Search Documents

By Sutham Niyomwas

Silicon-Silicon Carbide (Si-SiC) composites were synthesized by self-propagating high temperature synthesis (SHS) from a powder mixture of SiO2-C-Mg. The reaction was carried out in a SHS reactor under static argon gas at a pressure of 0.5 MPa. The standard Gibbs energy minimization method was used to calculate the equilibrium composition of the reacting species. The effects of silica sources and carbon mole ratio in precursor mixture on the Si-SiC conversion were investigated using X-ray diffraction and scanning electron microscope technique. The as-synthesized products of Si-SiC-MgO powders were leached with 0.1M HCl acid solution to obtain the Si-SiC composite powders.

Jan 1, 2009

By P. N. Anyalebechi

The effects of solidification rate on the cast microstructures of aluminum alloys 6009 and 6016 have been investigated with directionally cooled laboratory-size ingots, at 0.2-10.1 K/s and 0.4- 23.1 K/s, respectively. These ranges of solidification rate are within those observed in commercial-size ingots. In both alloys, the average dendrite cell size and second phase particle size decreased with increase in average solidification rate and with a decrease in average local solidification time. However, at comparable solidification rates, the dendrite cells and second phase particles are finer in the shorter freezing range alloy 6009 than in the longer freezing range alloy 6016. This is provisionally attributed to the earlier formation of second phase intermetallics at higher temperatures during solidification and to the formation of greater amount of the relatively coarse plate-like ß -phase (Al9Fe2Si4) phases in alloy 6016. In general, in both alloys, the types and relative amounts of the second phase particles in both alloys are independent of solidification rate.

Jan 1, 2006

By Manis Kumar Jha

Leaching studies were carried out for the recovery/ recycling of metals from PCBs containing 17.05% Cu, 0.74% Ni, 1.74% Fe, 4.35% Pb and 8.32% Sn using various acids such as H2SO4, HCl and HNO3. While sulfuric acid was not a suitable leachant for the dissolution of metals from PCBs, hydrochloric acid selectively dissolved tin. The nitric acid was found to be effective lixiviant with the recovery of 99.99% Cu, Fe, Ni and 36.7% Pb in 6M HNO3 at S/L ratio of 100 g/L and 90oC. The kinetic studies carried out with 2M and 4M HNO3 at 90oC showed ?Ash diffusion control dense constant size-spherical particles? model.

Jan 1, 2010

By Thais Cristina da Costa Caldas, Carlos Mauricio Fontes Vieira, Alline Sardinha Cordeiro Morais, Sergio Neves Monteiro

"This work has as its objective to evaluate the effect of the incorporation of a glass powder waste obtained from discarded and Hg-cleaned fluorescent lamp into clayey ceramics used to fabricate bricks and roofing tiles. Formulations were prepared with incorporation of the waste in amounts up to 10 wt.% into the clayey body. Rectangular specimens were prepared by uniaxial mold-press at 20 MPa to fire at 850 and 1050°C. The physical and mechanical properties evaluated were: linear shrinkage, water absorption and flexural rupture strength. The microstructure of the fired ceramics was evaluated by optical microscopy. The results showed that the waste incorporation significantly improved the evaluated properties mainly at 1050°C.IntroductionFluorescent lamps use mercury as a main component for its operation. This metal is potentially toxic and can contaminate soils, animals and water bodies. The problem is aggravated if considerations are made with respect to the amount of lamps that are commercialized and discharged in emergent countries like Brazil [ 1].By using appropriate recycling processes applied to discharging fluorescent lamps it is possible to reuse most constituents of these lamps into new productive processes. A study has shown that one million common fluorescent lamps can generate 900,000 tubes of clean glass [2]. Moreover, this Hg-cleaned gloss may be recycled in different products.In fact, to recovery and recycle all materials that constitute the lamp instead of discharging them. This action protects the soil avoiding the formation of environmental passives [3]. It is also relevant to mention that the glass from fluorescent lamps is 100% recyclable while its permanence in the environment would correspond to very long time pollution, since its decomposition time is undetermined [4]."

Jan 1, 2011

By Qiang Guo, Zongliang Zuo, Mengqi Wei, Qingbo Yu, Qin Qin

Activated carbons, derived from waste ion-exchange resin by CO2 physical activation, were applied to separate CO2 from flue gas against global warming. The BET specific surface areas of activated carbons at different activation temperatures and times were investigated. The CO2 adsorption capacity was tested under non-isothermal and isothermal conditions. The experimental results show that when keeping the activation temperature constant, the specific surface area increases firstly and then decreases with increasing activation time. For the given activation time, the specific surface area rises firstly and then declines with increasing activation temperature. The adsorption capacity decreases with increasing temperature. The maximum adsorption capacity is 51.46 mg/g under the condition of 298 K and pure CO2. Fractional order kinetic model is the best one to describe the kinetics of CO2 adsorption. The activated carbons show the potential to be an effective adsorbent for the removal of CO2 from flue gas.

Mar 1, 2018

By Xingjian Gao

The mechanical properties of a low carbon low alloy steel in the austenite and _-ferrite regions have been examined by thermal-tensile tests using a Gleeble-1500D system at temperatures in the range 600oC to 1300oC and at a strain rate of 10-3/s; these being the conditions that apply to the unbending operation during the continuous casting of steel. The yield strength and tensile strength of steel decreased with increasing test temperature and the embrittlement zone occurred in the temperature range 800oC to 970oC. In the embrittlement zone, the fracture surfaces and microstructures of the tensile specimens were examined by scanning electron microscope. The results showed that the cause of the embrittlement at 950oC in which the minimum %R of A was around 36% is the second phase particles precipitated along the _ grain boundary during deformation leading to inter-granular brittle fracture.

Jan 1, 2010

By Patrick R. Taylor

In the search for the development of more "environmentally friendly" and more intensive waste disposal approaches to meet more and more stringent environmental regulations, thermal plasma-based processes are considered one of the most promising alternatives to well- established technologies such as incineration. This paper presents an overview on the research and development status of thermal plasma-based waste remediation technologies. The properties of thermal plasma are described. Due to its unique feature of high-energy intensity and super high temperature, thermal plasma is particularly capable of destroying organic- containing wastes. Its potential and promising application to waste remediation may include: treatment of incinerator ashes; metallurgical dusts (especially, electric arc furnace dust); medical wastes; radioactive wastes; and other Resource Conservation and Recovery Act (RCRA) listed hazardous wastes. Many research institutes and vendors have been involved in the development of thermal plasma-based waste treatment technology encouraged by the cleanup programs supported by the Environmental Protection Agency (EPA), the Department of Energy (DoE) and the Department of Defense (DoD). More recently, thermal plasma-based waste treatment technologies (sometimes called plasma-enhanced pyrolysis) are focused more and more on not only just destroying organic wastes but also on how to practically, and economically recover energy contained in the organic waste materials in addition to the recovery of metals in order to offset the high operating costs.

Jan 1, 2003

By R. C. Chaturvedi, S. B. Padwal

"Padwal and Chaturvedi have developed the model based on M-K theory, considering Hosford's yield criterion and critical thickness strain criterion"" to predict the sheet metal forming limits under simple (constant) strain ratio paths. This analysis has been extended in this paper to predict the sheet metal forming limits under complex strain paths. The effects of exponent ""a"" in Hosford's yield criterion and strain paths on the forming limits under complex strain paths are studied using this analysis. The predictions of the present analysis are compared, both for simple and complex strain paths, with experimental results of Ishigaki for A.K. steel and also with the predictions of Rao and Chaturvedi's model. The quantitative analysis of the error in predicting the forming limits has also been carried out using a method suggested by the authors earlier.1. INTRODUCTIONThe constant strain ratio condition has been assumed in the theories developed for prediction of forming limit diagrams (FLO). In actual forming operation, this condition is seldom satisfied. Even in the case of simple single stage press formed components, the strain path becomes curved and non-linear. In the case of pressings with complex shapes, or multiple stages of forming, the changes in strain path are more pronounced and even abrupt.Experimental study of the forming limits, under two stage strain paths, by Ishigaki [1], has shown that the forming limits are path dependent. It has been observed that the forming limits lower than that under simple strain paths, may be obtained under certain strain paths (when the first stage strain path is either equibiaxial tension or uniaxial tension, followed by the second stage strain path as plane strain). Rasmussen's work [2J, on the theoretical study of forming limits under curvilinear strains paths, has shown that a large drop in formability can result from very small changes in strain path. Thus if a deformation process gives rise to failures due to plastic instability, the failure is not necessarily due to insufficient formability of the material. In such cases, FLOs based on constant strain ratio path should not be used directly in predicting the success or failure of the forming operation. Thus the knowledge of forming limits under complex strain paths is of great importance to the interpretation of press-shop problems."

Jan 1, 1994

By Ji-He Wei

Keywords: stainless steel, AOD refining, side and top combined blowing, mixing characteristics, water modeling The fluid mixing characteristics in the bath during the side and top combined blowing AOD (argon-oxygen decarburization) refining process of stainless steel have preliminarily been studied on a water model unit of a 120 t AOD converter. The geometric similarity ratio between the model and its prototype (including the side tuyeres and the top lances) was 1:4. On the basis of the theoretical calculations for the parameters of the gas streams in the side tuyeres and the top lances, the gas blowing rates used for the model have more reasonably been determined. The influence of the tuyere number and position arrangement, and the gas flow rates for side and top blowing on the characteristics has been examined. The results demonstrated that the liquid in the bath underwent vigorous circulatory motion during gas blowing, without obvious dead zone in the bath, resulting in a well mixing effectiveness. The gas flow rate of the main tuyere had a governing role on the characteristics, a suitable increase in the gas flow rate of the subtuyere could improve mixing efficiency, and the gas jet from top lance could make the mixing time prolong. Corresponding to the oxygen top blowing rate specified by the technology, a roughly equivalent and good mixing effectiveness could be reached by using six side tuyeres with an angle of 27° between each tuyere, and five side tuyeres with an angular separation of 22.5° or 27° between each tuyere. The relationships of the mixing time with the gas blowing rates of main-tuyeres and sub-tuyeres and top lance, the angle between each tuyere, and the tuyere number have been obtained.

Jan 1, 2005

By T. Shibasaki, S. Kamio, K. Kanamori

"Mitsubishi Process has been proven through fifteen years operation to be highly productive, cost efficient and easy to abate environmental requirements. However, in order the process to remain competitive from now on, it should also be adaptable to a variety of varying conditions. Various test works have been conducted from such a stand point of view and some of the new concepts have been implemented to the actual operation.The paper discusses the adaptability of the process to the change of concentrate grade with respect to copper and also impurities, acceptability of the secondary materials and the potential to increase unit capacity. IntroductionThe first commercial plant of Mitsubishi Process with 48,000 mt copper annual capacity started its operation at Naoshima Smelter of Mitsubishi Metal Corporation in 1974, and the second plant with 65,000 st annual capacity started in 1981, at Kidd Smelter, Timmins, Ontario, now Kidd Creek Division of Falconbridge Limited 2. These plants have increased their capacities to 90,000 mtpa respectively by adding oxygen and acid plant capacities while maintaining the original furnace design uncharged. Thereby both smelters have established more cost efficient operations. (3), (4)Mitsubishi Process applies so-called multi-furnace continuous system. Figure 1 shows conceptual flowsheet. Backgrounds that required and justified the development of such system are as follows:"

Jan 1, 1988

By Z. Zak Fang, P. Fan, S. Middlemas

"Titanium dioxide (T1O2) has been widely used as pigment in paints, paper and cosmetic products, as well as high-tech applications such as PV Cells, semiconductors, biomedical devices and air purification. T1O2 pigment is primarily produced by the high temperature chloride process, resulting in considerable CO2 emissions. A novel hydrometallurgical process for making T1O2 pigment without direct CO2 emission is investigated. The new method promises to eliminate direct CO2 emissions, consume significantly less energy, and produce minimal environmental waste. The novel process involves molten salt roasting of titania slag, with subsequent washing, leaching, solution purification, hydrolysis, calcination and post-treatment stages, resulting in high-purity anatase or rutile pigments while realizing significantly reduced environmental impacts. Pigment whiteness is critically sensitive to trace amounts of discoloring impurities such as iron and chromium. Several methods for reducing the levels of these impurities are investigated. Energy consumption and emission models are also developed.IntroductionTitanium dioxide (T1O2) is one of the most commonly used minerals in the chemical manufacturing industry. It has been commercially processed since the early 1900's, and has a wide variety of applications. Pigment is used in paints [1], plastics and paper [2], sunscreen [3], cosmetics and even as a food additive [4]. T1O2 has also been used in photovoltaic cells [5], biomedical devices [6], and in air purification [7]. T1O2 pigment has a refractive index of 2.7, which imparts a high level of opacity (and hence whiteness) to whatever material it is added [8]."

Jan 1, 2012

By Derek J. Fray

The need for on-line sensors is outlined and it is demonstrated that the control of many processes is prevented by the availability of these devices. The use of solid electrolytes is described for the sensing of elements in molten pyrometallurgical phases. In the cases where there is no suitable electrolyte, the addition of a second phase of a compound containing both the element to be measured and the element whose ion is mobile in the electrolyte can be used. For the measurement of high concentrations of an element a method based on current measurement is proposed.

Jan 1, 1994

By Valerio Viti

In High Pressure Die Casting a molten metal is injected through a thin gate into the cast cavity. High injection pressures and high gate velocities create atomization phenomena which can negatively affect the final quality of the cast. In order to control atomization process it is essential to understand the atomization patterns and the two-phase flowfield that exist at the gate exit. In the present work, 2D numerical simulations of the flow of molten Magnesium through a high aspect-ratio rectangular gate are performed using a water analogue for an open and closed cavity. The numerical simulations made use of VOF-type (Eulerian) physical models and Lagrangian models. Further, a sub-grid scale model was implemented that, in conjunction with VOF-type equations can efficiently predict the general atomization pattern without the need for high-resolution grids. The numerical results were compared to experimental data for validation.

Jan 1, 2006

By A. J. Rigby

Refractory linings in converters or anode furnaces used to over-oxidize the blister copper will suffer rapid deterioration, due to prolonged contact with copper oxide-rich slag. Nitrogen stirring with COP KIN porous plugs and use of SEMTECH OPC in converters and anode refining vessels can considerably reduce both refractory wear and processing times. In addition, careful control of the vessel atmosphere and the use of real-time optical process control minimize both slag volume and contact time with the vessel refractory.

Jan 1, 2005

By C. I. A. John

The slag dump at ZCCM's Nkana Division contains some 16 million tomes of slag, deposited since the mid-1930's. The average cobalt grade of the slag is 0.65% with some areas as high as 3%. Current arisings of slag from Nkana Smelter also contain significant tonnages of cobalt. Intensive investigations were conducted in the past into methods of recovering cobalt from these slags, although none of the processes was developed to a commercial scale. The company is now working to develop a long-term strategy for ensuring the continuing production of cobalt at optimum levels, and the resource represented by the Nkana slags will be a major component in such a strategy. The present paper reviews the various processes which have been considered for recovering cobalt, both from the dump slag and from the current slags.

Jan 1, 1993

By H. Matsuda, T. Iwashita, H. Awata, H. Liwei, D. Hirabayashi, Y. Saito, S. Ozawa, Y. Goto

"The present study is concerned with investigating the effect of chemical treatment on enhancing the HCl absorption capacities of coal burnt ash and slag. It was found that the HCl absorption capacity of coal burnt ash discharged from fluidized bed combustor was improved by hydration with water and 5% polyethylene glycol solution. This phenomenon was based on an increase of the specific surface area of treated coal burnt ash. The HCl absorption capacity of hydrated ash with polyethylene glycol solution was almost equivalent to that of standard CaO and Ca(OH)2. In particular, the specific surface area of hydrated ash with polyethylene glycol solution was found to be 19 m2/g, which was more than over eight times larger than that of raw sample. Hydrated slag treated with lON sodium hydroxide solution also showed high HCl absorption capacity, with highly improved surface area. It was found that the absorption capacity of slag for HCl depended on the treatment time, showing the maximum absorption capacity for 12 hours of hydration treatment.IntroductionA large amount of coal burnt ash, slag and dust are discharged from such industrial processes as coal combustion and metal refinery etc., and it becomes an serious problem to recover and diminish these solid wastes because of the shortage of dump sites and subsequent metal elution to the environment. Figure 1 shows the present situation of reutilization of coal burnt ash and slag in Japan [1,2]. It is shown in this figure that these solid wastes are recycled as materials in the fields of earthwork, agriculture and forestry etc. A part of these solid wastes, however, is still dumped to landfill. To decrease this dumped amount, the development of environmentally friendly reutilization technique for these solid wastes is of great importance."

Jan 1, 2000

By K. P. V. Lei

The U.S. Bureau of Mines investigated a hydrothermal sulfidation procedure to recover lead and silver from plumbojarosite. The plumbojarosite, generated during pressure-oxidative leaching of zinc concentrate in a commercial operation, contained, in percent, 25.4 pb, 18.8 Fe, 1.4 Zn, 29.5 SO,2-, 3.2 s?, 13.4 total sulfur, and 7.4 oz/ton Ag. The sulfidation was conducted in an autoclave and converted the plumbojarosite to amorphous iron oxide and liberated the lead and silver as sulfides. The best operating conditions were using 50 9 of plumbojarosite and 7 pct s? (2.04 9 S? added) in 500 mL of 2.0 mol/L NH3, 150? C, and 1 h. The sulfidation product contained, in percent, 37 Pb, 28 Fe, 6 S2-, 2 SO,2-, and 11.2 oz/st Ag. Ferric chloride leaching extracted 98 pct Pb and 97 pct Ag from the sulfidation product.

Jan 1, 1990

By Hui Lu

The structural changes in solutionized AA2618 during natural aging and their effects on subsequent artificial aging were investigated by hardness measurements, X-ray diffraction, differential scanning calorimetry and transmission electron microscopy. The changes in lattice parameter and hardness during natural aging indicate that copper-enriched clusters form in the earliest stage, followed by the formation of magnesium-enriched clusters and coppermagnesium co-clusters. Prior natural aging consistently weakened the hardening during subsequent artificial aging at 180, 200 and 230 °C but had no effects on artificial aging at 150 °C. The decreased age hardening was attributed to the reversion of small clusters/zones that formed during prior natural aging. The lattice parameter exhibited erratic changes with increasing artificial aging time, reflecting the complex sequence of the reversion and precipitation.

Jan 1, 2006

By Liyuan Chai, Qin Liu, Bing Peng, Jia Wang, Qiang Zhang

"Electrolytic Manganese Residue (EMR) was used as the main material to prepare cementing material activator for the utilization of the residue from electrolytic manganese dioxide (EMD) or electrolytic metallic manganese (EMM) production. The effects of chemical activation, thermal activation and mechanical activation on retarding activity and excitation activity of EMR were investigated according to the setting time and activity index of EMR-slag cementing material. The results showed that the EMR exhibited good activating performance after being ball-milled for 18 min and then treated for 1-2 hours at temperature range of 350-450 ?. The optimal properties of cementing material activator were achieved at the weight percent ratio 30 : 3 : 5 of EMR/Ca(OH)2/cement clinker.IntroductionMany hazardous industrial solid wastes such as blast furnace slag, fly ash, steelmaking slag, chromic slag and electrolytic manganese residue [1] are generated n China and their amounts increases every year. The accumulation of the solid wastes during past years is very huge and they could be hardly recycled effectively as a sustainable resource. 2.35 billion tons of industrial solid wastes have been produced up to now [2]. It is estimated that they would exceed 3.3 billion tons by the end of 2015 [3]. On the other hand, the quick development of Chinese infrastructural construction needs more cementing materials. The production of traditional building materials consumes lots of natural resource such as clay and limestone and discharges at least 1 ton CO2 and other pollutants per ton clinker [4]. Therefore, it is necessary to develop new types of cementing materials instead of clinker [5,6]."

Jan 1, 2012

By Othon do Rêgo Monteiro Neto

[The present study has investigated the extraction of copper from a chalcopyrite flotation concentrate using an adapted strain of Thiobacillus ferrooxidans and shake flasks, tank leaching and Warburg respirometer techniques. From the shake flask experiments, the activation energy and the frequency factor have been determined to be ?ka = 59.4 kJ and A = 3.3 x 105 S-1, respectively. The temperature coefficient was found to be Q10 = 2.2 in the range of 20 to 35°C. It was suggested that the reaction mechanism of chalcopyrite leaching by T. ferrooxidans involves the formation of an activated complex. whose thermodynamic values have been calculated to be ?G? = 92.1 kJ, ?S? -148.8 J K-1 and ?H$ = 47.8 kJ. The maximum volumetric oxygen mass transfer coefficient for the reactor leaching was found to be achieved by using an optimum air flow rate of 1970 cm min l at a rotational frequency of 1000 min-1. The highest copper extraction in tank (reactor) leaching experiment was 86.8% after 17 days of leaching, while in the sterile runs the corresponding copper extraction was only 40.1%. The copper extraction was suggested to be diffusion controlled. The power requirement of the aerated reactor was calculated to be Pg = 2.02 watts. During leaching, the oxygen saturation concentration was found to be C* = 6.70 mg dm-3. Using the gassing out method the critical oxygen concentration was assessed to be CCrit 0.05 mg dm 3. From the Warburg experiments, the kinetic parameters of the Monad equation were derived with a new evaluation technique to be Vmsp = 9.0 µm3 02 min-1 mg protein-1 and K = 7.4% pulp density for the effect of substrate concentration. The order of reaction and the overall reaction rate constant were determined from the modified van't Hoff plot to be n = 0.0 and k = 1.49 p dm3 02 min-1 mg Protein -1 for the chalcopyrite concentrate oxidation by T. ferrooxidans. On the basis of this experimental work, a preliminary flow sheet has been proposed for the bioextraction of copper from flotation concentrates.]

Jan 1, 1985