By J. L. Luo, D. G. Ivey, A. H. Adeleke

Double-edge-notched flat tensile samples of X70 steel were used for both slow strain-rate testing (SSRT) and cyclic loading testing with the notch located in the zone of interest, i.e., the weld metal (WM), base metal (BM) and heat affected zone (HAZ). By using both optical and scanning electron microscopy, the stress corrosion cracking (SCC) behaviour with respect to crack morphology and various forms of microstructure was investigated. In all the samples considered, the mode of failure was predominantly transgranular with cleavage facets around the edges of the fracture surface. The BM, with a bainitic microstructure, had the highest resistance to SCC when compared with the mixed microstructures of acicular ferrite-primary ferrite and acicular ferrite-grain boundary ferrite observed in the WM and HAZ, respectively. The effect of microstructure on stress corrosion cracking behaviour is discussed based on experimental observations.

Jan 1, 2005

By H. Al-Kazzaz

The 2-mm butt joints of ZE41A-T5 sand castings were laser welded using 1.6 mm EZ33A-T5 filler wire and a continuous wave Nd:YAG system at a power of 4 kW, surface defocusing and various welding speeds, Compared with the base metal, the fusion zone showed significant grain refinement due to high cooling rate, No grain coarsening was observed in the heat affected zone (HAZ). The porosity area percentage and total solidification crack length in the fusion zone (FZ) were reduced as the welding speed increased from 4 to 7 m/min, Fusion zone area, total penetration depth, and weld width decreased with increased welding speed, The hardness in the FZ was similar to or higher than the base metal after a natural aging of about one year, but there was a drop in the hardness of the HAZ, The HAZ width decreased with increasing the welding speed, Tensile test showed that a joint efficiency of approximately 75 ? 90 % was obtained.

Jan 1, 2005

By J. A. Herbst

Mineral liberation modeling can be traced back to the early work 0fA.M. Gaudin up through more recent population balance modeling by R.p. King, J.A. Herbst and G.T. Adel. A more micro-scopic look was taken at the University of Utah in the form of the J.E. Sepulveda and J.D. Miller Pargen model which permits the creation of an arbitrary shape, multiphase particle made up of discrete grains. Recent work on image analysis and tomographic analysis by J.D. Miller and C.L. Lin have laid the experimental ground work for model validation, but until now it hasn't been possible to include the necessary physics of the particle stressing process to allow the development of a 'ffirstprinciples"mode1 which does not presuppose a "mode” of liberation (e.g., random or by detachment). Recent developments in discrete grain breakage (DGB) modeling now make a generalized physics based model feasible. This paper describes current work that is being done to develop a physics based discrete grain liberation (DGL) model. Two-dimensional and three dimensional simulation results exploring the effects of particle size, phase properties and loading type are presented. Relationships between energy based liberation efficiency, degree of random liberation and material properties are identified.

Jan 1, 2005

Driefontein Gold Mine together with Kloof Gold Mine and Beatrix Gold Mine forms part of Gold Fields South Africa. Driefontein Gold Mine is situated near the town of Carletonville, 50 km south of Johannesburg, in the Gauteng Province. The 4 Shaft East complex comprises of the 4 Main Shaft and the 4 Subvertical Shaft. The main shaft is 9150 m in diameter and was sunk in 1984 to a depth of 2000.5 m. The 4 Subvertical Shaft is 7320 m in diameter and was sunk during 1985 to a depth of 3006 m. Full production was, however, only reached during 1988. Intensive mining is currently being done between levels 28 to 42. In 2002 a decision was made to start mining the shaft pillar, situated between 32 and 33 level in the subvertical shaft. Intensive studies showed that with selective mining scheduling the total mineÆs life could be lengthened by nine years if accessed timeously. The higher grades present in the shaft pillar can be mixed with lower grades from the same reef band presently mined 1500 to 2000 m away from the subshaft pillar area. The shaft pillar comprises 50 per cent of the remaining ore resources available. However, no provisions were made in the initial phases of the shaft development to extract the shaft pillar. Grades between 4300 cmgt to 2500 cmgt relating to 23 and 14 g/t are present in the shaft pillar and an estimated 50 tonnes of gold can be produced from this pillar in the period from 2007 to 2015. The pillar extraction is the key to DriefonteinÆs long-term gold profile. Every geological feature possible is represented in this to-be-mined pillar area. The pillar around the shaft is a complex structure featuring hard and soft lava, sedimentary structures/plane parting that moves against each other, quartzite capping, etc. Replacement of services and secondary support systems were designed, modelled and put in place. The original steelwork was not designed to cope with the various stresses and movements, which are expected once the extraction process is started. Existing shaft steelwork was used as far as practically possible. The principal behind the design was that the steelwork would be totally disconnected from the shaft lining over its total length of 132 m in the area of the reef intersection. This will allow the steelwork to move independently from the geological structures surrounding it, allowing a certain degree of distortion of the shaft lining, moderate twist and tilt to take place without interfering with hoisting operations.

Jan 1, 2005

By J. C. Jansen

The platinum mining industry has experienced a significant increase in fatal accidents. Mine accidents are in principle preventable, and there is enormous pressure on employers to reverse this trend. This paper reviews safety management systems (SMS) as well as behaviour-based safety (BBS). Based on the review, SWOT analyses are performed on the SMS and BBS processes and a model of an integrated safety management system (ISMS) is introduced. A number of fatal accidents is analysed to identify factors that contributed to accidents in the mining industry. Thereafter the potential weaknesses of an SMS of a platinum mine are exposed and the potential benefits of implementing the ISMS for this case study are demonstrated.

Jan 1, 2005

By M. Vallée

"RÉSUMÉDurant les 10 dernières années, les améliorations dans le contrôle des limites des sautages et les arpentages après l’exploitation ont fourni des informations préalables et post facto sur les limites minières réalisées par rapport à la planification, plus particulièrement pour les grands chantiers exploités par les méthodes chambres vides et sous-niveaux. Cependant, peu de recherches ont été faites pour améliorer la délimitation du minerai, l’estimation des ressources et des réserves, les études de faisabilité et la récupération minière dans d’autres types de gisements. Il faudra d’abord expliciter les impacts des lacunes, en quantité et en qualité, de l’information géologique et de l’échantillonnage sur le rendement de l’extraction. Il faudra également remplacer la notion de « dilution générale » par celles de « dilution » et de « perte de minerai ». Les impacts des lacunes observées sur l’exploitation des gisements d’or filoniens sont démontrés par une simulation basée sur des résultats d’études antérieures à la mine Thompson d’Inco, des impacts financiers de densités d’information moindre et par des analyses des valeurs actualisées nettes (VAN) de deux cas types.Deux gisements similaires, de 3 m et 6 m de largeur et exploités par chambres vides sont étudiés, en prenant pour cas de base la délimitation sur maille de 7,5 m (25 pi.) et en étudiant les impacts des limites moins précises supportées par une maille de 15 m (50 pi.), en assumant que ces imprécisions moyennes de +/- 0,62 m se transforment soit en surestimation (dilution), soit en sous-estimation (pertes de minerai).Les impacts d’information moins précise ont été beaucoup plus forts sur le gisement plus étroit : autant la dilution que les pertes de métal ont diminué les VAN du gisement de 3 m de 39,27 % et 45,41 % respectivement, tandis que les VAN du gisement de 6 m ont été diminuées que de 12,84 % et 11,55 %.Ces impacts des valeurs actualisées nettes diminuées justifient et exigent des efforts plus systématiques pour s’assurer que les travaux de mise en valeur et les études de faisabilité soient réalisés de façon requise pour optimiser l’exploitation et offrir aux investisseurs des rendements compétitifs par rapport à ceux des autres secteurs industriels. ABSTRACTDuring the past 10 years, research work to improve the survey of stope limits after mining supplied useful information, particularly for large open and sub-level stopes, regarding waste dilution caused by differences between final production limits and planned stope limits.However, the efficiency of this information to improve the overall efficiency of the mining process is limited, given that the impacts of inaccurate ore limits leading to dilution (sensu stricto) and ore losses have not been considered adequately. Geological/sampling information should be optimized in terms of quantity and/or quality for the deposit characteristics and the constraints of the mining method used. As industry practice regarding the definition and recording of dilution is flexible and as ore losses frequently are poorly documented, the use of these terms is reviewed.Simulations were carried out on two typical narrow gold deposits, based on an earlier study at Inco’s Thompson mine regarding the impacts of wide to narrow delineation grids using recorded variations of vein geometry. Vertical to sub-vertical deposits of 3 m and 6 m widths mined by long-hole open stopes were considered. Deposits delineated by 7.5 m (25 ft) grids were taken as a base case and the impacts of less accurate limits in conjunction with long hole mining based only on a 15 m (50 ft) delineation grid. The impacts of overestimation (dilution) and underestimation (metal losses) were considered separately, using the average error of +/-0.62 m recorded in the Inco study.The impact of less accurate information was much stronger on the narrower deposit: both dilution and ore losses diminished the net present value of the 3 m wide deposit"

Jan 1, 2005

By C A. Locke, M Stevens, P Vidanovich, J Cassidy, J L. Mauk

The Karangahake adularia-sericite epithermal gold-silver deposit, located at the southern end of the Waitekauri Corridor, Hauraki Goldfield, occurs as quartz veins with associated alteration haloes. Integrated geophysical studies were undertaken to determine the expression, location, and extent of these alteration zones. Aeromagnetic data show an extensive, magnetic æquietÆ zone over Karangahake and the southern Rahu Ridge that represents a zone of magnetite destruction resulting from hydrothermal alteration. Analytic signal data are used to define the boundary of this zone; the resulting 6 km2 area is elongate north-south with an irregular boundary. A detailed gravity survey over the area reveals a positive residual gravity anomaly, up to 30 gu in amplitude, over the Karangahake deposit. Density measurements on near-surface rocks give low values indicating that the source of this positive gravity anomaly must be deep; possible causative bodies include an igneous intrusion or dense sulfide mineralisation. To the west and east of the host Waipupu Formation, strong gravity gradients of 100 gu/km and 65 gu/km reflect the faulted boundary of the Hauraki Rift, and the edge of the Waihi Basin respectively. High resolution airborne radiometric data define a 2.2 km2 area of potassium enrichment. This area is elongate north-south and has an irregular boundary. It coincides approximately with the centre of the magnetic quiet zone and the peak of the gravity high, and correlates with known areas of intense mineralisation. Anomalously high potassium counts and elevated K/Th ratios correlate with areas of potassic alteration that have undergone K-metasomatism. Underexplored portions of this zone may indicate areas of gold-silver prospectivity. Combined geophysical data therefore reveal the extent of hydrothermal alteration, and the central zone of Kmetasomatism that is most likely to contain orebodies.

Jan 1, 2005

By Xiaodong Ma, Marek Pawlik

Introduction Guar gum is a natural nonionic polysaccharide. Guaran, the functional polysaccharide in guar gum is a chain of (1?4)-linked ß-D-mannopyranose units with a-D-galactopyranose units connected to the mannose backbone through (1?6) glycosidic linkages. The poly-mannose chain is randomly substituted with galactose units at a mannose-to-galactose ratio of 1.8-1.0 [1]. Cheng et al. reported that the molecular weight of natural guar gum is 1.935 • 106 [2]. Robinson et al. found that the molecular weights of five grades of commercial guar gums ranged from 4.4 • 105 to 16.5 • 105 [3]. Guar gum is frequently used as a depressant of naturally hydrophobic gangue minerals (e.g. talc) in the flotation of PGM-bearing ores, and according to Harris et al. a wide variety of modified guar gums are available for this application [4]. The Canadian potash industry utilizes natural guar gum as a blinder of water-insoluble slimes in the flotation of potash (sylvinite) ores, a process that is carried out in a saturated KCl/NaCl brine. The role of the polysaccharide is to prevent a primary amine collector from adsorbing onto these unwanted fine minerals. Hydrophobic interactions between basal cleavage planes and the polymer appear to be involved in guar gum adsorption on talc [5,6]. Liu and Laskowski stressed the importance of metal impurities on mineral surfaces that can serve as the active sites for polysaccharide adsorption [7]. This postulate was consistent with the later observation that, in addition to hydrogen bonding, the adsorption of guar gum onto talc was strongly dependent on the surface concentration of magnesium sites [8,9]. In this case the adsorption process was visualized as metal-polysaccharide complexation facilitated by the cis-configuration of the hydroxyl groups of mannose monomers. Hydrogen bonding and chemical interactions with metal sites were also suggested by Rath and Subramanian in their studies on guar gum adsorption on biotite mica [10]. In a recent study, Wang et al. demonstrated that hydrogen bonding is the main driving force behind guar gum adsorption onto talc [11]. Their data also show that the adsorption density of guar gum on alumina is about five times lower than the adsorption density on talc. Pawlik and Laskowski reported that the amount of guar gum adsorbed on illite was independent of ionic strength over a wide range of salt concentrations [12]. The adsorption density of the polysaccharide on illite did not measurably change with ionic strength from that of distilled water to about 50%-saturated KCl/NaCl potash brine (~3N KCl/NaCl). However, guar gum adsorption on dolomite dramatically decreased over the same range of ionic strengths, and no reliable explanation of that phenomenon was proposed [12]. The water structure-breaking or structure-making capabilities of background ions are usually ignored when discussing adsorption mechanisms of polymers. The concept of “structure breakers” and “structure makers” was first introduced by Gurney, and Frank and Wen who postulated that each ion is surrounded by three distinct regions of water structure [13,14]. In the first layer, water molecules are tightly bound to the ion. The second region extends farther away from the ion and is referred to as the region of structure breaking. Only at larger distances, where the ionic field is weak, water molecules form the “normal” ice-like structure. It is also now recognized that the first layer can be further divided into the primary and secondary hydration shells. Small, strongly hydrated ions reinforce the “normal” structure of water and the region of structure breaking disappears. In contrast, large less-hydrated ions disturb the ice-like structure and generate an extensive region of structure breaking. Experimentally, these two effects can readily be distinguished through viscosity measurements. Increasing concentrations of structure-breaking ions result in a decrease of the viscosity of aqueous solutions. On the other hand, increasing amounts of structure-makers significantly reduce the viscosity of water. Alkali metal cations form a sequence known as the Hofmeister series. The Hofmeister series - Cs+, K+, Na+, Li+ - orders the cations from the least hydrated to the most hydrated. Based on literature viscosity data for aqueous

Jan 1, 2005

By Georgios Kalamaras, Chiaia Dinu, Platania Paolo, Alessio Carlo, Giampiero Cirvegna, Claudio Santucci

The Project alignment initiates north of Pinerolo, along the State Road 23[S.S. 23] that is one of the principal arteries to the northwestern Alps where a number of Olympic events for the 2006 Winter Games will be held. The 3.5 km ring road bypasses the Porte habitat by traversing twice the Chisone River. It consists of the following principal structures [Figure 1]: San Martino bridge [130 m in four bays] Prarostino viaduct [130 m in four bays] Craviale tunnel [1055 m] Turinella bridge [a 50 m long bridge that connects the two tunnels] Turina tunnel [665 m] Malanaggio viaduct [350 m in 9 bays]. The road section is 13 m wide and is made up of two 3.75 m lanes, a hard shoulder [1.50 m wide] and a 1.25 m wide curb for each lane. The Project maximum velocity is 100 km/h.

Jan 1, 2005

By D. Bessinger, J. M. A. Geldenhuis

High titania slag is produced from the smelting of ilmenite. These slags contain approximately 85 per cent TiO2 and consist mainly of a M3O5 solid-solution phase. During cooling the slag can decrepitate to a fine particulate material, which decreases the value of the product. Based on X-ray diffraction analyses of the decrepitated slag after cooling, it was found that the M3O5 phase had almost disappeared. The disappearance of the M3O5 phase was linked to oxidation of the slag. A M6O11 phase formed in the decrepitated slag. It is postulated that decrepitation of high titania slag is caused by volume changes due to the oxidation of the M3O5 phase in the slag.

Jan 1, 2005

By K McLeod

{Figure 1} The Placer Dome-Western Areas Joint Venture?s South Deep Twin Shaft Complex, has been planned and dreamt of for nearly 20 years. [ ] The gold reserve at the bottom of these shafts is one of the largest single intact gold deposits remaining in the world today, containing an estimated 57 million ounces. This is about the size of the fictitious reserve created by inventive prospectors for the infamous BREEX scam in Kalimantan about ten years ago and about the size of the reserve Harmony claims as its own in it?s current hostile takeover bid for Gold Fields. So it is certainly of the magnitude that dreams are made of. [ ] {Figure 2} The unique orebody lies in a continuous, highly concentrated, thick deposit, an estimated twelve kilometres along dip and a two kilometre wide strike. Due to the thickness of some sections of the reef, up to 60 metres in places, bulk mining methods will be required for it?s extraction. [ ] {Figure 3} The twin shaft system comprises a main shaft which had an initial design depth of 2765m and a ventilation shaft of 2760m, making them the world?s deepest to be sunk in a single lift. The shafts were

Jan 1, 2005

By M Miller

Operators of nickel laterite pressure acid leach and gold pressure oxidation technology frequently employ a series of steam condensing heaters to preheat the leach feed slurry. The heaters are an economic pinch point û although the thermal performance of the heaters is critical to overall process viability and operating cost minimisation, they are also a significant capital item and must be sized accordingly. Despite this, discussions of the factors underlying heater design are conspicuously absent from technical literature, and existing operations feature a conflicting range of heater sizes and configurations. This variety would suggest that at least some of the chosen heater designs are oversized. As part of its detailed design stage, the Ravensthorpe Nickel Project (RNP) constructed and tested a pilot plant heater to develop an understanding of the heating process and to ensure that the RNP heaters were appropriately sized. This testwork used RNP slurry at design density and viscosity on a 450 mm diameter, 6500 mm high column. The pilot plant testwork demonstrated the intrinsic efficiency of the direct steam condensation heating process, which was essentially independent of slurry density and viscosity. Presence of non-condensable gases in the steam phase decreased the heat transferred in certain circumstances, but heater performance remained consistent with thermodynamic limitations. Stagewise heat transfer within the column was rapid, and suggested either a very high slurry surface area or excellent heat transfer within the slurry phase. While the testwork did not set out to distinguish between these effects, physical evidence pointed to droplet formation in the inter-tray shower zone, giving a high heat transfer area. For scale-up purposes, the key facts were that the heat transfer rate was not limited by using high viscosity slurries and heaters could be designed using the principles applied to the smaller of those in existing operations. This paper discusses existing slurry heater designs, the current understanding from open literature, the pilot plant testwork, results and analysis, and scale-up to commercial sized equipment.

Jan 1, 2005

By K Kongolo, M K. Kalenga

It is well known that the electrochemical precipitation of metals from aqueous solutions is conducted by the electrochemical standard potential scale. This scale indicates the order of nobility of different metals. Consequently, the standard potential scale shows the nocivity of metals when they are present as impurities in aqueous solutions containing metals. In the hydrometallurgy of cobalt, nickel and zinc are co-deposited during cobalt electrodeposition. Nickel has almost the same chemical, physical and electrochemical properties as cobalt. Furthermore, the electrochemical potential of nickel is relatively higher than that of cobalt. For this reason nickel is preferentially reduced at the cathode in the presence of cobalt. The presence of small amounts of zinc in solution leads to contamination of cobalt electro won. In spite of its lower electrochemical potential in comparison to cobalt, zinc is reduced on the cathode because of its higher hydrogen-overvoltage. But, in the hydrometallurgy of zinc, small amounts of cobalt present into solution will contaminates the zinc reduced at the cathode. This is easily explained by the fact that cobalt is more electropositive than zinc. The co-deposition mechanism of sulphur at the cathode is not yet well understood. Great attention has to be paid to the mechanism of co-deposition of sulphur during cobalt electrolysis..This work aimed to investigate the influence of some parameters on the co-deposition of nickel, zinc and sulphur during cobalt electrowinning. The following parameters have been investigated : Co2+ concentration in the electrolyte, current density and ammonium sulphate (NH4)2SO4 additions. It has been established that important nickel, zinc and sulphur co-deposition takes place at relatively low Co2+ concentration in solution. The behaviour of these elements with regard to the cathodic phenomena has been established.

Jan 1, 2005

By J Walasiak

In the climate planning of mines and tunnelling with anticipated poor climatic conditions, and especially in case of longer working shifts, the main question is whether it can be reliably prevented that certain climatic limits laid down be exceeded. Working at high temperature and/or humidity can lead to reduced human working energy û a very important economic aspect û and to a risky lack of concentration on the part of the miners or to heat collapse and extremely dangerous heat stroke. With the Deutsche Montan Technologie GmbH (DMT) climate prediction programs, both the dry and the extremely significant humid heat transfer can be calculated. This is due to the high planning reliability involved. With the help of these climate prediction programs it is already possible to determine the anticipated climatic values for the operation phase as early as the planning stage of new ore or coal fields or of tunnel construction projects and to design the optimum air cooling system for every underground project with due regard to technical and economic aspects.

Jan 1, 2005

By J. O. G. Posada

Magnesium derived foams were prepared by using the so-called baking of powder blended precursor material method. This method comprises mixing magnesium powder with a small fraction of blowing agent (ZrH2, Cs2CO3 and CaH2) and Ni like catalyst, compacting this mix and creating a foam by heat treatment above the magnesium melting temperature. The resulting samples were characterised by microscopy, gas adsorption (BET method) and by small angle neutron scattering. Several mathematical models were used in order to determine particle size distribution, fractal dimension and total pore volume fractions.

Jan 1, 2005

By P. Venkatraman

Laboratory and pilot-scale test data have shown that the innovative feed presentation of the CrossFlow separator provides improved metallurgy when compared to traditional hindered-bed or teeter-bed classifiers. This design feature prevents excess water from entering the separation chamber and disrupting the overall fluidization flow rate within the teeter zone. Recent side-by-side industrial-scale evaluations have verified that this technology can improve overall efficiency, reduce the cut point of separation, and increase throughput capacity. This paper describes the important features that make this novel separator ideally suited for size classification and density concentration. Test data from heavy mineral, phosphate, and industrial mineral applications are also discussed.

Jan 1, 2005

By M. Morrongiello

The Kalgoorlie Consolidated Gold Mines Fimiston Open Pit is mining through a dense network of disused level workings and stopes of varied sizes and orientations. This study investigated the interaction between underground workings and the pit slope stability, in particular for the ultimate pit depth of over 600 metres. Parametric analyses were conducted on the structural and rock mass properties in order to provide realistic input. Several cases in both 2D and pseudo 3D using UDEC were modeled and analyzed to investigate the performance of the rock mass at various mining stages. The concept of equivalent property factor was also introduced to model the 3D behavior using 2D models. Based on the modelling results, the possible failure mechanisms and deformation of the pit walls were assessed. Factors of safety have been derived for the pit slope at different mining stages using the strength reduction technique. The modelling results agree well with pit performance monitoring results to date. The concept and results presented in this paper could be a useful reference for operations with similar circumstances and stress regimes.

Jan 1, 2005

By Zhang Chuanfu

Keywords: solid solution, Ni-Co alloy powders, thermal decomposition, fibres. Synthesis of fibrous Ni-Co alloy powders was achieved by thermal decomposition of precursor of complex Ni-Co oxalates solid solutions obtained via modified coprecipitation method among intimate mixing solution of NiCl2?6H2O , CoCl2?6H2O and H2C2O4?2H2O in the presence of surfactant polyvinylpyrrolidone (PVP) and organic solvent ethanol. Scan electron microscopy (SEM), X-ray diffraction (XRD), X-Ray photoelectron spectroscopy (XPS), disperse energy X-ray analyses (EDX) were used to characterize the structure features and chemical compositions of the as-prepared fibres. The influences of decomposition conditions, including temperature, time, the flow rate of N2+H2, and the heating rate, on the morphology, average size and specific surface area of the Ni-Co alloy powders were investigated. It is found that a trend of the mutual alloying of nickel and cobalt: the formation of perfect solid solution for any compositions NixCo100-x was indicated and corresponding NixCo100-x alloys with fcc phase can be obtained under the optimal conditions.

Jan 1, 2005

By Jesús Contreras

Within its programme for continuous improvement and cultural change, Atlantic Copper has installed the Six Sigma methodology as a basic tool for the improvement of management techniques in all its production centres. Following an implementation period, the methodology is widely used for analysis and improvement, not only in the fields of production and maintenance, but also in other areas of the business such as supplies or energy management. The present paper describes, phase-by-phase, the project that was developed to improve the quality of converter slag through the application of Six Sigma techniques, from the initial set up to the final results obtained.

Jan 1, 2005

By S. Achilleoudes

This paper describes the various factors that contribute to the maximum design pressures acting on box fronts and how these factors influence the mass and economy of box front steelwork. The influence of material density, rock size and moisture content on the incidence of hang ups and mud rushes in the rock pass is also highlighted. The loads acting on any box front are a function of several different parameters. These include natural, operational and excavational parameters. A case study analysis was carried out using UG2 ore and a typical box front structure to demonstrate the relationship between the mass of the box front and the material pressures resulting from variations in the above parameters. Based on the results of this case study, the required design mass of a side mounted box front for a rock pass containing platinumUG2 increases in (close to) linear proportion to % overbreak and is also linearly proportional to the pressure on the face of the box front beyond saturated conditions. The mass of the box front structure also doubles with a 100%increase in over-break which emphasises that a box hole excavation that is as neat as possible will yield a lighter and more econimical box front structure.

Jan 1, 2005