Search Documents

By T. P. Papazoglou, N. A. D. Parlee, W. C. Phelps

HE high vapor pressures of metals such as lead, calcium, lithium, bismuth, and magnesium at steel-making temperatures present experimental problems which have thus far rendered it almost impossible to obtain really reliable data for their solubilities in liquid iron. Many investigators have attempted to equilibrate liquid iron in the same crucible with the undissolved liquid phase of such volatile metals. The published results,l-6 although useful, are often questionable on the grounds of not being obtained under true equilibrium conditions. Such information is not always of practical value in any case since the equilibrium vapor pressure is often several atmospheres and steel is not currently made at these pressures. Solubility measurements at lower partial pressures (< 1 atm) appeared to be more practical and easier to make. These data could be used to calculate solubilities at other pressures where Henry&apos;s Law is obeyed, and to estimate solubilities under other conditions of temperature and pressure with useful accuracy. This note outlines the development of a general technique for the measurement of solubilities in systems of this kind. The method involves equilibration of the high-boiling metal at known temperatures with the vapors of a low-boiling metal at known partial pressures. Analyses of quenched samples provide vapor pressure-solubility data and make calculations of alloy thermodynamics possible. The principle involved is similar to the closed-system diffusion-transport method which is difficult to apply with most high-melting liquid metals like iron, due to closure problems. A two-zone horizontal (molybdenum wire element) tube furnace, Fig. 1, provides two constant-temperature zones in a reaction tuve (3/4 in. ID by 1 in. OD by 36 in.). A high-boiling metal sample, 9, introduced in the higher-temperature zone, is maintained at temperature T1, and a volatile metal sample, 7, in the lower-temperature zone, is held at T2. A stream of argon with 10 pct hydrogen is passed via flowmeters, 1, and mixing-drying towers, 2 and 3. through the reaction tube at a favorable flowrate and acts as a carrier gas which entrains vapor from the volatile liquid metal at a specific constant partial pressure. The gas mixture passes through a system of constrictions, 6 and 8, to the higher-temperature zone, establishes intimate contact with the high-boiling liquid sample, 9, and exits through a small condenser tube. The entire system is at (nearly) atmospheric pressure and the volume of carrier gas passed is measured with a wet gas meter. When the high-boiling sample attains equilibrium with the vapor phase, both samples are removed and quenched. Analysis of the high-boiling sample for solute content reveals its solubility for the low-boiling metal at a vapor pressure calculated from carrier-gas volume and either a) weight loss of volatile metal or 6) weight gain of high-boiling sample plus condenser (which collects the undissolved vapors). To test the capabilities of the method, liquid silver at 1403&apos;C was equilibrated with lead vapor at various partial pressures. The relatively simple Pb-Ag system was particularly suitable for uncovering experimental problems and providing the first step toward investigations with more volatile metals and more difficult combinations.

Jan 1, 1965

By H. Papazian, Robert A. Lad

SINCE it can be shown both theoretically&apos;&apos; : and experimentally that disordered Cu3Au has a greater internal energy than the ordered alloy, it might be expected that its chemical reactivity would be greater. Experiments were initiated&apos; to test this hypothesis. This note will describe some recent results obtained in the study of the rates of corrosion of ordered and disordered polycrystalline Cu3Au by aqueous FeCl., The work of Robertson&apos; has indicated that the attack by such solutions is intergran-ular and highly orientation dependent. It was of interest to see whether the order-disorder effect was great enough to overcome the variations from specimen to specimen which would arise from this type of attack. The polycrystalline alloy specimens (0.020 in. wire, 1¾ in. long) were preannealed in ½ atm H, at 700°C for 2 hr. The subsequent heat treatments to produce order and disorder were performed in M atm He. Disordered specimens were obtained by heating at 450°C for 2 hr and quenching in water. Ordered specimens were produced by heating for 2 hr at 450°, furnace cooling to 380°, and soaking at 380°C for 80 to 90 hr. Room temperature was reached by cooling to 150" at a rate never exceeding 7" per hr, and water quenching from 150°C. The specimens so produced exhibited electrical resistivities characteristic of the two states; of the order of 11.27x10 ohm-cm for the disordered, and 4.28x10 ohm-cm for the ordered specimens. The corrosion rates were studied at 30°C in ferric chloride solutions of several concentrations (?,¼, 1.5, and 1 molar). The specimens were attached to a stirrer during the tests. Tests were interrupted at intervals, and the specimen weight change was determined after washing and drying. Analysis of the solutions showed that the attack was limited to the copper. The higher corrosion rate for the disordered alloy, as illustrated in Fig. l, is typical of the results obtained. The effect of variation in ferric chloride concentrations is indicated in Table I for typical specimens. The variations in the ratio of reactivity for disordered and ordered specimens at the different concentrations are within experimental error, and the best value is estimated to be near 1.4. The experimental variation was due in part to the mode of attack, as mentioned, and in part to the fact that films were formed on the specimens under some conditions. Electron diffraction patterns of the films were very complex and indicated the presence of metallic iron, as did chemical analysis. In an attempt to eliminate the difficulties arising from the mechanism of attack, single crystal specimens were used. A greater reaction rate was again measured for the disordered specimens, but the reproduci-bility was no better than that for the polycrystalline metal. This would indicate that film formation was primarily responsible. It was concluded that the reaction with aqueous ferric chloride served to demonstrate that the reactivity of disordered Cu3Au is greater than that of the ordered alloy. However, the difficulties with film formation did not permit determinations of a precision great enough to warrant extension of the study to partially ordered alloy systems.

Jan 1, 1957

By A. C. Losekamp, R. M. Fincel, J. B. Conway

TANTALUM like several other metals exhibits a great affinity for or reactivity with certain gases. Tested in atmospheres which are not completely pure this metal becomes contaminated by certain impurities (notably nitrogen, oxygen, and hydrogen) with a resultant change in various properties. Well-known are the drastic changes in hardness, ductility, and electrical resistivity. Also previously recorded are the distortions of the lattice1,2 accompanying the increased content of oxygen and nitrogen in tantalum. This pronounced affinity for certain gases along with the significant property variations thereby produced makes it necessary to observe additional experimental precautions in making various property determinations with tantalum. Some recent measurements of the linear thermal-expansion characteristics of tantalum have made this point quite emphatically. Failure to observe the greatest precautions in reducing the contaminating influence has led to some extremely distorted results. Not only does such operation lead to different heating and cooling curves during the thermal-expansion measurements, but upon cooling to room temperature the sample is found to have suffered a permanent (actually semipermanent since the specimen can be returned to its original length by a 3-hr degassing treatment in vacuum at 2300°C) elongation. In addition, subsequent heatings will not follow the initial heating curve unless the expansion measurements are based on the actual specimen length at the beginning of the heating cycle. These thermal-expansion measurements were made by positioning the specimen horizontally at the longitudinal midpoint of a 20-in.-long, 4-in.-diam resistively heated tungsten tube furnace. The specimens were in the form of 20-mil sheet formed into a sharp U-shape about 0.3 in. in width and 0.3 in. in depth. Fiducial marks in the form of 0.010-in. holes drilled at either end of the 2.5-in.-long sheet specimens were viewed by a paired filar micrometer telescope system mounted on an Invar bar on the top of the furnace. Tests were made in helium with temperatures measured by a Pt/Pt-lORh thermocouple to 1000°C; above 1000°C temperature was measured by means of an optical pyrometer sighted into a black-body hole drilled into the specimen-holding fixture in the vicinity of the specimen. Previous tests with black-body holes drilled in a 0.25-in.-diam rod specimen had confirmed the temperature uniformity between specimens and specimen-holding fixture in this furnace. A typical thermal-expansion curve for arc-cast tantalum in helium is shown in Fig. 1 for the case where no attempt is made to remove all the impurities from the cover-gas atmosphere. The initial heating curve appears smooth and has a shape characteristic of all metals. However, it is known that the sample begins absorbing impurities at temperatures above 1000°C which are sufficient to distort the lattice and lead to specimen lengths which are somewhat larger than would be obtained in the absence of contamination. During the cooling cycle the expansion curve is seen to be significantly different from the heating curve. This is due to the impurity content causing a semipermanent (i.e., permanent until the impurities are removed by vacuum degassing) deformation which will not allow the speci-

Jan 1, 1965

By P. A. Beck, A. Merlini

Quantitative texture determinations were made for rolled and for rolled and annealed strips of 3, 6, and 10 pct Zn brasses. The main components of the rolling texture gradually shift over a wide composition range from the orientation characteristic of copper to that of 70-30 brass. At least the main features of the corresponding gradual changes in the annealing texture may be accounted for qualitatively on the basis of the oriented growth theory of annealing textures. All the oriented nucleation-type theories are notably less successful in accounting for the observed textures. EARLIER investigations by von Goeler and Sachs,&apos; Dahl and Pawlek,&apos; and Brick, Martin, and Angier" suggested that the annealing texture of copper is more sensitive to the addition of solute elements than the rolling texture. It was reported3 that the cube texture changes over into a brass-type recrys-tallization texture on addition of about 1 pct Zn, while the deformation texture changes only at about 5 pct Zn. Such behavior would be difficult to reconcile with any theory of annealing texture formation that relates the annealing texture to the deformation texture. In particular, the oriented growth theory of the cube texture" is based on a certain orientation relationship between the cube texture and the main components of the deformation texture which could not be reconciled with the reported behavior of low brasses. It was, therefore, of interest to re-examine these textures by means of the quantitative methods now available. The deformation and annealing textures of rolled a brasses with approximately 3, 6, and 10 pct Zn have been determined in terms of (111) and (200) pole figures. Experimental Methods The chemical analyses of the Cu-Zn alloys of commercial purity used in the present work are given in Table I. Chill-cast bars of the tabulated compositions were rolled and annealed according to the following schedule: I—rolling from 1.2 to 1.02 in. thickness, 15 pct reduction area, annealing 15 min at 450°C; 2— rolling from 1.02 to 0.867 in. thickness, 15 pct reduction area, annealing 15 min at 450°C; 3—rolling from 0.867 to 0.600 in. thickness, 31 pct reduction area, annealing 2 hr at 540°C; 4—rolling from 0.600 to 0.400 in. thickness, 33 pct reduction area, annealing 2 hr at 480°C. In the final straight rolling of 96.25 pct reduction area, the strips were reversed end to end after each pass. The final annealing temperature was determined for each alloy by annealing specimens of the cold-rolled strips in salt bath for 5 min at varying temperatures. The results of the hardness measurements are given in Fig. 1, where the final annealing temperature used for each alloy in determining the annealing texture is indicated by a cross.

Jan 1, 1956

By P. G. Shewmon, F. N. Rhines

THE determination of the self-diffusion coefficient of magnesium has been made possible recently by discovery1-1 of a radioactive isotope, Mg28 having a half-life of 21.3 hr,1 and subject to manufacture in useful quantity. In the present research this material was condensed from the vapor phase upon a surface of high purity magnesium. The progress of diffusion of the tracer atoms into polycrystalline magnesium was followed by machining layers and measuring the change in the intensity of radiation as a function of the distance of each layer from the surface. The self-diffusion coefficient was found to be 2.1 X 10-8 sq cm per sec at 627°C, 3.6 X 10-9 sq cm per sec at 551°C, and 4.4 X 10-10sq cm per sec at 468°C; the activation energy is about 32,000 cal per mol. Experimental Procedure Since there was no other published measurement of a diffusion velocity in any magnesium-base material, is was necessary to employ a number of new experimental techniques. The short half-life of Mg28 made it necessary to complete the entire experimental procedure within three or four days. This meant that the work had to be done where a cyclotron was readily accessible and that all operations, prior to the diffusion heat treatment, had to be so designed as to minimize their time requirements. Unusual problems were imposed also by the chemical reactivity of magnesium, its high vapor pressure, and the fact that no satisfactory method for elec-trodepositing magnesium on magnesium is presently available. Finally, the machining and handling of the easily air-borne radioactive-magnesium chips involved certain health hazards, resulting in the need for further experimental restrictions. Preparation of Mg28 The Mg28 was produced in the Carnegie Institute of Technology syncrocyclotron by the neutron spallation of chlorine.5 his involved bombarding a 2 gram crystal of high purity NaCl with a beam of 350 mev protons for a period of 2 hr, after which the crystal was dissolved in warm water and the Mg28 was concentrated and purified by chemical means (see Appendix). About 50 microcuries of Mg28 thus were obtained in the form of magnesium oxinate (8 hydroxyquin-olatc?), which was ignited in air to produce MgO. This in turn was reduced to magnesium metal vapor, by the method of Russell, Taylor, and Cooper," in the vacuum apparatus shown schematically in Fig. 1. Here the essential part is a tantalum ribbon, slightly dished to receive the MgO. The ribbon, pre- viously outgassed at high temperature, is heated to about 1700°C by passing an electric current through it, whereupon tantalum oxide is formed, magnesium vapor is released almost instantaneously, and condensed partly upon the diffusion sample. Diffusion-Sample Preparation: Hot-extruded magnesium rod, 21/32 in. round was used in making the diffusion specimens. The magnesium analyzed as follows: 0.004 pct Al, 0.027 pct Fe, 0.040 pct Mn, 0.0004 pct Cu, 0.0002 pct Ni, and less than 0.01 pct Ca, 0.0004 pct Pb, 0.0011 pct Si, 0.001 pct Sn, and 0.001 pct Zn. A brief study of the crystal texture of this material revealed a sharp fiber texture with the (001) plane roughly parallel to the extrusion axis. Cylindrical samples 1/2 in. long by 5/8 in. were machined from this rod, the end faces dressed on 3/0 emery, and lightly etched with 20 pct HC1 in water. These samples then were annealed for at least twice the intended time of diffusion, at the intended diffusion temperature, in order to stabilize the grain structure at about 1 mm average diameter. The annealing treatments were conducted in argon in the same apparatus and in the same manner as the subsequent diffusion treatments, which will be described presently. Thus, a strain-free plane surface was produced, but there remained a layer of MgO which had largely to be removed before the layer of Mg28 was deposited. Most of this layer was taken off by two light passes over 3/0 emery paper. The balance of the oxide and a thin layer of metal were then removed by etching 5 to 10 min in 4 pct nital (4 pct HNO3 and 96 pct ethyl alcohol) made with absolute alcohol. There followed immediately three quick rinses in: 1-49 1/2 pct methanol, 49 1/2 pct acetone, and 1 pct formic acid, 2-50 pct methanol and 50 pct acetone, and 3-pure benzene. This procedure is essentially that of Sturkey.7 The resulting surface, which was of almost elec-tropolished brightness, remained plane and was free of cold work. It could be kept clean by storing under benzene, or in a desiccator; short exposure

Jan 1, 1955

By Edgar L. Newhouse

The lead smeltery at East Helena, Mont., controlled by the American Smelting & Refining Co. since 1899, has been in continuous operation for the past 25 years. Most of the old smelting and roasting practices have been superseded by newer and more modern methods, but on account of the difficulties involved in changing the original construction, some of the methods in use of handling materials are not the most modern. This plant, however, is particularly interesting as being one of the few essentially lead smelteries in the United States. At Federal, Ill., Collins-ville, Herculaneum, and possibly other places, similar work is being done, but it is doubtful whether any of them produces as much lead as the East Helena plant, whose monthly production averages 6,500 tons. The situation, 5 miles east of Helena, is convenient to both the Great Northern and Northern Pacific railroads, while the electric power is obtained from Canyon Ferry, 12 miles east on the Missouri river. Local quarries supply the requisite amount of lime rock, which the contracts require to be crushed to 5 in. Of the 450 men on the monthly pay roll, a census showed 200 Austrians, 110 Americans, and 30 Italians, the balance being made up of miscellaneous nationalities. The ore supply is mainly derived from the Coeur d&apos;Alene mines in Idaho, and consists of crude ore, coarse and fine concentrates, middlings, and slimes. About one-half of the total output of the Coeur d&apos;Alene camp is sent to East Helena. An average analysis of these ores gives approximately 40 per cent. lead and 11 per cent. sulphur. Local shipments, varying from month to month, are mostly highly siliceous gold and silver ores carrying little lead. Small shippers, leasers of old mines, and prospectors are very numerous throughout Montana, and it is the policy of the company to encourage these men by every possible means, including the free sampling and analysis of their ores and aid in the development of their mines and prospects, whenever their results show promise.

Jan 1, 1915

By S. R. Goodman, Hsun Hu

The rolling texture transition in copper as a function of deformation temperature is found to be quite similar to that in high-purity silver. The ordinary copper type texture changes gradually to the brass type, accompanied by an increase in the stacking fault frequency, as the temperature of deformation decreases. The rolling textures obtained at low temperatures and the corresponding annealing textures compare remarkably well with the ordinary rolling and annealing textures of low-zinc brasses. Furthermore, it is also found that the observed stacking fault energies of copper specimens deformed at low temperatures correspond closely with those of low-zinc brasses, as deduced from measurements of the dislocation nodes. These results are consistent with the idea that texture transition may be significantly dependent on the stacking fault energy. It was shown in a series of previous publications1"3 that the rolling texture of high-purity silver changes gradually from the common silver type (or the brass type) to the copper type* with increasing temperature *The silver or brass type rolling textures are commonly described as (110)[112],4,5 whereas the copper type rolling textures are mainly (123) [a121 and (146)[211].5 Other ideal orientations have been used by various investigators for the copper type rolling textures, but the actual difference among these ideal orientations is rather small. of deformation, and that such texture transition can be correlated with the change in stacking fault frequency as a function of rolling temperature. Furthermore, it was shown that the formation of annealing textures in high-purity silver from the various rolling textures obtained during the course of texture transition depends entirely upon the deformation texture. From a common silver type or brass type rolling texture (such as produced by rolling at 0" or at 50° C) the recrystallization texture is mainly (120)[211], which is quite different from the recrystallization texture of brass.* However, for both ma- terials the orientation relationship between the rolling texture and the recrystallization texture can be expressed in terms of similar rotations around [Ill.] axes of approximately 30 or 35 deg. They differ in that the [Ill] rotational axes are different. In the case of high-purity silver, the axes of rotation are the two (111) poles near the plane normal of the deformed specimen with a (11l)[112] type rolling texture, whereas in brass, they are the (111) poles near the direction of rolling. For high-purity silver with a predominantly copper type rolling texture (such as produced by rolling at 150° or 200°C) the recrystallization texture is mainly (100)[001], or the cube texture, plus its twin orientations. It was shown previously6 that such reorientation observed in copper or aluminum can be described as [Ill] rotations of 30 to 40 deg. For intermediate cases, i.e., when the rolling textures are composed of a

Jan 1, 1963

By Henry W. Brandt

In a proposal submitted by Fenix & Scisson International, Inc., of Tulsa, Okla., conversion of an abandoned mine for underground storage of crude oil proved to be all effective storage technique. The conversion was done on an abandoned coal mine for S. F. F. Association, an agent of the South African Government, Johannesburg, South Africa. The mine was found to be structurally stable and appeared capable of retaining this stability over a long period. Surrounding formations were relatively free of fractures and were found to have low permeability. Slight problems appeared in the hydrostatic test, but were quickly stabilized. Additional information was positive, and conversion and filling were completed in 1969. Total puchasing, testing, and coverting cost was less than $0.20 per barrel of oil stored or 15% of conventional steel tank cost. Operating and maintenance costs are about 2% of those at two large tank farms owned and operated by the Association.

Jan 1, 1975

By J. T. Norton, J. G. McMullin

An 1820°C isothermal cross section of the Ti-Ta-C ternary diagram was prepared from X-ray diffraction and metallographic data. No phases other than those appearing in the three binary diagrams were observed. At temperatures above the titanium transition temperature titanium and tantalum form a complete series of solid solutions containing up to 2 atomic pct C. The phases Tic and TaC also form a continuous series of solid solutions extending across the diagram. PREVIOUS work on this alloy system was very limited. Of the three binary constitution diagrams involved, only one, the Ta-C system was available in the literature. Preliminary data on the other two systems was received from the investigators during the course of the investigation and both have been published in recent months. It had been shown that Tic and TaC formed a continuous series of solid solutions, but the range of carbon content in this phase was not known. While Ta2C had been described, its solubility for or reactions with other carbides had not been reported. It was not known whether or not any ternary compounds occurred in the system. The present program was undertaken to determine experimentally the general form of the ternary diagram. It is hoped that the results will be of value in furthering the development of sintered carbide cutting materials and high temperature ceramets, many of which contain combinations of Tic and TaC. The Binary Systems Of the three binary diagrams involved only that of Ta-C was available at the time this project was started. The diagram of Ellinger¹ redrawn in Fig. 1, shows a hexagonal phase Ta2C having a very small composition range and a cubic TaC phase having a composition range of from 40 to 50 atomic pct C. The authors made a separate determination of the composition range of TaC using lattice constant values and found the range to extend from 40 to 49.7 atomic pct C in good agreement with Ellinger&apos;s diagram. Two determinations of the Ti-Ta system have appeared recently.2,3 These two diagrams are in good agreement and show that ß titanium and tantalum form a complete series of solid solutions. The Ti-C diagram by Cadoff and Nielsen4 shows a very limited solubility of carbon in both a and ß titanium. The single carbide formed persists over a wide range of carbon contents. Several values for the upper limit of carbon content of this phase have been reported."&apos; The highest value obtained in the M.I.T. Laboratory was 47.5 atomic pct C with a lattice constant of 4.328?.5 Fattinger7 describes a gas carburization method which he claims produces stoichiometric Tic although he does not present any data showing that he actually had 50 atomic pct combined carbon. Several complete analyses on

Jan 1, 1954

By J. M. Sands

Production of oil in Oklahoma during 1927 amounted to 273,256,900 bbl. (Table l), an increase of nearly 100,000,000 bbl. over the previous year. All of the major fields declined with the exception of those of the Seminole district which produced 136,105,000 bbl., almost one-half of the total production of the state. Because of this large new production, most of the development in the state during the year took place in that district. The Seminole City pool located in T.-9-N., R.-6-E., was the first of these pools to be developed. The Indian Territory Illuminating Oil Co. brought in the first well in this field in March, 1926, for 1100 bbl. This well is located in Sec. 24-T.-9-N., R-6-E., and produced from the Hunton lime reached at depth of 3900 ft. The first Wilcox production was developed by the Independent Oil & Gas Co. and R. S. Garland in Sec. 26, T.-9-N, R-6-E. This well was being drilled for production in the Hunton lime but was dry in this horizon and was deepened to the Wilcox sand in July, 1926, and at the total depth of 4069 ft. developed a maximum production of 8000 bbl. daily. It held up in wonderful manner and was the cause of not only the development of this pool but the prospecting of the whole district for the Wilcox sand. This led to the discovery of the other major pools in that district. Seminole City pool reached a peak production of 264,500 bbl. on February 22, 1927, and slowly declined so that by December it had a daily average of 56,200 bbl. from 321 wells. The second pool in this district to be discovered was the Searight pool which was discovered by F. J. Searight et al. in Sec. 33, T-10, R-6, in April, 1926. The first well was drilled to the Hunton lime encountered at 4115 ft., and came in for 1300 bbl. daily. During August, 1926, the second well was drilled on the same farm through the Hunton lime to the Wilcox sand which was encountered at 4360 ft. It came in for an initial production of 4000 bbl. daily. This started active drilling in this field for the Wilcox sand. The field had a peak production of 40,621 bbl. on June 15, 1927, and declined to a daily average of 22,300 bbl. from 73 wells during December.

Jan 1, 1928

By D. A. Kraai, S. Floreen

The effect of 1 to 50 ppm S on the ductility of nickel at 800° to 1400°F was studied. Results at each temperature showed a decrease in the reduction of area from approximately 95 to 5 pet over the sulfur range studied. Ductility varied with grain size, but only to a minor extent relative to the sulfiw effect. The effects of sulfur were completely offset by the addition of small amounts of magnesium. The results indicate that the "hot-short" loss in ductility is not an inherent property of nickel. Some possible mechanisms which cause the loss in ductility are described. MANY metals or alloys that normally possess high ductility exhibit a ductility loss at intermediate temperatures. This loss in ductility is often called "hot-shortness". Numerous examples of this phenomenon have been reported in the literature. Much of this work has been reviewed by McLean1 and by Rhines and Wray.2 To date there is no fully satisfactory explanation of the cause of this intermediate-temperature hot-shortness. It is generally recognized that impurities, and particularly impurities that form low-melting phases, can cause embrittlement. Examples of hot-shortness have been reported, however, where there were no obvious impurities present which would lower the ductility. Thus there has been some basis for believing that hot-shortness is an inherent property, and that even the purest metal would display a hot-short loss in ductility. This latter hypothesis was recently put forward by Rhines and wray2 based on studies of nickel and nickel alloys. In the discussion of this paper, however, Guard noted that high-purity nickel showed no hot-shortness.3 Thus there is reason to doubt whether pure nickel, or by inference any other pure metal, will inherently exhibit hot-shortness. The present work was initiated to determine the extent to which hot ductility was sensitive to very small amounts of an impurity element. If it could be demonstrated that hot-shortness could be induced by only minor amounts of an impurity, then it might be argued that hot-shortness in general is an impurity effect, and not a fundamental property of pure metals. The particular impurity studied was sulfur in nickel. The deleterious effects of sulfur are well- known. It is also well-known, and will be shown below, that additions of magnesium will render sulfur innocuous. When no such refining agents are added, however, the Ni-S system is a very useful one for studying the influence of small amounts of impurities. EXPERIMENTAL PROCEDURE Two heats containing -24 ppm S were vacuum-melted and small amounts of magnesium were then added under an argon atmosphere. These alloys were used to show the effectiveness of the normal magnesium treatment in overcoming the influence of sulfur. A second series of alloys with a sulfur range of 1 to 50 ppm was then prepared by vacuum melting nickel in alumina crucibles. No elements, such as magnesium, which tend to combine with sulfur were added. The higher sulfur contents were attained by adding nickel sulfide. Lower sulfur contents were prepared using a method in which the melt was oxidized under vacuum to produce the reaction S + 2O = SO2 These heats were subsequently deoxidized with carbon. Ten- to twenty-pound ingots were cast of all of the alloys studied. The compositions are given in Table I. The ingots were forged and hot-rolled to 3/4-in. bar. They were then annealed at either 2000" or 1600°F to produce different grain sizes. One-quarter-in.-diam tensile specimens were machined from the bars. These were tested at 800°, 1000o, 1200°, and 1400°F. The specimens were held at temperature approximately 45 min before testing. The strain rates were 0.005 min-1 to yielding, and 0.05 min-&apos; after yielding. No extensometers or gage marks were placed on the specimens because the higher sulfur heats tended to fracture at the knife-edge indentations or gage marks. The properties measured were ultimate tensile strength and reduction of area. The analytical technique for determining sulfur at low levels was that developed by Burke and Davis.4 They reported a standard deviation of 1 ppm at an average sulfur level of 4 ppm in NBS standards. A standard deviation of 3 ppm is probably more realistic for the alloys used in this investigation considering the possibility of some segregation in the ingots. RESULTS A summary of the tensile results is given in Table I. As shown in the table, both heats to which

Jan 1, 1964

By Knut L. Sandvik, Aage Solbakken

it is an established fact that the collecting properties of xanthates and anionic collectors are dependent on the hydrocarbon chain length. This is ascribed to the greater adsorption densities caused by increasing the xanthate chain length. As batch flotation tests showed similar trends for amines, an investigation of the adsorbing properties of amines was undertaken. Because earlier investigations showed adsorption densities for dodecylamine salts on quartz varying as much as 20 times under apparently similar conditions,1-4 it was decided to make a survey of the changes in adsorption density due to the drying conditions of the quartz. EXPERIMENTAL PROCEDURE The quartz, handpicked in the pegmatite quarries of Iveland, Setesdal, had the following composition: SiO2 99.81, A12O3 0.01, Fe2O3 0.05 and loss by ig-

Jan 1, 1969

By P. Somasundaran, I. J. Lin

There are several methods described in the literature for the determination of the order and the rate constant for the flotation of minerals. These often involve some type of computational or graphical procedures. A relatively simpler method developed on the basis of a technique used by Chang" in chemical kinetics is described in this paper. Chang&apos;s technique, like most others in chemical kinetics," is based on the law of mass action which states that the rate of a chemical reaction is proportional to the active masses of the reacting substances at any given time. Application of this law to the flotation of minerals would involve the adaptation of the terms "flotation" for "chemical reaction" and "floatable amount of the minerals" for "the active masses of the chemical reactants." There are indeed a large number of physical processes controlling the actual flotation rate. The most inefficient one of these could be considered equivalent to the slowest reaction in a series of chemical reactions. If variables such as aeration rate and agitation are kept at constant levels, the rate of flotation under free flotation conditions (i.e., conditions under which the suspension is dilute) will be given by the following equation: where C is the concentration of the floatable minerals in the pulp at any given time t, K is the rate constant, and n is the order of the reaction. If we represent the floated fraction of the floatable mineral at time t as m (0 m - 1) and C at t = 0 as Ca, integration of Eq. 1 yields

Jan 1, 1974

By Edgar Newhouse

THE lead smeltery at East Helena, Mont., controlled by the American Smelting & Refining Co. since 1899, has been in continuous operation for the past 25 years. Most of the old smelting and roasting practices have been superseded by newer and more modern methods, but on account of the difficulties involved in changing the original construction, some of the methods in use of handling materials are not the most modern. This plant, however, is particularly interesting as being one of the few essentially lead smelteries in the United States. At Federal, Ill., Collinsville, Herculaneum, and possibly other places, similar work is being done, but it is doubtful whether any of them produces as&apos; much lead as the East Helena plant, whose monthly production averages 6,500 tons. The situation, 5 miles east of Helena, is convenient to both the Great Northern and Northern Pacific railroads, while the electric power is obtained from Canyon Ferry, 12 miles east on the Missouri river. Local quarries supply the requisite amount of lime rock, Which the contracts require to be crushed to 5 in. Of the 450 men on the monthly pay roll, a census showed 200 Austrians, 110 Americans, and 30 Italians, the balance being made up of miscellaneous nationalities. The ore supply is mainly derived from the Coeur d&apos;Alêne mines in Idaho, and consists of crude ore, coarse and fine concentrates, middlings, and slimes. About one-half of the total output of the Coeur d&apos;Alêne camp is sent to East Helena. An average analysis of these ores gives approximately 40 per cent. lead and 11 per cent. sulphur. Local shipments, varying, from month to month, are mostly highly siliceous gold and silver ores carrying little lead. Small shippers, leasers of old mines, and prospectors are very numerous throughout Montana, and it is the policy of the company to encourage these men by every possible means, including the free sampling and analysis of their ores and aid in the development of their mines and prospects whenever their results show promise.

Jan 8, 1914

By B. C. Raynes

IN the early part of 1952, under the auspices of the U. S. Atomic Energy Commission, Horizons Inc. undertook an investigation dealing with the preparation of high purity thorium metal in order to develop an economically competitive production process for this metal based on a recovery of the metal by a fused salt electrolysis, since a survey of the literature of thorium chemistry indicated that electrolytic methods had not received much attention, despite the consideration that electrochemical production methods often offer attractive commercial potentialities. Thorium metal has been prepared by methods which fall into four general categories: 1) reduction of halides or double halides; 2) reduction of the oxide; 3) thermal decomposition of halides; and 4) electrolytic methods. Some of the important results obtained by various investigators since about 1900 in recorded attempts to prepare pure thorium metal are summarized in Table I. A bibliography of pertinent literature is included in this paper. Thorium is strongly electropositive and possesses a great affinity for oxygen and nitrogen. As a result the prospects for the production of high purity thorium from aqueous media or oxygen bearing compounds are remote. The most promising and profitable area of investigation for production of thorium metal lies in fused salt electrolysis. Thorium has been produced previously by this technique from halide salts in fused alkali chloride eutectic mixtures. Until recently, however, the lack of known large uses for thorium has inhibited the investigation of these methods. The basic problem in an investigation into fused salt production methods for thorium is to develop a suitable fused salt system for the economic preparation of thorium. The first portion of the work in these laboratories was a small scale investigation of the electrolysis of potassium thorium fluoride, KThF5, under a variety of conditions. High purity thorium was prepared in this manner, but the process did not appear to offer the simplest and most attractive continuous commercial operation. The work reported here relates to an all-chloride system employing thorium chloride as the cell feed. ThCL4 was produced as an anhydrous material stabilized in molten sodium chloride. This product, further diluted in NaCl, was subjected to electrolysis. The electrolytic process has been studied in cells capable of holding up to 50 lb total salt charge. Ductile, pure thorium metal has been reproducibly obtained in this operation. Considerable experimentation was carried out in the preparation of ThCL as a cell feed free from moisture, oxides, and other impurities. Thorium was cathodically deposited as a coarsely crystalline powder interspersed with residual bath salts. Aqueous procedures for separating and recovering the metal were developed. The thorium metal powder obtained has been evaluated with respect to its hardness, chemical purity, and certain other physical properties. Preparation of ThC1,—Thorium chloride, and the chlorides of some other metals (aluminum, beryllium, tantalum, zirconium, etc.) cannot be obtained from aqueous solution by direct heating and evaporation. Evaporation and heating of a solution of thorium chloride yields a hydrated salt or partially hydrated salt, and finally Tho,. Anhydrous thorium chloride is obtained by forming a hydrated ammonium chloride complex salt in acidified water solution, dehydrating this compound, and finally decomposing the double salt and subliming the ammonium chloride component. Various methods for the preparation of anhydrous thorium chloride, in accordance with this concept, were investigated as indicated in Table I1 from hydrated thorium chloride (ThCl, . 3H2O), and from thorium oxycarbonate (ThOCO,). In the method found most satisfactory for this work, thorium oxycarbonate was dissolved in an excess of concentrated HC1 to give a clear yellow solution. At least 2 mol NH,Cl were added to the solution per mol of contained thorium. Ammonium thorium chloride hydrate was crystallized from solution by cooling and saturation with HC1. The resultant complex, (NH,Cl),ThCl;xH,O, was dehydrated by evaporation at 130° to 150°C and thoroughly dried at about 250°C. The dried ammanium thorium chloride was then mixed with sodium chloride in proportions to form NaThCL or to produce a ThCL4-NaCl mixture with a given thorium content. The ammonium chloride was sublimed off at temperatures above 500°C in an inert atmosphere furnace to give an anhydrous chloride source electrolyte, essentially free of Tho, and of NKC1.

Jan 1, 1958

By William D. Klopp

A study was conducted of the tensile and creep properties of are-melted and electron-beam-melted tungsten over the temperature range 2250° to 4140°F. The tensile and creep strengths vary with pain size, the finer -grained materials being stronger. The activation energy for transient creep at 2250° to 3500°F is 95,000 cal per (g)(mole), while that for steady creep at 3300o to 4000°F is 141,000 cal per (g)(mole). At 2875o to 3300°F the apparent activation energy for steady creep decreased with decreasing temperature. It is suggested that cross slip is rate controlling during transient creep, while dislocation climb is rate controlling during steady creep above 3300° F. ALTHOUGH considerable data have been generated on the high-temperature tensile properties of powder-metallurgy tungsten,1 relative few data have been published on the properties of are-melted2 or electron-beam melted tungsten.3 Furthermore, the available data show a fairly large amount of scatter at high temperatures. The effects of structure and purity have not yet been defined, aside from observations that high-purity electron-beam (EB)-melted tungsten3 and single-crystal-plasma-flame tungsten4 are weaker than less pure powder-metallurgy tungsten. The creep behavior of powder-metallurgy tungsten has been studied, but no data are available on the creep behavior of tungsten consolidated by melting. Green5 found that powder-metallurgy tungsten exhibited linear creep at 4082° to 5072°F with an activation energy of 160,000 cal per (g) (mole). The similarity of this activation energy to that of 153,000 cal per (g)(mole) for volume self-diffusion6 suggests that recovery of strain hardening by dislocation climb is rate controlling in this temperature range. In studies at 4800°F, Sutherland and Klopp7 concluded that grain size significantly affected the creep behavior of commercial powder-metallurgy materials. This grain-size effect was suggested by sherby,8 although the opposite relation had been reported for aluminum.&apos; The purpose of the present study was twofold: first, to provide baseline data on high-temperature tensile and creep properties of are-melted and EB-melted tungsten for concurrent tungsten alloy studies, and, second, to determine the phenomenolo-gical effects of structural and purity variables on the high - temperature mechanical properties of tungsten. EXPERIMENTAL The are-melted tungsten materials were prepared by melting sintered 1-1/4-in.-diam electrodes into 2-1/2-in.-diam by 5-in.-long ingots. The are-melting facility has been described previously.&apos; Eight ingots were melted, machined, and hot-extruded at

Jan 1, 1965

By R. Laird Auchmuty

FOREWORD THE A. I. M. E. Subcommittee on Bituminous Mining has been trying for several years to secure the information that was collected by the Marquette Cement Manufacturing Co. on the subsidence of its property caused by mining coal beneath it. The Marquette company was willing to have these data used, but it was impossible to obtain them because the records had been filed away. About two years ago these records became available and the engineering data presented herewith were compiled from them by R. L. Auchmuty, assisted by L. E. Young, who was connected with the collection of the information. On account of the cost, it is impossible to reproduce all of the data here, although the original information is on file with the records of the Committee on Ground Movement and Subsidence. The accompanying charts show representative and average data and give only the engineering information with enough description to tell how it was obtained. It is hoped that all of those connected with the original case will participate in the discussion that this will bring forth. HOWARD N. EAVENSON, Chairman, Subcommittee on Bituminous Coal Mining.

Jan 1, 1931

By W. H. Gunniss

When the copper smelters were built, in Montana, all of the refractory products which were used in their construction were shipped in from Eastern factories. It was apparent that if a material suitable for the manufacture of these products could be found within the State, a saving of freight could be effected and a new industry built up. Prospecting for such materials was started and experiments were made with samples from numerous deposits. Considerable effort and funds were expended in an attempt to manufacture silica brick from Dillon quartz, a light colored sandstone that is found near Dillon, Mont., on the Oregon Shortline railroad. As a brick material the Dillon quartz was a failure, but it has proved very satisfactory as a silica cement. It is now being used in laying silica brick and for reverberatory furnace bottoms. A bed of quartzite that is particularly suited to the manufacture of high-grade silica brick was finally discovered at Browns Spur, 6 miles west of Anaconda. The material from this deposit is now being used in the manufacture of the Anaconda silica brick, which have gained a wide reputation for heat-resisting and lasting qualities. The analysis of an average sample of this quartz is: SiO2, 96.7; Fe2O3, 0.3; Al208, 2.5; CaO, 0.3 per cent. The very low percentage of fluxing ingredients makes this a most refractory material. All of the Anaconda silica brick are hand molded. Various types of brick machines have been tried, but the hand-mold process proved the best suited to the manufacture of silica brick from this material. The silica is first put through a jaw crusher and is then dumped into wet pans, where 4 per cent. of lime paste is added, to produce a bond. Without the lime the material would not be plastic enough to mold. After a few minutes&apos; grinding in the wet pans the material is conveyed to the molder, who forces it into the molds by hand. The brick are then dumped on pallets and placed in the drier, where they are left. until dry enough to be set in the kilns. Some of the brick are re-pressed before being dried. They are burned about five days, in round down-draft kilns. It is not necessary to have as much heat in the kilns as the brick will be subjected to when in use in the furnaces. Montana refractories are used in smelters throughout the West. Prospecting for fire clays was also carried on. After experimenting with clays from several different deposits, it was found that a mixture of

Jan 1, 1914

By E. T. Turkdogan, P. Grieveson

The self-diffusion coefficient of oxygen in a liquid silicate slag containing 40 pct SiO2, 40 pct CaO, and 20 pct Al2O3, was determined using the capillary eff;usion technique. Two stable isotopes of oxygen (O17 and O18) were used as tracers. After each diffision run, the slags were reduced with graphite, the evolved carbon monoxide collected and converted into CO,. The oxygen isotope concentrations were obtazned by measuring the (CO2)45/(CO2)44 and the (CO2)46/(CO2) ratios of the gas. It was found that for O17 Exchange of oxygen between neighboring silicate anions, possibly accompanied by the rotation of these complexes, is a probable diffusion mechanism. The exchange of oxygen atoms between holes in the silicate "lattice" may also be postulated. A full understanding of the properties of slags is unlikely unless the structural details are clearly established. Thus properties such as surface tension, viscosity, expansivity, electrical conductivity, ionic mobility, density, compressibility, and so forth, have been studied. Of importance also are the self-diffusion coefficients and the energies of activation for diffusion of the component ions. The self-diffusion coefficients of calcium, 1-3silicon,, sulfur,4 and aluminumS in a ternary silicate slag have been determined with the aid of radio-isotopes. The self-diffusion coefficient of oxygen in such a slag was investigated in the course of the work reported here.

Jan 1, 1962

By Fred C. Bond

Many grindability tests have been made in the Allis-Chalmers laboratory since the tabulated results were last published.&apos; The lists of standard ball-mill and standard rod-mill grindability tests are brought up to date in this paper, and considerable new material is added. This includes a tabulation of open-circuit grinding tests, with impact and compression-crushing tests. The standard ball-mill grindability tests (Table I) were made in a standard laboratory ball mill, 12 by 12 in. inside, running at 70 rpm, with a charge of 285 iron balls ranging from 1½ to 3/4 in. in diameter and weighing 20,125 grams. Seven hundred cubic centimeters of minus 6-mesh stage-crushed dry feed was used, and the circulating load was maintained constant at 250 pct by adjusting the number of mill revolutions for each grinding period. Tests were made at all mesh sizes from 28 to 200, and the grindability is the number of net grams of screen undersize produced per revolution. The table includes 479 tests. It has been calculated that the ball mill does 52.3 joules of useful work on the ore per revolution2 with 93 joules input to the mill. The standard rod-mill grindability tests (Table 2) were made in a laboratory tilting rod mill, 12 in. in diameter by 24 in. long inside, with a wave-type lining, running at 46 rpm. The grinding charge consisted of six I1/4-in. diameter and two 13/4-in. diameter steel rods, all 21 in. long and weighing 33,380 grams. The mill was rotated level for eight revolutions, then tilted up 5&apos; for one revolution, down 5° for one revolution, and returned to level for eight revolutions. It was discharged by tilting downward at 45° for 30 revolutions. Feed consisted of 1250 cc of minus in. stone and the circulating load was maintained constant at 100 pct by adjusting the number of mill revolutions for each grinding period. Tests were made at all mesh sizes from 3 to 65, and the rod-mill grindability is the number of net grams of screen undersize produced per revolution. The table includes 105 tests. The impact and compression-crushing tests (Table 3) are given in a table that is an extension of a previous publication8 in which the method of testing was described in detail. Two equal hammers weighing about 30 lb each were arranged to strike simultaneous blows on opposite sides of the test specimen. Broken pieces of rock passing a 3-in. square and retained on a 2-in. square were set up with the smallest dimension between the hammers, and this distance was measured. The height of the hammers was increased slightly before each blow until the specimen broke, and the foot-pounds per inch of thickness was calculated. Ten pieces

Jan 1, 1949