By K. M. Parida

The kinetics of dissolution of manganese dioxide in dilute sulphuric acid solution have been investigated using iron pyrites as a reductant. The dissolution rate of manganese is independent of the speed stirring but depends upon temperature, particle size, specific surface area of manganese ore, acid concentration, Fe(II) concentration and amount of pyrite. The activation energy is 43.6 KJ/mol and the linear relationship between the rate of dissolution and lido indicates that the reaction is chemically-controlled. The redox reactions of MnO2 with iron pyrites and Fe(II) are the rate-controlling reactions.

Jan 1, 1990

By C. F. Ferron

A process has been developed to treat the copper gold ores from the Guelb Moghrein mine in Mauritania. The process consists of pressure leaching the sulphide concentrate, neutralising with the oxide ore, recovery of copper by SX/EW and of gold by cyanidation of the autoclave residue. This paper focuses on the pressure leaching step, and presents data from bench and pilot plant test programs. In particular, attention is drawn to the effects of temperature, grind size, neutralisation, retention time and solution recycle on the kinetics of copper dissolution from various flotation concentrates. Likely leach mechanisms are briefly discussed.

Jan 1, 2000

By José Carlos Abreu

This work presents a kinetics study covering the effects of temperature over the reduction rates of a carbon composite briquette, aiming its use as burden in some of the new alternate ironmaking technologies, such as the Tecnored process. It is reported that increases in the temperature increases the reaction rate. Additionally, the morphology of the iron phase generated during the reduction of these briquettes is presented. It was possible to verify that three types of iron morphology occurred during the process: an external, dense and continuous iron layer, the presence of iron globules at the center of the briquettes and whiskers at the briquette's core. The measurement of the carbon content on the globules and the external iron layer is also presented.

Jan 1, 2003

By José Carlos Abreu

This work presents a kinetics study covering the effects of temperature over the reduction rates of a carbon composite briquette, aiming its use as burden in some of the new alternate ironmaking technologies, such as the Tecnored process. It is reported that increases in the temperature increases the reaction rate. Additionally, the morphology of the iron phase generated during the reduction of these briquettes is presented. It was possible to verify that three types of iron morphology occurred during the process: an external, dense and continuous iron layer, the presence of iron globules at the center of the briquettes and whiskers at the briquette's core. The measurement of the carbon content on the globules and the external iron layer is also presented

Jan 1, 2003

By P. C. Chaubal

The overall kinetics of oxidation of single partic1es of chalcopyrite have been studied for temperatures up to 1273 K. The experiments were conducted in a stationary bed reactor using a non-isothermal technique. Any mass and heat transfer effects on the kinetics of oxidation were eliminated by using a high-enough gas flowrate. Up to temperatures of 873 K, pore-bl1ocking kinetics were applicable, whereas above 873 K, power-law kinetics gave a satisfactory fit of the data. The activation energy was 215 kJ/mol below 754 Kand 23.7 kJ/mol above 1,060 K. Predominance area diagrams were constructed at various temperatures and used in conjunction with X-ray analyses of partially oxidized samples to determine the intermediate phases formed during the reaction. The analysi1s also provides a justification for the kinetic models used. The results indicate that the reaction rate is first order with respect to oxygen concentration and inversely proportional to the square of the particle size throughout the ranges of temperature studied.

Jan 1, 1985

By Xiang Ma, Halvor Dalaker, Kai Tang, Stefan Andersson

Silicon carbide (SiC) is one of the most important non-oxide ceramic materials for many industrial applications and is mainly synthesized by carbothermic reduction of silicon oxide by coke above 2200°C. Replacing natural gas (mostly methane, CH4) for coke in SiC synthesis could considerably reduce energy consumption and CO2-emissions owing to higher carbon activity of CH4 at lower temperature. The generally accepted reaction mechanism is that SiC is synthesized through gaseous intermediate silicon monoxide, SiO. In the present study, the reaction mechanism for the SiO and CH4 gaseous mixture has been examined using atomic scale modelling. Molecular dynamics (MD) using a reactive force field (ReaxFF) has been utilized to examine the initial stages of reactions involving a gas mixture of SiO and CH4 and surfaces of SiC. The MD results revealed some interesting SiC formation mechanisms. The reaction energies of the critical intermediate species were also estimated by density functional theory (DFT) calculations and the implications for the force field parameters used in ReaxFF was discussed.

Jan 1, 2015

By C. Hecker, J. A. Garcia

To determine the kinetic reaction mechanism, electrochemical experimental techniques of stationary polarization, linear voltammetry and faradaic impedance were used. Gold electrodeposition experiments were realized using an electrolysis cell, provided· by a rotary disk of vitreous carbon and or' platinum counter electrode of platinum mesh and reference electrode. Using an automatic measurement system voltarnmograrns and Nyquist faradaic impedance spectra were obtained. In this paper, responses for different cases were analyzed through faradaic impedance criteria, considering several kinds of diagrams obtained. The importance diffusion influence of aurocyanide ions and adsorption as controlling steps previous charge transfer was verified. A model of proposed mechanism is discussed.

Jan 1, 1997

By Baozhong Zhao

Experimental results have shown that fluxing with soda ash (Na:zC03) can remove As and Sb from molten copper at the rate of As>Sb, but is relatively ineffective in removing Hi. The rate of impurity removal is controlled by impurity mass transfer in the metal phase. In this paper, a mathematical model was developed to describe the impurity removal phenomena. The model incorporates the effects of molten bath mixing intensity, soda ash feeding rate, oxygen content in the molten copper and soda ash fluxing by surface addition and injection. The model predictions are in good agreement with experimental results and may be used in designing large scale tests.

Jan 1, 1996

By Harrison Hodge

In the Bayer process for alumina production, between 2–35% Al2O3 is lost with bauxite residue due primarily to incomplete dissolution of aluminiumbearing minerals during caustic leaching or the precipitation of sodium alumino-silicate solids. The recovery of sodium and aluminium from the residue, and particularly from the contained sodium alumino-silicates, is becoming an increasingly critical issue from both an environmental and economic standpoint. Lime-soda residue sintering followed by selective leaching has been proposed as a method to recover sodium and alumina. The factors influencing the sintering mechanisms and kinetics, and the subsequent leaching have not been well described to date. In this study, the physical and chemical changes taking place during isothermal sintering of bauxite residue in air, particularly at short reaction times are investigated using scanning electron microscope (SEM) and X-ray diffraction (XRD). The impacts of these changes on the recovery of valuable materials are reported.

By Paul L. Wichlacz

A mathematical model of growth and ferrous iron oxidation for attached bacteria was applied to rotating biological contactor (RBC) units treating acidic mine drainage. The model describes attached bacterial growth as a saturation function, where the rate of substrate utilization is determined by a maximum substrate oxidation rate constant, a half saturation constant, and the concentration of substrate within the RBC. The maximum oxidation rate constant was proportional to flow rate and the substrate concentration in the reactor varied with influent substrate concentration. The model was tested at three separate sites and with three different size RBC units. The ability of the model to predict the rate of iron oxidation under all test conditions was significant. The accuracy of the model was found to be affected by unit size and vary with specific test site.

Jan 1, 1985

By N. Kanari

Kinetics of the carbochlorination of Cr2O3 has been studied with C12+CO gas mixtures between 500 °C to 900 °C using thermogravimetric analysis. The apparent activation energy is about 100 kJ/mol. Mathematical fitting of the experimental data suggests that the shrinking sphere model is the most adequate to describe the carbochlorination mechanism of chromium oxide and that is controlled by the chemical reaction. In the temperature range of 550 "C to 800 OC, the reaction order is about 1.34 and is independent of temperature. Changing the C12+CO content from 15 pct to 100 pct increases the reaction rate and does not affect the reaction mechanism. Similarly, changing the ratio of C12/(Cl2+CO) from 0.125 to 0.857 do not modify the carbochlorination mechanism of Cr203. In these conditions, the reaction rate passes through a maximum when using a chlorinating gas mixture having a Cl2/(C12+CO) ratio of about 0.5.

Jan 1, 1998

By Taiping Lou

The coarsening process of precipitates in non-equilibrium systems was studied, and then a physical model of coarsening was proposed. The coarsening process of CaO'TiO2 in MgO-TiO2-Al2O3-SiO2-CaO-CaF system was investigated. It is shown that the coarsening process by the model predicting is agreed with the experimental results.

Jan 1, 2000

By M. J. Adam

The U.S. Bureau of Mines is investigating the partitioning of selected complex minerals into simple phases using sulfidation reactions. Successful partitioning of complex mineralogy to simple phases may afford an opportunity to improve selective extraction of mineral constituents of economic value. The research has shown that complex minerals, such as chalcopyrite (CuFeS2) and pentlandite [(Fe,Ni)9Se]' may be partitioned to the simpler phases covellite (CuS) plus pyrite (FeS2) and vaesite (NiS2) plus pyrite (FeS2), respectively. Demonstrations of these reactions were verified through long-react ion-time (24 h or more) experiments, but basic rate investigations and modeling were not included in the previous research. This report describes research aimed at determining the rate at which the complex mineral CuFeS2 converts to the simple sulfides CuS plus FeS2. Small samples of CuFeS2 were blended with elemental S prior to thermal treating under an He atmosphere for time periods up to 4 h. Products from each treatment period were characterized using metallography, chemical analysis, X-ray diffraction (XRD), and scanning electron microscopy (SEM). Results of the investigation revealed a rapid conversion of CuFeS2 to CuS plus FeS2 early in thermal treatment periods. As the reaction occurred, a CuS rimming of particles was observed which separated the reacting species (CuFeS2 and S) and caused a considerable decrease in transformation rate.

Jan 1, 1991

By Milorad Cirkovic

Kinetics of copper concentrate oxidation in roasting processes in a fluidized bed reactor has been studied at temperatures between 600°C and 720°C using particles of 0.038 to 2.5 mm in average size. The analysis of composition of samples has been done by chemical methods. Phase composition has been determined by Siemens X-ray equipment with Cu anticathode and Ni filters at a voltage of 40 kV and a current of 18 mA. The content of sulphur has decreased from 33.23 to 19.02 mass percent with the increase of temperature, but the content of Fe304 has increased from 0.15 to 17.14 mass percent. The new mechanism of copper concentrate oxidation in a fluidized bed reactor is proposed in this study. It has been shown from the mathematical model that the velocity of oxidation of copper concentrate between 600°C and 720°C is virtually controlled by the rate of diffusion of 02 through the layer of reaction product.

Jan 1, 1999

By N. Kanari

The kinetics of oxychlorination of MgO by Cl2+O2 was studied in the temperature range of 850 °C - 1025 °C, using thermogravimetric analysis. The effects of C12/02 ratio, gas velocity, temperature and partial pressure of reactive gases on the reaction rate were investigated. The oxychlorination process was characterized by an apparent activation energy of about 214 kJ/mol. The reaction orders with respect to C12+O2. C12 and O2 at 950 °C were about 0.65.0.98, and -0.37, respectively. Some data about oxychlorination kinetics of MgO, Cr2O3, and MgCr2O4 contained in chromite were compared. Efficiency of using oxychlorination for the removal of iron oxides contained in magnesia was demonstrated.

Jan 1, 1999

By Kezhuan Gu

Data on the kinetics and thermodynamics of dephosphorization are analyzed in terms of the dynamic partition ratio, determined by a combination of slag thermodynamic properties and the balance of oxygen supply and consumption. A recently developed phosphate capacity correlation is combined with data on kinetics to quantify the most significant parameters in controlling the interfacial oxygen potential. The role of slag composition, entrained gas fraction and temperature are discussed in addition to metal carbon and sulfur content. It is demonstrated that the mass transport of oxygen in the slag is enhanced by factors increasing conductivity and inhibited by entrained gas. The mass transfer of phosphorus in the metal is described considering surface renewal induced by CO bubbles.

By Shengfan Zhou, XUEWEN WANG, Bianfang Chen, Mingyu Wang

Vanadium was leached from roasted stone coal by NaOH solution, and the effect of leaching temperature, leaching time, addition of NaOH, liquid to solid ratio, the grinding fineness of stone coal, and stirring speed on the vanadium leaching rate was studied. The kinetics analysis for the process is presented by the shrinking core model. The results show that the vanadium leaching ratio of roasted stone coal can be beyond 75% at the 6% NaOH addition, leaching temperature of 95°C, leaching time of 7h, liquid to solid ratio of 1.2mL/g, and grinding fineness of 0.111mm. The leaching process is controlled by interfacial reaction kinetics and the apparent activation energy was 59.36kJ/mol.

Jan 1, 2016

By Rashmi Kumar, Amit Chatterjee, Sanjay Chandra

The practice of adding alloying materials to a molten bath is an integral feature of many pyrometallurgical operations. However, very little is known about the dissolution rate and solution mechanisms of solid additives in liquid melts. In foundries where large tonnages of liquid metals are handled, there is considerable interest in achieving optimum metal quality at minimum cost. This objective is influenced by several factors and the solution is often plant specific. Though the amount, sequence and mode of ferroalloy addition vary from plant to plant, various fundamental factors determine how quickly these additions dissolve in the bath. At the Ingot Mould Foundry (IMF) in TATA STEEL blast furnace hot metal is used to cast ingot moulds. The composition of hot metal desired for making ingot moulds demands addition of 20 kg each of Ferromanganese and Ferrosilicon in the 12 T transfer ladles into which the blast furnace metal is poured at the IMF. Owing to low temperature of hot metal at the IMF, casting commences immediately and complete dissolution of the ferroalloys is often not possible. To study this aspect in detail and to evolve suitable corrective measures, a mathematical model for the melting of a solid particle in a liquid metal bath was developed at TATA STEEL. The model was validated using the data available in literature. In keeping with published work, two separate dissolution periods were identified - a "shell period" and a "free dissolution period". The maximum thickness of the crust formed around a spherical particle shortly after immersion, can be obtained by using the mathematical model which has been developed. The model can also be used to investigate the effect of various parameters such as superheat of the bath, size of the particle, etc., on the maximum crust thickness and the particle melting time. On the basis of this study, the addition of ferromanganese and ferrosilicon was optimized at the IMF in Tata Steel.

Jan 1, 1996

By Rodney J. Ishak

The reduction of Mn3O4 to MnO has been investigated in a thermobalance apparatus. The charge was composed of manganese ore (decomposed by heating/calcination or pre-reduction to mainly Mn304) and coke. The material was charged to a crucible, which was suspended in the balance. CO-gas was distributed through a grid in the bottom of the crucible. Two sizes of ores were used; 2.4-4.8 mm and 6.7-9.5 mm. Coke particles were in the size range 4.8-6.7 mm. Experiments were conducted in the 900-1100°C temperature range. The composition of the product gas was monitored continuously. External mass transport between bulk gas and particle surface does not seem to limit the rate of reduction. Assuming that both diffusion through product layer and chemical reaction at the interface between MnO and Mn304 are rate controlling, the data was tried both in a shrinking core model and in a grain model using regression. The grain model gives the best physical description of the process, because the reactant is in fact a porous medium. With this model the effective diffusivity was calculated to be in the 1.5-6.10-5 m2/s range. The pore size was mainly between 0.1 and 10 um.

Jan 1, 2003

By Rodney J. Ishak

The reduction of Mn3O4 to MnO has been investigated in a thermobalance apparatus, The charge was composed of manganese ore (decomposed by heating/calcination or pre-reduction to mainly Mn3O4) and coke. The material was charged to a crucible, which was suspended in the balance. CO-gas was distributed through a grid in the bottom of the crucible. Two sizes of ores were used; 2.4-4.8 mm and 6,7-9.5 mm. Coke particles were in the size range 4.8-6.7 mm. Experiments were conducted in the 900-1100°C temperature range. The composition of the product gas was monitored continuously. External mass transport between bulk gas and particle surface does not seem to limit the rate of reduction. Assuming that both diffusion through product layer and chemical reaction at the interface between MnO and Mn)04 are rate controlling, the data was tried both in a shrinking core model and in a grain model using regression. The grain model gives the best physical description of the process, because the reactant is in fact a porous medium. With this model the effective diffusivity was calculated to be in the 1.5-6.10.5 m2/s range. The pore size was mainly between 0.1 and 10 um,

Jan 1, 2003