By Y. Yang, S. Peelman, J. Sietsma, Z. H. I. Sun

The rare earth elements (REEs) present in the Kiruna iron ore mine tailings are being considered as a new REE resource for the EU. These tailings, after beneficiation, contain approximately 5000 ppm of rare earths, concentrated in apatite and monazite minerals. To economically extract the REEs from these tailings the phosphorous contained within the apatite must also be extracted and the waste production of the process should be minimal. To achieve the extraction of REEs and phosphorous HCl and HNO3 were investigated as possible leaching agents. Based on the results a leaching process using HNO3 is proposed. This process produces H3PO4 from the apatite while simultaneously dissolving the REEs. The resulting leach liquor is then cooled to remove the unwanted Ca as Ca(NO3)2. Analysis of the leach liquor reveals extraction ratios of between 75% and 100% for the heavy REE (e.g. Y, Eu, Dy, …) and below 40% from the light REEs (i.e. Ce, La). Full phosphorous extraction was also achieved.

Jan 1, 2016

By Jiangwei Shen, Cong Wang, Haibin Zuo

The research on the formation of Silico-Ferrite of Calcium and Aluminium (SFCA) in the process of cooling and solidification is rarely reported. The crystallization process was observed by using scanning electron microscopy (SEM) and optical microscope in this paper. The effect of different cooling system on the microstructure and phase composition of the sinters was investigated to obtain the appropriate cooling rate to improve the metallurgical properties of sinters. The experimental results show that the crystallization of calcium ferrite is getting better when the cooling rate is decreased from water quenching to cooling in the air. There are a large number of hematite phases with interconnected crystal structure in the sample cooled in the air. In the case of the compressive strength, it was determined by the mineral composition and pore structure, higher SFCA and hematite contents in sinter cooling in the air lead to a higher strength. Glass phase in the water quenching sinter was the major reason for the lowest strength. High porosity contributes to a decrease in compressive strength for the sinter cooling in the furnace. Therefore the air cooling was the appropriate cooling rate to achieve high quality sinter under this experimental condition.

Jan 1, 2016

By Yuanbo Zhang, Yingming Chen, Zijian Su, Bingbing Liu, Jun Chen

Iron, tin-bearing tailings is a kind of hazardous solid waste generated from cassiterite dressing operation. It is difficult to utilize the tailings by present mineral processing methods due to the complex dissemination characteristics. In this study, a process of gas-based magnetizing roasting followed by magnetic separation was studied for separating and recovering iron from the tailings. The effects of roasting and magnetic separation parameters on the recovery of iron were systematically investigated. The optimum parameters were proposed as follows: CO/(CO+CO2) content of 5%, roasting temperature of 850 C, roasting time of 60 min, grinding particle size of 90% less than 45 μm and magnetic field intensity of 800 Gs. Under these conditions, the magnetic concentrate containing 68.5% Fe and 0.06% Sn was achieved, which can be used as high-quality raw materials for direct reduction iron production.

Jan 1, 2016

By Jiang Diao, Yong Qiao, Xuan Liu, Tao Zhang, Bing Xie

The equilibrium experiments between the FeO-SiO2-MnO-TiO2-V2O3-Cr2O3-MgO slag system and solid pure iron were performed to investigate the vanadium and chromium distribution ratio under Ar atmosphere. The influence of w(FeO), w(V2O3) and w(Cr2O3) in slag on vanadium and chromium distribution ratios were studied at 1653 K. The experimental results were compared with calculated distribution ratios based on molecule and ions coexistence theory. Both of them showed that higher FeO content in slag would improve the distribution ratios of V and Cr between slag and hot metal. The distribution ratio of Cr or V increased with the increase of Cr2O3 or V2O3 content, respectively. To optimize the oxidation of V and Cr from hot metal, a high oxidizing slag and suitable content of Cr2O3 and V2O3 in the slag were recommended. The results provided reference for the further study on the extraction of V and Cr in VTi magnetite.

Jan 1, 2016

By Bart Blanpain, Muxing Guo, Zhuangzhuang Liu

In order to stabilize free lime in the basic oxygen furnace (BOF) slag to achieve high value products, quartz sand and other additives are injected into slag. However, the current hot stage slag stabilization does not work in case of slag (before treatment) with a liquid fraction lower than 90%, where the slag containing solid particles is too viscous. Therefore, it is essential to understand how solid phases affect the viscosity of the slag system. In this study, the industrial BOF slags were investigated with respect to the correlation between volume fraction of solid phases and its viscosity. Slag viscosity was measured with a rotating type viscometer at temperatures below the liquidus. The volume fraction of solid phases was quantitatively calculated with FactSage. The Einstein-Roscoe equation was employed to predict the viscosity of BOF slag.

Jan 1, 2016

By Tianzu Yang, Weifeng Liu, Lin Chen, Wei Chen, DUCHAO ZHANG, HUI XIAO

Carbonaceous refractory materials are widely accepted in many reducing smelting processes such as iron and ferroalloys. Oxidizing processes such as copper concentrate smelting traditionally use magnesia and/or alumina/silica refractory materials. The main objection to the use of carbon-based refractories as the exposed working lining in oxidizing applications is the potential for free oxygen to react with the carbon at high temperature, which could rapidly degrade the refractory lining. In 2013, Outotec and GrafTech conducted joint trials of a thermally conductive, carbonaceous lining for smelting copper concentrates in the Outotec® pilot-scale top-submerged-lance (TSL) furnace in Dandenong, Australia. This testwork had two equally important goals; to demonstrate the ability of carbon refractories to withstand oxidizing process conditions, while ensuring that neither furnace operating conditions nor process stability were negatively affected by the refractory material. The paper discusses the input parameters of the trials, key observations during the testwork program, and the results and conclusions from both process and refractory design standpoints.

Jan 1, 2016

By Yongqi Sun, Zuotai Zhang

Hot slags, at the temperatures of 1450-1650 oC, carry a substantial amount of high quality thermal energy, which represents the largest undeveloped energy source in the steel industry. However, the waste heat recovery rate in China is less than 2%; thus there is a great potential of waste heat recovery. In this study, we investigated a chemical method to extract the waste heat from high temperature blast furnace slags, i.e., sludge gasification. Sewage sludge, another substantial waste produced in the municipal system, need to be timely disposed, the organics of which could be gasified using the waste heat in the slags for the purpose of syngas production. Both the kinetics and thermodynamics of the sludge gasification process were clarified here. Most importantly, an integrated system composed of multiple systems such as the steel industry, the cement industry, the municipal system and the chemical engineering industry, was analyzed in this study.

Jan 1, 2016

By Wenjun Duan, Zongliang Zuo, Qingbo Yu, Qin Qin, Junxiang Liu

Moving bed has been widely used in the field of heat and mass transfer and reaction between solid particles and gas. In order to enhance the heat exchange coefficient, there will be tube banks inserted in the moving bed. In the process of drying ammoniates particles or heat recovery from high-temperature particles with moving bed, the particles flow behavior around the tube banks is significant. In this paper, the particles flow behavior around the tube banks is investigated, and all the results can provide guidance for the design and operation of a moving bed.

Jan 1, 2016

By Wenjun Duan, Qingbo Yu, Qin Qin, Junxiang Liu

In the study, the coke-oven gas (COG)-steam reforming process using hot blast furnace slag (BFS) as the heat carrier is explored for producing hydrogen and recovering high-grade waste heat of hot BFS. The method of the Gibbs energy minimization approach through Lagrange multiplier is adopted in the thermodynamic analysis of reforming process. The simulation is carried out to study the operation pressure, temperature and steam to carbon ratio (S/C) based on the chemical equilibrium calculations. The optimal operation conditions are determined to improve the yield and fraction of hydrogen in the COG-steam reforming process. The results suggest that the preferential operation conditions for COG-steam reforming process to produce hydrogen are achieved at 600ºC, 1.5MPa and S/C (5.0). Due to the CaO and other melts in BFS, CH4, CO and CO2 in COG are converted and removed efficiently, especially CO2. The hydrogen fraction reaches to 86.7% and its production is about 1.22mol with 1mol of the COG.

Jan 1, 2016

By Guangliang Wu, Dong-chang Huang, Xin-bin Liu

High temperature mechanical properties of 50Cr5MoV roll steel was investigated by Gleeble 1500 thermal simulator testing machine The morphology, composition and microstructure of fracture surface were observed and analyzed by OM, SEM and EDS The results are indicative of that, there are two brittle temperature zones of 50Cr5MoV roll steel at the temperature of 600°C~950°C and 1300°C~1450°C, respectively. The section shrinkage rate is less than 60% The fracture mode changes from mixed ones dominated by intergranular to toughness transgranular one with the increase of temperature at the range of 650°C~1300°C. The fracture is along the solid--liquid phase at the range of 1300°C~ melting point It is crucial to formulate the 50Cr5MoV casting technology, to prevent the cracks and improve the quality of 50Cr5MoV roll steel.

Jan 1, 2016

By Aiyuan Ma, Kun Yang, Weiheng Chen, Jinhui Peng, Shiwei Li, Feng Xie, Libo Zhang

In this thesis, a new process of recovering zinc sulfide ores was developed. The novel synthetic coordination leaching process mainly included two steps: microwave assisted phase reconstruction and compound coordination leaching. By applying various techniques, such as chemical composition analysis, X-ray diffractometry (XRD) and Raman spectroscopy, it could be concluded that sulfide phases would directly oxidized to zinc oxides under the 500 ºC microwave roasting and adding 30% Na2O2. What’s more, zinc leaching rate reached to 61.16% within 2 hours. Compared to the current technologies, this procedure had the advantage of avoiding SO2 emission, high leaching efficiency, simple process, manipulate easily, and low cost, which could be expected tremendous application potentials.

Jan 1, 2016

By Tianzu Yang, Weifeng Liu, Lin Chen, Qingkai Xiao, DUCHAO ZHANG

To solve the problem of low leaching ratio of direct gold cyanide leaching from arsenical refractory gold concentrate, this paper proposed a matte smelting process for gold enrichment in low grade copper matte. The effects of copper content in the mixed material, ratio change in slag type, smelting temperature and reaction time on recovery rate of gold and copper were investigated. The experimental results indicated that the recovery rate of gold increased with the increase of copper content in the mixed materials, temperature and reaction time. It was also noted that the recovery rate of gold and copper were respectively 98.16% and 96.39% when the addition of copper content in the mixed material was 3%, slag type of CaO/SiO2 and FeO/SiO2 were 0.6 and 0.9 in 1250°C and the time of reaction was 40min. Most of the arsenic was oxidized into As2O3 existed in the dust. The results showed that the matte smelting method can achieve efficient recovery of gold from arsenical refractory gold concentrate.

Jan 1, 2016

By Anja Pfennig, Thomas Böllinghaus, Marcus Wolf

During CCS components are exposed to a corrosive environment and mechanical stress which results in corrosion fatigue and is inevitably followed by the lifetime reduction of these components. The lifetime reduction of the cyclically loaded high alloyed stainless injectionpipe steel AISI 420C (X46Cr13, 1.4034) constantly exposed to highly corrosive CO2- saturated hot thermal water is demonstrated in in-situ-laboratory experiments (T = 60 °C, brine: Stuttgart Aquifer, flow rate: 30 l/h, CO2) in an environment similar to the on-shore CCS-site in the Northern German Bassin. In-situ tension-compression experiments were established simultaneously along with electrochemical measurements using a newly designed corrosion chamber in a resonant testing machine at a frequency as low as 30 – 40 Hz. In addition technical CO2 was introduced into the closed system at a rate close to 9 L/h. S-N plots, micrographic analysis and surface analysis of the fracture surface are demonstrated. X46Cr13 (surface roughness Rz = 4) reached the maximum number of cycles (12.5 x 106) at stress amplitude of 173 MPa producing a low scatter range of 1:3.5. Hydroxide and siderite layers were found on pits and crack surfaces. No typical fatigue limit exists. Pit corrosion prior to crack initiation may be identified as failure cause.

Jan 1, 2016

By Jie Li, Zhongliang Tian, Xun Hu, Kai Zhang, Yanqing Lai, Hongliang Zhang

The Al-Sc Alloys show many advanced properties for a wide range of engineering applications. But the metal Sc must be added into the metal Al in the form of the Al-Sc master alloy, which is usually produced by the thermal reduction process. In this paper, the decomposition voltages of Sc2O3 and Al2O3 in Na3AlF6-K3AlF6-AlF3 melt were calculated based on the Nernst equation. And the Al-Sc master alloy was prepared in the melt at 950°C by electrolysis. The results show that the Al-Sc master alloy can be prepared by the co-deposition of Sc3+ and Al3+ at the cathode if the concentration ratio of Sc2O3 to Al2O3 in the melt is more than 2:1 under the condition of the aluminum electrolysis. SEM and ICP analysis of the product indicates that the Al-Sc master alloy is made of the phase Al and the phase Al3Sc.

Jan 1, 2016

By Tianzu Yang, Weifeng Liu, Lin Chen, Wei Chen, DUCHAO ZHANG

Ni-M (Metal=Cu, Fe, Co, Mn, Zn, Cr) aerogel catalysts were tested for CH4 oxy-CO2 reforming. It was found that the Ni-Co bimetallic aerogel catalyst had the highest activity and stability in methane oxy-CO2 reforming among all the Ni-M aerogel catalysts. It exhibited a steady activity of 79 % (in terms of CH4 conversion) at 750 oC, which is the highest activity under a similar reaction condition as compared with those published in literature. Characterizations for the reduced catalysts indicated the formation of Ni-Co alloy, while other transition metals separated from Ni during the reduction process. Therefore, the active species in the Ni-Co bimetallic catalyst showed a stronger interaction than those in other Ni-M catalysts, which might be one of the main reasons for the better catalytic performance of the catalyst.

Jan 1, 2016

By Yang Hai-long, FAN Gang, LI Cun-xiong, WEI Chang, LI Min-ting, LI Xing-bin, DENG Zhi-gan

Hydrothermal sulfidation of pure cerussite with elemental sulfur has been reported in the present paper. The variables considered in the study were temperature, time, particle size and elemental sulfur fraction in the reacting mixture. Temperature was the most important factor at temperatures above 180 , PbS and PbSO4 were the only stable reaction products in the sulfidation of cerussite. The experimental data indicated that under the hydrothermal conditions with a particle size of -74+58 μm and sulfur fraction in reacting mixture of 15% at 200 °C for 120 min, and 92% of lead sulfidation rate was achieved.

Jan 1, 2016

By Xudong Liu, Feng Chen, Yufeng Guo, Wei Chen, Tao Jiang

Willemite is typically found in oxidized zinc ores and metallurgical secondary resources but without effective extraction method yet. Based on the ideas of zinc phase reconstruction in the willemite, the extraction of zinc from willemite by calcified-roasting using CaO as additive and ammonia-leaching process was studied in this paper. The influences of CaO dosage, roasting temperature, roasting time on the phase transformation and zinc leaching rate were studied, which were characterized by XRD. The results indicated that Zn2SiO4 was transformed into ZnO or Zn2CaSi2O7 .After roasted with 1.4 times of theoretical CaO dosage at l280 for 40 minutes, willemite was thoroughly transformed into ZnO. The zinc leaching rate of the roasted sample was 97.45% in NH4Cl-NH3 H2O leaching system, which increased by 91.40 % compared with zinc leaching rate of 6.05% when willemite was directly leached in NH4Cl-NH3 H2O system.

Jan 1, 2016

By Chen Chen, Wang Yanze, Hong Xin

Furnace superalloy was applied in harsh environment within the erosion of high temperature and oxidizing atmosphere. With plasma powder surfacing technology, iron-based alloy powder was sprayed on the surface of 310S stainless steel to form oxidation layer that increases the oxidation resistance and reduces the cost of materials. With optimum technological parameters, in this paper, oxidation test of 100 hours on iron-based cladding alloy and furnace alloy were carried out at 1200 . The technique of XRF, XRD and EDS were used to characterize composition, oxide morphologies and surface mechanical properties. The results showed that Element composition of cladding layer formed by Plasma powder surfacing was well distributed. Its oxidation weight gain rate of 100 hours was 0.4552g/m2h, belonged to antioxidant level. The oxidation weight gain rate of furnace alloy was 1.4617g/m2h, belonged time-antioxidant level. And on the mechanical comparison test, surfacing alloy is relatively excellent than furnace alloy.

Jan 1, 2016

By Bart Blanpain, Tom Peter Jones, Muxing Guo, Liugang Chen, Huayue Shi

Fayalite based slag is formed during the smelting process of secondary copper resources. It was found that with the presence of high ZnO, the slag became viscous, causing a slag tapping problem. In the present paper, the phase relations of the slag system ZnO-“FeO”-SiO2-Al2O3- CaO (ZnO = 0-12 wt%, Al2O3% = 0-15 wt%, CaO = 0-1.5 wt%, with iron saturation) at 1150 °C is studied by using quenching technique followed by phase identification and compositional analysis of equilibrated samples. The dependence of FeO and Al2O3 solubility in the liquid slag on the chemical composition of slag is characterized. Based on the experimental data, the solid fraction of the slag, which may considerably, influences the slag viscosity, at the tapping temperature can be reasonably estimated and, therefore an appropriate modification of the slag composition can be made.

Jan 1, 2016

By Qiang Zhong, Qian Li, Yongbin Yang, Tao Jiang

Thermogravimetric analysis (TGA) has been used to research the pyrolysis and combustion processes of coal used in rotary kiln of iron ore oxide pellet. Furthermore, the effects of air flow and oxygen concentration on the combustion behavior of coal were examined with TGA. The results showed that two individual stages can be distinguished for the pyrolysis of coal, the water evaporation stage and the de-volatilization stage. And the information on ignition and burnout characteristics can be obtained from the combustion process analyzed by TGA. Large air flow almost has no effect to the combustion process except that it enhances combustion intensity. However, the combustion process is further accelerated under oxygen-enriched conditions. With all experimental results, it could provide an attractive approach of analyzing coal for the rotary kiln process.

Jan 1, 2016