Search Documents

By Scott, Turner

IN 1933, the monetary metals were produced in a ratio of 6.7 oz. of silver to 1 oz. of gold, the lowest relatively for silver since the period from 1851 to 1865. At the beginning of that period, the virgin placers of California -and Australia began producing almost simultaneously; in consequence, there was an abrupt fall in the high silver side of the ratio that had prevailed through the centuries after America was discovered. The output from the Comstock and other silver-bearing lodes, located a decade after this influx of new gold began, soon restored the production ratio to its former proportion, that is, a relatively large weight of silver compared to gold.

Jan 1, 1934

By O. G. Lellep

Modern shaft kilns in Europe are fully mechanized and burn cement of acceptable quality at 700,000 Btu per bbl and lime at 3.2 million Btu per net ton. Rotary kilns for cement have increased in thermal efficiency by using exit gas heat for preheating incoming raw material and by recovering heat from outgoing clinker in air-quench coolers. The dry process Lepol or ACL kiln has the lowest fuel consumption, 580,000 to 630,000 Btu per bbl, and very low dust loss, about 1 pct weight of clinker. The Holdebank-Gygi system reaches 720,000 Btu per bbl. The calcinator kiln for the wet process consumes 1.1 million Btu per bbl. IN every country economic circumstances prescribe the method used to produce a commodity at lowest cost. In Pennsvlvania a man's wages for working 4 hr buys a ton of coal wholesale; in Germany a laborer must work 40 hr, or ten times as long. In western Europe, therefore, conservation of fuel is of primary importance, and recent practices of burning lime and cement differ from those employed in the United States. 'This Paper presents data collected during a trip through western Europe in 1953. Considered uneconomical, shaft kilns for burning

Jan 1, 1955

Jan 1, 1879

By R. J. Brison, W. C. Bleimeister

The International Salt Company has long been interested in finding an efficient process for the removal of impurities from rock salt, and particularly from the rock salt produced at the Detroit mine. Methods which have been used previously at the Detroit mine included both hand sorting and differential crushing in a Bradford breaker with rejection of the oversize. Neither of these methods was adequately effective. The development of a new process for removal of impurities from rock salt has been described in the preceding article." Basically, the process consists of exposure of crude rock salt to radiant heating which selectively heats the impure particles. Subsequently the heated particles are removed by adhesion to a heat sensitive-coating on a conveyor belt. This method was found to be effective in improving both the quality and appearance of rock salt by the rejection of the dark, impure particles. The first commercial unit employing the new thermoadhesive method of dry separation of minerals was installed at the Detroit mine of International Salt Company in Detroit, Mich. (Fig. l). This unit was first put into operation in March 1957. The purpose of the Detroit installation was 1) to serve as a pilot plant for evaluating the process on a commercial scale and 2) to produce marketable quantities of rock salt of improved quality and ap- pearance. The design of this plant was based on the results and information obtained from a 1-tph pilot plant at Battelle Memorial Institute. DESCRIPTION OF PLANT Location: The separation plant was installed underground near the crushing and screening plant, for this was the most suitable location from the standpoint of material handling. Furthermore, ample space was availabe at this location. Because the process requires a relatively constant temperature, the uniform year-around temperature of the mine (57°F) gave an added advantage to an underground operation. Feeding: The rock salt is conveyed to a surge bin, from which it is fed to the heating unit by a conveyor. The feed-rate control consists simply of an adjustable gate at the bottom of the surge bin. The plant may be fed either No. 1 grade of rock salt (0.279 to 0.375 in.) or No. 2 grade (0.375 to 0.500 in.) with a maximum input capacity of 500 tons per 15-hour day. Heating Unit: The heating unit (Fig. 2) consists of a panel of infrared lamps suspended inside a low-speed revolving screen. The radiant-heat panel, which is curved for most effective utilization of the heat, holds 240 infrared lamps of standard industrial type, each rated at 500 watts. The position of the panel is adjustable so that it can be placed centrally over and to within 6 in. of the salt bed on the screen. The entire heat panel is suspended by rollers in ¦ R. J. Brison and O. F. Tangel: Development of a Thermo-adhesive Method for Dry Separation of Minerals.

Jan 1, 1961

By C. A. Hartnagel

The year 1944 marks the eightieth anniversary of the discovery of petroleum by drilling in New York State. It was in 1864 that a half dozen shallow wells were drilled at Limestone in Cattaraugus County, in a region that now forms the northern extension of the 82,000-acre Bradford pool. These early wells found oil, but not in paying quantities. They did, however, attract attention to the district and were a factor in the development of the still active Bradford pool of Pennsylvania and New York. During 1943, the production of petroleum in New York amounted to 5,029,000 bbl. This represents a decrease over the previous year, in which 5,421,000 bbl. was produced. The flush production for the New York fields occurred in the early eighties shortly after the discovery of oil in the Richburg pool of Allegany County. During the flush period, production was in excess of five million barrels annually. By 1887, however, the output had decreased to an amount only slightly more than two million barrels, and through the early years of the present century the annual total was often less than one million barrels. Flooding of the oil sands for increasing productioil was made legal in 1919, and in 1927 the output once more reached the two million mark. Two years later it had increased to over three million barrels. In Table r is shown production since 1935, in which year for the first time the output under flooding methods was in excess of four million barrels. From this table, it is evident that oil production in New 'I'ork is rather well stabilized, and since most of the oil is obtained by the flooding, or water-drive, method, with little or no prospect of discovery of new oil territory, rapid changes in yield from year to year are not to be expected. In thickness, the oil sands have a maximum of about 50 ft., and by means oi flooding may produce 10 to 12 thousand barrels an acre and proportional amounts for thinner sands. In some cases, floods have been developed in sands only 12 ft. thick. Under good flooding conditions a yield of 2000 bbl. an acre is about the lower limit at which oil can bc produced at the present price of $3.00 a barrel. The average cost for the physical development ol a lease, not including the cost ol the lease itself, is $5000 an acre. Since several months must intervene before the flood begins to act on the oil wells, and a year or more is required to bring thc wells to maximum daily production, it is evident that a considerable interval occurs before maximum returns are realized. Once a flood is developed and the wells

Jan 1, 1944

By C. A. Hartnagel

The year 1944 marks the eightieth anniversary of the discovery of petroleum by drilling in New York State. It was in 1864 that a half dozen shallow wells were drilled at Limestone in Cattaraugus County, in a region that now forms the northern extension of the 82,000-acre Bradford pool. These early wells found oil, but not in paying quantities. They did, however, attract attention to the district and were a factor in the development of the still active Bradford pool of Pennsylvania and New York. During 1943, the production of petroleum in New York amounted to 5,029,000 bbl. This represents a decrease over the previous year, in which 5,421,000 bbl. was produced. The flush production for the New York fields occurred in the early eighties shortly after the discovery of oil in the Richburg pool of Allegany County. During the flush period, production was in excess of five million barrels annually. By 1887, however, the output had decreased to an amount only slightly more than two million barrels, and through the early years of the present century the annual total was often less than one million barrels. Flooding of the oil sands for increasing productioil was made legal in 1919, and in 1927 the output once more reached the two million mark. Two years later it had increased to over three million barrels. In Table r is shown production since 1935, in which year for the first time the output under flooding methods was in excess of four million barrels. From this table, it is evident that oil production in New 'I'ork is rather well stabilized, and since most of the oil is obtained by the flooding, or water-drive, method, with little or no prospect of discovery of new oil territory, rapid changes in yield from year to year are not to be expected. In thickness, the oil sands have a maximum of about 50 ft., and by means oi flooding may produce 10 to 12 thousand barrels an acre and proportional amounts for thinner sands. In some cases, floods have been developed in sands only 12 ft. thick. Under good flooding conditions a yield of 2000 bbl. an acre is about the lower limit at which oil can bc produced at the present price of $3.00 a barrel. The average cost for the physical development ol a lease, not including the cost ol the lease itself, is $5000 an acre. Since several months must intervene before the flood begins to act on the oil wells, and a year or more is required to bring thc wells to maximum daily production, it is evident that a considerable interval occurs before maximum returns are realized. Once a flood is developed and the wells

Jan 1, 1944

By AIME AIME

A DOCUMENT of progress and of great interest to engineers is the report of the Military Affairs Committee of 'the Engineering Council, which has just been accepted and sent to the secretary of War. It provides .a plan whereby civilian engineers holding commissions in the Reserve Corps may; with their con- sent, be called into service of the army during peace at any time, either with troops in the field or in a consulting capacity on any government engineering work. The Military Affairs Committee finds ample authority in the military bill passed by Congress on June 4, 1920, for this arrangement and also for extending the privilege to military engineer, officer-s of the regular army to engage in civilian work during times of peace. It is hoped that the Secretary of War will adopt the suggestions and put the program outlined into effect. This is a constructive piece of work comparable to the efforts of the military Committee before the war which developed so much in the way of preparedness, particularly in the program of military lectures which, held in the auditorium in the Engineering Societies Building, became so popular that each lecture had

Jan 1, 1920

By W. G. SWART

THE best estimate on reserves of iron ore in the Lake Superior district is that made, in 1920, by Mr. R. C. Allen, amounting to 2,947,225,000 tons of assured and probable ore. This includes direct- shipping or so-called merchantable ores, and those capable of beneficiation by demonstrated processes. De- ducting from this the 287,000,000 tons shipped since 1920, leaves a present reserve of approximately 2,500,- 000,000 tons, or; about 50 years' supply. The assured ore in this estimate is given as 1,560,500,000 tons, which checks Mr. Lake's estimate of 1,528,948,000 tons, or about 30 years' supply. This is not a long time in the life of the steel industry, and it can be readily appreciated that the matter is important enough to war- rant the attention it is beginning to receive. The first question that engages our attention is, What is merchantable ore? In 1902 the average of all Mesabi shipments was 56.07 per cent iron and 4.35 per cent silica. Twenty-five years later it had dropped to 51.99 per cent iron, with silica up to 7.92 per cent. It has remained around these figures for' ten or twelve years and, except for a probable rise in silica, can stay there for an indefinite period. Most of these figures I am giving cover the Mesabi Range. Including the other ranges does not change the figures greatly, and the Mesabi Range commands the situation, since it produces about 65 per cent of the total annual tonnage and, according to Mr. Allen, contains 81 per cent of the assured reserves, 50 per cent of the probable reserves, and 66 per cent of both the assured and the probable reserves.

Jan 1, 1926

By E. D. Gardner

AGAIN in 1945, the fourth year of World War 11, the American mining industry met the necessary demand made upon it for metals. Lack of labor prevented full production in some districts; maximum output, however, was maintained with the man power available. Development work and maintenance of mechanical equipment were neglected in favor of immediate production. Drafting of the younger men continued throughout the year, and the loss of personnel to war industries with higher wage rates continued up to "V-J" Day, Aug. 14. Labor shortages were more critical in 1945 than in 1944 though the man-power situation eased for some districts in the last quarter of the year. The trend in mining for the most part was to increase tons per man-shift by continued increased mechanization and refinements in methods and practices; larger equipment was installed where practicable. Labor shortages, together with the current higher wage rates, have advanced mechanization several years ahead of normal progress. The manpower shortage and the employment of inexperienced men had the effect of decreasing the average efficiency of the individual workman, but this condition was largely balanced by improved organization, greater efforts to improve labor relationship, and increased use of incentive pay systems. Safety instruction was emphasized, personnel contacts were increased, and more frequent foremen meetings were held to clarify contract agreements. Many of the large companies maintained schools to train green workmen.

Jan 1, 1946

Jan 1, 1884

By Garth M. Crosby

Hugh E. McKinstry (Professor of Geology, Laboratory of Mining Geology, Harvard University, Cambridge, Mass.) Pre-Cambrian age for the Coeur d'Alene mineralization, as indicated by isotope studies and recently discussed by Silverman, Long, and Kulp' would explain some features of the mineralogy of the district that have long been a puzzle. In the Silver Belt, especially in the Sunshine mine, lead-zinc min erali zation passes downward into tetrahedrite ore. Although commercially speaking this is a rich silver zone, the silver is, quantitatively, a mere impurity amounting to a small fraction of 1 pct. In effect the zonal change is from lead-zinc down into copper mineralization—-the usual zonal change that occurs in many districts. In the Burke-Mullan portion of the district, on the other hand, lead-zinc ore does not pass downward into copper mineralization of the Sunshine type. Instead, pyrrhotite appears in depth while the tenor in lead and zinc declines. The change occurs at increasingly greater depth away from the Gem stocks, deepening irregularly by some 3000 ft within two to four miles. As noted by Crosby, biotite, grunerite, and garnet appear in the deep zone. The marked difference between this apparent zonal change and the more nomal change to a copper zone is quite explainable if already existing pre-Cambrian veins have been locally metamorphosed by a Tertiary intrusive. The chief obstacle to this explanation is the evidence that mineralization cuts Laramide intrusives, but evidence on this point is conflicting as indicated by Crosby's observations and summary. This is not the first instance of a problem in determining the time-relationship of mineralization to a spatially associated intrusive. At the Noranda mine veins of chalcopyrite extend into a diabase dike which apparently cuts the ore, although Price2 concludes that the ore is later. However, at the Normetal mine diabase of a similar dike is thought3 to intrude the orebody but is cut by stringers of chalcopyrite. In the Sullivan Mine, B. C.,4 galena follows a fracture in a larnprophyre dike which, itself, cuts the main orebody. In the Sudbury district dikes of olivine diabase are clearly younger than the nickel ore, yet where they cut the Creighton orebody they contain stringers of chalcopyrite. In the laboratory, Hawley5 has developed veinlets of sulfide (chalcopyrite) it] silicate gangue by heating specimens of ore in a stream of H2S at 410 °C. From this and other evidernce. it seems clear that sulfides can be transferred from one site to another — at least through short distances — at temperatures well below their melting points. It would seem then that even if sulfide Mineralization in the Gem stocks can be shown unequ ivocably to be later than the intrusive the possibility of "remobiliza tion" need not be more than local. Thus the zonal relationships are quite in accord with a pre-Cambrian age for original deposition of the lead, zinc, copper, silver, and uranium in the Coeur d'Alene district. REFERENCES 1. A. Silverman, A. Long, and J. L. Kulp: Discussion of: The Gem Stocks and Adjacent Orebodies, Coeur d'Alene District, Idaho. Mining Engineering, May 1960, pp. 470-471; AME Trans., 1960, vol. 217, p. 117. 2. Peter Price: Geol. & O. D. at the Home Mine, Noranda, Quebec. Can. Inst. M & M Bull 263, 1934, p. 108; also,Trans. CIMM 1939, pp. 108-140. 3. w. L. Brown Nometal Mine in structural Geology of Canadian Ore Deposits, Montreal, 1948, p. 690. 4. C. O. Swanson and H. C. Gunning: Geology of the Sullivan Mine. Can. Inst. Mining & Met. Trans. vol. 48, 1945, p. 653. 5. J. E. Hawley: Heat Effects on Sulphides and Possible Applications. Univ. Toronto Studies, Geol. Ser. No. 46, 1941, p. 34.

Jan 1, 1961

By K. Tangri, M. Chaturvedi

On water-quenching from within the (a + ß) phase region Zr-2.5 Nb and Zr-2.5 Nb-0.5 Cu alloys can undergo w transfirmation. This transformation has been attributed to the enrichment of ß Zr phase, at the solution-treatment temperature, by the solute atoms. The ß—w transformation is accompanied by a hardening 01 the alloys and in the optimum condition w-bearing specimens of the ternary alloy are about 14 pct harder than those bearing only a' phase. On aging crl reverls thermally to more stable phases, which results in a considerable softening of the specirnens, as follows: w quenched -waged + ß Zr (enriched) waged - a + ß Nb The high-temperature bcc ß Zr in certain zirconium alloys can transform to a metastable w phase which has a primitive hexagonal structure. In the Zr-Nb alloy system w phase has been observed in the composition range of 7 to 15 wt pct Nb by a number of investigators.'-' In this composition range w can form by water-quenching ß Zr or by aging. known as athermal and thermal w, respectively. Hatt and Roberts' have found that thermal w has a constant c/a ratio of 0.622 +0.002 regardless of the composition and tha: the lattice parameters are of the order of a = 5.02A and c = 3.0 ?. The actual lattice parameters depend upon composition and the temperature of aging. The lattice constants of athermal w. however, depend upon alloy composition.3 The presence of w phase in zirconium alloys can cause substantial strengthening which has been attributed as probably due to the coherency between w and parent ß Zr phase. Robinson et al.' found that the presence of w can raise the strength of Zr-5.0 Nb-2.0 Sn and Zr-5.0 Mo-2.0 Sn alloys to about 170.000 psi: however. the ductility is considerably reduced. With the growing use of Zr-2.5 Nb and Zr-2.5 Nb-0.5 Cu alloys in the nuclear reactors, and the significant effect of w transformation on the mechanical properties of zirconium alloys studies were undertaken to study the w transformation in Zr-2.5 Nb and Zr-2.5 Nb-0.5 Cu alloys. This paper is concerned with the formation and reversion of w phase in these alloys. 1) MATERIALS AND EXPERIMENTAL TECHNIQUES The following two alloys were studied: 1) Zr-2.5 Nb-0.5 Cu (referred to as the ternary alloy): 2) Zr-2.5 Nb (referred to as the binary alloy). The chemical analysis of the alloys is given in Table I. The alloys, in the form of 3/8-in.-diam rods and 1/8-in.-thick sheets, were supplied by the Chalk River Nuclear Laboratories of the A.E.C.L. Initial fabrication for preparation of various specimens was carried out by cold rolling and swaging with intermediate anneals at 1000°C. All the heat treatments were carried out after the specimens were wrapped in zirconium foils and encapsulated in silica tubes under a vacuum of 5 x 10-% m of Hg. For optical metallography and hardness measurements disc specimens + in. diam by + in. thick were used. After the required heat treatments the specimens were mechanically and then chemically polished in a 45 pct HNO3, 45 pct H20. and 10 pct HF solution. The hardness measurements on the chemically polished specimens were carried out on a Vickers hardness tester using a 10-kg load. For each specimen at least fifteen indentations were made in order to obtain a representative hardness value. The phase identification and structural analysis were carried out using X-rays and electron diffraction techniques. Wires of 1.5 mm diam reduced to 0.12 mm diam by chemical etching were used for making Debye-Scherrer powder patterns using copper K-a radiations in 114.6-mm-diam camera. Thin films for transmission electron microscopy were prepared by electropolishing heat-treated a by 7 by 0.005-in.-thick strips using a modified Bollmann-Window technique. The 10 pct perchloric acid-90 pct methyl alcohol electropolishing bath was kepl at -5OCC and polishing was done at 5 to 10 v. The thinned specimens were washed in ethyl alcohol at -30" to -40°C and dried between filter papers. The thin films

Jan 1, 1970

By B. W. Levinger

THE system Ti-CI- has been studied by several investigators." ' Though titanium and chromium are completely miscible at high temperatures, an intermediate phase of the approximate atomic proportions TiCr, has been identified at various compositions between 60 and 68 wt pct Cr. The structure of this phase was established as the cubic C15 (MgCu2) type with 24 atoms per unit cell and a lattice parameter 6.929 kX.2 During a study of the ternary system, Ti-Mo-Cr,5 the existence of a high temperature modification of the TiCr, phase was discovered. In a series of alloys annealed at 1300°C and containing from 60 to 70 wt pct Cr and 5 pct Mo, a new phase was present which did not correspond to either ß solid solution or TiCr,. By trial, the new phase was identified to be of the hexagonal C14 (MgZn2) structure with 12 atoms per unit cell. Further work showed that the hexagonal structure was. in fact, also present in binary Ti-Cr alloys quenched from high temperatures. To make the identification more certain, the intensities of the various reflections were calculated assuming a composition TiCr2 and C14 structure. Table I lists reflection planes, interplanar distances, calculated intensities, and a comparison of these values with the lines of a binary Ti-Cr alloy (66 pct Cr) annealed for 20 min at 1385°C and water quenched. Since high angle lines were more diffuse, the correspondence between visually observed and calculated intensities was not as good at these angles. Lattice parameters were computed to be a = 4.922 kX, c = 7.945, c/a :- 1.614. The corresponding interatomic distances are: titanium to titanium distance, 3.00:, kx, chromium to chromium distance, 2.43, kX, titanium to chromium distance, 2.88,, kX. These compare to 3.00, 2.45, and 2.87 kX in the cubic phase, respectively.' The atomic positions in the C14 structure are as follows: Titanium 1/3, 2/3, Z; 1/3, 2/3, 1/2: 2/3, 1/3, i; 2/3, 1/3, (1/2-z); Chromium 0, 0, 0: 0, 0, 1/2; 2x, 2, 1/4; 232, x, %; X, 22, 1/4; X, 2x, 3/4; x. x, 1/4; x, x, 3/4; The values of x and z were calculated for the alloy mentioned and found as follows: z — 0.061, x = 0.165. The values assumed in the intensity calculations were those for an ideal close-packed lattice or z = 1/16, x = 1/6. Work in the Ti-Mo-Cr system indicates that y2 the hexagonal modification of TiCr2, is the stable phase above 1300°C, while y1 with the cubic structure is stable below 1000°C. X-ray examination of a number of alloys annealed at intermediate temperatures showed that the hexagonal and cubic phases can coexist. Alloys quenched from 1000°C and annealed at 1100" and 1200°C showed small amounts of y2 at the higher temperature. A considerable amount of y, seemed present, however, in cast alloys annealed at 1100°C. It further appears that there is a small but definite solubility range for both phases in the ternary system. Acknowledgment The results of this paper represent work carried out in conjunction with a project sponsored by Watertown Arsenal, Contract No. DA-11-022-ORD-272. References 'M. K. McQuillan: Journal Inst. Metals (1951) 79, p. 379. 2 P. Duwez and J. L. Taylor: Trans. ASM (1952) 44, p. 495. W. J. Van Thyne,. H.. D. Kessler, and M. Hansen: Trans. ASM (1952) 44, p. 974. 1 F. B. Cuff, N. J. Grant, and C. F. Floe: Trans. AIME (1952) 194, p. 848; Journal of Metals (August 1952). Unpublished Research, Armour Research Foundation. "H. J. Wallbaum: Ztsch. Krist. 103, p. 391.

Jan 1, 1954

By E. D. Gardner

IN 1947 the metal-mining industry . passed through a year of readjustment; catching up on development work has caused production to suffer. Skilled labor has been short in most mining districts, notwithstanding the highest wage rate paid in the history of the industry. The trend has continued toward increased mechanization and refinements in practices and methods to increase the tons produced per man-shift. Improvements in procedures, however, have not kept pace with rising labor rates; and, in general, labor costs per ton mined have steadily increased since the war years. Prices of base metals have been the highest in a generation, but most producing companies can afford to pay the high wages. Capital expenditures have been approved for improvements to increase the output per man, both to reduce unit labor costs and to increase output. Surveys indicate a continuing

Jan 1, 1948

By William H. Baer, George M. Carlton, Blake M. Loring

IT is a well known fact that age-hardening alloys remain in a supersaturated, or partially supersaturated, condition only for limited periods of time at temperatures below the solvus. In order to develop optimum properties by subjecting the quenched alloy to precipitation or age-hardening treatment at a specified temperature, it is necessary that the cooling rate be sufficiently high to maintain the required degree of supersaturation of the solid solution. In practical applications the size and shape of the specimens obviously have considerable influence on the rate of cooling and there is need for more information on the effects of various rates of cooling. Cooling rates of quenched aluminum alloys generally have been established by the type of quenching medium, the temperature of the medium and the dimensions of the specimen.1,2,3 Except for the work of Roth3 little quantitative information is available on the measurement of cooling rates of aluminum alloys and the significance of the influence of various cooling rates upon the mechanical properties. The purpose of the present investigation was to study the use of the Jominy test for aluminum alloys (Table I). EXPERIMENTAL PROCEDURE The material for this investigation consisted of extruded rods 1 ¼ to 1 ½ in. in diam. The chemical compositions were as follows: [ ] The modified L-type Jominy specimen with dimensions shown in Fig I was selected as the most convenient means for obtaining a wide range of cooling rates. The standard Jominy specimen was not satisfactory because its cooling rate was not sufficiently high. The four flat surfaces machined at right angles along the length of the L-type specimen to a depth of 0-015 in. facilitated the hardness measurements. The specimens were machined from the extruded stock with no intermediate forging. New specimens were used for each aging experiment. The specimens were given solution treatments of 2 hr duration at recommended temperatures in a Hoskins furnace (Table 2). The temperature of the furnace was maintained constant to ±3°C. No protective atmosphere was necessary because the thin film of oxide that formed on the surface of the specimens had no effect on the hardness measurements.

Jan 1, 1948

By Robert T. DeGavre

INTRODUCTION The $645 million financing for Inco Ltd's Soroako nickel project in Indonesia not only represents a significant human achievement but also there are certain important lessons that can be derived from Inco's experience in financing the project. The paper will not present a technical assessment of the project since Inco Ltd. submitted a series of papers on this subject at the international Laterite Symposium as part of the 108th Annual Meeting of the AIME in February 1979. BRIEF HISTORY OF THE SOROAKO PROJECT Table 1 summarizes the milestones achieved in the Soroako project and its financing. Exploration Phase A contract of Work was signed on July 27, 1968 by the Republic of Indonesia and F.T. International Nickel Indonesia (P.T. Inco) covering an extensive area of over 25,000 square miles on the two southeastern arms of the island of Sulawesi. The Contract provides that P.T. Inco has the sole responsibility for financing the project and determining the terms on which the financing should be obtained, that P.T. Inco has the right to receive and hold outside of Indonesia foreign exchange revenues and to freely dispose of such revenues, and that Indonesians have the right to purchase up to 20% of the equity of P.T. Inco over a period following start of production. P.T. Inco began field investigations in the Contract Area in August 1968. Preliminary reconnaissance sampling with portable drills broadly outlined areas of favorable laterite terrain which were then systematically sampled on surveyed grids. By early 1971 sufficient exploration work had been completed to indicate that the laterite deposits near Soroako could sustain a major nickel-producing plant (figure 1). Pilot plant studies in 1970 and 1971 at Inco's research station in Port Colborne, Ontario, using two bulk samples of Soroako ore material, also confirmed that the ore could be upgraded and treated for the recovery of its metal values. Feasibility Phase Encouraged by the results of its exploration program and pilot-plant work, Inco Ltd. commissioned Toyo Engineering Company of Japan in August 1971 to prepare a capital cost estimate for a relatively small nickel project called "Stage I". Stage I was to be a single-line pyrometallurqical process plant with an annual capacity of approximately 15,000 metric tons of nickel contained in 75% nickel sulphide matte (see Figure 2). Electric power was to be supplied by a thermal power station. It is important to recognize that Inco's strategy was to develop the Soroako ore deposits in several stages: first, construct a small project to gain experience and to reduce the initial capital outlay and then later expand in one or more steps to a much larger project to achieve maximum economies. The strategy reflected both Inco's financial position in 1971 as its sales and earning dropped sharply and the difficulties previously experienced by Inco in trying to launch in the late 1960's very large "greenfield" nickel projects in New Caledonia and Guatemala. Toyo's Project Development Study was completed. in January 1972. Based upon Toyo's cost estimate for physical facilities, Inco estimated the total capital cost of Stage I to be $115 million. For the next several months, Inco ran numerous in-house financial feasibility studies, using as inputs Toyo's cost estimate and the results of its exploration and pilot plant programs. In September 1972, Inco completed a project feasibility study which was based upon a capital cost estimate of $135 million. The feasibility study was immediately made available to potential partners and lenders. Partner Negotiations The Japanese nickel market had from the outset been central to Inco's planning for the Soroako project. That market had been growing dramatically at rates in excess of 20% per annum during the 1950's and 1960's. Japan had established, for rational security and other reasons, a domestic

Jan 1, 1985

By W. H. Corbould

The township of Cloncurry is situated in the northwestern part of Queensland, about latitude S. 20" 42' 53" and longitude E. 140" 30' 25". Townsville is the port through which all the trade passes and is about 470 miles east-northeast of Cloncurry township. The Cloncurry copper district covers an area about 200 miles long by 40 miles wide. Unfortunately the mines are very scattered over this area, there being no large groups of mines. Mount Elliott mine is situated about 70 miles south from the township of Cloncurry, and Mount Oxide mine about 150 miles north of Cloncurry. The district has been known for the last 35 years, and in the early stages a large amount of capital was expended with little to show for it; but within the last four years the railway has been extended from Townsville to Mount Elliott and about 40 miles north of Cloncurry, which has made possible the treatment of the ores of the mines on this extension. The Mount Elliott company within the last few years has smelted and converted on its mine 169,688 tons of ore for 20,554 tons of blister copper, containing 20,377 tons of copper, 35,642 oz. of gold and 28,841 oz. of silver, at a cost of about 233 per ton of blister copper, f.o.b. Townsville. This cost included all development, wages, salaries, general management, office, agency, legal expenses, freight, etc. The gold and silver contents would practically pay for freight to Europe, refining, realization charges, etc. The costs of supplies are as follows: Firewood, 15s., coke, 75s., mine timber, 54s., and coal, 60s. per long ton; explosives: dynamite and gelignite, 50s., and blasting gelatine, 65s. 6d. per case, Mount Elliott Mine The pay shoot of the orebody outcrops at the surface for about 200 ft., and lies between two slate walls about 40 ft. apart., having a general

Jan 1, 1915

By M. S. Burton, J. E. Ritter

The sessile-drop technique was employed to study the effect of atmosphere and alloy additions of titanium and chromium on the surface tension and contact angle of nickel on sapphire substrates at 1500oC. Shear tests were conducted on the solidified sessile drops. The liquid-gas surface tension of pure nickel on sapphire was found to be 1747 ergs per sq cm, with a contact angle of 109.6 deg. The surface tension and contact angle were not affected significantly by the four atmospheres, vacuum, impure argon, pure argon, and pure hydrogen. Small additions of titanium and chromium decreased the contact angle and for the same alloy content, contact angles were lower in pure argon than in pure hydrogen. On the basis of shear-test results , the most probable cause for adhesion in the Ni-Al2O system is the formation of NiO:Al2O3 spinel at the interface; in the titanium alloy-Al2O3 system adhesion is thought to be due to a mechanical interlocking effect; in the chromium alloy-Al2O3 system adhesion is believed to be the result of solid-solution formation involving Cr2O3 and Al2O3 at the interface. In the last few years there has been considerable interest in reinforcing metals with ceramic whiskers. It has been postulated that, by reinforcing nickel with sapphire whiskers, high-temperature strengths su- perior to those of the best current nickel alloys can be achieved.' To fabricate a whisker-metal composite having optimum density and strength, understanding of wettability and adherence in the system is of prime importance. Although there has been some previous research in this a a need for further studies has been cited4-8 to understand better the effects of impurities, alloys additions, and atmosphere on the wetting and bonding of metals to metal oxides. The purpose of this research was to investigate the factors involved in the wetting and adherence of nickel/nickel alloys to sapphire (single-crystal a Al2O3). Sessile-drop experiments were conducted in vacuum, impure argon, pure argon, and pure hydrogen, to determine the effect of atmosphere on the contact angle of the metals on sapphire, and the liquid-gas surface tension of pure nickel. The solidified sessile drops were sheared from the sapphire substrate to measure the bond strength between the metal and ceramic. The alloy additions chosen were titanium and chromium since both enhance the wetting of nickel on sapphire.2, 3c Also, titanium is commonly used when brazing metal-to-ceramic seals to improve adherence. Since chromium forms an oxide that is completely soluble in sapphire, it was thought that the oxide could serve as a transition phase to promote bonding between the Ni-Cr alloy and sapphire. I) EXPERIMENTAL APPARATUS AND PROCEDURE The sessile-drop apparatus was a horizontal furnace, with an induction-heated, cylindrical molybdenum susceptor in a water-cooled Pyrex chamber. This apparatus was patterned after that of Williams and Nielsen.7 A flat Pyrex window at each end of the furnace allowed temperature measurements to be made at one

Jan 1, 1968

By AIME AIME

APROXIMATELY one third of the world's iron ore is mined in the United States; and about 80 per cent of this third is mined in the Lake Superior ore region, and about 60 per cent in Minnesota. The Lake Superior iron ore region covers a vast area in the vicinity of Lake Superior that contained in early geological times large areas of iron-bearing sediments, which today form metamorphosed iron-bearing rocks, such as jasper, chert, taconite, and slates. Concentration of the iron content chiefly through solution and resultant removal of silica produced the ore bodies we find today in rock folds as on the Menominee range, at dike or impervious wall intersections such as on the Gogebic range, and blanket-type enriched ore bodies ly¬ing on or within the ore formation, such as occur on the Mesabi and in steeply pitching ore lenses elsewhere. In many places, folding and subsequent erosion of the tops of the folded areas has resulted in steep dips in the ore formation and contained ore bodies. The upper eroded edges are mostly buried under glacial over-burden. The slightly dipping Mesabi formation is the principal exception as to steeply dipping ore bodies.

Jan 1, 1941

By Alexander R. Troiano, Taylor Lyman

Studies of the transformation of aus-tenite at constant subcritical temperatures have been numerous since the work of Davenport and Rain.' Considerable information has been obtained on low-alloy steels and on high-carbon alloys containing undissolved carbide or graphite at the austenitizing temperature. Little is known of the isothermal transformation of aus-tenite containing in solution large amounts of both carbon and a single alloying element. In this investigation four steels containing one per cent carbon and with chromium in the range 3 to 9 per cent have been examined with the view to establishing the fundamental character of the isothermal reactions when all carbon and chromium are initially in solution in austenite. Experimental Procedure Alloys The chemical compositions of the steels investigated are given in Table I. The 4 per cent Cr alloy is a commercial steel. The other steels were made by the Carpenter Steel Co. as 50-lb., induction-furnace heats and rolled to 5/8 -in. round bars. Bars were softened at 650' to 700°C. before the specimens were cut. Most of the lines on the transformation diagrams presented here have been placed on the basis of the microscopic examinatioll of partially reacted specimens, Thees specimens were approximately 1/2 by 1/4 by 1/8 in. ill size, specimens of the 9 per cent cr steel were held 10 to 12 hr, at 1200°to 1225°C. before quenching to the various subcritical temperatures. The other steels were held for 2 to 2 1/2 hr. at 12ooOC. before quenching. These treatments, carried out in an atmosphere of purified nitrogen, produced an austenite grain size larger than A.S.T.M. So. I, some grains being 1 to 2 mm. in diameter. There were a few undissolved carbide particles in some specimens of the 9 per cent Cr steel. It is believed, however, that any errors in the results due to incomplete solution of carbon and chromium in austenite are negligible; that is, austenite compositions may be considered as being those listed ill Table I. X-ray Methods Constituents were identified and mar-tensite axial ratios determined from Debye

Jan 1, 1945