By G. H. Kessler

ALTHOUGH considerable attention has been devoted to reaction mechanisms and equilibria of a number of endothermic reactions through which metals or their refractory compounds can be formed upon heated surfaces, only a comparatively small amount of work has been done to develop rate information for these systems. The interestin and very worthwhile work of Holden and Kopelman, Runnalls and Pidgeon,Dijring and Moliere, and Herrick and ICrieble4 is to be noted; however, their work was done under very specific conditions and the rate information which they have developed is not applicable to many systems which have been studied experimentally. That a more generalized approach is needed is shown by the diversity of these systems and of the experimental conditions which they require. These include the preparation of titanium, zirconium, tungsten, molybdenum, chromium, co-lumbium, aluminum, and silicon by decomposition or disproportionation of their halides, in some instances through hydrogen reduction; the preparation of nickel and iron by decomposition of their car-bonyls; and the preparation of copper by decomposition of the acetylacetonate. They may be carried out at temperatures ranging from 100" to over 2000°C and at pressures of from less than one mm Hg to superatmospheric. The physical mechanism of the overall process can be broken down into several steps, any one of which may be rate-determining; and the rate associated with each of these basic physical processes can be predicted. Consequently, by proper application of the present technology of rate processes, it is possible to arrive at a rate of metal deposition in the system of interest and to reach an understanding of the influence of' each major variable upon the deposition rate. It is the purpose of this paper to illustrate how this can be done and to present experimental results for a specific system for comparison with theory. The overall process of deposition of metal upon a heated surface which is immersed in vapors of a compound of the metal can be broken down into the following steps: 1) Transport of the reactant vapors to the surface. 2) Decomposition of the reactant in the immediate vicinity of the surface to a) establish chemical equilibrium if reaction rates are high; or to b) establish a dynamic equilibrium in accordance with the several reaction rates. 3) Diffusion of reaction products away from the vicinity of the surface, with or without simultaneous recombinations to form still other products. The overall process is said to be diffusion controlled if Step 1, or the equivalent Step 3, is slow; it is reaction-rate controlled if Step 2b is slow. When experimental evidence shows the reaction rate to be controlling, the well-known theories of Eyring' and others can be used as a basis for correlating and extrapolating the experimental data. Although these theories give only approximate estimates of reaction rates, they are of considerably greater value in correlating experimental data. Most deposition systems operate at surface temperatures sufficiently high that reaction rates near the surface are very high. Mass-transport rates then become controlling; and it is this regime of diffusion controlled rates which is most often of concern and Which will be considered here. When the system pressure is very low, i.e., in the micron range, then the transport processes are those of molecular movement, and the results of kinetic theory can be applied to specify a rate of arrival of reactant molecules at the heated surface. If the condensation coefficient can be estimated, then the deposition rate will be given by the product (rate of arrival) x (condensation coefficient), Conversely, experimental data can be used to determine a condensation coefficient, as was done by Holden and Kopelman' for the decomposition of zirconium tetraiodide upon a heated molybdenum surface, who found the coefficient for zirconium on molybdenum to be 1.0 at temperatures of 1382°C and above. In this pressure range, the geometry of the system. and in particular the distance between the source of reactant molecules and the heated surface, can exert a considerable effect upon the deposition rate;

Jan 1, 1961

By W. R. Opie, O. W. Mole

By confining the electrolytic reduction of TiCl4 to the interior of a porous basket-cathode the electrolyte between the anode and the cathode can be kept free of reduced chlorides of titanium eliminating undesirable reactions of reduced titanium chlorides with brickwork or oxygen in the cell atmosphere. Semiwalls are not needed. Operating conditions are given and discussed. Titanium yields based on TiCl4 introduced are 93 pct. Cell voltage and amperage characteristics are adaptable to multiple cathode-series cell urmngements. EXPERIMENTS conducted in the National Lead Co., Titanium Division, Research Laboratories showed that titanium metal could be deposited in an electrolytic cell in which titanium tetrachloride was introduced through a tubular cathode.' The reduced chlorides as formed were confined to the vicinity of the cathode. They were reduced to form a cocoon-shaped growth of sponge titanium metal at the end of the cathodic tube below the surface of a sodium chloride-strontium chloride electrolyte. No diaphragm was needed.' Although high-purity, coarse crystalline metal was produced in the cocoon growth, the yields of metal removed from the cell, based on the amount of titanium introduced as TiCl4, were usually only 40 to 60 pct. The growth of the cocoon deposits was away from the cathodic tube for introduction of TiC14 toward the anode following the flu lines. The reduced chlorides of titanium diffused through the deposit and were reduced to titanium electrolytically within the deposit or on the outer surfaces. Deposition within the pores of the cocoon was detrimental to further deposition because it plugged the passages used by the reduced chlorides to diffuse away from the point of titanium introduction. As plugging due to deposition in the pores proceeded, the reduced chlorides in the center of the cocoon would force their way out by forming a channel and would escape from the vicinity of the cathode without being reduced to metal. Some work had been done previously1, 2 which indicated that if the end of the cathodic tube for introducing TiC14 was surrounded by a screen connected to the tube so that it too was cathodic, growth could be made to occur within the screen. Direction of growth was observed to be from the screen toward the point of TiCl4 introduction. Through a series of design modifications a cathode evolved which consisted of an introduction tube surrounded by a perforated metal basket as shown in Fig. 1. Modifications of this design are described in Refs. 3, 4, and 5. This basic cathode designa" was incorporated in electrolytic cells containing graphite anodes and constructed of high-silica brick refractory for containing the electrolyte (see Fig. 2). The inner crucible was surrounded by insulating brick and the entire unit contained in a welded steel shell. Suitable cooling chambers with inert gas atmospheres were devised so that the cathode could be removed from the cell without exposing the deposit to air while hot. Various alkali and alkaline earth chlorides were used as electrolytes.

Jan 1, 1961

By D. R. Irving

Prior to this time, ample supplies of high grade mineral fillers, such as clay, have been available close to consuming centers. Now depletion of these accessible deposits, coupled with other factors such as increasing demand due to population expansion and standard of living rise, has made development of upgrading techniques attractive to producers. Various investigations being carried out by the U.S. Bureau of Mines are described. Factors making the development of improved methods for upgrading clays attractive to producers include: depletion of accessible deposits of high-grade clays, rising transportation and labor costs, more exacting specifications, and increased demand resulting from an expanding population and a constantly rising standard of living. Industry recognizes the need for upgrading presently unusable materials and has cooperated with the U.S. Bureau of Mines by providing samples from submarginal deposits and by evaluating the products that USBM upgrades. Following are some examples of recent clay beneficiation work by the Bureau. FIRE CLAY BENEFICIATION At the Rolla Metallurgical Center, Rolla, Mo., the Bureau is conducting research to develop technically and economically feasible mineral-dressing methods to remove quartz, pyrite, and other impurities from submarginal fire clays. The research has been spurred by the growing shortage of high-grade bur-ley, flint, and plastic clays in the Missouri fire-clay district resulting from increased consumption and the low rate of discovery of new deposits of adequate quality. There apparently is ample tonnage of submarginal flint and plastic clays to maintain the industry for many years if such material can be upgraded to commercial quality. Samples have been submitted to USBM by several major producers of refractories, including A. P. Green Fire Brick Co.; Harbison-Walker Refractories Co.; Mexico Refractories Div., Kaiser Aluminum and Chemical Corp.; and Wellsville Fire Brick Co. Research on some samples has been completed and still is in progress on others. The Bureau has found that specimens containing quartz or pyrite in grains coarser than the accompanying clay generally can be upgraded either with a gravity table or hydraulic cyclone. The improvement in quality is notable not only in chemical analysis but in an increase in pyrometric cone equivalent (PCE) of one or more cones. As an example, consider the results attained on a sandy flint—a fine-grained mixture of kaolin and halloysite with quartz and minor quantities of iron and manganese oxides. Chemical analysis was: 35.4 pct alumina (A12O3) and 47.8 pct silica (SiO2). The sample contained 9.2 pct free silica as quartz. The PCE was 33. The sample was crushed to -10-mesh, blunged with water, and then stage-ground to -48-mesh. The ground sample was tabled to yield a clay fraction containing 37.6 pct A12O3, and 45.3 pct SiO2 of which 2.4 pct was free silica. The PCE was 34. Recovery of alumina by this process was 73.6 pct. Concentration of the same clay in the hydraulic cyclone was even more effective in respect to quartz removal. The clay fraction analyzed 38.6 pct A12O3, 45.0 pct SiO2 of which 0.5 pct was free silica as quartz, and had a PCE of 34. Recovery of alumina was 71.9 pct. The hydraulic cyclone was also effective in reducing the pyrite content of a plastic clay which likewise was a mixture of kaolin and halloysite, plus some pyrite, quartz, and carbonaceous material. It analyzed 30.6 pct Al2O3, 52.3 pct SiO2, 2.3 pct Fe2O3, and 0.76 pct S. The sample was blunged and screened through 10-mesh to remove some coarse pyrite, then ground to -65-mesh and cycloned to remove most of the remainder. The final product recovered 81.8 pct of the alumina at a grade of 32.3 pct A12O3, 50.9 pct SiO2, 1.4 pct Fe2O3, and 0.1 pct S. The PCE was 32-1/2, compared with a PCE of 31-1/2 for the crude clay. The fine beneficiated clays, of course, must be pelletized and dried or fired to meet commercial acceptance. This operation has already been solved by industry. Little progress has been made on two remaining problems. One is that of fine-grained impurities, not separable by table or cyclone. Flotation is being investigated to solve this. Although fine pyrite is readily rejected, a satisfactory quartz-clay separation has not been attained. The second problem, a stubborn one, is that of alkali. Samples containing as much as 5 pct potas-

Jan 1, 1961

By J. H. Wernick, S. Geller

A number of new AB, compounds, in which A is a rare earth or yttrium atom and B is Al, Mn, Fe, Co, or Ni, having the cubic MgCu, structure (Laves phase) are reported. In most of the compounds, the interatomic distances are normal; the lanthanide contraction is observed. However, in the compounds CeB2, B = Fe, Co, Ni, Ce appears to have a valence substantially greater than three; in CeAl2, Ce appears to be trivalent. These results are interpreted as vesulting from an energetically more favorable situation for the 4f electron of Ce to be lost to the 3d band of Fe, Co, nnd Ni. Evidence for the existence of homogeneitj! ranges in these compounds is presented. THE purpose of this paper is to report on the crys-tallographic investigations of a large number of new compounds, Table I, with the MgCuz structure (cubic Laves phase). It is a part of a continuing study of the magnetic properties and structures of binary systems involving the rare earths. In a previous paper' some of the magnetic properties of such systems were reported briefly. We have also reported2 a number of compounds of the CusCa type. The compounds were prepared by induction melting in Argon atmosphere of mixtures of stoichiomet-ric amounts of the constituent elements.* For most of the compounds fused alumina or silica crucibles were used as the containing vessel; graphite crucibles were used to prepare CeA12, NdAl2 and TbA12. X-ray powder photographs were taken with CrKa radiation and the use of Straumanis-type Norelco cameras of 114.6 mm diam. The compounds AB2 belong to space group Fd3m-Ol with 8A in a): (000; 01/2 '/2;3) + 000-; b % XA and 16B in dl: (000; oVa %; 3) + 5/87; % %; 7e % Vs\£>. Because the intensities of the reflections on the powder photographs of the different compounds are similar, relative intensities were computed only for DyMnz for CrKa radiation, Table 11. In the calculation of intensities, the Thomas and umeda3 atomic scattering factors, corrected for dispersion,4 were used. The agreement between observed and calculated intensities leaves little doubt that DyMnz has the MgCuz structure. Crystallographic data for the ABz compounds are given in Table JII. Twelve of these compounds have been reported by other authors. A comparison of the published results with our work is given in Table W.* ers of elements of lower purity, to peritectic reactions in some cases, and to the presence of homogeneity ranges in these alloys, so that melting losses would still result in single phase alloys. The possibility of existence of homogeneity ranges in these compounds was investigated systematically only for GdMnz. At room temperature, the solid solution range is between

Jan 1, 1961

By J. F. Pashak, T. E. Leontis

The effects of zirconium on the properties of sand cast Mg-rare earth metal alloys were discussed in detail in an earlier publication.' It was shown that a significant improvement in strength properties at temperatures up to 400°F resulted from the zirconium addition. In general, the properties of cast Mg-Didymium-Zr alloys were superior to the corresponding alloys containing Mischmetal and the optimum rare-earth level was approAmately 3 pet. Jessup, Emley, and Fisher have also shown the advantages of didymium in Mg-rare earth-Zr alloys, 2

Jan 1, 1961

By Martin Epner, Eric Gregory

DURING the past decade, considerable work has been carried out on various cermet systems in an effort to produce materials suitable for high-temperature applications in gas turbines. Most of the materials have not, as yet, met the requirements of the engine manufacturers, primarily because of their lack of room-temperature ductility and thermal shock resistance. In the field of tool materials, however, although ductility is still of prime importance, much has been accomplished by improving design parameters and the quality of carbide materials with a view to using cermet compositions successfully. The systems described in this paper were designed primarily for application in this field, although their development was a natural outcome of work on similar compositions designed for high-temperature service. In steel-bonded titanium carbide, the steel binder imparts heat treatability to the system while the carbide provides abrasion and wear resistance. Combining the carbide and the steel matrix in carefully controlled proportions results in a composite material which, when the steel is hardened, has man of the properties of cemented tungsten carbide. In the annealed condition, this material can be readily machined by the conventional chip-removal techniques. Titanium carbide has certain distinct advantages over many of the other carbides when combined with a steel matrix. It is among the hardest of the carbides and is one of the most stable. Liquid iron wets titanium carbide, and this wetting assists in the formation of a dense cermet. Once the composite structure has been formed, the titanium carbide acts as a relatively inert phase during the heat treatment of the matrix. PREPARATION OF ALLOYS The steel-bonded titanium-carbide materials described in this paper were prepared by the liquid-phase sintering technique. The titanium carbide used had an average particle size of 6 to 7 p, a total carbon content of 19.4 pct and 0.35 pct free carbon. This was blended with the elemental metal powders by ball milling them together in a hexane medium. After drying, paraffin wax was added to the blend to provide green strength in the pressed briquettes, and compacting was performed at 15 tsi. Liquid-phase sintering was carried out in vacuum at temperatures which depended on the chemical composition of the system involved, but which were usually around 2640° F. The resultant materials had a density approaching 100 pct of theoretical. The

Jan 1, 1961

By F. Petkovich, M. P. Sudbury

Development of a new method of treating flotation concentrates for the preparation of feed suitable for direct charging to blast furnaces or converters is described. The method takes advantage of the fact that pyrrhotite contained in the concentrates can be made to undergo exothermic reactions which, under properly controlled conditions, result information of oxidation products that serve to cement the concentrate particles together. Thus green concentrates either in the form of pellets or briquettes containing 5 to 8 pct moisture not only were hardened, but also completely dried autogenously by continuous countercu,vrent shaft treatment with air. The process was developed through pilot plant operations ranging from 35 1b per hr to 2.5 tph, culminating in products evaluation tests on a railway-car scale. Falconbridge Nickel Mines Ltd., Falconbridge, Ont., have practised sintering, on a travelling grate machine, for many years to prepare a pyr-rhotite-bearing Cu-Ni sulfide flotation concentrate for blast furnace smelting. In recent years the development of new mines, and the construction of concentration plants some 40 miles from the smelter has increased the quantity of concentrate shipped, and encouraged the search for a method of producing dry, hard pellets or briquettes suitable for direct charging to a blast furnace or converter, and capable of withstanding considerable handling. The cementing properties of pyrrhotite oxidation products were discovered during a search for a suitable agglomeration method for sulfide concentrates, and were exploited in a process subsequently developed for autogenously drying and hardening pellets and briquettes of pyrrhotite-bearing Cu-Ni sulfide flotation concentrate. EARLY TEST WORK The production of hard, dry pellets of concentrate filter cake was attempted in the drying plant of one of the new concentrators. While soft pellets were produced containing 5 pct moisture, attempts at further drying resulted in disintegration of the pellets and intolerable dusting. The plant therefore was controlled to produce a concentrate containing about 6 pct moisture. The partially dried concentrate, which was shipped to Falconbridge for sintering, tended to heat spontaneously in transit. An at- tempt to briquette the moist concentrate at Falconbridge, in a plant incorporating a muller, a 20-in. roll briquetting press, and a steam-heated travelling grate oven, was more successful, although the equipment corroded rapidly due to the acid nature of the concentrate after spontaneous heating had occurred. LABORATORY STUDIES OF SPONTANEOUS HEATING OF CONCENTRATE The spontaneous heating of partially dried concentrate was studied in the laboratory. Moist concen-

Jan 1, 1961

By Alan Lawley

AS part of a programme of experimental work on single crystals of rhenium and ruthenium, it was found necessary to have the crystallographic angles for these elements. The angles given in Table I were determined to the nearest minute of arc, by Univac Computer. The angle $ between (HKIL) and (hkil) is given by the formula: The angles given for rhenium should be particularly useful in view of the increasing interest in this element. For completeness, angular values are also given for cadmium zinc and magnesium; these form a more complete set of values than those given by Salkovitz.' The assistance of Professor J. Hobstetter and Mr. J. Crozier in the programming of this data is acknowledged. The work is sponsored by the Office of Naval Research under contract No. NONR 551 (19).

Jan 1, 1961

By W. L. Phillips

The recovery properties of compression-deformed lithium fluoride single crystals were investigated as a function of prior strain, annealing time, and annealing temperature. The recovery process was studied by observation of etch pits and birefringence stress patterns. The recovery process involved first a redistribution of the dislocations and then a decrease in their number. Only by annealing at high temperatures after small strains (<0.02 in. per in.) was it possible to obtain complete recovery of mechanical properties. LITHIUM fluoride affords unusual opportunities to extend the knowledge of deformation mechanisms of nonmetallic crystalline compounds. Single crystals of high purity are readily available. These crystals deform by slip on the (110) <110> system.&apos; Unlike those of several other ionic crystals, the stress-strain curves of annealed lithium fluoride are reproducible.2 Dislocations generated in the crystals during deformation can be revealed by etch pits.3 This fact makes possible more detailed studies of mechanisms than is usually the case with metals. Also, because lithium fluoride is transparent, it is possible to follow the recovery process with birefringence stress patterns. It has been shown that with metals an increase in temperature increases the amount of recovery for a given time, and the amount of recovery increases with increasing time at the same temperature.4-6 The yield stress has also been shown to be dependent on the rate of cooling after annealing.&apos; Annealing germanium, a covalent-bond material, at high temperatures after deformation redistributes the dislocations and reduces their number. The purpose of the present paper is to extend the knowledge of recovery properties to an ionic crystal, lithium fluoride. The effect of strain, time, and temperature of recovery on the stress-strain curve was investigated. The recovery process was followed by observations of etch pits and birefringence stress patterns. EXPERIMENTAL PROCEDURE Specimens measuring approximately 0.10 by 0,10 by 0.30 in. long were cleaved from a single bulk

Jan 1, 1961

By H. Linder, W. H. Dennen

The graphitic carbon content of soils may be used to detect and delimit subsurface graphitic zones. Spectrographic measurement of carbon in C horizon soils from several areas in the northeastern United States shows good correlation with known graphitic bodies. Bodies of graphite and sulfides are readily located by electromagnetic prospecting methods, but these methods cannot generally discriminate between them. Usual practice, therefore, requires follow-up work on electrically anomalous areas by trenching, drilling, or soil sampling in order to determine the mineralogical nature of the conductor. The efficiency and cost of such follow-up is consequently an important factor in prospecting. The presence of buried sulfide deposits is often reflected in concentrations of metals in the superincumbent soil. Simple chemical tests for such metal concentrations have been developed and applied with considerable success. Bodies of graphite or mixtures of graphite and sulfides are, however, very common and a means whereby buried graphite could be detected by soil testing should provide valuable additional information in the search for ore sulfide and graphite deposits. Graphite is a notably stable substance and should persist in soil above graphite-rich horizons. Microscopic examination of soil samples high in carbon, however, failed to reveal any recognizable graphite fragments indicating a grain size in the clay range. Presumably such small particles would have some mobility in a soil by a translocation mechanism similar to that proposed for the movement of clay particles in a soil profile. Experimental data supports this idea since the boundary between background and anomalous soils carbon values is quite sharp, but the anomalous zone is slightly broader than the graphitic source rock. A simple spectrochemical technique for the determination of carbon in geological materials has been described by Dennen,1 and may be directly applied to soils. A modification of this technique which employs an arcing chamber through which nitrogen is passed is recommended to decrease contributions from atmospheric carbon dioxide. Tests indicate that soils over graphitic zones may be strongly enriched in carbon. The spectrochemical determination of carbon depends upon the formation of the cyanogen molecule (CN) from carbon in a sample and atmospheric nitrogen, under the high temperatures associated with a dc arc. Samples for analysis are dried, lumps broken, and screened. A small portion of the -100 mesh fraction is packed into a copper electrode and excited as the cathode of a dc arc. The band spectra of cyanogen are recorded photographically and the density of the bandhead CN 3883A is measured. The limit of detection of the method is about 0.01 pct C and its coefficient of variation is about 15 pct. Soils, of course, contain carbon in other forms than graphite, and the amount of interference from such sources was examined. The C horizon of several soils from Massachusetts, Maine, and Pennsylvania were found to have a carbon content of 0.3 to 0.5 pct by weight. This content is chiefly due to the presence of carbonates and vegetable matter in the sample and may be readily eliminated, or at least

Jan 1, 1961

By N. J. Grant, Hans Brunner

ThE materials used in this investigation were furnished by the Aluminum Co. of America and consisted of high-purity alurhinum (99.995 pct) and two aluminum-magnesium alloys containing approximately 2 and 5 pct Mg. The compositions of these alloys are listed in Table I. The materials were received as hot rolled 3/8-in. diam rods and were made from the same heats as the materials which were previously used in this laboratory.&apos;j3 The rods were cold swaged to 1/4-in. diam by 1 in. long, and then had two parallel flats machined over the gage length 0.085 in. apart. The test bars were annealed for 10 min at 700° F, and strained 1 pct in tension at room temperature. They were electropolished (80 pct acetic acid; 20 pct perchloric acid, 70 pct concentration) at a temperature of 60°F at approximately 20 v. A grid, transverse or square, spaced 0.2 mm apart, was impressed by rolling a fine threaded screw (128 threads per in.) across the flat surfaces. The depth of the grooves was less than 5 p. For final annealing and grain size control the specimens were enclosed in aluminum foil and sealed in Vycor tubes. Annealing conditions varied from 1 hr at 700° F to 5 days at 1050° F, depending on the alloy content, to give for most of the specimens a final grain size of about 1 mm. This treatment was followed by electropol-ishing as described above. For the test series presented in Figs. 4 and 5 round specimens were used instead of flat ones, and fine machining marks served as marker lines instead of the impressed grid lines. Electropolishing was omitted. The major advantage is that the spacing of the machining marks is only about 1 u as compared to the 200 u of the impressed grid lines, permitting higher precision in strain measurements. Unfortunately the strain annealing necessary for grain size control also resulted in some preferred orientation of the grains. The preferred orientation of three arbitrary specimens was measured by X-ray diffraction methods and the averaged results are shown in Fig. 1. The possible effects of the preferred orientation on the test results will be discussed later. The testing temperatures were 410°, 515", 725", and 940° F, with one exception in the case of the 5.1 pct Mg alloy. Since the solubility limit of this alloy is 520°F, a test temperature of 545°F was cho-se sen instead of 515°F. The selection of the test temperature was based on two considerations: 1) at 900°F and above, extensive grain boundary migration made it more difficult to measure grain boundary sliding; 2) at 400°F and below, there was so little grain boundary sliding that it was again difficult to make precise measurements. The stress was chosen to give a creep rate of approximately 2.7 pct per hr in connection with Figs. 2

Jan 1, 1961

By G. V. Jere, C. C. Patel

Chlorination of the various constituents of ilmenite by different chlorinating agents in presence of various reducing agents, have been considered on the basis of the standard free energy and standard enthalpy changes as a function of temperature. The standard free energy change considerations show that it is beneficial to chlorinate ilmenite by chlorine in the presence of carbon and also that iron constituent of ilmenite can be preferentially chlorinated by clzlorine, titanium tetrachloride or their mixture. These findilzgs have been corroborated from the published work. METALLURGICAL processes involving the use of titanium tetrachloride have gained in importance because of the use of the latter in the manufacture of titanium metal. Since ilmenite is more abundant in nature than any other titanium mineral, the future of the metallurgical processes depends on the utilization of ilmenite for the production of titanium tetrachloride. In these laboratories, investigations have been carried out on the chlorination of ilmenite under a variety of conditions.1&apos;2 During these studies, it was noticed that 1) preferential chlorination of iron was effected at low temperatures (400° to 600°C) and at low carbon content (6 to 7 pct), 2) carbonyl chloride retarded the chlorination of iron oxides and titania perceptibly, while 3) carbon-tetrachloride, compounds of sulphur and some other catalysts favored the chlorination. Moles3 has found that oxides of iron are chlorinated in preference to titania at high temperatures, while wilcox4 has claimed the preferential chlorination of titania between 1200" and 1500°C. It has been shown in this paper that preferential chlorination of titania claimed by Wilcox is not likely to occur. Daubenspeck and coworkers5,6 have claimed the preferential chlorination of iron by chlorine or by a mixture of titanium tetrachloride and chlorine between 700° and 1050°C in the absence of carbon. Even when plain titanium tetrachloride is employed as the chlorinating agent, pascaud7 noticed the preferential chlorination of iron and other oxides. The purpose of this paper is to explain from thermodynamical considerations, the various chlorination reactions studied so far. ILMENITE CONSTITUENTS AND THEIR CHLORINATION PRODUCTS Although the general composition of the ilmenite mineral is represented as FeTiO,, most of the ilmenites found in nature have variable quantities of TiO2 (44.6 to 64 pct), FeO (4.7 to 36 pct) and Fe2O3 (6.9 to 28 pct).8 The higher content of ferric iron in ilmenites was attributed by Millerg to the presence of arizonite (Fe2O3.3TiO2). But the X-ray studies by Overholt, Vaw, and odd" have shown that arizonite is a mixture of haematite, ilmenite, anatase, and rutile. Except for the anatase, similar views have been advanced by Lynd, Sigurdson, North, and Anderson8 from magnetic, X-ray, and optical and electron microscope studies. The ilmenite ores can, therefore, be assumed to consist of mineral aggregates of ilmenite, rutile and haematite. From the free energy of formation of ilmenite (FeTiO3), it has been shown by Kelley, Todd, and King11 that ilmenite is stable even up to its melting point (1367°C) and would not undergo decomposition into its constituent oxides. Schomate, Naylor, and Boericke12 have found that in the presence of a reducing agent the iron constituent of ilmenite is selectively reduced. The reaction of chlorine with ilmenite in presence of a reducing agent can, therefore, be synonymous with that of the reaction of chlorine with the constituents of ilmenite, viz., TiO2, FeO, and Fe2O3. Most of the reaction products of chlorination of ilmenite in the presence of reducing agents will be in equilibrium with their dissociation products, depending on the temperature. The titanium tetrachloride is, however, quite stable up to 1500°C due to its covalent nature. The equilibrium for the ferric chloride system has been investigated by Kangro and Bernstorff, 13, schafer14 and Kangro and petersen,15 and the results are summarized in Fig. 1, curves a, b, and c respectively. From these results, it is clear that the ferric chloride disociates as follows: 324° to 700°C FeaCl6(g) ?2FeCl2(c) + Cl2(g) [1] 324°to 900°C Fe2Cl6(g) =2 Fe Cl2 Reaction [I] (curve a) occurs in the forward direction to about 6 pct at 400°C but falls off very rapidly with increase in temperature and beyond 600°C, it is practically negligible, perhaps due to the formation of the stable monomer, FeC13(g). As the temperature is further increased, the amount of FeCl,(g) in-

Jan 1, 1961

By P. K. Guerrero, N. Arbiter

The correlation of power consumed by a tumbling mill with the dimensions, speed, and load has been attempted by three principal methods. One of these, the torque formula, has been reviewed critically elsewhere.&apos; This approach, while analytical, disregards the individual motion and speed of the tumbling bodies and assumes that the gross geometry of the entire load is sufficient to establish the power requirement. A more general approach, using dimensional analysis, has been applied in this laboratory by the present authors1&apos;1, and more recently by Rose.3 This disregards the internal conditions within the mill entirely and in effect is an empirical procedure for correlating data. Finally, the complete analysis of tumbling mill dynamics as first made by Davis&apos; attempts to develop the power requirement from individual ball and rod paths and velocities. Although Davis&apos; result is applicable only at a single speed for a given size and load it could be useful, since his optimum speed is at the upper limits of conventional tumbling mill practice. Where power values predicted by the Davis equation were compared with actual mill requirements, they were found too low for small mills and much too high for the largest mills. This suggested that the agreement with actual intermediate range requirements might be fortuitous, and the development of the equation was examined critically. The probable source of error was found to lie in an erroneous assumption made by Davis in converting the energy of ball or rod motion to power. With the same approach, but with different assumptions, a modified equation has been obtained which predicts results that are usually consistently high. This is to be expected, since it is assumed that there is no slip between load and shell and no interference among tumbling bodies. Both these effects should account for the difference. Development of Equation: When a cylindrical shell charged with a substantial weight of rods or balls is slowly rotated about a horizontal axis, the load surface first assumes an inclination that gradually increases to a maximum. Continued rotation results in failure within the load, characterized by a sliding of the top layers down the slope and a reduction in the angle of inclination. Further rotation again increases the angle, and the cycle repeats. If the speed is increased, there is continuous load failure and build-up and a continuous stream of rods or balls descends over the upcoming mass, which moves in circular arcs. At higher speeds the up-

Jan 1, 1961

By J. F. Shea, O. F. Tangel

Battelle Memorial Institute participated in a program for the General Services Administration aimed at developing a nickel-cobalt separation process that could be integrated in the Nicaro nickel plant. At the time the programwas being carried out, the Nicaro process was a straight-through operation, in which the ore was reduced and leached, after which the pregnant solution was boiled to produce a so-called "bulk precipitate" which contained virtually all of the nickel and cobalt which had been dissolved in the leaching step. The weight ratio of nickel to cobalt in Nicaro ore is approximately 15 to 20:l. The weight ratio of nickel to cobalt in the finished product had to be 100:l or higher to meet specifications. Because the Nicaro process embodied no nickel-cobalt separation step, the only way that a bulk precipitate of the specified nicke1:cobalt ratio could be produced was to so adjust roasting and leaching conditions that nickel would be selectively leached and most of the cobalt would be rejected with the tailings. The required selectivity, however, was achieved at the expense of nickel recovery, which was 5 or more per cent less than might have been obtained with the existing equipment, utilities, man power, etc., had selectivity been no object. The over-all purpose of the program was to develop a separation step that could be fitted into or onto the Nicaro facilities and which would permit the manufacture of a product that would meet the desired specifications and still permit the recovery of a maximum amount of nickel. Battelle suggested that this might be accomplished by reprocessing off-specification bulk precipitate and specifically suggested the process based on ammonium sulphate leaching followed by hydrogen reduction of the leach solution according to techniques developed commercially by Sherritt Gordon Mines Limited. Such a process would not only satisfy the objectives of the research but would present two additional advantages. (1) It would produce a separate cobalt product which could be further processed into metal, alloys, oxides, or salts. (2) It would yield nickel in metallic form which might be more generally marketable and command a slightly higher price per unit of nickel than the Nicaro oxide product. DESCRIPTION OF THE PROCESS Figure 1 is a flowsheet of the process. The essential features are: (1) Extraction of about 97 per cent of the nickel and about 85 per cent of the cobalt from bulk precipitate by a principal leach with ainmonium sulphate solution (Step A). Extraction of virtually all of

Jan 1, 1961

By M. J. Saarivirta, P. P. Taubenbla

This paper presents some high-temperature properties of copper-zirconium conductor alloy compared to copper-chromium alloy. Definite superiority of the copper -zirconium alloy over the copper-chromium alloy at high temperatures is shown. RECENT investigations have shown that cold-worked copper-zirconium alloy possesses good room-temperature strength, ductility, and conductivity and maintains most of its strength at temperatures up to 450°C (840°F). As a result, this alloy is now used for many applications, such as commutator segments, resistant welding wheels and tips, rectifier bases, electrical contacts, and so forth. Early investigations1-3 have shown that the maximum solid solubility of zirconium in copper is close to 0.15 pct and the alloy containing Cu-0.10-0.15 pct Zr exhibits the optimum mechanical and physical properties. Results2 have also shown that the alloy has better elevated temperature strength and ductility than copper-chromium and copper-silver alloys. The present investigation was undertaken to learn more about the elevated temperature properties of copper-zirconium alloy and to compare these properties with those of the copper-chromium alloy. WORK PROCEDURE The commercial copper-zirconium alloy, Amzirc was selected for this investigation. Because this alloy is composed of oxygen-free high-conductivity copper and 0.10-0.15 pct Zr, it was believed that possible disturbance from impurities would thus be negligible. Copper-chromium alloys used in this investigation contained 0.40 and 0.70 pct Cr and balance copper. The Cu-0.40 pct Cr alloy was a commercial brand, whereas the Cu-0.70 pct Cr alloy was made from OFHC copper and Cu-5 pct Cr master alloy. It was made in a graphite crucible under argon gas cover and cast. In the preparation of specimens, all three alloys were treated to give the optimum properties; thus the Cu-0.15 pct Zr alloy was solution annealed at different temperatures to determine the desirable solution annealing temperature. It was then cold worked and aged at 375" to 400°C (705" to 750" F). A solution annealing temperature of 1000°C (1830°F) was selected for the copper-chromium alloys because this temperature is widely used in commercial practice. The same alloy was aged at 450°C (840°F) after solution annealing and cold working. It was found that the maximum precipitation hardening of the copper-chromium alloy occurred at this temperature. When aged after solution annealing, the aging temperature was 500°C (930"F) for both alloys. The following properties were determined: 1) Tensile properties as a function of temperature. 2) Effect of solution annealing temperature on high-temperature tensile properties. 3) Stress to rupture strength at 350° and 400°C (660"to750°F). 4) Impact strength. 5) Electrical conductivity and resistivity as function of temperature. 6) Thermal expansion.

Jan 1, 1961

By R. H. Doremus, E. F. Koch

The first carbide phase that precipitates at 120°C from a iron containing about 0.02 wt pct, C was studied with the electron microscope. In both strained and unstrained material the carbide particles appeared to form on the dislocations in the iron, in agreement with the results of the kinetic study in part II. The structure of the carbide was tentatively identified as an expanded a-iron lattice (body-centered tetragonal) with about 0.7 wt pct C. This phase appeared to be metastable and apparently transformed into cementite or epsilon carbide when the iron was over-aged. WhEN a iron containing less than about 0.025 wt pct C is quenched from 700°C to room temperature the carbon is retained in solid solution and precipitates out slowly with time. The morphology and structure of the precipitating phase are still in doubt, two different carbide phases, epsilon carbide and cementite, have been identified, but there is considerable disagreement about the time and temperature at which they appear.1-4 Epsilon carbide seems to form at lower temperatures than cementite, although one group of investigators4 found only the latter phase over a wide range of aging temperatures. Usually these two phases have been identified after aging times much longer than needed to drain the carbon from supersaturated solution, at least for aging temperatures below 200oC. The precipitated carbides have been observed with the electron microscope,&apos;-5 but again most results have come from samples aged much longer than necessary to reduce the carbon concentration in solution to a low value. In this study the carbide phases were observed in earlier stages of precipitation with the electron microscope, in order to learn more about the shape, size, and distribution of the carbide particles. Samples strained small amounts before aging, as well as unstrained samples, were studied, and the structure of the carbide phase was tentatively identified. EXPERIMENTAL "Ferrovac E" vacuum-melted iron, from which the wires for kinetic studies were also made (Refs. 6 and 7 and the following paper) was used for this work. An analysis of this material is given in Table I; it agrees well with the manufacturer&apos;s values. The number of inclusions in the iron was very small, as can be seen in the optical micrograph in the following paper. Pieces of iron about 1 mm thick and 5 to 10 mm in diam were used for all the studies except for those in which the sample was strained before aging; then the specimen was a rod 3 to 6 mm in diam and 20 cm long. The samples were held at about 700°C in wet hydrogen for at least an hour to remove residual carbon and nitrogen, after which they were heated to 950" (in the y region) and cooled to room temperature in the furnace. This treatment gave an average grain diam of more than 1 mm, so that the effect of grain boundaries on the precipitation process was negligible. The samples were carburized at 710°C for about 2 hr in hydrogen that had passed over toluene held at -30°C; then they were rapidly quenched into water. From chemical analysis this treatment gave a carbon concentration of from 0.012 to 0.016 wt pct, which is less than the solubility of carbon at this temperature. After quenching, the samples were aged at 120 "C in an oil bath for vari-

Jan 1, 1961

By L. S. Castleman, R. Resnick

The self-diffusion coefficient of columbium has been measured over the temperature range 1535o to 2120°C, using the radioactive isotope Nb95 as the tracer. The data for the temperature dependence of the self-diffusion coefficient are best fitted by the equation D = (12.4 ± 0.8) exp [(-105,000 ± 3000)/RT] cm2/sec. THE increasing need for high-temperature structural materials has stimulated considerable interest in the properties of columbium, since it is a strong, ductile metal with a high melting point—in the vicin- ity of 2450oc.l One fundamental property which has not heretofore been measured is the self-diffusion coefficient. The self-diffusion coefficient plays an important role in theories of oxidatioq2 creep,&apos; sintering4 and other phenomena. Accordingly, the investigation reported in this paper was undertaken to determine the value of the self-diffusion coefficient and its temperature dependence by the use of Mb95.

Jan 1, 1961

By A. E. Gorum, I. Cornet

Fatigrle of ionic crystals has been studied primarily in magnesinm oxide. under cyclic stress dislocations move irrreversibly; they multiply; slip bands form and grow; cracks mucleate and propagnte, and failure occurs. The use of ionic crystals such as MgO is advantageorus in such investigations because they are optically transparent. Individual dislocation Intersections with {100} surfaces may be observed with a standard microscope, using etch-pit techniques. Slip, deformation, crack .formation, and fracture in MgO crystals under cyclic stress are compared with cotrresponditzg processes in metals. ThE effect of cyclic loading in metals has been studied for many years. The appearance of slip lines is readily observed and the ensuing fracture may also be seen. From these observations it is possible to predict the behavior of a material and make an educated guess as to what is happening internally, but the actual changes taking place within the structure are not readily apparent. If one could obtain a material in which the individual glide components could be observed, it would be invaluable in determining the actual slip distribution resulting from cyclic loading as well as the distribution of slip in the neighborhood of a growing crack. Such a material is magnesium oxide. Dislocation arrays may be observed by means of etch pits

Jan 1, 1961

Jan 1, 1961

[Officers and Committees of the Society of Petroleum Engineers 1 Officers and Staff of the AIME 2 Officers of AIME Sections Predominantly Petroleum in Membership 3 Society of Petroleum Engineers By-Laws 5 Alphabetical List of Members 9 Geographical List of Members 110 List of Members by Companies 127 Advertisers&apos; Index 137]

Jan 1, 1961