but poor control of the oxygen content was experienced in most instances. Table I shows the chemical analyses of the heats. Melting and Casting. Electrolytic-iron chips were melted by high frequency induction in a prefired, clay-graphite crucible lined with rammed magnesite.

Jan 1, 1962

Jan 1, 1962

By S. A. Ronlov

The importance of recognizing vibration problems during the plant design stage is emphasized in this paper. Often an experienced designer can recommend what type of support to use and how to tune the structure. However, obtaining sufficient information is a serious problem dealing with vibration. Vibration is a well known phenomena which, simply and generally, can be defined as a periodic motion. It is experienced in nature as caused by eerth- quake, wind, or ocean waves, and must be dealt with in the design of structure or ships. It must be realized that wherever there are moving or rotating elements, it is possible that unbalanced forces may induce vibration in the elements themselves, in adjacent parts, or in the supporting structure. Under certain circumstances, vibration will destroy machines or structures quickly and totally. The most widely known case is the total collapse of the Tacoma bridge when subjected to a wind of only 42 mph. Failures due to vibration of machines and/or their supports may occur in industrial plants where heavy equipment employed in the process must be supported and several machines are combined in close proximity. In the Metallurgical and Chemical Div. of The

Jan 1, 1962

By Charles White Merrill, James W. Pennington

No metallurgical process developed in the 20th century compares with froth flotation in its effect on the mineral industry. Processes like gravity - concentration, amalgamation, and pyrometallurgical reduction are of ancient origin; others like cyanidation and electrolytic reduction were well established by 1900. Such metallurgical processes as heavy-media separation, ion-exchange, and solvent extraction belong to this century, but their influence is small compared with froth flotation. Data collected by the U. S. Bureau of Mines* in a canvass of 202 froth flotation plants reveal that, in 1960, 198- million tons of material was treated to recover 20-million tons of concentrates which contained approximately $1 billion in recoverable products. SIGNIFICANCE OF FLOTATION Froth flotation as described in this chapter refers to a wet process for separating properly ground mineral particles into two or more products. It involves the separation of mineral particles from each other in a liquid pulp by means of air bubbles. Finely crushed ore is agitated in water with the addition of air or other gases. Various chemicals and oils are added to cause the selected mineral particles to attach themselves to the air or gas bubbles. These bubbles, carrying the mineral particles, rise to the surface where they are removed in a froth, while the other particles remain suspended in the pulp. The earliest flotation divided the raw material into two products: a bulk concentrate that was removed as a froth and a tailing that remained in the flotation machine. The froth usually contained the valuable constituents. The successful application of such a process depended on the recovery of a single concentrate from which one or more valuable constituents could be recovered by a chemical or smelting process. With the advance of the art, however, the principle of selective flotation, by which two or more relatively pure products could be recovered from complex raw materials, was evolved. Other chapters in this volume describe the developments during the last 50

Jan 1, 1962

By Paul A. Beck, M. N. Parthasarathi

The vecrystallization texture. formed by selective growth of random nuclei in an 80 pct volled 99.997 pct A1 crystal of initial orientation mear (123) (41.21 was found to consist of components related to the single-component rolling texture by 40 deg. rota-tiows around [111]axes. The relative-volume fractiovz of the various recrystallization-texture componezts may be accouzted for 012 the basis of the Lou) mobility of twist boundaries, if it is assumed that the mobility of the tilt boundaries also varies with their orientation. Similar results with a, aluminum-alloy cystal of the (110) [112] orientation, containing iron, silicon, and zinc, show that these solute contents do not impair the effectivezess of the oriented growth mechanism of re cry s-tallization- texture formation. In a previous investigation1,2 it was found that a sharp recrystallization texture is formed as a result of the oriented growth of random artificial nuclei in an aluminum crystal rolled to 80 pct RA, on the (110) plane in the [ 112] direction. Four recrystallization-texture components were found to occur, with orientations corresponding to 40-deg rotations around [111 1 axes of the deformation texture. Reorientations of this type were already found in earlier work,3,4 where the presence of random nuclei could be reasonably assumed, but was not rigorously documented. The same orientation relationship was found also by Lucke and Liebmann, who actually measured the orientation dependence of boundary-migration rates in the recrystallization of A1 crystals slightly deformed in tension.5,6 The occurrence in the recrystallization texture of only four of the eight crystallographically equivalent orientations of the type referred to above remained unexplained,1,2 although it was clearly not a result of the absence of suitable nuclei. Recently Burgers7 suggested that this effect may be due to the aniso-tropy of boundary mobility observed2&apos;6; it was found that the recrystallized grains of the 40-deg [111]-rotated type grow much faster in directions perpendicular to the [ 111] they have in common with the matrix than parallel to this direction, i.e., the tilt boundaries have much higher mobility than the twist boundaries. The four orientations corresponding to

Jan 1, 1962

By J. E. Pavlick, A. G. Guy

The total creep of tin alloys containing antimony in solid solution was observed to decrease with increase in antimony content. However, near the solubility limit an anomalous maximum in deformation was. found, in agreement with similiar observations by Bochvar. IT has long been recognized that alloys may deform more rapidly under stress if there is a tendency for a phase change or other structural change to occur simultaneously. However, the phenomena involved are complex and in some instances the opposite effect, strengthening, may result.&apos; This area of research has not attracted much interest in the western world, and although Russian investigators have studied it for the past 15 years their work has not received due attention here. Recently diametrically opposing views on one aspect of this problem have been espoused by two Russian investigators, Kornilov and Bochvar. The question is this: in certain binary alloys tested in creep at the temperature where the solute is at the limit of solid solubility, does the incipient formation of the second phase strengthen or weaken the alloy? Korni-lov&apos;s arguments in favor of strengthening were presented at the 1954 Symposium at the National Physical Laboratory, =Creep and Fracture of Metals at High Temperatures.The most recent statement of Boch-var&apos;s theory of weakening is in Oding&apos;s new book on creep and rupture.3 Although Bochvar agrees that strengthening occurs in some alloy systems, he argues that in certain alloys an anomalous weakening is observed. However, the extensive work of Korni-lov&apos;s group on creep properties of alloy systems has not revealed any anomaly of this type, but instead has tended to refute Bochvar&apos;s theory. This clear-cut controversy offered a good opportunity for a simple experiment to resolve the problem. The experiment and its results supporting Bochvar are the subject of this paper. However, it will be helpful first to sketch the present status of the larger question of the effect of a phase change or other structural change on plastic deformation. PREVIOUS WORK One of the first researches in this area was by Pfei1,37 who investigated the creep resistance of an 80 Ni-20 Cr alloy containing varying amounts of titanium. He found that the resistance to creep increased rapidly as the solid solubility limit in the alloy at 775&apos;c was approached and slightly exceeded. With further addition of titanium the creep resistance decreased, presumably because of precipitation effects. Bochvar&apos;s first work in this field was a study in 1945 of "superplasticity" in zinc alloys containing 15 to 25 pct Al.4 He found that alloys quenched from about 400 had anomalously low hardness when tested below this temperature. The following year, in a paper on the dependence of mechanical properties on the composition and structure of alloys,5 he extended some observations of Kurnakov to predict that at high temperatures of testing the hardness values for solid-solution alloys might be lower than those for the component metals. He also pointed out the influence of changes in solidus temperature in affecting curves of hardness vs composition, and he

Jan 1, 1962

By H. D. Mellom

The direction of the optic or "C" axis of a uniaxial metal crystal can be found with the metallurgical polarizing microscope by examining two planes of section on the crystal. Complete orientation of the crystal can be determined if a twin crystal is common to both surfaces of section. Examination of Uniaxial Metals in Polarized Light-Rotation of a uniaxial crystal surface, properly prepared,&apos; shows four extinction positions 90 deg apart, provided that the surface is not close to a basal section. One of these two extinction directions corresponds with the projection of the optic axis on the surface of section. This direction can be found if the &apos;sign of the rotationr2 for the metal is known. To find the direction of the optic axis, the crystal is rotated on the stage 45 deg from an extinction position. With a crystal of negative sign, to produce extinction the analyser must be rotated towards the optic axial direction and vice versa. All sections, other than basal, of a uniaxial crystal have the same sign of rotation and, since there is no change in sign with wave length, white light can be used for these measurements. U the sign of the rotation is not known the presumed direction of the optic axis can be determined assuming a positive sign. A third section cut normal to the presumed optic axis will show basal extinction if the assumption is correct. It is convenient to use the edge between the two planes of section as a fiducial direction common to both surfaces. The optic axis can be related to this direction. If the above measurements are repeated on the other plane of section and the angle between the two section planes measured, stereographic projection can be used to determine the orientation of the crystal optic axis. Determination of Complete Orientation—The complete orientation of a uniaxial crystal can be determined provided that a twin crystal is common to both surfaces of section, and the twin law is known. The orientation of the twin crystal optic axis can be determined in the same way as for the main crystal

Jan 1, 1962

By Franklin J. Hill, Theodore D. Tiemann

Sized fractions of Wisconsin Gogebic taconite were reduced with hydrogen over the temperature range from 600° to 1000°C. In general, the degree and rate of reduction increase with temperature. Particle size has no observable effect except in the smaller fractions at 900°C and above, where reduction is impeded, possibly due to the siliceous nature of the ore. Gaseous diffusion appears to be significant as a rate controlling factor at certain stages. THE depletion of high grade iron ore reserves in the United States has established the need to utilize all available iron ore deposits, both in long range planning and from the viewpoint of national emergency. This has led to extensive research and development in this field. The beneficiation of Wisconsin Gogebic taconite ore has been previously studied by investigators at the University of Wiscconsin, 1 the United States Bureau of Mines,, Battelle Memorial Institute, 3 and others. Methods investigated have included concentration by flotation processes, magnetic and gravity separation, magnetic roasting and various combinations of them. The foregoing studies have been concerned with the production of an enriched ore suitable for blast furnace use. If the ore could first be reduced to metallic iron and then beneficiated, the product could be used directly in the open hearth or electric steel-making furnace. The by-passing of the blast furnace should enhance the economic feasibility of the beneficiating process. The work reported here,4 was undertaken to establish data on the hydrogen reduction of Wisconsin taconite that would eventually lead to the development of an economic direct reduction process for this and perhaps other low grade siliceous ores. The volume of work on direct reduction can be judged by the fact that 240 direct reduction processes were patented in the United States alone up to 1951, 5 and numerous additional processes have since been developed. Some of the factors contributing to direct reduction development are: 1) The increasing capital cost of the blast furnace and its accessory equipment. 2) The decreasing availability of high grade domestic ore. 3) The high cost of steel scrap for use in the open hearth and electric furnaces. In general, direct reduction processes can be divided into two types; those using a solid reductant (coal, peat, lignite) usually carried out in a kiln, and those using a gaseous reductant (H2, CO) in a shaft furnace or a fluidized bed retort. As there is no low cost coal readily available in northern Wisconsin but natural gas could be quite easily obtained, it is believed a gaseous reductant process would offer the greater feasibility for use on Wisconsin taconite. It is hoped that this preliminary work will beof interest to other investigators in this increasingly important field. TACONITE ORE The ore used in the investigation was obtained originally from the U. S. Bureau of Mines, and consisted of a representative composite made up from trench samples of the Norrie, Pabst, Plymouth, Pence, and Yale members of the Wisconsin Gogebic range iron formation. Chemically, the ore contains approximately 52 pct SiO, and 30 pct Fe. X-ray diffraction and other studies indicate the principal minerals to be quartz (SiO2), hematite (Fe2O3), and goethite (Fe2O3. H2O). Minor amounts of iron containing silicates, siderite (FecO3), and magnetite (FeO-Fe2O3) are present. The iron minerals and quartz are so finely disseminated that the ore requires grinding to less than 200 mesh (74 µ) for essential liberation.l,2 The iron content of each of the several size fractions studied is shown in Table I. EXPERIMENTAL METHOD The method used throughout the investigation was based on that developed by the U. S. Bureau of Mines in Minneaopolis6,7 in which the course of reduction is followed by the loss in weight of the ore sample. More specifically, a 100-g sample of the size frac-

Jan 1, 1962

By H. W. Meyer, H. N. Lander, F. D. Delve

A method of calculating the changes in blast-furnace performance brought about by burden and/or blast modifications is presented. Essentially the method consists of three simultaneous equutions derived from materials and heat balances. These equations can be used not only to evaluate quantitatively the effect of changes in process operating variables on furnace performance, but also to provide a useful means of evaluating changes in process variables which cannot be measured directly. It has been customary for a number of years to use simple heat and materials balances as a basis for assessing blast-furnace practice. A good example of the method used to set up these balances is that proposed by Joseph and Neustatter.1 This approach to process assessment has limited utility, however, in that it cannot be used to predict the furnace coke rate or production under new operating conditions. Using an approach based on multiple correlation of blast-furnace variables, R V. Flint2 has developed an equation which may be used to predict the change in coke rate that will result from some changes in operating conditions with a reasonable degree of accuracy. Although this equation has useful applications in production planning, it cannot be used to study the relationships between the operating variables and the fundamental thermochemi-cal characteristics of the process. In attempting to analyze the blast-furnace process quantitatively, the idea of dividing the furnace into zones3 may at first appear attractive. In our present state of knowledge, however, it is not possible to define with any accuracy the physical limits of such zones in relationship to their temperatures or to the reactions which may occur in them. Although its application is restricted, the zonal approach to blast-furnace analysis is useful in some instances. For example, the change in the calculated flame temperature in the "combustion zone" caused by injecting steam constitutes information which is helpful in understanding why the addition of steam to the blast is best accompanied by an increase in blast temperature. The zonal approach cannot, at the present time, be used to establish the relationships between process variables and process performance if the whole process rather than part of it is to be considered. One of the earliest approaches to the problem of relating blast-furnace operating variables to pro- duction and coke rate was that developed by Marshall.4 Essentially Marshall&apos;s work showed that it was possible to estimate the performance of a furnace by solving three simultaneous equations which consisted of rudimentary carbon and heat balances plus a further equation relating the production, wind rate, and the carbon burned at the tuyeres. Although these equations did not include all of the chemical and thermal variables of the process, their derivation and application seems to be the earliest attempt which achieved any success in relating prior furnace operating data to the calculation of furnace performance under different blast conditions. Work carried out in Germany has been directed mainly towards prediction of coke rates using material and thermal balances rather than statistical methods. wesemann5 used prior furnace operating data as part of the basis for predicting the change in coke rate accompanying a change in burden composition. This author employed a method of successive approximations to estimate the secondary changes in slag volume and stone rate brought about by the change in coke rate. The most recent analysis, which seems to have been developed concurrently with the thermochemical model presented in this paper, has been described by Georgen.6 This author has succeeded in improving on Wesemann&apos;s approach by expressing the total changes in the slag volume and stone rate in terms of the change in coke rate itself. This is accomplished in a manner similar to that used in the thermochemical model described in this paper. Although Georgen makes use of a calculated furnace heat loss, he does not relate the heat loss per unit of hot metal to the production rate as is done in the present work. Georgen&apos;s approach may be used to calculate the changes in materials requirements accompanying changes in furnace operation; it cannot be used to assess the resulting changes in production. The fact that blast-furnace behavior can be interpreted by consideration of the heat requirements of the process was demonstrated by Dancy, Sadler, and Lander.7 In the analysis of blast-furnace operation with oxygen and steam injection these authors showed that it was possible to account for the changes in production and coke rate

Jan 1, 1962

By Hsun Hu

The formation of annealing textures in high-purity silver, from the various rolling textures obtanled in the course of texture transition, was studied. It was found that from a brass-type rolling texture the recrystallization texture is mainly (120) [211] type, which is quite different from the recrystallization texture of brass. From a predominantly copper-type rolling texture, the reclystallization texture is mainly (100) [001]. The recrystallization texture of silver- varies also with the degree of purity. In each case, however, the reorientation can be expressed as [Ill] rotations of 30° to 40°, which is consistent with the oriented growth theory of the formation of annealing textures. ThE recrystallization textures of rolled silver were studied long ago by Glocker and co-workers (1924-27) and were reported to be (113) [iil] upon annealing at low temperatures.1 Since that time, no further study of the recrystallization textures of silver, particularly with the modern techniques of quantitative texture determinations, has been reported in the literature. In a previous study2y3 it was found that the rolling texture of high-purity silver (99.999 +pct pure) is changed gradually from the common silver- or brass-type to the copper-type by raising the temperature of rolling from 0" to 200°C. The formation of annealing textures from the various rolling textures in the same material is, therefore, of considerable interest. The present paper constitutes the results of such a study. MATERIAL AND METHOD Specimens were taken from the same strips of high-purity silver* that were used previously for

Jan 1, 1962

By J. R. Lucas, H. E. Rutherford

The primary objective of this research was to evaluate the feasibility of ultrasonic testing for the purpose of analyzing the structure and properties of rock material. A secondary objective of this study was to determine experimentally the elastic wnstants of various rock specimens with the use of ultrasonic equipment. Elastic constants can definitely be determined quickly and accurately by ultrasonic investigation. With proper equipment there are indications that ultrasonic waves could be utilized in the detection of flaws, such as fractures and planes of weakness, measurement of thickness, and the study of structure of rock material. Ultrasonic principles have been applied in many industries for the purpose of determining the structural characteristics of various materials. The principal applications of interest here are detecting flaws, measuring thicknesses, and determining elastic constants. The main advantage of ultrasonic analysis is that it is nondestructive. It also has extreme sensitivity, high penetrability, good accuracy, rapid response, and the necessity to have access to only one side of the specimen. These various applications and advantages lead one to think that ultrasonic principles might be applied to rock material in situ for purposes of analyzing its structural characteristics. Therefore, the primary objective of this research was to evaluate the feasibility of ultrasonic testing for the purpose of analyzing the structure and properties of rock material. A secondary objective of this research was to determine experimentally the elastic constants of various rock specimens with the use of ultrasonic equipment. The term ultrasonics is given to that branch of acoustics dealing with periodic sounds whose fre- quencies are above the audible range or above approximately 15,.000 to 20,000 cps. The first practical production of this high frequency sound was made possible after World War I due to developments of electronically controlled sound wave sources. At the present, the maximum practically attainable ultrasonic frequency is approximately 1000 megacycles per sec. Sound waves of sufficiently high frequency can be made to travel in a beam with little spreading. Therefore, such a beam can explore a material and detect nonhomogeneities in it by reflection. This is the principle of the ultrasonic reflectoscope invented by F. A. Firestone&apos; in 1942. An ultrasonic beam, on pulse-penetratink a solid material medium, produces an echo when it strikes a flaw which has different acoustical properties than the surrounding medium. This echo can be detected by the same transducer which sends out the original pulse. This principle is the basis of the important industrial techniques of nondestructive ultrasonic testing of metals and other solid material. Later developments in the field of ultrasonic testing of solid material have been mostly improvements in equipment and instrumentation. To date, most of the industrial applications of ultrasonic analysis of solid bodies have been in the aircraft, electrical, and nuclear energy fields on the nondestructive testing of metal. The one solid material similar somewhat to rock material, upon which some work has been done to apply ultrasonic testing techniques to study structural integrity, is concrete. Jones and Gatfield3 briefly summarize this work on concrete. Their basic conclusion was that the strength of concrete was a function of the change of the longitudinal sound wave velocity in the concrete. Only recently has any extensive study been made to apply ultrasonic testing techniques to rock material. Lutsch studied rock material by an ultrasonic pulse method to determine the extent and degree of fracture of rock faces. Lutsch states that the number of observed reflections is a measure of the degree of fracture and that only ultrasonic waves are able to detect fractured zones subjected to high pressure. Suzuki, Sasaki, and Siohara5 studied the characteristics of the sonic wave in rock for propagation over a wide range of wave lengths. They indicated that, in rock, the propagation constant and attenuation of the

Jan 1, 1962