Search Documents

By Jiang Diao, Yong Qiao, Xuan Liu, Tao Zhang, Bing Xie

The equilibrium experiments between the FeO-SiO2-MnO-TiO2-V2O3-Cr2O3-MgO slag system and solid pure iron were performed to investigate the vanadium and chromium distribution ratio under Ar atmosphere. The influence of w(FeO), w(V2O3) and w(Cr2O3) in slag on vanadium and chromium distribution ratios were studied at 1653 K. The experimental results were compared with calculated distribution ratios based on molecule and ions coexistence theory. Both of them showed that higher FeO content in slag would improve the distribution ratios of V and Cr between slag and hot metal. The distribution ratio of Cr or V increased with the increase of Cr2O3 or V2O3 content, respectively. To optimize the oxidation of V and Cr from hot metal, a high oxidizing slag and suitable content of Cr2O3 and V2O3 in the slag were recommended. The results provided reference for the further study on the extraction of V and Cr in VTi magnetite.

Jan 1, 2016

By N. J. Tannyan

Laboratory bath smelting tests were conducted to determine the feasibility of smelting nickel- copper concentrate directly to a low iron matte in one step. Concentrate, air/oxygen and a silica flux were fed to a matte-slag bath kept in MgO crucibles at I 300°C. Various oxygen enrichments and smelting rates were used to maintain 0.5 to 2 wt% iron in the product matte. The slag losses are comparable to those obtained under similar industrial conditions. Due to the highly oxidizing conditions required to produce mattes with low iron contents, it is not recommended to target iron contents below about 2% in the matte. The specific bath smelting rates were equal to or higher than those in various industrial bath smelting processes.

Jan 1, 2003

By T. A. Larssen

The efficiency in production of manganese ferroalloys is dependent on the gaseous reduction of the higher manganese oxides in the ores used as raw materials. The materials, descending in the furnace, will meet the furnace gas that contains significant amounts of CO(g) and reduce in subsequent steps, the last step being reduction of Mn3O4 to MnO. This step may to varying extent occur at temperatures exceeding 800 °C, i.e. in the active region of the Boudouard reaction. The gas reduction of Assmang and Comilog manganese ores were investigated in CO-CO2-atmosphere at temperatures up to 1000 °C. It was seen that decreasing ore size correlates to a lower reduction temperature and increasing reduction rate. Similar effect was observed with increasing CO-content in the gas atmosphere. Further, it was found that Comilog ore obtained a complete prereduction at 600 °C, whereas reduction of Assmang ore was not complete at 800 °C for the majority of the experiments.

By Chonghe Li, Pengyue Gao, Xionggang Lu, Juyun Kang, Wajid Ali, Guangyao Chen, Ziwei Qin

A refractory U–Mo associated ore containing jordisite which enclose U, Mo component, and impede penetration, diffusion process of leaching, oxidation agent was investigated through three approaches of focusing on U, Mo extraction. The results indicate flotation beneficiation without followed metallurgical process is not appropriate because of high target metals loss rate via water leaching. H2SO4, H2O2 dosage recommended to oxidation leaching are 10 and 6–8% of ore mass, and U, Mo leaching rate are 92.71 and 52.16% respectively. For the acid pressure leaching, U, Mo leaching rate 93.75 and 76.07% are achieved under optimal temperature 130–140 °C and H2O2 dosage 8% combined with pressure air 0.6 MPa. Fluidized bed furnace roasting parameters include air flow rate 0.64 m/s, air ore ratio 0.3 m 3/kg at roasting temperature 550 °C with U, Mo leaching rate 93.2 and 89.5%, so enhanced metallurgical process effectively destroy wrapper and increase metal recovery rate.

Mar 1, 2018

By Zhuokun Cao

Manufacture of aluminum foams still suffer from nonuniformity and poor reproductively for there is lack of basic knowledge of foaming process. In this paper, carbon fibers are used as novel stabilizing additive for aluminum foams, and the structure evolution of aluminum foams with different fiber content was studied. A laser rangefinder was used to detect the expansion rate of different al foams. Al foam samples are solidified at different foaming time to determine its relative density and cell size distribution. Results indicate that the cell size of foams linearly increases with the decrease of density, and the slope of the line is influenced by fiber content. The relationship between expansion ratio, density and cell size of the foams is discussed. It is concluded that the density of resulting foam is influenced by the rate of gravity driven drainage, and its cell size is determined by expansion ratio and foaming time.

Jan 1, 2010

By Z. Zhang, Zongshu Zou, Nan Wang

"Thermodynamic calculation is applied to make an investigation on the equilibrium phase relations and liquids of CaO-SiO2-Al2O3-FeOx system for different temperatures. The calculated results with FactSage6.1 show that the effect of temperature on the the equilibrium phase relations and liquidus of CaO-SiO2-Al2O3-FeOx system and its sub-systems is appreciable. The liquid phase regions enlarge with increasing temperature from 1573K to 1873K, while the primary phase fields reduce distinctly.IntroductionThe main oxide components of vitrified bottom ash slag are CaO, Al2O3, SiO2, Fe2O3, MgO, and Na2O, accounting for more than 90% of the bottom ash by weight[1]. During slag processing, the knowledge of thermodynamic properties and liquidus temperature in the related slag systems is highly required [2, 3], which is not yet available. Through literature survey [4-6], it is clear that the systematic information on the concerned complex slag system is scarce. So far the engineers in the field have to make assumptions of the thermodynamic properties of the simplified oxide system, without taking into consideration the interactions of the different oxide components, which hinders the development of the slag valorization and utilization. In order to provide thermodynamic properties for the application of the vitrified bottom ash, the six-component oxide system (CaO-MgO-Al2O3-SiO2-FeOx-Na2O) is highly required. A preliminary phase diagram of the CaO-MgO-Al2O3-SiO2-FeOx-Na2O system can be obtained from extrapolation of the thermodynamic functions of constituent subsystems such as CaO-SiO2-FeOx-MgO, CaO-SiO2-FeOx-Al2O3, CaO-SiO2-Na2O-MgO and CaO-SiO2-Na2O-Al2O3. In this work, the equilibrium phase relation and liquidus of CaO-SiO2-FeOx-Al2O3 system, one subsystem of the concerned complex slag system, are calculated and the effect of temperature is also discussed."

Jan 1, 2012

By ZHANG Ting

In view of the high consumption and contamination of traditional vanadium extraction technology, a new process of leaching the converter vanadium slag without roasting with titanium dioxide waste was proposed. Extraction mechanism of P204 in the leaching solution had been researched and single factor experiments show that after a prereduction of Fe, and under conditions: ambient temperature，leaching solution original pH=2.5, phase ratio (A/O)=1:3, shaking time 8min, the extraction rate of V is more than 98.62% meanwhile the separation rate between V and Fe is up to 135.3 in the 20%P204-10%TBP-Sulfonated kerosene extraction system.

Jan 1, 2015

By Hwasoo Park

Keywords: FC mold, Argon, Magnetic, Solidification Fluid flow plays a significant role for steel surface quality in continuous casting. Although water models are able to model fluid flow, the flow pattern is not of practical interest since the moving solidifying shell cannot be accounted. Computer modeling has become a popular and dependable tool to analyze the complex phenomena occurring in continuous casting. In this numerical simulation we coupled momentum and energy equations considering the solidification of steel along with turbulence ?-e model. The vertical bending mold is equipped with bifurcated nozzle with 15 degrees of port angle. FC mold is supplied with DC induced magnetic fields. Influence of argon and magnetic fields on molten steel flow and heat transfer is investigated by solving momentum equations adding source terms due to multiphase ? magneto hydrodynamics. The results show that magnetic fields reduce the jet velocity from port by lower magnetic core induced field but the influence on meniscus velocity is complex to describe. Magnetic fields increase surface temperature and homogenize its distribution on surface and inside a mold.

Jan 1, 2005

By Pengfu Tan

A thermodynamic model of KIVCET lead smelting process has been developed. The model has the capability to predict the distribution behaviors of Pb, Zn, Fe, S, O, As, and heat balance in KIVCET direct lead smelting furnace. The compositions of lead bullion, matte, slag and gaseous phases, and heat balance are calculated. The effect of the ratio between oxygen and feed on the chemistry of the smelt and heat balance of the coke checker has been simulated and discussed. The thermodynamic model also helps to understand the tapping issue of the lead bullion. In this paper, some applications of this model in the industry have been presented.

Jan 1, 2006

By B. Farouk, D. Apelian

"A numerical model has been developed to predict the temperature history of particles injected in a low pressure d.c. plasma jet. The temperature and velocity fields of the plasma jet are predicted as a free jet by solving the parabolized compressible Navier-Stokes equations using a spatial marching scheme. Particle trojectories and heat transfer characteristics are calculated using the predicted plasma jet temperature and velocity fields. Correction factors have been introduced to take into account non-continuum effects encountered in the low pressure environment. The plasma jet profiles as well as the particle/plasma interactions under different jet pressure ratios (from underexpanded to overexpanded) have been investigated.I. IntroductionIn the plasma spraying process a d.c. plasma jet is used as a heat source to melt and accelerate powder particles which subsequently impinge and solidify on a given substrate. During low pressure plasma deposition (LPPD) prooess, the plasma jet is expanded into a low pressure environment (40-80 Corr) which results in high plasma jet velocities with Mach numbers ranging from 2 to 3. Previous efforts to predict heat transfer and fluid flow in plasmas have made use of incompressible flow formulation employing turbulence models [1-3] for atmospheric plasma spraying. However, these theoretical calculations have been limited to the subsonic flow regime; hence, the compressibility effects and viscous heat dissipation were neglected. In the LPPD process, the plasma jet is operated at the supersonic flow regime, therefore, the compressibility effects and viscous heat dissipation are no longer negligible. This is the main motivation of this work.In addition, production of high quality dense deposits requires that a large fraction of the injected particles be in a molten state when they impact the substrate. An additional motivation for this work is that it is important to understand the plasma/particle heat and momentum transfer since these phenomena dictate both the particle thermal history and particle trajectory.Early computational works in supersonic nozzle field flow [4,5,6] consisted of patching methods that divided the flow field into an invisoid free stream and a viscous boundary and. mixing layers. Each was analyzed independently and coupled through appropriate boundary conditions. Later schemes [7,8] involved solving time-dependent, compressible Navier-Stokes equations over the entire computational domain. These schemes show a great promise in predicting flows with complex structure, and where the viscous effects became prevalent."

Jan 1, 1986

By M. Brian Maple

A rich variety of phenomena are produced by superconducting-magnetic interactions in rare earth and actinide compounds. These phenomena, and the materials in. which they have been observed, are described in this talk, with an emphasis on the new high superconducting transition temperature (Tc) copper oxides. The Materials The-materials in which these phenomena occur can' be divided into two classes. In the first group, there are two distinct interpenetrating systems of electrons, a set of localized 4f or 5f electrons and a set of itinerant electrons. The localized f electrons carry magnetic moments and interact with the spins and momenta of the the itinerant electrons, which are involved in the superconductivity, via exchange and electromagnetic interactions; respectively. This category includes materials containing rare earth (R) and actinide elements with partially-filled f electron shells which have been inroduced as substitutional impurities [e.g., La1-xCexA12, Th1-xUx] or form a sublattice in compounds [e.g., RRh4B4, RMo6S8, RMo6Se8, the high Tc. superconductors RBa2Cu3O7-d(d - 0.05)]. Materials of the second type are characterized by a single band of electrons that is responsible for both superconductivity and magnetic order. This group includes heavy electron rare earth and actinide compounds [e.g., CeCu2Si2, UBe13, UPt3, URu2Si2], and the high Tc copper oxide superconductors such as the hole-doped systems Lag- MxCuO4 (M = Ca, Sr, Ba, Na) and RBa2Cu3O7-d(0 =d= 1) and the electron-dope system Ln2-xMxCuO4-y (Ln = Pr, Nd, Sm, Eu; M = Ce, Th; x = 0.15; y - 0.02).

Jan 1, 1992

By Won C. Park

Experiments showed changes in the mineral content of dolomitic oil shale at temperatures and exposure times which bracket conditions encountered during in situ retorting. Laboratory results correlate with cores from a spent in situ retort at Occidental's Logan Wash test site at Garfield County, Colorado. Dolomite, CaMg(CO3)2, decomposes rapidly to form periclase, MgO, calcite, CaCO3, and CO . Both calcite and periclase are intermediate products that can be stabilized by CO atmosphere at lower temperatures, while steam accelerates the formation 2 of silicates. The decarbonation of calcite appears to involve a direct reaction with both quartz and periclase in forming these silicates. Decarbonation preceeds the formation of akermanite, Ca2 MgSi 207, and diopside, CaMgSi 206, within several hours of heating and is followed by the nucleation of forsterite Mg2SiO4, and monticellite, CaMgSiO4. Under in situ retorting conditions, akermanite and diposide are the major minerals above 800°C. Equilibrium is not attained within 200-300 hours. In situ retorting temperatures above 800°C for extended periods of time should reduce potential ground water leaching by the formation of silicate minerals. These silicates are less soluble than free lime, magnesium or alkali oxides. There is a corresponding decrease in the natural pH of these silicates from approximately 12 down to 7.5 to 9:

Jan 1, 1981

By A. René Silva

The separation of Fe(III) from simulated Ni(II) solutions using different ion exchange resins was studied. The resins tested included cation exchangers with sulfonic and carboxylic groups and chelating resins with iminodiacetic, aminophosphonic, and mixed sulfonic and phosphonic groups. The dosage of resins was varied from 0.1 to 0.5 g/mL to study the impact of resin type and dosage on iron separation from simulated nickel leach solution containing 25 g/L Ni(II) and 25 g/L Fe(III) at pH 1.5. Also, the effects of different metal ion concentrations, Fe (III):Ni(II) ratios in solution, pH, and adsorption times were investigated. Experimental results demonstrate that all the chelating resins selected favored the adsorption of Fe(III) over Ni(II) with high Fe(III) loading. Soft cation exchange resins also favored the adsorption of Fe(III) over Ni(II), but no significant Fe(III) loading was observed. In contrast, strong cation exchange resins did not show adsorption preferences. The most efficient separation was observed using resin with aminophosphonic groups at resin dosage of 0.2 g/mL, having a Fe(III) adsorption over 94% and Ni(II) adsorption below 5%.

By Huyang Xie, Rishi Raj, Vera A. Versteeg

"A new method for MOCVD has been developed in which a precursor solution is directly injected into a reaction chamber. The vaporization of short pulses of liquid is facilitated by atomization with a piezoelectrically-operated nozzle. The system has been used successfully to grow oriented, thin Ti02 (rutile) films on sapphire substrates with the crystalline relationship (101)[010]R I (1120)[0001]s. A growth rate of approximately 2 monolayers per pulse was achieved at 650°C for a reactant impingement rate of about 800 monolayers per pulse. Also, epitaxial LiTaO3 thin films were grown on (0001) sapphire from a single source, bimetallic precursor, lithium tantalum hexa-t-butoxide as the precursor. X-ray diffraction shows that the LiTaOa c-axis is normal to the sapphire surface. The x-ray pole figure and crosssection TEM diffraction show that the films were also in-plane oriented, with sapphire [1010] parallel to lithium tantalate [1010]. These films are shown to have extremely low optical attenuation, and refractive index that compares well with bulk values.IntroductionMetalorganic chemical vapor deposition (MOCVD) techniques have come into increasing use in recent years, due to the growing versatility and availability of precursors and improved environmental advantages over the halogenated compounds used for conventional CVD. Most commonly, the films are deposited by dissolving the metalorganic reactant (typically a metal alkoxide) in a carrier gas, which is carried through heated lines to a heated substratel . The metal alkoxides decompose by pyrolysis, leaving the films on substrates. While this method has been used to produce excellent epitaxial and heterepitaxial films, it has the disadvantages of complexity: the precursor must be heated to fix its vapor pressure, the gas flow rate carefully controlled, and the carrier lines heated to prevent condensation before reaching the reactor. Additionally, this conventional method cannot be used with certain low-volatility precursors that decompose upon heating."

Jan 1, 1994

By Xiangwen Wang

Electrochemical measurements associated with the electrowinning of lead metal from concentrated brine (NaCI) - lead chloride (PbCI,) electrolytes at temperatures in the range 328 to 353°K (55 - 80°C) were conducted. The electrodeposition of lead metal onto a lead rotating-disk electrode may be described by the electrodic reaction: {PbCl 4 2 + 2e- = Pb° + 4Cl-} The deposition-overpotential requirements are low (approximately 41mV per decade of current density - Am+), with a corresponding high exchange current (approximately 0.018 A.cm2). The diffusion coefficient of the electroactive PbC142- species in a 3.5 NaCl electrolyte at 353°K was insensitive to the total PbCI, concentration (0.01 to 0.1M), and its value was found to be (1.21*0.1)~10-5 cm2Is with a temperature-sensitivity coefficient (E,/R) of approximately 1.98x103K-1 (328OK(T<353OK).

Jan 1, 1993

By Wang Zhi

High-Mg-content concentrates are usually treated in Jinchuan flash smelting Furnace. Because the viscosities of high-Mg-content slag is very high, the operation of flash smelting becomes very difficult. To solve this problem, the viscosities of the semi-synthesized FeO-MgO-SiO2 slag of different compositions were measured. The results showed that when in the slag the weight percentage of MgO [w(MgO)] is 6-10%, the ratio of the weight percentage of iron to that of Si02, w(Fe)/w(Si02) is 1.1-1.4 and the temperatures are within 1473-1773K, the slag viscosities increased with the increase of W(MgO) and w(Fe)/w(SiO,). When w(Mgo)<6%, the smelting temperature should be controlled at I 300°C in order to to keep the smooth operation. When w(MgO)>10%, the temperature should be kept above I 633K. When the content of MgO is higher, a lower viscosity slag can be produced by decreasing the ratio of w(Fe)/w(SiO,). The appropriate ratio of w(Fe)/w(SiO,) for Jinchuan flash smelting furnace is about 1.2.

Jan 1, 2003

By Fumitaka Tsukihashi

Phase diagrams of the CaO-SiO2-FeOx-MgO, Al2O3 systems arc necessary for the analysis of copper smelting reactions and sintering process of iron ore. The effect of MgO and Al2O3 addition on the liquidus of the phase diagram of the CaO-SiO2-FeOx system at low oxygen partial pressure was observed. The liquid phase area changed bi the addition of MgO and Al2O3 with a changing oxygen partial pressure from 10-8 to 10-3 atm (10-3 to 10 2 Pal at 1573K. The effect of Fe3+ / Fe2+ ratio on the melting mechanism is discussed.

Jan 1, 2003

By Guiming Yang, Xiaoxian Huang, Zhiyun Ji, Min Gan, Lishun Yuan, Xiaohui Fan, Zhiyuan Yu

"The roasting characteristics of hematite pellets containing MgO were studied where magnesia powder, serpentine and magnesite were used as magnesium-additives respectively. The mechanical strength of both preheated and roasted pellets decreased when MgO content increased, which implied the addition of MgO had an adverse effect on pellet consolidation. By adding flux containing CaO, the mechanical strength of both preheated and roasted pellets were improved. The addition of calcium flux facilitated the formation of calcium ferrite and provided a certain amount of liquid phase, resulting in faster diffusion ofMg2+ and Fe3+. The result showed that diffusing speed of Mg2+ was enhanced by 1.48 times, and rate constant of Fe203 crystalline growth was enhanced by 62% when basicity was around 0.4. Improvement of mineralization degree and recrystallization of Fe203 assisted in consolidation of hematite pellets containing MgO.IntroductionOxidized pellets are ideal iron-bearing burdens in blast furnace. At present, magnetite is the main raw material for oxidized pellet production in China. However, as the rapid development of iron and steel industry, resources of magnetite have been depleted and cannot satisfy the requirement of pellet production. Using hematite concentrates to produce oxidized pellets has become a trend [1, 2]. Many pellet enterprises abroad nowadays have adopted high proportions of hematite concentrates when producing oxidized pellets, e.g. the percentage is 100% in a lot of Brazilian factories [3, 4]. But high proportion of hematite concentrates will lead to low mechanical strength and high reduction swelling index of pellets. Some studies show that Mg-bearing pellets have excellent metallurgical properties, and the reduction swelling phenomenon can be solved by adding fluxes containing MgO [5, 7]. However, there are problems such as low pellet strength and bad roasting characteristics for MgO-bearing pellets, which remains an obstacle in pellet industry. Hence, it's vital to undertake the study on strengthening measures for indurations of Mg-bearing hematite pellets."

Jan 1, 2013

By W. C. Chang

Phases and magnetic evolutions of melt spun Nd9.5(Fe1-xCox)85.5B5 (x=0, 0.05, 0.1 and 0.15), (Nd1-yLay)9.5Fe85.5B5 (y=0, 0.0.5, 0.1; and 0.15) and (Nd0.95La0.05)9.5(Fe1-zCrz)81.5B9 (z=0, 0.033, 0.067 and 0.1) nanocomposites: have been investigated. It was found that a. dilute Co substitution for Fe, x=0:05-0:15, in Nd9.5(Fe1-xCox) 85.5B5 improved not only Curie temperature but also the remanence and maximum energy product. Partial substitution of La for Nd in(Nd1-yLay)9.5Fe85.5B5 may suppress the grain growth of the materials during thermal treatment. Exchange coupling between the Nd2Fe14B and a-Fe was found: to increase with increasing La content. A dilute La-substitution, y=O. 10, has proven to decrease the optimum wheel speed required for preparing melt spun ribbons with better magnetic properties; Furthermore; a slight substitution of La for Nd in (Nd0.95La0.05)9.5(Fe1-xCrx)81.5B9 nanocomposite reduced the crystallization temperature of the over-quenched ribbons and led to the formation of a multiple phases mixture. Nevertheless, a dilute Cr addition increases the Tg of (Nd0.95La0.05)9.5(Fe1zCrz)81.5B9 and also suppresses the formation of the undesired (Nd,La)2Fe23B3 and Fe3B phases: Cr was found to play an important role in grain smoothening or magnetic separation which consequently increased the Hc of Cr-containing materials.

Jan 1, 1997

By Reinhard Bott

The Companhia Mineira de Metais (Brazil) runs a Zn-recovery plant in Tres Marias, federal state Minas Gerais, Brazil. The Zn-production is about 65,000 t/a, This corresponds to a concentrate throughput of about 255,000 t/a with a Zncontent of about 29.5 % at an output of 85 %, The plant is run continuously 360 d/a and 24 h/d, respectively. From this it can be concluded that: Input: approx. 650 - 700 t/d ore-concentrate and approx. 29 t/h ore-concentrate, respectively.

Jan 1, 1990