By John M. Kelly

New Mexico produced 39,475,388 bbl. of oil in 1944, the greatest amount in one year in the oil history of the state. This production was 593,046 bbl. or 1.25 per cent more than in 1943. New Mexico retained its position as the seventh largest oil-producing state. The maximum per well allowable on Jan. I, 1944 was 48 bbl. daily and at the end of the year it was 45 bbl. daily. Allocations as set by the New Mexico Oil Conservation Commission closely followed the recommendations made by the' Petroleum Administrator for War. The average daily pipe-line runs were within 4 per cent of the allocation. Production by counties was as fol1ows;Lea County, 33,509,548 bbl.; Eddy County, 5,504,498; Northwestern New Mexico 461, 342. Drilling activity for New Mexico in 1944 was well above that of 1943, with 362 completions. Of these, 283 were oil wells, 12 gas wells and 67 dry holes. The ratio of dry holes to producers, about I to 4, was an improvement over 1943. Wildcat drilling during 1944 was responsible for the discovery of six new fields and the extension of two present producing areas. Drilling records were established in New Mexico during 1944 with the deepest producer ever completed, the Humble Leonard Oil Company's No. I at 11,969 ft., in the Ellenburger section of Ordovician age near Jal, Lea County. The discoveries in Lea County during 1944 were as follows: West Lovington field, where Fred Turner, Jr. drilled his No. I State B .in C SE SW sec. 4-17-36 and completed it for 122 bbl. of oil in 8 1/2 hr., in the San Andreas section of Permian age. The Tonto field, where the T-exas Company completed its No. I Baskin at a total depth of 3586 ft. in Seven Rivers lime of Permian age, with an initial production of 254 bbl. of oil in 21 hours. The Drinkard area, where the Gulf Oil Corporation's Drinkard No. I flowed 782 bbl. of oil in 14 hr. from the Yeso section of lower Permian age, thus opening the first lower Permian production in the state. The total depth of this discovery was 6508 ft. and oil was 38.8" A.P.I. gravity. The Dublin area, where the Humble Oil and Refining Co. established a drilling depth record of 11,969 ft. drilling and completing its No. I Leonard Oil Co. well in the Ellenburger lime of Ordovician age. This well flowed 221 bbl. of oil per day, of 48.9º A.P.I. gravity oil. It is in sec. 12-26-37. The new pay horizon discovery of the Continental Oil Co. in the Skaggs area, where the company completed its Skaggs B-23 No. 2 in sec. 23-20-37 for 236 bbl. of oil in 21 hr. from the Wolfcamp section of lower Permian age, at a total depth of 7725 ft. This well was drilled to granite at 10,465 ft. and plugged back to the Wolf-camp for a new pay zone completion.

Jan 1, 1945

By Theodore B. Counselman

Of all natural resources, iron ore made into steel is the most important both in tonnage and value. The primary reason for the prosperity of the United States in the last century has been its pre-eminence in domestic supplies of iron ore and steel. The depletion of these reserves by two world wars and by the demand for richer blast furnace charges, as well as the constantly growing world- wide demand for steel, has fostered the recent quest for new iron ore mines around the globe. These developments have made a dramatic change in the iron ore picture of the world. It is the purpose here, however, to look briefly at the development of the United States iron ore industry, which has played such an important role in the events leading to the modern day boom in iron ore exploration.

Jan 7, 1965

The Committee on Nominations begs to submit the following names as its nominees for the respective offices indicated: For President, SIDNEY J. JENNINGS, New York. For Vice-Presidents, WALTER H. ALDRIDGE, New York; MARK L. REQUA, San Francisco. For Directors, J. E. JOHNSON, JR., New York; ALLEN H. ROGERS, Boston; HOWARD N. EAVENSON, West Virginia; ROBERT M. RAYMOND New York; WILLET G. MILLER, Canada.

Jan 12, 1916

AMERICANIZE THE MINING INDUSTRY Americanization is the snaking of American citizens; men and women controlled by the ideals of American citizenship, which have been built up by this country's heritage and its unceasing struggle for freedom and democracy and opportunity. That means, first of all, a necessary understanding of what those ideals are and what they mean for the newly arrived foreigner. It means that every kind of anti-American propaganda must be stamped out; that racial prejudices and the misunder-standings which lead to unrest and disloyalty and make fruitful soil for anti-American propaganda must be overcome. The foreigner must understand. He must understand what we are trying to do here in America; he must understand something, at least, of the kind of government we have built up in our efforts to, accomplish our particular aims; he must understand how lie can fit into it all, not only to help America, but to help himself-to make it possible for hint to get from this country what he carne here seeking. First of all, he must learn the American language. He must be able to talk with his fellow Americans-those who were born here and those who have recently cone, like himself, but from a different land. The most dramatic, the most crucial demonstration of the urgency of the need of all this is given to us right now. At the time when it is most essential for this country to be solidly American, enemy propagandists are winning an occasional success here because they give their message to men and women and boys and girls who do not understand our language and consequently do not understand us. These foreigners, whom the enemy is trying to make disloyal, are really in our army, the big army that is fighting the war for America. Most of them are not among the soldiers who will fight on the battle front, but they are in the lines back of these soldiers. The worker in the shipyards and in the mines is just as important a soldier in this war as the man in the trenches. That has been said over and over, but it cannot be said too often. It is just as vital for that man in the mine to know why we are at war as it is for the soldier. His employer has just as great a responsibility to the country as has any general, and it is the same responsibility.

Jan 8, 1918

By NONE NA

[Allen -Sherman -Hoff. Pump Co Third Cover Dee Carlton Brown, Advertising Allis-Chalmers Mfg. Co 733, 750 Compton Advertising, Inc. American Cyanamid Co James J. McMahon. Inc. American Manganese Steel Div., American Brake Shoe Co 746 Fuller & Smith & Ross, Inc. Anaconda Copper Mining Co Kenyon & Eckhardt Inc. Carlon Products Corp 748 Penn and Hamaker, Inc. Chicago Pneumatic Tool Co 744, 745 G. M. Basjord Co.]

Jan 1, 1952

By A. S. Nowick, C. Y. Li

It is deMonstrated that quenching from an elevated temperataupe accelerates the grain boundary relaxation in two solid solutions (aAg-Zn and a Cu-Al). This result is consistent with the proposal that, in solid solutions, grain boundary relaxation occurs by a mechanism of' self diffusion. Nevertheless, an alternative possibilitg, that quenching introduces vacancies into the boundary itself, must also be considered. THE phcnomenon of grain boundary relaxation has been well known for many years,1,2 yet the mechanism of this process is very poorly understood. One of the most interesting suggestions which relates to the mechanism of grain boundary relaxation was that of Ke,3 who claimed that the activation energy for grain boundary relaxation and for lattice self diffusion were essentially the same. The implication is therefore that the elementary step in the two processes is the same. This suggestion is particularly startling in view of the fact that activation energy for self diffusion along a grain boundary is very significantly lower than that for volume self-diffusion. Later evidence5-7 showed that there really are two grain boundary peaks, one which appears in high-purity metals, and the other (which develops at a higher temperature than the first) which appears in solid solutions beginning at solute concentrations in the range of 0.1 pct. Data for silver6 show that Kg's hypothesis is surely incorrect for the grain boundary peak in the high-purity metal, since it has an activation energy of only 22 kcal per mole, but that the hypothesis may still be correct for the grain boundary peak in various silver solid solutions, for which activation energies in the range 40 to 50 kcal per mole are observed. If the elementary step in the grain boundary relaxation process were the same as that for self-diffusion, it would be expected that the relaxation process could be hastened by quenching, 2.c. by introducing a non-equilibrium excess of lattice vacancies. Such a quenching effect has already been demonstrated in the case of another anelastic relaxation process, viz., the Zener relaxation effect. The Zener effect, which occurs in essentially all solid solutions, may be attributed to the reorientation of pairs of solute atoms in the presence of an applied shear stress,' and therefore must take place by means of a volume diffusion mechanism. The hastening of this process through quenching9 has been one way of demonstrating that atom movements in the lattice take place through a defect mechanism, presumably single vacancies. In order to see if the grain boundary relaxation is affected by quenching, it is particularly convenient to compare the grain boundary relaxation with the Zener effect, by choosing a specimen for which both relaxation effects appear. Specifically, a fine-grained sample of a solid solution shows in the curve of internal friction vs temperature, first a peak due to the Zener effect, then a second rise (and eventually a peak at substantially higher temperatures) due to the grain boundary relaxation. The same phenomena are also observable in static anelastic measurements, such as creep at very low stress levels. Thus, for the same fine-grained solid solution, the creepstrain, when plotted against log time, falls on a sigmodial curve with a sharp inflection point, due to the Zener effect, which is followed by a second rise and inflection resulting from the grain boundary relaxation. To look for a quenching effect, static measurements are preferable to the dynamic internal friction measurements, due to the fact that quenching effects tend to anneal out too rapidly at the temperatures at which the internal friction is measured.9 RESULTS AND DISCUSSION Creep experiments in torsion were carried out in an apparatus similar to that described by Ke1, whereby a wire is held under constant torque and its angular displacement is observed as a function of time. The alloy Ag-30 at. pct Znwas selected because of the large Zener relaxation that it displays. The two samples used were a "coarse grained" wire with a mean grain size about twice the diameter of the wire (diam = 0.032 in.), and a "fine-grained" wire which had several grains across the diameter. In Fig. 1 a comparison is made of the creep curves at 160°C of these two samples after they had been cooled slowly from 400°C. Curve A, which represents the coarsegrained sample, shows a unique relaxation process due to the Zener relaxation, with a relaxation time, T , in the vicinity of 100 sec. Curve B, which represents the behavior of the fine-grained sample, on the other hand, shows first the same relaxation process as that in A, followed by a turning up of the curve which corresponds to the onset of a second overlap-

Jan 1, 1962

By Claus Guenter Goetzeil

(New York Meeting, February, 1937) The object of this investigation was to determine whether silver alloys could be used instead of the currently employed insert of high-expansion Average Coefficient per Deg. C. over Range 20° to 200° C. Pure aluminum..................................... 24.6 X 10-6 Cast low-expansion Si-Cu-Ni-A1 piston alloy............ 20.0 X 10-6 High-expansion austenitic Cu-Ni cast iron.............. 19.3 X 10-6 Cast steel (0.25-0.35 C, 0.40-1.0 Mn).................. 12.6 X 10-6 Cast iron (3.15 total C, 2.16 Si)....................... 12.8 X 10-6 Pure silver.......................................... 18.9 X 10-6 austenitic ferronickel alloy, to reduce the wear of ring grooves in light metal pistons. A typical example of a piston containing a ferronickel insert is shown in Fig. 1. The high coefficient of expansion of silver made it worthy of consideration, while the small size of the insert would render its use feasible in Germany as an emergency measure. The coefficients of linear expansion of several metals and ailoys are as shown in the table above. Obviously the melting point of the insert must be high enough to prevent it from melting when the light alloy is cast around it. This imposes a lower limit of about 850" C. for the solidus of the silver alloy. Pure silver melts at about 961" C., so that the tolerable depression in the solidus is rather small. To avoid deformation of the insert during use a Brinell hardness number of at least 60 appears necessary.

Jan 1, 1937

By Rex O. McLellan

The formation of a monovacancy in a metal is simulated in an elastic model by the displacement of the surface of a small spherical cavity in a large elastic continuum. The application of linear elasticity to this distortion results in a well- known formula for the energy and an expression for the concomitant entropy change due both to the shear strain in the continuum and also to the dilation of the solid resulting from the boundary conditions at the surface of the solid. Elastic data (the sliear modulus and its temperature coelficient) are used to calculate the entropy and energy of formation for many metals. Despite the simplicity of the assumptions involved, the agreement between the calculated entropies and energies and experimental values is remarkably good. In recent years there has been a large increase in measurements of the absolute concentration of mono-vacancies in metals as a function of temperature. Hence new data for both the energy and the noncon-figurational entropy of formation of monovacancies has become available. Recent measurements&apos; of the anomalous (non-Arrhenius) self-diffusion in many bcc metals has also focused interest on the prediction of the thermodynamic parameters of mono- and multi-vacancies in those metals for which no data are available. Damask and Dienes&apos; have discussed the various theoretical calculations of the energy of formation EL, of a monovacancy. These include simple models involving the breaking of atomic bonds on moving atoms from the interior of a crystal to the surface, models combining elastic calculations with surface-energy terms and detailed quantum mechanical calculations. The simler models give the correct order of magnitude of &, but tend to overestimate it by a factor of about two. The quantum mechanical calculations4"7 have been carried out for the noble and alkali metals with generally reasonably good agreement with the available Ef data. The calculation of entropy of formation Sfv14 lnvolves a fundamental calculation of the perturbation of the phonon spectrum caused by the creation of a vacancy. Huntington, Shirn. and wajda8 have given an approximate evaluation of sJV by considering an Einstein model for the localized vibrations in the immediate neighborhood of the defect and then using elastic theory to calculate the entropy associated with the shear stress field in the distorted crystal (as originally proposed by Zenerg). They also included a term due to the dilation of the crystal. They obtained a value of 1.47k for copper, in good agreement with the experimental value (1.50k). However, Nardelli and Tetta- manzi1° have recently shown that neglecting the coupling between atoms (Einstein Model) may lead to a serious error so the agreement may be somewhat fortuitous. In this work simple linear elastic theory is used to calculate the entropy and energy of formation of mono-vacancies. Despite the simplicity of some of the assumptions involved, the agreement with the available experimental data is remarkable. However. the reasonable degree of success in the application of linear elastic calculations to the excess entropy of a solute atom in a dilute solid solution1&apos; indicates that the application of elastic theory to vacancies. where the interaction of different atomic species is not involved, may not be inappropriate. THE ELASTIC MODEL The metal is assumed to be a spherical elastic continuum. A small spherical cavity of volume V = 4i;v:&apos;/3 is cut from the center. removed. and dissolved rever-sibly in the bulk of the material. TO a good approximation no net atomic bonds are broken and the material does not undergo a volume change although the externally measured volume of the body would increase by V. The radius of the sphere of metal is much larger than r Next a negative pressure is applied to the cavity causing its surface to be displaced inward by an amount simulating the relaxation of the lattice around a monovacancy. In this model the energy and entropy accompanying the distortion are taken as 4, and <. As a first approximation the equation of state for the solid is taken as: r = ro(i + *~D LiJ where K is the bulk modulus. P the hydrostatic pressure. Vo the volume of the material at 0°K and zero pressure. and d+/dT = 30. where 0 is the linear thermal expansion coefficient. The variation of entropy with hydrostatic pressure is given by the Maxwell equation: These equations give the entropy change resulting from increasing the hydrostatic pressure from 0 to P as: and since • we have: This is the entropy arising from the dilation resulting

Jan 1, 1970

Henry LOUIS, London, England (communication to the Secretary) : Prof. Richards&apos;s paper has impressed me as highly valuable. Without entering upon any discussion of it as careful and thorough as it deserves, I venture to mention one or two points which a perusal of it has recalled to my mind in connection with my own study and practice of ore-dressing. I always mentally divide jigging into two phases: 1. A particle at rest on the jig-bed is lifted and carried upwards by the rising current of water, at an increasing velocity, which tends to a maximum. When the upward current is stopped, the particle continues to rise with rapidly diminishing velocity until it comes to rest. This completes the first phase. 2. In the second phase, the particle falls from its position of rest with an increasing velocity which tends again to a maximum, and continues to fall until the rising current of water has reduced its velocity to zero. This completes the second phase. The second phase will evidently be greatly modified by the effect of suction, as Prof. Richards shows; but I do not see that his experiments very clearly imitate the action of the second phase. And the brief intervals at the end of each phase, when the mineral particle, by reason of its acquired velocity, is still moving, though in opposition to the water-current, yet remain to be investigated. I feel especially, in Prof. Richards&apos;s paper, a difficulty which I have felt with regard to all similar previous investigations, namely, that the experiments deal with particles falling a long distance, when the velocity becomes uniform. I question whether this uniform maximum velocity is attained in actual jigging-practice. If so, it is certainly for a comparatively very small proportion only of each stroke. It seems to me that an investigation like that of Prof. Richards, but confined to the first 6 or 8 inches of fall only, and carried out with suitably delicate recording-apparatus, is what we

Jan 1, 1895

By Vard H. Johnson

IN 1943 the U. S. Bureau of Mines undertook drilling in an effort to develop new reserves of coking coal in an area near Paonia, Colo., as a part of an attempt to alleviate the shortage of known coking coal of good quality in the western United States. Geologic mapping of the area was undertaken by the U. S. Geological Survey with the purpose of first furnishing guidance in location of drillholes and later aiding in interpreting the results of the drilling. The drilling program was under the general supervision of A. L. Toenges of the U. S. Bureau of Mines. J. J. Dowd and R. G. Travis were in charge of the work in the field. Geologic mapping was started by D. A. Andrews of the Geological Survey in the summer of 1943 and was continued from the spring of 1944 to 1949 by the writer. The first few holes drilled failed to locate coking coal, but in the summer of 1944 coking coal was discovered by drilling 6 miles east of Somerset, Colo., the site of present mining. In the succeeding years, 1945 to 1948, 100 to 150 million tons of coal suitable for coking were blocked out by drilling. The ensuing discussion of the geologic controls on the distribution of coking coal in the area is based on the geologic mapping as well as the drilling done in the Paonia area, more complete descriptions of which have appeared or are in process of publication."&apos; In order that the possible geologic controls affecting the present distribution of coking coal may be considered, it is necessary to discuss briefly the indicators of coking quality coals. Coking Coal Coal that cokes has the property of softening to form a pastelike mass at high temperatures under reducing conditions in the coke oven. This softening is accompanied by the release of the volatile constituents as bubbles of gas. After release of the contained gases and upon cooling, a hard gray coherent but spongelike mass remains that is referred to as coke. This substance varies greatly in physical properties and, to be suitable for industrial use, must be sufficiently dense and strong to withstand the crushing pressure of heavy furnace loads. Western coals have a generally high volatile content and therefore form a satisfactory coke only when they attain a rather high fluidity during the process of heating arid distillation in the coke oven. When this high degree of fluidity is developed, the volatile constituents escape and leave a finely porous coke. On the other hand, when the degree of fluidity is low the product is an excessively porous and therefore physically weak mass that is called char." Small quantities of oxygen present in coal are believed to decrease the fluidity of the material during the coking process and to favor the development of char rather than coke. In consequence, coal chemists have for some time considered the possibility of developing an index to coking qualities by inspection of chemical analyses of coals.&apos; A formula has now been developed that does permit a rough preliminary estimate of the cokability of coal on the basis of the analysis on an ash and moisture-free basis. Coals may be eliminated as possible coking fuels if the oxygen content is greater than 11 pct. Similarly the ratio of hydrogen to oxygen must be greater than 0.5 and the ratio of fixed carbon to volatile constituents must be greater than 1.3. If the coal, on the basis of these limiting factors, appears to have possible coking qualities, the following formula permits determination of the coking index: a+b+c+d Coking index = -------- 5 a equals 22/oxygen content on ash and moisture-free basis, b equals two times the hydrogen content divided by oxygen content on moisture and ash-free basis, c equals fixed carbon/l.3 x volatile matter, and d equals the heating value on moist, ash-free basis/13,600. Coking indices higher than 1.0 suggest that the coal will coke, and indices above&apos; 1.1 indicate good coking tendencies. Although generally usable, this formula &apos;is not completely satisfactory because the percentage of oxygen shown in ultimate analyses is derived only by difference; i.e., by subtracting the sum of the percentages of the constituents determined analytically from 100 pct. Although the coking index indicates the coking tendencies of coal, it is necessary to make physical tests of coke before its industrial value can be determined. The U. S. Bureau of Mines has developed a standard procedure for determining the approximate strength of coke that would be formed from a given coal. In this test one part of ground coal, mixed with 15 parts of carborundum, is baked to form a standard briquette. The weight, in kilograms, necessary to crush the briquette is termed the agglutinating index. This test determines the relative fluidity attained in the coking process by measuring the cementing strength of the coal in the briquette. A

Jan 1, 1953

By Vard H. Johnson

IN 1943 the U. S. Bureau of Mines undertook drilling in an effort to develop new reserves of coking coal in an area near Paonia, Colo., as a part of an attempt to alleviate the shortage of known coking coal of good quality in the western United States. Geologic mapping of the area was undertaken by the U. S. Geological Survey with the purpose of first furnishing guidance in location of drillholes and later aiding in interpreting the results of the drilling. The drilling program was under the general supervision of A. L. Toenges of the U. S. Bureau of Mines. J. J. Dowd and R. G. Travis were in charge of the work in the field. Geologic mapping was started by D. A. Andrews of the Geological Survey in the summer of 1943 and was continued from the spring of 1944 to 1949 by the writer. The first few holes drilled failed to locate coking coal, but in the summer of 1944 coking coal was discovered by drilling 6 miles east of Somerset, Colo., the site of present mining. In the succeeding years, 1945 to 1948, 100 to 150 million tons of coal suitable for coking were blocked out by drilling. The ensuing discussion of the geologic controls on the distribution of coking coal in the area is based on the geologic mapping as well as the drilling done in the Paonia area, more complete descriptions of which have appeared or are in process of publication."&apos; In order that the possible geologic controls affecting the present distribution of coking coal may be considered, it is necessary to discuss briefly the indicators of coking quality coals. Coking Coal Coal that cokes has the property of softening to form a pastelike mass at high temperatures under reducing conditions in the coke oven. This softening is accompanied by the release of the volatile constituents as bubbles of gas. After release of the contained gases and upon cooling, a hard gray coherent but spongelike mass remains that is referred to as coke. This substance varies greatly in physical properties and, to be suitable for industrial use, must be sufficiently dense and strong to withstand the crushing pressure of heavy furnace loads. Western coals have a generally high volatile content and therefore form a satisfactory coke only when they attain a rather high fluidity during the process of heating arid distillation in the coke oven. When this high degree of fluidity is developed, the volatile constituents escape and leave a finely porous coke. On the other hand, when the degree of fluidity is low the product is an excessively porous and therefore physically weak mass that is called char." Small quantities of oxygen present in coal are believed to decrease the fluidity of the material during the coking process and to favor the development of char rather than coke. In consequence, coal chemists have for some time considered the possibility of developing an index to coking qualities by inspection of chemical analyses of coals.&apos; A formula has now been developed that does permit a rough preliminary estimate of the cokability of coal on the basis of the analysis on an ash and moisture-free basis. Coals may be eliminated as possible coking fuels if the oxygen content is greater than 11 pct. Similarly the ratio of hydrogen to oxygen must be greater than 0.5 and the ratio of fixed carbon to volatile constituents must be greater than 1.3. If the coal, on the basis of these limiting factors, appears to have possible coking qualities, the following formula permits determination of the coking index: a+b+c+d Coking index = -------- 5 a equals 22/oxygen content on ash and moisture-free basis, b equals two times the hydrogen content divided by oxygen content on moisture and ash-free basis, c equals fixed carbon/l.3 x volatile matter, and d equals the heating value on moist, ash-free basis/13,600. Coking indices higher than 1.0 suggest that the coal will coke, and indices above&apos; 1.1 indicate good coking tendencies. Although generally usable, this formula &apos;is not completely satisfactory because the percentage of oxygen shown in ultimate analyses is derived only by difference; i.e., by subtracting the sum of the percentages of the constituents determined analytically from 100 pct. Although the coking index indicates the coking tendencies of coal, it is necessary to make physical tests of coke before its industrial value can be determined. The U. S. Bureau of Mines has developed a standard procedure for determining the approximate strength of coke that would be formed from a given coal. In this test one part of ground coal, mixed with 15 parts of carborundum, is baked to form a standard briquette. The weight, in kilograms, necessary to crush the briquette is termed the agglutinating index. This test determines the relative fluidity attained in the coking process by measuring the cementing strength of the coal in the briquette. A

Jan 1, 1953

By Vard H. Johnson

IN 1943 the U. S. Bureau of Mines undertook drilling in an effort to develop new reserves of coking coal in an area near Paonia, Colo., as a part of an attempt to alleviate the shortage of known coking coal of good quality in the western United States. Geologic mapping of the area was undertaken by the U. S. Geological Survey with the purpose of first furnishing guidance in location of drillholes and later aiding in interpreting the results of the drilling. The drilling program was under the general supervision of A. L. Toenges of the U. S. Bureau of Mines. J. J. Dowd and R. G. Travis were in charge of-the work in the field. Geologic mapping was started by D. A. Andrews of the Geological Survey in the summer of 1943 and was continued from the spring of 1944 to 1949 by the writer. The first few holes drilled failed to locate coking coal, but in the summer of 1944 coking coal was discovered by drilling 6 miles east of Somerset, Colo., the site of present mining. In the succeeding years, 1945 to 1948, 100 to 150 million tons of coal suitable for coking were blocked out by drilling. The ensuing discussion of the geologic controls on the distribution of coking coal in the area is based on the geologic mapping as well as the drilling done in the Paonia area, more complete descriptions of which have appeared or are in process of publication.1-5 In order that the possible geologic controls affecting the present distribution of coking coal may be considered, it is necessary to discuss briefly the indicators. of coking quality coals. Coking Coal Coal that cokes has the property of softening to form a pastelike mass at high temperatures under reducing conditions in the coke oven. This softening is accompanied by the release of the volatile constituents as bubbles of gas. After release of the contained gases and upon cooling, a hard gray coherent but spongelike mass remains that is referred to as coke. This substance varies greatly in physical properties and, to be suitable for industrial use, must be sufficiently dense and strong to withstand the crushing pressure of heavy furnace loads. Western coals have a generally high volatile content and therefore form a satisfactory coke only when they attain a rather high fluidity during the process of heating and distillation in-the coke oven. When this high degree of fluidity is developed, the volatile constituents escape and leave a finely porous coke. On the other hand, when the degree of fluidity is low the product is an excessively porous and therefore physically weak mass that is called char.6 Small quantities of oxygen present in coal are believed to decrease the fluidity of the material during the coking process and to favor the development of char rather than coke. In consequence, coal chemists have for some time considered the possibility of developing an index to coking. qualities by inspection of chemical analyses of coals.7 A formula has now been developed that does permit a rough preliminary estimate of the cokability of coal on the basis of the analysis on an ash and moisture-free basis. Coals may be eliminated as possible coking fuels if the oxygen content is greater than 11 pct. Similarly the ratio of hydrogen to oxygen must be greater than 0.5 and the ratio of fixed carbon to volatile constituents must be greater than 1.3. If the coal, on the basis of these limiting factors, appears to have possible coking qualities, the following formula permits determination of the coking index: Coking index =[ a+b+c+d 5] a equals 22/oxygen content on ash and moisture- free basis, . b equals two times the hydrogen content divided by oxygen content on moisture and ash-free basis, c equals fixed carbon/1.3 x volatile matter, and d equals the heating value on moist, ash-free basis/13,600. Coking indices higher than 1.0 suggest that the coal will coke, and indices above 1.1 indicate good coking tendencies. Although generally usable, this formula is not completely satisfactory because the percentage of oxygen shown in ultimate analyses is derived only by difference; i.e., by subtracting the sum of the percentages of the constituents determined analytically from 100 pct.8,9 Although the coking index indicates the coking tendencies of coal, it is necessary to make physical tests of coke before its industrial value can be determined. The U. S. Bureau of Mines has developed a standard procedure for determining the approximate strength of coke that would be formed from a given coal. In this test one part of ground coal, mixed with 15 parts of carborundum, is baked to form a standard briquette. The weight, in kilograms, necessary to crush the briquette is termed the agglutinating index. This test determines the relative fluidity attained in the coking process by measuring the cementing strength of the coal in the briquette. A

Jan 1, 1952

By W. F. Rogers, J. A. Stewart, P. J. Kalish, E. O. Bennett

Detailed descriptions are given of materials, apparatus and the experimental procedure used to study the effect of bacteria on sandstone permeability. The factors affecting permeability during injection of bacterial suspensions which have been investigated are: (I) concentration of bacteria; (2) core permeability and median pore size; (3) species of bacteria, mode of aggregation and relative size; (4) injection rate or pressure differential; (5) mean pressure; and (6) depth of penetration of bacteria. The investigation demonstrated that bacteria cannot reduce core pertneability to zero and that their effect on permeability is subject to definite limitations. Remedial or permeability restoration studies also were made. Acidization in combination with reverse flow war found to be an effective method for restoring permeability In cores partially plugged with bacteria. The relationship between the bacterial quantities in the laboratory tests and those found in field operations is discussed. The linear laboratory flow data have been translated into terms of field radial systems; these data indicate the most practical methods of maintaining injection rates in the presence of bacteria are to increase injection pressures or hydraulically fracture the formation. INTRODUCTION It has long been known that various bacteria flourish in the above-ground components of oil field water-injection systems. The presence of these bacteria has led to the suspicion that they might enter into the causes for reduction of injection well permeability, but only recently has an attempt been made to describe the effects quantitatively.1 Biocides are used in many cases without a firm knowledge as to whether the bacteria are killed, or if they are, whether the dead cells affect formation permeability. This project was undertaken as part of a study to determine the effect of bacteria, residual oil and precipitated solids such as iron sulfide or calcium carbonate on the permeability of sandstones and to learn whether any of these materials adversely affect brine injectivity in secondary recovery or disposal operations. This report deals with that portion relating to the effect of bacteria. MATERIALS CORES Three different permeability ranges of Berea sandstone cores were used in the study. The range of initial, absolute brine permeabilities kj were: high — 278 to 400 md: medium—130 to 162 md; and low—17.7 to 48.3 md. The permeability data for the cores used in the tests are included in Table 1. All cores were cut to a nominal 1 in. diameter. Following air permeability determinations, they were molded with an epoxy resin in 1.5 in. ID aluminum sleeves. The sleeves had drilled and tapped holes for intermediate pressure connections along the length of the cores. After molding, the high- and medium-permeability cores were trimmed to 4 in. in length and the low-permeability cores to 2 in. These lengths resulted in pore volumes of approximately 10.9, 10.4 and 4.4 ml, respectively, for the high-, medium- and low-permeability cores. Pressure-transmitting channels were drilled through the plastic into the core proper, using the sleeve holes as drill guides. Width and depth of channel penetration into the core proper were approximately 0.03 in. and 0.05 in., respectively. Three pressure taps were used with all cores; for the high- and medium-permeability cores the taps were spaced 1 in. apart; for the low-permeability cores the taps were spaced 0.4, 0.8 and 1.2 in. from the inlet end. Pore size distributions were calculated from restored-state capillary pressure curves for representative cores in each of the three permeability ranges. In each case the pore size range with the greatest percentage of the pore space included the very small pores up to 0.5 micron in radius. The median pore radii were in the 5.5 to 6 micron range for the high-permeability cores; in the 4.5 to 5 micron range for the medium-permeability cores; and in the 3.5 to 4 micron range for the low-permeability cores.

Jan 1, 1965

By Edward Wisser

The environment of an ore body is taken to mean not only its physical surroundings but every factor, passive or active, that conditioned the ore shoot, saving only the original composition of the solutions that formed the shoot. Collection of data related to the shape and characteristics of veins should be followed by correlation of the data and the formulation of generalizations regarding ore formation. The nature of the criteria used in arriving at these generalizations is discussed. Certain of the criteria, when used with an understanding of their underlying causes, become "ore- guides." In the course of his study the geologist must not confine himself to the immediate surroundings of the veins, but should attempt to work out the geologic history of events culminating in the crucial epoch for any mining district, the period of mineralization. The work may involve study of features far removed from the veins and related to them only indirectly. It commonly means thorough study of the geology of the entire region surrounding the ore deposits. THE following question has been suggested for discussion: [t] "Are there any criteria by which one can determine when mining operations have reached the roots of an ore deposit?" The question deals less with the roots of a particular ore body than with the lower limit of the vertical range within which ore bodies may be expected. It concerns a critical line upon the longitudinal vertical projection of a vein.[t] Below this line it is useless to look for ore shoots; above the line exploration below the bottoms of individual ore shoots may be justified. Can we learn to determine the position of such a line? In some multivein districts the line for any given vein may be approximated by simple interpolation or extrapolation. Where this is possible the bottoms of the lowest ore shoots in the various veins are points on an imaginary, gently rolling surface. The trace of this surface upon the vein is our critical line for that vein. The imaginary surface rolls so gently that it may be projected from two or more known veins to an unexplored vein near by. Here is a criterion for the bottoming of ore that has nothing to do with changes in the appearance of the vein in question; it rests solely on the depth at which the ore bottomed in adjacent veins. The method is not applicable in districts only slightly explored in depth, nor where the lower limit of the ore-bearing horizons

Jan 1, 1939

By George A. Miller

OIL, the abundance of it in the hands of the Allies and the lack of it in the hands of the Axis, played a major role in winning World War II. It bids fair to implement the winning of the peace. In fact the signing of the revised agreement on petroleum between the Government of the United Kingdom of Great Britain and Northern Ireland and the Government of the United States of America on Sept. 24, 1945, may be considered as the first step in establishing a new pattern in foreign relations by our Government. The significance of this agreement on petroleum is that it was arrived at on the part of the United States of America through the advice and consent of the most interested parties, the leaders of the petroleum industry and the Government, distinctly a first step toward unifying the power of business and the strength of the Government, which places us on a par with the British Crown which has always had the advice and counsel of its business leaders in formulating its foreign trade policies. And what is the thing so patently discernible in this new first step toward winning the peace? It is that the petroleum agreement, the first draft of which, signed in Washington on Aug. 8, 1944, almost caused an epidemic of apoplexy among the leaders of the oil industry, represents the desire of the people most concerned with the problems of petroleum both at home and abroad. This new agreement, which will come up before the Senate for ratification this month-hearings will commence in January - derives its "power from the consent of the governed," something about which our forefathers were vitally concerned once upon a time.

Jan 1, 1946

By W. V. Green

The creep-rupture behavior of commercial powder-metallurgy tungsten rod is reported for temperatures of 2250°, 2500°, 2700°, and 2800°C, stresses up to 7000 psi, and times up to 4 hr. The temperature dependence and the stress dependence of creep rates are evaluated. Rupture time is fitted to the Larson-Miller parameter and compared to lower-temperature and higher stress results reported by pugh.4 THE tensile strength of single-crystal wire1 and of polycrystalline wire2 have been measured by Goucher. More recently Bechtold3 and pugh4 have studied the mechanical properties of tungsten rod between room temperature and 1200°C. Since tungsten has the highest melting point of all metals, it should retain useful strength to very high temperatures, and should find many applications in missiles, rockets, and so forth. Therefore, the mechanical usefulness of polycrystalline tungsten rod was investigated in the 2250" to 2800°C temperature range by short-time creep-rupture tests. MATERIALS TESTED Creep specimens were machined from 1/2-in. round commercial tungsten rod which was manufactured from powder by cold pressing, sintering, and hot swaging. Purity reported by the vendor was 99.95 pct W. Spectrochemical analyses showed "traces" (less than 0.01 pct) of silicon, iron, and titanium, and "faint traces" (less than 0.001 pct) of calcium and manganese. Carbon content was 30 ppm and nitrogen content was 70 to 110 ppm. No oxygen analysis was obtained. Room-temperature stress-strain tests on the as-received tungsten gave badly scattered results. Threaded end specimens broke at the threads. When these specimens were retested using shoulder grips, the specimens broke at the shoulders. No fractures occurred in the gage lengths. The fracture stresses were: 127,000; 137,000; and 154,000 psi for three specimens which fractured at the shoulders. The microstructure of the as-received tungsten rod is shown in Fig. 1. SPECIMENS USED Fig. 2 shows the two types of creep specimens tested. The threaded-end type specimen, which was used in most tests, had a 3/4-in. gage length and 1/4-in. gage diam. The cone-end specimen, which was used primarily to investigate the effects of a smaller gage diameter and the practicability of the modified grips and specimen, had a 3/4-in. gage length and a 1/8-in. gage diam. In both cases, the gage length terminated at 0.005-in. high shoulders which served as fiducial marks for optical strain measurements. Surface finish on the gage length was 16 µ-in. rms. Creep rates and rupture times were not significantly different for the two types of specimens and were not affected by electropolishing the specimens before testing. TESTING PROCEDURE The constant-load creep-testing machine used has been described by Smith, Olson, and Brown.5 In it the specimen is held vertically by grips of similar material and on the axis of a cylindrical tungsten or tantalum heater-tube. The specimen is loaded by means of the specimen grips, a pull rod (which is sealed to the chamber lid by a vacuum-tight bellows), a mechanical lever system, and hanging dead weights. Both specimen and grips are heated by radiation from the heater-tube, which is heated by its own electrical resistance. An optical system views the incandescent specimen through slits in the radiation shielding and heater-tube. The optical system projects an enlarged image of the specimen gage length on a ground-glass screen. Periodic gage-length measurements are made on this image with two cathetometers. Thorium oxide coatings on the specimen threads or conical end surfaces completely prevented diffusion-welding of specimens to grips, and were used

Jan 1, 1960

By L. H. Robinson

Triaxial compression tests on Indiana limestone indicate that chemical additives in the pore fluids can increase or decrease the strength in plastic failure but not in brittle failure. Tests using a series of the sodium salts of dicarboxylic acids show that odd-number carbon-atom chains decrease the yield strength as much as 3.0 x 10 3 psi, and even-number carbon-atom chains increase the yield strength as much as 9.0 x 102 psi. ,The most effective chemical (sodium citrate) decreased the yield strength of Indiana limestone from 16.0 x 103 to 12.0 x 103 psi. The chemical additives investigated have no influence on microbit drilling rate when drilling with zero differential pressure. However, when drilling at a 2.0 x 103-psi pressure differeniial and using an odd-number carbon chain compound as the circulating fluid, the roller bit drilling rates were slower than with water whereas the drag bit drilling rates were faster. One even-number carbon chain compound added to the circulating fluid produces the opposite effect: the roller bit drilling rate is slightly faster than with water and the drag bit slower than with water. INTRODUCTION A Russian book by Rehbinderl published in 1944 generated much interest in the possibility of aiding and accelerating the destruction of solids by the action of a liquid in which the solids are deformed. This book describes a process in which microcracks are generated during elastic deformation. To describe this process, the rock is divided into three zones: (1) the zone in which the destruction takes place, (2) the predestruc-tion zone (an affected area immediately below the destroyed zone) and (3) the undisturbed specimen. Consider a load applied normally to a surface of an infinite slab of rock. Immediately below the point of application of the load, the rock is destroyed by compression or shear forces. Below this area of destruction, because of a great number of discontinuities ranging from defects to weak points in crystals of discontinuities in crystal latices, very small cracks are created in or between the crystals (often referred to as microcracks). Upon removing the load, the broken rock in the destroyed zone could be removed. In the lower predestruction zone, however, the microcracks in and between the crystals could disappear by the process of rehealing, i.e., the molecular attraction from one side of the crack to the other side being sufficient to completely eliminate the crack. Thus, a large number of these microcracks possibly exist only for a relatively short period of time. The concept of small cracks being generated within the crystals of a rock is not unreasonable. If the rock matrix is deformed below the yield point, some of the defects present within the crystalline structure could start small cracks through the interior of the grains. Upon removal of the load, these microcracks reheal (or the newly generated surfaces come back together) so that all evidence of cracks completely disappears. Under various types of loading, and in various types of fluids, the rehealing of these cracks would be time dependent. If a liquid adhered to the surface of a rock, it could penetrate into the microcracks and thus delay or prevent the rehealing process. This suggests that the prevention of healing of the microcracks may be dependent upon the wetting characteristics of the solid. Thus, rocks which are water-wet should be more easily destroyed in water than in nonpolar hydrocarbon liquid. Adsorption of a liquid could also reduce the free surface energy which could explain the decrease in strengths of materials under nonrepetitive-type loading. Rehbinder&apos;s work prompted Boozer, Hiller and Serdengecti 2 to examine the effects of pore fluids on the deformation of rocks subjected to triaxial compression over a range of confining pressures, temperatures and strain rates. Fluids which strongly adsorbed on the rock grain surfaces decreased the strength of sandstone and limestone, which deformed plastically. For certain strain

[MINING AND EXPLORATION DIVISION Established as Mining, Geology and Geophysics Division, Sept. 27, 1949 Name changed February 19, 1958. Lyman H. Hart, Chairman Robert J. Lacy, Assistant Chairman Vice Chairmen: John C. Wangaard, Membership J. M. Ehrhorn, Program John G. Hall, Publications C. E. Nelson, Secretary American, Smelting and Refining Co. 120 Broadway New York 5, New York Editor, Rock-in-the-Box: J. W. Chandler.]

Jan 1, 1961

Council PRESIDENT OF THE COUNCIL. JOHN HAYS HAMMOND NEW YORK, N. Y. (Term expires February, 1908 ) VICE-PRESIDENTS OF THE COUNCIL. HENRY M. HOWE NEW YORK, N. Y. J. B. GRANT DENVER, COLO. JAMES D. HAGUE NEW YORK, N. Y. (Term expires February, 1908.) SAMUEL B. CHRISTY BERKELEY, CAL. JOHN A. CHURCH NEW YORK, N. Y. PERSIFOR FRAZER PHILADELPHIA, PA. (Term expires February, 1909 )

Jan 1, 1910

By J. Lohrenz, R. J. Francis, G. C. Clark

Compositional material balance methods have been extended to solution gas-gas cap-water drive reservoirs. Partial or complete pressure maintenance as well as reservoir repressuring by gas and/or water injection may be considered. Increrments of reservoir withdrawals and injections equivalent to a given time increment are used as the basic iterative step to allow the extension. An example field study shows how the reservoir volumes. extent of the water drive, and relative permeability ratio function may be estimated. Knowing these, the methods can be used to predict reservoir behavior. INTRODUCTION The compositional material balance is similar to conventional material balances in many aspects. The assumption of a pressure-homogenous reservoir with no transients is common to all conventional material balances1-1 although numerical methods are different. The compositional material balance also contains this assumption. Inclusion of phase equilibria directly in reservoir calculations is the key difference and improvement in the compositional material balance. A continuous account of the compositions of the reservoir fluids and effluents is determined. Calculations of fluid phases and properties can be based on these compositions. Excepting fluid phases and properties determined in this manner, the compositional material balance uses procedures exactly analogous to conventional methods. Brinkman and Weinaug5 and Jacoby and Berry6 have given compositional material balances for simple solution gas drive reservoirs; subsequently Jacoby and Berry&apos; extended their procedure to include pressure maintenance by gas injection at constant reservoir pressure. This paper extends compositional material balance techniques to a more general combination drive reservoir with various types of pressure maintenance operations. The procedure for this extended compositional material balance and an example of its field application are presented. PROCEDURE The numerical calculations of this compositional mate- rial balance are performed on a high-speed digital computer. The most comprehensive case the present compositional material balance program can handle is a solution gas-gas cap-water drive reservoir with (1) water production, (2) water influx, (3) separate or commingled production from the oil and gas zones, (4) any surface processing arrangement including LPG and gasoline production, and (5) gas injection into the gas and/or oil zones." This description of the procedure applies to this most comprehensive case. Appropriate deletions in the procedure can be made for more simple mechanisms. ASSUMPTIONS In common with conventional material balances, the compositional material balance makes the following assumptions: (1) the total reservoir is at a uniform pressure at a given time; (2) the volumetric ratio of gas to liquid withdrawal at reservoir conditions is directly proportional to their mobilities; and (3) instead of assuming a pressure-dependent total gas-oil equilibrium, the cornpbsitional material balance makes a sianificantly different and more rigorous assumption as follows. Thermodynamic equilibrium exists for each component in the liquid-gas mixtures in the reservoir and in surface processing. These three assumptions are fundamental in the compositional material balance procedure. Other assumptions involve arbitrary simplifications of the reservoir mechanisms. This compositional material balance uses the following simplifying assumptions: (1) no bulk mixing occurs between the gas and oil zone; (2) total mixing occurs between any injected gas and the contents of the injection zone; (3) no in situ hydrocarbon liquid is produced from the gas zone; (4) no reservoir gas is retained behind any net bottom-water influx; (5) the residual saturation of hydrocarbon liquid at reservoir conditions behind any net bottom-water influx is constant; and (6) fluids retained behind any net bottom-water influx exert no further influence on the reservoir. These six assumptions are not fundamental. Modifications of the present procedure can be made for different assumptions of the reservoir mechanisms. THE TIME INCREMENT Previous compositional material balances have used a pressure increment for simple solution gas drive reservoirs"" and an increment of injected gas for pressure maintenance.&apos; These increments are suitable for these simple cases. They are, however, inadequate for reservoirs with time dependent drive mechanisms including water drive. A time increment removes this inadequacy and is