Search Documents

By Jiang Feng, Zhang Libo, Peng Jinhui, Guo Zhanyong, Ju Shaohua, Lei Ting

The clean utilization of the residue containing chloride, CuCl residue, produced from zinc hydrometallurgy is very important for the recycle of valuable metals. And drying is the main process in recycling. In this study, response surface methodology was used to optimize operating conditions of the drying of CuCl residue in a convection oven and desirability function used as the methodology for the optimization. Optimization factors were air temperature (80–100°C), material thickness (10–25mm) and process time (80–120min) while investigated responses was final moisture content. The optimum conditions were found to be the temperature of 95.48°C with the material thickness of 13.47mm for the process time of 89.48 min. Under optimum conditions, the predicted moisture content of CuCl residue was 4.11% while the experimental date was 4.13%. The experimental value after process optimization was found to agree satisfactory with the predicted value. After drying, XRD was used to analyze the main phases of CuCl residue. The CuCl residue is made up of CuCl,Cu2O, ZnS and other compounds.

Jan 1, 2015

By Guanyong Shi, Zhihe Dou, Cong Wang, Ting'an Zhang, Hongyan Zhang

We prepared the CuCr alloy by thermit reduction-electromagnetic casting. But there are the defects such as stomata and oxide inclusions in CuCr alloy. In this paper, the existing state and distribution of inclusions and stomata in CuCr alloy are systematically analyzed. The alloy was characterized via SEM, EDS and metallographic microscope, in which the existing state and micro-structural defects of inclusions are analyzed. The results show that: there are three distinct areas: copper-rich areas, chromium-rich areas and the inclusion areas. Inclusions are mainly in the form of stomata and Al2O3 phase, mainly locating in the copper-rich phase and the interface area of chromium-rich phase and the copper-rich phase. Then, the composition of phases of the smelting slags and alloy were characterized via XRD. The results show that: the slag consists of Al2O3 and a little of Cr, the alloy consists of Cr, Cu and a little of Al2O3.

Jan 1, 2015

By Kai Kang, Jun Bao, Shouping Liu, Xiao Sun

Powder characteristics have a significant influence on selective laser melting (SLM) process. In this research, particle size, surface contour and the microstructure of IN718 powder used in SLM were tested, and the physical and chemical changes during heating process of the powder were investigated as well. The shape characteristic and fluid properties of IN718 powder were defined and measured. It is shows that most particles of IN718 powder exhibited nearly spherical shapes, and the particle size is about 22.95μm. On this basis, IN718 sample was fabricated by SLM process using the powder and the microstructure of the fabricated sample was investigated. The results indicated that the sample has a dense microstructure, no macro-defects but a few micropores and porosity. Compared with the powder, there was no new phase formed in the sample and melting point of the sample was little less than that of the powder.

Jan 1, 2015

By O. P. Pandey, Rama Arora, Gurmel Singh, Suresh Kumar

The tribological behavior of Dual Particles Size (DPS) rutile reinforced LM13 alloy composite was investigated under varying applied pressure from 125 kPa to 625 kPa at a constant sliding speed of 1.6 m/s. In the present studies, 15 wt.% of rutile particles of different sizes (50-75 μm and 106-125 μm) are reinforced in the Al-12Si alloy (LM13) by liquid metallurgy route. Microhardness of the prepared samples was measured in different phases. Microstructure, wear mechanism and surface morphology of the wear surfaces and debris was observed under optical and scanning electron microscope. The change in wear behavior has been explained with reference to the observed EDS analysis of the wear track and debris. However, an interesting change in wear feature, mild to severe wear transition at critical pressure was noticed in wear behavior of the composite. The Al-DPS composite has immense potential to be used as a component material for tribological applications.

Jan 1, 2015

By M. Z. Quadir, M. A. Islam, P. J. Hazell, G. J. Appleby-Thomas, J. P. Escobedo

The mechanical response of closed-cell aluminium metallic foams subjected to low and high strain-rate loading has been investigated. A set of quasi-static and dynamic (shock) compressive tests have been conducted on closed-cell aluminium foams (CYMAT) with densities of 0.50 and 0.30 g/cc. Post-mortem characterization via optical microscopy and electron backscatter diffraction (EBSD) was performed on pristine and deformed specimens to elucidate the dominant deformation mechanisms in these materials. The combination of these techniques allowed for the assessment of critical deformation parameters such as changes in cell geometry and morphology, as well as microstructural evolution and deformation of the aluminium cellular network. These findings aim to aid in the design and development of optimized material structures for impact and blast protection.

Jan 1, 2015

By Gui-fang ZHANG, Zhe SHI, Lei GAO

Secondary V-recycling slag, an industrial waste containing high gallium is being dumped continuously, which causes the loss of gallium. Thus, the alkali fusion process was employed to recover gallium from this slag. The effects factors on extraction of gallium such as roasting temperature, roasting time, alkali fusion agent concentration and CaO concentration were investigated in the paper. The experimental results indicated that excessive roasting temperature and roasting time is unfavorable to the recovery rate of gallium. The appropriate roasting temperature and duration are 1000 and 2 hours, respectively; The appropriate proportioning of Na2CO3: NaOH is 2:1 when the concentration of alkali fusion agent weighs 0.4 times the mass of the slag; In order to remove SiO2 from the leaching liquor, CaO should be used as an additive in the roasting process. The appropriate concentration of CaO should weigh 0.2 times the mass of the slag. Employing these optimal alkali fusion conditions in the roasting process, gallium recovery is above 90%

Jan 1, 2015

By Mao Chen, Baojun Zhao, Zhixiang Cui

Bottom blown oxygen copper smelting process, operated at high grade matte (up to 75 wt% Cu) with relatively low (2-3 wt%) Cu in slag, has been commercialized for more than five years at Dongying Fangyuan Nonferrous Metals CO., Ltd. Quenched slag and matte samples have been collected at different operating conditions while the slag temperature was measured by thermocouple. The samples were analysed by X-ray Fluorescence and Electron Probe X-ray Microanalysis. FactSage computational software was used to explain the observations of the industrial samples. The analyses show that the copper loss was closely related to the operation parameters. The Fe/SiO2 in slag and temperature determine the solid proportion, which significantly affects the physical entrained and also chemically dissolved copper in the slag. The present study will be useful in understanding the slag chemistry of bottom blown copper smelting furnace and in optimization of the operating conditions to lower Cu loss in the slag.

Jan 1, 2015

By Xiang-dong XING, Zhen-yang wang, Xing-le LIU, Jian-Liang Zhang

Experiments were carried out by adding CaF2 as catalyst in a Ar atmosphere to study the isothermal reduction kinetics of vanadium titano-magnetite carbon composite pellets under high temperature in the range from1473 to 1673K. By analyzing reduction mechanism, it was found that the rate controlling step was gas diffusion, and the activation energy was 178.39kJ•mol-1 without adding any catalysts. Adding CaF2 of 3% to vanadium titano-magnetite carbon composite pellets can decrease the apparent activation energy of reduction, and the decrease extent was 14.95kJ•mol-1. In addition, temperature is an important factor influencing on reaction rate.

Jan 1, 2015

By Ting Liu, Qian Li, Peng Deng

The wastewater containing Hg2+ and Pb2+ does great harm to the environment and human bodies. Traditional wastewater treatment cannot fundamentally put a stop to heavy metals pollution for producing secondary pollution. In this paper, Hg2+ and Pb2+ in wastewater were removed and recovered by sulfide precipitation- flotation. Sodium sulfide was used as precipitant and butyl ammonium aerofloat was used as collector. Results indicated that Hg2+ and Pb2+ could be reduce to less than 0.03mg/L and 0.16mg/L respectively by both coprecipitation- floatation and fractional precipitation- floatation. In these two methods, fractional precipitation flotation could not only remove Hg2+ and Pb2+ from wastewater, but also could recover mercury and lead effectively. The infrared spectrograms showed that the adsorption between butyl ammonium aerofloat and mercury precipitate or lead precipitate is chemisorption.

Jan 1, 2015

By B. K. Chakrabarti

Modeling and a screening design of experiment (DOE) was performed with the process variables to identify the greatest effect of variables on the response quality in the dead burning of magnesite refractory in a rotary kiln. Among various interdependent variable factors, the design variables chosen were raw magnesite (RM) feed rate, kiln rotation time i,e, seconds per rotation(SPM) and burning zone temperature (BZT). The response variables chosen were exit gas temperature and density of dead burnt magnesite(DBM). ANOVA and normal plots were used to evaluate the effects.This work had enabled to correlate the BZT, RPM, RM feed with the exit gas temp and density of magnesite produced. The result opens up an avenue to look into the optimum region of operations within the ranges of variables considered in order to conserve energy and to minimize the exhaust gas temperature and to maximize the density of the DBM produced

Jan 1, 2015

By Yuzhe Zhang, Xiaodi Huang, Xinli Wang, Bowen Li, Matthew Andriese, Jiann-Yang Hwang, Zhiwei Peng

The recycling of waste tires has been a big environmental problem. About 280 million waste tires are produced annually in the United States and more than 2 billion tires are stockpiled, which cause fire hazards and health issues. Tire rubbers are insoluble elastic high polymer materials. They are not biodegradable and may take hundreds of years to decompose in the natural environment. Microwave irradiation can be a thermal processing method for the decomposition of tire rubbers. In this study, the microwave absorption properties of waste tire at various temperatures are characterized to determine the conditions favorable for the microwave heating of waste tires.

Jan 1, 2015

By Xinlei Jia, Wenming Guo, Yanling Zhang

A large amount of stainless steel dust rich in Fe, Cr, and Ni has been being generated in China. Smelting treatment is accepted as a practical method for the recovery/reutilization of these second resources, during which Fe, Cr, and Ni is reduced into one metal phase and then separated from the residue slag. Based on the typical compositions of stainless steel dust, the residual slag can be termed as CaO-SiO2-MgO-Al2O3 system. In this paper, the activity coefficients of Cr in Fe-Cr-Ni-C (-Si/Al) melt and the properties of CaO-SiO2-MgO-Al2O3- 1%CrO system thermodynamically approached. Then, in laboratory experiments, the recovery ratios of Cr and its distribution behaviors between Fe-Cr-Ni-C melt and CaO-SiO2-MgO-Al2O3 slag system were examined.

Jan 1, 2015

By Sadegh Safarzadeh, Anne-Marie Suriano, Stanley Howard

The electrodeposition of metal ions from aqueous electrolyte solutions has been a well-known process for the last half century. With numerous industrial applications such as electroplating, electrowinning and electrorefining, the kinetics of electrochemical reactions involved in the process has been extensively researched. Arrhenius-type rate equations, the Butler-Volmer equation, and the empirical Tafel equation are among the most important models to explain the rate of electrochemical reactions. The study of the kinetics of metal deposition is critical to understanding the underlying mechanisms through which a certain morphology of metal deposit is formed on the cathode. The purpose of this paper is to elucidate the influence of experimental parameters such as pH and additives on the rate and the reaction mechanism determining the rate limiting step of the electrodeposition reactions.

Jan 1, 2015

By Chao Zhang, Jian Guo, Chaoquan Yao, Leige Xia, Xinyu Li, Jianliang Zhang

In this research, analytical reagents were used for the sintering experiments. And the sinters were using X-ray diffraction, scanning electron microscope and mineralogical microscope analysis to study the effect mechanism of manganese on the silico-ferrite of calcium and aluminum (SFCA) bonding phase formation during the sintering process. The results indicated that the increasing content of manganese would greatly reduce the content of SFCA, and promote the formation of calcium aluminum silicate and the amount of pores and cracks. The existence of manganese inhibited the silicon form into the SFCA and a great deal of Fe2O3 was participated in the crystal transition to Fe3O4. When the ratio of the added manganese was less than 3% in the mixing, the calcium ferrite was in substantially interleaving corrosion with hematite and magnetite. Both the porosity and silicate glass phase content were low simultaneously, which contributed to the sintering production.

Jan 1, 2015

By Jing Zhan, Tian-zu Yang, Wei-feng Li, Li-Hua Jiang, Shi-yan Xu, Jian-yang Huang, Chuan-fu Zhang, Yan-qing Fan

The amount and activity of coal, reduction temperature and other parameters of the process of bottom-blown reduction of liquid high lead slag were investigated in laboratory. Methods to strengthen the bottom-blown reduction process were studied by industrial production. The results were in the follows: the reduction temperature was 1150℃; reduction time was 1.5h; the reductant was anthracite; lead content in slag was controlled to 2%; the rate of coal was 7% and gasification loss of coal in high temperature was severe; liquid lead slag reduction rate was faster with coal; prolonging the reaction size had little effect on reducing lead in slag; the size of the reactor can be further reduced.

Jan 1, 2015

By Saynbaatar, Gangping Ma, Jianhua Fu, Qiqige, Jinghua Wang

The influence on the performance of foam concrete made by replacing cement with some industrial waste residues was researched in this paper. The result shows that the 7d and 28d compressive strength of foam concrete increases firstly and then decreases with the increasing amount of industrial waste residue. The proper added range is 10%-20% for steel slag, blast furnace slag and coal ash, but, 8% for desulfurized fly ash. With the proper adding ratio, the compressive strength of foam concrete always increased comparing with the pure cement foam concrete. When adding 48% of the compound industrial waste residues, the 28d compressive strength of the foam concrete reached the 2.9MPa which could match the pure cement foam concrete. The results indicates that there is a synergistic effect among the compound industrial waste residue, and this effect is benefit to improving the compressive strength of foam concrete.

Jan 1, 2015

By Cong Wang, Kexin Jiao, Yongan Zhao, Haibin Zuo, Jianliang Zhang

Traditional refractory materials for blast furnace hearth lining are mainly composed of carbon bricks and the ceramic cup. However, these materials can’t meet the demands for long service life design of blast furnaces. In this paper, a new refractory called carbon composite brick (CCB) was introduced, which combined the advantages of carbon bricks and the ceramic cup. In this case, the resistance of the CCB against corrosion was equal to the ceramic cup and the thermal conductivity of the CCB was equal to carbon bricks. From the results of more than 20 blast furnaces, the CCB could be well used in small blast furnaces and large blast furnaces. In the bad condition of low grade burden and high smelting intensity, the CCB gave full play to the role of cooling system, and effectively resisted the erosion of hot metal to improve the service life of blast furnaces.

Jan 1, 2015

By I. M. Richardson, M. Janssen, I. J. Bennett, V. A. Popovich

The most critical processing step during the manufacture of screen-printed crystalline solar cells is firing aluminium and silver contacts, which generates residual stresses and solar cell bowing. In this paper, an alternative Ag contact formation mechanism is proposed and aspects related to electrical contact properties, residual stresses and layer delamination are investigated. It is found that there are two main processing parameters affecting the uniformity and delamination of the Ag/Si interface, namely the peak firing temperature and the silicon surface roughness. Silicon surface polishing gives a better wetting of the silicon surface by the glass layer, resulting in a good contact and lower incidence of large voids, compared to the case of highly textured surfaces. The non-uniformity in the glass layer and large voids at the Ag/Si interface (in the case of a textured surface) are expected to have a negative effect on the mechanical strength of the solar cell.

Jan 1, 2015

By Jesse White, Tyler Salisbury

Research projects contain many stages of development from the conception of an idea to a fullscale commercial operation. The transition from laboratory-scale research to bench-scale roasting can represent a significant increase in complexity and cost, depending on how many variables are being evaluated. Thermogravimetric analysis (TGA) can simulate roasting conditions and produce a small sample for chemical analysis or materials characterization. A simultaneous thermogravimetric and differential scanning calorimetry (TG–DSC) can identify endothermic and exothermic reaction temperatures. Using thermal analysis, some of the process variables can be tested and eliminated such as ore and reagent blends, retention times, operating temperatures, and some atmospheres.

Jan 1, 2015

By Ligang Zhang, Wen Chen, Xinghua Liu, Jialin Li, Xiaoyin Liu, Zhenhong Liao

A research-scale fluidization and magnetization roasting device was developed to evaluate a processing option that might offset the complexity and high cost of the conventional magnetization roasting process on siderite. In this study, the operating parameters of the fluidization and magnetization roasting device for siderite were evaluated through cold-flow tests and magnetization roasting tests. The reaction mechanism functions of the fluidized roasting process are revealed with kinetic studies.

Jan 1, 2015