By Sherwin F. Kelly

THE geophysical scene shifts and alters, the emphasis changes, and new possibilities loom, but the tendency is always towards widening the field and deepening the analytical penetration. Seismic methods have had their heyday, the torsion balance is being displaced by the gravimeter, electrical methods are showing deeper penetration, soil analysis is the newest tool, and gamma-ray logging appears on the horizon. One of the striking features of re- cent geophysical work in the oil fields has been the marked decrease in the number of seismic crews employed. Although the percentage of company crews is believed to have increased appreciably. the sum total has fallen sharply, as shown by the figures for the Gulf Coast area. About two years ago probably over 100 seismic parties were operating there, whereas now there are only about 35. This decrease may be partly due to the low prices of petroleum with a consequent reluctance to spend money to increase crude-oil re- serves but more probably to the fact that reflection and refraction shooting have been carried on so extensively that they have been applied to a large pro- portion of the areas in which they may reasonably be expected to succeed. Some of the earlier enthusiasm, particularly over reflection prospecting, may have erred on the side of over- optimism; some of the present curtailment may be due to over pessimism; but in the opinion of various observers seismic work at the present rate seems to be at it- optimum. It nevertheless remains pre-eminent as a technique for detailing structures in areas where good reflections can be obtained and is the only method that will give accurate depth to definite beds. Results may be poor in certain areas but many regions still remain wherein it can be applied, so that plenty of structural mapping remains to be done by the reflection seismic method.

Jan 1, 1940

By R. A. Vandermeer, J. C. Ogle

The preferred crystallographic orientations (texture) developed in randomly oriented, poly crystalline niobium during rolling were studied by means of X-ray diflraction techniques. The evolution of texture at both the surface and center regions of the rolled strip was carefully examined as a function of increasing defamation throughout the range 43 to 99.5 pct reduction in thickness. Certain aspects of the center texture development in niobium are in agreement with the predictions of a theory by Dillamore and Roberts, but others cannot be explained by the theory in its present form. Above 87 pct reduction by rolling, a distinctly different texture appeared in the surface layers which was unlike the center texture. The present results are compared with previous results obtained from other bcc metals and alloys. RANDOMLY oriented, poly crystalline metal aggregates when plastically deformed to a sufficiently large extent develop preferred orientations or textures. In a recent review article, Dillamore and Roberts1 pointed out that the nature of the developed texture may be influenced by a large number of variables. These include both material variables such as crystal structure and composition and treatment variables such as stress system, amount of deformation, deformation temperature, strain rate, prior thermal-mechanical history, and so forth. From a practical point of view, the control of preferred orientation may often be important for the successful fabrication of metals into usable components. During the past few decades many experiments have been devoted to the study of deformation textures. This work, however, has been confined in large part to metals and alloys that have an fcc crystal lattice. By comparison, bcc metals and alloys have received much less attention, and consequently our understanding of preferred orientations in these materials is only shallow. This state of affairs worsens when it is realized that almost all of our present howledge about this class of materials derives from studies on irons and steels.' The bcc refractory metals, which are relative newcomers to the industrial world, have, on the other hand, been given at best only passing glances in the area of texture development. Our understanding of the evolution of preferred orientations in bcc metals can only remain fairly limited until systematic studies of metals and alloys other than the irons and steels have been carried out and the influence of the many variables has been determined. To that end a program was initiated to investigate in detail texture development in niobium. The present paper reports some of the results of this study. Textures were determined at both the center and surface of strips rolled variously to as much as 99.5 pct reduction in thickness at subzero temperatures. Emphasis in this paper is on texture description and on texture evolution during rolling to progressively heavier deformation. EXPERIMENTAL PROCEDURE The niobium was purchased from the Wah Chang Corp. as a 3-in.-diam electron-beam-melted billet. Chemical analysis indicated the impurities to be less than 300 ppm Ta, 40 ppm C, 10 ppm H, 170 ppm 0, and 110 ppm N. All other impurities were below the limits of detection by spectrochemical analysis. This large-grained billet was fabricated into specimen stock so that a fine-grained randomly oriented grain structure resulted. This was accomplished in three deformation steps alternated with recrystalli-zation anneals of 1 hr at 1200°C in a vacuum of low 10"6 Torr range after each deformation step. The first step was to alternately compress the billet 10 to 20 pct in each of three orthogonal directions. The second step was to compress in only two directions 90 deg apart to produce a 2-in.-sq bar. The final step was to roll this bar 50 pct to give a 1-in. by 2-in. cross section. After the final anneal, metallo-graphic examination showed the material to have an average grain size equivalent to ASTM No. 5 at 100 times (i.e., 0.065 in. diam). Specimens cut from the center and edges of this bar gave no indication of detectable preferred orientation when examined by X-ray diffraction. Samples 1.5 in. long, either 0.625 or 0.750 in. wide, and approximately 0.400 in. thick were machined from this fabricated ingot. The surfaces corresponding to the rolling planes were ground so as to be parallel. The samples were chemically polished in a solution of 60 pct nitric acid and 40 pct hydrofluoric acid (48 pct solution) prior to rolling to remove any cold work introduced in the machining operations. Rolling was accomplished with a 2-high hand-operated laboratory rolling mill that had 2.72-in.-diam rolls. Prior to operation, the rolls were polished with 600 grit paper, cleaned with acetone, and then soaked in a container of liquid nitrogen for several hours. The samples were also soaked in liquid nitrogen prior to rolling and were recooled between each pass. While some slight heating of the samples occurred during rolling, this procedure maintained the sample temperature well below 0°C at all times. The samples were rolled unidirectionally, and the rolling plane surfaces were not inverted during any phase of the operation. The draft per pass averaged between 0.010 to 0.012 in. After 96 or 97 pct reduction the draft was reduced to 0.001 to 0.002 in. per pass. Samples were rolled to various reductions in thickness between 43 and 99.5 pct.

Jan 1, 1969

BRANCH COUNCILS MINING BRANCH R E Byler, '53, Chairman (Minerals Beneficiation) - C M. Cooley, Acting Secretary A Lee Barrett, '54, (Coal) Carroll A Garner, '53, (Coal) E. H Crabtree, '54, (Minerals Beneficiation) Ian Campbell, '54, (Industrial Minerals) A B. Cummins, '53, (Industrial Minerals) E. D Gardner, '53, (Mining, Geology, and Geophysics) LeRoy Scharon, '54, (Mining, Geology, and Geophysics) R. T Gallagher, (Mineral Industry Education) John H Ffolliott, (Mineral Economics)

Jan 1, 1952

By J. F. Kemp

The use of nickel-steel has directed increasing interest of late towards the deposits of nickel, and at the same time the parallel advance in our knowledge of the basic igneous rocks has rendered these deposits a subject of important geological inquiry. Investigations have led to some views, more or less new, on the igneous origin of certain ores, which, though not universally accepted, have a growing number of adherents. In Europe, the mines in Norway have been especially suggestive subjects of study, and others somewhat less generally known have also added their testimony; while in this country the great economic importance and scientific interest of the developments in the Sudbury district of Canada, have furnished the principal texts for the discourses that have appeared among us. The purpose of the present paper is to set forth these views through the medium of one interesting ore-body, of which but little has been written ; and, by the description of another, to place in contrast two different geological associations in which nickeliferous pyrrhotite occurs, and to indicate a generalization, based upon these different geological characters, and justified by the experience so far gained. To Prof. J. H. L. Vogt, of Christiania, Norway, is due the chief credit for the revival of interest in the geology of nickel. His important contributions* of recent date have made generally available

Jan 1, 1895

THERE are, as I have heard, varying opinions among men experienced in minerals as to whether silver has its own mineral [i.e., occurs native] or not. Mineralogical reasons and the authority of the majority persuade me that it has, not only because I have seen the natural material separate but also because I know that in mines of gold, copper, lead, and other metals pieces of pure metal are found without admixture, and I have heard that pieces of silver, gold, and copper have been found that had been reduced to their ultimate purity by natural causes. This is also confirmed by a German, Georgius Agricola, who says* that in a mine in Saxony a piece of metallic silver was found so large that the Duke who was prince and patron of the place had a whole dining table of square German style made from it without its being enlarged or worked on by any human artifice except for the tripod legs, and he often boasted that in this he surpassed the greatness of the Emperor. In truth I have never seen any metal except copper that was brought out from the mine pure and without any mineral, but I think that such a thing is indeed possible, since I believe in the greatness and power of Nature, who strives toward no other goal than perfection and purity. Indeed most of the minerals that I have seen have not been without admixture, not only of their earth but also of other metals, and this is more true of that which I have heard called silver than of any of the others. I except the silver that is mined in Schio in the region of Vicenza. These doubts, therefore, are not born without some shadow of apparent reason. As I told you above I believe that silver may have and does have its own mineral, for every substance that is converted into metal can exist pure by itself in its own species, as it also exists separately even though it be mixed with others, since it is seen that in each ore its metal is generated in a single body. Therefore it happens many times that whoever speaks of the ore of silver in one breath, without distinction, speaks of that of all the other metals, because there are few ores that are not mixed. But because the most noble things always have the prerogative of including in their name that of the others, where there is gold or silver the ores are not called

Jan 1, 1942

By V. V. J. Sarma

Interpretation of earth resistivity data involves not only obtaining depth to interfaces but also determining the nature of formations from their resistivity characteristics. Moore's method of interpretation envisages obtaining depths to the interfaces alone. A simple method of estimating the true resistivity values of formations by applying Hummel's formula of average resistivities is proposed. The method would increase the interpretative value of Moore's method as originally proposed. For most of the earth resistivity measurements, the four-electrode configuration developed by Wennerl is employed. In principal, the method consists of energizing (Current I) the ground through two outer electrodes and measuring the resultant potential (v) between the two inner electrodes. The configuration is such that the separation (a) between any two successive electrodes is equal. The apparent resistivity (pa) for such a configuration is given by 2p- a (V/I). By increasing the electrode separation (pa vs a) curves are obtained. Ideally, a homogeneous isotropic formation underground has a characteristic resistivity. However, the field conditions do not present such ideal cases. Almost invariably, even in the same geological bed, the physical conditions are widely different at different parts in the bed. It is further shown that the penetration of the current into the ground for a given horizontal electrode separation, a, is roughly down to a depth, equal to a. It is therefore, evident that the apparent resistivity calculated from the field observations is a weighted average of the resistivities of the materials present down to this depth. With some prior knowledge about the relative dispositions of the geological formations and their physical conditions, it would be possible, by resistivity surveys, to obtain characteristic resistivities for these formations. It is, thus, that the apparent resistivity-electrode separation curves enable one to decipher the resis- tivity distribution at various depth levels and therefore the nature of the geological formations present. Both empirical and theoretical methods have been developed for determining resistivity characteristics of the various formations. The theoretical methods proposed by Tagg2 and Roman3 are derived from studies of the potential distribution on the surface due to the presence of layers of widely differing resistivities underground. The more recent methods of Wetzel and McMurry4 and Wetzel and Mooney5 are but extensions of the original Roman method of superposition. These methods suffer from lack of similarity of the actual field conditions with those of assumed conditions in developing the theory. The empirical methods such as the one developed by Gish and rooneY6 depend purely on personal observation and local peculiarities, and are applicable only for those limited areas. Out of the empirical methods, moore's7 cumulative resistivity method is still found to be applicable in several localities of differing conditions. While Reudy in 1945 adduced some theoretical justification for the method (Eve and Keys),8 Muskat9 and Mooney 10 tried to show the lack of theoretical basis for the same. It is, however, observed that the method in practice "forms a valuable means of successfully attacking the apparent resistivity curves which fail to respond to the Gish-Rooney, the Tagg or the Roman logarithmic methods" (Ramachandra Rao). 11 Comparatively good results are also reported by Melbyel2 by employing Moore's method in interpreting the resistivity results obtained for ground water in the city of Gunnison, Colo. MOORE'S METHOD As has already been pointed out, the application of the theoretical methods is time-consuming, laborious and sometimes not applicable for quick and accurate interpretation of the field data. moore7 has developed a quick method for obtaining depths to interfaces by plotting the cumulative sums of resistivities, against the corresponding electrode separations a instead of plotting the usual Pa — a curve. In this process of continuous integration, corrections for small variations in resistivities, arising due to local surface conditions or adjacent layers, are made, while large consistent variations are brought out

Jan 1, 1963

By F. A. Orth

COAL-mine opera- tors face a difficul- ty in notifying men when there is no work. If the miners come to the shaft when there is no work, they must be paid, by agreement, two hours' wages. This involves a considerable loss since it is not uncommon to em- ploy two or three hun- dred men or more at a single shaft. Many mines have solved the problem by using an electric siren. This carries the "no work" message to all of the miners within a ra- dius of from one and one- half to two miles, so they do not trudge uselessly to work and the operator saves the two-hours wage payment. At the Valley Smokeless Coal Co., Johns- town, Pa., such a siren serves as a start and quit- work signal for three mines which previously re¬ quired three individual signal systems. Similar units are used by the Old Ben Coal Corp. mines, Dolly's Smokeless Coal Co., Rhonda Coal Co., Bird Coal Co., and hundreds of others. Many other applications of the electric siren have been found in mines. They are used on underground locomotives, to awaken miners in the morning, to tell them it is time to come to work, to sound the start and quit-work signal, and to warn of fire or accident. The sirens are most generally used to give a start and quit-work signal, fire, and general emergency alarms as well as no-work signals. They require 3 and 5 hp. to operate. The smaller unit has a sound radius of from three-quarters to one mile, while the larger siren can be heard over a distance of from one and one-half to two miles. The 5-hp. unit has been heard for as great a distance as 14 miles, and 10 miles is not at all uncommon. One of the outstanding features of the 3 and 5-hp. units, which is uncommon in the smaller sirens is that they may be adapted to sound code signals. When used to sound a fire or general emergency alarm the siren may tell at the same time where the fire or acci-dent is. When a remote control device is used with a siren it is possible to operate the siren from any number of distant points. Any number of "start" buttons may be placed at various places. By using one "start and stop" button where the remote control is mounted, and one or more "start" buttons at various places about the plant, it is necessary to run only two wires to the various "start" buttons. If "start" and "stop" buttons are used altogether, then three wires must be run.

Jan 11, 1927

T. H Aldrich '96 Walter H. Aldridge '89 R M. Atrater, Jr '97 James B Bailey '00 Samuel Barker, Jr. '00 John F Berry '93 Charles A Bohn '93 H. A Brassert '99 Victor B. Buck '98 Frederick Burbidge '87 Frederick P Burrall '97 John Cabot, Jr '99 William McC. Cameron '97 W Gaston Caperton '94 Norman Carmichael '99 Alvin B. Carpenter '97 Charles A Chase '00

Jan 1, 1952

By R. D. Carter

Nurnerical .solutions are presented to some problems of unsteady-state radial flow of gas in which Darcy's law holds. These solutions are intended to aid in explaining the observed behavior of gas wells during drawdown tests. The variation of viscosity and Z-factor with pressure is accounted for in the solutions. Results are presented for three types of problems: (I) unfractured wells producing at a constant rate, (2) fractured wells producing at a constant rate and (3) unfractured wells producing through a critical flow prover. In the critical-pow-prover solutions, a correction of the calculated well-bore pressure to account for non-Darcy flow is made. A good correlation is shown between the solutions to the problem of Type 1 and the corresponding diffusivity-equation solution. Using this correlation, the diffusivity solution may be used to obtain gas-well solutions. The solutions to the problems of Type 2 illustrate the difference in drawdown-curve behavior to be expected between fractured and unfractured gas wells. Methods for estimatting fracture radius and flow capacity are presented and verified from solutions of Type 2. The solutions to the problems of Type 3 illustrate the differences to be expected between critical-flow-prover drawdown tests and constant-rate tests. An equation is presented for correcting critical-flow-prover data to constant-rate conditions. A description of the methods used in obtaining the solulions appears in the Appendix. INTRODUCTION It is necessary for many engineering purposes, such as predicting future deliverability performance, to be able to relate bottom-hole flowing pressure, formation pressure and flow rate for conditions of stabilized flow in gas wells. This information is customarily given as a plot of on logarithmic co-ordinates. It is desirable to be able to predict stabilized performance curves for gas wells based on data obtained from drawdown tests of short duration. Tests of long duration may be wasteful of gas, and low-permeability wells do not stabilize in a short-duration test. Although it is now commonly recognized that non-Darcy flow plays a significant part in gas-well behavior, it is believed that an understanding of transient behavior of systems obeying Darcy's law is still important in the interpretation of short-term test data, and the prediction of stabilized performance curves therefrom. In this connection, an equation for correcting Darcy flow It seems likely that solutions of the type presented herein, combined with the non-Darcy flow correction of the type of Eq. 1 and the usual laminar-flow skin factor, could provide a model which would adequately explain transient gas-well behavior for times after the non-Darcy flow region (which should be confined to a small area surrounding the well) has been established. The solutions presented in this paper are for three types of problems: (1) unfractured wells producing at a constant rate, (2) fractured wells producing at a constant rate and (3) unfractured wells producing through a critical flow prover. In the problems of Types I and 2, no corrections for non-Darcy flow were made in the results presented, since it was reasoned that the constant-rate boundary condition would facilitate such a correction if it was desired later. For the problems of Type 3, however, a condition of varying flow rate required that a non-Darcy flow correction of the type of Eq. 1 be included. This was done. Based on the numerical results presented, a number of approximations and a correlation are presented which may be useful in analyzing gas-well test data. It is assumed that the system can be described as a finite cylindrical gas reservoir produced by a single cylindrical well located at the center of the reservoir. Flow is strictly radial.

By George C. Stone

WHEN George C. Stone, a Director of the Institute, and so well known to our Members in connection with the Institute's many activities was abroad in 1.919, he secured an interesting collection of these coins, which appeared in Zinc, a publication by the New Jersey Zinc Co. Regarding this collection of coin, Mr. Stone says: "During the war, all gold and most of the silver disappeared, making small change very scarce. As the French Government was fully occupied by the war, it allowed various Chambers of Commerce and other bodies to issue money, both paper and coins. Many of the latter were made of zinc, and I secured several while in Paris. We had all heard of the Belgian and German zinc coins, but I imagine few knew how many different kinds there were. The accompanying plates show both sides of those I got. I took all that the dealer had; but he said that there were a number of others in existence. The coins in the bottom line were issued by the Germans in Belgium during the war and all are still in common use. The first two in the next to the bottom line are German. All of the others were issued by Chambers of Commerce or corporations. A few have been nickel plated; these look and wear much better than the others. "Coins" made of pasteboard were also issued by similar bodies, also notes.

Jan 1, 1920

By Ian MacGregor

As I drove in from the airport on Sunday somebody said 'On the right you will see Duntroon, which is the military training school of Australia.' So I asked the driver, where did they get that name? 'Oh,' he said, 'from some people who built a house there. That was it's name- Duntroon.' It strikes a note with me because, that's the name of a 12th century castle on the west coast of Scotland where I spend what leisure hours I have and, therefore, it establishes the long connection between Australia and my native land. There is also a story I should tell you about the oil industry and its upsurge in Scotland recently which has resulted in great prosperity. And in Edinburgh, the walls of the banks are bulging-because of the incursion of foreign exchange and other resources. Charlotte Square, as some of you know, is the centre of the Scottish financial world and at one of the corners of Charlotte Square, where ho streets intersect, there are three stores-three emporia on the ground floor. Two of them at opposite corners are banks: The Royal Bank of Scotland, and not to be beaten by that, The Bank of Scotland. But the third building is occupied, or was occupied, by a furniture store over many years-very high-grade, high quality furniture that the elite of the Edinburgh society always supported. And suddenly, the store was cleared out and in came a bunch of carpenters and other people busily engaged in rebuilding the store, and finally the new tenants arrived on the scene.

Jan 1, 1978

By AIME AIME

HOLDING the annual dinner-dance of the Institute at the Waldorf-Astoria had become such a tradition that there was widespread regret when it became known that the demolition of the building to make way for a huge office structure would perforce bring to an end the long and enjoyable series of gatherings our Institute had held there. This year the . Commodore was the place at which it was held and the commuters on the New York Central and the New Haven railroad systems, at least, found it a more convenient place for them. Except for the famous "Hoover" dinner, which will probably set a mark for all time, it was the largest dinner the Institute held, 1000 being present, and it taxed the facilities of the hotel to the utmost.

Jan 1, 1930

By P. Greenfield, C. C. Smith, A. M. Taylor

The Mg-Zr alloy ZA and Mg-Mn alloy AM503(S) are shown to have a markedly improved resistance to creep deformation after suitable heat treatments. This improvement makes them suitable for certain stress-bearing fuel element components in nuclear reactors. The extent of strengthening is described and an explanation of the behavior of both materials is given, based on a combination of strain-aging and grain growth. The increase in operating temperatures of fuel element components in Calder Hall type nuclear reactors has necessitated the development of magnesium base alloys with a very high resistance to creep at temperatures up to 500°C. Such alloys are not required for fuel element cans, which require high-creep ductility rather than strength, but for can supporting and stabilizing components, which are needed to support the imposed loads without deforming more than about 1 pct in times of up to 40,000 hr. The amount and type of alloying addition made to magnesium for these parts is limited by the necessity of keeping the cross-section to thermal neutrons as low as possible. The alloys must also possess a high resistance to oxidation in CO2. Alloys which have been developed for this application include ZA, an alloy of magnesium with 0.5 to 0.7 pct Zr and AM503(S), an alloy of magnesium with 0.5 to 0.75 pct Mn. In the as-extruded condition these alloys are very weak and ductile in creep but it has been found that they can be strengthened to a significant extent by heat treatment. This paper describes the method of developing a high-creep resistance in ZA and AM503(S), the extent of the strengthening produced and discusses the probable mechanisms of strengthening. TEST MATERIALS Specimens were taken from typical casts of ZA and AM503(S) alloys extruded into 2 1/4-in.-diam bars, supplied by Magnesium Elektron Ltd. Typical analyses of the bars were as follows: The as-extruded mean grain diameter was 0.001 to 0.002 in. for the ZA alloy and 0.003 in. for the AM503(S) alloy. EXPERIMENTAL METHODS Extruded bars of ZA alloy, 2 1/4 in. in diameter and 9 in. long, were heat treated in electrical resistance furnaces in an atmosphere of flowing CO2 containing 50 to 300 ppm water, thereby reducing the extent of oxidation compared with that which would have occurred in air. Heat treatments were carried out at 600oc for times of 8, 24, 48, 72, and 96 hr and material was subsequently both furnace cooled and water quenched. In order to measure the effect of time of heat treatment, specimens were creep tested at 400°C and 336 psi for about 1000 hr. Subsequently, the behavior of material heat treated for 96 hr at 600°C and furnace cooled was tested at a variety of stresses from 200° to 500°C. Tests were also conducted at 200o and 400°C on material in the as-extruded condition for comparative purposes. With the AM503(S) alloy, only the effect of heat treatment at 565°C for 4 hr was examined. It has been shown1 that such a heat treatment produces marked strengthening in this alloy. Tests on this material were conducted at a variety of stresses at 200°, 300°, and 400oc with comparative tests on as-extruded material at 200o and 400°C. The creep tests were carried out on machines using dead-weight loading and direct micrometer strain measurements on specimens 5 in. long and 0.357 in. diameter. At temperatures of 400° C and below, the creep tests were conducted in air, but at higher temperatures an atmosphere of CO2 was used. Grain size measurements were made on ZA in the extruded and heat treated states and on each specimen after creep testing. This was done by a line count of a minimum of 20 grains in two or three random fields in the longitudinal and transverse directions. The same method was used for measuring the grain size of as-extruded AM503(S), but the grain size of the heat treated material was so large that this method could not be employed. For heat-treated AM503(S) the large grained characteristics (between 0.1 and 1 in.) were confirmed by the measurement of individual grains. In the case of the ZA alloy, specimens taken from various stages in the program were analysed for hydrogen by a combustion method. Material in various states was also analysed for the soluble and insoluble zirconium content by dissolving in dilute hydrochloric acid. This technique has been useda for the determination of amounts of zirconium present

Jan 1, 1962

By R. I. Jaff, H. R. Ogden, D. J. Maykuth

A phase diagram for alloys containing from 0 to 66.9 pct Mn was determined. Two compounds, tentatively labeled 6 and y, were found in this range. The 6 compound is located at about 66.9 pct Mn and melts congruently at 1330°C. The ? compound has a composition near 53 pct Mn and originates in a peritectic reaction at 1200°C between liquid and 6. ß and Y enter into a eutectic reaction at 1175°C. The ß phase field terminates in a very sluggish eutectoid reaction between a and ? at 550°C. MANGANESE is one of the important alloying addition elements to titanium. As a ß-stabiliz-ing addition for a-ß and ß alloys, it provides high strength with adequate ductility.' Two of the earliest commercial alloys contain manganese as a major alloying component.' The earliest published data on the constitution of Ti-Mn alloys was that of Wallbaum,~ who reported the existence of the compound TiMn2. The transformation range of commercial-purity Ti-Mn alloys was investigated by Craighead, Simmons, and Eastwood' who found limited a solubility and a lowering of the ß transus to about 790°C at 7 pct Mn. Preliminary work by the authors of this paper, using high-purity titanium, confirmed the ß-stabilizing action of manganese and showed the existence of several intermediate phases in the Ti-Mn system." More recently, McQuillan3 determined the ß transus temperatures for high-purity Ti-base alloys containing up through 4.4 pct Mn. These data are given in Fig. 1. The present investigation covered alloys made with a high-purity base. The constitution of titanium-rich alloys made with commercial titanium has been reported4," by Holladay, Kura, and Jackson. The alloy range covered in the present investigation was from 0 to 69.5 pct Mn. This alloy range extends slightly beyond the composition of the first congruent-melting compound encountered on proceeding from the titanium end of the system. A description of the materials and methods used in the determination of the diagram is given in the Appendix. The partial phase diagram determined for the Ti-Mn system is shown in Fig. 2. Details on equilibria in the titanium-rich alloys are given in Fig. 3. Liquid-Solid Relationships Observations on the cast structures of the arc-melted ingots showed that the terminal solid solution of manganese in ß titanium enters into a eutectic reaction with an intermetallic compound labeled ?. As will be shown later, this compound has a composition around 53 pct Mn. The eutectic reaction temperature was determined as 1175°C by thermal analysis which also showed that the ? phase originates in a peritectic reaction at 1200°C. Fig. 4 shows typical eutectic structures for alloy compositions on both sides of the eutectic composition which is located at 42.5 pct Mn. In alloys over the range of 45.4 through 69.5 pct Mn, a second intermetallic compound, labeled 6, was identifield as the primary phase. This phase consistently increased in amount as the manganese content approached 66.9 pct, and, as shown in Fig. 5, an alloy structure containing 66.9 pct Mn consisted essentially of the 6 compound. Thermal-analysis data indicate a melting point of about 1330°C for the 6 intermediate phase. At 67.0 pct Mn, small quantities of a new, higher manganese-content phase were observed in the form of Chinese-script eutectic particles. Comparison of Fig. 6a and b shows an increasing quantity of this phase as the composition was increased to 69.5 pct Mn. The formation of peritectic ? in arc-melted alloys containing 45.4 pct Mn and above appears to be almost entirely suppressed, as shown in Fig. 7a and b. This is because of the narrow freezing range available for its formation by peritectic reaction and because of the very high cooling rates obtained in

Jan 1, 1954

By R. Grierson, R. N. Parkins

The m.echanica1 properties, at high lzomologous temperatures, of the intermetallic compounds InzBi and Mg17A112 were measured as a .function of temperature, applied strain rate, previous thermal and mechanical history, and composition. Mgl,Al12 was investigated ilz compression, whereas Zn,Bi was investigated in tension. A decrease inflow stress with increasing strain was observed jor both alloys. The results obtained are discussed in terms of the dislocation-multiplication processes in these materials. MANY intermetallic compounds are reported to undergo a brittle-ductile transition at high homologous temperatures.' There is evidence in the literature that some of these compounds exhibit a large yield drop when plastically deformed.'j3 Both of these forms of behavior are shown by the covalent elements germanium and silicon4,5 and also by certain ionic compounds.8 The present work is a study of the deformation, at high homologous temperatures (>2/3 Tm), of two intermetallic compounds, In2Bi and Mg17Al12. InzBi has a disordered hexagonal structure7 (c/a = 0.598) and a solubility range of 32.3 — 33.2 at. pct Bi.8 It has a melting range from 72° to 89°C. Mg17Al12 has an ordered bcc (A12 type)7 structure and exists over the range 50 to 60 at. pct Mg8 with a melting range from 437° to 462°C. We have been unable to find any reference to previous investigations of the mechanical properties of BiIn,. Novikovg has reported that cast samples of Mg17A112 show ductility, when bend-tested, at temperatures above 380°C. EXPERIMENTAL Ingots of In2Bi and Mg17Al12 were melted under an argon atmosphere and cast, in situ, in a graphite crucible. The materials used were of 99.99 pct purity. The alloys prepared contained 66.9 at. pct In in the case of In2Bi and 58.4 at. pct Mg in the case of m17A112. The ingots were homogenized and then extruded. Two-in.-diam Mg17Al12 ingots were extruded at 375°C to give 3/8-in.-diam rod. The rate of formation of this rod was 0.25 in. per min. One-in.-diam InzBi ingots were extruded at 20°C, using a rate of 1 in. per min, to give 1/8-in.-diam rod. In both cases the extruded rod had a recrystal- lized, fine-grain, structure. (For Mg17Al12, d = 11.2 µ; for BiIn2, d = 22 µ.) Mechanical-property determinations were made in a hard-beam machine, in tension in the case of In2Bi and in compression with Mgl7Al12. The tensile tests were on specimens having a gage length of 1.1/2 in. and a diameter of 1/8 in. The compression tests on Ml7A112 were on specimens of 3/8 in. diam by 3/8 in. high and the ends were coated with poly-tetrafluorethylene to minimize friction. RESULTS In2Bi. Fig. 1 shows, particularly at the higher applied strain rates, that In2Bi exhibits a marked yield drop as the deformation increases to about 2 pct, after which the material shows neither hardening nor softening up to 15 pct strain. The magnitude of the yield drop, the stress in the region of flow under constant stress (the stress plateau), and the 0.5 pct proof stress were all dependent upon the applied strain rate according to an expression of the form

Jan 1, 1965

"Power is transmitted to Butte, a distance of 130 miles, over two separate lines running parallel on the same right of way.The transmission line embodies the most approved ideas in construction. The conductors are No. O. B. & S. gauge, hard drawn copper strand. The insulators are of the suspension type, each insulator consisting of six units, 10 inches in diameter. The insulators will stand a wet test of over 300,000 volts, and were selected after long and careful tests by the company's engineers. The wires are carried on steel towers of four-legged, single crossarm type, manufactured by Milliken Bros. The three conductors are suspended in a horizontal row from the crossarm, and there are no transpositions in either line. Above the power wires and symmetrically located are two galvanized steel strands, Vs-inch in diameter, grounded at each tower, which serve as a protection against lightning.The distance between towers in level country is 600 feet. In mountainous country, however, the spans are irregular in length and spans of 1,500 or 2,000 feet are common. The longest one in the line is that crossing- the Missouri River and is equal to 3,034 feet. The length of this span is such that a person standing at one end of it can sec the wires go off and vanish into space, while the tower at the other end is barely visible to the naked eye on a clear day. The towers at one end of this span arc shown in the accompanying photograph. The line starts at an elevation of 3,200 feet, rises to an elevation of 8,200 feet as it crosses the Continental Divide, and again descends to 6,100 feet, the elevation at Butte.Quantity of coppc1· in transmission line, 1,330,000 pounds.Number of towers, 2,-1-00.Steel used in construction, approximately, 2,-1-00 tons."

Jan 1, 1913

By H. H. Klepfer, K. J. Gill, P. Chiotti

SOME observations relative to the U-Zn system have been made by other investigators. Chipman1 and Carter2 have reported the preparation of several U-Zn alloys and point out that these alloys are generally difficult to prepare. Chipman1 reported evidence for a high melting compound at about 90 atomic pct Zn and the possible existence of a eutec-tic between the compound and uranium. Raynor," in a theoretical discussion of the alloying properties of uranium, included zinc among the elements predicted to have little or no solubility in a, p, or y uranium. In the present investigation, thermal analyses, X-ray, metallographic, and vapor-pressure data were obtained to determine the phase boundaries. The relatively high zinc pressure over most of the alloys at temperatures of 900 °C and above proved troublesome and special techniques had to be employed in preparing suitable alloys. Materials and Preparation of Alloys The metals employed in this investigation were Ames Laboratory biscuit uranium containing less than 500 ppm total impurities and Bunker Hill slab zinc or Baker Analyzed reagent granulated zinc, both with a purity of 99.99+ pct. Due to the high vapor pressure of zinc and the high reactivity of both uranium and zinc with oxygen at only moderately high temperatures, alloys were prepared in closed containers which had either been evacuated or evacuated and filled with helium. High purity magnesia, magnesia containing 10 pct calcium fluoride, and tantalum proved to be suitable crucible materials. Tw-o different procedures, described below, were used to prepare alloys, the latter being the most satisfactory. The metals, uranium turnings and granulated zinc, were cleaned with dilute nitric acid, rinsed, dried, and placed immediately in a helium-fill'ed dry box. The two metals were placed' in a 10 mil Ta crucible. The charge was enclosed in the tantalum crucible by welding on a preformed tantalum cap. This assembly was enclosed inside a stainless steel (AISI 309) bomb. The bomb was made by welding a piece of stainless steel plate on each end of a stainless steel pipe. All these operations were carried out in a helium atmosphere. These assemblies were heated in a muffle furnace at temperatures between 1100" and 1200°C for 10 to 15 min or held as long as 15 to 20 hr in the 950" to 1000°C temperature range before quenching. Spectrographic and chemical analyses showed no tantalum pickup by the alloys, indicating no reaction between the alloys and the crucibles. However, some of these crucibles failed, probably due to imperfections in the welds of the stainless steel or tantalum crucibles. The second and most satisfactory method was to prepare the alloys by powder metallurgy techniques. The procedure was to press degreased and acid-etched uranium turnings with granulated zinc into 20 g compacts under 20,000-psi pressure. The compacts were placed in MgO crucibles, and sealed in evacuated Vycor or fused silica tubes. The alloys were then heated as long as two weeks at about 550°C in a muffle furnace. The pressed compacts were observed to expand by several volume percent during heating and it was necessary to make allowances for this expansion in order to avoid breaking the crucible and Vycor tube. This method was found very satisfactory for preparing alloys which were suitable for thermal analysis or vapor pressure studies. Experimental Methods and Results The phase diagram for the U-Zn system at 1 atrn pressure, shown in Fig. 1, is based primarily on vapor pressure measurements and on thermal analysis taken at temperatures below 950°C. Fig. 2 shows the U-Zn diagram at 5 atrn pressure, constructed on the basis of thermal analysis of alloys in sealed containers up to 1150°C and on the basis of metallographic, X-ray, and analytical data. The alloys sealed under vacuum were actually under their own vapor pressure and those sealed in an atmosphere of helium were under an additional pressure due to the helium. At temperatures up to 1100°C the zinc pressure is 5 atrn or less for these alloys; consequently the maximum pressure over the alloys sealed under a helium atmosphere was 10 atrn or less at temperatures up to 1100°C. Changes in pressure of this order of magnitude do not appreciably alter the position of most solid-solid or liquid-solid phase boundaries. In constructing the phase diagram for a pressure of 5 atm, the effect of pressure on all phase boundaries except those for liquid-vapor or solid-vapor regions was considered negligible.

Jan 1, 1958

By V. Leroy, A. G. Guy

Serious disagreements are often found between experimentally determined intrinsic diffusion coefficients and those calculated employing the usual form of the vacancy theory. In the new theory it is proposed that the total intrinsic flux, Ji, of component i, is the sum of a part, f, due to the usual random exclzanges of component i with the vacancies, and a second part, Ji, due to exchanges with the uacancies composing the net vacancy flux. The present treatment, while less powerful than that of Manning, has the advantage of easy uisualization and of facilitating the application of the vacancy-flux effect to complex systems. IT is becoming increasingly evident that there are serious deficiencies in the version of the vacancy theory of diffusion that has been widely used for the past 20 years. One type of evidence is the frequent lack of agreement between intrinsic diffusion coefficients and tracer diffusion coefficients, even taking account of the thermodynamic factor. A second kind of evidence is the observation of a Kirkendall shift larger than theoretically possible, that is, larger than can be accounted for without assigning a negative value to one of the two intrinsic diffusion coefficient.'- The thermodynamic factor could conceivably make both coefficients negative, but not just one. It is clear that a cause of these anomalies, apart from any inadequacy of the usual vacancy theory, might lie in an oversimplified treatment of the data. Adequate experimental techniques, including the use of moderate pressure during the diffusion anneal, are now available to insure that porosity, lateral expansion, and so forth, can be kept negligibly small in most cases. The effect of differences in atomic volume can be of major importance, and it is essential that one of the available methods4 be used to account for this factor. In the present treatment this is accomplished by the consistent use of moles per cubic centimeter as the unit of concentration. Of the various possible inadequacies of the vacancy theory, attention will be given here only to effects of the net vacancy flux. annin' has previously considered this question, beginning with an analysis of atomic jumping of tracer atoms. When he added the effect of a concentration gradient, new terms arose that could be associated with the flow of vacancies. The present treatment uses quite a different approach. The usual vacancy flux, J,, is introduced explicitly, and a simple analysis predicts major changes in the intrinsic diffusion coefficients from this cause. The usual assumptions are made that only a vacancy mechanism is operative, that the formation of voids can be neglected, and that changes in the partial molal volumes, vl and v2, are negligible. The significant diffusion coefficients for the present topic are Dl and D,, the intrinsic coefficients, which enter in the equations, where the flux Ji, moles per sq cm per sec, is that crossing the Kirkendall interface. The concentration, ci, is in units of moles per cu cm, and the concentration gradient, aci/ax, is evaluated at the Kirkendall interface. It will be recalled' that the calculation of Dl and D2 involves the measurement of areas on the diffusion curve with respect to the positions of the Kirkendall and Matano interfaces. In the case of the anomalies mentioned earlier, the Kirkendall shift is too large to be accounted for by the diiferetzce in fluxes (J2 -J1), given by Eqs. [I] and [2]. The logical inference is that the flux of the solvent atoms, J1, is actually in the same direction as the flux of the solute atoms, Jz. In terms of Eq. [I] this requires that Dl have a negative value. However, it would be somewhat misleading to state that the solvent atoms are diffusing up their own concentration gradient. The explanation that will be advanced here pictures competing processes producing the net flux of solvent atoms: 1) diffusion of the solvent atoms down their own gradient by random exchanges with vacancies; and 2) diffusion of solvent atoms in the opposite direction by exchanges with the net vacancy flux. ACTION OF THE NET VACANCY FLUX Theories of vacancy diffusion can be formulated with varying degrees of refinement, and the present theory has purposely been kept as simple as appeared adequate to explain the phenomenon in question. In particular the following aspects have been neglected: 1) the gradient of vacancy concentration in comparison to the gradient of the atomic species; 2) departure of vacancy concentration from the local equilibrium value; 3) variation of the jump frequency, LO, with the specific surroundings of the atom-vacancy pair being considered; 4) correlation effects. These and other refinements can be considered once the essential mechanism has been established. The essential idea of the present analysis is to calculate the total intrinsic flux, Ji, of component i as the sum, JlJ?±j{ [3] where J; is attributable to the usual random atomic jumping, and J{ is a contribution arising from the net vacancy flux, J,. The latter quantity, of course,

Jan 1, 1967

By J. L. Brimhall, R. A. Huggins, M. J. Klein

IN a recent paper1 it was shown that small additions of magnesium, copper, and oxygen decrease the stacking fault probability in plastically deformed silver. Correlation of :X-ray data with measurements of the twinning frequency and metallographic observation of slip lines indicated that this effect may be due to an increase in the relative stacking fault energy. It is the purpose of the present note to report experiments on these alloys of known stacking fault probability that relate to the stacking fault contribution to electron scattering in silver. There has been a considerable amount of disagreement in the literature concerning the contribution of dislocations to electrical resistivity in metals. Calculations relating to the scattering of conduction electrons by the dislocation core, its strain fields, and related effects have been made by several authors.2-5 In addition, experimental work on Cu,3,6-10 Ni,11 and Ni-Co alloys1:! has shown that dislocations in those materials exert an anomalously large effect on resistivity, this effect being related to the presence of extended dislocations. The problem of the scattering due to the stacking fault region between partial dislocations has been treated theoretically using several different procedures.13-'0 The results of these calculations show a wide range of predicted values, from rather large to completely negligible, due to the models and the approximations involved. Almost all of this work has been applied to the specific problem of scattering in copper. The more complete theoretical treatments depend rather critically. on the shape of the Fermi surfaces and the effective mass parameters. The scattering from stacking faults might therefore be expected to vary significantly from one metal to another. Unfortunately, sufficiently accurate information is not available .which would allow one to have any confidence in a theoretical prediction of the scattering in the case of silver. Resistivity measurements were made on small wire specimens of vacuum melted high purity silver and several dilute alloys. These measurements were made at approximately 20°C, with great care being given to temperature measurement and corrections. At such temperatures phonon scattering is significantly greater than imperfection scattering. However, the experimental technique was such that measurements on similarly treated samples were reproducible to better than 2.4 X 10-9 ohm-cm, which was satisfactory for this work. Values of the stacking fault probability and the increase in resistivity after severe plastic deformation are given in Table I. The increases in resistivity resulting from plastic deformation agree quite well with previous work on silver.14,21-26 In addition, it has been previously found that interetitials and vacancies in silver anneal out well below room temperature, so that the residual imperfection scattering in these experiments could be expected to be primarily associated with dislocations;. It is seen from the data in Table I that large changes in stacking fault probability are accompanied by differences in resistivity due to imperfection scattering of only a few percent. If the scattering of conduction electrons by extended dislocations is primarily due to the area of the stacking fault region independent of the stacking fault energy, and not the core and strain fields associated with partial dislocations, the resistivity increase should be proportional to the product of the dislocation density and the stacking fault width, as is the stacking fault probability. Therefore, the imperfection scattering caused by plastic deformation of the alloys should be considerably smaller than that found in the pure silver. Since this was not observed, these results sugegest the possibility that stacking faults do not themselves contribute appreciably to the electrical resistivity of silver deformed at room temperature. An alternative explanation of these observations is that the scattering by the stacking fault is roughly proportional to the stacking fault energy, rather than being determined by the total area of such faults. Sufficient evidence is not yet available to separate these two possibilities. This work was supported by the Office of Naval Research.

Jan 1, 1962

By George Stern

The purpose of this investigation has been to study one method for making ordinary carbon steel by the powder metallurgy technique. This method con- sists of pressing and subsequently sintering an intimate mixture of iron powder and gaphite in a suitable atmosphere to Produce a steel. Two types of iron Powder have been studied, electrolytic and reduced. The sinkring of mixtures of loose Car-bonyf iron and carbon black for several hours at I000 to 1100 C. (1830' to 2010°F.), followed by forging of the resultant ingots to bars, has been studied by Offermann.' TrailZ has reported on the properties of hydrogen-reduced and electrolytic iron powders, both containing 0.5 per cent carbon. Methods for making steel bodies by powder metallurgy have also been sug- gested by Goetzel13 who recommends the addition of steel powder of well-defined carbon content to pure iron powder, and Volterra,~ who suggests compaction and subsequent sintering of a mixture of steel powder, iron oxide and iron powder. Additional methods for making steel bodies by powder metallurgy have been reported in the literature by Kohering Allen,6 Balke,7 Wulff,8 Boegehold,9 and others.,0,11,12 It is felt that the method of pressing iron powder and graphite, as described herein, lends itself best to production be-Cause of the lubricating action of the

Jan 1, 1946